Electroless Nickel Deposition: An Alternative for Graphene Contacting

Oct 21, 2016 - (6, 7) Contact resistances on graphene have previously been reported in ... in acetone, hence inhibiting further nickel deposition in t...
0 downloads 0 Views 2MB Size
Subscriber access provided by CORNELL UNIVERSITY LIBRARY

Article

Electroless Nickel Deposition: an Alternative for Graphene Contacting Sinziana Mirela Popescu, Anders J. Barlow, Sami Ramadan, Srinivas Ganti, Biswajit Ghosh, and John Hedley ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.6b08290 • Publication Date (Web): 21 Oct 2016 Downloaded from http://pubs.acs.org on October 24, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Electroless Nickel Deposition: an Alternative for Graphene Contacting Sinziana M. Popescu†*, Anders J. Barlow§, Sami Ramadan¥, Srinivas Ganti¥, Biswajit Ghosh‡, John Hedley† †

School of Mechanical and Systems Engineering, Newcastle University, NE1 7RU, United Kingdom §

National EPSRC XPS Users' Service (NEXUS), Newcastle University, NE1 7RU, United Kingdom ¥

School of Electrical and Electronics Engineering, Newcastle University, NE1 7RU, United Kingdom



School of Energy Studies, Jadavpur University, Kolkata 700 032, India

*Corresponding author email address: [email protected]

ABSTRACT: We report the first investigation into the potential of electroless nickel deposition to form ohmic contacts on single layer graphene. Aiming to minimize the contact resistance on graphene, a statistical model was used to improve metal purity, surface roughness and coverage of the deposited film by controlling the nickel bath parameters (pH and temperature). The metalized graphene layers were patterned using photolithography and contacts deposited at temperatures as low as 60°C. The contact resistance was 215 ± 23 Ω over a contact area of 200 µm x 200 µm, which improved upon rapid annealing to 107 ± 9 Ω. This method shows promise towards low-cost and large-scale graphene integration into functional devices such as flexible sensors and printed electronics.

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 24

KEYWORDS: contacting graphene, electroless nickel, contact resistance, transmission line method, interface characterization INTRODUCTION Novel nanomaterials such as graphene pose a challenge for available ohmic contact deposition techniques, as the associated contact resistance represents a major drawback in high-performance electronics applications 1. Different methods have been employed in order to reduce and control contact resistance on graphene, such as improved surface cleanliness 2, controlled introduction of graphene edges

3,4

and high purity controlled metal deposition 5. Contact arrangement and

interface engineering have also been attempted for graphene-metal interface improvement

6,7

.

Contact resistances on graphene have previously been reported in the range 294 Ω·µm 8 – 12 kΩ·µm

7

using conventional (thermal and e-beam) evaporation techniques. The reproducibility

of contacting methods onto various types of graphene is acknowledged as a major challenge 9,10. The electroless nickel plating method provides opportunities over conventional evaporation approaches, the foremost being the processing time (in the order of a few minutes), cost and accessibility as it does not require the clean room infrastructure normally associated with evaporation techniques. It can be achieved at low temperatures (T