Electron Paramagnetic Resonance as a Structural Tool to Study

1. 2. 3. 4. 5. 6. 7. 8. 9. 10. 11. 12. 13. 14. 15. 16. 17. 18. 19. 20. 21. 22. 23. 24. 25. 26. 27. 28. 29. 30. 31. 32. 33. 34. 35. 36. 37. 38. 39. 40...
0 downloads 0 Views 1MB Size
Subscriber access provided by Nottingham Trent University

C: Physical Processes in Nanomaterials and Nanostructures

Electron Paramagnetic Resonance as a Structural Tool to Study Graphene Oxide: Potential-Dependence of the EPR Response Bin Wang, Alistair J. Fielding, and Robert A.W. Dryfe J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.9b04292 • Publication Date (Web): 14 Aug 2019 Downloaded from pubs.acs.org on August 18, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1

Electron Paramagnetic Resonance as a Structural

2

Tool to study Graphene Oxide: Potential-

3

dependence of the EPR response Bin Wang,† Alistair J. Fielding‡* and Robert A.W. Dryfe†*

4 5

†School

of Chemistry, University of Manchester, Oxford Road, Manchester M13 9PL, United

6 7

Kingdom ‡School

8

of Pharmacy and Biomolecular Science, Liverpool John Moores University, James Parsons Building, Byrom Street, Liverpool, L3 3AF, United Kingdom

9 10 11 AUTHOR INFORMATION 12 Corresponding Author 13

*Email:

[email protected] (A.J.F.)

14

*Email:

[email protected] (R.A.W.D.)

15

16

ACS Paragon Plus Environment

1

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 27

1 ABSTRACT

2 Electron paramagnetic resonance (EPR) spectroscopy is reported as a tool to probe the behavior 3 of graphene oxide (GO). The potential-dependent response of GO is reported for the first time, 4 and correlated with the observed electrochemical response. The EPR signal, de-convoluted into 5 two constituent parts, was used along with lineshape simulation and the temperature dependence 6 to probe the electrochemical processes. The EPR signal is found to be well described by two 7 components: the narrower one is associated with unpaired electrons on localised functional 8 groups, and shows a reversible increase as the GO is biased to positive potentials. The Curie 9 behaviour of this component suggests that it increases because of the formation of stable radical 10 species, such as semiquinones, derived from quinones and other carbonyl functional groups 11 found on GO. A stronger dependence of the narrow component with potential, and an elevated g 12 value over 2.0034, is found in alkaline conditions compared to neutral electrolytes, reflecting the 13 greater stability of seminquinone-like species at higher pH. By contrast, the second, broader 14 component of the EPR signal was found to be potential independent. The EPR approach 15 described here offers a solution phase alternative, which can be employed under electrochemical 16 control, to techniques such as X-ray photoelectron spectroscopy and Raman spectroscopy, as a 17 means to probe the structure of GO and related materials.

18

19

20

ACS Paragon Plus Environment

2

Page 3 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1 TOC GRAPHICS

2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18

ACS Paragon Plus Environment

3

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 27

1 INTRODUCTION 2

There has been much interest in the application of 2D materials, derived from the prototypical

3 material graphene, in electrochemical energy storage.1-5 Although microscopic (electron 4 microscopy, atomic force microscopy) and spectroscopic (X-ray photoelectron spectroscopy, 5 Raman spectroscopy) methods are widely used to probe the structure of the materials, and 6 consequently relate the structure to the observed electrochemical response, only the Raman 7 approach is readily compatible with in situ solution phase studies. For the use of GO in 8 supercapacitors, for example, it is important to be able to relate structure to function as GO can 9 store charge via classical “double-layer” mechanisms and via pseudo-capacitive routes, 10 involving the oxidation/reduction of oxygen-containing functional groups. The key challenge 11 with supercapacitors is to optimize structure to improve energy density, by improving their 12 capacitance (such as nanostructuring and/or enhancing their pseudo-capacitive component), or 13 maximizing their usable voltage range (by using ionic liquid electrolytes or hybrid 14 supercapacitors).2,5-9 15

Functionalization with oxygen groups is a promising method to enhance supercapacitors

16 because these functional groups provide external pseudo-capacitance and improve the wetting 17 properties of the electrode in aqueous solution.5,

8, 10-23

For example, functionalized graphene

18 prepared by a low-temperature thermal treatment has a gravimetric capacitance of up to 450 F 19 g−1.8 In addition, the pseudo-capacitance, imparted to graphene by representative oxygen20 containing groups, has been shown to be pH dependent13, 16, 20:

21

(1)

ACS Paragon Plus Environment

4

Page 5 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1

(2)

2

(3)

3 Quinone groups are generally supposed to cause pseudo-capacitive enhancement in acidic 4 conditions, whereas carboxyl groups are thought to produce the faradaic reactions under alkaline 5 condition, due to the relative ease of oxidation of the carboxylate group at high pH [Eqns. 1-3].11, 6

16, 21, 23

Understanding of the charge storage mechanism of oxygen-functionalized graphene at the

7 microscopic level is still lacking, despite the computational approaches to the problem reported 8 in a number of papers.24-27 9

GO is a particularly complex material, both in terms of chemical structure and its re-assembly

10 to form a laminate type material, a form which has been widely used as an electrode for studies 11 of supercapacitance.28-30 Electron paramagnetic resonance (EPR) spectroscopy has been used 12 previously to study GO, although we are unaware of any previous in situ electrochemical EPR 13 work.31-42 Recent work by Augustynika-Jablokow et al. has shown the existence of slowly 14 relaxing paramagnetic centers in GO attributed to isolated unfunctionalized carbons in highly 15 functionalized regions.31, 32 Our previous paper described the magnetic properties of GO, without 16 metal impurities associated with its formation, and its pH dependent behavior. This work 17 identified two types of spin on GO: localized sigma “dangling bond” spins associated with 18 defects with a narrow linewidth. By “defect” we mean any functional group or atom that can act 19 as a local “trap” for unpaired electrons. A broader signal is associated with delocalised π 20 electrons from the remaining aromatic domains.33 The EPR signal of GO was found to be pH21 dependent, i.e. the greatest EPR signal was detected when exposed to aqueous KOH solutions,

ACS Paragon Plus Environment

5

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 27

1 which was explained in terms of a further oxidative fragmentation of the carbonaceous 2 framework. 3

In this contribution, in situ electrochemical EPR spectroscopy is used to study the potential-

4 dependent response of GO in Na2SO4 and KOH (1 M) aqueous electrolytes based on a three 5 electrode capillary cell after a stabilization process due to radical quenching in aqueous 6 solutions (Figure S1). Additionally, temperature-dependent EPR spectroscopy was used to study 7 the relationship between the unpaired spins and structure. We are only aware of one previous 8 study of the potential-dependent EPR response of graphene-based materials, which focusses on 9 graphene (as opposed to GO) prepared by chemical vapor deposition and used a polymer gel 10 electrolyte to reveal a correlation between the spin susceptibility of the material and in-plane 11 conductivity.43 No specific analysis of the electrochemical response was made in this work on 12 CVD graphene. Additionally, the nature of the spins generated by redox reactions in the alkaline 13 electrolyte employ herein can be tested through the changes in the g value of the EPR 14 spectroscopic signal. Quantitative analysis in different electrolytes shows a correlation between 15 the increased capacitance seen in the alkaline electrolyte, and the spectroscopic signal which we 16 ascribe to the enhanced pseudo-capacitive behavior of the oxygenated functional groups. Further 17 simulations allowed the distribution of the mobile electrons as a function of potential to be 18 investigated, which is also beneficial for understanding the pseudo-capacitive process on 19 graphene-based materials. 20 Methods 21

Graphene oxide: GO was prepared by a modified Hummer’s method, as reported elsewhere.44

22 To remove impurities, such as residual manganese ions and oxidative debris, a simple base wash 23 was used, following previous reports.33, 42, 45 The base reflux also reduces oxygen functionalities

ACS Paragon Plus Environment

6

Page 7 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1 (mainly hydroxyls) by the dehydration reaction, and further acidification was used to re2 protonate the COO- groups.42 In particular, GO (1.2 mg/mL) was refluxed in aqueous 0.1 M 3 NaOH (Sigma-Aldrich) for 1 h at 100 ◦C, and then the treated GO was separated by filtration. 4 The obtained product was dispersed in 0.1 M HCl (Fisher Chemical) followed by reflux for 1 h 5 at 100 ◦C. The final product was washed by filtration. The flake size of the GO is in the range of 6 1-5 μm2:33 the above washing procedure is followed to eliminate small molecule organic and Mn 7 residues initially present in the sample, which otherwise greatly affect the observed EPR 8 response.33, 42 9 Working electrode: The GO film was prepared by a simple filtration process, described below, 10 and used as the working electrode in the three electrode, in situ experiments. The GO suspension 11 (re-dispersed in water by sonication for 2 h at 37 kHz and 350 W effective power, Fisherbrand 12 FB11205 Ultrasonic Cleaner) was filtered onto a PTFE membrane (25 mm diameter hydrophilic 13 PTFE membrane filter with a 0.1 μm pore size and maximum thickness of 140 μm, Merck 14 Millipore Company). After drying at 80 ◦C, the polymer-supported GO film was twined with Pt 15 wire (99.99% purity, Advent Research Materials Ltd., UK) to bind the film and to function as the 16 current collector for the GO working electrode (WE), in line with our previous report.46 The 17 surface area of the resultant WE is around 5 mm2. 18

The resistance (Rs) of the GO based membrane was measured by the four-probe meter (Jandel

19 Engineering, Linslade, UK) with the nanovoltmeter (2182A) and current source (6220, Keithley 20 Instruments, Cleveland, OH, USA). The conductivity (σ) was calculated based on the membrane 21 thickness (l) and the resistance: σ=1/(l* Rs).

ACS Paragon Plus Environment

7

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 27

1 The in situ electrochemical EPR cell was based on a three-electrode system as previously used 2 (Figure 1),46 where CE and RE denote the counter and reference electrodes, respectively. All 3 potentials are reported with respect to the RE: the Ag|AgCl RE was prepared by oxidation of 4 partly exposed Ag wire (99.99% purity, Advent Research Materials Ltd., UK) and Pt mesh 5 (99.99% purity, Advent Research Materials Ltd., UK) was used as the CE. Epoxy was used to 6 seal the connecting joint between the exposed Ag wire contact and the Pt wire used to bind the 7 GO WE. This helps to avoid internal short circuit. The diameter of the quartz capillary is 1 mm. 8 The potential waveform was applied with a potentiostat (EmStat3+ Blue, PalmSens, the 9 Netherlands). The EPR spectra were recorded using a continuous-wave (CW) Bruker EMXmicro 10 spectrometer at room temperature. In all cases, the microwave frequency was approximately 9.8 11 GHz, and the modulation amplitude was 2 G. Triplicate samples were made for in the in situ 12 EPR experiment, with the reported spectra being the average of 20 scans. The spin density of 13 purified GO was found to be 3.5(3)  1019 spins g-1 (Figure S2). The quality factor (Q factor) was 14 measured by the Ruby and found to be constant over the potential range used.46 Temperature 15 dependent experiments (from 4 K to 200 K), to study the origin of the EPR signal as a function 16 of applied potential, were achieved by freezing the electrodes rapidly (within 5 secs) in liquid 17 nitrogen after applying the relevant potential for 5 mins. Temperature calibration was carried out 18 using a temperature sensor (Cernox®, Lake Shore Cryotronics, Inc.) inserted into the sample 19 position. Further details of electron microscopy (used for GO characterization) and EPR signal 20 characterization are provided in the Supporting Information.

ACS Paragon Plus Environment

8

Page 9 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1

2 3 4 5 6 7 8 9 10

Figure 1. Schematic diagram of the in situ EPR cell with a three electrode system in the capillary. a) Supporting Pt wire (diameter 0.5 mm); b) WE, GO membrane coated onto Pt wire, with the length of ~ 2 cm; c) intertwined Pt wire (diameter 0.05 mm); d) Sealant epoxy, prevent the short-circuit, not in the EPR detecting area; e) RE, insulated Ag wire (diameter 0.2 mm, coated with PTFE) with one end oxidized; f) Insulated Ag wire (diameter 0.2 mm, coated with PTFE) to line the WE and the potentiastant; g) CE, Pt mesh; h) Quartz capillary (diameter 1 mm); i) Aqueous electrolytes, e.g. Na2SO4/KOH; j) Sealant epoxy; k) In situ cell introduced into the EPR cavity.

11 12 Results and Discussion 13

The oxygen atoms of GO are thought to be distributed amongst various functional groups such

14 as hydroxyl, carbonyl and carboxyl.33 The electrochemical performance of the GO membrane 15 (thickness of 3 μm, Figure S3) in different pH electrolytes was recorded using the three-electrode 16 configuration: the resultant cyclic voltammograms (CVs) are shown in Figure 2. The 17 voltammetric responses of GO are pH dependent: the capacitance in 1 M KOH (54 F g−1 at a 18 scan rate of 50 mV s−1) is higher than that in 1 M Na2SO4 solution (44 F g−1). The oxygen19 containing functionalities responsible for the faradic reaction are observed more clearly in the 20 CV under alkaline conditions. This increase in capacitance can be attributed to the redox 21 reactions of the carboxyl groups in KOH electrolyte. The capacitance of our GO sample is higher 22 than some reported values for GO (e.g. ~ 27 F g−1 in 1 M Na2SO428), while it is somewhat lower 23 than other literature, which have generally modified the GO materials (e.g. 135 F g−1 in 5.5 M

ACS Paragon Plus Environment

9

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 27

1 KOH30; reduced graphene oxide with a capacitance to 220 F g−1 in 4 M KOH13). The lower 2 capacitance in our sample could be related to its low conductivity (3.6 S m−1) and also the 3 limited space within the narrow bore in situ EPR cell meaning the GO sample thickness is lower 4 than frequently used in previous reports. Although there have been numerous reported 5 mechanistic explanations of the pH dependence of the capacitance, here we employ in situ EPR 6 spectroscopy to probe GO in different electrolytes.

7 8 Figure 2. The electrochemical performance of the GO electrode in different electrolytes at a scan 9 rate of 50 mV s-1. 10 11

Initially, the GO material was tested at room temperature for slow relaxing spin centers, using

12 in-phase and out-of-phase EPR signals, as described by Augustynika-Jablokow et al.31-32 13 However, no significant out-of-phase signal was observed (Figure S4) suggesting that faster 14 relaxing centers exist in our material. This apparent discrepancy is very likely caused through 15 differences in preparation and washing procedures. The GO structure is known to be very 16 sensitive to “sample history”.31-37, 42

ACS Paragon Plus Environment

10

Page 11 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

The in situ electrochemical continuous-wave (CW) 9 GHz EPR study of the GO electrode was

2 carried out by applying a constant potential to the electrode and monitoring the EPR signal. The 3 cell was cycled 20 times (by cyclic voltammetry at 50 mV s−1, over potential limits from −0.8 V 4 to 0 V in each electrolyte) to obtain a stable response before the in situ EPR experiment. The 5 spectroscopic response obtained from GO during potentiostatic charging and discharging in 1 M 6 Na2SO4 is summarized in Figure 3. The EPR signal of the GO electrode was found to increase as 7 the applied potential was swept positive (shown in Figure 3a), and returned to the original when 8 the cell was discharged from 0 V to −0.8 V reversibly, as shown in Figure 3b.

9 10 Figure 3. In situ EPR response of GO in 1 M Na2SO4 over the potential range −0.8 V to 0 V. (a) 11 EPR spectra during charging from −0.8 V to 0 V; (b) EPR spectra during discharging from 0 V 12 to −0.8 V. 13

ACS Paragon Plus Environment

11

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Page 12 of 27

The EPR lineshapes are assumed to be described by Lorentzian functions due to the

2 homogeneous distribution of radical species.47 The EPR spectra in neutral electrolyte can be 3 fitted with two components (Figure 4a, b and Figure S5): a narrow Lorentzian curve with 4 linewidth around 2.5 G; an asymmetric broad Lorentzian curve (asymmetry ratio, A/B ~1.5, 5 Figure S6) with linewidth of 12 G, that is characteristic of conducting samples with mobile 6 electrons. The EPR component with the narrow linewidth indicates a localized state with long 7 spin relaxation times, suggesting defect related spins likely to be oxygen centered radical species 8 from the redox reaction of the oxygenated functional groups.33, 46 The double integration value 9 (the absolute area value) of the EPR signal, which is related to the spin density of the active 10 material, increases by ~20 % over the positive potential sweep (Figure 4c). Although the narrow 11 resonance shows a reversible increase in spin density, the broad resonance does not change 12 (while the relative ratio changes from 30% to 25% from −0.8 V to 0 V due to the increase of the 13 narrow component). The g value of the narrow curve was found to be 2.0031, suggesting these 14 spins are carbon-based although located on carbon atoms with proximity to oxygen atoms, which 15 is consistent with our interpretation of the electrochemical data. The potential independent broad 16 component has a lower g value of 2.002 and the g value did not show a regular change with 17 potential. The broad curve has been related to conductive -carriers propagating in the extended 18 aromatic graphite-like structure.33,

35, 40, 42, 48-50

The linewidth of both components remained

19 constant over the potential range studied.

ACS Paragon Plus Environment

12

Page 13 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1 2 Figure 4. EPR lineshape simulation of GO under potentials in 1 M Na2SO4 during (a) charging 3 and (b) discharging; (c) summary of the double integration value of simulated components over 4 charging/discharging 5 6

Additionally, an in situ EPR experiment of the GO electrode was carried out in a 1 M KOH

7 solution to investigate the enhanced capacitance observed in basic electrolyte (see Figure 2). A 8 similar change to that seen in neutral electrolyte was found, as shown in Figure 5a,b: the EPR

ACS Paragon Plus Environment

13

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 27

1 signal of GO in KOH increased with potential and then returned when the potential was 2 decreased from 0 V to −0.8 V.

3 4 Figure 5. In situ EPR experiment of GO in 1 M KOH over the potential range −0.8 V to 0 V. (a) 5 EPR spectra during charging from −0.8 V to 0 V; (b) EPR spectra during discharging from 0 V 6 to −0.8 V. 7 8

In this case, however, only a single Lorentzian signal with a linewidth of 2.5 G was required to

9 give an acceptable fit to experiment (see Figure 6a, b): the disappearance of the broad component 10 suggests a more defective structure when the GO was exposed to aqueous KOH.31 A summary of 11 the spin density change with potential is shown in Figure 6c, with the relative percentage 12 increasing by 27% from −0.8 V to 0 V. The narrow curve has a higher g value, of 2.0034, and 13 presents a stronger potential dependence compared to the neutral electrolyte case (as shown in

ACS Paragon Plus Environment

14

Page 15 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1 Figure 7). The higher g value means more oxygen-centered radical species are generated, which 2 is consistent with the known redox chemistry of common oxygen-containing functional groups 3 (specifically, the favored oxidation of hydroquinone or phenolate groups to semiquinone or 4 phenoxy species, respectively) at high pH.51 The linewidth was also constant over the potential 5 range.

6 7 Figure 6. EPR lineshape simulation of GO under potentials in 1 M 1 M KOH during (a) charging 8 and (b) discharging; (c) double integral of EPR signal as a function of applied potential.

ACS Paragon Plus Environment

15

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 27

1 2 Figure 7. Comparison of the potential dependent g value of the narrow component of the GO 3 electrode in 1 M Na2SO4 and KOH electrolytes. 4 5

To study the origin of the spins during charging/discharging, the temperature dependence of

6 the EPR signal from GO at 0 V was studied and is shown in Figure 8. The spin susceptibility, 7 calculated from double integration (the absolute value) of the first derivative EPR signal, is fitted 8 by the sum of the Curie-Weiss law and the Pauli law: 9 10

𝜒𝐸𝑃𝑅 = 𝜒𝑃 + 𝜒𝐶 ― 𝑊 = 𝜒𝑃 + 𝐶 (𝛵 ― 𝑇0)

(4)

Here χEPR, χP and χC-W stand for the potential-dependent spin susceptibility of the GO

11 electrode, the Pauli susceptibility and the Curie susceptibility, respectively; C is the Curie 12 constant and T0 is the Curie-Weiss temperature. The Curie-Weiss behavior suggests the narrow 13 signal comes from localized spins including the oxygen-centered radicals formed at defects 14 during the reduction process. The negative Curie-Weiss temperature (T0, −2.4 K in Na2SO4 and 15 −5.4 K in KOH) suggests anti-ferromagnetic behavior, which may be related to the localized 16 states on different sublattices.52, 53

ACS Paragon Plus Environment

16

Page 17 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

1 2 Figure 8. Temperature-dependent EPR behaviour of the GO film at 0 V in different electrolytes: 3 (a) 1 M Na2SO4 and (b) 1 M KOH. The temperature was varied from 4.2 K to 200 K. The solid 4 line represents the fitting results of the sum of Curie-Weiss and the Pauli Law (Equation 4). 5 6

The in situ EPR experiment was carried out to reveal the change of unpaired electron density

7 on GO during its charge and discharge in aqueous solution. GO, according to the Leif-Klinowski 8 model, contains oxygenated functional groups with hydroxyl groups decorating the basal plane, 9 and carboxylate and quinone groups on its edge.54 The comparison of the CV response of GO 10 (Figure 2) reveals redox peaks in both electrolytes, which have been attributed to the reactions 111 3 (see Introduction, written as reductions):13 Hydroquinone-type groups are oxidized to quinones 12 in proton-rich conditions (Equation (1)), but can be oxidized to the semiquinone intermediate 13 under alkaline conditions (Equation (2)). The redox reaction of carboxylate groups (Equation 14 (3)) in alkaline electrolyte also contributes to the pseudo-capacitive behavior. Electron transfer 15 between isolated quinone units in the extended structure of the GO is possible because the 16 material possesses some conductivity (vide supra) meaning that electrons can be transferred 17 within the solid, at least over limited regions. The same argument can also be applied to the 18 suggested reversible oxidation/reduction of the carboxylate species (Equation 3), assumed to 19 form at high pH. Such a radical would be expected to be highly unstable as part of a small

ACS Paragon Plus Environment

17

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 27

1 molecule, but would be stabilized somewhat as part of a more extended pi-system as found in 2 GO.55 Less distinct redox reactions are found in neutral electrolyte than in KOH electrolyte, 3 leading to lower capacitance, in agreement with previous reports, presumably because the above 4 reactions are less favored – or are less reversible – at lower pH.13, 20 5

The complexity of the structure causes the different origin of the spins: localized spins related

6 to functional groups after oxidation (e.g. semiquinone radicals); the delocalized mobile electrons 7 on the aromatic graphitic-like domains. The broad component of GO in Na2SO4 electrolyte was 8 found to be potential independent and the narrow signal shows the major variation in both 9 electrolytes during the in situ EPR measurement. Oxidation of the surface-bound oxygen 10 functional groups on the GO as the potential of the latter is swept positive causes the increase of 11 the density of localized spins, reflected in the increased narrow EPR signal with increasing 12 potential seen in Figures 3 and 5.46 The EPR signal intensity decreases when the potential is 13 swept to negative values, reflecting the resultant depletion of unpaired electron density. The 14 potential dependent narrow component in neutral electrolyte therefore suggests a pseudo15 capacitive origin from functionalities such as quinone and carboxylate groups. The variation of 16 the double integration value of the narrow resonance in 1 M KOH (ca. 7, Figure 6c) is much 17 higher than in the neutral electrolyte (ca. 3, Figure 4c), and the g value in 1 M KOH is greater 18 (Figure 7). The higher potential-sensitivity of the narrow resonance in 1 M KOH (Figure 6c) 19 should reflect the greater propensity to form semiquinone radicals (Equation 2). The in situ EPR 20 results directly correlate with the enhanced pseudocapacitive process seen in alkaline electrolyte, 21 thus explaining the enhanced capacitance of oxygen-rich carbon materials in alkaline conditions. 22

ACS Paragon Plus Environment

18

Page 19 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

To conclude, in situ electrochemical EPR spectroscopy has been used to study the capacitive

2 behavior of GO to explore the electron transfer process. The simulation of the spectral lineshape 3 of GO as a function of potential determined that two types of spins exist, each associated with 4 different structures. The narrow signal, which increases during the charging process and 5 reversibly returns when discharged, is related to the generation of more stable semiquinone 6 radicals from the oxidation of hydroquinone at higher pH. The broad component, arising from 7 mobile electrons in extended sp2 graphitic-like structure, shows potential independent behavior 8 in both electrolytes. Comparison between a neutral electrolyte (Na2SO4) and an alkaline 9 electrolyte (KOH) indicated that the increased capacitance in the KOH environment contributes 10 to the pseudo-capacitive behavior of the oxygen functional groups. 11 12 ASSOCIATED CONTENT 13 Supporting Information. 14 Experimental section includes the characterization of the GO, in situ EPR measurement and the 15 temperature dependent measurement, the EPR Lorentzian/Dysonian lineshape simulation. Result 16 section includes the SEM image of the prepared GO membrane, the micrograph of prepared 17 working electrode, the EPR lineshape simulation results and also the g value change results. 18 AUTHOR INFORMATION 19 Notes 20 The authors declare no competing financial interests. 21

ACS Paragon Plus Environment

19

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 27

1 ACKNOWLEDGMENT 2

We thank the U.K. National EPSRC EPR Service and Facility for support, the EPSRC for

3 funding (grant references: EP/K016954/1, EP/I023879/1 and EP/N032888/1) and the ISCF 4 Faraday Challenge Fast Start project on “Degradation of Battery Materials” made available 5 through grant EP/S003053/1. B.W. is grateful for the award of a President’s Doctoral 6 Scholarship from the University of Manchester. We also acknowledge great technical assistance 7 from Mr. Adam Brookfield for the EPR measurements. 8 9 REFERENCES 10

1.

Winter, M.; Brodd, R. J. What Are Batteries, Fuel Cells, and Supercapacitors? Chem. Rev.

11 2004, 104 (10), 4245-4270. 12

2.

Simon, P.; Gogotsi, Y. Materials for Electrochemical Capacitors. Nat. Mater. 2008, 7,

13 845. 14

3.

Conway, B. E. Electrochemical Supercapacitors: Scientific Fundamentals and

15 Technological Applications. Plenum Publisher: New York, 1999. 16

4.

Conway, B. E. Transition from “Supercapacitor” to “Battery” Behavior in

17 Electrochemical Energy Storage. J. Electrochem. Soc. 1991, 138 (6), 1539-1548. 18

5.

Wang, Y.; Song, Y.; Xia, Y. Electrochemical Capacitors: Mechanism, Materials,

19 Systems, Characterization and Applications. Chem. Soc. Rev. 2016, 45 (21), 5925-5950. 20

6.

Zhang, Q.; Uchaker, E.; Candelaria, S. L.; Cao, G. Nanomaterials for Energy Conversion

21 and Storage. Chem. Soc. Rev. 2013, 42 (7), 3127-3171.

ACS Paragon Plus Environment

20

Page 21 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

7.

Lang, X.; Hirata, A.; Fujita, T.; Chen, M., Nanoporous Metal/Oxide Hybrid Electrodes

2 for Electrochemical Supercapacitors. Nature Nanotech. 2011, 6, 232. 3

8.

Yan, J.; Wang, Q.; Wei, T.; Jiang, L.; Zhang, M.; Jing, X.; Fan, Z., Template-Assisted

4 Low Temperature Synthesis of Functionalized Graphene for Ultrahigh Volumetric Performance 5 Supercapacitors. ACS Nano 2014, 8 (5), 4720-4729. 6

9.

Fang, Y.; Luo, B.; Jia, Y.; Li, X.; Wang, B.; Song, Q.; Kang, F.; Zhi, L., Renewing

7 Functionalized Graphene as Electrodes for High-Performance Supercapacitors. Adv. Mater. 8 2012, 24 (47), 6348-6355. 9

10. Frackowiak, E.; Béguin, F., Carbon Materials for the Electrochemical Storage of Energy

10 in Capacitors. Carbon 2001, 39 (6), 937-950. 11

11. Bleda-Martínez, M. J.; Maciá-Agulló, J. A.; Lozano-Castelló, D.; Morallón, E.; Cazorla-

12 Amorós, D.; Linares-Solano, A., Role of Surface Chemistry on Electric Double Layer 13 Capacitance of Carbon Materials. Carbon 2005, 43 (13), 2677-2684. 14

12. Lin, Z.; Liu, Y.; Yao, Y.; Hildreth, O. J.; Li, Z.; Moon, K.; Wong, C. P., Superior

15 Capacitance of Functionalized Graphene. J. Phys. Chem. C 2011, 115 (14), 7120-7125. 16

13. Oh, Y. J.; Yoo, J. J.; Kim, Y. I.; Yoon, J. K.; Yoon, H. N.; Kim, J. H.; Park, S. B.,

17 Oxygen Functional Groups and Electrochemical Capacitive Behavior of Incompletely Reduced 18 Graphene Oxides as a Thin-film Electrode of Supercapacitor. Electrochim. Acta 2014, 116, 11819 128. 20

14. Hsieh, C. T.; Teng, H., Influence of Oxygen Treatment on Electric Double-Layer

21 Capacitance of Activated Carbon Fabrics. Carbon 2002, 40 (5), 667-674.

ACS Paragon Plus Environment

21

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Page 22 of 27

15. Okajima, K.; Ohta, K.; Sudoh, M., Capacitance Behavior of Activated Carbon Fibers

2 with Oxygen-Plasma Treatment. Electrochim. Acta 2005, 50 (11), 2227-2231. 3

16. Chen, C. M.; Zhang, Q.; Zhao, X. C.; Zhang, B.; Kong, Q. Q.; Yang, M. G.; Yang, Q. H.;

4 Wang, M. Z.; Yang, Y. G.; Schlögl, R.; et al., Hierarchically Aminated Graphene Honeycombs 5 for Electrochemical Capacitive Energy Storage. J. Mater. Chem. 2012, 22 (28), 14076-14084. 6

17. Oda, H.; Yamashita, A.; Minoura, S.; Okamoto, M.; Morimoto, T., Modification of the

7 Oxygen-Containing Functional Group on Activated Carbon Fiber in Electrodes of an Electric 8 Double-Layer Capacitor. J. Power Sources 2006, 158 (2), 1510-1516. 9

18. Barisci, J. N.; Wallace, G. G.; Baughman, R. H., Electrochemical Studies of Single-Wall

10 Carbon Nanotubes in Aqueous Solutions. J. Electroanal. Chem. 2000, 488 (2), 92-98. 11

19. Cheng, P. Z.; Teng, H., Electrochemical Responses from Surface Oxides Present on

12 HNO3-treated Carbons. Carbon 2003, 41 (11), 2057-2063. 13

20. Andreas, H. A.; Conway, B. E., Examination of the Double-Layer Capacitance of an

14 High Specific-Area C-Cloth Electrode as Titrated from Acidic to Alkaline pHs. Electrochim. 15 Acta 2006, 51 (28), 6510-6520. 16

21. Centeno, T. A.; Stoeckli, F., The Role of Textural Characteristics and Oxygen-

17 Containing Surface Groups in the Supercapacitor Performances of Activated Carbons. 18 Electrochim. Acta 2006, 52 (2), 560-566. 19

22. Centeno, T. A.; Stoeckli, F., On the Specific Double-Layer Capacitance of Activated

20 Carbons, in Relation to Their Structural and Chemical Properties. J. Power Sources 2006, 154 21 (1), 314-320.

ACS Paragon Plus Environment

22

Page 23 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

23. Kim, H.; Fortunato, M. E.; Xu, H.; Bang, J. H.; Suslick, K. S., Carbon Microspheres as

2 Supercapacitors. J. Phys. Chem. C 2011, 115 (42), 20481-20486. 3

24. Kerisit, S.; Schwenzer, B.; Vijayakumar, M., Effects of Oxygen-Containing Functional

4 Groups on Supercapacitor Performance. J. Phys. Chem. Lett. 2014, 5 (13), 2330-2334. 5

25. Park, S.W.; DeYoung, A. D.; Dhumal, N. R.; Shim, Y.; Kim, H. J.; Jung, Y., Computer

6 Simulation Study of Graphene Oxide Supercapacitors: Charge Screening Mechanism. J. Phys. 7 Chem. Lett. 2016, 7 (7), 1180-1186. 8

26. DeYoung, A. D.; Park, S.W.; Dhumal, N. R.; Shim, Y.; Jung, Y.; Kim, H. J., Graphene

9 Oxide Supercapacitors: A Computer Simulation Study. J. Phys. Chem. C 2014, 118 (32), 1847210 18480. 11

27. Xu, K.; Ji, X.; Chen, C.; Wan, H.; Miao, L.; Jiang, J., Electrochemical Double Layer

12 Near Polar Reduced Graphene Oxide Electrode: Insights from Molecular Dynamic Study. 13 Electrochim. Acta 2015, 166, 142-149. 14

28. Liu, Y.; Yan, D.; Li, Y.; Wu, Z.; Zhuo, R.; Li, S.; Feng, J.; Wang, J.; Yan, P.; Geng, Z.,

15 Manganese Dioxide Nanosheet Arrays Grown on Graphene Oxide as an Advanced Electrode 16 Material for Supercapacitors. Electrochim. Acta 2014, 117, 528-533. 17

29. Jeong, H. K.; Jin, M.; Ra, E. J.; Sheem, K. Y.; Han, G. H.; Arepalli, S.; Lee, Y. H.,

18 Enhanced Electric Double Layer Capacitance of Graphite Oxide Intercalated by Poly(sodium 419 styrensulfonate) with High Cycle Stability. ACS Nano 2010, 4 (2), 1162-1166. 20

30.

Stoller, M. D.; Park, S.; Zhu, Y.; An, J.; Ruoff, R. S., Graphene-Based Ultracapacitors.

21 Nano Lett. 2008, 8 (10), 3498-3502.

ACS Paragon Plus Environment

23

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Page 24 of 27

31. Augustyniak-Jablokow, M. A.; Tadyszak, K.; Strzelczyk, R.; Fedaruk, R.; Carmieli, R.,

2 Slow Spin Relaxation of Paramagnetic Centers in Graphene Oxide. Carbon 2019, 152, 98-105. 3

32. Augustyniak-Jablokow, M. A.; Fedaruk, R.; Strzelczyk, R.; Majchrzycki, L., Identification

4 of a slow relaxing Paramagnetci Center in Graphene Oxide. Appl. Magn. Reson. 2019, 50, 7615 768. 6

33. Wang, B.; Fielding, A. J.; Dryfe, R. A. W., Electron Paramagnetic Resonance

7 Investigation of the Structure of Graphene Oxide: pH-Dependence of the Spectroscopic 8 Response. ACS Appl. Nano Mater. 2019, 2, 19-27. 9

34. Szabó, T.; Berkesi, O.; Forgó, P.; Josepovits, K.; Sanakis, Y.; Petridis, D.; Dékány,

10 I. Evolution of Surface Functional Groups in a Series of Progressively Oxidized Graphite 11 Oxides. Chem. Mater. 2006, 18, 2740– 2749 12

35. Diamantopoulou, Α.; Glenis, S.; Zolnierkiwicz, G.; Guskos, N.; Likodimos, V., Magnetism

13 in Pristine and Chemically Reduced Graphene Oxide. J. App. Phys. 2017, 121 (4), 043906. 14

36. Feng, R.; Zhou, W.; Guan, G.; Li, C.; Zhang, D.; Xiao, Y.; Zheng, L.; Zhu, W. Surface

15 Decoration of Graphene by Grafting Polymerization using Graphene Oxide as the Initiator. J. 16 Mater. Chem. 2012, 22, 3982– 3989. 17

37. Hou, X. L.; Li, J. L.; Drew, S. C.; Tang, B.; Sun, L.; Wang, X. G. Tuning Radical Species

18 in Graphene Oxide in Aqueous Solution by Photoirradiation. J. Phys. Chem. C 2013, 117, 6788– 19 6793.

ACS Paragon Plus Environment

24

Page 25 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

38. Ćirić, L.; Sienkiewicz, A.; Gaál, R.; Jaćimović, J.; Vâju, C.; Magrez, A.; Forró, L. Defects

2 and Localization in Chemically-derived Graphene. Phys. Rev. B: Condens. Matter Mater. 3 Phys. 2012, 86, 195139. 4

39. Komeily Nia, Z. K.; Chen, J. Y.; Tang, B.; Yuan, B.; Wang, X. G.; Li, J. L. Optimizing the

5 Free Radical Content of Graphene Oxide by Controlling its Reduction. Carbon 2017, 116, 703– 6 712. 7

40. Rao, S. S.; Stesmans, A.; Wang, Y.; Chen, Y. Direct ESP Evidence for Magnetic Behavior

8 of Graphite Oxide.Phys. E 2012, 44, 1036– 1039. 9

41. Ćirić, L.; Sienkiewicz, A.; Djokić, D. M.; Smajda, R.; Magrez, A.; Kaspar, T.; Nesper,

10 R.; Forró, L. Size Dependence of the Magnetic Response of Graphite Oxide and Graphene 11 Flakes – an Electron Spin Resonance Study. Phys. Status Solidi B 2010, 247, 2958– 2961. 12

42. Su, C.; Acik, M.; Takai, K.; Lu, J.; Hao, S. J..; Zheng, Y.; Wu, P.; Bao, Q.; Enoki, T.;

13 Chabal, Y. J.; Ping Loh, K., Probing the catalytic activity of porous graphene oxide and the 14 origin of this behaviour. Nat. Commun. 2012, 3, 1298. 15

43. Fujita, N.; Matsumoto, D.; Sakurai, Y.; Kawahara, K.; Ago, H.; Takenobu, T.;

16 Marumoto, K., Direct Observation of Electrically Induced Pauli Paramagnetism in Single-Layer 17 Graphene using ESR Spectroscopy. Sci. Rep. 2016, 6, 34966. 18

44. Hummers, W. S.; Offeman, R. E., Preparation of Graphitic Oxide. J. Am. Chem. Soc. 1958,

19 80(6), 1339-1339.

ACS Paragon Plus Environment

25

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

45.

Page 26 of 27

Rourke, J. P.; Pandey, P. A.; Moore, J. J.; Bates, M.; Kinloch, I. A.; Young, R. J.;

2 Wilson, N. R., The Real Graphene Oxide Revealed: Stripping the Oxidative Debris from the 3 Graphene-like Sheets. Angew. Chem. Int. Ed. 2011, 50(14), 3173-3177. 4

46. Wang, B.; Fielding, A. J.; Dryfe, R. A. W., In situ electrochemical electron paramagnetic

5 resonance spectroscopy as a tool to probe electrical double layer capacitance. Chem. Commun. 6 2018, 54(31), 3827-3830. 7

47. Chechik, V.; Carter, E.; Murphy, D. Electron Paramagnetic Resonance; Oxford University

8 Primers, U.K., 2016. 9

48. Tampieri, F.; Silvestrini, S.; Riccò, R.; Maggini, M.; Barbon, A., A Comparative Electron

10 Paramagnetic Resonance Study of Expanded Graphites and Graphene. J. Mater. Chem. C 2014, 11 2 (38), 8105-8112. 12

49. Enoki, T.; Takai, K., The Edge State of Nanographene and the Magnetism of the Edge-

13 State Spins. Solid State Commun. 2009, 149 (27), 1144-1150. 14

50. Joly, V. L. J.; Takahara, K.; Takai, K.; Sugihara, K.; Enoki, T.; Koshino, M.; Tanaka, H.

15 Effect of Electron Localization on the Edge State Spins in a Disordered Network of 16 Nanographene Sheets. Phys. Rev. B 2010, 81, 115408. 17

51. Guin, P. S.; Das, S.; Mandal P. S., Electrochemical Reduction of Quinones in Different

18 Media: A Review. Int. J. Electrochem. 2011, 816202. 19

52. Augustyniak-Jabłokow Maria, A.; Tadyszak, K.; Maćkowiak, M.; Yablokov Yurii, V.,

20 EPR Evidence of Antiferromagnetic Ordering in Single-Layer Graphene. Phys. Status Solidi 21 RRL 2011, 5 (8), 271-273.

ACS Paragon Plus Environment

26

Page 27 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The Journal of Physical Chemistry

53. Augustyniak-Jabłokow, M. A.; Tadyszak, K.; Maćkowiak, M.; Lijewski, S., ESR Study

2 of Spin Relaxation in Graphene. Chem. Phys. Lett. 2013, 557, 118-122. 3

54. He, H.; Riedl, T.; Lerf, A.; Klinowski, J., Solid-State NMR Studies of the Structure of

4 Graphite Oxide. J. Phys. Chem. 1996, 100 (51), 19954-19958. 5

55. Stathi, P.; Gournis, D.; Deligiannakis, Y.; Rudolf, P., Stabilization of Phenolic Radicals on

6 Graphene Oxide: an XPA and EPR Study. Langmuir 2015, 31 (38), 10508-10516. 7 8