Exploring the Potential of Biocompatible Osmoprotectants as Highly

Nov 21, 2017 - Apart from osmotic injury, ice injury caused by ice formation/growth is the other cause of cellular death during the freeze–thaw cycl...
1 downloads 22 Views 4MB Size
Subscriber access provided by READING UNIV

Article

Exploring the potential of biocompatible osmoprotectants as high efficient cryoprotectants Jing Yang, Chao Pan, Jiamin Zhang, Xiaojie Sui, Yingnan Zhu, Chiyu Wen, and Lei Zhang ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b12189 • Publication Date (Web): 21 Nov 2017 Downloaded from http://pubs.acs.org on November 29, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Exploring the Potential of Biocompatible Osmoprotectants as High Efficient Cryoprotectants Jing Yanga,b,c,1,Chao Pana,b,c,1, Jiamin Zhanga,b,c, Xiaojie Suia,b,c, Yingnan Zhua,b,c, Chiyu Wena,b,c and Lei Zhanga,b,c* 1 a

The first two authors contributed equally to this work. Department of Biochemical Engineering, School of Chemical Engineering and

Technology, Tianjin University, Tianjin 300072, PR China b

Key Laboratory of Systems Bioengineering of the Ministry of Education, Tianjin

University, Tianjin 300072, PR China c

Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin

University, Tianjin, 300072, PR China E-mail: [email protected]

ABSTRACT: Cryoprotectants (CPAs) are critical to successful cryopreservation because they can protect cells from cryoinjuries. Due to the limitations of current CPAs, especially the toxicity, the search for new effective CPAs is attracting increasing attentions. In this work, we reported that natural biocompatible osmoprotectants, which could protect cells from osmotic injury in various biological systems, might also be ideal candidates for CPAs. Three representative biocompatible osmoprotectants (proline, glycine and taurine) were tested and compared. It was found that besides presenting different ability to prevent osmotic injury, these biocompatible osmoprotectants also possessed

different

ability

to

inhibit

ice

formation

and

thus

mitigated

intracellular/extracellular ice injury. Due to the strongest ability to prevent the two types of injuries, we found proline performed the best in cryopreserving five different types of cells. Moreover, the natural osmoprotectants are intrinsically biocompatible to the cells, superior to the current state-of-the-art CPA—dimethyl sulfoxide (DMSO) which is a toxic organic solvent. This work opens a new window of opportunity for DMSO-free cryopreservation, and sheds light on the applications of osmoprotectants in cryoprotection, which may revolutionize the current cryopreservation technologies.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

KEYWORDS: cryopreservation; osmoprotectant; cryoprotectant; ultrarapid; cryoinjury

INTRODUCTION Living cells are key elements of various cell-based applications for modern medical care, such as drug discovery, cell therapy and tissue engineering, etc.1-3 For example, in lymphocytic leukemia treatment, transferred T cells could be transplanted into patients to achieve over 90% overall response rate.4 With the escalating demand of living cells, cell preservation technologies have received increasing attentions to ensure the quality and safety of therapeutic cells, and also can directly influence the therapeutic outcomes. For example, only after overnight storage in suboptimal conditions, peripheral blood stem cells could dramatically decrease their therapeutic efficiency by ~67%.5 Therefore, effective preservation of living cells is critical and holds the huge potential to improve the outcomes of various cell-based applications. Cryopreservation is the most reliable technology for long-term storage of mammalian cells.1 However, during freeze-thaw cycle, cells will suffer from irreversible damage due to osmotic and ice cryoinjuries caused by ice formation.6-8 During the freezing process, extracellular ice formation can induce the water efflux from cells, and thus the cells will be damaged by excessive shrinkage in response to osmotic shock (known as osmotic injury). Meanwhile, intracellular ice formation will cause mechanical damage to cells (known as ice injury) (Figure 1A). Cryoprotectants (CPAs) can help to prevent cells from the cryoinjuries, and thus are highly required for successful cell cryopreservation.8 The current state-of-the-art strategy of cryopreservation is to add large amounts of organic solvents, such as dimethyl sulfoxide (DMSO), as shown in Figure 1B. 9 However, as the most widely-used CPA, DMSO has shown several drawbacks which have restrained its clinical cell-based applications. Firstly, DMSO is an organic solvent with intrinsic toxicity. It has been reported that DMSO was related to the dysfunctions of cellular metabolism and development, impaired enzymatic function, and cell apoptosis.10,11 In addition, DMSO was demonstrated to strongly promote the uncontrolled differentiation of stem cells.12,13 Moreover, in clinical cell transplantation, DMSO was believed to be the causal agent of various adverse reactions to patients, including allergic/neurological

ACS Paragon Plus Environment

Page 2 of 36

Page 3 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

complications and renal/hepatic dysfunctions, etc.14,15 Secondly, to minimize adverse effects caused by DMSO, the time-consuming washing steps are required. Meanwhile, during DMSO removal, the osmotic shock will also lead to cellular damage, because the transmembrane diffusion rate of DMSO is much slower than the transport rate of water through aquaporin.16 Thirdly, stepwise freezing protocol has to be utilized, but it is complex and time-consuming, and requires well-developed equipments.17 Therefore, the alternative to this golden standard CPA is urgently needed. Significant efforts have been made to explore novel and non-toxic CPAs from nature. For example, antifreeze proteins have been found in Antarctic fish which can survive in sub-zero polar oceans.18,19 These proteins can inhibit ice recrystallization and have been reported as novel additives to enhance cell survival in cryopreservation. However, they have shown limited benefits, and are difficult to be isolated from native sources or obtained through biosynthetic pathway. Moreover, they are immunogenic heterologous proteins to human.20-23 Another example is some natural sugars, such as trehalose and sucrose. They can offer biological protection and stabilize the proteins. However, their poor permeability into cell membrane is the primary obstacle to achieve viable cryopreservation. A variety of complex techniques such as genetically engineered pores, biopolymers or microinjection, are essential to deliver sugars into cells to insure intracellular bioprotection for cryopreservation.24-28 It is well known that natural biocompatible osmoprotectants can protect cells in response to osmotic shock. Because under hypertonic environment, cells can rapidly internalize osmoprotectants to counteract the intracellular water outflow, and prevent cells from osmotic injury without disturbing vital cellular functions. It can be expected that they can also help to protect cells from osmotic injury in cryopreservation. Moreover, most osmoprotectants are hydrophilic molecules, we hypothesize that some of them may also possess the ability to interfere ice formation/growth and consequently protect cells from ice injury.29,30 Therefore, we proposed to study the potential of natural biocompatible osmoprotectants as ideal candidates for CPAs in this work. Proline (Pro), glycine (Gly) and taurine (Tau) are three types of representative biocompatible osmoprotectants and naturally exist in mammalian plasma, tissues, muscle and heart

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(Figure 1C-E).31-34 They have been found to maintain the osmotic balance under hypertonic environment in many biological systems. For example, after exposed to high salinity environment (200 mM NaCl), peanut leaves could accumulate 18-fold amount of Pro to prevent them from osmotic injury. Similarly, Gly and Tau have been reported to maintain osmotic balance in mammalian oocytes and heart.34-38 Most interestingly, it has been found that Pro is associated with freezing tolerance in some plants and insects.39-41 For example, after 24 h cold acclimation (-2 °C), the transgenic tobacco plants that could accumulate a large amount of Pro, significantly enhanced survival against freezing stress.42 Moreover, it has been reported that Pro could improve cryopreservation efficacy of some mammalian cells.43-46 Motivated by these findings, in this work we explored the potential of three biocompatible osmoprotectants to serve as CPAs for cryopreservation of mammalian cells. In addition, we utilized them to cryopreserve several cell lines using a time-saving and feasible ultrarapid freezing protocol. Most importantly, we discovered their different ability to prevent two injuries, and subsequently investigated their cryoprotection efficacy.

Figure 1. (A) Schematic drawing of cryoinjuries (osmotic and ice injuries) in the freezing process and the molecular structures of (B) DMSO, (C) Pro, (D) Gly and (E) Tau.

ACS Paragon Plus Environment

Page 4 of 36

Page 5 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Experimental section Materials. Pro, Gly, Tau were all purchased from J&K Scientific Ltd. NaCl was obtained from Alfa Aesar. Roswell Park Memorial Institute-1640 (RPMI-1640), Dulbecco's Modified Eagle's Medium (DMEM), Dulbecco's Modified Eagle Media, Nutrient Mixture F-12 (DMEM/F12) and fetal bovine serum (FBS) were all purchased from Gibco. Penicillin-streptomycin (PS), trypsin-EDTA (0.025%-0.01%), DMSO, and phosphate buffered saline (PBS) were all purchased from Beijing Solarbio Science and Technology Co. Ltd. The culture medium for GLC-82, LTEP-a-2 cells contained RPMI-1640 with 10% FBS and 1% PS. The culture medium for 3T3 cells and smooth muscle cells (SMCs) contained DMEM and DMEM/F12, respectively, with 10% FBS and 1% PS. Milli-Q water (18.2 MΩ·cm-1) was used in all experiments. Cell preparation. Sheep red blood cells (SRBCs) were stored in 4 °C and washed 3 times with PBS before experiment. GLC-82, LTEP-a-2, 3T3 cells and smooth muscle cells (SMCs) were all incubated at 37 °C under an atmosphere of 95% air and 5% CO2. For the experiments, cells were trypsinized with trypsin-EDTA to detach the cells from culture substrates. Cells were collected by centrifugation at 800 rpm for 4 min and suspended in medium, and finally diluted to the desired concentrations for experiments. Cell survival efficiency assays. The cell survival efficiency was evaluated using live/dead staining (Live/Dead viability/cytotoxicity kit, Molecular Probes). Cell suspension from each sample (20 µL) was added to calcein-AM/ethidium homodimer-1 reagent mixture solution (80 µL) in 96-well TCPS plates, respectively. The plates were incubated at room temperature for 30 min away from light, and then observed and analyzed using an inverted microscope (Nikon Eclipse Ti-S). The survival efficiency was calculated by counting the number of live (green) and dead (red) cells in more than 3 duplicate samples. Cell attachment tests. Cell samples were washed with PBS and suspended in culture medium. Then, the cell suspension was added into 24-well TCPS plates. After 12 h (37 °C, 5% CO2), 3 fields were randomly selected under inverted microscope to observe

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

cell attachment efficiency and cell morphology. The cell numbers per square millimeter were calculated by counting the cells in each field. Osmotic regulation tests. GLC-82 cells were exposed for 1 or 3 days (37 °C, 5% CO2) in culture medium containing 0.05 M NaCl, 0.05 M NaCl+0.1 M Pro, 0.05 M NaCl+0.1 M Gly, 0.05 M NaCl+0.1 M Tau, 0.1 M NaCl, 0.1 M NaCl+0.1 M Pro, 0.1 M NaCl+0.1 M Gly and 0.1 M NaCl+0.1 M Tau, respectively. Then cell viability was evaluated with live/dead staining, and cell attachment tests were performed as described above. Differential scanning calorimetry (DSC) tests. DSC assessment of ice formation was performed with Pro/water, Gly/water and Tau/water mixtures. Samples were added to 40 µL aluminium pans and accurately weighted to ±0.01 mg and transferred to a DSC-1 STARe System (Mettler-Toledo, DSC 1/500). Heat flow (W/g) was measured and recorded against an empty pre-weighted 40 µL aluminium reference pan from 10 °C to -40 °C at 10 °C·min-1, followed by from -40 °C to 10 °C at 2 °C·min-1, with the presence of two large endothermic peaks which demonstrated water freezing and ice melting. The depression of water freezing point was detected at the beginning of the frozen mixture solutions melt. The water crystallization temperature (Tf) and freezing enthalpy (△Hfreeze) could be obtained from the first freezing exotherm during cooling, where Tf was determined as the onset temperature (in K), and △Hfreeze was obtained by integration from Tf to the end temperature of the exothermic peak. The following equation was used to calculate the freezing enthalpy of pure water at Tf: △    = −334 − 2.05 − 273 J/g The weight percentage of freezable water to total water content in the sample at Tf was:  =

− △  1 −  △  

where w is the mass concentration of solute. So, the weight percentage of bound water to total water content at Tf was determined with the following equation: 47

ACS Paragon Plus Environment

Page 6 of 36

Page 7 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

 = 1 −  = 1 −

− △  1 −  △  

Ice formation and melt tests. 6% (w/v) of Pro, Gly, Tau and pure water respectively laden in glass tubes were plunged into liquid nitrogen until these samples were completely frozen. Then, theses samples were warmed back in water bath (37 °C). Cell cryopreservation with ultrarapid freezing protocol. Different concentrations of three CPAs (Pro, Gly or Tau) and 10% DMSO in medium containing 10% FBS were prepared. SRBCs (100 µL), 1×106 GLC-82, LTEP-a-2, 3T3 cells and SMCs were added to 1.5 mL CPA solutions in cryovials (Corning, 1.8 mL). Each sample was then directly plunged into liquid nitrogen immediately. The cooling rates were tested by a thermocouple thermometer. For recovery, cells were immediately thawed in 37 °C water bath, then the cell survival efficiency and cell attachment were tested as described above. Measurement of SRBC integrity rates. 100 µL of the prepared SRBCs suspension was respectively added into 1.5 mL PBS (0% hemolysis, 100% integrity rate) as positive control and H2O (100% hemolysis, 0% integrity rate) as negative control samples. Post-thaw SRBCs samples and control samples were centrifugated at 2000 rpm for 10 min, and the absorbance of supernatant in each post-thaw sample (A), positive control (A1) and negative control (A0) were measured at 450 nm by multiscan spectrum (Tecan, Infinite M200 PRO). Each SRBC integrity rate (cell recovery) was calculated in 3 duplicate samples by subtracting the hemolysis rate from 100% with the equation: ) − )* Cell integrity rate = 100% − ( + × 100% ) − )* Cell proliferation tests. Post-thaw GLC-82 cells using three osmoprotectants and fresh cells were cultured in 12-well TCPS plates. The cell number on the substrates was counted daily for 1 to 4 days using microscopy. Cytotoxicity evaluation. GLC-82 cells were exposed in the medium containing 2% of Pro, Gly, Tau or DMSO at 37 °C under an atmosphere of 95% air and 5% CO2 for 1 to 5 days. After 1, 3 or 5 days, cell viability and morphology were tested.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Data analysis. All statistics and calculations for cell survival rates were determined using Microsoft Excel 2016 for Mac. Significance determination used a two-tailed homoscedastic Student’s t-test with a 95% confidence interval.

Results and discussion The ability to protect cells from osmotic injury In cryopreservation, extracellular ice formation/growth and CPA introduction/removal can induce osmotic injury to cells, which is one of the major causes of cellular damage.6-8 Osmoprotectants can prevent cells from osmotic injury, because they can be taken up or released by cells to counter the water flow under osmotic shock. Moreover, the biocompatible osmoprotectants can achieve high intracellular concentrations without disturbing cellular functions, because they can form a monolayer of water around the proteins and maintain their stabilization.30, 48 In this work, we chose three representative biocompatible osmoprotectants--Pro, Gly and Tau to investigate their ability to protect cells from osmotic injury. As shown in Figure 2A, GLC-82 cells were exposed in hypertonic environment formed by dissolving 0.05 M and 0.1 M NaCl in culture medium at 37 °C for 1 and 3 days. The culture medium was isotonic to physiological saline (0.154 M), so the osmotic pressure of these two samples was increased by ~32% or ~65% compared with isotonic environment. Due to the fatal osmotic injury to cells, their viability was only ~57% or ~4% after 3-day exposure (Figure 2B and C). Interestingly, three osmoprotectants that were respectively added into 0.05 M of NaCl medium could all significantly enhance cell survival, but the protection efficacy of Tau was the lowest (Figure 2B and C). Moreover, when cells were exposed in a higher hypertonic medium (0.1 M NaCl), Pro and Gly could both improve cell viability by 31% after 1-day exposure (35% and 22% after 3-day exposure), indicating their similar ability to prevent osmotic injury. While adding Tau into this hypertonic medium, cell viability was even lower than control sample, suggesting that the osmotic protection of Tau was limited. Meanwhile, the survived cells in Pro, Gly and Tau samples could attach to substrates with normal morphology, as shown in Figure 2D, revealing that the functionalities of living cells were also not affected. These results

ACS Paragon Plus Environment

Page 8 of 36

Page 9 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

showed the ability of three osmoprotectants to protect cells from osmotic injury under hypertonic environment (Tau performed worst).

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 2. The ability to prevent osmotic injury: (A) Schematic diagram of the tests of the ability to

ACS Paragon Plus Environment

Page 10 of 36

Page 11 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

protect cells from osmotic injury. (B) Fluorescence images of the live/dead assay and (D) cell attachment of GLC-82 cells after exposed in medium, medium containing 0.05 M NaCl, 0.05 M NaCl+0.1 M Pro, 0.05 M NaCl+0.1 M Gly, 0.05 M NaCl+0.1 M Tau, 0.1 M NaCl, 0.1 M NaCl+0.1 M Pro, 0.1 M NaCl+0.1 M Gly, 0.1 M NaCl+0.1 M Tau for 3 days. Green: live cells. Red: dead cells. Scale bar=100 µm. (C) The cell viability after exposed in medium (gray), 0.05 M NaCl (orange), 0.05 M NaCl+0.1 M Pro (red), 0.05 M NaCl+0.1 M Gly (blue), 0.05 M NaCl+0.1 M Tau (green), 0.1 M NaCl (orange with bias), 0.1 M NaCl+0.1 M Pro (red with bias), 0.1 M NaCl+0.1 M Gly (blue with bias), 0.1 M NaCl+0.1 M Tau (green with bias) for 1 and 3 days. Value = mean ± standard deviation, n≥3. * P < 0.05; ** P < 0.01; *** P < 0.001.

The ability to protect cells from ice injury Apart from osmotic injury, ice injury caused by ice formation/growth is the other cause of cellular death during freeze-thaw cycle.6-8 As is well known, ice formation highly depends on the infinite hydrogen-bond between water molecules, and its subsequent growth will accompany with the aggregation of water molecules and the development of hydrogen-bond network. Therefore, CPAs are commonly hydrophilic molecules, which can form bound-water to break the strong hydrogen-bond between water molecules and prevent them from attending ice crystals. Thus, they can inhibit ice formation/growth to protect cells from cryoinjuries.49,50 In this work, to investigate the ability of three osmoprotectants to prevent ice injury, we investigated their ability to inhibit water crystallization, depress water freezing point, and bound water molecules (Figure 3A-E). In Figure 3A-C, all samples showed an endothermic peak due to the melt of solute-water system. The minimum peak temperatures in Pro and Gly samples were both inversely proportional to the solute concentrations, while in Tau samples, the temperatures showed no obvious difference among the increasing concentrations, suggesting that Tau could not significantly inhibit water crystallization. Meanwhile, Pro-water system revealed smaller melting peak than Gly-water system at comparable concentrations, indicating its stronger inhibition to water crystallization. Figure 3D presented that Pro and Gly could both depress water freezing point, and Pro performed better. However, Tau could not obviously influence water freezing point and it showed inferior water-solubility. Figure 3E showed the ratio of

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

bound water in three systems based on their freezing thermograms (Figure S1), suggesting their different ability to bound water molecules (Pro>Gly>Tau). Moreover, to further explore their effects on water behaviors, we tested ice formation and melt in Pro, Gly and Tau solutions (6%). At 79 s after the freezing process started, large ice crystals could be observed in the pure water sample, but not in the three osmoprotectant samples, probably indicating their ability to inhibit ice formation and excessive ice growth (Figure 3F, Movie S1). During the thawing process, as expected, ice recrystallization (ice crystals grew larger) occurred in the pure water sample. Interestingly, the three osmoprotectant samples performed different appearance. At 27 s after the thawing process started, taurine sample presented even larger ice crystals than the pure water sample (Figure 3G, Movie S1); while ice seemed to melt faster in Pro and Gly samples. These phenomena revealed that the osmoprotectants Pro and Gly could both inhibit ice formation/growth and thus preventing cells from ice injury (Pro>Gly). However, Tau showed no obvious inhibition on ice formation, probably even promoted ice recrystallization, and thus it could induce the promotion of ice injury.

ACS Paragon Plus Environment

Page 12 of 36

Page 13 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 3. The ability to prevent ice injury: Differential scanning calorimetry (DSC) melting thermograms of 0 M (dark blue), 0.1 M (red), 0.3 M (green), 0.5 M (purple), 1 M (light blue), and 1.5 M (orange) of (A) Pro, (B) Gly and (C) Tau solutions. (D) The depression of water freezing point and (E) the ratio of bound water in three systems. Photo images caught at 79 s after the freezing process started (F) and 27 s after the thawing process started (G) in three systems and pure water.

Post-thaw cell survival with ultrarapid freezing protocol After the tests of their ability to protect cells from two injuries, we further verified the efficiency of three osmoprotectants serving as CPAs to cryopreserve different cell lines. Firstly, the anuclear SRBCs were evaluated, as shown in Figure 4. Compared with the

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

complete hemolysis in control sample, the post-thaw intact SRBC rates were much higher at optimum concentrations in Pro, Gly and Tau samples (72.0%, 59.0% and 51.6%), as shown in Figure 4B. Moreover, the efficiency of Pro was significantly higher than 10% of DMSO (commonly used concentration), indicating its potential to serve as a promising alternative to current cytotoxic CPA. It was noticed that SRBCs were in the absence of most organelles and cell nucleus. Therefore, in SRBCs cryopreservation, osmotic injury induced by extracellular ice formation could be considered as the primary source of cell cryoinjury.51,52 So as expected, three osmoprotectants could achieve exceptional SRBCs cryoprotection efficacy.

Figure 4. Post-thaw intact SRBCs with ultrarapid freezing protocol: (A) Photos of post-thaw SRBCs using three osmoprotectants (Pro, Gly and Tau) at optimum concentration compared with control samples. (B) Post-thaw intact SRBC rates using three osmoprotectants (Pro, Gly and Tau) at optimum concentration compared with control samples. ND: not detected. Value= mean ± standard deviation, n≥3. * P < 0.05; *** P < 0.001.

However, the anuclear SRBCs could not proliferate, so any toxic effects would be less pronounced. Therefore, secondly we evaluated different nucleated and immortalized cell lines (GLC-82 cells, LTEP-a-2 cells, 3T3 cells, SMCs), as shown in Figure 5 and 6. The bell-shaped relationship between osmoprotectant concentrations and post-thaw cell

ACS Paragon Plus Environment

Page 14 of 36

Page 15 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

survival efficiency could be observed, and the optimum concentrations of Pro, Gly and Tau were 6-8%, 2-4%, 4-6%, respectively (Figure 6). In addition, their optimum efficiency was significantly higher than blank control samples, and interestingly, the efficiency also decreased as this order: Pro>Gly>Tau. It indicated that three osmoprotectants could all offer cryoprotection to nucleated cell lines, and the efficiency was highly associated with their ability to prevent osmotic and ice injuries. Notably, ultrarapid freezing protocol for cryopreservation was utilized in this work. This protocol was achieved by directly immersing samples into liquid nitrogen (the cooling rate could reach ~180 °C/min as shown in Figure S2), which is time-saving and cost-effective. However, current CPAs often do not work at such high cooling rates, possibly due to the lack of time for cell dehydration or CPA permeation into cell membranes for intracellular protection.9, 53 Herein, with ultrarapid freezing protocol, three osmoprotectants (especially Pro) performed well in cryopreservation of five cell types (efficiency of Pro could achieve ~80%), suggesting that they could promptly enter cells to protect intracellular ice injury and balance cellular osmotic stress.

Figure 5. Fluorescence images of the live/dead assay of GLC-82 cells (first row), LTEP-a-2 cells (second row), 3T3 cells (third row) and SMCs (fourth row) respectively cryopreserved with three osmoprotectants at optimum concentrations (Pro: 6% and 8%; Gly: 2% and 4%; Tau: 4% and 6%), DMSO (10%) and control culture medium as well as fresh cells with ultrarapid freezing protocol. Green: live cells. Red: dead cells. Scale bar=100 µm.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 6. Post-thaw survival efficiency of (A) GLC-82 cells, (B) LTEP-a-2 cells, (C) 3T3 cells and (D) SMCs evaluated at fresh cells (light blue) and different concentrations of Pro (red), Gly (dark blue), Tau (green) compared with that of 10% DMSO (orange) and control sample (gray). ND: not detected. Value= mean ± standard deviation, n≥3. * P < 0.05; ** P < 0.01; *** P < 0.001.

The functionalities of recovered cells Apart from the cell viability, cryoinjuries may impair the cellular enzyme or mitochondrial function, further influence cell behaviors including attachment and proliferation. Therefore, after cryopreservation using three osmoprotectants, we recovered the post-thaw survival cells to evaluate their attachment or proliferation, as presented in Figure 7. It was found that the recovered cells could not only attach to the substrates, but maintain membrane integrity and cellular morphology similar with the fresh cells (Figure 7A). As expected, the numbers of attached cells also decreased as this

ACS Paragon Plus Environment

Page 16 of 36

Page 17 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

order: Pro>Gly>Tau (Figure 7B). Moreover, the growth curves of recovered cells in three samples almost overlapped that of the fresh cells, indicating these cells maintained their normal ability of proliferation (Figure 7C). Therefore, these phenomena demonstrated that after cryopreservation using Pro, Gly and Tau, the functionalities of recovered cells were not affected.

Figure 7. The functionalities of recovered cells: (A) The cell morphology and (B) cell attachment numbers per square millimeter of LTEP-a-2 cells (upper row) and 3T3 cells (lower row) respectively after cryopreservation with Pro, Gly and Tau in optimum concentrations compared with fresh cells. Scale bar=100 µm. (C) The proliferation curves of recovered GLC-82 cells after cryopreservation with Pro, Gly and Tau compared with fresh cells. Value= mean ± standard deviation, n≥3.

Cytotoxicity evaluation The toxicity of current state-of-the-art CPA—DMSO remains as the bottleneck of its widespread use in clinical cell-based applications. It has been reported that the toxic effects would induce cellular dysfunctions, including cell membrane damage,

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

intracellular Ca2+ upregulation and nitric oxide production, etc.54,55 Therefore, it has significant meaning to evaluate the toxicity of novel CPAs. In this work, Pro, Gly and Tau are all biocompatible osmoprotectants naturally found in various biological systems.32, 56-58 Therefore, to verify their non-toxicity, GLC-82 cells were exposed in medium containing 2% of Pro, Gly, and Tau compared with 2% of DMSO. As shown in Figure 8A and B, after 3-day and 5-day exposure, cell viability in three osmoprotectant samples was same as the control sample, and cells could attach to substrates and assume normal morphology with the spindle shape. In contrast, large numbers of cells were floating in DMSO sample, and when attached to substrates, the survived cells exhibited abnormal morphology compared with the control sample. These results demonstrated the non-toxicity of three natural osmoprotectants, highly superior to current state-of-the-art CPA.

Figure 8. Cytotoxicity evaluation: (A) Cell viability and (B) attachment of GLC-82 cells after exposed in medium containing 2% of Pro, Gly, Tau and DMSO for 3 days (upper row) and 5 days (lower row), and pure medium as control. Scale bar=100 µm. Value= mean ± standard deviation, n≥3. *** P < 0.001.

Proposed mechanism Based on the above results, a mechanism could be proposed (Figure 9).

ACS Paragon Plus Environment

Page 18 of 36

Page 19 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Firstly, the osmoprotectant (Pro, Gly or Tau) was added to form a hypertonic environment for cells. Subsequently, via specific transport systems, they could be taken up by cells due to higher extracellular osmotic stress in order to prevent osmotic injury. Meanwhile, it also could ensure the intracellular bioprotection from cryoinjuries in the following freezing process. Generally, these transporters could individually translocate their substrates across the plasma membrane using ion gradient as driving force. Notably, many transporters (such as PAT1, or transport system A) prefer neutral amino acid (such as Pro and Gly) instead of acidic amino acid (Tau), which may be the major reason for the better ability of Pro and Gly to protect cells from osmotic injury. 48, 59-61 Secondly, during the freezing process, osmoprotectants could maintain the osmotic balance avoiding osmotic injury to cells. More importantly, they possessed different ability to prevent ice formation/growth, due to their different ability to bound water molecules (Pro>Gly>Tau). In addition, ultrarapid freezing protocol also could prevent extensive ice growth to protect cells from further ice injury, compared with the conventional controlled-rate freezing protocol using DMSO. Thirdly, when the vitrification (a “glassy state”) of solution occurred at a certain low temperature, the cryoinjuries would be avoided, and the survived cells could remain intact for a very long time in liquid nitrogen (-196 °C). Finally, during the thawing process, Pro and Gly could probably inhibit ice recrystallization, which could further promote the cryoinjuries to cells. On the contrary, the Tau sample might cause more serious recrystallization than pure water sample, which also resulted in its worst cryoprotection efficacy.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 9. A proposed mechanism. The role of (A) Pro, (B) Gly and (C) Tau to protect cells from the cryoinjuries (osmotic and ice injuries) during freeze-thaw cycle in cryopreservation.

Conclusions In summary, basing on the cryoinjury mechanisms, we hypothesized that natural osmoprotectants might also hold great potential as promising CPAs. Therefore, in this work we presented the strategy which could compare the abilities of natural

ACS Paragon Plus Environment

Page 20 of 36

Page 21 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

osmoprotectants to prevent osmotic injury and ice injury and predict their potential as CPAs. Three natural osmoprotectants were studied using this strategy. It was found that Pro possessed the highest ability of osmoregulation to prevent osmotic injury, and the highest ability of inhibition water crystallization to prevent ice injury. As expected, it also performed the best in cryopreservation of five different types of cells. This work offered a new avenue for the search of high efficient and biocompatible CPAs, which might revolutionize current cryopreservation reagents and methods.

Supporting Information. Differential scanning calorimetry (DSC) freezing thermograms of three osmoprotectants and cooling rates of ultrarapid freezing process. Movie of ice formation and melt tests.

Author Information Corresponding Author *E-mail: [email protected] ORCID Lei Zhang: 0000-0003-3638-6219 Notes: The authors declare no competing financial interest.

Acknowledgements The authors acknowledge the financial support from the National Natural Science Funds for Excellent Young Scholars 21422605, National Natural Science Funds for Innovation

Research

Groups

21621004,

Tianjin

Natural

Science

Foundation,

14JCYB-JC41600, Research Fund for the Doctoral Program of Higher Education of China 20130032120089, Program for New Century Excellent Talents in University NCET-13-0417.

References (1) Marquez-Curtis, L. A.; Janowska-Wieczorek, A.; McGann, L. E.; Elliott, J. A. W. Mesenchymal Stromal Cells Derived from Various Tissues: Biological, Clinical and Cryopreservation Aspects. Cryobiology 2015, 71, 181-197.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(2) Yang, J.; Zhu, Y.; Xu, T.; Pan, C.; Cai, N.; Huang, H.; Zhang, L. The Preservation of Living Cells with Biocompatible Microparticles. Nanotechnology 2016, 27: 265101. (3) Yang, J.; Pan, C.; Sui, X.; Cai, N.; Zhang, J.; Zhu, Y.; Zhang, L. The Hypothermic Preservation of Mammalian Cells with Assembling Extracellular-Matrix-Mimetic Microparticles. J. Mater. Chem. B 2017, 5, 1535-1541. (4) Rosenberg, S. A.; Restifo, N. P. Adoptive Cell Transfer as Personalized Immunotherapy for Human Cancer. Science 2015, 348, 62-68. (5) Seo, J. Y.; Huh, H. J.; Park, H. K.; Choung, H. K.; Kim, D. W.; Koo, H. H.; Sung, K. W.; Kang, E. S. Evaluation of Overnight Storage Conditions for Autologous Peripheral Blood Stem Cell Products: Comparison of Three Different Conditions. Vox Sang. 2012, 103, 150-158. (6) Mazur, P. Freezing of Living Cells: Mechanisms and Implications. Am. J. Phys. 1984, 247, C125-142. (7) Mazur, P.; Leibo, S. P.; Chu, E. H. A Two-Factor Hypothesis of Freezing Injury. Evidence from Chinese Hamster Tissue-Culture Cells. Exp. Cell Res. 1972, 71, 345-355. (8) Yang, J.; Cai, N.; Zhai, H.; Zhang, J.; Zhu, Y.; Zhang, L. Natural Zwitterionic Betaine Enables Cells to Survive Ultrarapid Cryopreservation. Sci. Rep. 2016, 6: 37458. (9) Deller, R. C.; Pessin, J. E.; Vatish, M.; Mitchell, D. A.; Gibson, M. I. Enhanced Non-Vitreous Cryopreservation of Immortalized and Primary Cells by Ice-Growth Inhibiting Polymers. Biomater. Sci. 2016, 4, 1079-1084. (10) Aita, K.; Irie, H.; Tanuma, Y.; Toida, S.; Okuma, Y.; Mori, S.; Shiga, J. Apoptosis in Murine Lymphoid Organs Following Intraperitoneal Administration of Dimethyl Sulfoxide (DMSO). Exp. Mol. Pathol. 2005, 79, 265-271. (11) Liu, J.; Yoshikawa, H.; Nakajima, Y.; Tasaka, K. Involvement of Mitochondrial Permeability Transition and Caspase-9 Activation in Dimethyl Sulfoxide-Induced Apoptosis of El-4 Lymphoma Cells. Int. Immunopharmacol. 2001, 1, 63-74. (12) Ji, L.; de Pablo, J. J.; Palecek, S. P. Cryopreservation of Adherent Human Embryonic Stem Cells. Biotechnol. Bioeng. 2004, 88, 299-312. (13) Marks, P. A.; Breslow, R. Dimethyl Sulfoxide to Vorinostat: Development of This Histone Deacetylase Inhibitor as an Anticancer Drug. Nat. Biotechnol. 2007, 25, 84-90. (14) Pal, R.; Mamidi, M. K.; Das, A. K.; Bhonde, R. Diverse Effects of Dimethyl Sulfoxide (DMSO) on the Differentiation Potential of Human Embryonic Stem Cells. Arch. Toxicol. 2012, 86, 651-661. (15) Shu, Z.; Heimfeld, S.; Gao, D. Hematopoietic Sct with Cryopreserved Grafts: Adverse Reactions after Transplantation and Cryoprotectant Removal before Infusion. Bone Marrow Transplant. 2014, 49, 469-476. (16) Buchanan, S. S.; Gross, S. A.; Acker, J. P.; Toner, M.; Carpenter, J. F.; Pyatt, D. W. Cryopreservation of Stem Cells Using Trehalose: Evaluation of the Method Using a Human Hematopoietic Cell Line. Stem Cells Dev. 2004, 13, 295-305. (17) Katkov, I. I.; Kim, M. S.; Bajpai, R.; Altman, Y. S.; Mercola, M.; Loring, J. F.; Terskikh, A. V.; Snyder, E. Y.; Levine, F. Cryopreservation by Slow Cooling with DMSO Diminished Production of Oct-4 Pluripotency Marker in Human Embryonic Stem Cells. Cryobiology 2006, 53, 194-205. (18) DeVries, A. L. Glycoproteins as Biological Antifreeze Agents in Antarctic Fishes. Science 1971, 172, 1152-1155. (19) Capicciotti, C. J.; Poisson, J. S.; Boddy, C. N.; Ben, R. N. Modulation of Antifreeze

ACS Paragon Plus Environment

Page 22 of 36

Page 23 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Activity and the Effect Upon Post-Thaw Hepg2 Cell Viability after Cryopreservation. Cryobiology 2015, 70, 79-89. (20) Deller, R. C.; Vatish, M.; Mitchell, D. A.; Gibson, M. I. Glycerol-Free Cryopreservation of Red Blood Cells Enabled by Ice-Recrystallization-Inhibiting Polymers. ACS Biomater. Sci. Eng. 2015, 1, 789-794. (21) Deller, R. C.; Vatish, M.; Mitchell, D. A.; Gibson, M. I. Synthetic Polymers Enable Non-Vitreous Cellular Cryopreservation by Reducing Ice Crystal Growth During Thawing. Nat. Commun. 2014, 5: 3244. (22) Wang, T.; Zhu, Q.; Yang, X.; Layne, J. R., Jr.; Devries, A. L. Antifreeze Glycoproteins from Antarctic Notothenioid Fishes Fail to Protect the Rat Cardiac Explant During Hypothermic and Freezing Preservation. Cryobiology 1994, 31, 185-192. (23) Koshimoto, C.; Mazur, P. Effects of Warming Rate, Temperature, and Antifreeze Proteins on the Survival of Mouse Spermatozoa Frozen at an Optimal Rate. Cryobiology 2002, 45, 49-59. (24) Eroglu, A.; Russo, M. J.; Bieganski, R.; Fowler, A.; Cheley, S.; Bayley, H.; Toner, M. Intracellular Trehalose Improves the Survival of Cryopreserved Mammalian Cells. Nat. Biotechnol. 2000, 18, 163-167. (25) Russo, M. J.; Bayley, H.; Toner, M. Reversible Permeabilization of Plasma Membranes with an Engineered Switchable Pore. Nat. Biotechnol. 1997, 15, 278-282. (26) Eroglu, A.; Toner, M.; Toth, T. L. Beneficial Effect of Microinjected Trehalose on the Cryosurvival of Human Oocytes. Fertil. Steril. 2002, 77, 152-158. (27) Lynch, A. L.; Chen, R.; Dominowski, P. J.; Shalaev, E. Y.; Yancey, R. J., Jr.; Slater, N. K. H. Biopolymer Mediated Trehalose Uptake for Enhanced Erythrocyte Cryosurvival. Biomaterials 2010, 31, 6096-6103. (28) Lynch, A. L.; Chen, R.; Slater, N. K. H. Ph-Responsive Polymers for Trehalose Loading and Desiccation Protection of Human Red Blood Cells. Biomaterials 2011, 32, 4443-4449. (29) Yancey, P. H. Organic Osmolytes as Compatible, Metabolic and Counteracting Cytoprotectants in High Osmolarity and Other Stresses. J. Exp. Biol. 2005, 208, 2819-2830. (30) Kempf, B.; Bremer, E. Uptake and Synthesis of Compatible Solutes as Microbial Stress Responses to High-Osmolality Environments. Arch. Microbiol. 1998, 170, 319-330. (31) Wyse, A. T. S.; Netto, C. A. Behavioral and Neurochemical Effects of Proline. Metab. Brain Dis. 2011, 26, 159-172. (32) Wu, G.; Bazer, F. W.; Burghardt, R. C.; Johnson, G. A.; Kim, S. W.; Knabe, D. A.; Li, P.; Li, X.; McKnight, J. R.; Satterfield, M. C.; Spencer, T. E. Proline and Hydroxyproline Metabolism: Implications for Animal and Human Nutrition. Amino Acids 2011, 40, 1053-1063. (33) Wang, W.; Wu, Z.; Dai, Z.; Yang, Y.; Wang, J.; Wu, G. Glycine Metabolism in Animals and Humans: Implications for Nutrition and Health. Amino Acids 2013, 45, 463-477. (34) Schaffer, S. W.; Jong, C. J.; Ramila, K. C.; Azuma, J. Physiological Roles of Taurine in Heart and Muscle. J. Biomed. Sci. 2010, 17 Suppl 1: S2. (35) Pogorelova, M. A.; Golichenkov, V. A.; Pogorelova, V. N.; Panait, A. I.; Smirnov, A. A.; Pogorelov, A. G. Amino Acid Correction of Regulatory Volume Decrease Evoked by

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Hypotonic Stress in Mouse Oocytes in Vitro. Bull. Exp. Biol. Med. 2015, 159, 35-37. (36) Baltz, J. M.; Tartia, A. P. Cell Volume Regulation in Oocytes and Early Embryos: Connecting Physiology to Successful Culture Media. Hum. Reprod. Update 2010, 16, 166-176. (37) Sobahan, M. A.; Akter, N.; Ohno, M.; Okuma, E.; Hirai, Y.; Mori, I. C.; Nakamura, Y.; Murata, Y. Effects of Exogenous Proline and Glycinebetaine on the Salt Tolerance of Rice Cultivars. Biosci. Biotechnol. Biochem. 2012, 76, 1568-1570. (38) Hossain, M. A.; Ashrafuzzaman, M.; Ismail, M. R. Salinity Triggers Proline Synthesis in Peanut Leaves. Maejo Int. J. Sci. Technol. 2011, 5, 159-168. (39) Xiang, Y.; Huang, Y.; Xiong, L. Characterization of Stress-Responsive Cipk Genes in Rice for Stress Tolerance Improvement. Plant Physiol. 2007, 144, 1416-1428. (40) Misener, S. R.; Chen, C. P.; Walker, V. K. Cold Tolerance and Proline Metabolic Gene Expression in Drosophila Melanogaster. J. Insect Physiol. 2001, 47, 393-400. (41) Ershadi, A.; Karimi, R.; Mahdei, K. N. Freezing Tolerance and Its Relationship with Soluble Carbohydrates, Proline and Water Content in 12 Grapevine Cultivars. Acta Physiol. Plant. 2016, 38, 1-10. (42) Parvanova, D.; Popova, A.; Zaharieva, I.; Lambrev, P.; Konstantinova, T.; Taneva, S.; Atanassov, A.; Goltsev, V.; Djilianov, D. Low Temperature Tolerance of Tobacco Plants Transformed to Accumulate Proline, Fructans, or Glycine Betaine. Variable Chlorophyll Fluorescence Evidence. Photosynthetica 2004, 42, 179-185. (43) Grein, T. A.; Freimark, D.; Weber, C.; Hudel, K.; Wallrapp, C.; Czermak, P. Alternatives to Dimethylsulfoxide for Serum-Free Cryopreservation of Human Mesenchymal Stem Cells. Int. J. Artif. Organs 2010, 33, 370-380. (44) Sun, H.; Glasmacher, B.; Hofmann, N. Compatible Solutes Improve Cryopreservation of Human Endothelial Cells. Cryoletters 2012, 33, 485-493. (45) Li, Y. H.; Si, W.; Zhang, X. Z.; Dinnyes, A.; Ji, W. Z. Effect of Amino Acids on Cryopreservation of Cynomolgus Monkey (Macaca Fascicularis) Sperm. Am. J. Primatol. 2003, 59, 159-165. (46) Zhang, L.; Xue, X.; Yan, J.; Yan, L.-Y.; Jin, X.-H.; Zhu, X.-H.; He, Z.-Z.; Liu, J.; Li, R.; Qiao, J. L-Proline: A Highly Effective Cryoprotectant for Mouse Oocyte Vitrification. Sci. Rep. 2016, 6: 26326. (47) Rasmussen, P. H.; Jorgensen, B.; Nielsen, J. Aqueous Solutions of Proline and Nacl Studied by Differential Scanning Calorimetry at Subzero Temperatures. Thermochim. Acta 1997, 303, 23-30. (48) Wehner, F.; Olsen, H.; Tinel, H.; Kinne-Saffran, E.; Kinne, R. K. H. Cell Volume Regulation: Osmolytes, Osmolyte Transport, and Signal Transduction. Rev. Physiol. Biochem. Pharmacol. 2003, 148, 1-80. (49) Macfarlane, D. R.; Forsyth, M. Recent Insights on the Role of Cryoprotective Agents in Vitrification. Cryobiology 1990, 27, 345-358. (50) Sei, T.; Gonda, T.; Arima, Y. Growth Rate and Morphology of Ice Crystals Growing in a Solution of Trehalose and Water. J. Cryst. Growth 2002, 240, 218-229. (51) Scott, K. L.; Lecak, J.; Acker, J. P. Biopreservation of Red Blood Cells: Past, Present, and Future. Transfus. Med. Rev. 2005, 19, 127-142. (52) Fowler, A. J.; Toner, M. In Biotransport: Heat and Mass Transfer in Living Systems; Diller, K. R., Ed.; 1998; pp 245-252. (53) Meryman, H. T. Cryopreservation of Living Cells: Principles and Practice.

ACS Paragon Plus Environment

Page 24 of 36

Page 25 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Transfusion 2007, 47, 935-945. (54) Nygren, P.; Larsson, R.; Rastad, J.; Akerstrom, G.; Gylfe, E. Dimethyl Sulfoxide Increases Cytoplasmic Ca2+ Concentration and Inhibits Parathyroid Hormone Release in Normal Bovine and Pathological Human Parathyroid Cells. Biochim. Biophys. Acta 1987, 928, 194-198. (55) Trubiani, O.; Salvolini, E.; Staffolani, R.; Di Primio, R.; Mazzanti, L. DMSO Modifies Structural and Functional Properties of Rpmi-8402 Cells by Promoting Programmed Cell Death. Int. J. Immunopathol. Pharmacol. 2003, 16, 253-259. (56) Melendez-Hevia, E.; de Paz-Lugo, P.; Cornish-Bowden, A.; Cardenas, M. L. A Weak Link in Metabolism: The Metabolic Capacity for Glycine Biosynthesis Does Not Satisfy the Need for Collagen Synthesis. J. Biosci. 2009, 34, 853-872. (57) de la Puerta, C.; Arrieta, F. J.; Balsa, J. A.; Botella-Carretero, J. I.; Zamarron, I.; Vazquez, C. Taurine and Glucose Metabolism: A Review. Nutr. Hosp. 2010, 25, 910-919. (58) Lambert, I. H.; Kristensen, D. M.; Holm, J. B.; Mortensen, O. H. Physiological Role of Taurine - from Organism to Organelle. Acta Physiol. 2015, 213, 191-212. (59) Brandsch, M. Transport of L-Proline, L-Proline-Containing Peptides and Related Drugs at Mammalian Epithelial Cell Membranes. Amino Acids 2006, 31, 119-136. (60) Tunnicliff, G. Membrane Glycine Transport Proteins. J. Biomed. Sci. 2003, 10, 30-36. (61) Kubo, Y.; Akanuma, S.-i.; Hosoya, K.-i. Impact of Slc6a Transporters in Physiological Taurine Transport at the Blood-Retinal Barrier and in the Liver. Biol. Pharm. Bull. 2016, 39, 1903-1911.

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Table of Contents/Abstract Graphics:

ACS Paragon Plus Environment

Page 26 of 36

Page 27 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 1. (A) Schematic drawing of cryoinjuries (osmotic and ice injuries) in the freezing process and the molecular structures of (B) DMSO, (C) Pro, (D) Gly and (E) Tau. 82x70mm (299 x 299 DPI)

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 2. The ability to prevent osmotic injury: (A) Schematic diagram of the tests of the ability to protect cells from osmotic injury. (B) Fluorescence images of the live/dead assay and (D) cell attachment of GLC-82 cells after exposed in medium, medium containing 0.05 M NaCl, 0.05 M NaCl+0.1 M Pro, 0.05 M NaCl+0.1 M Gly, 0.05 M NaCl+0.1 M Tau, 0.1 M NaCl, 0.1 M NaCl+0.1 M Pro, 0.1 M NaCl+0.1 M Gly, 0.1 M NaCl+0.1 M Tau for 3 days. Green: live cells. Red: dead cells. Scale bar=100 µm. (C) The cell viability after exposed in medium (gray), 0.05 M NaCl (orange), 0.05 M NaCl+0.1 M Pro (red), 0.05 M NaCl+0.1 M Gly (blue), 0.05 M NaCl+0.1 M Tau (green), 0.1 M NaCl (orange with bias), 0.1 M NaCl+0.1 M Pro (red with bias), 0.1 M NaCl+0.1 M Gly (blue with bias), 0.1 M NaCl+0.1 M Tau (green with bias) for 1 and 3 days. Value = mean ± standard deviation, n≥3. * P < 0.05; ** P < 0.01; *** P < 0.001. 82x170mm (299 x 299 DPI)

ACS Paragon Plus Environment

Page 28 of 36

Page 29 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 3. The ability to prevent ice injury: Differential scanning calorimetry (DSC) melting thermograms of 0 M (dark blue), 0.1 M (red), 0.3 M (green), 0.5 M (purple), 1 M (light blue), and 1.5 M (orange) of (A) Pro, (B) Gly and (C) Tau solutions. (D) The depression of water freezing point and (E) the ratio of bound water in three systems. Photo images taken at 79 s after the freezing process started (F) and 27 s after the thawing process started (G) in three systems and pure water. 178x180mm (299 x 299 DPI)

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 4. Post-thaw intact SRBCs with ultrarapid freezing protocol: (A) Photos of post-thaw SRBCs using three osmoprotectants (Pro, Gly and Tau) compared with control samples. (B) Post-thaw intact SRBC rates. ND: not detected. Value= mean ± standard deviation, n≥3. * P < 0.05; *** P < 0.001. 82x63mm (299 x 299 DPI)

ACS Paragon Plus Environment

Page 30 of 36

Page 31 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 5. Fluorescence images of the live/dead assay of GLC-82 cells (upper row), LTEP-a-2 cells (second row), 3T3 cells (third row) and SMCs (lower row) respectively cryopreserved with three osmoprotectants in optimum concentrations (Pro: 6% and 8%; Gly: 2% and 4%; Tau: 4% and 6%), DMSO 10%) and control culture medium as well as fresh cells with ultrarapid freezing protocol. Green: live cells. Red: dead cells. Scale bar=100 µm.

178x87mm (299 x 299 DPI)

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 6. Cell cryopreservation: Post-thaw survival efficiency of (A) GLC-82 cells, (B) LTEP-a-2 cells, (C) 3T3 cells and (D) SMCs evaluated at fresh cells (light blue) and different concentrations of Pro (red), Gly (dark blue), Tau (green) compared with that of 10% DMSO (orange) and control sample (gray). ND: not detected. Value= mean ± standard deviation, n≥3. * P < 0.05; ** P < 0.01; *** P < 0.001. 178x131mm (299 x 299 DPI)

ACS Paragon Plus Environment

Page 32 of 36

Page 33 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 7. The functionalities of recovered cells: (A) The cell morphology and (B) cell attachment numbers per square millimeter of LTEP-a-2 cells (upper row) and 3T3 cells (lower row) respectively after cryopreservation with Pro, Gly and Tau in optimum concentrations, compared with fresh cells. Scale bar=100 µm. (C) The proliferation curves of recovered GLC-82 cells after cryopreservation with Pro, Gly and Tau, compared with fresh cells. Value= mean ± standard deviation, n≥3. 82x66mm (299 x 299 DPI)

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 8. Cytotoxicity evaluation: (A) Cell viability and (B) attachment of GLC-82 cells after exposed in medium containing 2% of Pro, Gly, Tau and DMSO for 3 days (upper row) and 5 days (lower row), and pure medium as control. Scale bar=100 µm. Value= mean ± standard deviation, n≥3. *** P < 0.001. 178x66mm (299 x 299 DPI)

ACS Paragon Plus Environment

Page 34 of 36

Page 35 of 36 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Figure 9. A proposed mechanism. The role of (A) Pro, (B) Gly and (C) Tau to protect cells from the cryoinjuries (osmotic and ice injuries) during freeze-thaw cycle in cryopreservation. 178x198mm (299 x 299 DPI)

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Table of Contents/Abstract Graphics 84x35mm (299 x 299 DPI)