Fabrication of Gold Nanosphere Oligomers for Surface-Enhanced

Nov 7, 2017 - limited availability. A reliable method for substrate .... through two narrow bandpass filters, while the broadband probe pulse was crea...
0 downloads 0 Views 1MB Size
Subscriber access provided by READING UNIV

Article

Fabrication of Gold Nanosphere Oligomers for SurfaceEnhanced Femtosecond Stimulated Raman Spectroscopy Bogdan Negru, Michael O. McAnally, Hannah E Mayhew, Tyler Ueltschi, Lingxuan Peng, Emily Sprague-Klein, George C. Schatz, and Richard P. Van Duyne J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.7b09664 • Publication Date (Web): 07 Nov 2017 Downloaded from http://pubs.acs.org on November 16, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry C is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Fabrication of Gold Nanosphere Oligomers for Surface-Enhanced Femtosecond Stimulated Raman Spectroscopy Bogdan Negru†, Michael O. McAnally, Hannah E. Mayhew, Tyler Ueltschi, Lingxuan Peng, Emily Sprague-Klein, George C. Schatz, Richard P. Van Duyne* Department of Chemistry, Northwestern University, 2145 Sheridan Road, Evanston, Illinois 60208, United States

ABSTRACT: Surface-enhanced femtosecond stimulated Raman spectroscopy (SE-FSRS) is a technique that has the potential to study the ultrafast dynamics of surface adsorbates with simultaneously high temporal and spectral resolutions. One of the greatest impediments to the further development of SE-FSRS is the lack of high quality plasmonic substrates that permit excitation and prove wavelength agility as well as flexible selection of the adsorbate molecule. Herein, we present a simple aggregation/stabilization procedure for the formation of gold nanosphere oligomers with tunable plasmonic properties and flexible choice of adsorbate that are ideal for SE-FSRS and other coherent Raman spectroscopies.

ACS Paragon Plus Environment

1

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 14

INTRODUCTION Femtosecond stimulated Raman spectroscopy (FSRS) has been developed to study the ensemble-averaged structure of chemical systems on the time scale of molecular motion.1-3 This technique probes changes in molecular structure by acquiring Raman spectra with a temporal resolution in the range of 10 – 100 fs.1, 4-5 FSRS has been used to study the vibrational dynamics of many molecules,6-8 but has been limited to highly concentrated systems with large Raman scattering cross-sections.

This limitation was surpassed for ground-state FSRS by the

development of surface-enhanced femtosecond stimulated Raman spectroscopy (SE-FSRS).9 SE-FSRS has the capability of studying surface chemistry with high spectral and temporal resolution. SE-FSRS uses a combination of the electromagnetic and chemical mechanisms active in surface-enhanced Raman scattering10 (SERS) to amplify the FSRS signal by as much as four to six orders of magnitude.9 Ground state SE-FSRS was demonstrated on Au nanosphere oligomers (also called SERS nanotags) that were commercially available. These nanoparticles are Au cores (90 nm or 60 nm in diameter), surface functionalized with trans-1,2-bis(4-pyridyl)-ethylene (BPE) as the adsorbate, and capped with a thick (~60 nm) silica shell.9, 11 Numerous attempts were made in our laboratory to acquire SE-FSR spectra on Au film over nanosphere (AuFON) surface and nanotriangles fabricated by nanosphere lithography (NSL), all such attempts failed due to sample damage caused by the high peak powers of pulsed pump and probe beams. All SE-FSRS studies published thus far have been limited to Au nanosphere oligomers.9, 12-17 While these commercial substrates are very durable and highly enhancing, they are limited to only a few adsorbate molecules and have limited availability. A reliable method for substrate synthesis is, therefore, of utmost importance if SE-FSRS is to be used for the investigation of ultrafast dynamics of

ACS Paragon Plus Environment

2

Page 3 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

relevant plasmonic chemistry systems:18 such as plasmon-enhanced solar cells19-20 and plasmonenhanced photocatalysis.21-23 A wide variety of synthetic approaches for SERS substrates have been published in literature, including colloidal pastes,24 thin metal films, NSL nanotriangles,25-26 metal FONs,27 and polymer-fiber-nanoparticle assemblies.28 In order to implement time-resolved (TR)-SEFSRS two femtosecond and one picosecond pulse must be overlapped in space and time. Effectively, these pulses interrogate a volume of sample in which the three pulses are overlapped, necessitating substrates that occupy a volume that is greater than the diameter of the focal spot times an interaction length of a few millimeters.29-30 Depending on beam overlap, the FSRS signal can be observed as far as 1 cm or more from the focal spot created by a 10 cm focal length lens. The Au nanosphere oligomers are dispersed in solution with pathlengths of 1-10 mm, while two-dimensional substrates, such as FONs and NSL triangles, only minimally interact with the laser pulses, due to the near-zero interaction length. The short interaction length problem coupled with surface damage caused by the intrinsically high peak powers of laser pulses amplified at electromagnetic hot spots9, 17 accounts for the lack of success in using these substrates for SE-FSRS. For these reasons, the gold nanosphere oligomers have proven to be the best, and presently only, platform for SE-FSRS.9, 12-13, 15-17 Herein we present a simple and reliable protocol for the synthesis of gold nanosphere oligomers. This protocol can be used for the development of highly enhancing substrates that are exceptionally stable to ambient environments, femtosecond laser pulses, and contain a wide range of user chosen adsorbates. To demonstrate the utility of this protocol, the synthesis of gold nanosphere oligomers with the following adsorbates: tris-(2,2′-bipyridine)ruthenium(II) ([Ru(bpy)3]2+),

tris-(2,2′-bipyridine)iron(II)

([Fe(bpy)3]2+),

4,4′-azopyridine,

2,2′:6′,2″-

ACS Paragon Plus Environment

3

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 14

terpyridine (Terpy), and β-carotene is provided. All of these molecules are of significant interest for time-resolved photodynamics and have been studied in solution by TR-FSRS.3 For example, previous studies explored the excited state dynamics of [Ru(bpy)3]2+ in solution and observed rapid formation of triplet metal to ligand charge transfer state (3MLCT) after 1MLCT  1A1 excitation.31-32 However, the impact of adsorbing [Ru(bpy)3]2+ to a plasmonic surface on the photophysics of this system is unknown. METHODS The synthesis of gold nanosphere oligomers followed a bottom-up approach that started with gold monomer solutions. Gold colloids of two different sizes, roughly 50 nm and 90 nm in diameter, were prepared by a standard citrate reduction method.33 Briefly, a 50 mL 0.1% wt/wt HAuCl4 in MilliQ water solution was brought to a boil. A single addition of either 0.40 mL or 0.22 mL 1% wt/wt Na3-citrate was made under vigorous stirring conditions. After 30 minutes of boiling, the solution was slowly cooled and stored in the dark. A previously described34 highresolution localized surface plasmon resonance instrument (HR-LSPR) was used to continuously monitor the extinction spectra of the gold monomer solution in-situ from 500 to 1100 nm. Aggregation of gold monomers was induced by the repeated addition of 10 µL aliquots of MilliQ water containing the adsorbate molecule of interest. In the case of BPE, the aggregating solution consisted of a 100-fold dilution of room temperature saturated BPE aqueous solution. The aggregation of gold monomers can be monitored in real time by the acquisition of extinction spectra, as shown in Figure 1. In addition, aqueous solutions of [Ru(bpy)3]2+, [Fe(bpy)3]2+, 4,4′azopyridine, and other analytes were successfully used to aggregate gold monomers. It is important to note that nanosphere oligomers were successfully created with a wide range of adsorbate molecule concentrations: from µM to mM regimes.

ACS Paragon Plus Environment

4

Page 5 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Most importantly, monomer aggregation was stopped and newly formed nanosphere oligomers were stabilized by the addition of 0.2 mL of 10% wt/wt 55 kDa polyvinylpyrrolidone (PVP) solution in ethanol. PVP is a water soluble polymer commonly employed in nanoparticle synthesis.35 A thin (approximately 3 nm) polymer layer can be observed in the transmission electron microscopy (TEM) scan presented in Figure 2. All reagents were purchased from Sigma-Aldrich and used without further purification, with the exception of BPE, which was purified by sublimation.

Figure 1: Real time extinction spectra of 90 nm gold monomers aggregating due to the addition of dilute aqueous solution of trans-1,2-bis(4-pyridyl)-ethylene.

A detailed description of the experimental setup for SE-FSRS spectroscopy has been described previously.9,

12

In short, the fundamental of a Coherent RegA 100 kHz ultrafast

amplifier was split into two pulses: pump and probe. The picosecond Raman pump pulse at 795 nm was created by passing the beam through two narrow bandpass filters, while the broadband probe pulse was created by continuum generation in an undoped YAG window. Both pulses are recombined in a macroscopic cuvette sample, with Raman gain determined by dividing the pump-on spectra by the pump-off spectra. Surface-enhanced Raman scattering spectra were

ACS Paragon Plus Environment

5

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 14

collected on an inverted microscope.36 Briefly, the sample was mounted on a Nikon Eclipse TiU inverted microscope and illuminated with a 785 nm CW laser (Renishaw Inc.). A 20X objective was used to both focus the laser light onto the sample and collect the scattered signal. Stokes-shifted signal was focused into an ACTON 2300 spectrometer outfitted with a PIXIS 400BR CCD camera (Princeton Instrument).

Figure 2: Transmission electron microscopy (TEM) scan of nanosphere oligomer aggregated with 2,2′:6′,2″-terpyridine and stabilized with 55 kDa polyvinylpyrrolidone. The image was acquired with a Hitachi H-8100 at 200 kV.

RESULTS AND DISCUSSION The HR-LSPR setup allows for continuous monitoring of the extinction spectrum, and thus sample aggregation as shown in Figure 1. Initially, the monomer peak was observed near 560 nm. Aggregate formation can be tracked by monitoring the appearance of broad spectral features at longer wavelengths. Monomers aggregate to form dimers and trimers, then continue aggregating to form larger and larger nanosphere oligomers. For this reason, the LSPR peak corresponding to the oligomers shifts to longer and longer wavelengths.

As the average

nanosphere oligomer size increases, the size distribution also increases, leading to broader LSPR peaks.

Nanosphere oligomers are formed from monomers, so the monomer LSPR peak

ACS Paragon Plus Environment

6

Page 7 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

decreases in intensity but does not vanish as oligomers still retain a monomer LSPR band.11 Nanosphere oligomer solutions can be slowly aggregated over a period of days by the addition of a small number of adsorbate molecules. Alternatively, they can be aggregated in a few seconds if a large amount of adsorbate is added.

Step-wise addition of adsorbate solution with

continuous LSPR monitoring makes it easy to achieve the desired state of oligomerization. It is important to note that the oligomerization of gold monomers can be instantaneously stopped, at the macroscopic scale, by the addition of PVP, a weakly bound nitrogen-based capping agent.37 Figure 3a compares the LSPR spectra of BPE aggregated nanosphere oligomer samples. One sample was produced from smaller gold monomers roughly 50 nm in diameter (trace 3, red), and the rest from gold monomers approximately 90 nm in diameter. The latter samples (traces 1, 2, and 4) were arrested at different states of oligomerization resulting in substrates with varying plasmonic properties. In addition, Figure 3 displays the overlap between nanosphere oligomer LSPR and FSRS laser pulses. The spectral overlap between the LSPR of enhancing substrate and Raman pump/probe laser pulses influences both gain and dispersion of FSRS signal,16 as seen in Figure 3b. The dispersive peak shapes observed in SE-FSRS arise from coupling between adsorbed molecules and the plasmon resonances in the nanosphere oligomers.12, 16 The lineshapes observed in these samples appear very different, although they were collected sequentially with identical laser and spectrometer parameters. The LSPR characteristics of these highly enhancing substrates are crucial for SE-FSRS, and the preparation technique described herein can be used reliably to generate substrates that are optimized for the laser pulses available to the user.

ACS Paragon Plus Environment

7

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 14

Figure 3: The effect of nanosphere oligomer LSPR on SE-FSRS lineshape and amplitude. a) Spectral overlap between Raman pump/probe and nanosphere oligomer LSPR. The colored traces labeled 1,2, and 4 represent 90 nm Au monomers arrested at different points in the aggregation process using PVP and trace 3 represents a sample made with 50 nm Au monomers. b) SE-FSRS signal from samples 1-4, showing varying Fano lineshapes and amplitudes dependent on the sample LSPR position relative to the Raman pump/probe pulse pair.

Close observation of the extinction spectrum of the nanosphere oligomer sample allows one to manipulate the rate of oligomerization by controlling adsorbate addition. Furthermore, since the LSPR has direct influence over the enhancing capabilities of the nanosphere oligomer,16 the extinction spectrum can be used to determine the optimal moment to stop aggregation by polymer addition. On the timescale of oligomerization, the gold nanospheres are stabilized instantaneously, and their plasmonic properties at the time of PVP addition are preserved indefinitely (at least to several months).

PVP stabilization of gold nanosphere

ACS Paragon Plus Environment

8

Page 9 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

oligomers provides unparalleled molecular control: making it possible to produce samples with desired plasmon resonances for stimulated Raman spectroscopies. The use of PVP for arresting oligomerization is a general and simple procedure. The addition of 200 µL solutions of 55 kDa PVP effectively stopped the aggregation of gold monomers driven by many adsorbates of interest, including BPE, Terpy, [Ru(bpy)3]2+, [Fe(bpy)3]2+, and 4,4′-azopyridine (Figure 4). Figure 4 displays ground-state SE-FSRS and SERS spectra of gold nanosphere oligomers aggregated with [Ru(bpy)3]2+ and 4,4′-azopyridine. These samples produced SER and SE-FSR spectra of excellent quality, opening the door for TRSE-FSRS experiment on chemical systems with ultrafast dynamics.

ACS Paragon Plus Environment

9

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 14

Figure 4: SERS and SE-FSRS spectra of nanosphere oligomers aggregated with a) tris-(2,2′bipyridine)ruthenium(II), and b) 4,4′-azopyridine. SERS spectra were acquired for 10 seconds with 110 µW at 785 nm.

CONCLUSION We have demonstrated that Au nanosphere oligomers are the best substrate presently available for SE-FSRS experiments. The use of polyvinylpyrrolidone (PVP) to stop monomer oligomerization is a straight-forward approach for the fabrication of gold nanosphere oligomers containing user selectable adsorbate molecules. A variety of adsorbate molecules interest to us were used to prepare Au nanosphere oligomers. PVP (55 kDa) polymer was used to arrest and stabilize Au nanosphere oligomers. The stabilizing effect of the polymer is instantaneous on the

ACS Paragon Plus Environment

10

Page 11 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

timescale of oligomerization, facilitating the fabrication of SE-FSRS substrates with precisely tuned plasmonic properties. AUTHOR INFORMATION Corresponding Authors *E-mail: [email protected]. Present Addresses †

B.N.: Department of Chemistry, Sonoma State University, 1801 East Cotati Avenue, Rohnert

Park, California 94928, United States Author Contributions The manuscript was written through contributions of all authors. All authors have given approval to the final version of the manuscript. Notes The authors declare no competing financial interest. ACKNOWLEDGMENT This work was supported by the National Science Foundation Grant CHE-1414466 and the Center for Chemical Innovation (CCI) dedicated to Chemistry at the Space-Time limit (CaSTL). BN would also like to thank the School of Science and Technology at Sonoma State University for support. We thank Natalie L. Gruenke, Naihao Chiang, and Dmitry Kurouski for helpful discussions.

The authors also thank Northwestern University’s Atomic and Nanoscale

Characterization Experimental Center (NUANCE) for the use of their imaging facilities.

ACS Paragon Plus Environment

11

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 14

REFERENCES 1. Kukura, P.; McCamant, D. W.; Mathies, R. A. Femtosecond Stimulated Raman Spectroscopy Annu. Rev. Phys. Chem. 2007, 58, 461-488 2. Frontiera, R. R.; Mathies, R. A. Femtosecond Stimulated Raman Spectroscopy Laser & Photonics Reviews 2011, 5, 102-113 3. Dietze, D. R.; Mathies, R. A. Femtosecond Stimulated Raman Spectroscopy ChemPhysChem 2016, 17, 1224-1251 4. McCamant, D. W.; Kukura, P.; Yoon, S.; Mathies, R. A. Femtosecond Broadband Stimulated Raman Spectroscopy: Apparatus and Methods Rev. Sci. Instrum. 2004, 75, 49714980 5. Kukura, P.; McCamant, D. W.; Yoon, S.; Wandschneider, D. B.; Mathies, R. A. Structural Observation of the Primary Isomerization in Vision with Femtosecond-Stimulated Raman Science 2005, 310, 1006-1009 6. McCamant, D. W.; Kukura, P.; Mathies, R. A. Femtosecond Stimulated Raman Study of Excited-State Evolution in Bacteriorhodopsin Journal of Physical Chemistry B 2005, 109, 10449-10457 7. Yoon, S.; Kukura, P.; Stuart, C. M.; Mathies, R. A. Direct Observation of the Ultrafast Intersystem Crossing in Tris(2,2 '-Bipyridine) Ruthenium(Ii) Using Femtosecond Stimulated Raman Spectroscopy Mol. Phys. 2006, 104, 1275-1282 8. Weigel, A.; Dobryakov, A.; Klaumunzer, B.; Sajadi, M.; Saalfrank, P.; Ernsting, N. P. Femtosecond Stimulated Raman Spectroscopy of Flavin after Optical Excitation Journal of Physical Chemistry B 2011, 115, 3656-3680 9. Frontiera, R. R.; Henry, A. I.; Gruenke, N. L.; Van Duyne, R. P. Surface-Enhanced Femtosecond Stimulated Raman Spectroscopy J. Phys. Chem. Lett. 2011, 2, 1199-1203 10. Stiles, P. L.; Dieringer, J. A.; Shah, N. C.; Van Duyne, R. R. Surface-Enhanced Raman Spectroscopy Annual Review of Analytical Chemistry 2008, 1, 601-626 11. Tyler, T. P.; Henry, A.-I.; Van Duyne, R. P.; Hersam, M. C. Improved Monodispersity of Plasmonic Nanoantennas Via Centrifugal Processing The Journal of Physical Chemistry Letters 2011, 2, 218-222 12. Frontiera, R. R.; Gruenke, N. L.; Van Duyne, R. P. Fano-Like Resonances Arising from Long-Lived Molecule-Plasmon Interactions in Colloidal Nanoantennas Nano Lett. 2012, 12, 5989-5994 13. Buchanan, L. E.; Gruenke, N. L.; McAnally, M. O.; Negru, B.; Mayhew, H. E.; Apkarian, V. A.; Schatz, G. C.; Van Duyne, R. P. Surface-Enhanced Femtosecond Stimulated Raman Spectroscopy at 1 Mhz Repetition Rates J. Phys. Chem. Lett. 2016, 7, 4629-4634 14. Gruenke, N. L.; Cardinal, M. F.; McAnally, M. O.; Frontiera, R. R.; Schatza, G. C.; Van Duyne, R. P. Ultrafast and Nonlinear Surface-Enhanced Raman Spectroscopy Chemical Society Reviews 2016, 45, 2263-2290 15. Gruenke, N. L.; McAnally, M. O.; Schatz, G. C.; Van Duyne, R. P. Balancing the Effects of Extinction and Enhancement for Optimal Signal in Surface-Enhanced Femtosecond Stimulated Raman Spectroscopy J. Phys. Chem. C 2016, 120, 29449-29454 16. McAnally, M. O.; McMahon, J. M.; Van Duyne, R. P.; Schatz, G. C. Coupled Wave Equations Theory of Surface-Enhanced Femtosecond Stimulated Raman Scattering J. Chem. Phys. 2016, 145, 094106

ACS Paragon Plus Environment

12

Page 13 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

17. Buchanan, L. E.; McAnally, M. O.; Gruenke, N. L.; Schatz, G. C.; Van Duyne, R. P. Studying Stimulated Raman Activity in Surface-Enhanced Femtosecond Stimulated Raman Spectroscopy by Varying the Excitation Wavelength The Journal of Physical Chemistry Letters 2017, 8, 3328-3333 18. Christopher, P.; Moskovits, M. Hot Charge Carrier Transmission from Plasmonic Nanostructures Annu. Rev. Phys. Chem. 2017, 68, 379-398 19. Pillai, S.; Catchpole, K. R.; Trupke, T.; Green, M. A. Surface Plasmon Enhanced Silicon Solar Cells J. Appl. Phys. 2007, 101, 093105 20. Catchpole, K. R.; Polman, A. Plasmonic Solar Cells Opt. Express 2008, 16, 21793-21800 21. Gao, H.; Liu, C.; Jeong, H. E.; Yang, P. Plasmon-Enhanced Photocatalytic Activity of Iron Oxide on Gold Nanopillars ACS Nano 2012, 6, 234-240 22. Mukherjee, S.; Libisch, F.; Large, N.; Neumann, O.; Brown, L. V.; Cheng, J.; Lassiter, J. B.; Carter, E. A.; Nordlander, P.; Halas, N. J. Hot Electrons Do the Impossible: Plasmon-Induced Dissociation of H2 on Au Nano Lett. 2012, 13, 240-247 23. Hou, W.; Cronin, S. B. A Review of Surface Plasmon Resonance-Enhanced Photocatalysis Advanced Functional Materials 2013, 23, 1612-1619 24. Idone, A.; Gulmini, M.; Henry, A. I.; Casadio, F.; Chang, L. R.; Appolonia, L.; Van Duyne, R. P.; Shah, N. C. Silver Colloidal Pastes for Dye Analysis of Reference and Historical Textile Fibers Using Direct, Extractionless, Non-Hydrolysis Surface-Enhanced Raman Spectroscopy Analyst 2013, 138, 5895-5903 25. Hulteen, J. C.; Van Duyne, R. P. Nanosphere Lithography: A Materials General Fabrication Process for Periodic Particle Array Surfaces Journal of Vacuum Science & Technology A: Vacuum, Surfaces, and Films 1995, 13, 1553-1558 26. Haynes, C. L.; Van Duyne, R. P. Nanosphere Lithography: A Versatile Nanofabrication Tool for Studies of Size-Dependent Nanoparticle Optics Journal of Physical Chemistry B 2001, 105, 5599-5611 27. Dick, L. A.; McFarland, A. D.; Haynes, C. L.; Van Duyne, R. P. Metal Film over Nanosphere (Mfon) Electrodes for Surface-Enhanced Raman Spectroscopy (Sers):  Improvements in Surface Nanostructure Stability and Suppression of Irreversible Loss The Journal of Physical Chemistry B 2002, 106, 853-860 28. Mondal, S.; Rana, U.; Malik, S. Facile Decoration of Polyaniline Fiber with Ag Nanoparticles for Recyclable Sers Substrate ACS Applied Materials & Interfaces 2015, 7, 1045710465 29. Mukamel, S., Principles of Nonlinear Optical Spectroscopy; Oxford University Press on Demand, 1999. 30. Cheng, J.-X.; Xie, X. S., Coherent Raman Scattering Microscopy; CRC press, 2016. 31. Damrauer, N. H.; Cerullo, G.; Yeh, A.; Boussie, T. R.; Shank, C. V.; McCusker, J. K. Femtosecond Dynamics of Excited-State Evolution in [Ru(Bpy)3]2+ Science 1997, 275, 54-57 32. Bhasikuttan, A. C.; Suzuki, M.; Nakashima, S.; Okada, T. Ultrafast Fluorescence Detection in Tris(2,2 '-Bipyridine)Ruthenium(Ii) Complex in Solution: Relaxation Dynamics Involving Higher Excited States Journal of the American Chemical Society 2002, 124, 83988405 33. Frens, G. Controlled Nucleation for the Regulation of the Particle Size in Monodisperse Gold Suspensions Nature Phys Sci 1973, 241, 20-22 34. Willets, K. A.; Van Duyne, R. P. Localized Surface Plasmon Resonance Spectroscopy and Sensing Annu. Rev. Phys. Chem. 2007, 58, 267-297

ACS Paragon Plus Environment

13

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 14

35. Sun, Y.; Xia, Y. Shape-Controlled Synthesis of Gold and Silver Nanoparticles Science 2002, 298, 2176-2179 36. Zrimsek, A. B.; Henry, A. I.; Van Duyne, R. P. Single Molecule Surface-Enhanced Raman Spectroscopy without Nanogaps J. Phys. Chem. Lett. 2013, 4, 3206-3210 37. Quintanilla, A.; Butselaar-Orthlieb, V. C. L.; Kwakernaak, C.; Sloof, W. G.; Kreutzer, M. T.; Kapteijn, F. Weakly Bound Capping Agents on Gold Nanoparticles in Catalysis: Surface Poison? J. Catal. 2010, 271, 104-114

ACS Paragon Plus Environment

14