Facile Fabrication of Ethoxy-Functional Polysiloxane Wrapped LiNi Co Mn O Cathode with Improved Cycling Performance for Rechargeable Li-Ion Battery Hao Wang, Wujie Ge, Wen Li, Feng Wang, Wenjing Liu, Mei-zhen Qu, and Gongchang Peng ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.6b04644 • Publication Date (Web): 30 Jun 2016 Downloaded from http://pubs.acs.org on July 3, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 40

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Facile Fabrication of Ethoxy-Functional Polysiloxane Wrapped LiNi0.6Co0.2Mn0.2O2 Cathode with Improved Cycling Performance for Rechargeable Li-Ion Battery Hao Wang, †,‡ Wujie Ge, †,‡ Wen Li,§ Feng Wang,‡ Wenjing Liu,‡ Mei-Zhen Qu,‡ Gongchang Peng*,‡ †

Graduate University of Chinese Academy of Sciences, Beijing 100039, P.R. China.



Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu 610041, P.R.

China. §

Hebei Academy of Sciences, Shijiazhuang 050000, P.R. China.

ABSTRACT

Dealing with the water molecule on the surface of LiNi0.6Co0.2Mn0.2O2 (NCM) cathode and hydrogen fluoride in the electrolyte is one of the most difficult challenges in Li-ion battery research.

In this

paper, the surface polymerization of tetraethyl orthosilicate (TEOS) on NCM to generate ethoxy-functional polysiloxane (EPS) wrapped NCM (E-NCM) cathode under mild conditions and without any additions is utilized to solve this intractable problem.

The differential scanning

calorimetry, transmission electron microscope and X-ray photoelectron spectroscopy results show that the formed amorphous coating can provide a protecting shell to improve the NCM thermal stability, suppress the thickening of the solid electrolyte interphase (SEI) layer and scavenge HF in the electrolyte.

The E-NCM composite with 2 mol% EPS delivers a high discharge capacity

retention of 84.9% after 100 cycles at a 1 C discharge rate in the 2.8 - 4.3 V potential range at 55 °C. Moreover, electrochemical impedance spectroscopy measurements reveal that the EPS coating could alleviate the impedance rise during cycling especially at an elevated temperature.

1 Environment ACS Paragon Plus

Therefore, the

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

fabricated E-NCM cathode with long-term cycling and thermal stability is a promising candidate for use in a high-energy Li-ion battery.

KEYWORDS: Ni-rich layered oxide, polysiloxane, surface modification, thermal stability, Li-ion battery.

2 Environment ACS Paragon Plus

Page 2 of 40

Page 3 of 40

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

1. INTRODUCTION Layered lithium transition metal oxides Li[NixCoyMnz]O2 (0≤x,y,z