Gellan Gum-Hyaluronic Acid Spongy-like Hydrogels and Cells from

Oct 31, 2014 - Currently available substitutes for skin wound healing often result in the formation of nonfunctional neotissue. Thus, urgent care is s...
1 downloads 6 Views 2MB Size
Subscriber access provided by Nanyang Technological Univ

Article

Gellan Gum-Hyaluronic Acid Spongy-like hydrogels and cells from adipose tissue synergize promoting neoskin vascularization Mariana T. Cerqueira, Lucília Pereira da Silva, Tircia C. Santos, Rogerio P. Pirraco, Vitor M. Correlo, Rui L. Reis, and Alexandra P. Marques ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/am504520j • Publication Date (Web): 31 Oct 2014 Downloaded from http://pubs.acs.org on November 5, 2014

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Gellan Gum-Hyaluronic Acid Spongy-like hydrogels and cells from adipose tissue synergize promoting neoskin vascularization Mariana Teixeira Cerqueira 1,2, Lucília Pereira da Silva1,2, Tírcia Carlos Santos1,2, Rogério Pedro Pirraco1,2, Vítor Manuel Correlo1,2, Rui Luís Reis1,2 , Alexandra Pinto Marques1,2* 1 3B’s Research Group - Biomaterials, Biodegradables and Biomimetics, University of Minho, Headquarters of the European Institute of Excellence on Tissue Engineering and Regenerative Medicine, AvePark,4806-909 Taipas, Guimarães, Portugal 2 ICVS/3B’s - PT Government Associate Laboratory, Braga/Guimarães, Portugal

Name of the Authors/degree/email: Mariana Teixeira Cerqueira1,2, PhD, [email protected] Lucília Pereira da Silva1,2, MSc, [email protected] Tircia Carlos Santos1,2, PhD, [email protected] Rogério Pedro Pirraco1,2, PhD, [email protected] Vitor Manuel Correlo1,2, PhD, [email protected] Rui Luís Reis1,2, PhD, [email protected] Alexandra Pinto Marques1,2, PhD, [email protected]

Work developed at 3B’s Research Group, University of Minho

1 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 36

Corresponding author: Alexandra Pinto Marques ([email protected]) Headquarters of the European Institute of Excellence on Tissue Engineering and Regenerative Medicine AvePark, Zona Industrial da Gandra S. Cláudio do Barco 4806-909 Caldas das Taipas – Guimarães PORTUGAL

2 ACS Paragon Plus Environment

Page 3 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

ABSTRACT Currently available substitutes for skin wound healing often result in the formation of nonfunctional neotissue. Thus, urgent care is still needed to promote an effective and complete regeneration. To meet this, we proposed the assembling of a construct that takes advantage of cell-adhesive gellan gum-hyaluronic acid (GG-HA) spongy-like hydrogels and a powerful cellmachinery obtained from adipose tissue, human adipose stem cells (hASCs) and microvascular endothelial cells (hAMECs). In addition to a cell-adhesive character, GG-HA spongy-like hydrogels overpass limitations of traditional hydrogels, such as reduced physical stability and limited manipulation, due to improved microstructural arrangement characterized by pore wall thickening and increased mean pore size. The proposed constructs combining cellular mediators of the healing process within the spongy-like hydrogels that intend to recapitulate skin matrix, aim to promote neoskin vascularization. Stable and off-the-shelf dried GG-HA polymeric networks, rapidly re-hydrated at the time of cell seeding then depicting features of both sponges and hydrogels, enabled the natural cell entrapment/encapsulation and attachment supported by cell-polymer interactions. Upon transplantation into mice fullthickness excisional wounds, GG-HA spongy-like hydrogels absorbed the early inflammatory cell infiltrate and lead to the formation of a dense granulation tissue. Consequently, spongy-like hydrogel degradation was observed and progressive wound closure, re-epithelialization and matrix remodelling was improved in relation to the control condition. More importantly, GG-HA spongy-like hydrogels promoted a superior neovascularization, which was enhanced in the presence of human hAMECs, also found in the formed neovessels. These observations highlight the successful integration of a valuable matrix and pre-vascularization cues to target angiogenesis/neovascularization in skin full-thickness excisional wounds.

Keywords: skin, tissue engineering, gellan gum, hyaluronic acid, vascularization, stem cells

INTRODUCTION 3 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 36

The healing of deep skin wounds in adults takes place by both undesirable wound contraction and scar formation, leading to non-functional neotissue formation 1. To tackle this problematic, varied skin tissue engineered substitutes based on polymeric matrices derived from both natural (collagen

2-3,

hyaluronic acid (HA) 4, gelatin 5, fibrin

6

, laminin and elastin 7) and

synthetic (polypropylene 8, polycaprolactone 9 and polyethylene terephthalate 10) sources have been proposed. Emphasis has been given to scaffolding matrices that are though to reduce/avoid skin contraction during the regeneration process. The mimicking of tissue extracellular matrix (ECM) has been seen as a route to be pursued. The use of hydrogels, extremely hygroscopic 11 and potentially depicting soft tissues-like mechanical properties 3, for wound healing purposes has 3, 12

or are

13-17,

act as

been then explored. However hydrogels, except for those that are protein-derived combined/modified with these or with specific cell-adhesive peptide sequences

mere cell delivery vehicles. While contributing to improved cell engraftment 18, they still fail at providing biological cues due to the lack of cell adhesion sites in their networks 19. This might be particularly relevant to achieve an appropriate revascularization of the skin tissue substitutes that so far does not occur in a favorable time fashion and that has been hampering their success

20-21.

Different approaches have been followed to improve wound healing by

promoting a faster and better vascularization of the skin substitutes 22-30. The incorporation of soluble angiogenic factors, such as vascular endothelial growth factor growth factor proteins

27-28,

26,

25

or basic fibroblast

the genetic modification of the transplanted cells to produce angiogenic

as well as the pre-vascularization of matrices and scaffolds with progenitor or

endothelial cells

29-31,

are the most explored. Pre-vascularization turned out to be the more

efficient in promoting inosculation and consequently in achieving a superior outcome. Despite the significant range of progenitor and endothelial cells that have been experimented along with a wide assortment of scaffolds, these strategies still fail in the recapitulation of the in vivo process. In fact, one of the causes of this problematic seems to be the source of endothelial cells; endothelial progenitor cells endothelial cells

29

31,

umbilical vein endothelial cells

32,

or microvascular

are usually from allogeneic sources and if autologous, have limited

availability and thus relevance in a clinical setting. Mesenchymal stem cells (MSCs), including ASCs, have been known to release paracrine factors and thus influence different host cells during wound healing. Wound closure acceleration, improved neovascularization, and reduced scar formation have been associated in particular to ASCs

33-36,

that in addition to their immunomodulatory properties, represent 4 ACS Paragon Plus Environment

Page 5 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

valuable features from a cell therapy perspective 37. In one of our previous works, we were also able to demonstrate that hASCs embedded in their own ECM as cell-sheets contributed to neoepidermal morphogenesis but in a way that was dependent on the nature of the ECM 38, confirming the importance of the matrix in which cells are embedded. We have previously reported the development of cell-adhesive gellan gum (GG)-based matrices with physical properties between sponges and hydrogels

39-40

that, although not capable of sustained the

self-organization of the freshly isolated skin cellular fractions, impacted early vascularization in full-thickness mice wound healing. These results suggested that GG-hyaluronic acid (HA) spongy-like hydrogels provided a suitable environment to sustain endothelial cells survival and phenotype/functionality 41. Thus, considering that by providing cells with a valuable matrix that would permit their natural organization and interaction prior to implantation would be beneficial, we propose a tissue engineered construct combining a GG-HA spongy-like hydrogel and adipose tissue microvascular endothelial cells and stem cells aiming at promoting skin wound neovascularization. The proposed approach takes advantage of the angiogenic elements that can be isolated from a single cell source, adipose tissue, and an off-the-shelf 3D structure that mimics skin ECM composition and, upon hydration, presents similarities with its physical properties.

MATERIALS AND METHODS 1. Gellan Gum-Hyaluronic Acid Spongy-like hydrogels

1.1. Preparation Gellan Gum-Hyaluronic Acid spongy-like hydrogels were prepared as previously described 3940.

Briefly, a solution of 0.75 % (m/V) hyaluronate (1.5 MDa, LifeCore Biomedical, USA) and

1.25 % (m/V) gelzan (Sigma-Aldrich, France) was prepared at 90ºC and then transferred onto 24-well plates. The addition of divalent cations was performed in order to form the hydrogels by ionic crosslinking. Phosphate-buffered saline (PBS, Sigma USA) solution was added to the hydrogels for further hydration for 48 h. Following that, hydrogels were frozen at -80ºC overnight and then freeze-dried (Telstar, Spain) for three days by hydration with culture medium at the time of cell seeding. Dried polymeric networks and spongy-like hydrogels were photographed using a Stereo Microscope Stemi 1000 (Zeiss, Germany).

5 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 36

1.2. Micro-computed tomography (micro-CT) Dried polymeric networks microarchitecture was analyzed using an X-Ray Microtomography System Skyscan 1072 scanner (Skyscan, Belgium) in a high-resolution mode with a pixel size of 11.3 µ m and integration time of 1.7 sec. The X-ray source was used at 35 keV energy and 215 µ A current. A binary picture was obtained through the transformation of representative data sets of 250 slices, using a dynamic threshold of 60e255 (grey values) in order to distinguish polymer material from pore voids.

1.3 Scanning Electron Microscopy (SEM) Gold coated (Cressington Sputter Coater, UK) GG-HA dried polymeric networks were analyzed by SEM using XL 30 ESEM-FEG microscope (Phillips, UK) at an accelerating voltage of 15 kV. 1.3.1 Cryo-SEM A JEOL JSM 6301F/Oxford INCA Energy 350/Gatan Alto 2500 microscope (JEOL, Japan) was used to analyze the micro-structure of spongy-like hydrogels and the hASCs organization within GG-HA spongy-like hydrogels. Samples were positioned on a vacuum transfer rod, slam-frozen to -210°C in N2 slush and moved to the cryostat chamber at -130°C. The top rivet was flicked off to produce a fractured surface that was sublimed at -90°C for 2 minutes and coated with gold/palladium.

1.4 Water uptake Water uptake measurements were carried out by immersing dried polymeric networks in αMEM culture medium up to seven days at 37 ºC. Samples were weighted initially (Wd) and then again 1, 3, 6, 9, 24, 48, 72, 96, 108 and 156 h post-immersion in culture medium, as spongy-like hydrogels, and after removal superficial liquid (Ww). Percentage of water uptake was obtained using the following equation: Water uptake (%) = (Ww – Wd)/Wd x 100. Wd – Weight of dried polymeric networks, Ww – Weight of spongy-like hydrogels 6 ACS Paragon Plus Environment

Page 7 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

2. Cell Isolation hASCs and hAMECs were both isolated from human subcutaneous adipose tissue obtained from liposuction procedures (3 different donors). Tissue samples were provided by Hospital da Prelada (Porto), after patient’s informed consent and 3B’s Research Group/Hospital ethical committees approval. After digestion with 0.05% Collagenase type II (Sigma, USA), a filtration and centrifugation at 800 g were performed and the stromal vascular fraction (SVF) obtained. The SVF pellet was incubated with red blood cell lysis buffer (155mM of ammonium chloride, 12 mM of potassium bicarbonate and 0.1M of ethylenediaminetetraacetic acid (all from SigmaAldrich, Germany) in distilled water) for 10 minutes at room temperature,and further centrifuged at 300g for 5 minutes. The red blood cells-free SFV was either resuspended in Alpha-MEM medium (Invitrogen, USA) containing 10% fetal bovine serum (FBS) (Invitrogen, USA) and 1% Antibiotic/Antimycotic (Invitrogen, USA), or in endothelial growth medium (EGM-2MV) (Lonza, USA), respectively for hASCS and hAMECs isolation. hASCs were selected by plastic adherence approximately 5 days after isolation. For both cell lineages cell culture medium was changed 48 hours after initial plating and every 3 days thereafter. hAMECs cultures in 0.7% gelatin coated flasks were at 90% confluence 7days post isolation. Both cell types were harvested with Tryple select (Invitrogen, USA).

3. Flow Cytometry

hASCs and hAMECs (both at P0) were resuspended in a 3% BSA solution and incubated at room temperature for 20 minutes with fluorescent labelled antibodies. hASCs were incubated with mouse anti-human antibodies CD105-FITC, CD73-PE, CD90-APC, CD45-FITC, CD34-PE and CD31-APC, and hAMECs with mouse-anti human CD31-APC, HLA-DR and CD34-PE antibodies (all BD Biosciences, Germany) at manufacturer recommended concentrations. Cells were subsequently washed with PBS, centrifuged, fixed with 1% paraformaldehyde and analysed in a FACs Calibur Flow Cytometer (BD Biosciences, USA) using the CELLQuest software V3.3.

4. Matrigel Assay

7 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 36

hAMECs were seeded at a concentration of 1.5 x104/per well on Matrigel (BD Biosciences, USA) prepared in 96 well-plates and incubated in EGM-2MV at 37ºC in a humidified incubator with 5% CO2 for 20 hours. Viable cells were then identified with calcein-AM (Invitrogen, USA) and their organization visualized under an inverted microscope (Zeiss, Germany) and an Axioplan Imager Z1M microscope (Zeiss, Germany). Images were acquired and processed with AxioVision V.4.8 software (Zeiss, Germany). 5. Uptake of acetylated low-density lipoprotein (DiI-Ac-LDL) To assess Dil-AC-LDL uptaked, hAMECs were cultured in 0.7% gelatin coated polystyrene coverslips. Upon reaching confluence, cells were incubated for four hours at 37ºC with 5% CO2 in EGM-2MV containing 5µg/mL of Dil-AC-LDL (Invitrogen, USA). After being washed with PBS and fixed in 3.7% (v/v) buffered formalin (Sigma, USA) for 1 hour at room temperature, hAMECs nuclei were stained with 4’,6-diamidino-2-phenylindole (DAPI, Invitrogen, USA) and samples were visualized under a AXIOIMAGER Z1M (Zeiss) microscope, using axiovision software. 6. Preparation of the constructs Two different types of constructs, one with hASCs entrapped (homotypic) and one with cocultured hASCs and hAMECs (heterotypic), were prepared in vitro. To obtain homotypic spongy-like hydrogels, hASCs were ressuspended in α-MEM medium in a concentration of 1x107 cell/mL. The heterotypic spongy-like hydrogels were prepared with heterotypic cell suspension combining hASCs (1 x 106 cell/mL) and hAMECs (5 x 106 cell/mL). For both constructs, 100µL of respective cell suspension was added to the GG-HA dried network structures. Constructs were incubated at 37ºC and 5% CO2 for 30 minutes to increase cell entrapment. Constructs were cultured in vitro for 2 days prior in vivo implantation in α-MEM medium and EGM-2MV (2 mL/per well).

7. In vivo implantation in mouse excisional wound healing model Sixty-four Swiss Nu/Nu male mice (Charles River Laboratories, France) were randomly divided into four groups, comprising the experimental GG-HA Spongy-like hydrogel (spongy-like

8 ACS Paragon Plus Environment

Page 9 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

hydrogel), GG-HA Spongy-like hydrogel with hASCs (homotypic), GG-HA Spongy-like hydrogel with hASCs and hAMECs (heterotypic) and the control group (control) without any material implanted. This study was conducted after approval by Direcção-Geral de Alimentação e Veterinária (DGAV), the Portuguese National Authority for Animal Health and all the surgical /necropsy procedures were performed according to the applicable national regulations that comprise international animal welfare rules Four animals were used per condition and per time point (3, 7, 14 and 21 days). Mice were anaesthetised with a mixture of Imalgene (ketamine) (75mg/Kg) (Merial Portuguesa, Portugal) plus Domitor (medetomidine) (1mg/kg) (Esteve Farma, LDA, Portugal). A 1.2 cm diameter full-thickness excision was performed in each mouse at approximately 0.5 cm caudal to the intra-scapular region. Spongy-like hydrogels constructs was placed on top of the wounds, which were covered with transparent dressing Hydrofilm (Hartmann, UK) and a final set of bandages. A subcutaneous injection of Depomedrol (20mg/Kg BW) (Pfizer,Portugal) was applied to the animals at days 0, 7 and 14, in order to delay wound healing 42. Mice were maintained in separated compartments throughout the experiments, euthanized by CO2 inhalation at the referred timepoints, and explants obtained for histological analysis.

8. Histological procedure Skin explants were collected at days 3, 7, 14, and 21, fixed in 10% formalin and embedded in paraffin. Representative sections were stained following routine protocols for H&E and Masson’s trichrome. Sections were analysed with a Axioplan Imager Z1m microscope, and images acquired and processed with AxioVision V.4.8 software. 9. Immunolabeling Immunostaining of hAMECs cultured in gelatin-coated coverslips, homotypic and heterotypic spongy-like hydrogels constructs, histological sections of in vivo explants were performed after fixation with 3.7% (v/v) buffered formalin, permeabilization with 0.2% TritonX-100 and blocking with 3% Bovine Serum Albumin (BSA) (Sigma, USA). Regarding paraffin embedded samples, sections were re-hydrated and antigen retrieval was performed with Tris-EDTA buffer (10mM Tris Base, 1mM EDTA Solution, 0.05% Tween 20, pH 9.0) (all Sigma, USA) before permeabilization and blocking. Primary antibodies CD31 (mouse anti-human, 1:30, Dako, Denmark), von Willebrand factor (vWF) (rabbit anti-human/mouse, 1:200, Dako, Denmark), and

9 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 36

CD31 (rabbit anti-human/mice, 1:20, Abcam, UK), and tagged secondary antibodies, rabbit anti-mouse Alexa-fluor 594 and donkey anti-rabbit Alexafluor 488 (1:500, invitrogen, USA), were used. VECTASTAIN Elite ABC Kit (Vector Labs, USA) was further employed for the detection of CD31, according to manufacturer’s instructions. Nuclei were stained either with DAPI (Invitrogen, USA) or Mayer’s hematoxylin. Phalloidin-TRITC (Sigma, USA) was used to stain cytoskeleton F-actin fibers in GG-HA spongy-like hydrogels constructs prior implantation. AXIOIMAGER Z1M or Olympus Fluoview FV1000 laser confocal microscope (Olympus, Japan) were used for visualization of the samples. 10. Quantification of collagen and non-collagenous proteins Sirius Red/Fast Green Collagen Staining Kit (Chondrex, Inc, USA) was used to quantify the amount of collagen and non-collagenous proteins in the histological sections of 21 days postoperative in vivo explants following manufacturer instructions.

Briefly, after being

deparifinized and rehydrated, sections were incubated with the solution of dye at room temperature for 30 minutes. Afterwards, sections were rinsed with water to eliminate excess of dye. Dye extraction solution was added until the color was eluted from the tissue section and OD was measured at 540 nm and 605 nm in a Synergy HT microplate reader (Biotek, USA).

11. Image Analysis 11.1 Wound Closure Assessment The percentage of wound closure was calculated by analysing the planimetric digital images taken at day 0, 7, 14 and 21 post-implantation for all four animals of each condition and time point, according to the following equation: (area of original wound – area of actual wound) / (area of original wound) x 100 Wound was considered completely closed when wound area was equal to zero.

11.2 Quantification of Vessels density and diameter The number and diameter of vessels were quantified at days 7 and 14 postoperative in the 10 ACS Paragon Plus Environment

Page 11 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

CD31 stained samples. Quantification and measurement were performed in randomly selected five high–power fields of five non-consecutive tissue sections per time point and per animal within each group. Only vessels with a diameter of < 50µm 43 were considered. Mean results of the number of vessels per field are expressed as vessels density.

11.3 Dermal Differentiation Newly formed skin quality was assessed after 21 days of implantation, through the quantification of the dermal differentiation on Masson’s Trichrome stained histological samples, according to criteria described by Sun et al. 15, using following criteria: grade 1, thin, dense, and monotonous fibrosis; 2, thicker but still dense and monotonous fibrosis; 3, two layers but not completely discreet; 4, two discreet layers with superficial fibrosis and loose alveolar tissue within the deep layer.

11.4 Epidermal thickness quantification The epidermal thickness was measured on H&E stained histological sections, of both experimental and control groups, explanted at day 21. Four tissue sections per animal within each group were examined after a random selection of five high-power fields per section and by performing 5 measurements of the epidermal thickness per field.

12. Statistic Analysis Statistical analysis of wound closure was performed using two-way ANOVA with Bonferroni post-tests, while for vessels diameter kruskal-wallis test, with Dunns post test was used. For vessel number, epidermal thickness, epithelial maturation and dermal differentiation one-way ANOVA with Tukey’s post-tests was employed (GraphPad Prism 4.02). Significance levels, determined using post tests between negative control and the three experimental groups, were set at: *p < 0.05, **p < 0.01, and ***p < 0.001.

RESULTS

11 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 36

1. Gellan Gum-Hyaluronic Acid spongy-like hydrogel constructs: elements properties and in vitro assembling GG-HA spongy-like hydrogels have been previously proposed 39-40 as cell-adhesive structures generated through a sequential processing method that includes stabilization, freezing, freezedrying and rehydration. GG-HA hydrogels (Fig. 1A) were freeze-dried giving rise to dried polymeric networks (Fig. 1 B) that in turn originated spongy-like hydrogels after re-hydration with any saline solution, as for example PBS (Fig. 1 C). The dried polymeric networks presented a highly interconnected porous microstructure with a pore size between 11.32 and 509.36 µm, as depicted by µ-CT (Fig. 1D) and SEM (Fig. 1E) analysis. Moreover, those structures were able to uptake about 2000% of water within 15 minutes when hydrated with culture medium (Fig. 1 F) thus forming the spongy-like hydrogels. The hydration equilibrium in cell culture medium was reached after 20 hours of incubation, at which the spongy-like hydrogels presented around 1500% of water content (Fig. 1F). Moreover, spongy-like hydrogels retain the attractive features of hydrogels and present advantages in relation to standard hydrogels that render them as interesting soft tissues ECM analogues 39-40. The phenotype of both the hASCs and hAMECs populations at passage 0, isolated from the same lipoaspirate sample and used to create the constructs, was analysed to confirm the respective mesenchymal and endothelial phenotypes. After flow cytometry analysis the expression of CD105, CD90 and CD73 by more than 90% of the hASCs and the neglectable expression of CD34, CD45 and CD31 markers was confirmed (Fig. 2A). Furthermore, around 90% of the hAMECs population expressed the CD31 endothelial characteristic marker (Fig. 2A). The endothelial phenotype of the hAMECs was further confirmed by the co-expression of CD31 and vWF by immunocytochemistry (Fig. 2B), as well as by the ability of the cells to uptake Dil-AC-LDL (Fig. 2C) and to form tubular-like structures on matrigel remaining viable, as confirmed by calcein-AM staining (Fig. 2D). In what concerns the expression of HLA-DR, while its expression was absent in the hASCs population, around 15% of the hAMECs were positive for that marker (Fig. 2A). Replicates of the constructs formed by hydration of the GG-HA dried polymeric networks at the time of seeding, thus entrapping/encapsulating the respective cells, were analysed after the in vitro culture aiming at providing insight on the interaction of the cells with the matrix and consequent arrangement prior implantation. Two days after entrapment, hASCs were adhered to the pore walls of the spongy-like hydrogel, as observed by cryo-SEM technique (Fig. 3A). This cellular interaction with the polymeric structure was further evidenced in confocal 12 ACS Paragon Plus Environment

Page 13 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

microscopy images, where the embossment of the shape of the cells on the material surface was clearly visualized (Fig. 3B). Moreover, hASCs exhibited their typical fibroblast-like morphology with an organized cytoskeleton in both homotypic (Fig. 3C) and heteroptypic constructs (Fig. 3D), while hAMECs, identified by vWF staining in the heterotypic construct, were found to interact with hASCs but not with the matrix (Fig. 3D).

2. Wound healing progression Wound closure macroscopic/qualitative analysis (Fig. 4i) and quantification (Fig. 4ii) performed along the implantation time allowed to assess the influence of the different test groups over wound closure rate. The percentage of wound closure was slightly higher in experimental groups than in the control at days 7 and 14, though a significant difference (p