Article

One-pot synthesis of LDH/GO composites as high effective adsorbent for the decontamination of U(VI) Wensheng Linghu, Hai Yang, Yanxia Sun, Guodong Sheng, and Yuying Huang ACS Sustainable Chem. Eng., Just Accepted Manuscript • Publication Date (Web): 10 May 2017 Downloaded from http://pubs.acs.org on May 17, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Sustainable Chemistry & Engineering is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

1

One-pot synthesis of LDH/GO composites as high effective adsorbent

2

for the decontamination of U(VI)

3

Wensheng Linghu†*, Hai Yang†, Yanxia Sun†, Guodong Sheng†, Yuying Huang‡

4



5

312000, P.R. China

6



7

Physics, Chinese Academy of Sciences, Shanghai 201204, P.R. China

8

*Corresponding authors: Email: [email protected] (Wensheng Linghu, No. 508

9

Huancheng Rd. Shaoxing)

College of Chemistry and Chemical Engineering, Shaoxing University, Zhejiang

Shanghai Synchrotron Radiation Facility (SSRF), Shanghai Institute of Applied

10

ABSTRACT: The removal mechanism of U(VI) on Mg-Al-layered double

11

hydroxides–supported graphene oxide (LDH/GO) composites was investigated by

12

batch, spectroscopic and surface complexation modeling. The batch experiments

13

showed that the enhanced removal of U(VI) on LDH and LDH/GO composites in the

14

presence of carbonate was observed at pH < 5.0, whereas the presence of carbonate

15

significantly inhibited U(VI) removal at pH starting from 7.0 to 9.0. It is demonstrated

16

that the oxygenated functional groups (i.e., -OH) were responsible for the high

17

effective removal of U(VI) by XPS analysis. The results of XANES and EXAFS

18

spectra indicated that adsorption of U(VI) on LDH/GO composites was inner-sphere

19

surface complexation. According to surface complexation modeling, the removal of

20

U(VI) on LDH/GO composites can be satisfactorily fitted by diffuse layer model with

21

an ion exchange (X2UO2), two inner-sphere surface complexes (SOUO2+ and

22

SOUO2(CO3)23- species). The maximum adsorption capacities of LDH and LDH/GO

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

23

composite calculated from Langmuir model at pH 4.5 and T = 293 K were 99.01 and

24

129.87 mg/g, respectively. These findings indicated that GO-based composites can be

25

used as a high effective adsorbent for the preconcentration and immobilization of

26

radionuclides in environmental cleanup.

27

KEYWORDS: Uranium, LDH, Graphene oxide, Modeling, Spectroscopic techniques

28

INTRODUCTION

29

With the rapid development of nuclear-relative industries, abundant radioactive

30

contaminants were discharged into sub-environments.1-3 Radionuclide contamination

31

is still problematic issues at nuclear facilities.4 Uranium is the typical and common

32

radioactive contaminant could lead to serious threats to ecological environments and

33

human health.5-8 Therefore, the removal of uranium from aqueous solutions has been

34

extensively investigated by various adsorbents such as Fe/Al-(hydr)oxide9-15

35

carbon-based materials7,

36

becoming increasingly common method to remove radionuclides.25-30 In hitherto

37

studies, the effect of environmental factors on the adsorption of radionuclides at the

38

water-solid interface had been elucidated by batch techniques.31-34

39

Owing to the abundant oxygenated functional groups (hydroxyl, epoxy and carboxyl

40

groups), graphene oxide (GO) as highly efficient adsorbent has been extensively

41

investigated to remove radionuclides in recent years.6, 35-40 However, the GO was not

42

easily separated from liquid-phase due to its excellent dispersity in aqueous solutions.

43

Layered double hydroxide (LDH, [MII1-xMIIIx(OH)2]x+(An-)x/n·mH2O) is typical

44

brucite-like layered hydroxides with divalent (MII) and trivalent (MIII) metal ions in

16-19

and clay minerals.1,

20-24

ACS Paragon Plus Environment

Adsorption approach is

Page 2 of 31

Page 3 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

45

the octahedron and n-valent anion (An-).41-44 LDH can be regarded the excellent

46

adsorbent in environmental cleanup due to its exchangeable capacity of anions. It is

47

determined that LDH/GO composites can be used as an excellent adsorbent, which

48

can be separated easily from liquid-phase.45 The contribution of GO in the LDH/GO

49

composites was to significantly enhance their adsorption performance. A thorough

50

understanding of the chemical interactions of U(VI) with LDH-based composites is

51

essential in building a robust safety case for the long-term geological disposal of

52

nuclear waste and for the management of radionuclide-bearing sites. Although the

53

removal of U(VI) on LDH/GO composites was investigated, the effect of carbonate

54

on the speciation and fate of U(VI) remains poorly understood.46

55

The aims of this manuscript were (1) to synthesize the LDH/GO composites and

56

characterize them by TEM, FT-IR and XRD techniques; (2) to investigate the effect of

57

environmental factors (e.g., reaction time, pH, carbonate concentration and

58

temperature) on U(VI) removal onto LDH and LDH/GO composites by batch

59

techniques; (3) to determine interaction mechanism of U(VI) and LDH and LDH/GO

60

composites at a molecular level by XPS, XANES, EXAFS and surface complexation

61

modeling. This manuscript highlighted the application of GO-based composites for

62

removal of radionuclides in environmental cleanup.

63

MATERIALS AND METHODS

64

Synthesis of LDH/GO Composites. The LDH/GO composites were synthesized by a

65

hydrothermal process.43 Firstly, the GO was obtained by the oxidation of flake

66

graphite (< 30 micros, Qingdao, China) under the concentrated H2SO4 conditions.47

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 31

67

Briefly, 1.0 g graphite and 0.5 g NaNO3 were added into 100 mL fuming sulphric acid

68

under ice-bath conditions. Then 4.5 g KMnO4 was slowly added the aforementioned

69

suspension, and MnO4- was eliminated by adding 6 mL of H2O2 solution. Then, 7.8

70

mmol MgCl2·6H2O, 2.6 mmol AlCl3·6H2O and 9.2 mmol hexamethylene tetramine

71

were added into 20 mL 2.0 g/L GO solutions under vigorous stirring conditions for 1

72

h. The aforementioned suspensions were transferred into 50 mL Teflon-lined

73

stainless- steel autoclave and then were heated at 140 °C for 12 h. After cooled to

74

room temperature, the black slurries were washed with Milli-Q water and

75

centrifugation it several times. The LDH/GO composites were obtained by drying it at

76

vacuum oven at 60 °C overnight. To identify the contribution of GO, the LDH/GO2

77

composited was also synthesized by adding the same amount of Mg2+ and Al3+ into

78

the twice concentration of GO solution (20 mL 4.0 g/L) under the same experimental

79

conditions.

80

UO2(NO3)2.6H2O (analytical purity, Sigma-Aldrich) into 0.01 mol/L HNO3 solution

81

under glovebox conditions.

82

Characterization. The morphology of as-prepared LDH/GO composites was

83

characterized by TEM (JEOL-2010 microscope). The surface groups of LDH/GO

84

composites were determined by FT-IR (Nicolet Magana-IR 750 spectrometer) from

85

400 to 4000 cm-1. The mineralogy of as-prepared composites were recorded by XRD

86

pattern (Philips X’Pert Pro Super X-ray Diffractometer) with Cu-Kα radiation

87

(λ=1.5416 Å). The change in surface electron state of LDH/GO composites was

88

performed by XPS (VG Scientific ESCALAB Mark II spectrometer) equipped with

The

stock

solutions

of

U(VI)

were

prepared

ACS Paragon Plus Environment

by

dissolving

Page 5 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

89

an Mg Kα radiation source (1253.6 eV) at 10 kV and 5 mA under 10-8 Pa residual

90

pressure. Surface charging effects were corrected with the C 1s peak at 284.6 eV as a

91

reference.

92

Batch Adsorption. The triple adsorption experiments of U(VI) on LDH and LDH/GO

93

composites (m/v = 1.5 g/L) were conducted in polycarbonate centrifuge tubes at pH

94

4.5 and in presence of 0.01 mol/L NaClO4 solutions (as an inert anion). Briefly, the

95

suspension of LDH/GO composites were pre-equilibrated with NaClO4 solutions

96

overnight, and then U(VI) solution was provided to reach the desired concentration.

97

The pH value of suspensions was adjusted by adding negligible volumes of 0.01-1.0

98

mol/L HClO4 or NaOH solution. After equilibrium, the solid phase was separated

99

from liquid phase by centrifugation at 5000 rpm for 30 min and then filtered using

100

0.22 µm nylon membrane filters. The recycling experiments were conducted 6

101

successive cycles by U(VI) adsorption- desorption experiments. Briefly, after U(VI)

102

adsorption, UVI)-containing wet solid phase was orderly desorbed by adding 0.01

103

mol/L HNO3, 0.2 mol/LNa2CO3 and 0.01 mol/L EDTA solutions.23 The concentration

104

of U(VI) in supernatant was measured by inductively coupled plasma-mass

105

spectrometry (ICP-MS, Agilent 7500CX, USA). The adsorbed amount of U(VI) on

106

LDH/GO composites can be calculated by the difference of the initial and equilibrated

107

concentration.

108

Surface Complexation Modeling. The modeling approach allowed for a clear

109

determination of the reactive surface sites of LDH/GO composites for U(VI)

110

adsorption. Diffuse layer model of surface complexation modeling was done by visual

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 31

111

MINETQ program.48 Equilibrium constants for surface complexes were obtained by

112

simulating adsorption edges for three surface complexation reactions. The speciation

113

was used by mass balance constraints to optimize the equilibrium constants. The

114

equilibrium constants were obtained from the apparent stability constants by

115

converting the concentration of each surface species to its mole fraction.

116

Preparation and Analysis of XANES and EXAFS spectra. The samples for

117

XANES and EXAFS analysis were prepared in the golvebox (purged with 95 % N2

118

and 5 % H2). Briefly, the suspension of LDH/GO composites was pre-equilibrated

119

with NaClO4 (0.01 mol/L) 24 h, then UO22+ solutions were slowly added into

120

aforementioned suspension under vigorous stirring conditions. The values of pH in

121

aqueous solutions were adjusted to 3.0 and 6.0 by adding 0.01-1.0 mol/L HCl and/or

122

NaOH solutions. After reaction 2 days, the wet solid phase was obtained by

123

centrifuging the suspension at 9800 rpm for 20 min. Then wet pastes were mounted in

124

Teflon sample holders sealed with Kapton tape. The uranium L3-edge XANES and

125

EXAFS

126

uranium-containing LDH/GO at different pH conditions were performed with Si(111)

127

double-crystal monochromator at the BL14W1 beamline of Shanghai Synchrotron

128

Radiation Facility (SSRF, Shanghai, China). All spectra were conducted in

129

fluorescenc mode expect for crystalline U(IV)O2(s), which was recorded in

130

transmission mode. The fitting of EXAFS data were carried out by Athena and

131

Artemis interfaces of IFFEFIT 7.0 mode.49, 50

132

RESULTS AND DISCUSSION

spectra

for

reference

standards

(e.g.,

U(IV)O2(s),

ACS Paragon Plus Environment

U(VI)O22+)

and

Page 7 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

133

Characterization. The morphology of LDH/GO composites was characterized by

134

TEM image. The hexagonal LDH platelets with 20 nm thicknesses revealed the good

135

crystallinity due to slow nucleation process (Figure 1A). As shown in Figure 1B, the

136

LDH nanoplates were uniformly deposited on the surface of GO nanosheets, which

137

was consistent with the previous studies.43, 51 Figure 1C shows the FT-IR spectrum of

138

LDH/GO composites. The significant peaks at 3450 and 1365 cm-1 could be ascribed

139

to the stretching vibration of O-H groups associated with the interlayer water

140

molecules and CO32- ions in the interlayer of Mg/Al LDH, respectively.43 However,

141

the bands at 1730, 1620 and 1220 cm-1 were attributed to the stretching vibration of

142

C=O, C=C, C-O groups of GO, respectively.17, 26, 52 The abundant bands at 500-800

143

cm-1 could be due to the stretching/bending vibrations of metal-oxygen lattices such

144

as Mg/Al-O, O-Mg/Al-O, and Mg/Al-O-Mg/Al groups.46 The result of FT-IR

145

spectrum showed that LDH nanoplate was successfully synthesized on the GO surface,

146

moreover the oxygenated functional groups of GO provided the much more reactive

147

sites for U(VI) removal. As shown by XRD pattern in Figure 1D, the diffraction peaks

148

at 2θ= 11.5, 23.6, 35.1, 39.5, 47.2, 60.8 and 62.2° can be indexed into the (003), (006),

149

(012), (015), (018), (110) and (113) planes of Mg/Al LDH (JCPDS No. 15-0087),

150

respectively.53 No diffraction peaks of GO (e.g., (002) plane of GO at 9.12) and other

151

impurities were observed. In additions, sharp and symmetric peaks revealed the high

152

crystallization. As shown in Table 1, the N2-BET specific surface area and average

153

pore size of as-prepared LDH/GO composites were calculated to be 28.73 m2/g and

154

3.2 nm, respectively, which were lower than that of LDH (45.64 m2/g and 3.8 nm for

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

155

specific surface area and average pore size, respectively). The characteristic results

156

indicated the occurrence of abundant oxygen-containing functional groups of

157

LDH/GO composites.

158

Effect of pH and Carbonate Concentration. Figure 2A shows the adsorption of

159

U(VI) on LDH and LDH/GO composites at different pH conditions. One can see that

160

the slight increase in U(VI) adsorption on LDH was observed at pH < 4.0, whereas

161

the adsorption of U(VI) on LDH was significantly increased at pH 4.0 – 6.5, and then

162

kept the high-level adsorption at pH 6.5-7.5. The decreased adsorption of U(VI) on

163

LDH was discerned at pH > 8.0. For LDH/GO composites, the significant increase of

164

U(VI) adsorption was observed at pH 2.0-5.0, and then remained the adsorption of

165

U(VI) at pH 5.0-8.0, whereas the slight decrease of U(VI) adsorption was found at

166

pH > 8.5. At pH 6.0, approximately 91 and 99.8 % of U(VI) was removed by LDH

167

and LDH/GO composites, respectively. Compared to LDH, the pH-edge adsorption of

168

U(VI) on LDH/GO composites was shifted to the lower pH values. These results

169

indicated that the GO enhanced the adsorption of U(VI). Figure 2B shows the effect

170

of carbonate concentration on adsorption of U(VI) onto LDH and LDH/GO

171

composites. At pH < 5.0, the adsorption of U(VI) on LDH and LDH/GO composites

172

in the presence of carbonate was significantly higher than that of U(VI) on LDH and

173

LDH/GO composites in the absence of carbonate. However, the carbonate inhibited

174

the adsorption of U(VI) on LDH and LDH/GO composites at pH > 7.0. It is

175

demonstrated the negative carbonato- uranyl complexes (i.e., UO2(CO3)22- and

176

UO2(CO3)34- species) was obtained in the presence of carbonate conditions.14, 20 As

ACS Paragon Plus Environment

Page 8 of 31

Page 9 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

177

shown in Table 1, the pHPZC (pH at point of zero charge) of LDH and LDH/GO

178

composites were calculated to be 7.1 and 6.5, respectively. Therefore, the increased

179

adsorption of U(VI) on LDH and LDH/GO composites in the presence of carbonate

180

could be attributed to the electrostatic attraction between positive charged of LDH and

181

LDH/GO composites and negative charged of carbonato-uranyl complexes at pH
7.0 could be ascribed the electrostatic repulsion between negative charged of

184

LDH and LDH/GO composites and negative charged of carbonato-uranyl complexes.

185

The high-level adsorption of U(VI) on LDH and LDH/GO composites at pH 6.0- 7.0

186

could be surface co-precipitation and/or surface complexation reaction of U(VI) with

187

LDH and LDH/GO composites.

188

Adsorption Kinetics and Isotherms. Figure 3A and 3B shows the adsorption

189

kinetics and isotherms of U(VI) on LDH and LDH/GO composites, respectively. As

190

shown in Figure 3A, the remarkable increase of U(VI) adsorption on LDH and

191

LDH/GO composites was observed with in reaction time of 6 h, and then kept the

192

high-level adsorption at reaction time more than 6 h. Approximately 100 % and 86 %

193

of U(VI) were removed by LDH/GO composites and LDH, respectively. The kinetic

194

data were fitted by pseudo-first and pseudo-second order kinetic models. The linear

195

forms of pseudo-first and pseudo-second order kinetic models can be described by

196

Eqns. (1) and (2): respectively:

197

ln(qe - qt) =lnqe - kf×t

(1)

198

t/qt = 1/(ks×qe2) + t/qe

(2)

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 31

199

where qe and qt (mg/g) were the amount of U(VI) adsorbed at equilibrium and at time

200

t, respectively. kf and ks referred to the rate constants of pseudo-first and

201

pseudo-second order kinetic model, respectively. The optimized parameters of

202

pseudo-first and pseudo-second order kinetic model were shown in Table 2. As shown

203

in Table 2, the removal kinetics of of U(VI) on LDH and LDH/GO composites can be

204

satisfactorily simulated by pseudo-second-order kinetic model with high correlation

205

coefficients (R2 =1) compared to pseudo-first-order kinetic model (R2 < 0.6), which

206

were consistent with previous studies.54, 55

207

Figure 3B shows removal isotherms of U(VI) on LDH and LDH/GO composites. It is

208

observed that removal of U(VI) on LDH was significantly lower than that of

209

LDH/GO composites. It should be noted that the U(VI) on LDH/GO composites was

210

lower than that LDH/GO2 composites, indicating that the U(VI) removal increased

211

with increasing GO concentration. The data of removal isotherms were simulated by

212

Langmuir and Freundlich models. The equations of Langmuir and Freundlich models

213

can be described by Eqns. (3) and (4), respectively:

214

Ce / Qe = 1/ (KL×Qm) + Ce / Qm

215

log Qe = log KF + 1/n log Ce

216

where Ce (mg/L) and Qm (mg/g) are equilibrated concentration and the maximum

217

removal capacity of LDH or LDH/GO composites at complete monolayer coverage.

218

KL (L/mg) and KF are a Langmuir and Freundlich constant, respectively. 1/n is the

219

heterogeneity of the adsorption sites. All parameters of Langmuir and Freundlich

220

model were showed in Table 3. As shown in Table 3, the adsorption of U(VI) on LDH

ACS Paragon Plus Environment

(3) (4)

Page 11 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

221

and LDH/GO composites can be satisfactorily fitted by Langmuir model. The

222

maximum adsorption capacities of LDH and LDH/GO composites calculated from

223

Langmuir model at pH 4.5 and 293 K were 99.01 and 129.87 mg/g, respectively,

224

which indicated that the introduction of GO in LDH/GO composites can significantly

225

increase the maximum adsorption capacity of LDH. As compared in Table 4, the

226

maximum adsorption capacity of LDH/GO composites was significantly higher than

227

that of metal (hydr)oxides (e.g., 11.6, 5.59 and 50.62 mg/g for nanoporous alumina9,

228

hematite56 and ferrihydrite57, respectively) and carbon-based nanoparticles (e.g., 26.18

229

and 97.5 mg/g for multiwalled carbon nanotubes58 and GO59, respectively). Therefore,

230

LDH/GO composites can be regarded as a promising adsorbents for the removal and

231

immobilization of U(VI) from aqueous solutions at low pH condition.

232

Figure 4A and 4B show the recycling experiments of U(VI) removal on LDH and

233

LDH/GO composites, respectively. After 6 recycling experiments, the decreased

234

extent of maximum adsorption capacity for LDH/GO composites (from 129.87 to

235

108.45 mg/g) was slightly lower than that of GO composites (from 99.01 to 72.69

236

mg/g), indicating that LDH/GO composites can be long-term use in the wastewater

237

treatment. The results of recycling experiments revealed that LDH/GO composites

238

can be used as environmentally renewable and low cost adsorbent due to the presence

239

of the excellent capacity of regeneration and the efficient performance.

240

XPS Analysis. Figure 5A and 5B show the total scan and high resolution U 4f XPS

241

analysis of LDH/GO composites before and after U(VI) removal, respectively. As

242

shown the total survey spectra in Figure 5A, there are four predominant elements of

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

243

LDH/GO composites (i.e., C 1s, O 1s, Al 2p and Mg 2p) before U(VI) adsorption,

244

whereas the weak U 4f peaks and the decreased relative intensity of O 1s were

245

observed after U(VI) adsorption. These evidence indicated that U(VI) was attached on

246

the surface of LDH/GO composites. After U(VI) desorption, the relative intensity of

247

O 1s was significantly higher than that of O 1s after U(VI) adsorption, indicating that

248

oxygen-containing functional groups were responsible for the high effective

249

adsorption of U(VI) on LDH/GO composites. As shown in Figure 5B, the U 4f peaks

250

can be deconvoluted into two sub-peaks at ~ 381 and 392 eV, which were

251

corresponded to U 4f7/2 and U 4f5/2, respectively.14 The results of XPS analysis

252

indicated that the adsorption of U(VI) on LDH/GO composites was attributed to the

253

abundant oxygen-containing functional groups of GO.

254

Surface Complexation Modeling. Figure 6A and 6B show the surface complexation

255

modeling of U(VI) on LDH and LDH/GO composites using double layer model,

256

respectively. The optimized parameters of surface complexation modeling were

257

summarized in Table 5. It is observed that the adsorption of U(VI) on LDH and

258

LDH/GO composites can be satisfactorily fitted by double layer model with a cation

259

exchange sites (X2UO2) and two inner-sphere complexation sites (SOUO2+ and

260

SOUO2(CO3)23- species) at pH < 7.0, whereas the fitted results under-evaluated the

261

experimental data at pH > 8.0 . As shown in Figure 6A and 6B, the X2UO2 species

262

was observed at pH < 4.0, whereas SOUO2+ and SOUO2(CO3)23- species dominated

263

the adsorption of U(VI) on LDH at pH 4.0-6.0 and pH > 6.0, respectively. However,

264

the main species of U(VI) adsorption on LDH/GO composites were SOUO2+ and

ACS Paragon Plus Environment

Page 12 of 31

Page 13 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

265

SOUO2(CO3)23- species at pH < 4.0 and pH > 5.0, respectively. The results of surface

266

complexation modeling indicated that the adsorption of U(VI) on LDH and LDH/GO

267

composites at pH < 4.0 was cation exchange. However, the adsorption of U(VI) on

268

LDH and LDH/GO composites at pH > 5.0 was inner-sphere surface complexation.

269

XANES and EXAFS Analysis. Figure 7A and 7B show the uranium L3-edge

270

XANES and EXAFS spectra of standards (U(IV)O2(s), U(VI)O22+) and uranium-

271

containing LDH/GO at different pH conditions, respectively. As shown in Figure 7A,

272

the positions of adsorption edge for U(IV)O2(s) and U(VI)O22+ were ~17174 and 17176

273

eV, respectively. The position and type of uranium-containing LDH/GO was

274

consistent with U(VI)O22+ standard, indicating that uranium redox states in LDH/GO

275

composites was U(VI) species. The results of XANES spectra revealed that the

276

removal of U(VI) on LDH/GO composites was mainly adsorption without reduction.

277

The uranium L3-edge EXAFS spectra for uranium-containing LDH/GO composites at

278

different pH were showed in Figure 7B. Table 6 summarized the optimized

279

parameters (e.g., sub-shell, coordination number, Debye-Waller factor) of fitting

280

results. Attempt to distinguish U-Oeq shell into two sub-shell (e.g., U-Oeq1 and

281

U-Oeq2) resulted to the convergence of two sub-shell at the similar bond distance,

282

therefore only U-Oeq shell were obtained in this study. As shown in Figure 7B, the FT

283

features of uranium-containing samples and reference standard at ca. 1.45 and 1.95 Å

284

can be satisfactorily fitted by two axial oxygen (U-Oax) at ca. 1.8 Å and ~ five

285

equatorial oxygen (U-Oeq) at ~ 2.35 Å (Table 6), respectively.60 The EXAFS spectra

286

of uranium-containing LDH/GO composites at pH 3.0 and pH 6.0 were significantly

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

287

different from EXAFS spectra of UO22+ species. For LDH/GO composites at pH 3.0

288

and pH 6.0, the third FT features can be simulated by ~ 1.3 alumina/magnesium

289

(U-Al/Mg shell) at ~ 3.18 Å (Table 6).20 Moreover, the coordination number of U-Mg

290

shell decreased with increasing pH from 3.0 to 6.0 (CN = 1.22 and 1.20 for pH 3.0

291

and 6.0, respectively). The results of EXAFS spectra indicated that inner-sphere

292

surface complexation dominated the removal of U(VI) on LDH/GO composites,

293

which was consistent with the batch adsorption experiments.

294

CONCLUSIONS

295

The LDH/GO composites were successfully synthesized by hydrothermal method.

296

The adsorption kinetics and isotherms of U(VI) on LDH and LDH/GO composites

297

can be satisfactorily fitted pseudo-second-order kinetic and Langmuir model,

298

respectively. The adsorption of U(VI) on LDH and LDH/GO composites at pH < 5.0

299

significantly increased with increasing carbonate concentration, whereas the

300

carbonate accumulated the desorption of U(VI) from LDH and LDH/GO composites

301

at pH 7.0-9.0. According to XPS analysis, oxygen-containing functional groups were

302

responsible for the adsorption of U(VI) on LDH/GO composites. The results of

303

surface complexation modeling indicated that the adsorption of U(VI) on LDH and

304

LDH/GO composites at pH < 4.0 and pH > 5.0 was cation exchange and inner-sphere

305

surface complexation, respectively. These observations indicated that LDH/GO

306

composites can be a promising adsorbent for the high efficient adsorption of

307

radionuclide from aqueous solutions in environmental cleanup.

308

Acknowledgements

ACS Paragon Plus Environment

Page 14 of 31

Page 15 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

309

This work was supported by the Shaoxing University of Research Startup Project

310

(20155029).

311

References

312 313 314 315 316 317 318 319 320 321 322 323 324 325 326 327 328 329 330 331 332 333 334 335 336 337 338 339 340 341 342 343 344 345 346 347 348 349

[1] Y.B. Sun, J.X. Li, X.K. Wang, The retention of uranium and europium onto sepiolite investigated by macroscopic, spectroscopic and modeling techniques, Geochim. Cosmochim. Acta, 140 (2014) 621-643. [2] G. Sheng, P. Yang, Y. Tang, Q. Hu, H. Li, X. Ren, B. Hu, X. Wang, Y. Huang, New insights into the primary roles of diatomite in the enhanced sequestration of UO22+ byzerovalent iron nanoparticles: An advanced approach utilizing XPS and EXAFS, Appl. Catal. B, 193 (2016) 189-197. [3] S.T. Yang, D.L. Zhao, G.D. Sheng, Z.Q. Guo, Y.B. Sun, Investigation of solution chemistry effects on sorption behavior of radionuclide Cu-64(II) on illite, J. Radioanal. Nucl. Chem., 289 (2011) 467-477. [4] X.X. Wang, Q.H. Fan, S.J. Yu, Z.S. Chen, Y.J. Ai, Y.B. Sun, A. Hobiny, A. Alsaedi, X.K. Wang, High sorption of U(VI) on graphene oxides studied by batch experimental and theoretical calculations, Chem. Eng. J., 287 (2016) 448-455. [5] Q. Wang, L. Chen, Y.B. Sun, Removal of radiocobalt from aqueous solution by oxidized MWCNT, J. Radioanal. Nucl. Chem., 291 (2012) 787-795. [6] Y.B. Sun, S.T. Yang, G.D. Sheng, Z.Q. Guo, X.K. Wang, The removal of U(VI) from aqueous solution by oxidized multiwalled carbon nanotubes, J. Environ. Radioact., 105 (2012) 40-47. [7] Y.B. Sun, Z.-Y. Wu, X.X. Wang, C.C. Ding, W.C. Cheng, S.-H. Yu, X.K. Wang, Macroscopic and microscopic investigation of U(VI) and Eu(III) adsorption on carbonaceous nanofibers, Environ. Sci. Technol., 50 (2016) 4459-4467. [8] G. Sheng, J. Hu, A. Alsaedi, W. Shammakh, S. Monaquel, F. Ye, H. Li, Y. Huang, A.S. Alshomrani, T. Hayat, B. Ahmad, Interaction of uranium (VI) with titanate nanotubes by macroscopic and spectroscopic investigation, J. Mol. Liq., 212 (2015) 563-568. [9] Y.B. Sun, S.T. Yang, G.D. Sheng, Z.Q. Guo, X.L. Tan, J.Z. Xu, X.K. Wang, Comparison of U(VI) removal from contaminated groundwater by nanoporous alumina and non-nanoporous alumina, Sep. Purif. Technol., 83 (2011) 196-203. [10] Y.B. Sun, S.B. Yang, Q. Wang, A. Alsaedi, X.K. Wang, Sequestration of uranium on fabricated aluminum co-precipitated with goethite (Al-FeOOH), Radiochim. Acta, 102 (2014) 797-804. [11] Y.B. Sun, Q. Wang, S.T. Yang, G.D. Sheng, Z.Q. Guo, Characterization of nano-iron oxyhydroxides and their application in UO22+ removal from aqueous solutions, J. Radioanal. Nucl. Chem., 290 (2011) 643-648. [12] Y.B. Sun, C.L. Chen, X.L. Tan, D.D. Shao, J.X. Li, G.X. Zhao, S.B. Yang, Q. Wang, X.K. Wang, Enhanced adsorption of Eu(III) on mesoporous Al2O3/expanded graphite composites investigated by macroscopic and microscopic techniques, Dalton Trans., 41 (2012) 13388-13394.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

350 351 352 353 354 355 356 357 358 359 360 361 362 363 364 365 366 367 368 369 370 371 372 373 374 375 376 377 378 379 380 381 382 383 384 385 386 387 388 389 390 391 392 393

[13] C.C. Ding, W.C. Cheng, Y.B. Sun, X.K. Wang, Novel fungus-Fe3O4 bio-nanocomposites as high performance adsorbents for the removal of radionuclides, J. Hazard. Mater., 295 (2015) 127-137. [14] C.C. Ding, W.C. Cheng, Y.B. Sun, X.K. Wang, Effects of Bacillus subtilis on the reduction of U(VI) by nano-Fe0, Geochim. Cosmochim. Acta, 165 (2015) 86-107. [15] C.C. Ding, W.C. Cheng, Z.X. Jin, Y.B. Sun, Plasma synthesis of beta-cyclodextrin/Al(OH)3 composites as adsorbents for removal of UO22+ from aqueous solutions, J. Mol. Liq., 207 (2015) 224-230. [16] Y.B. Sun, S.B. Yang, C.C. Ding, Z.X. Jin, W.C. Cheng, Tuning the chemistry of graphene oxides by a sonochemical approach: application of adsorption properties, RSC Adv., 5 (2015) 24886-24892. [17] Y.B. Sun, S.B. Yang, Y. Chen, C.C. Ding, W.C. Cheng, X.K. Wang, Adsorption and desorption of U(VI) on functionalized graphene oxides: A combined experimental and theoretical study, Environ. Sci. Technol., 49 (2015) 4255-4262. [18] C.C. Ding, W.C. Cheng, Y.B. Sun, X.K. Wang, Determination of chemical affinity of graphene oxide nanosheets with radionuclides investigated by macroscopic, spectroscopic and modeling techniques, Dalton Trans., 43 (2014) 3888-3896. [19] W.C. Cheng, M.L. Wang, Z.G. Yang, Y.B. Sun, C.C. Ding, The efficient enrichment of U(VI) by graphene oxide-supported chitosan, RSC Adv., 4 (2014) 61919-61926. [20] Y.B. Sun, R. Zhang, C.C. Ding, X.X. Wang, W.C. Cheng, C.L. Chen, X.K. Wang, Adsorption of U(VI) on sericite in the presence of Bacillus subtilis: A combined batch, EXAFS and modeling techniques, Geochim. Cosmochim. Acta, 180 (2016) 51-65. [21] S.H. Lu, J.S. Hu, C.L. Chen, C.J. Chen, G. Yu, Y.B. Sun, X.L. Tan, Spectroscopic and modeling investigation of efficient removal of U(VI) on a novel magnesium silicate/diatomite, Sep. Purif. Technol., 174 (2017) 425-431. [22] J.Y. Huang, Z.W. Wu, L.W. Chen, Y.B. Sun, The sorption of Cd(II) and U(VI) on sepiolite: A combined experimental and modeling studies, J. Mol. Liq., 209 (2015) 706-712. [23] W.C. Cheng, C.C. Ding, Y.B. Sun, X.K. Wang, Fabrication of fungus/attapulgite composites and their removal of U(VI) from aqueous solution, Chem. Eng. J., 269(2015) 1-8. [24] W.C. Cheng, C.C. Ding, Y.B. Sun, M.L. Wang, The sequestration of U(VI) on functional beta-cyclodextrin-attapulgite nanorods, J. Radioanal. Nucl. Chem., 302 (2014) 385-391. [25] H. J. Yan, J. W. Bai, X. Chen, J. Wang, H. S. Zhang, Q. Liu, M. L. Zhang, L. H. Liu, High U(VI) adsorption capacity by mesoporous Mg(OH)2 deriving from MgO hydrolysis. RSC Adv., 2013, 3, 23278-23289. [26] Y.B. Sun, Q. Wang, C.L. Chen, X.L. Tan, X.K. Wang, Interaction between Eu(III) and graphene oxide nanosheets investigated by batch and extended X-ray absorption fine structure spectroscopy and by modeling techniques, Environ. Sci. Technol., 46 (2012) 6020-6027. [27] H.B. Liu, Y.K. Zhu, B. Xu, P. Li, Y.B. Sun, T.H. Chen, Mechanical investigation of U(VI) on pyrrhotite by batch, EXAFS and modeling techniques, J. Hazard. Mater., 322 (2017) 488-498.

ACS Paragon Plus Environment

Page 16 of 31

Page 17 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

394 395 396 397 398 399 400 401 402 403 404 405 406 407 408 409 410 411 412 413 414 415 416 417 418 419 420 421 422 423 424 425 426 427 428 429 430 431 432 433 434 435 436 437

[28] Z.X. Jin, X.X. Wang, Y.B. Sun, Y.J. Ai, X.K. Wang, Adsorption of 4-n-nonylphenol and bisphenol-A on magnetic reduced graphene oxides: A combined experimental and theoretical studies, Environ. Sci. Technol., 49 (2015) 9168-9175. [29] C.C. Ding, W.C. Cheng, X.X. Wang, Z.-Y. Wu, Y.B. Sun, X.K. Wang, S.-H. Yu, Competitive sorption of Pb(II), Cu(II) and Ni(II) on carbonaceous nanofibers: a spectroscopic and modeling approach, J. Hazard. Mater., 313 (2016) 253-261. [30] W.C. Cheng, C.C. Ding, X.X. Wang, Z.-Y. Wu, Y.B. Sun, S.-H. Yu, T. Hayat, X.K. Wang, Competitive sorption of As(V) and Cr(VI) on carbonaceous nanofibers, Chem. Eng. J., 293 (2016) 311-318. [31] G. Sheng, Y. Tang, W. Linghu, L. Wang, J. Li, H. Li, X. Wang, Y. Huang, Enhanced immobilization of ReO4- by nanoscale zerovalent iron supported on layered double hydroxide via an advanced XAFS approach: Implications for TcO4- sequestration, Appl. Catal. B, 192 (2016) 268-276. [32] G. Sheng, J. Hu, H. Li, J. Li, Y. Huang, Enhanced sequestration of Cr(VI) by nanoscale zero-valent iron supported on layered double hydroxide by batch and XAFS study, Chemosphere, 148 (2016) 227-232. [33] H. Dong, Y. Chen, G. Sheng, J. Li, J. Cao, Z. Li, Y. Li, The roles of a pillared bentonite on enhancing Se(VI) removal by ZVI and the influence of co-existing solutes in groundwater, J. Hazard. Mater., 304 (2016) 306-312. [34] D. Zhao, G. Sheng, C. Chen, X. Wang, Enhanced photocatalytic degradation of methylene blue under visible irradiation on graphene@TiO2 dyade structure, Appl. Catal. B, 111 (2012) 303-308. [35] G. Sheng, Y. Li, X. Yang, X. Ren, S. Yang, J. Hu, X. Wang, Efficient removal of arsenate by versatile magnetic graphene oxide composites, RSC Adv., 2 (2012) 12400-12407. [36] Y.B. Sun, X.X. Wang, W.C. Song, S.H. Lu, C.L. Chen, X.K. Wang, Mechanistic insights into the decontamination of Th(IV) on graphene oxide-based composites by EXAFS and modeling techniques, Environ. Sci. Nano, 4 (2017) 222-232. [37] Y.B. Sun, X.X. Wang, Y.J. Ai, Z.M. Yu, W. Huang, C.L. Chen, T. Hayat, A. Alsaedi, X.K. Wang, Interaction of sulfonated graphene oxide with U(VI) studied by spectroscopic analysis and theoretical calculations, Chem. Eng. J., 310 (2017)292-299. [38] W.C. Song, T.T. Yang, X.X. Wang, Y.B. Sun, Y.J. Ai, G.D. Sheng, T. Hayat, X.K. Wang, Experimental and theoretical evidence for competitive interactions of tetracycline and sulfamethazine with reduced graphene oxides, Environ. Sci. Nano, 3 (2016) 1318-1326. [39] Y.B. Sun, C.C. Ding, W.C. Cheng, X.K. Wang, Simultaneous adsorption and reduction of U(VI) on reduced graphene oxide-supported nanoscale zerovalent iron, J. Hazard. Mater., 280 (2014) 399-408. [40] Y.B. Sun, C.L. Chen, D.D. Shao, J.X. Li, X.L. Tan, G.X. Zhao, S.B. Yang, X.K. Wang, Enhanced adsorption of ionizable aromatic compounds on humic acid-coated carbonaceous adsorbents, RSC Adv., 2 (2012) 10359-10364. [41] Y.D. Zou, X.X. Wang, Y.J. Ai, Y.H. Liu, J.X. Li, Y.F. Ji, X.K. Wang, Coagulation behavior of graphene oxide on nanocrystallined Mg/AI layered double hydroxides: Batch experimental and theoretical calculation study, Environ. Sci. Technol., 50 (2016)

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

438 439 440 441 442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 458 459 460 461 462 463 464 465 466 467 468 469 470 471 472 473 474 475 476 477 478 479 480 481

3658-3667. [42] J.Z. Zhou, Y.Y. Wu, C. Liu, A. Orpe, Q.A. Liu, Z.P. Xu, G.R. Qian, S.Z. Qiao, Effective self-purification of polynary metal electroplating wastewaters through formation of layered double hydroxides, Environ. Sci. Technol., 44 (2010) 8884-8890. [43] T. Wen, X. Wu, X. Tan, X. Wang, A. Xu, One-pot synthesis of water-swellable Mg-Al layered double hydroxides and graphene oxide nanocomposites for efficient removal of As(V) from aqueous solutions, ACS Appl. Mater. Interface, 5 (2013) 3304-3311. [44] C. Wang, J. Gao, C. Gu, Rapid Destruction of Tetrabromobisphenol A by iron(III)-tetraamidomacrocyclic ligand/layered double hydroxide composite/H2O2 System, Environ. Sci. Technol., 51 (2017) 488-496. [45] J. Wang, X. Wang, L. Tan, Y. Chen, T. Hayat, J. Hu, A. Alsaedi, B. Ahmad, W. Guo, X. Wang, Performances and mechanisms of Mg/Al and Ca/Al layered. double hydroxides for graphene oxide removal from aqueous solution, Chem. Eng. J., 297(2016) 106-115. [46] L. Tan, Y. Wang, Q. Liu, J. Wang, X. Jing, L. Liu, J. Liu, D. Song, Enhanced adsorption of uranium (VI) using a three-dimensional layered double hydroxide/graphene hybrid material, Chem. Eng. J., 259 (2015) 752-760. [47] W.S. Hummers, R.E. Offeman, Preparation of graphitic oxide, J. Am. Chem. Soc., 80 (1958) 1339-1339. [48] J.P. Gustafsson, A windows version of MINTEQ,http://http://www.lwr.kth.se/ English/OurSOrware/vminteq/index.htm, (2009). [49] M. Newville, EXAFS analysis using FEFF and FEFFIT. J. Synchrontron Radiat., 2001, 8, 96-100/ [50] B. Ravel, M. Newville, ATHENA, ARTEMIS, HEPHAESTUS: data analysis for Xray adsorption spectroscopy using IFEFFIT. J. Synchrotron Radiat., 2005, 12, 537-541. [51] S. Huang, G.-N. Zhu, C. Zhang, W.W. Tjiu, Y.-Y. Xia, T. Liu, Immobilization of Co-Al layered double hydroxides on graphene oxide nanosheets: Growth mechanism and supercapacitor studies, ACS Appl. Mater. Interface, 4 (2012) 2242-2249. [52] Y.B. Sun, D.D. Shao, C.L. Chen, S.B. Yang, X.K. Wang, Highly efficient enrichment of radionuclides on graphene oxide-supported polyaniline, Environ. Sci. Technol., 47 (2013) 9904-9910. [53] Z.P. Xu, G.Q. Lu, Hydrothermal synthesis of layered double hydroxides (LDHs) from mixed MgO and Al2O3: LDH formation mechanism, Chem. Mater., 17 (2005) 1055-1062. [54] S.J. Yu, X.X. Wang, W. Yao, J. Wang, Y.F. Ji, A. Alsaedi, T. Hayat, X.K. Wang, Macroscopic, spectroscopic, and theoretical investigation for the interaction of phenol and naphthol on reduced graphene oxide, Environ. Sci. Technol., 51(2017) 3278-3286. [55] X.X. Wang, S.B. Yang, W.Q. Shi, J.X. Li, T. Hayat, X.K. Wang, Different interaction mechanism of Eu(III) and 243Am(III) with carbon nanotubes studied by batch, spectroscopy technique and theoretical calculation, Environ. Sci. Technol., 2015, 49, 11721-11728. [56] D. Zhao, X. Wang, S. Yang, Z. Guo, G. Sheng, Impact of water quality parameters on the sorption of U(VI) on hematite, J. Envrion. Radioact., 2012, 103,

ACS Paragon Plus Environment

Page 18 of 31

Page 19 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

482 483 484 485 486 487 488 489 490 491 492 493 494

20-29. [57] H. Foerstendorf, K. Heim, Spectroscopic identification of ternary carbonate complexes upon U(VI)-sorption onto ferrihydrite, Geochim. Cosmochim. Acta, 2009, 73, A386-A386. [58] D. Shao, Z. Jiang, X. Wang, J. Li, Y. Meng, Plasma induced grafting carboxymethyl cellulose on multiwalled carbon nanotubes for the removal of UO22+ from aqueous solutions. J. Phys. Chem. B, 2009, 113, 860-864. [59] G. Zhao, T. Wen, X. Yang, S. Yang, J. Liao, J. Hu, D. Shao, X. Wang, Preconcentraiton of U(VI) ions on few-layered graphene oxide nanosheets from aqueous solutions. Dalton Trans., 2012, 41, 6182-6188. [60] Y. Arai, M. McBeath, J.R. Bargar, J. Joye, J.A. Davis, Uranyl adsorption and surface speciation at the imogolite-water interface: self-consistent spectroscopic and surface complexation models, Geochim. Cosmochim. Acta, 2006, 70, 2492-2509.

495

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

496

Figure Captions

497

Figure 1. Characterization of LDH/GO composites. A and B: TEM images of LDH

498

and LDH/GO composite, respectively; C: FT-IR spectra; D: XRD pattern.

499

Figure 2. The effect of pH (A) and carbonate concentration (B) on U(VI) removal on

500

LDH and LDH/GO composites, C0 = 10 mg/L, m/v = 1.5 g/L, I = 0.01 mol/L NaClO4,

501

T = 293 K.

502

Figure 3. Adsorption kinetics (A) and isotherms (B) of U(VI) removal by LDH and

503

LDH/GO and LDH/GO2 composites, pH 4.5, m/v = 1.5 g/L, I = 0.01 mol/L NaClO4,

504

T = 293 K.

505

Figure 4. Recycling of LDH (A) and LDH/GO composites (B) for U(VI) removal, pH

506

4.5, m/v = 1.5 g/L, I = 0.01 mol/L NaClO4, T = 293 K.

507

Figure 5. The XPS analysis of LDH/GO after U(VI) adsorption (LDH/GO-U-A) and

508

desorption (LDH/GO-U-D), A: total scans; B: high resolution of U 4f, C0 = 10 mg/L,

509

pH 4.5, m/v = 1.5 g/L, I = 0.01 mol/L NaClO4, T = 293 K.

510

Figure 6. Surface complexation modeling of U(VI) on LDH (A) and LDH/GO (B)

511

under different pH conditions, C0 = 10 mg/L, m/v = 1.5 g/L, I = 0.01 mol/L NaClO4,

512

T = 293 K.

513

Figure 7. Uranium L3-edge XANES spectra (A) and Fourier transform (FT) of

514

EXAFS spectra (B) for U(IV)O2(s), U(VI)O22+ and U(VI)-containing LDH/GO

515

composites at pH 3.0 and 6.0, m/v = 1.5 g/L, T = 293 K, I = 0.01 mol/L NaClO4.

516

ACS Paragon Plus Environment

Page 20 of 31

Page 21 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Table 1. The selective properties of LDH/GO composites LDH

LDH/GO

pHPZC

0 mV at pH 7.1

0 mV at pH 6.5

SBET (m2/g)

45.64

28.73

Average pore size (nm)

3.8

3.2

Table 2. Parameters of pseudo-first-order and pseudo-second-order kinetic model for the adsorption of U(VI) on LDH (1) and LDH/GO composites (2)

pseudo-first-order

pseudo-second-order

qe(mg/g)

kf(h−1)

R2

qe(mg/g)

ks(g /(mg×h))

R2

(1)

3.53

0.1164

0.5836

17.67

3.11E-5

1

(2)

5.12

0.0232

0.4077

20.04

1.12E-5

1

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 31

Table 3. Parameters of Langmuir and Freundlich model for the adsorption of U(VI) on LDH (1) and LDH/GO composites (2) Langmuir KL Qm (L/mg) (mg/g)

R

2

Freundlich Log KF 1/n n (mg/g)/(mg/g)

R2

(1)

0.0628

99.01

0.9978

1.9109

0.7587

0.9968

(2)

0.1851

129.87

0.9988

3.1775

0.5675

0.9829

Table 4. Comparison of adsorption performance of various adsorbents for U(VI) Adsorbents

Exp. Conditions

Qm (mg/g)

Nanoporous alumina

pH 4.5 T= 298 K

11.6

9

Hematite

pH 5.5 T= 298 K

5.59

56

Ferrihydrite

pH 5.5 T= 298 K

50.62

57

Carbon nanotubes

pH 5.0, T= 298 K

26.18

58

GO

pH 5.0 T= 293 K

97.5

59

LDH

pH 4.5 , T= 293 K

99.01

This study

LDH/GO composite

pH 4.5 , T= 293 K

129.87

This study

ACS Paragon Plus Environment

Ref.

Page 23 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Table 5. Optimized parameters of U(VI) adsorption on LDH/GO composites by surface complexation modeling Reactions

Log K

2>XNa + UO22+ = (>X)2UO2 + 2Na+

3.2

>SOH + UO22+ = >SOUO2+ + H+

-2.7

>SOH +2H2CO3 + UO22+ = >SOUO2 (CO3)23- + 5H+

-18.9

Table 6. Optimized parameters of uranium L3-edge EXAFS spectra for reference and uranium-containing samples Samples

Shell

R(Å)a

CNb

σ2(Å2)c

U(VI)O22+

U-Oax

1.78

2.0

0.0033

U-Oeq

2.35

4.9

0.0054

U-Oax

1.78

2.0

0.0026

U-Oeq

2.33

4.8

0.0039

U-Mg/Al

3.18

1.22

0.0087

U-Oax

1.78

2.0

0.0041

U-Oeq

2.31

4.6

0.0038

U-Mg/Al

3.17

1.20

0.0072

LDH/GOpH3

LDH/GOpH6

a

: bond distance; b: coordination number; c: Debye-Waller factor.

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 31

(A)

(B)

(C)

(D)

Figure 1

ACS Paragon Plus Environment

Page 25 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 2

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 3

ACS Paragon Plus Environment

Page 26 of 31

Page 27 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 4

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 5

ACS Paragon Plus Environment

Page 28 of 31

Page 29 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

Figure 6

ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 7

ACS Paragon Plus Environment

Page 30 of 31

Page 31 of 31

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

TOC

Manuscript title: One-pot synthesis of LDH/GO composites as high effective adsorbent for the decontamination of U(VI) Names of all authors: Wensheng Linghu†*, Hai Yang†, Yanxia Sun†, Guodong Sheng†, Yuying Huang‡ Brief synopsis: LDH/GO presented high adsorption capacity and good recyclability and recoverability for radionuclides in environmental cleanup.

ACS Paragon Plus Environment