Graphene with Fe and S Coordinated Active Centers: An Active

Jan 18, 2018 - Physical and Materials Chemistry Division, CSIR-National Chemical Laboratory, Pune, Maharashtra 411008, India. ‡ Academy of ... In pu...
0 downloads 8 Views 1MB Size
Subscriber access provided by University of Florida | Smathers Libraries

Article

Graphene with Fe and S Coordinated Active Centers: An Active Competitor for the Fe-N-C Active Centre for Oxygen Reduction Reaction in Acidic and Basic pH Conditions Siddheshwar N. Bhange, Sreekuttan M Unni, and Sreekumar Kurungot ACS Appl. Energy Mater., Just Accepted Manuscript • DOI: 10.1021/acsaem.7b00053 • Publication Date (Web): 18 Jan 2018 Downloaded from http://pubs.acs.org on January 19, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Energy Materials is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Graphene with Fe and S Coordinated Active Centers: An Active Competitor for the Fe-N-C Active Centre for Oxygen Reduction Reaction in Acidic and Basic pH Conditions Siddheshwar N. Bhange a,b, Sreekuttan M. Unni c and Sreekumar Kurungot a,b* a.

Physical and Materials Chemistry Division, CSIR-National Chemical Laboratory, Pune, Maharashtra, India-411008.

b.

Academy of Scientific and Innovative Research (AcSIR), CSIR-NCL Campus, Pune, Maharashtra, India-411008. c.

Division of ECPD, CSIR-CECRI, Karaikudi, Tamilnadu, India-630003.

KEYWORDS: S-doped Graphene, Oxygen reduction reaction, Electrocatalyst, Fuel cell, Zincair battery

ABSTRACT: Proton exchange membrane fuel cells (PEMFCs) and metal-air batteries are getting enormous attention due to their capability to fulfil the energy demand of the ever increasing population. Since the major bottleneck in the forward path of commercialization of such systems is mainly caused by the precious metal catalysts, there has been a paradigm shift on the development of Pt-free electrocatalyst for making the PEMFC systems cost competitive.

ACS Paragon Plus Environment

1

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Here, we report a Pt-free, iron and sulphur-doped, scrolled graphene

Page 2 of 31

(P12-900) prepared via

annealing of polyethylenedioxythiophene (PEDOT) as a potential oxygen reduction electrocatalyst which could perform exceptionally well under acidic and basic electrolyte conditions. The residual iron chloride retained by the polymer matrix, which was employed as the oxidizing agent for the polymerization reaction, plays a vital role in generating the potential ORR active sites based on the iron and sulphur doped graphene in the system. The composition designated as P12-900 displays an ORR activitiy with substantially reduced overpotential in both acidic and basic electrolyte conditions, which is a unique feature reported in these class of materials. In the basic medium, P12-900 displays an ORR activity which is similar to that of the performance of 40 wt.% Pt/C, whereas, under acidic condition, the inhouse system displays only 80 mV overpotential in the onset potential compared to its Pt counterpart. Single cell demonstration of a Nafion based PEMFC by employing P12-900 catalyst as a cathode delivered the maximum power density (PD) of 345 mW/cm2 at 60 oC without applying any back-pressure. Equally, when tested as the air electrode for zinc-air battery with KOH electrolyte, the cell displayed a maximum power density of 320 mW/cm2 and a maximum current density of 685 mA/cm2, which are comparable to performance of the the system based on the state-of-the-art Pt/C (322 mW/cm2 and 649 mA/cm2, respectively) cathode. Thus, the prepared precious metalfree catalyst performs as a promising candidate for the replacement of noble metal catalyst for PEMFCs and zinc-air battery systems with its unique capability to facilitate the electrode reactions under acidic and basic electrolyte conditions.

ACS Paragon Plus Environment

2

Page 3 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

1. Introduction The green renewable energy devices such as proton exchange membrane fuel cells (PEMFCs) and metal-air batteries have attracted much research attention in recent days in view of the increasing global energy demand and environmental impact of the traditional energy sources. 1-4 The cathodic oxygen reduction reaction (ORR) in these energy devices plays a key role in determining the energy efficiency.5 The high kinetic barriers of ORR at low temperature demands the need of precious metal electrocatalysts (e.g. Pt/C).6 However, the high cost along with poor stability and intolerance to fuel crossover of noble metals impede the wide-spread commercialisation potential of a futuristic energy system such as PEMFC.7 A splendid study has been conducted to develop low-cost alternatives to the Pt group metals (PGM). In pursuit of the development of non-precious electrocatalysts, the heteroatom doped carbon morphologies (dopants like N, S, B, P etc.) have received wide attention because some of them possess the ability to display ORR activity comparable to Pt/C in basic medium.8-12 The literature deals with quite extensive information on the promising ORR activity of N- or S-doped carbons in alkaline medium.51 However, majority of such systems fail to perform in acidic medium owing to the high overpotential incurred by the reaction under the low pH conditions.13-15 Also, reports are available for the co-doping of S and N or N and B or N and P in the carbon framework to enhance the overall ORR activity.16-19 One important factor which decides the overall ORR activity in terms of the achievable current density from the doped carbon catalysts is the number density of the active reaction sites responsible for dioxygen adsorption and its subsequent reduction.20,

21

Even with several structural modifications practiced to improve the surface

density of such active centres, the general trend is that, the heteroatom doped carbon catalysts display poor performance in acidic medium compared to basic environment.22 One effective way

ACS Paragon Plus Environment

3

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 31

to overcome this limitation is by coordinating the doped heteroatom centres with the 3d transition metals such as iron or cobalt. There are reports highlighting the promising ORR activities displayed by such systems in acidic conditions.23, 24 Fe-Nx doped carbon usually shows reasonable ORR activity in acidic condition (still experiences higher overpotential compared to Pt/C) and excellent activity in alkaline conditions.25-27 Experimental and theoretical studies have been carried out extensively to understand the improved performance displayed by such systems.25, 28-30 It is found that, there exists a cooperative interaction by which Fe increases the O-O bond length through back bonding with adsorbed oxygen, whereas, the doped nitrogen moieties activate the neighbouring carbon atoms through charge density/spin density changes.31 Apart from the Fe-Nx type active centres, report on the Fe-P type interactions also proven to be catalysing the reduction of dioxygen molecule in acidic environment.31 However, the ORR activity of the Fe-P systems is low in comparison to the Fe-Nx counterparts. Moreover, improvement in the ORR activity of the Fe-Nx doped carbon has also been observed with additional doping of S atoms in the carbon matrix.32, 33 The exact role of S in such systems is still unclear but this moiety is expected to incur activation of the carbon atoms through spin density changes as reported by Yang et al.34 In the ongoing efforts of our group to develop an ORR catalyst that can work well in both acidic and basic electrolyte conditions, we have noticed some reports on the iron pyrite (FeS 2) systems which display ORR activity in both alkaline and acidic conditions. However, they are found to be offering lesser activity compared to the Fe-Nx type coordination. This lesser activity contribution is originated primarily from the poor electrical conductivity of the pyrite type materials.35 The ORR activity modulation in systems based on the Fe-S bonding is possible by adopting a strategy through which a strong interaction between the doped-S and Fe can be

ACS Paragon Plus Environment

4

Page 5 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Scheme 1. A schematic representation of the synthesis of P12-900, showing the Fe and S-doped graphene sheets where the surface C-S and Fe-S works as the catalytic active centre for facilitating electrochemical oxygen reduction reaction in both acidic and alkaline pH conditions. The scheme also shows the demonstration of the catalyst as the cathode electrode material for PEMFC (acidic condition) and Zn-air battery (basic condition).

achieved on the carbon surface. This work is based on such a strategy, wherein, we could prepare Fe and S-doped graphene with enriched Fe-S coordination sites in the graphene matrix via a simple process involving annealing of polyethylenedioxithiophene (PEDOT) subsequent to its formation from ethylenedioxythiophene as the monomer and FeCl3 as the oxidizing agent. The Fe moieties present in the system establishes the Fe-Sx coordination with a fraction of the doped S species in the graphene matrix which are formed during the pyrolysis of PEDOT (Scheme 1). The catalyst shows substantially improved ORR activity compared to the Fe-Nx type catalysts in both the acidic and basic medium, positioning it as a strong competitor for the Fe-Nx type

ACS Paragon Plus Environment

5

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 31

systems to serve as an alternate to Pt/C in both acid and alkaline conditions. The work also demonstrates the practical system level application of the present catalysts by testing the single cells of PEMFC and Zn-air battery, which are based on acidic (Nafion) and basic (KOH) electrolytes, respectively.

2. Experimental Section 2.1 Materials: Ethylenedioxythiophene (EDOT), anhydrous iron chloride (FeCl3) and potassium hydroxide were procured from Sigma Aldrich. Sulphuric acid, acetonitrile and zinc dust were obtained from Thomas Baker, India. All the chemicals were used without any further purification. 2.2 Synthesis: 400 mg of the EDOT monomer was mixed with 40 ml of acetonitrile in a beaker and the mixture was kept for stirring. A solution of FeCl3 (5.475 g) in acetonitrile (20 ml) was added dropwise into the monomer solution. The ratio of the monomer to FeCl 3 was maintained as 1:12. The mixture was continuously stirred for 24 h at room temperature to ensure complete polymerization of the EDOT monomer into PEDOT. The polymer was dried at 80 oC and then annealed at different temperatures like 800, 900 and 1000 oC for 1 h in argon atmosphere. This was followed by acid wash using 0.5 M H2SO4 at 80 oC for 8 h to remove the surface metal oxide impurities. It was then filtered and washed several times with deionised water (DI) and dried overnight at 80 oC. A second annealing in inert atmosphere was performed to the acid washed carbon recovered from the first annealing process for 1 h at 800, 900 and 1000 oC. Thus obtained final carbon samples after the second pyrolysis process are respectively named as P12800, P12-900 and P12-1000. For the comparison purpose, PEDOT was also prepared without using FeCl3 to get the final catalyst free from Fe. This was achieved by preparing PEDOT

ACS Paragon Plus Environment

6

Page 7 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

through electrochemical deposition on a conducting substrate (FTO). The main purpose of the electrochemical method of EDOT polymerization is to avoid the presence of any kind of nitrogen impurities in the polymer. Lithium perchlorate and EDOT monomer were used as the supporting electrolyte and monomer respectively in acetonitrile solution. The electrochemical deposition on the FTO plate was performed at 10 mA/cm2 current density. The as deposited PEDOT on FTO was washed with acetonitrile solution and dried under IR lamp. After drying, the PEDOT polymer was scratched out from the FTO plate and annealed at 900 oC in inert atmosphere for 1 h. The annealed sample was subjected to acid washing at 80 oC in 0.5 M H2SO4 for 8 h. After drying, it was again annealed for 1 h at 900 oC in argon atmosphere. Thus obtained control sample is named as P-900. To make activity comparison of Fe-Sx with Fe-Nx type coordination, we prepared Fe-Nx doped carbon (FeN/C-900) as another control sample by following the procedure reported by Zelenay et al. (SI, Section 1.1) for comparing the ORR activity.36 The prepared samples were tested in both the pH conditions (acidic and basic) in order to validate their unique characteristics as systems which can perform towards the electrochemical ORR at two extreme pH conditions. Since the Nafion based PEMFC operates under acidic conditions, a set of experiments were performed in order to validate the ORR characteristics in 0.5 M H2SO4 and its realistic validation in a single-cell mode by fabricating a membrane electrode assembly (MEA) with Nafion as the proton conducting membrane and P12-900 as the cathode catalyst. Similarly, as a means to validate the performance of the catalyst in basic condition, the ORR characteristics was initially evaluated in 0.1 M KOH solution and later by employing P12-900 as the cathode in a zinc-air battery.

3. Results and Discussion

ACS Paragon Plus Environment

7

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 31

Information on the textural and morphological features attained during the transformation of the polymer to the carbon phase has been gathered first by performing powder X-ray diffraction analysis (PXRD) of P12-900 and P-900 (Figure 1a). In Figure 1a, both the samples shows a broad peak at a 2θ value of ~25.9o which corresponds to the (002) graphitic plane of the carbon. In the case of P12-900, additional peaks at 35.54o, 43.2o and 65.54o (JCPDS No. 65- 3356) are appeared, which are attributed to the presence of the hexagonal metal sulphide (FeS) phase.37 In contrary to the XRD results, Raman spectrum of P12-900 (Figure 1b) does not show any peak corresponding to the FeS particles which is usually observed in these types of materials below 1000 cm-1.38 One possible reason for this is that the FeS nanoparticles are well encapsulated within the graphene sheets. The D band (corresponding to the defective sites of carbon) and G band (representing the graphitization of the system) of P12-900 and P-900 are positioned at 1317 and 1593 cm-1, respectively.39 The ID/IG ratio (the intensity ratio of the D and G bands) of P-900 is less (1.13) compared to that of P12-900 (1.17). With respect to the increasing calcination temperature, the ID/IG ratio follows the order: P12-800 (1.05) < P12-900 (1.17) < P12-1000 (1.21). At high

Figure 1. (a) X-ray diffraction (XRD) profiles and (b) Raman spectra of the P12-900 and P-900 electrocatalysts.

ACS Paragon Plus Environment

8

Page 9 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

temperature, the encapsulated FeS moieties decompose and produce sulphur gases. Expulsion of the sulphur gases from the graphene matrix may assist the doping of the graphene sheets with sulphur while inducing the defective sites.

Investigation of the material with the help of

scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed fine details on the morphology and microstructure of the materials. The SEM images of P12-900 as

Figure 2. Morphological investigation of P12-900 with the help of SEM and TEM: (a) SEM image of P12-900 indicating the infolding of the PEDOT derived graphene; b) the TEM image of P12-900 displaying the transparent lamellar structure of the graphene sheet; c) the TEM image showing the presence of encapsulated FeS nanoparticles by the graphene sheets; d) magnified TEM image of P12-900 displaying the scrolled nature of graphene; e and f) shows the HRTEM images of the graphene sheets displaying the transparent graphene layers with the lattice fringes and their buckled nature due to heteroatom doping are clearly evident.

ACS Paragon Plus Environment

9

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 31

presented in Figure 2a suggest the morphology of the material similar to buckled graphene nanosheets with large inherent porosity. Interestingly, the SEM image of the P12-800 and P121000 electrocatalysts show the morphologies which differ from that of P12-900 (Figure S3, SI). It indicates that the morphology of the carbon derived from the polymer strongly depends on the annealing temperature. Further analysis with the help of TEM provides more insightful information on the surface of the carbon layer (Figure 2b-f). For example, the TEM image shown in Figure 2b displays the scrolled nature of the carbon nanosheets possessing transparent lamellar structure with wrinkles as in the case of the graphene sheets prepared by the conventional routes. On the other hand, Figure 2c shows the presence of the encapsulated FeS nanoparticals in the graphene sheet as indicated by the red arrows. Most of these nanoparticles are well wrapped with the graphene sheets. Figure 2d to f correspond to the high resolution TEM (HRTEM) images of P12-900, which show the presence of disordered lattice fringes of the carbon. The d-spacing calculated from the HRTEM image corresponding to P12-900 is 0.35 nm (Figure 2f) and it indicates effective graphitization of the carbon sheets. Buckling of the graphene layers is a characteristic feature of the heteroatom doped graphene systems and the clear appearance of the disordered nature in the present case indicates effective doping of the heteroatoms in the sheets.40 The elemental mapping gives a clear indication of the uniform distribution of the S and Fe present in the matrix of the graphene nanosheet (Figure S6, SI). The buckled graphene nanosheet is thereby believed to contain uniformly distributed of S and Fe moieties. The Brunauer Emmett Teller (BET) surface area analysis of the samples calcined at different temperatures (Figure S7 a, SI) show that as the annealing temperature increases, the BET surface area also concomitantly increases in the order of P12-800 (1125 m2/g) < P12-900 (1684 m2/g) < P12-1000 (1860 m2/g). This trend is in accordance with the previously discussed

ACS Paragon Plus Environment

10

Page 11 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

differences in the morphologies of the materials as revealed through the SEM images of the samples prepared by calcining at different temperatures. The pore size of the P12 samples mainly lies in between 1-4 nm (Figure S7b, SI). The cumulative pore area of the P12 samples was found to be increased with increase in the pyrolysis temperature. The X-ray photoelectron spectroscopy (XPS) investigation gives information of the presence and nature of the coordination of carbon, oxygen, iron and sulphur over the graphene sheet surface. The C1s spectrum of P12-900 (Figure S8b, SI) is fitted to get an insight on the different types of carbon bonding existing on the surface. The peak at 283.24 eV corresponds to the metal carbide and the peak at 284.50 eV is attributed to the C=C coordinations.41 Further to this, a strong indication on the presence of the C-S bond due to S doping is obtained from the peak at 285.74 eV.42 The peaks corresponding to the binding energy value of 287.16 eV and 288.83 eV of the fitted C1s spectra also provide information on the C=O and -O-C=O type interactions of the carbon.41 The similar kind of peaks are also observed in the case of P12-800 and P12-1000 (Figure S8a and c, SI). Figure 3a-c show the deconvoluted Fe2p spectra of P12-800, P12-900 and P12-1000. The Fe 2p3/2 and Fe 2p1/2 peaks of lower binding energy (709.70 eV) and higher binding energy (721.01 eV) are ascribed to the +2 oxidation state of Fe in the Fe-S bond.42-45 On the other hand, the peaks appeared at the binding energies of 711.96 eV and the 723.83 eV represent the +3 oxidation state of Fe.45,

46

Since iron sulphide has high reactivity towards

oxygen, it is expected that the reaction with the oxygen present in PEDOT and iron sulphide can lead to the formation of iron oxide during the pyrolysis process. All the three samples display similar features in their Fe2p spectral characteristics. Figure 4 shows the fitted S2p spectra of the three P12 catalysts. The peaks appeared at around 163.5 and 164.74 eV are representing the 2p3/2 and 2p1/2 states, respectively, of S and the presence of these peaks suggests the major

ACS Paragon Plus Environment

11

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

contribution by S2-.42,

45, 47

Page 12 of 31

Another peak appeared at 167.36 eV is indicating C-SOx-C

interactions.41, 42 Moreover, the peak expected at ~ 162.0 eV from the thiol groups is absent in the XPS spectra of all the samples.48 This suggests that the sulphur doping is occurring mainly at the edges of the graphene sheets thereby facilitating efficient coordination

Figure 3. Fitted Fe 2p spectra of (a) P12-800, (b) P12-900, and (c) P12-1000.

with the iron moieties. The change in spin density of the carbon and sulphur is expected to play a crucial role in attaining improved ORR activity of these types of carbon catalysts. 34 Since the XPS spectra give valid evidence for the existence of the Fe-S bonding along with the doping of iron and sulphur in the PEDOT derived graphene sheets, it is believed that the coexistence of these sites will act as efficient ORR active centres in these catalysts. Calculation of the atom percentage (at. %) of Fe and S from the XPS data for P12-900 gives 5.3 at. % of Fe and 2.44 at.

ACS Paragon Plus Environment

12

Page 13 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

% of S. It is interesting to note that the iron content in the P12 catalysts is increasing whereas the sulphur content is decreasing with increase in the annealing temperature (Table S1, SI). This could be possibly caused by the partial removal of the less stable sulphur species at high temperature, leading to a proportional increase in the Fe content in the overall composition.

Figure 4. The deconvoluted S2p spectra of (a) P12-800, (b) P12-900, and (c) P12-1000.

The oxygen reduction reaction (ORR) activity of the P12 samples under acidic and basic pH conditions was evaluated by performing the rotating disc electrode (RDE) and rotating ring disc electrode (RRDE) techniques in 0.5 M H2SO4 and 0.1 M KOH solutions. The linear sweep voltammogram (LSV) was measured at a scan rate 10 mV/s with different electrode rotation speeds (Figure S9, SI). A glassy carbon electrode was used as the working electrode and a graphite rod and reversible hydrogen electrode were used as the counter and reference electrodes, respectively. Figure 5a shows the LSV profiles were measured at an electrode rotation speed of 1600 rpm in 0.5 M H2SO4. The catalyst P12-900 shows an onset potential of 0.92 V (for Pt/C, the onset potential is 1.0 V) and a half-wave potential of 0.78 V (for Pt/C half-wave potential is

ACS Paragon Plus Environment

13

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 31

0.86 V) vs. RHE, which are more positive than that of P12-800 and P12-1000. The onset potentials of P12-800 and P-12-1000 are observed at 0.90 V, each is 16 mV less compared to that of P12-900. Similarly, the half-wave potentials of P12-800 and P12-1000 are observed at 0.77 V and 0.75 V, respectively. This is respectively 14 mV and 34 mV less compared to the corresponding value of P12-900. P12-900 shows overpotential difference of 80 mV for the onset and half wave potentials compared to the commercial Pt/C (40 wt. %). It is also important to note that the ORR activity of the P12-900 catalyst is superior to the recently reported systems which are active in acidic medium (shown in SI, Table S4). It also should be noted that the prepared control sample P-900, which contains only the doped S sites without coordinating to Fe, shows poor performance towards ORR in acidic condition. This substantial difference in terms of the ORR performance of the P12 catalysts and their iron-free counterpart highlights the necessity of the generation of the Fe-Sx active centres to make the system enable for facilitating ORR under acidic conditions. In order to differentiate how the Fe-S and Fe-N active centres differ in terms of the ORR activity in acidic conditions, the activity of P12-900 catalyst is compared with FeN/C-900 (prepared by the synthesis method used by Zelenay et al.36,50). With FeN/C-900 displays onset and half-wave potentials at 0.89 and 0.75 V vs RHE, it is confirmed that this catalyst is inferior to P12-900 by an overpotential of 30 mV each in the onset potential as well as half-wave potentials. It indicates that the Fe-Sx active sites in P12-900 are more efficient to facilitate ORR in acidic conditions compared to the Fe-N active sites present in FeN/C-900. The Tafel slope measured in the case of P12-900 is 61 mV decade-1, which specifies that the dioxygen reduction mechanism is apparently similar to that of Pt/C (68 mV decade-1). On the other hand, P12-800 (88 mV decade-1) and P12-1000 (99 mV decade-1) show much higher Tafel slope values,

ACS Paragon Plus Environment

14

Page 15 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

indicating less facile reactions in these cases compared to P12-900 (Figure S11, SI). The mass activity is calculated for all the catalysts at a fixed potential of 0.85 V vs. RHE. The activity estimated in the case of P12-900 is 0.833 A/g, which is superior to both P12-800 (0.630 A/g) and P12-1000 (0.530 A/g), respectively.

Figure 5. (a) The comparative LSVs of the different electrocatalysts measured under O2 saturated 0.5 M H2SO4 at 10 mV/S scan rate using the electrode rotation rate of 1600 rpm., (b) LSVs of P12-900 before and after 10000 potential cycling, (c) schematic representation of the proton exchange membrane fuel cell (PMFCs) and, (d) comparison of the single cell polarization plots of the MEAs fabricated by using P12-900 and FeN/C900 as the cathode (2 mg/cm2) catalysts and Pt/C (0.5 mg/cm2) as the anode catalyst. The testing was carried out at a cell temperature of 60 oC without applying any back pressure. The number of electron transfer and the hydrogen peroxide formation (H2O2 %) during ORR were measured using the rotating ring disc electrode (RRDE) studies. The RRDE voltammograms are recorded at a scan rate of 10 mV/s with the electrode rotation speed of 1600

ACS Paragon Plus Environment

15

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 31

rpm in oxygen saturated 0.5 M H2SO4. The Equations S1 and S2 (Supporting Information) were used to calculate the percentage of H2O2 and number of electron transferred during ORR. The P12-800, P12-900 and P12-1000 are found to show less than 3% peroxide yield compared to the substantial amount of ca. 64% recorded in the case of P-900. This certainly shows that the P12 catalysts possess the fertile surface with the right combination of the active sites which are able to drive the dioxygen reduction kinetics through the preferred 4-electron pathway. In particular, the drastic differences between P-900 and P12-900 in terms of their ORR activity and kinetic pathways clearly indicate the decisive role played by the Fe-Sx active sites in the latter case to enable its functioning as a potential ORR electrocatalyst in acid environment. The magnitude of the performance improvement accomplished simply by changing the nature of the active sites suggests that the dependency of the ORR activity on the electrolyte pH is strongly a function of the nature of the active centres present in the case of the Pt-free electrocatalysts. Once such active sites are created and their number density is maintained by strategically tuning the preparation protocols, realization of the Pt-free catalysts with the activity characteristics similar that of the state-of-the-art Pt catalysts under proton exchange conditions is a clear possibility. The physically dispersed Fe moieties are vulnerable to leaching under the acid environment. Also, since these active sites are stitched on the carbon framework of the graphene, even carbon corrosion can remove some of the active sites with performance degradation. Hence, it is important to validate that the Fe based active centres generated in the present case can survive the potential induced conditions under acid environments. This has been validated by performing accelerated durability test (ADT) of P12-900 by maintaining an electrochemical condition which can accelerate the carbon corrosion. The material was subjected to 10000 potential cycling in the potential range of 0.6 to 1.0 V vs RHE. From the ADT profiles presented

ACS Paragon Plus Environment

16

Page 17 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

in Figure 5b, it can be seen that P12-900 suffers only 30 mV potential shift in the half-wave potential with apparently no change in the onset potential. In comparison to P12-900, Pt/C suffers 73 mV drop in the half-wave potential after subjecting to 5000 potential cycling, accounting to ~2.5 times higher degradation compared to P12-900. The morphology of P12-900 was investigated with the help of TEM analysis subsequent to ADT. The TEM images present in Figure S5 show that the morphological features are more or less completely retained even after ADT. This high degree of retention of the morphological features and lower rate of performance loss subsequent to ADT correlate to the strong structural integrity possessed by the material, which plays a key role in maintaining the active sites intact under the drastic conditions of different pH and potential induced conditions. Since, the material shows excellent ORR activity in acidic medium, as a realistic system level validation, a single cell of PEMFC was assembled and tested by fabricating a membrane electrode assembly (MEA) in which P12-900 was employed as the cathode catalyst (2 mg/cm2 loading). The commercial Nafion® membrane was employed as the proton conducting electrolyte membrane. The anode was prepared by using the commercial Pt/C catalyst by maintaining a loading of 0.5 mg/cm2. As can be seen from the current (I)-voltage (V) polarization plot presented in Figure 5d, the system displays an onset potential (OCV) of 0.89 V which is 30 mV lesser compared to the half-cell data. The polarization curve displays the standard features of the I-V plot in the case of the Pt based MEAs, consisting of the all three distinct overpotential regions corresponding to activation, ohmic and mass transfer. The system delivered a maximum power output of 345 mW/cm2 (at 0.32 V) and a maximum current density of 1.47 A/cm2 (at 0.2 V) without applying any back pressure. Thus, looking at the performance profile based on the single cell evaluation of the P12-900 catalyst-derived MEA, the catalyst as

ACS Paragon Plus Environment

17

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 31

the cathode electrode can be seen as performing exceptionally well by delivering a power density value which is comparable to that reported till date for the non-Pt based electrocatalysts in PEMFC.24,

49

Furthurmore, the performance of P12-900 is comparable to the electrocatalyst

prepared using silica template to obtain mesoporosity.51 However, in this work high surface area and microporpous structure is achieved without using any template. Thus, the intrinsic ORR activity of P12-900 as revealed through the half-cell studies could be translated in terms of power output in its realistic performance validation in a single cell mode by employing the catalyst as the cathode of the system. Even though the performance of this system is lower than that of the MEAs based on Pt/C cathode, this one of the best results obtained on a Pt-free system reported so far offers new avenues for designing potential catalysts by logically developing strategies to enrich the Fe-Sx active centre density in the catalyst system. Similarly, for comparison, we have fabricated an MEA by employing FeN/C-900 as the cathode catalyst (2 mg/cm2, loading), and by maintaining the rest of the conditions as in the case of the P12-900 based MEA. The FeN/C-900 based MEA delivers a maximum power density of 306 mW/cm2 (at 0.32 V) and current density of 1.35 A/cm2 (at 0.2 V) without applying any back pressure (Figure 5d). Thus, the comparision of the single cell data in the above two cases substantiates the high intrinsic ORR activity displayed by P12-900 over FeN/C-900. A comparison of the single cell data and analysis parameters of the present systems with the similar systems reported in the literature is presented in Table S6 in the Supporting Information. The electrochemical stability of the single cell fabricated from P12-900 was carried out, the corresponding data is presented in Figure S15, by monitoring the current output from the MEA at a constant potential of 0.4 V for the 12 h. The system delivered a current density of ~ 475 mA/cm2 without applying any backpressure at 60 oC in H2 and O2 atmosphere and 100 % humidification. The MEA displays stable

ACS Paragon Plus Environment

18

Page 19 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

performance once the cell reached 475 mA/cm2, 4 h after the the commencement of the test. It is observed from the stability data that the performance shows a gradual improvement in the initial hours and, thereafter, it stabilises by delivering a steady 475 mA/cm 2 current. The initial improvement in the performance could be due to the activation of the catalyst under the electrochemical conditions.

Figure 6. (a) The comparative LSVs of the different prepared catalysts recorded using O 2 saturated 0.1 M KOH at 10 mV/S scan rate under an electrode rotation rate of 1600 rpm, (b) LSVs of P12-900 before and after 10000 potential cycling, (c) schematic representation of the zinc-air battery (ZAB) unit, and (d) polarization plots recorded on the ZABs based on P12-900 and Pt/C as the cathode catalysts.

Compared to the performance of the system in acidic medium, in basic condition (0.1 M KOH), P12-900 shows closely comparable ORR activity to that of the commercial Pt/C. P12-900 displays an onset potential of 1.02 V which is similar to the result obtained on 40 wt. % Pt/C (1.04 V) (Figure 6a). Moreover, the half-wave potential (0.86 V vs. RHE) of the homemade catalyst is also comparable to its Pt/C counterpart (0.86 V vs. RHE). Figure 6a also shows that

ACS Paragon Plus Environment

19

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 31

both P12-800 and P12-1000 show almost comparable onset (0.99 V vs. RHE) and half-wave potential (0.85 V vs. RHE) values. On the other hand, P-900 in which S is not coordinated with Fe, displays significantly high overpotential for both in terms of the onset as well as half-wave potential compared to its P12 counterparts. This result shows that, as in the case of the performance in the acid electrolyte, the Fe-Sx active sites show exceptionally high performance in basic condition as well. Since it is known that the Fe-N sites show high intrinsic activity towards ORR in basic electrolyte conditions, we compared the performance of P12-900 with FeN/C-900 which contains the Fe-N coordinated sites. The LSV profile of FeN/C-900 presented in Figure 6a shows the onset and half-wave potentials at 0.98 and 0.82 V vs RHE, respectively. This result clearly indicates that the ORR activity of the P12-900 system, which holds the Fe-Sx active sites, has a distinct advantage over the FeN/C-900 catalyst with the Fe-N active sites in alkaline condition. The mass activity of the P12 catalysts calculated at 0.85 V follows the order as P12-900 (7.36 A/g) > P12-800 (6.49 A/g) > P12-1000 (5.9 A/g). The mass activity of the Pt/C catalyst at 0.85 V is estimated to be 7.55 A/g. Also, the Tafel slope of P12-900 (77 mV decade-1) is found to be comparable to that of Pt/C (79 mV decade-1). These results clearly emphasise that P12-900 in terms of its intrinsic ORR activity is closely comparable to the Pt based catalyst in the basic conditions. In order to look into the durability aspect of P12-900 in the basic medium, ADT was carried out by following the procedure as illustrated before in the case of the acidic electrolyte. ADT induced a reduction in the half-wave potential by 11 mV without affecting the onset potential value. The limiting current density is also found to be unaffected during ADT. On the other hand, ADT leads to a reduction in the half-wave potential by 35 mV in the case of Pt/C. Apparently, ADT did not induce morphological alterations in the case of P12-900 as evident

ACS Paragon Plus Environment

20

Page 21 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

from the TEM image of the spent catalyst (presented in Figure S5b, SI). Thus, as in the case of the acidic condition, P12-900 displays high activity and stability towards ORR in alkaline environment as well. Since a zinc-air battery (ZAB) works based on an alkaline electrolyte (KOH) and oxygen reduction catalyst as the cathode, the system level feasibility of P12-900 has been validated by fabricating a ZAB by utilizing it as the cathode in the cell. The anode of the cell was fabricated by using zinc power. The catalyst ink of P12-900 was prepared by maintaining a Nafion to catalyst ratio of 0.5 in isopropyl alcohol (IPA) solvent. The ink was applied on the gas diffusion layer by keeping the P12-900 loading of 2 mg/cm2 to get the cathode. In the case of the control experiment using Pt anode, the catalyst slurry containing 40 wt. % Pt/C and Nafion to carbon ratio of 0.5 in IPA was coated on the gas diffusion layer to achieve a Pt loading of 1 mg/cm2. The schematic representation of the ZAB assembly is shown in Figure 6c. The performance of the cell was evaluated by using 6 M KOH as the electrolyte. For avoiding electronic contact, a Celgard membrane was used as the separator. Subsequent to air purging on the cathode side of the cell, the P12-900 based system displays an onset potential of 1.47 V which is closely comparable to the value displayed by the Pt/C based cell (1.48 V) (Figure 6d).

During

polarization of the cell, a close matching performance profiles have been displayed by the P12900 and Pt/C. Both the systems display a maximum power density of 320 mW/cm 2, justifying the comparable intrinsic activity characteristics obtained in the case of the P12-900 and Pt/C catalysts in the half-cell mode of measurements.

ACS Paragon Plus Environment

21

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 31

4. Conclusion Here, we prepared Fe and S-doped graphene which display exceptionally high ORR activity in both acidic and basic environments. The material derived from PEDOT after its controlled pyrolysis under inert atmosphere possesses scrolled graphene structure with C-S and Fe-S active sites. The catalyst prepared by pyrolyzing at 900 oC (P12-900) displays ORR activity with substantially reduced overpotential in acidic and basic electrolyte conditions. Such performance characteristics displayed by a single system under two extreme pH conditions is a unique feature reported in these class of materials. In the basic medium, the ORR activity of P12-900 is found to be similar to that of the performance of 40 wt. % Pt/C in terms of the onset and half-wave potentials. Under acidic condition also the inhouse system displays high ORR activity but lower than that of Pt/C by 80 mV in terms of the onset potential. During single cell evaluation of a Nafion based PEMFC, the P12-900 based cell delivered a maximum power density of 345 mW/cm2 at 60 oC in the absence of any applied back-pressure. The zinc-air battery systems derived from P12-900 and standard Pt/C as the cathode catalysts and KOH as the electrolyte displayed nearly comparable performance profiles, delivering a maximum power density of 320 mW/cm2 in both the cases. The prepared precious metal-free catalyst enriched with the Fe and Sdoped graphene can be thus considered as a promising alternative for the noble metal catalysts for PEMFCs and zinc-air battery systems with its unique capability to facilitate ORR under acidic and basic pH conditions of the electrolyte.

ACS Paragon Plus Environment

22

Page 23 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

ASSOCIATED CONTENT Supporting Information. Detailed experimental procedures and Materials characterization, XRD, Raman, SEM images, TEM images and rotating ring disc electrode study, single cell study and table of comparison. AUTHOR INFORMATION Corresponding Author *E-mail: [email protected] Physical and Materials Chemistry Division, CSIR-National Chemical Laboratory, Pune 411008, Maharashtra, India Present Addresses Physical and Materials Chemistry Division, CSIR-National Chemical Laboratory, Pune 411008, Maharashtra, India Author Contributions The manuscript was written through equal contributions of all the authors. All authors have given approval to the final version of the manuscript. ACKNOWLEDGMENT SNB acknowledges CSIR for Senior Research Fellowship (SRF) and KS acknowledges TLP003526 for the financial assistance.

ACS Paragon Plus Environment

23

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 31

REFERENCES 1. Yang, Z.; Nie, H.; Chen, X. a.; Chen, X.; Huang, S., Recent Progress in Doped Carbon Nanomaterials as Effective Cathode Catalysts for Fuel Cell Oxygen Reduction Reaction. J. Power Sources 2013, 236, 238-249. 2. Costa, R. A.; Camacho, J. R., The Dynamic and Steady State Behavior of a PEM Fuel Cell as an Electric Energy Source. J. Power Sources 2006, 161, 1176-1182. 3. Andújar, J. M.; Segura, F., Fuel Cells: History and Updating. A Walk Along Two Centuries. Renewable and Sustainable Energy Reviews 2009, 13, 2309-2322. 4. Yuan, C.; Wu, H. B.; Xie, Y.; Lou, X. W., Mixed Transition-Metal Oxides: Design, Synthesis, and Energy-Related Applications. Angew Chem. Int. Ed. 2014, 53, 1488-1504. 5. Wang, S.; Zhang, L.; Xia, Z.; Roy, A.; Chang, D. W.; Baek, J.-B.; Dai, L., BCN Graphene as Efficient Metal-Free Electrocatalyst for the Oxygen Reduction Reaction. Angew. Chem. Int. Ed. 2012, 51, 4209-4212. 6. Tse, E. C. M.; Gewirth, A. A., Effect of Temperature and Pressure on the Kinetics of the Oxygen Reduction Reaction. J. Phys. Chem. A 2015, 119, 1246-1255. 7. Kang, Y.; Murray, C. B., Synthesis and Electrocatalytic Properties of Cubic Mn−Pt Nanocrystals (Nanocubes). J. Am. Chem. Soc. 2010, 132, 7568-7569. 8. Zhang, J.; Dai, L., Heteroatom-Doped Graphitic Carbon Catalysts for Efficient Electrocatalysis of Oxygen Reduction Reaction. ACS Catalysis 2015, 5, 7244-7253. 9. Yang, L.; Jiang, S.; Zhao, Y.; Zhu, L.; Chen, S.; Wang, X.; Wu, Q.; Ma, J.; Ma, Y.; Hu, Z., Boron-Doped Carbon Nanotubes as Metal-Free Electrocatalysts for the Oxygen Reduction Reaction. Angew. Chem. 2011, 123, 7270-7273. 10. Gong, K.; Du, F.; Xia, Z.; Durstock, M.; Dai, L., Nitrogen-Doped Carbon Nanotube Arrays with High Electrocatalytic Activity for Oxygen Reduction. Science 2009, 323, 760-764.

ACS Paragon Plus Environment

24

Page 25 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

11. Li, W.; Yang, D.; Chen, H.; Gao, Y.; Li, H., Sulfur-doped Carbon Nanotubes as Catalysts for the Oxygen Reduction Reaction in Alkaline Medium. Electrochim. Acta 2015, 165, 191-197. 12. Liu, Z.-W.; Peng, F.; Wang, H.-J.; Yu, H.; Zheng, W.-X.; Yang, J., Phosphorus-Doped Graphite Layers with High Electrocatalytic Activity for the O2 Reduction in an Alkaline Medium. Angew. Chem. 2011, 123, 3315-3319. 13. Wohlgemuth, S.-A.; White, R. J.; Willinger, M.-G.; Titirici, M.-M.; Antonietti, M., A Onepot Hydrothermal Synthesis of Sulfur and Nitrogen Doped Carbon Aerogels with Enhanced Electrocatalytic Activity in the Oxygen Reduction Reaction. Green Chem. 2012, 14, 1515-1523. 14. Mo, Z.; Liao, S.; Zheng, Y.; Fu, Z., Preparation of Nitrogen-doped Carbon Nanotube Arrays and Their Catalysis Towards Cathodic Oxygen Reduction in Acidic and Alkaline Media. Carbon 2012, 50, 2620-2627. 15. Wei, W.; Liang, H.; Parvez, K.; Zhuang, X.; Feng, X.; Müllen, K., Nitrogen-Doped Carbon Nanosheets with Size-Defined Mesopores as Highly Efficient Metal-Free Catalyst for the Oxygen Reduction Reaction. Angew. Chem. 2014, 126, 1596-1600. 16. Yang, S.; Zhi, L.; Tang, K.; Feng, X.; Maier, J.; Müllen, K., Efficient Synthesis of Heteroatom (N or S)-Doped Graphene Based on Ultrathin Graphene Oxide-Porous Silica Sheets for Oxygen Reduction Reactions. Adv. Funct. Mater. 2012, 22, 3634-3640. 17. Wang , S.; Iyyamperumal , E.; Roy, A.; Xue, Y.; Yu, D.; Dai, L., Vertically Aligned BCN Nanotubes as Efficient Metal-Free Electrocatalysts for the Oxygen Reduction Reaction: A Synergetic Effect by Co-Doping with Boron and Nitrogen. Angew. Chem. 2011, 123, 1196011964. 18. Dong, L.; Hu, C.; Huang, X.; Chen, N.; Qu, L., One-pot Synthesis of Nitrogen and Phosphorus Co-doped Graphene and Its Use as High-performance Electrocatalyst for Oxygen Reduction Reaction. Chem. Asian J. 2015, 10, 2609-2614. 19. Yu, D.; Xue, Y.; Dai, L., Vertically Aligned Carbon Nanotube Arrays Co-doped with Phosphorus and Nitrogen as Efficient Metal-Free Electrocatalysts for Oxygen Reduction. J. Phys. Chem. Lett. 2012, 3, 2863-2870.

ACS Paragon Plus Environment

25

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 31

20. Liang, W.; Chen, J.; Liu, Y.; Chen, S., Density-Functional-Theory Calculation Analysis of Active Sites for Four-Electron Reduction of O2 on Fe/N-Doped Graphene. ACS Catalysis 2014, 4, 4170-4177. 21. Zhang, L.; Xia, Z., Mechanisms of Oxygen Reduction Reaction on Nitrogen-Doped Graphene for Fuel Cells. J. Phys. Chem. C 2011, 115, 11170-11176. 22. Rao, C. V.; Cabrera, C. R.; Ishikawa, Y., In Search of the Active Site in Nitrogen-Doped Carbon Nanotube Electrodes for the Oxygen Reduction Reaction. J. Phys. Chem. Lett. 2010, 1, 2622-2627. 23. Wu, G.; More, K. L.; Johnston, C. M.; Zelenay, P., High-Performance Electrocatalysts for Oxygen Reduction Derived from Polyaniline, Iron, and Cobalt. Science 2011, 332, 443-447. 24. Bashyam, R.; Zelenay, P., A Class of Non-precious Metal Composite Catalysts for Fuel Cells. Nature 2006, 443, 63-66. 25. Sa, Y. J.; Seo, D.-J.; Woo, J.; Lim, J. T.; Cheon, J. Y.; Yang, S. Y.; Lee, J. M.; Kang, D.; Shin, T. J.; Shin, H. S.; Jeong, H. Y.; Kim, C. S.; Kim, M. G.; Kim, T.-Y.; Joo, S. H., A General Approach to Preferential Formation of Active Fe–Nx Sites in Fe–N/C Electrocatalysts for Efficient Oxygen Reduction Reaction. J. Am. Chem. Soc. 2016, 138, 15046-15056. 26. Monteverde Videla, A. H. A.; Zhang, L.; Kim, J.; Zeng, J.; Francia, C.; Zhang, J.; Specchia, S., Mesoporous Carbons Supported Non-noble Metal Fe–NX Electrocatalysts for PEM Fuel Cell Oxygen Reduction Reaction. J. Appl. Electrochem. 2013, 43, 159-169. 27. Unni, S. M.; Illathvalappil, R.; Bhange, S. N.; Puthenpediakkal, H.; Kurungot, S., Carbon Nanohorn-Derived Graphene Nanotubes as a Platinum-Free Fuel Cell Cathode. ACS Appl. Mater. Interfaces 2015, 7, 24256-24264. 28. Kattel, S.; Atanassov, P.; Kiefer, B., A Density Functional Theory Study of Oxygen Reduction Reaction on Non-PGM Fe-Nx-C Electrocatalysts. PCCP 2014, 16, 13800-13806.

ACS Paragon Plus Environment

26

Page 27 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

29. Lin, L.; Zhu, Q.; Xu, A.-W., Noble-Metal-Free Fe–N/C Catalyst for Highly Efficient Oxygen Reduction Reaction Under Both Alkaline and Acidic Conditions. J. Am. Chem. Soc. 2014, 136, 11027-11033. 30. Velázquez-Palenzuela, A.; Zhang, L.; Wang, L.; Cabot, P. L.; Brillas, E.; Tsay, K.; Zhang, J., Fe–Nx/C Electrocatalysts Synthesized by Pyrolysis of Fe(II)–2,3,5,6-tetra(2-pyridyl)pyrazine Complex for PEM Fuel Cell Oxygen Reduction Reaction. Electrochim. Acta 2011, 56, 47444752. 31. Singh, K. P.; Bae, E. J.; Yu, J.-S., Fe–P: A New Class of Electroactive Catalyst for Oxygen Reduction Reaction. J. Am. Chem. Soc. 2015, 137, 3165-3168. 32. Hu, K.; Tao, L.; Liu, D.; Huo, J.; Wang, S., Sulfur-Doped Fe/N/C Nanosheets as Highly Efficient Electrocatalysts for Oxygen Reduction Reaction. ACS Appl. Mater. Interfaces 2016, 8, 19379-19385. 33. Bhange, S. N.; Unni, S. M.; Kurungot, S., Nitrogen and Sulphur Co-doped Crumbled Graphene for the Oxygen Reduction Reaction with Improved Activity and Stability in Acidic Medium. J. Mater. Chem. A 2016, 4, 6014-6020. 34. Yang, Z.; Yao, Z.; Li, G.; Fang, G.; Nie, H.; Liu, Z.; Zhou, X.; Chen, X. a.; Huang, S., Sulfur-Doped Graphene as an Efficient Metal-free Cathode Catalyst for Oxygen Reduction. ACS Nano 2012, 6, 205-211. 35. Abraitis, P. K.; Pattrick, R. A. D.; Vaughan, D. J., Variations in the Compositional, Textural and Electrical Properties of Natural Pyrite: A Review. Int. J. Miner. Process. 2004, 74, 41-59. 36. Li, Q.; Wu, G.; Cullen, D. A.; More, K. L.; Mack, N. H.; Chung, H. T.; Zelenay, P., Phosphate-Tolerant Oxygen Reduction Catalysts. ACS Catalysis 2014, 4, 3193-3200. 37. Akhtar, M.; Malik, M. A.; Tuna, F.; O'Brien, P., The Synthesis of Iron Sulfide Nanocrystals From Tris(O-alkylxanthato)iron(iii) Complexes. J. Mater. Chem. A 2013, 1, 8766-8774. 38. Rémazeilles, C.; Saheb, M.; Neff, D.; Guilminot, E.; Tran, K.; Bourdoiseau, J.-A.; Sabot, R.; Jeannin, M.; Matthiesen, H.; Dillmann, P.; Refait, P., Microbiologically Influenced Corrosion of

ACS Paragon Plus Environment

27

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 31

Archaeological Artefacts: Characterisation of Iron(II) Sulfides by Raman Spectroscopy. J. Raman Spectrosc. 2010, 41, 1425-1433. 39. Dhavale, V. M.; Gaikwad, S. S.; Kurungot, S., Activated Nitrogen Doped Graphene Shell Towards Electrochemical Oxygen Reduction Reaction by Its Encapsulation on Au Nanoparticle (Au@N-Gr) in Water-in-oil "Nanoreactors". J. Mater. Chem. A 2014, 2, 1383-1390. 40. Palaniselvam, T.; Kannan, R.; Kurungot, S., Facile Construction of Non-precious Iron Nitride-doped Carbon Nanofibers as Cathode Electrocatalysts for Proton Exchange Membrane Fuel Cells. Chem. Commun. 2011, 47, 2910-2912. 41. Wang, Z.; Dong, Y.; Li, H.; Zhao, Z.; Bin Wu, H.; Hao, C.; Liu, S.; Qiu, J.; Lou, X. W., Enhancing Lithium–sulphur Battery Performance by Strongly Binding the Discharge Products on Amino-functionalized Reduced Graphene Oxide. Nature Commun. 2014, 5, 5002. 42. Vinayan, B. P.; Diemant, T.; Behm, R. J.; Ramaprabhu, S., Iron Encapsulated Nitrogen and Sulfur Co-doped Few Layer Graphene as a Non-Precious ORR Catalyst for PEMFC Application. RSC Advances 2015, 5, 66494-66501. 43. Xu, X.; Dai, Y.; Yu, J.; Hao, L.; Duan, Y.; Sun, Y.; Zhang, Y.; Lin, Y.; Zou, J., Metallic State FeS Anchored (Fe)/Fe3O4/N-Doped Graphitic Carbon with Porous Spongelike Structure as Durable Catalysts for Enhancing Bioelectricity Generation. ACS Appl. Mater. Interfaces 2017, 9, 10777-10787. 44. Wang, M.; Xing, C.; Cao, K.; Zhang, L.; Liu, J.; Meng, L., Template-directed Synthesis of Pyrite (FeS2) Nanorod Arrays with an Enhanced Photoresponse. J. Mater. Chem. A 2014, 2, 9496-9505. 45. Wang, X.; Xiang, Q.; Liu, B.; Wang, L.; Luo, T.; Chen, D.; Shen, G., TiO2 Modified FeS Nanostructures with Enhanced Electrochemical Performance for Lithium-Ion Batteries. Sci. Rep. 2013, 3, 2007. 46. Li, B.; Huang, L.; Zhong, M.; Wei, Z.; Li, J., Electrical and Magnetic Properties of FeS2 and CuFeS2 Nanoplates. RSC Adv. 2015, 5, 91103-91107.

ACS Paragon Plus Environment

28

Page 29 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

47. Kim, E.-J.; Kim, J.-H.; Azad, A.-M.; Chang, Y.-S., Facile Synthesis and Characterization of Fe/FeS Nanoparticles for Environmental Applications. ACS Appl. Mater. Interfaces 2011, 3, 1457-1462. 48. Castner, D. G.; Hinds, K.; Grainger, D. W., X-ray Photoelectron Spectroscopy Sulfur 2p Study of Organic Thiol and Disulfide Binding Interactions with Gold Surfaces. Langmuir 1996, 12, 5083-5086. 49. Proietti, E.; Jaouen, F.; Lefèvre, M.; Larouche, N.; Tian, J.; Herranz, J.; Dodelet, J.-P., Ironbased Cathode Catalyst with Enhanced Power Density in Polymer Electrolyte Membrane Fuel Cells. Nature Commun. 2011, 2, 416. 50. Wu, G.; More, K. L.; Xu, P.; Wang, H.-L.; Ferrandon, M.; Kropf, A. J.; Myers, D. J.; Ma, S.; Johnston, C. M.; Zelenay, P., A Carbon-Nanotube-Supported Graphene-Rich Non-precious Metal Oxygen Reduction Catalyst with Enhanced Performance Durability. Chem. Commun. 2013, 49, 3291-3293. 51. Kwak, D.-H.; Han, S.-B.; Lee, Y.-W.; Park, H.-S.; Choi, I.-A.; Ma, K.-B.; Kim, M.-C.; Kim, S.-J.; Kim, D.-H.; Sohn, J.-I.; Park, K.-W., Fe/N/S-doped Mesoporous Carbon Nanostructures as Electrocatalysts for Oxygen Reduction Reaction in Acid Medium. Applied Catalysis B: Environmental 2017, 203 (Supplement C), 889-898. 52. Ren, H.; Wang, Y.; Yang, Y.; Tang, X.; Peng, Y.; Peng, H.; Xiao, L.; Lu, J.; Abruña, H. D.; Zhuang, L., Fe/N/C Nanotubes with Atomic Fe Sites: A Highly Active Cathode Catalyst for Alkaline Polymer Electrolyte Fuel Cells. ACS Catalysis 2017, 7, 6485-6492.

ACS Paragon Plus Environment

29

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 30 of 31

ACS Paragon Plus Environment

30

Page 31 of 31 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials