Graphitic Nanocarbon–Selenium Cathode with Favorable Rate

Feb 23, 2017 - At the core of this effort will be the ability to efficiently convert, store, transport and access energy in a variety of ways. Batteri...
1 downloads 11 Views 5MB Size
Download PDF
Research Article www.acsami.org

Graphitic Nanocarbon−Selenium Cathode with Favorable Rate Capability for Li−Se Batteries Shuai-Feng Zhang,†,‡ Wen-Peng Wang,†,‡ Sen Xin,† Huan Ye,†,‡ Ya-Xia Yin,*,†,‡ and Yu-Guo Guo*,†,‡ †

CAS Key Laboratory of Molecular Nanostructure and Nanotechnology, and Beijing National Laboratory for Molecular Sciences, Institute of Chemistry, Chinese Academy of Sciences (CAS), Beijing 100190, P. R. China ‡ School of Chemistry and Chemical Engineering, University of Chinese Academy of Sciences, Beijing 100049, P. R. China S Supporting Information *

ABSTRACT: A well-organized selenium/carbon nanosheets nanocomposite(Se/CNSs) is prepared by confining chain-like Sen molecules in hierarchically micromesoporous carbon nanosheets. A unique two-dimensional morphology and high graphitization degree of carbon nanosheets benefits fast Li+/e− access to the active Se, which guarantees a high utilization of Se during the(de)lithiation process. Besides, the chain-like Se molecules confined in the carbon matrix could alleviate the shuttle effect of polyselenides and promise a stable electrochemistry. Therefore, the resultant Se/CNSs delivers a highly reversible capacity, a long cycle life and favorable rate capabilities. Furthermore, a Li−Se pouch cell built from a metallic Li anode and the as-prepared Se/CNSs cathode exhibits an excellent electrochemical performance, demonstrating the potential of Se/CNSs in serving future energy storage devices with high energy density. KEYWORDS: Li−Se batteries, graphitic carbon, Se cathode, chain-like Se molecules, high-rate capability

1. INTRODUCTION Commercial lithium-ion batteries(LIBs) with limitation in their theoretical energy output do not meet the ever-increasing demand on further elevating the energy density for future storage applications.1−4 Therefore, interests have been taken on Li−S batteries because of their high theoretical energy density of 2560 W h kg−1, which originates from the high electrode capacities (Li anode = 3860 mA h g−1, S cathode = 1672 mA h g−1) as yielded by the two-electron reaction between both electrodes.5−7 However, the S cathode in the Li−S battery suffers from the insulating nature of S and unavoidable dissolution of polysulfide intermediates during the cycling process.8 Carbon matrixes with high electric conductivity and optimized porous structure have been considered as the most promising ways to tackle the above problems with progress made in recent years.9−14 Unfortunately, limited cycling life and poor rate performance still inhibit the practical use of Li−S batteries. Selenium, which belongs to the same group as S, has similar two-electron electrochemistry versus Li. Meanwhile, the density of Se as high as 4.82 g cm−3 endows Li−Se batteries with high volumetric capacity of selenium(3253 mA h cm−3), which is close to that of S (3467 mA h cm−3).15−18 Apart from that, Se possesses much higher electric conductivity (10−5 S cm−1) than S (10−30 S cm−1). Therefore, Li−Se battery may be a promising candidate for both electric vehicles and electronic devices, where battery systems with high volumetric energy density are desired because of the limited space. However, polyselenide © 2017 American Chemical Society

dissolution during cycling in ether-based electrolytes (which is similar to the polysulfides) leads to fast capacity fading, low Coulombic efficiency, and poor cycling stability of Li−Se batteries.19−22 Much attempt has been made to suppress the dissolution of polyselenides.23,24 Confining Se in various carbon matrixes, such as mesoporous carbon,25 micromesoporous carbon,26−28 and graphene,29,30 has been proved to be an effective strategy to retard the dissolution of polyselenides and improve the electric conductivity of cathode. Carbon matrix with diverse pore structures plays a critical role in determining the specific presence of Se molecules (e.g., cyclic Se8, chain-like Sen) and consequently accounting for different physical/chemical properties of Se. It has been found that chain-like Sen molecules are thermodynamically more stable and facilitate faster electronic conduction than the cyclic Se8 molecules.31−33 According to literature, nanoporous carbon matrixes are commonly prepared from two or more steps including the pyrolysis of carbon precursor and tuning the pore structure by chemical activation (e.g., KOH, CO2, H2O).9,17 Nevertheless, the as-prepared nanoporous pyrolytic carbons are usually amorphous and deliver poor electric conductivity. Therefore, it is highly desired to develop a facile method to synthesize Received: December 28, 2016 Accepted: February 22, 2017 Published: February 23, 2017 8759

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

Research Article

ACS Applied Materials & Interfaces

Figure 1. Schematic illustration showing the preparation process of the Se/CNSs composite. selenium electrode was about 2 mg cm−1. Lithium foil was used as counter electrode and reference electrode. Celgard separator was used as the isolation layer between the cathode and the anode. A Land electrochemical testing system was used to perform the electrochemical measurements of Li−Se batteries. The CV test was performed at the voltage range of 1.0−3.0 V with a scan rate of 0.05 mV s−1 on a Princeton PARSTAT MC 1000 multichannel electrochemical workstation. A Li−Se pouch cell was fabricated by using the laminated structure with 4 cathodes and 5 anodes. The slurry consisting of Se/CNSs-850, SP, NaCMC, and SBR with the weight ratio of 93:3:1.5:2.5 was coated evenly on the both sides of the Al current collector. The area density of the obtained cathode was about 5.7 mg cm−2. The electrolyte used for pouch cell stayed the same. The electrochemical measurements were performed using the land electrochemical testing system with the current range from 1 mA to 5 A.

nanoporous carbon materials with a high graphitization degree to host chain-like Sen molecules.32 Herein, we present a new type of Se/C cathode material by confining chain-like Sen into a highly graphitic carbon nanosheet(CNS), which is prepared by pyrolysis of potassium citrate by a low-cost and easy-handing method. A highly reversible capacity (almost equal to the theoretical capacity of Se), a long cycle life (1000 cycles at 0.5 C), and favorable rate capabilities (390 mA h g−1 at 10 C) of Li−Se battery are achieved by using the Se/CNSs cathode. The superior electrochemical performance is attributed to a rich content of micro/mesopores and high graphitization degree of the carbon host. Furthermore, we have successfully realized a Li−Se pouch cell from the Se/CNSs cathode, which exhibits admirable cycling stability in carbonate-based electrolyte.

3. RESULTS AND DISCUSSION The CNSs were synthesized by one-step method without extra activation agent (Figure 1). According to the thermogravimetric analysis (Figure S1), the potassium citrate was first heated to 600 °C for 2 h under Ar atmosphere to completely decompose to C, H2O (g), and K2CO3. After that, the mixture was further carbonized at 850 °C for 2 h to obtain micromesoporous carbon materials (denoted as CNSs-850) by the self-generated K2CO3 activation.34−36 After the mixture of Se and CNSs-850 was heated at 240 °C in Ar atmosphere, Se was infiltrated into the micropores of CNSs-850 driven by the capillary force to obtain Se/C composites (abbreviated as Se/CNSs-850).37 For comparison, the Se/CNSs-600 was prepared with the similar process except that the carbon matrix was prepared by only carbonization at 600 °C for 2 h. SEM and TEM characterizations were employed to evaluate the morphology of the CNSs-850 and Se/CNSs-850. Figure 2a and 2c shows the two-dimensional nanosheet structure of CNSs-850. The CNSs-600 also has the similar structure (Figure S2a). The thickness of CNSs-850 is less than 100 nm, which is in favor of Li+ diffusion and electrolyte infiltration to the electrode. Meanwhile, the width of 3−8 μm can effectively prevent the agglomeration during the electrode fabrication procedure. Furthermore, one can clearly see from HRTEM image (Figure 2d) that CNSs-850 have abundant nanopores and the spacing of aligned lattice fringes in the CNSs is about 0.34 nm, in accordance with the (002) plane of the sp2 carbon, indicating its high electric conductivity. After loading selenium, no selenium residues can be observed on the surface of carbon materials(Figures 2b and S3a and b).38 The EDX elemental mappings (Figure 2e) demonstrate that the Se is uniformly distributed in the carbon materials, which is consistent with the results of the SEM images of Se/CNSs-850. Meanwhile, no obvious change of morphology feature about Se/CNSs-600 is achieved after loading Se into CNSs-600(Figure S2b). XRD patterns and Raman spectroscopy are used to further probe the structure features of Se/CNSs composites. XRD patterns of selenium power, Se/CNSs-850, Se/CNSs-600 are shown in Figure 3a. After the heating process, the diffraction peaks of crystalline Se in Se/CNSs-850 disappear, indicating

2. EXPERIMENTAL SECTION 2.1. Synthesis of Materials. 2.1.1. Synthesis of CNSs. All chemicals were purchased from Sinopharm Chemical Reagent Co., Ltd., and used directly without any further purification. In a typical synthesis, 10 g of potassium citrate was grinded to powder and then poured into a nickel boat. The white power was decomposed at 600 °C in Ar atmosphere for 2 h and subsequently carbonized at 850 °C for another 2 h with a heating ramp of 5 °C min−1. After it was cooled down to room temperature, the product was slowly added into diluted HCl and stirred for 1 h. Then, the mixture was filtered, washed with the deionized water several times, and dried at 80 °C for 12 h to obtain the carbon materials (denoted as CNSs-850). As a comparison, another carbon material was prepared under the same process except that the carbonization temperature was only 600 °C (denoted as CNSs-600). 2.1.2. Synthesis of Se/CNSs. The as-prepared CNSs-850 and Se powder with the weight ratio of 4:6 were mixed evenly and pressed into a slice at 10 MPa. After that, the Se/CNSs-850 was obtained by infusing Se into the carbon material under argon atmosphere at 240 °C for 12 h. The Se/CNSs-600 was also obtained in the same way for comparison. 2.2. Material Characterizations. Transmission electron microscopy (TEM) images and EDXS elemental mapping images were carried out by using a Tecnai G2 F20 U-TWIN operated at 200 kV. SEM images of the as-prepared samples were taken by a JEOL 6710F field-emission scanning electron microscope (FE-SEM) operated at 10 kV. XRD measurements were collected by using Cu Kα radiation on a Rigaku D/max 2500 diffractometer. Nitrogen adsorption/desorption isotherms were obtained to analyze the pore structure of obtained materials by using an Autosorb-1 analyzer from Quantachrome Instruments at 77.3 K. A TG Netzsch 449F3 was used to perform thermogravimetric analysis (TGA). Raman spectroscopy was obtained by using a Digilab FTS3500 (bio-Rad) with a laser wavelength of 532 nm. X-ray photoelectron spectroscopy (XPS) was measured through a Thermos Scientific ESCA Lab 250Xi with 200 W monochromatic Al Kα radiation. 2.3. Electrochemical Characterizations. A coin-type cell with 1 M LiPF6 dissolved in EC/DMC/DEC (1:1:1, based on volume) as electrolyte was assembled in an argon-filled glovebox with less than 0.1 ppm of O2 and 0.1 ppm of H2O and used to perform the electrochemical performance of Li−Se battery. The working electrode was prepared by coating the slurry consisting of Se/CNSs composite, Super P, NaCMC, and SBR at a weight ratio of 80:10:5:5 on the pure aluminum (99.6%, Goodfellow). The area density of obtained 8760

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

Research Article

ACS Applied Materials & Interfaces

demonstrating some crystal selenium still exists. According to the Figure 2b, the peaks of Se in Se/CNSs in Raman spectra is blueshifted to about 256.3 cm−1 in comparison with crystal Se and the peak intensity of Se in Se/CNSs-850 is lower than that of Se/CNSs-600, which may be attributed to the change of existing form of Se molecules.39,40 In addition, the peaks at ∼1350 cm−1 are related to the defected and disordered carbon and the peaks at ∼1580 cm−1 are related to the sp2 hybrid carbon atoms.41 The intensity ratio of ID/IG in Se/CNSs-850 is about 0.625 and lower than that of Se/CNSs-600, revealing that the CNSs-850 have high graphitization degree and excellent electric conductivity. This result is also proved by the 2D peeks at ∼2700 cm−1 in the Se/CNSs-850. The porous structures of the CNSs and Se/CNSs composite are investigated with N2 adsorption/desorption isotherms. According to Figure 3c, CNSs-850 has the type IV isotherm, implying the massive micro/mesopores existed in the carbon materials. Those pores in CNSs-850 are derived from the decomposition of the precursor before 600 °C and the activation of K2CO3 at the carbonization process of 850 °C. The specific BET area is 1358 cm2 g−1 and the total pore volume is about 0.631 cm3 g−1, in which the microporous volume contribution is 0.502 cm3 g−1(calculated from the Density Functional Theory method).42−44 In comparison, the CNSs-600 only has microporous structure and its pore volume (0.3 cm3 g−1) is lower than that of CNSs-850. This result suggests that CNSs-850 could host more Se than CNSs-600. Figure 3d shows that the pore size distribution of CNSs-850 is concentrated on nanopores of 0.8, 1.2, and 2 nm. These micropores have been proved to confine Se molecules in chainlike structure from previous report.18,33 After loading Se, the pore volume of Se/CNSs-850 is reduced to 0.03 cm3 g−1, demonstrating that Se is completely infiltrated into the nanopores of CNSs(Figure S4). Thermogravimetric analysis

Figure 2. Morphological characterization of the as-prepared CNSs-850 and Se/CNSs-850 composites. (a) SEM images of CNSs-850 and (b) Se/CNSs-850. (c) TEM images and (d) HRTEM images of CNSs850. (e) Images by scanning transmission electron microscopy (STEM) and corresponding elemental mappings of bare Se and C.

the selenium is in an amorphous state and completely dispersed into nanoporous carbon materials.20 However, the crystal diffraction peaks of Se in Se/CNSs-600 is clearly observed,

Figure 3. (a) XRD patterns and (b) Raman spectra of Se powder, Se/CNSs-600, and Se/CNSs-850. (c) N2 adsorption/desorption isotherms and (d) pore-size distribution curves of CNSs-600 and CNSs-850 obtained by the DFT method. 8761

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

Research Article

ACS Applied Materials & Interfaces

Figure 4. Electrochemical performance of the Se/CNSs-850 cathode in a Li−Se battery (a). Typical discharge/charge profiles and (b) cycling performance of Se/CNSs-850 at 0.1 C. (c) Discharge/charge voltage profiles and (d) cycling performance at different C rates. (e) Long cycling performance and Coulombic efficiency at 0.5 C. The specific capacity values are based on the mass of Se in composites.

theoretical capacity of Se and consistent with previous reports.40 Possible reason might come from the formation of a solid electrolyte interface (SEI) film on the surface of Se/ CNSs-850 and the reversible lithiation of highly graphitic carbon. The detailed reason will be discussed later. Upon second cycle, the specific discharge capacity is almost equal to theoretical capacity of Se, implying that chain-like Sen in micropores has high electrochemical activity. The cycling performance of Se/CNSs-850 is shown in Figure 4b. After 100 cycles, the reversible capacity retains about 600 mA h g−1, indicating the superior cycling stability. In addition, the Coulombic efficiency after the first cycle is nearly 100%, confirming the complete alleviation of shuttle effect. After disassembling the cell, the morphology of Se/CNSs-850 still keeps the same, proving its superior structure stability(Figure S7). To evaluate its long cycle performance, the Se/CNSs-850 was also performed at the current of 0.5 C for 1000 cycles. The reversible capacity still remains about 376 mA h g−1 and the fading rate is as low as 0.044% per cycle, proving the excellent cycling stability of Se/CNSs-850. As the comparison, the Se/

is used to determine the Se ratio of the composite. Figure S5 shows the percentage of Se in the Se/CNSs-850 is about 60%.45 Se/CNSs-600 is prepared with the same loading amount of Se for comparison. Coin cells (2032) were fabricated to evaluate the electrochemical performances of Li−Se batteries consisting of Se/ CNSs-850 composites as the cathode and Li foil as the anode. The cyclic voltammograms of Se/CNSs-850 was measured between 1.0 and 3.0 V at the rate of 0.05 mV s−1 (Figure S6). At the initial discharge−charge process, one pair of redox peaks is observed around 1.75/2.2 V, corresponding to the highly reversible conversion of chain-like Sen to Li2Se. In the subsequent cycles, sharp redox peaks almost overlap together, demonstrating that the composites have excellent cycling stability. Figure 4a shows the typical galvanostatic discharge/ charge curves (GDC) of Se/CNSs-850 at 0.1 C (1 C = 675 mA g−1), which coincides with the cyclic voltammetry analysis. At the initial cycle, Se/CNSs-850 exhibits the initial specific capacity of nearly 900 mA h g−1 based on the mass of Se in Se/ CNSs-850 composite, which is much higher than the 8762

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

Research Article

ACS Applied Materials & Interfaces

Figure 5. XPS spectra of the Se/CNSs-850 cathode. (a) C 1s spectra and (b) Se 3d spectra of the pristine cathode before discharge, after initial discharge to 1 V, and after initial charge back to 3 V.

Figure 6. Electrochemical performance of a Li−Se pouch cell based on the Se/CNSs-850 cathode. (a) Optical image showing the pouch cell is powering a light emitting diode(LED). (b) Voltage profiles and (c) cycling performance at 0.1 C.

process, two peaks at about 284.8 and 286.5 eV are observed in the C 1s spectra (Figure 5a), corresponding to the C−C and C−O, respectively.18 After the discharge process, three new peaks at 290.2, 288.6, and 283.9 eV are generated and ascribed to the C−F, −COOLi, and Cn−Li.47 The C−F and −COOLi generated during discharge process may be resulted from the decomposition of the electrolytes to from solid electrolyte interface (SEI) film on the surface of Se/CNSs-850 and the Cn−Li might come from the lithiation of sp2 hybrid carbon. After the subsequent charge process, the peaks of C−F, −COOLi still remain, but the peaks of Cn−Li disappear. Those results indicate that the irreversible decomposition of electrolytes and the reversible lithiation of highly graphitic carbon occur during the first discharge/charge process.48 As a result, Li−Se batteries show low Coulombic efficiency of 77.7% (Figure 4a) and slightly high capacity during the initial discharge/charge process. Similar phenomenon is also observed for pure CNSs-850 electrode (Figure S10). Furthermore, no obvious change of the peaks of C−F and −COOLi is observed at the second cycle (Figure S11), demonstrating that the stable SEI layer has generated after first cycle. This coincides with the high Coulombic efficiency about almost 100% after the first cycle in GDC curves of Se/CNSs-850. In the spectra of Se(Figure 4b), two peaks at 55.4 and 56.2 eV correspond to the Se3d5/2 and Se3d3/2, respectively, before cycling.18,33,49 After the discharge process, the binding energy of Se3d5/2 and Se3d3/2 is reduced to 55.1 and 55.9 eV due to the lithiation of Se. After the subsequent charge process, the binding energy is converted back to 55.4 and 56.2 eV respectively, indicating the excellent reversibility of chain-like Sen molecules in Se/CNSs-850.33 To further verify the practical application of our Se/CNSs composite, we prepared the Se/CNSs-850 through our easyhanding one-step method and assembled a Li−Se pouch cell

CNSs-600 has an obvious voltage profile platform at 2.4−2.2 V at the first discharge process (Figure S8a), which may be attributed to the side reaction between crystal Se molecules on the surface of carbon material and carbonate-based electrolytes. During the sequential cycles, the reversible capacity of Se/ CNSs-600 about 400 mA h g−1, lower than that of Se/CNSs850, is achieved because of fewer nanopores in the CNSs-600 (Figure S8b). The rate capability of Se/CNSs-850 is further investigated at various rates from 0.1 to 10 C (Figure 4c and d). The specific capacity is reduced from 700 to 390 mA h g−1 when the current density increases from 0.1 to 10 C, suggesting its superior rate capability. One slope voltage plateau at about 1.9 V still maintains and no obvious polarization is observed even at 10 C, validating the exceptional stability and conductivity of Se/ CNSs-850. When the current recovers to 0.5 C, the Se/CNSs850 still deliver the reversible capacity as high as 600 mA h g−1, which corresponds to 89% of the theoretical capacity (Figure 4d). These results manifest the remarkable rate capability and abuse tolerance of Se/CNSs-850.46 The interface resistance of Se/C electrode is measured through the electrochemical impedance spectroscopy (EIS). According to Figure S9a, the charge-transfer resistance (Rct) of the pristine Se/CNSs-850 cell is obviously smaller than that of Se/CNSs-600, proving the fast kinetic process of Se/CNSs-850 (Figure S9b). In addition, the interface resistance of Se/CNSs-850 cell does not change significantly even after 100 cycles, demonstrating the high interface stability of Se/CNSs-850. These results are also confirmed by the excellent electrochemical performances of Se/ CNSs-850. X-ray photoelectron spectroscopy was employed to further clarify the chemical composition change of Se/CNSs-850 during the discharge and charge process. Before discharge 8763

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

ACS Applied Materials & Interfaces

■

with laminated structure(Figure 6a). The electrochemical performance of Se/CNSs-850 prepared in large quantity is first tested in coin cells at 0.1 C. The reversible capacity of about 650 mA h g−1 is achieved, implying the excellent homogeneity and stability of Se/CNSs synthesis (Figure S12). In Figure 6b, the pouch cell exhibits a reversible capacity about 620 mA h at 0.1 C and the Coulombic efficiency is close to 100% after the first cycle. After 20 cycles, the reversible capacity still retains about 600 mA h, indicating the good cycling stability (Figure 6c). The Se/CNSs-850 with remarkable electrochemical performance can be attributed to the unique features of CNSs: (1) The micromesoporous structure of CNSs can load and confine Se into chain-like formation, thus suppressing the shuttle effect during the electrochemical process in carbonate-based electrolyte and promising high electrochemical activity and excellent cycling stability of Li−Se batteries. (2) The carbon materials with abundant hybrid sp2 carbon can effectively improve the electric conductivity of electrode and achieve high rate capability of Li−Se batteries. (3) The two-dimensional and interlinked structure can shorten Li+ ion diffusion distance and facilitate the electrolyte infiltration. Therefore, the twodimensional carbon nanosheets with abundant sp2 hybrid carbon prepared at 850 °C may be the ideal substrate materials for Li−Se batteries.

AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected] (Y.-X.Y.). *Tel/Fax:(+86)-10-82617069. E-mail: [email protected] (Y.G.G.). ORCID

Sen Xin: 0000-0002-0546-0626 Yu-Guo Guo: 0000-0003-0322-8476 Notes

The authors declare no competing financial interest.

■

ACKNOWLEDGMENTS This work was supported by the Ministry of Science and Technology of the People’s Republic of China (Grant No. 2016YFA0202500), the “Strategic Priority Research Program” of the Chinese Academy of Sciences (Grant No. XDA09010300), the National Natural Science Foundation of China (Grant Nos. 51225204, U1301244, and 21127901), and the Chinese Academy of Sciences.

■

REFERENCES

(1) Armand, M.; Tarascon, J. M. Building Better Batteries. Nature 2008, 451, 652−657. (2) Kang, B.; Ceder, G. Battery Materials for Ultrafast Charging and Discharging. Nature 2009, 458, 190−193. (3) Bruce, P. G.; Scrosati, B.; Tarascon, J. M. Nanomaterials for Rechargeable Lithium Batteries. Angew. Chem., Int. Ed. 2008, 47, 2930−2946. (4) Melot, B. C.; Tarascon, J. M. Design and Preparation of Materials for Advanced Electrochemical Storage. Acc. Chem. Res. 2013, 46, 1226−1238. (5) Yin, Y. X.; Xin, S.; Guo, Y. G.; Wan, L. J. Lithium-Sulfur Batteries: Electrochemistry, Materials, and Prospects. Angew. Chem., Int. Ed. 2013, 52, 13186−13200. (6) Manthiram, A.; Fu, Y.; Chung, S. H.; Zu, C.; Su, Y. S. Rechargeable Lithium-Sulfur Batteries. Chem. Rev. 2014, 114, 11751− 11787. (7) Cao, J.; Chen, C.; Zhao, Q.; Zhang, N.; Lu, Q.; Wang, X.; Niu, Z.; Chen, J. A Flexible Nanostructured Paper of a Reduced Graphene Oxide-Sulfur Composite for High-Performance Lithium-Sulfur Batteries with Unconventional Configurations. Adv. Mater. 2016, 28, 9629−9636. (8) Zhu, S.; Wang, Y.; Jiang, J.; Yan, X.; Sun, D.; Jin, Y.; Nan, C.; Munakata, H.; Kanamura, K. Good Low-Temperature Properties of Nitrogen-Enriched Porous Carbon as Sulfur Hosts for High-Performance Li-S Batteries. ACS Appl. Mater. Interfaces 2016, 8, 17253−17259. (9) Lee, J. T.; Zhao, Y.; Thieme, S.; Kim, H.; Oschatz, M.; Borchardt, L.; Magasinski, A.; Cho, W. I.; Kaskel, S.; Yushin, G. Sulfur-Infiltrated Micro- and Mesoporous Silicon Carbide-Derived Carbon Cathode for High-Performance Lithium Sulfur Batteries. Adv. Mater. 2013, 25, 4573−4579. (10) Ji, X.; Lee, K. T.; Nazar, L. F. A Highly Ordered Nanostructured Carbon-Sulphur Cathode for Lithium-Sulphur Batteries. Nat. Mater. 2009, 8, 500−506. (11) Wang, H.; Yang, Y.; Liang, Y.; Robinson, J. T.; Li, Y.; Jackson, A.; Cui, Y.; Dai, H. Graphene-Wrapped Sulfur Particles as a Rechargeable Lithium-Sulfur Battery Cathode Material with High Capacity and Cycling Stability. Nano Lett. 2011, 11, 2644−2647. (12) Cai, W.; Zhou, J.; Li, G.; Zhang, K.; Liu, X.; Wang, C.; Zhou, H.; Zhu, Y.; Qian, Y. B. N-Co-Doped Graphene Supported Sulfur for Superior Stable Li-S Half Cell and Ge-S Full Battery. ACS Appl. Mater. Interfaces 2016, 8, 27679−27687. (13) Bai, S.; Liu, X.; Zhu, K.; Wu, S.; Zhou, H. Metal−Organic Framework-Based Separator for Lithium−Sulfur Batteries. Nat. Energy 2016, 1, 16094.

4. CONCLUSIONS In summary, we have achieved a scalable synthesis of a novel Se/C composite cathode material at a low cost. Among Se/ CNSs composite, chain-like Sen molecule is confined in the micro/mesopores carbon nanosheets with highly graphitic degree, which effectively eliminate the shuttle of polyselenides and exhibit superior electrochemical performance in Li−Se batteries. The optimal Se/C composite (Se/CNSs-850) shows a reversible capacity as high as 672 mA h g−1(almost the theoretical capacity of Se), remains about 376 mA h g−1 after 1000 cycles at 0.5 C and is able to remain a reversible capacity of ∼390 mA h g−1 at a high rate of 10 C, which strongly supports the favorable electrochemical stability and rate capability of Se/CNSs cathode material. Furthermore, a Li− Se pouch-cell is built based on the above Se/C composite cathode. We believe such a carbon matrix host with high graphitization degree and abundant micro/mesopores is promising for building electrode materials with large specific capacities to enable high-energy storage systems.

■

Research Article

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acsami.6b16708. TGA measurement of potassium citrate, SEM images of CNSs-600 and Se/CNSs-600, TEM image and HRTEM image of Se/CNSs-850, N2 adsorption/desorption of the Se/CNSs-850, TGA curve of Se/CNSs-850, CV profiles of Se/CNSs-850, SEM image of Se/CNSs-850 after 100 cycles, electrochemical performances of Se/CNSs-600, EIS of Se/CNSs, discharge/charge curves of CNSs-850 without loading Se, XPS spectra of the as-prepared Se/ CNSs-850 for C 1s region during the second cycle, and discharge/charge curves of Se/CNSs-850 prepared in quantity at the current of 0.1 C (PDF) 8764

DOI: 10.1021/acsami.6b16708 ACS Appl. Mater. Interfaces 2017, 9, 8759−8765

Research Article

ACS Applied Materials & Interfaces (14) Zhang, C.; Wu, H. B.; Yuan, C.; Guo, Z.; Lou, X. W. Confining Sulfur in Double-Shelled Hollow Carbon Spheres for Lithium-Sulfur Batteries. Angew. Chem., Int. Ed. 2012, 51, 9592−9595. (15) Yang, C. P.; Yin, Y. X.; Guo, Y. G. Elemental Selenium for Electrochemical Energy Storage. J. Phys. Chem. Lett. 2015, 6, 256−266. (16) Abouimrane, A.; Dambournet, D.; Chapman, K. W.; Chupas, P. J.; Weng, W.; Amine, K. A New Class of Lithium and Sodium Rechargeable Batteries Based on Selenium and Selenium-Sulfur as a Positive Electrode. J. Am. Chem. Soc. 2012, 134, 4505−4508. (17) Xu, G. L.; Xu, Y. F.; Fang, J. C.; Peng, X. X.; Fu, F.; Huang, L.; Li, J. T.; Sun, S. G. Porous Graphitic Carbon Loading Ultra High Sulfur as High-Performance Cathode of Rechargeable Lithium-Sulfur Batteries. ACS Appl. Mater. Interfaces 2013, 5, 10782−10793. (18) Li, Z.; Yuan, L.; Yi, Z.; Liu, Y.; Huang, Y. Confined Selenium within Porous Carbon Nanospheres as Cathode for Advanced Li−Se Batteries. Nano Energy 2014, 9, 229−236. (19) Qu, Y.; Zhang, Z.; Jiang, S.; Wang, X.; Lai, Y.; Liu, Y.; Li, J. Confining Selenium in Nitrogen-Containing Hierarchical Porous Carbon for High-Rate Rechargeable Lithium−Selenium Batteries. J. Mater. Chem. A 2014, 2, 12255−12261. (20) Jiang, S.; Zhang, Z.; Lai, Y.; Qu, Y.; Wang, X.; Li, J. Selenium Encapsulated into 3D Interconnected Hierarchical Porous Carbon Aerogels for Lithium−Selenium Batteries with High Rate Performance and Cycling Stability. J. Power Sources 2014, 267, 394−404. (21) Zhang, Z.; Yang, X.; Guo, Z.; Qu, Y.; Li, J.; Lai, Y. Selenium/ Carbon-Rich Core−Shell Composites as Cathode Materials for Rechargeable Lithium−Selenium Batteries. J. Power Sources 2015, 279, 88−93. (22) Wang, X.; Zhang, Z.; Qu, Y.; Wang, G.; Lai, Y.; Li, J. SolutionBased Synthesis of Multi-Walled Carbon Nanotube/Selenium Composites for High Performance Lithium−Selenium Battery. J. Power Sources 2015, 287, 247−252. (23) Cui, Y.; Abouimrane, A.; Lu, J.; Bolin, T.; Ren, Y.; Weng, W.; Sun, C.; Maroni, V. A.; Heald, S. M.; Amine, K. (De)Lithiation Mechanism of Li/SeSx(X = 0−7). Batteries Determined by in Situ Synchrotron X-ray Diffraction and X-ray Absorption Spectroscopy. J. Am. Chem. Soc. 2013, 135, 8047−8056. (24) Zhang, Z.; Yang, X.; Wang, X.; Li, Q.; Zhang, Z. TiO2−Se Composites as Cathode Material for Rechargeable Lithium−Selenium Batteries. Solid State Ionics 2014, 260, 101−106. (25) Luo, C.; Xu, Y.; Zhu, Y.; Liu, Y.; Zheng, S.; Liu, Y.; Langrock, A.; Wang, C. Selenium@Mesoporous Carbon Composite with Superior Lithium and Sodium Storage Capacity. ACS Nano 2013, 7, 8003− 8010. (26) Lee, J. T.; Kim, H.; Oschatz, M.; Lee, D.-C.; Wu, F.; Lin, H.-T.; Zdyrko, B.; Cho, W. I.; Kaskel, S.; Yushin, G. Micro- and Mesoporous Carbide-Derived Carbon-Selenium Cathodes for High-Performance Lithium Selenium Batteries. Adv. Energy Mater. 2015, 5, 1400981. (27) Zhang, H.; Yu, F.; Kang, W.; Shen, Q. Encapsulating Selenium into Macro-/Micro-Porous Biochar-Based Framework for HighPerformance Lithium-Selenium Batteries. Carbon 2015, 95, 354−363. (28) Xin, S.; Yu, L.; You, Y.; Cong, H. P.; Yin, Y. X.; Du, X. L.; Guo, Y. G.; Yu, S. H.; Cui, Y.; Goodenough, J. B. The Electrochemistry with Lithium versus Sodium of Selenium Confined to Slit Micropores in Carbon. Nano Lett. 2016, 16, 4560−4568. (29) Youn, H. C.; Jeong, J. H.; Roh, K. C.; Kim, K. B. GrapheneSelenium Hybrid Microballs as Cathode Materials for High-Performance Lithium-Selenium Secondary Battery Applications. Sci. Rep. 2016, 6, 30865. (30) Han, K.; Liu, Z.; Ye, H.; Dai, F. Flexible Self-Standing Graphene−Se@CNT Composite Film as a Binder-Free Cathode for Rechargeable Li−Se Batteries. J. Power Sources 2014, 263, 85−89. (31) Murphy, K. E.; Wunderlich, B. B.; Wunderlich, B. Effect of Structure on the Electrical Conductivity of Selenium. J. Phys. Chem. 1982, 86, 2827−2835. (32) Yang, C. P.; Xin, S.; Yin, Y. X.; Ye, H.; Zhang, J.; Guo, Y. G. An Advanced Selenium-Carbon Cathode for Rechargeable LithiumSelenium Batteries. Angew. Chem., Int. Ed. 2013, 52, 8363−8367.

(33) Ye, H.; Yin, Y.-X.; Zhang, S.-F.; Guo, Y.-G. Advanced Se−C Nanocomposites: A Bifunctional Electrode Material for Both Li−Se and Li-Ion Batteries. J. Mater. Chem. A 2014, 2, 13293−13298. (34) Sevilla, M.; Fuertes, A. B. Direct Synthesis of Highly Porous Interconnected Carbon Nanosheets and Their Application as HighPerformance Supercapacitors. ACS Nano 2014, 8, 5069−5078. (35) Valtchev, V.; Tosheva, L. Porous Nanosized Particles: Preparation, Properties, and Applications. Chem. Rev. 2013, 113, 6734−6760. (36) Fuertes, A. B.; Sevilla, M. Hierarchical Microporous/ Mesoporous Carbon Nanosheets for High-Performance Supercapacitors. ACS Appl. Mater. Interfaces 2015, 7, 4344−4353. (37) Zeng, L.; Wei, X.; Wang, J.; Jiang, Y.; Li, W.; Yu, Y. Flexible One-Dimensional Carbon−Selenium Composite Nanofibers with Superior Electrochemical Performance for Li−Se/Na−Se Batteries. J. Power Sources 2015, 281, 461−469. (38) Zhang, J.; Zhang, Z.; Li, Q.; Qu, Y.; Jiang, S. Selenium Encapsulated into Interconnected Polymer-Derived Porous Carbon Nanofiber Webs as Cathode Materials for Lithium-Selenium Batteries. J. Electrochem. Soc. 2014, 161, A2093−A2098. (39) Poborchii, V. V.; Kolobov, A. V.; Tanaka, K. An in Situ Raman Study of Polarization-Dependent Photocrystallization in Amorphous Selenium Films. Appl. Phys. Lett. 1998, 72, 1167−1169. (40) Zeng, L.; Zeng, W.; Jiang, Y.; Wei, X.; Li, W.; Yang, C.; Zhu, Y.; Yu, Y. A Flexible Porous Carbon Nanofibers-Selenium Cathode with Superior Electrochemical Performance for Both Li-Se and Na-Se Batteries. Adv. Energy Mater. 2015, 5, 1401377. (41) Zhang, L.; Yang, X.; Zhang, F.; Long, G.; Zhang, T.; Leng, K.; Zhang, Y.; Huang, Y.; Ma, Y.; Zhang, M.; Chen, Y. Controlling the Effective Surface Area and Pore Size Distribution of sp2 Carbon Materials and Their Impact on the Capacitance Performance of These Materials. J. Am. Chem. Soc. 2013, 135, 5921−5929. (42) Titirici, M.-M.; White, R. J.; Falco, C.; Sevilla, M. Black Perspectives for a Green Future: Hydrothermal Carbons for Environment Protection and Energy Storage. Energy Environ. Sci. 2012, 5, 6796−6822. (43) Yu, D.; Goh, K.; Wang, H.; Wei, L.; Jiang, W.; Zhang, Q.; Dai, L.; Chen, Y. Scalable Synthesis of Hierarchically Structured Carbon Nanotube-Graphene Fibres for Capacitive Energy Storage. Nat. Nanotechnol. 2014, 9, 555−562. (44) Huang, Y.; Peng, L.; Liu, Y.; Zhao, G.; Chen, J. Y.; Yu, G. Biobased Nano Porous Active Carbon Fibers for High-Performance Supercapacitors. ACS Appl. Mater. Interfaces 2016, 8, 15205−15215. (45) Lai, Y.; Gan, Y.; Zhang, Z.; Chen, W.; Li, J. Metal-Organic Frameworks-Derived Mesoporous Carbon for High Performance Lithium−Selenium Battery. Electrochim. Acta 2014, 146, 134−141. (46) Li, Q.; Liu, H.; Yao, Z.; Cheng, J.; Li, T.; Li, Y.; Wolverton, C.; Wu, J.; Dravid, V. P. Electrochemistry of Selenium with Sodium and Lithium: Kinetics and Reaction Mechanism. ACS Nano 2016, 10, 8788−8795. (47) Sun, J.; Zheng, G.; Lee, H. W.; Liu, N.; Wang, H.; Yao, H.; Yang, W.; Cui, Y. Formation of Stable Phosphorus-Carbon Bond for Enhanced Performance in Black Phosphorus Nanoparticle-Graphite Composite Battery Anodes. Nano Lett. 2014, 14, 4573−4580. (48) Luo, C.; Zhu, Y.; Wen, Y.; Wang, J.; Wang, C. Carbonized Polyacrylonitrile-Stabilized SeSx Cathodes for Long Cycle Life and High Power Density Lithium Ion Batteries. Adv. Funct. Mater. 2014, 24, 4082−4089. (49) Sun, F.; Cheng, H.; Chen, J.; Zheng, N.; Li, Y.; Shi, J. Heteroatomic SenS8-N Molecules Confined in Nitrogen-Doped Mesoporous Carbons as Reversible Cathode Materials for HighPerformance Lithium Batteries. ACS Nano 2016, 10, 8289−8298.