Growth and Electrical Properties of Free-Standing Zinc Oxide

Synthesis of free-standing two-dimensional semiconductor zinc oxide nanomembranes using a bottom-up approach on r-plane sapphire substrates utilizing ...
0 downloads 13 Views 5MB Size
Subscriber access provided by La Trobe University Library

Article

Growth and Electrical Properties of FreeStanding Zinc Oxide Nanomembranes Subrina Rafique, Lu Han, and Hongping Zhao Cryst. Growth Des., Just Accepted Manuscript • DOI: 10.1021/acs.cgd.5b01738 • Publication Date (Web): 01 Feb 2016 Downloaded from http://pubs.acs.org on February 11, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Crystal Growth & Design is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Growth and Electrical Properties of Free-Standing Zinc Oxide Nanomembranes Subrina Rafique 1†, Lu Han 1†, Hongping Zhao 1* 1

Department of Electrical Engineering and Computer Science, Case Western Reserve University, Cleveland, OH 44106, USA. *Correspondence to: [email protected] Abstract We report the synthesis of free-standing two-dimensional (2D) semiconductor zinc oxide

(ZnO) nanomembranes (NMs) using a bottom-up approach: nanomembranes grown from the faceted sidewalls of horizontally-oriented ZnO nanowires (NWs). The ZnO NMs were synthesized on r-plane sapphire substrates utilizing high purity ZnO powder and graphite mixture and oxygen (O2) as source materials, and argon (Ar) as carrier gas. Material characterization confirms that the horizontally-oriented ZnO NWs were guided grown via vapor-liquid-solid (VLS) growth mechanism using gold as catalyst. The ZnO NMs were nucleated from the coated gold catalysts on the sidewalls of NWs. The electrical properties of the ZnO NMs were characterized based on a back-gate field effect transistor (FET). The estimated carrier mobility of the ZnO NM is ~ 150 cm2 V-1s-1. The as-grown free-standing NMs can serve as the fundamental building blocks for a variety of applications in electronics and optoelectronics as well as sensing technologies. The unique bottom-up synthesis approach of the free-standing ZnO NMs is applicable for other material systems. Keywords: zinc oxide, free-standing nanomembrane, chemical vapor deposition, bottom-up approach, vapor-liquid-solid

1 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Introduction Two-dimensional (2D) semiconductor nanomembranes (NMs) are generally referred as monocrystalline structures with thicknesses of less than a few hundred nanometers and lateral dimensions at least two orders of magnitude larger than the thickness.1-3 Due to their unique geometrical shapes, semiconductor NMs exhibit a significantly reduced flexural rigidity as compared to their bulk counterpart,3 and thus can be attached to curved, irregular and stretched surfaces. In addition, their unique mechanical properties allow the using of strain to alter the interatomic bond length and thus engineering the physical properties of materials without prompting fracturing or buckling.2, 4, 5 NMs with appropriate thinness have quantum confinement characteristics in their electrical and photonic properties. NMs are also compatible with the traditional top-down processing technologies, which provide a new route to address the current assembly and manufacturing challenges associated with 0D and 1D nanostructures. Thus, semiconductor NMs have a great potential to serve as the important building blocks for future nanotechnology devices. Inorganic nanomembranes are attracting increasing interests recently in many applications ranging from electronics, catalysts and energy devices such as lithium-ion batteries because of their unique mechanical properties which allow them to bend and wrinkle. 6, 7

As a result they can buffer the strain of lithium ion insertion and extraction and also can delay

the pulverization of the electrode materials for lithium ion batteries. Current available methods to fabricate semiconductor NMs are essentially based on “topdown” approaches: (i) Chemical or mechanical exfoliation of NMs from solids that have naturally layered structures, such as graphite, semiconductor MoS2, GeS, GeSe, etc.8-10 This exfoliation approach yields large numbers of NMs but only applicable for certain classes of materials. And yet, it is still difficult to control their dimensions and shapes. (ii) Release of NMs

2 ACS Paragon Plus Environment

Page 2 of 30

Page 3 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

from bulk semiconductors by use of specialized anisotropic etching procedures. This method is applicable to specific materials that have anisotropic etching properties along different crystal orientations such as Si.11, 12 (iii) Release of NMs from epitaxially grown multilayer assemblies. For example, GaAs NMs can be released from GaAs/AlGaAs stacks by selective removal of AlGaAs with hydrofluoric acid.13, 14 Recently, GaN NMs with a freestanding thickness between 90 and 300 nm were obtained using conductivity-selective electrochemical etching.15 These approaches require the stacks to be epitaxially compatible, and the sacrificial layer needs to be removed with high selectivity with respect to the functional membrane. In addition, these selective etching processes are required to create via-holes15 to allow the etching solutions to access the sacrificial layers. Each of the above methods is applicable to a certain category of materials that have very specific properties, enabling the release of NMs from bulks or stacks via selective etching processes. Nevertheless, there does not exist a general and controllable approach for direct synthesis of free-standing NMs from the “bottom-up”. Wide band gap materials such as III-nitride16, SiC17 and Ga2O318 have been studied for applications in optoelectronic and electronic devices. ZnO with a wide direct bandgap (3.37 eV) and a large exciton binding energy (60 meV)19 represents one of the most attractive wide bandgap semiconducting materials for applications related to ultraviolet (UV) optical devices,20 solar cells,21 sensors,22 photocatalysis,23 transparent field effect transistor,24 and acoustic wave devices.25 In addition, ZnO has been applied for mechanical energy harvesting devices due to its outstanding piezoelectric property.26 ZnO-based nanostructures19-32such as nanowires, nanobelts, nanowalls, hierarchical nanostructures, nanobridges and nanonails have been extensively explored. However, it is still challenging to grow these ZnO nanomaterials (except ZnO NWs) at a large scale and with good uniformity for device applications.

3 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

In this paper, we present a new approach to synthesize free-standing ZnO NMs from the bottom-up by growing the NMs from the sidewalls of the horizontally-oriented NWs on r-plane sapphire substrates. The small lattice mismatch of 1.53% between two parallel planes of ZnO (11-20) and sapphire (01-12) led to the horizontal ZnO NW growth on r-plane sapphire substrate33, 34and simultaneous NMs growth from NW sidewalls with proper growth conditions. The ZnO NM growth mechanism was investigated. The electrical properties of the ZnO NMs were characterized based on a back-gate field effect transistor (FET). Experimental Section Growth of ZnO NMs: We used a single zone tube furnace for the synthesis of the ZnO NMs by the carbothermal reduction process. R-plane sapphires were used as the substrates for the growth. Prior the chemical vapor deposition (CVD) growth, the substrates were cleaned with acetone and isopropanol, rinsed by de-ionized water and dried with nitrogen flow. Au films with different thicknesses (0.5-5 nm) were deposited on top of the substrates via thermal evaporation. A mixture of equal amounts (by weight) of ZnO powder (Alfa Aesar, 99.99%) and graphite (Alfa Aesar,-200 mesh, 99.9995%) were used as the source materials. The mixture was put in an alumina crucible and placed at the center of a quartz tube of diameter 1 inch. The substrates were placed horizontally at the downstream of the tube separated from the source by 6 inches. Then the chamber was pumped down to a base pressure of about 1 mTorr. Prior to heating up the chamber to the desired growth temperature, the chamber was purged with argon (200 sccm) for 30 minutes. The chamber was then heated up to 915 oC under the flow of argon. Upon reaching the desired temperature, the growth was carried out under the flow of 10 sccm of oxygen and 200 sccm of argon. The growth pressure was maintained at around 1 Torr during the growth.

4 ACS Paragon Plus Environment

Page 4 of 30

Page 5 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Fabrication of ZnO NM based FETs: The free-standing ZnO NMs can readily be transfer-printed onto desired substrates to fabricate FETs. Using thermal release tape, ZnO NMs were transferred onto p-type doped Si (100) substrate coated with 300nm thermal silicon dioxide. Ti/Ni (100nm/50nm) contacts were deposited via electron beam evaporation. Characterization of ZnO NMs: The crystal structure and morphology of the ZnO NMs were characterized by using X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). XRD pattern was collected on a Bruker Discover D8 with Co Kα radiation (1.79026 Å). The X-ray beam diameter is 500 µm. FESEM images were taken with Helios 650. High resolution transmission electron microscopy (HRTEM) images and selected-area electron diffraction (SAED) were taken with FEI Tecnai F30 at 300 kV. The Raman spectrum was taken at room temperature using a linearly polarized laser beam of 532 nm. The beam was focused on the sample using a 100X objective. The laser power and the beam diameter were ~200 µW and ~1 µm respectively.

Transistor measurements were

performed with a probe station for contacting the electrodes, and with high-precision source measurement units in Keithley 4200 SCS for applying voltage and measuring current. All current-voltage traces were taken from positive to negative Vds or VG. Results and Discussions Figure 1 shows the as-grown ZnO NMs on r-plane sapphire substrate with a 0.5-inch wafer scale. Au film with thickness of 0.5 nm was deposited on the substrate as the catalyst. The sample was uniformly covered with ZnO NMs, which were grown with a tilted angle as respect to the substrate surface. As observed from Fig. 1, the NMs get tapered as they extend away from the horizontal nanowires, having a wider width at the bottom close to the nanowire where it started to grow first, and a narrower width at the tip. For the sample shown in Fig. 1, the lateral

5 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

dimension at the bottom of the NMs range between 1.5 to 3 µm. The thickness of the NMs ranges between 50 to 70 nm. To investigate the growth mechanisms of the ZnO NMs, we designed a series of growths with various growth times. Fig. 2 illustrated the ZnO NWs and NMs at different stages and confirmed that the ZnO NMs were nucleated and grew from the sidewalls of the horizontallyoriented NWs. Here, the growth process is composed of two parts: (i) The growth of horizontal NWs along the substrate surface via VLS growth mechanism; and (ii) The growth of NMs from the sidewalls of NWs with the assistance of the Au catalyst on the sidewalls. The Au catalyst deposited on the substrate act as the nucleation site for the horizontal ZnO NW growth on appropriate substrates. It is well known that the Au catalysts provide suitable sites for precursor deposition.35 Due to the selective wetting of Zn on Au, Zn vapor produced from the source was absorbed on the Au clusters. Thus, Au/Zn alloy droplets were formed through the diffusion of the Zn atoms into the Au clusters.19 The continuous supply of the Zn flux further supersaturated the alloy droplets and the nucleation of the Zn phase started. The Zn atoms that precipitated out of the alloy droplets then reacted with the oxygen atoms and led to the formation of ZnO nanowires. To enable the horizontal ZnO NW growth, r-plane sapphire substrate was used. The small lattice mismatch of 1.53 % between two parallel planes of ZnO (11-20) and sapphire (0112) along the growth direction led to the horizontal nanowire growth. The horizontal nanowires are enclosed by {10-10} side planes. As the growth of the NWs proceeded, the Au catalysts migrated from the tips to the sidewalls of the NWs. Such phenomena have been observed previously for the growth of silicon and ZnO nanowires using Au and Sn as catalysts respectively.36,

37

We believe that the diffusion of the Au catalysts to the sidewalls of the

nanowires and the growth of the lateral nanowires occurred simultaneously. These migrated Au

6 ACS Paragon Plus Environment

Page 6 of 30

Page 7 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

catalysts acted as the new nucleation centers for the formation of ZnO NMs. There was no intentional change of growth condition when the growth transited from nanowire to nanomembrane. However, it is possible that a perturbation of local energy may trigger the start of NM growth. The local energy perturbation leads to the transferring of the catalyst for NW growth to the NM growth. Thus, the NW growth was terminated when the NM started to appear. To support our hypothesis, top view FESEM images of ZnO NWs and NMs grown at different stages are shown in Figs. 2E-2H. The SEM images were selected from a series of experiments that were designed to illustrate the growth mechanisms of the ZnO NMs. Note that these SEM images do not represent different growth stage for the same sample. Fig. 2E shows the supersaturation of the Au catalysts and nucleation of lateral ZnO NWs. Fig. 2F-2H represent the nucleation and evolution of ZnO NMs morphology. The tapered shape of the ZnO NMs can be clearly seen from the images. Three possible reasons may contribute to the tapering of the NMs during the growth: (i) the reduction in the volume of the Au catalysts due to the evaporation, (ii) the migration of the Au catalysts from the tips to the surfaces and sidewalls of the NMs which resulted in the reduction of the Au catalyst volumes on the NM tips; and (iii) the lateral growth of the NMs due to VLS or vapor-solid (VS) growth mechanisms. From the high-resolution SEM images, it is clearly visible that the Au catalysts at the tips of the NMs got smaller as the growth proceeded. Figure 3A shows the schematic of the signal detection for tilted FESEM image for ZnO NMs. 30o tilted FESEM image of ZnO NMs grown on r-plane sapphire substrate using 0.5 nm thick Au film as the catalyst is shown in Fig. 3B. The tapered shape of the NMs is also visible in this image. Generally, the enclosed sidewall {10-10} planes of the horizontal NW form particular angles with the surface of the substrate. The NMs grown from the sidewall planes of

7 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

the NWs were tilted off the surface of the substrate. Here, as shown in Figure 3B, the NMs formed an angle of 60o with the surface of the substrate, due to the symmetric hexagonal crosssection of the horizontal NW. The equivalence of the sidewall planes of the horizontal NWs can lead to the growth of NMs from different planes. From our experiments, the growth of the ZnO NMs is bi-directional, as shown in Fig. 3C and Fig. 3D. Bi-directional NMs originated from sidewalls of different NWs intersect each other if grown for longer time and continue to grow along their original growth directions as can be seen from Fig. 3C and Fig. 3D. In Fig. 3B, the 30o titled FESEM differentiates the NMs grown from the two directions. This study confirmed that the ZnO NMs grown bi-directionally from the NWs sidewalls with a precise angle of 60o as respect to the surface of the substrate. Figure 4 shows the X-ray diffraction (XRD) pattern of the as-grown ZnO NMs. The precise match of the diffraction peaks with wurtzite ZnO suggests the ZnO NMs are of high quality. For the NMs, the dominant crystal orientation is (110) plane. Besides this peak, two additional peaks appeared at 36.8o and 42.2o which correspond to (100) plane and (101) plane of ZnO, respectively. However, the intensity of the (110) peak is much higher than that of (100) and (101) peaks. Based on the 2θ data of the (110) peak, the lattice parameter is 3.25Å (66.8o for (110) plane), which matches precisely with bulk ZnO lattice parameter. The (110) plane in the diffraction spectra correspond to [11-20] oriented ZnO NMs. The crystal structure of the as-grown ZnO NMs was characterized with transmission electron microscopy (TEM) as shown in Fig. 5. Figure 5A shows the bright field TEM image of ZnO NW with ZnO NM originated from the sidewall of the nanowire. The nanowire has a uniform diameter of ~75 nm. The thickness of the NM is ~ 20nm. Figure 5B shows the high resolution transmission electron microscopy (HRTEM) image of the interface between the NW 8 ACS Paragon Plus Environment

Page 8 of 30

Page 9 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

and the NM. The uniform lattice fringes across the interface between the NW and the NM is clearly visible. The individual HRTEM images of the NW and the NM are shown in Figure 5C and Figure 5D, respectively. The insets show the corresponding selected-area electron diffraction (SAED) patterns for both the NW and the NM. The diffraction patterns were taken along the [0110] zone axis. The SAED patterns confirm that the synthesized NMs and NWs are single crystalline wurtzite ZnO having the same crystal orientation. From Figure 5C, the interplanar spacing for the ZnO NW is 0.52 nm which corresponds to the distance of wurtzite ZnO (0001) plane. The (0001) plane is perpendicular to the NW growth direction which indicates that the NW grew along polar c-plane direction. The NM growth directions can be both perpendicular and parallel to the nanowire growth direction. Room temperature Raman spectrum of ZnO NMs taken with a linearly polarized laser beam of 532 nm wavelength is shown in Fig. 6. ZnO with wurtzite crystal structure belongs to the space group C6V. The optical phonon modes predicted by group theory for ZnO are A1+2B1+E1+2E2.

38, 39

Among them, A1 and E1 modes are polar and both Raman and infrared

active. They split into transverse optical (TO) and longitudinal optical (LO) phonons. E2 modes are nonpolar but Raman active, whereas B1 modes are Raman inactive. The phonon mode at 326.5 cm-1 is a second order feature originating from the zone-boundary phonons of 2-E2(M) for ZnO.39The mode at 438 cm-1 with the highest intensity is assigned to E2(high) phonon mode.38-41 This mode is a typical characteristic feature of wurtzite lattice and is used to understand the stress induced phenomena in wurtzite crystal structure. For free standing ZnO, this peak is located at 437 cm-1. A small increase of 1 cm-1 in the E2(high) phonon frequency of the ZnO NMs with respect to free standing ZnO is within the measurement tolerance limit and indicates that the ZnO NMs are not obviously under stress. The other first-order Raman peak at 376.8 cm-1

9 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 30

corresponds to A1(TO) mode.42 The absence of peaks from impurity in the spectrum indicates that the synthesized materials are phase pure and perfectly crystallized. Figure 7 demonstrates the mechanical property of the as-grown ZnO NM with significantly reduced flexural rigidity. By applying strain via a tungsten probe, the ZnO NM does bend, which indicates the NM has much reduced flexural rigidity as compared to its bulk counterpart. After removing the probe, the NM returns to its original flat morphology. The  flexural rigidity is proportional to ~ ℎ 12 , where E is the elastic modulus and h is the

thickness.43 Thus, the thinnest ZnO nanomembrane (thickness~20 nm) that we have synthesized is expected to have flexural rigidity 12 orders of magnitude smaller than that of the bulk ZnO wafer (thickness ~200 µm). With such small flexural rigidity, the behavior of semiconductor NMs can resemble that of a soft material, which previously belongs exclusively to organic materials. The demonstration of a significantly reduced flexural rigidity of the synthesized ZnO NMs provides an opportunity to apply them for flexible electronic and optoelectronic devices, which are of great scientific importance as they can be bent, stretched and their properties can be manipulated.44 Theoretical calculations based on first principle density functional theory (DFT) have shown strain effects on structural transformations, electronic structure and electron effective mass of wurtzite ZnO .45-47 Effects of bending and stretching on the electronic transport properties of ZnO based devices have been experimentally studied previously .

48-52

The change

in piezoelectric potential due to bending and stretching induced strain may shift the local Fermi level and modifies the local band structure. These changes in turn can affect the charge transport process due to modified effective mass of the charge carriers.

10 ACS Paragon Plus Environment

Page 11 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

To investigate the electrical properties of the as-grown ZnO NMs, back-gate FETs based on ZnO NMs were fabricated. Figure 8A shows a schematic illustration of the ZnO NM based FET device structure. Figure 8B shows a top view SEM image of the fabricated ZnO NM FET, with channel length of 7.5 µm and thickness of ~ 60 nm. All transistors were measured in the dark under ambient conditions. For all the measurements, the gate voltage was applied directly to the back of the Si substrate. A current-voltage plot in Fig. 9A shows a typical accumulation mode n-type transistor behavior. In general, IDS vs VDS curves are linear up to 5V, suggesting the electrodes on ZnO NMs are Ohmic contacts. As VDS further increases, the current gets saturated with positive bias, and eventually the breakdown occurs at VDS ~58V. A representative transconductance measurement (IDS vs VG) was obtained at VDS=0.1V, as shown in Fig. 9B, exhibiting n-type transistor behavior. By plotting the current on a logarithmic scale (Fig. 9B inset), we obtained the on-off current ratio (ION/IOFF) of ~106. From the transconductance plots, the mobility of ZnO NM FETs can be estimated by the relation of 53, 54   =  (1)   where µ is the carrier mobility and L is the length of the active ZnO NMs channel. The capacitance is given by, =

    (2) ℎ

where εSiO2 is the dielectric constant of the gate SiO2, and h is its thickness. A is the parallel area of ZnO NM crossing the channel. The carrier concentration (ne) is estimated by  =

  (3)  

11 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 30

where VNM is the volume of ZnO NMs crossing the channel. From Fig. 9, the mobility of the ZnO NM FET was estimated as 157 cm2 V-1s-1 and the estimated carrier concentration was 3.6 x1016 cm-3 by using the above equations. The carrier mobility of the as-grown ZnO NMs from this study is higher than that of the previously reported ZnO NWs (5-100 cm2V-1s-1) 55, 56 or ZnO thin films (~ 40 cm2V-1s-1)57, 58. Conclusion In summary, we have performed the synthesis of free-standing semiconductor ZnO NMs using a bottom-up approach: NMs grown from the sidewalls of horizontally-oriented ZnO NWs. HRTEM demonstrated the atomic uniformity at the junction between the lateral ZnO NW and the ZnO NM. Mechanical stressor applied on the NM indicates a significantly reduced flexural rigidity as compared to that of the bulk counterpart. The electrical measurements on the asgrown ZnO NM based FETs revealed a high carrier mobility of 157 cm2 V-1s-1. Due to their significantly reduced flexural rigidity, semiconductor ZnO NM with high material quality is a promising candidate for flexible, bendable and stretchable devices. Moreover, the presented synthesis approach and proposed growth mechanism of ZnO NMs is applicable to other material systems. Acknowledgments We thank Prof. Frank Ernst for the fruitful discussions on the TEM characterization. The authors acknowledge financial support through start-up funds from Case Western Reserve University. Part of the material characterization was performed at the Swagelok Center for Surface Analysis of Materials (SCSAM) at CWRU. The electrical characterization of FETs and Raman measurement were performed at Dr. Pghilip Feng’s lab at CWRU. authors

12 ACS Paragon Plus Environment



Equally contributed first

Page 13 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

References 1.

Miller, J. J.; Carter, R. N.; Mcnabb, K. B.; DesOrmeaux, J. P. S.; Striemer, C. C.; Winanas, J. D.; Gaborski, T. R. Lift-off of Large-scale Ultrathin Nanomembranes. J. Micromech. Microeng. 2015, 25, 015011.

2.

Delachat, F. ; Constancias, C.; Fournel, F.; Morales, C.; Drogoff, B. L.; Chaker, M.; Margot, J. Fabrication of Buckling Free Ultrathin Silicon Membranes by Direct Bonding with Thermal Difference. ACS Nano 2015, 9, 3654-3663.

3.

Rogers, J. A.; Lagally, M. G.; Nuzzo, R. G. Synthesis, Assembly and Applications of Semiconductor Nanomembranes. Nat. 2011, 477, 45-53.

4.

Shchepetov, A.; Prunilla, M; Alzina, F.; Schneider, L.; Cuffe, J.; Jiang, H.; Kauppinen, E. I.; Torres, C. M. S.; Ahopelto, J. Ultra-thin Free-standing Single Crystalline Silicon Membranes with Strain Control. Appl. Phys. Lett. 2013, 102, 192108.

5.

Scott, S. A.; Lagally, M. G. Elastically Strain-sharing Nanomembranes: Flexible and Transferable Strained Silicon and Silicon–germanium Alloys. J. Phys. D: Appl. Phys 2007, 40, 75.

6.

Liu, X.; Si, W.; Zhang, J.; Sun, X.; Deng, J.; Baunack, S.; Oswald, S.; Liu, L.; Yan, C.; Schmidt, O. G. Free-standing Fe2O3 Nanomembranes Enabling Ultra-long Cycling Life and High Rate Capability for Li-ion Batteries. Sci. Rep. 2014, 4, 7452.

13 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

7.

Page 14 of 30

Liu, X.; Zhang, J.; Si, W.; Xi, L.; Eichler, B.; Yan, C.; Schmidt, O. G. Sandwich Nanoarchitecture of Si/Reduced Graphene Oxide Bilayer Nanomembranes for Li-Ion Batteries with Long Cycle Life. ACS Nano 2015, 9, 1198-1205.

8.

Novoselov, K. S.; Jiang, D.; Schedin, F.; Booth, T. J.; Khotkevich, V. V.; Morozov, S. V.; Geim, A. K. Two-dimensional Atomic Crystals. Proc. Natl. Acad. Sci. 2005, 102, 10451-10453.

9.

Coleman, J. N.; Lotya, M.; O’Neill, A.; Bergin, S. D.; King, P. J.; Khan, U.; Young, K.; Gaucher, A.; De, S.; Smith, R. J. et al. Two-Dimensional Nanosheets Produced by Liquid Exfoliation of Layered Materials. Sci. 2011, 331, 568-571.

10. Radisavljevic, B.; Radenovic, A.; Brivio, J.; Giacometti, V., Kis, A. Single-layer MoS2 Transistors. Nat. Nanotech. 2011, 6, 147-150. 11. Baca, A. J.; Meitl, M. A.; Ko, H. C.; Mack, S.; Kim, H.-S.; Dong, J.; Ferreira, P. M.; Rogers, J. A. Printable Single-Crystal Silicon Micro/Nanoscale Ribbons, Platelets and Bars Generated from Bulk Wafers. Adv. Funct. Mater. 2007, 17, 3051-3062. 12. Mack, S.; Meitl, M. A.; Baca, A. J.; Zhu, Z. T.; Rogers, J. A. Mechanically Flexible Thin-film Transistors That Use Ultrathin Ribbons of Silicon Derived from Bulk Wafers. Appl. Phys. Lett. 2006, 88, 213101. 13. Yablonovitch, E.; Gmitter, T.; Harbison, J. P.; Bhat, R. Extreme Selectivity in the Lift‐ off of Epitaxial GaAs Films. Appl. Phys. Lett. 1987, 51, 2222. 14. Yoon, J.; Jo, S.; Chun, I. S.; Jung, I.; Kim, H. –S.; Meitl, M.; Menard, E.; Li, X.; Coleman, J. J.; Paik, U.; Rogers, J. A. GaAs Photovoltaics and Optoelectronics Using Releasable Multilayer Epitaxial Assemblies Nat. 2010, 465, 329-333.

14 ACS Paragon Plus Environment

Page 15 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

15. Park, S. H.; Yuan, G.; Chen, D.; Xiong, K.; Song, J; Leung, B.; Han, J. Wide Bandgap III-Nitride Nanomembranes for Optoelectronic Applications. Nano Lett. 2014, 14, 42934298. 16. Rafique, S.; Han, L.; Zhao, H. Chemical Vapor Deposition of m-plane and c-plane InN Nanowires on Si (100) Substrate. J. Cryst. Growth 2015, 415, 78-83. 17. Millan, J.; Godignon, P.; Perpina, X.; Perez-Tomas, A.; Rebollo, J. A Survey of Wide Bandgap Power Semiconductor Devices. IEEE Trans. Power Electron. 2014, 29, 21552163. 18. Rafique, S.; Han, L.; Zhao, H. Synthesis of wide bandgap Ga2O3 (Eg~4.6–4.7 eV) thin films on sapphire by low pressure chemical vapor deposition. Phys. Status Solidi A 2015, DOI: 10.1002/pssa.201532711. 19. Wang, X.; Song, J.; Summers, C. J.; Ryou, J. H.; Li, P.; Dupuis, R. D.; Wang, Z. L. Density-Controlled Growth of Aligned ZnO Nanowires Sharing a Common Contact:  A Simple, Low-Cost, and Mask-Free Technique for Large-Scale Applications J. Phys. Chem. B 2006, 110, 7720-7724. 20. Lupan, O.; Pauporte, T.; Viana, B.; Aschehoug, P. Electrodeposition of Cu-doped ZnO Nanowire Arrays and Heterojunction Formation with p-GaN for Color Tunable Light Emitting Diode Applications. Electrochim. Acta 2011, 56, 10543-10549. 21. Xu, C.; Wu, J.; Desai, U. V.; Gao, D. High-Efficiency Solid-State Dye-Sensitized Solar Cells Based on TiO2-Coated ZnO Nanowire Arrays. Nano Lett. 2012, 12, 2420-2424. 22. Sberveglieri, G.; Groppelli, S.; Nelli, P.; Tintinelli, A.; Giunta, G. A. A Novel Method for the Preparation of NH3 Sensors Based on ZnO-In Thin Films. Sensors and Actuators B 1995, 25, 588-590. 15 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 30

23. Yumoto, H.; Inoue, T.; Li, S. J.; Sako, T.; Nishiyama, K. Application of ITO Films to Photocatalysis. Thin Solid Films 1999, 345, 38-41. 24. Carcia, P. F.; Mclean, R. S.; Reilly, M. H.; Nunes, G. Jr.Transparent ZnO Tthin-film Transistor Fabricated by Rf Magnetron Sputtering. Appl. Phys. Lett. 2003, 82, 1117. 25. Panwar, B. S. Characteristics of Surface Acoustic Wave Convolver in the Monolithic Metal–zinc oxide–silicon nitride–silicon dioxide–silicon Structure. Appl. Phys. Lett. 2002, 80, 1832. 26. Zhu, G.; Yang, R.; Wang, S.; Wang, Z. L. Flexible High-Output Nanogenerator Based on Lateral ZnO Nanowire Array. Nano Lett. 2010, 10, 3151-3155. 27. Wang, Z. L. ZnO Nanowire and Nanobelt Platform for Nanotechnology Mater. Sci. Eng. 2009, 64, 33-71. 28.

Brewster , M. M.; Lu , M. -Y.; Lim , S. K.; Smith , M. J.; Zhou , X.; Gradečak, S. The Growth and Optical Properties of ZnO Nanowalls. J. Phys. Chem. Lett. 2011, 2, 19401945.

29. Lao, J. Y.; Wen, J. G.; Ren, Z. F. Hierarchical ZnO Nanostructures. Nano Lett. 2002, 2, 1287-1291. 30. Lao, J. Y.; Huang, J. Y.; Wang, D. Z.; Ren, Z. F. ZnO Nanobridges and Nanonails. Nano Lett. 2003, 3, 235-238. 31. Pan, Z. W.; Dai, Z. R.; Wang, Z. L. Nanobelts of Semiconducting Oxides. Sci. 2001, 291, 1947-1949. 32. Rafique, S.; Han, L.; Zhao, H. Density Controlled Growth of ZnO Nanowall–Nanowire 3D Networks. J. Phys. Chem. C 2015, 119, 12023-12029.

16 ACS Paragon Plus Environment

Page 17 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

33. Tsivion, D.; Schvartzman, M.; Popovitz-Biro, R.; Joselevich, E. Guided Growth of Horizontal ZnO Nanowires with Controlled Orientations on Flat and Faceted Sapphire Surfaces. ACS Nano 2012, 6, 6433-6445. 34. Shi, J.; Sun, X.; Zhang, J.; Lian, J.; Yu, Q.; Lin, M.; Li, H. Epitaxial Growth of Horizontally Aligned Zinc Oxide Nanonecklace Arrays on r-Plane Sapphire. J. Phys. Chem. C 2009, 113, 20845-20854. 35. Wang, X.; Ding, Y.; Li, Z.; Song, J.; Wang, Z. L. Single-Crystal Mesoporous ZnO Thin Films Composed of Nanowalls. J. Phys. Chem. C 2009, 113, 1791-1794. 36. Hannon, J. B.; Kodambaka, S.; Ross, F. M.; Tromp, R. M. The Influence of the Surface Migration of Gold on the Growth of Silicon Nanowires. Nat. 2006, 440, 69-71. 37. Gao, P.; Wang, Z. L. Self-Assembled Nanowire-Nanoribbon Junction Arrays of ZnO. J. Phys. Chem. B 2002, 106, 12653-12658. 38. Ngo-Duc, T.; Singh, K.; Meyyappan, M.; Oye, M. M.Vertical ZnO Nanowire Growth on Metal Substrates. Nanotechnology 2012, 23, 194015. 39. Chang, Y.; Wang, P.; Sun, Q.; Wang, Y.; Long, Y. Room Temperature Ferromagnetism of (Mn,Fe) Codoped ZnO Nanowires Synthesized by Chemical Vapor Deposition. J. Nanomater. 2011, 2011, 1-6. 40. Shen, G.; Dawahre, N.; Waters, J.; Kim, M. S.; Kung, P. Growth, Doping, and Characterization of ZnO Nanowire Arrays. J. Vac. Sci. Technol. B 2013, 31, 041803. 41. Amin, M.; Shah, N. A.; Bhatti, A. S.; Malik, M. A. Effects of Mg Doping on Optical and CO Gas Sensing Properties of Sensitive ZnO Nanobelts. Cryst. Engg.Comm. 2014, 16, 6080-6088.

17 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 30

42. Kumar, G. M.; Ilanchezhiyan, P.; Kawakita, J.; Subramanian, M.; Jayavel, R. Magnetic and Optical Property Studies on Controlled Low-temperature Fabricated Onedimensional Cr Doped ZnO Nanorods. Cryst. Engg.Comm. 2010, 12, 1887-1892. 43. Yuan, H. C.; Qin, G.; Celler, G. K.; Ma, Z. Bendable High-frequency Microwave Switches Formed with Single-crystal Silicon Nanomembranes on Plastic Substrates. Appl. Phys. Lett. 2009, 95, 043109. 44. Roberts, M. M.; Klein, L. J.; Savage, D. E.; Slinker, K. A.; Friesen, M.; Celler, G.; Eriksson, M. A.; Lagally, M. G. Elastically Relaxed Free-standing Strained-silicon Nanomembranes Nat. Mater. 2006, 5, 388-393. 45. Yadav, S. K.; Sadowski, T.; Ramprasad, R. Density Functional Theory Study of ZnX (X=O, S, Se, Te) Under Uniaxial Strain. Phys. Rev. B 2010, 81, 144120. 46. Yadav, S. K.; Ramprasad, R. Strain-assisted Bandgap Modulation in Zn Based II-VI Semiconductors. Appl. Phys. Lett. 2012, 100, 241903. 47. Wang, Y.; Tang, W.; Zhu, J.; Liu, J. Strain Induced Change of Band Structure and Electron Effective Mass in Wurtzite ZnO: A First-principles Study. Comp. Mater. Sci. 2015, 99, 145-149. 48. Chen, T.-P.; Young, S.-J.; Chang, S. –J.; Hsiao, C.-H.; Hsu, Y.-J. Bending Effects of ZnO Nanorod Metal–semiconductor–metal Photodetectors on Flexible Polyimide Substrate. Nanoscale Res. Lett. 2012, 7, 214. 49. Kang, J.; Keem, K.; Jeong, D.-Y.; Kim, S. Electrical Characteristics of ZnO NanowireBased Field-Effect Transistors on Flexible Plastic Substrates. Japan. J. Appl. Phys. 2007, 46, 6227-6229.

18 ACS Paragon Plus Environment

Page 19 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

50. Kwon, S.-S.; Hong, W.-K.; Jo, G.; Maeng, J.; Kim, T.-W.; Song, S.; Lee, T. Piezoelectric Effect on the Electronic Transport Characteristics of ZnO Nanowire Field-Effect Transistors on Bent Flexible Substrates. Adv. Mater. 2008, 20, 4557-4562. 51. Shao, R.-W.; Zheng, K.; Wei, B.; Zhang, Y.-F.; Li, Y.-J.; Han, X.-D.; Zhang, Z.; Zou, J. Bandgap Engineering and Manipulating Electronic and Optical Properties of ZnO Nanowires by Uniaxial Strain. Nanoscale 2014, 6, 4936-4941. 52. Wei, B.; Zheng, K.; Ji, Y.; Zhang, Y.; Zhang, Z.; Han, X. Size-Dependent Bandgap Modulation of ZnO Nanowires by Tensile Strain. Nano Lett. 2012, 12, 4595-4599. 53. Goldberger, J.; Sirbuly, D. J.; Law, M.; Yang, P. ZnO Nanowire Transistors. J. Phys. Chem. B 2005, 109, 9-14. 54. Song, S.; Hong, W. –K.; Kwon, S. –S.; Lee, T. Passivation Effects on ZnO Nanowire Field Effect Transistors under Oxygen, Ambient, and Vacuum Environments. Appl. Phys. Lett. 2008, 92, 263109. 55. Hong, W. –K.; Kim, B. –J.; Kim, T. –W.; Jo, G.; Song, S.; Kwon, S. –S.; Yoon, A.; Stach, E. A.; Lee, T. Electrical Properties of ZnO Nanowire Field Effect Transistors by Surface Passivation. Colloids Surf. A 2008, 313-314, 378-382. 56. Hong, W. –K.; Yoon, J.; Lee, T. Hydrogen Plasma-mediated Modification of the Electrical

Ttransport

Properties

of

ZnO

Nanowire

Field

Effect

Transistors.

Nanotechnology 2015, 26, 125202. 57. Esro, M.; Vourlias, G.; Somerton, C.; Milne, W. I.; Adamopoulos, G. High-Mobility ZnO Thin Film Transistors Based on Solution-processed Hafnium Oxide Gate Dielectrics. Adv. Funct. Mater. 2015, 25, 134-141.

19 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 30

58. Özgür, Ü.; Hofstetter, D.; Morkoç, H. ZnO Devices and Applications: A Review of Current Status and Future Prospects. Proc. IEEE 2010, 98, 1255-1268.

Figure 1. 30o tilted field emission scanning electron microscope (FESEM) image of ZnO NMs grown on r-plane sapphire substrate at 915 oC.

20 ACS Paragon Plus Environment

Page 21 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Figure 2. (A-D) Schematic illustration of the growth mechanism of free-standing ZnO NMs. (EH) Top view FESEM images of the as-grown ZnO NMs grown on r-plane sapphire substrate using Au film as catalyst.

21 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 30

Figure 3. (A) Schematic of the signal detection for the tilted FESEM image of ZnO NMS. (B) 30o tilted FESEM image of ZnO NMs showing the NMs forming an angle of 60o with the substrate. (C) High magnification top view FESEM image of the ZnO NMs intersecting each other with extended growth time. (D) 60o tilted FESEM image of ZnO NMs.

22 ACS Paragon Plus Environment

Page 23 of 30

Figure 4. XRD pattern of the as-grown ZnO nanowires and nanomembranes. The corresponding indices are marked above the respective diffraction peaks. 10000

(110)

Intensity (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

1000 100

(100) (101) 10 1 30

36

42

48

54

60

2θ (deg)

23 ACS Paragon Plus Environment

66

72

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 30

Figure 5. (A) TEM image of ZnO nanowire and nanomembrane grown on r-plane sapphire substrate. (B) HRTEM image of the interface between ZnO nanowire and nanomembrane. The interface is marked with the dashed line. (C) HRTEM image of ZnO nanowire. Inset shows the SAED pattern of the ZnO nanowire taken along the [01-10] zone axis. (D) HRTEM image of ZnO nanomembrane. Inset shows the SAED pattern of the ZnO nanomembrane taken along the [01-10] zone axis.

24 ACS Paragon Plus Environment

Page 25 of 30

Figure 6. Room temperature micro Raman spectrum of as grown ZnO NMs.

438

9000 8000 7000 6000 5000 3000 2000

376.8

4000

326.5

Intensity (a.u.)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

1000 0 300

400

500

600

Raman shift (cm-1)

25 ACS Paragon Plus Environment

700

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Figure 7. 30o tilted FESEM image of as-grown ZnO NM showing high degree of bendability.

26 ACS Paragon Plus Environment

Page 26 of 30

Page 27 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

Figure 8. (A) Schematic illustration of ZnO NM FET. (B) Top view FESEM image of ZnO NM FET.

27 ACS Paragon Plus Environment

Crystal Growth & Design

Figure 9. (A) IDS vs VDS curves of ZnO NM based FET at different gate voltages. (B) IDS vs VG curve of ZnO NM based FET on a logarithmic scale at VDS=0.1 V. 1.0E-06-6 1.0x10

1.5E-05-5 1.5x10

10 B1.0E-05

A

-5

1.0E-06 10-6

8.0E-07-7 8.0x10

1.0E-07 10-7

IDS (A)

1.0E-05-5 1.0x10

1.0E-08 10-8 1.0E-09 10-9

5.0E-06-6 5.0x10

1.0E-10 10-10

IDS (A)

6.0E-07-7 6.0x10

IDS (A)

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 30

0.0E+00 0

1.0E-11 10-11 1.0E-12 10-12 -60

-40

-20

0

20

40

VG(V)

4.0E-07-7 4.0x10 VG=30V G VG=25V G VG=20V G VG=15V G VG=10V G VG=5V G VG=0V G

-5.0E-06-6 -5.0x10

-1.0E-05-5 -1.0x10

2.0E-07-7 2.0x10

0 0.0E+00

-1.5E-05-5 -1.5x10 -1.5

-1

-0.5

0

0.5

1

-60

1.5

-40

-20

0

VG(V)

VDS(V)

28 ACS Paragon Plus Environment

20

40

Page 29 of 30

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Crystal Growth & Design

29 ACS Paragon Plus Environment

Crystal Growth & Design

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

For Table of Contents Use Only

Growth and Electrical Properties of Free-Standing Zinc Oxide Nanomembranes Subrina Rafique ǂ, Lu Han ǂ, and Hongping Zhao*  

30o tilted field emission scanning electron microscope (FESEM) image of ZnO nanomembranes (NMs) grown on r-plane sapphire substrate at 915 oC

ACS Paragon Plus Environment

Page 30 of 30