High-Performance Photovoltaic Readable Ferroelectric Nonvolatile Memory Based on La Doped BiFeO Films 3

Dong Li, Dongxing Zheng, Chao Jin, Wanchao Zheng, and Haili Bai ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.8b06246 • Publication Date (Web): 21 May 2018 Downloaded from http://pubs.acs.org on May 21, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

High-Performance Photovoltaic Readable Ferroelectric Nonvolatile Memory Based on La Doped BiFeO3 Films

Dong Li, Dongxing Zheng, Chao Jin, Wanchao Zheng and Haili Bai∗

Tianjin Key Laboratory of Low Dimensional Materials Physics and Processing Technology, Institute of Advanced Materials Physics, Faculty of Science, Tianjin University, Tianjin 300350, PRC

*

Author to whom all correspondence should be addressed. E-mail: [email protected]

1

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT

Epitaxial La0.1Bi0.9FeO3 (LBFO) films with SrRuO3 (SRO) bottom electrodes were fabricated on SrTiO3 (001) substrates by magnetron sputtering. The LBFO thin films exhibit strong ferroelectric properties. Electric field controlled nonvolatile reversible resistance switchings and switchable photovoltaic effects have been observed in Pt/LBFO/SRO heterostructures. With the optimized LBFO film thickness, the observed room temperature pulsed-read resistance switching ratio can reach 105 % magnitude by applying ±2.7 V pulse voltages. Besides, the observed ferroelectric switchable photovoltaic effect in the visible wavelength range shows a large tunable open-circuit photovoltage from –75 to –330 mV. The switching mechanisms in resistance and photovoltaic effects are demonstrated to be directly related to the ferroelectric reversal, which can be attributed to the polarization modulated interfacial barriers and deep trap states.

Keywords: bismuth ferrite, polarization, resistance switching, photovoltaic effect, heterostructure

2

ACS Paragon Plus Environment

Page 2 of 26

Page 3 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

 INTRODUCTION

Based on the ferroelectric spontaneous polarization and electric driven rapid inversion, ferroelectric random access memories (FeRAMs) have been designed for high speed and density information storage.1, 2 Compared with the magnetic random access memories (MRAMs), FeRAMs have significant advantages in the switching speed and the resistance ratio.3 While in conventional ferroelectric memories, the read-out of information is performed by the detection of polarization switching current, which is a destructive reading process and severely limits its utility.4 To search for the non-destructive read-out solutions, the ferroelectric related resistance and photovoltaic switchings have been studied in depth recently.5-8 Remarkable resistive switchings has been observed in several reports based on ultrathin (