Highly Efficient Interception and Precipitation of Uranium(VI) from

Nov 28, 2017 - Highly Efficient Interception and Precipitation of Uranium(VI) from Aqueous Solution by Iron-Electrocoagulation Combined with Cooperati...
0 downloads 12 Views 2MB Size
Subscriber access provided by READING UNIV

Article

Highly Efficient Interception and Precipitation of Uranium (VI) from Aqueous Solution by Iron-Electrocoagulation Combined with Cooperative Chelation by Organic Ligands Peng Li, Bao Zhun, Xuegang Wang, Ping Ping Liao, Guanghui Wang, Lizhang Wang, Yadan Guo, and Weimin Zhang Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b05288 • Publication Date (Web): 28 Nov 2017 Downloaded from http://pubs.acs.org on December 2, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 33

Environmental Science & Technology

1

Highly Efficient Interception and Precipitation of Uranium (VI) from

2

Aqueous Solution by Iron-Electrocoagulation Combined with

3

Cooperative Chelation by Organic Ligands

4 5 6 7 8 9 10 11

Peng Lia,b* , Bao Zhunb, Xuegang Wanga,b, PingPing Liaob, Guanghui Wanga,b, Lizhang Wangc* Yadan Guoa,b and Weimin Zhanga,b a

State Key Laboratory Breeding Base of Nuclear Resources and Environment, East China University of Technology, Nanchang City, Jiangxi 330013, China, PR China

b

School of Water Resource & Environmental Engineering, East China University of Technology, Nanchang City, Jiangxi 330013, PR China c

School of Environment Science and Spatial Informatics, China University of Mining and Technology, Xuzhou City, Jiangsu 221008, PR China

12

ABSTRACT: A new strategy combining iron-electrocoagulation and organic ligands (OGLs)

13

cooperative chelation was proposed to screen and precipitate low concentrations (0–18.52 µmol/L)

14

of uranium contaminant in aqueous solution. We hypothesized that OGLs with amino, hydroxyl,

15

and carboxyl groups, hydrophobically/hydrophiliclly would realize precuring of uranyl ion at

16

pH IDA >

190

EDTA > PANI, which is in line with their uranium removal performance in the bulk experiments.

191

Interestingly, Figure 1 shows that the optimum pH for uranium iron-electrocoagulation after the

192

cooperative chelation by OGLs remained at 6.0. This was corroborated by the Zeta potential

193

measurements of the obtained precipitated flocs at different pH conditions in Figure 2b. The zeta

194

potential at pH 6.0 was much lower than at other pH conditions, while the reactions in the

195

iron-electrocoagulation system reached the highest level. The generated iron oxides and

196

hydroxides would be important for screening the U-OGLs and the accumulative crystallization.

197

The identical optimum solution pH for uranium removal by iron-electrocoagulation in the

198

presence and in the absence of cooperative chelation by OGLs also indicates that analogous

199

precipitate evolution processes took place before and after the intercalation of OGLs, and that the

200

added OGLs did not affect the intrinsic electrochemical reactions of the iron-electrocoagulation

201

system.

ACS Paragon Plus Environment

Uranium concentration (mg/L)

Environmental Science & Technology

a)

4

4

4

4

4

3

3

3

3

2

2

2

2

2

1

1

1

1

1

0 3.0

4.5

6.0

7.5

9.0

0

0 3.0

4.5

6.0

7.5

9.0

3.0

4.5

Solution pH

Solution pH

6.0

7.5

9.0

0 3.0

4.5

6.0

7.5

9.0

3.0

Solution pH

Solution pH

Initial After Treatment

e)

d)

3

0

202

c)

b)

Page 10 of 33

4.5

6.0

7.5

9.0

Solution pH

203

Figure 1. Precipitation of uranium from water with iron-electrocoagulation in the absence and in presence of

204

organic ligands: a) in the absence organic ligands; b) IDA; c) Alizarin S; d) PANI; e) EDTA. Initial uranium

205

concentrations were in the range of 8.35 to 15.70 µmol/L (2.255 to 4.238 mg/L) as indicated in the figure. The

206

current density 0.6 mA/cm2, OGLs-to-U (VI) mole ratio 3:1. The solid blue circles represent the initial

207

concentrations of uranium in aqueous solution, while the empty red ones symbol those after 24 mins reactions

-5

-5.0

a) Zeta potential (mV)

Zeta potential (mV)

-7 -8 -9

-6.0 -6.5 -7.0 -7.5

-10

-8.0

-11 Without U and OGLs

208

b)

-5.5

-6

U with no OGLs

EDAT

Alizarin S

PANI

IDA

3

4

Different ion-electrocoagulation condition

5

6

7

8

9

Solution pH

209

Figure 2. Zeta potential of the precipitated flocs obtained at (a) different ion-electrocoagulation condition and (b)

210

Alizarin S as organic ligands at different solution pH values. The experimental condition was initial uranium

211

concentrations 8.35 to 15.70 µmol/L (2.255 to 4.238 mg/L), current density 0.6 mA/cm2, and OGLs-to-U (VI)

212

mole ratio 3:1

213

Alizarin S, the best organic ligand for cooperative chelation in the efficient interception and

214

precipitation of uranium (VI) from water by iron-electrocoagulation, was selected for the next

ACS Paragon Plus Environment

Page 11 of 33

Environmental Science & Technology

215

steps of testing. Critical parameters that affect the uranium precipitation, including solution pH,

216

applied current density, OGLs-to-U(VI) mole ratio, and initial uranium concentration were

217

comprehensively investigated, and the results are presented in Figure 3. As depicted in Figure 3a,

218

the optimum solution pH was 6.0, which was consistent with the experimental results in Figures 1

219

and 2. A higher applied current density would increase the uranium removal efficiency (Figure 3b),

220

which was 60.29%, 73.22%, 90.96%, and 98.50% at the current density of 0.6, 0.8, 1.0, and 1.4

221

mA/cm2, respectively. In the presence of Alizarin S, the iron-electrocoagulation method could

222

effectively remove uranium to meet the discharge standard, by using a low cell voltage (2.2 V for i

223

= 1.0 mA/cm2 and 2.6 V for 1.4 mA/cm2) and a short treatment time. Therefore, both high

224

uranium removal efficiency and low treatment cost could be achieved with the proposed

225

iron-electrocoagulation method when combined with the OGLs cooperative chelation.

226

An appropriate amount of added OGLs is necessary to reach a satisfactory uranium removal

227

efficiency, by improving the uranium interception and reducing the Zeta potential of the growing

228

flocculation precursor. As shown in Figure 3c, when the OGLs-to-U(VI) mole ratio was small

229

(3:1) means that the

231

uranyl ion would be encapsulated by excess organic ligands, producing a higher net negative

232

charge. As a result, a higher input cell voltage is required to compress the newly formed double

233

layer structure. Meanwhile, the rubber and bonded organic ligands would affect the settlement

234

characteristics of the generated flocs. The OGLs-to-U(VI) mole ratio of 3:1 was found to be the

235

optimal for uranium iron-electrocoagulation precipitation. At this ligand mole ratio, current

236

density of 0.6 mA/cm2, initial uranium concentration of 11.36 µmol/L (3.067 mg/L), and solution

ACS Paragon Plus Environment

Environmental Science & Technology

237

pH of 6.0, the uranium removal efficiency reached 99.65% (Figure 1c). The change of Fe3+

238

concentration with Alizarin S as OGL under various pH conditions in the iron-electrocoagulation

239

system is provided in SI, Table S2. At low pH values, a high Fe3+ concentration was detected, and

240

it decreased dramatically with increasing of the solution pH value. At pH = 6.0, a very low Fe3+

241

concentration was detected in the effluent, indicating that Fe3+ pollution can be avoided.

242

The initial uranium concentration affects its removal efficiency and determines the bulk

243

electrolysis time needed to achieve an acceptable effluent concentration. Figure 3d shows that the

244

uranium removal efficiency decreases with increasing initial uranium concentration, being 60.29%,

245

49.95%, 32.13%, and 24.95% for the respective initial uranium concentrations of 12.57, 27.31,

246

38.80, and 53.87 µmol/L (3.395, 7.375, 10.475, and 14.544 mg/L), under the operating conditions

247

of solution pH 3.0, current density 0.6 mA/cm2, and OGLs-to-U(VI) mole ratio of 3:1. The results

248

revealed that uranium precipitation with the iron-electrocoagulation method was an energy reigned

249

electrochemical reaction, and the amount of the formed flocculation precursor (iron oxides/

250

hydroxides) determined the uranium removal efficiency. A high initial uranium concentration

251

should be accompanied by a high current density. After the intercalation of organic ligands, the

252

uranium precipitation process was found to also follow the second-order kinetic model (SI, Figure

253

S3-6 and Table S1).

ACS Paragon Plus Environment

Page 12 of 33

Page 13 of 33

Environmental Science & Technology

4

a)

pH=3.0 pH=5.0 pH=6.0 pH=7.0 pH=9.0

3

2

1

0

Uranium concentration (mg/L)

Uranium concentration (mg/L)

4

b)

2

i=0.6 mA/cm 2 i=0.8 mA/cm 2 i=1.0mA/cm 2 i=1.4 mA/cm

3

2

1

0

0

4

8

16

20

4

8

c)

mOLGs:U=1:1

3.5

mOLGs:U=3:1 mOLGs:U=6:1

3.0

mOLGs:U=9:1 2.5 2.0 1.5

Uranium concentration (mg/L)

16

12

Time (min)

16

20

24

d) c0=14.544 mg/L

12

c0=10.475 mg/L

8

c0=7.375 mg/L 4 c0=3.395 mg/L 0

1.0

254

0

24

Time (min)

4.0

Uranium concentration (mg/L)

12

0

4

8

12

Time (min)

16

20

24

0

4

8

12

16

20

24

Time (min)

255

Figure 3 Uranium concentration on dependent of reaction time with iron-electrocoagulation in presence of Alizarin

256

S at different pH (a) (i=0.6 mA/cm2, OGLs-to-U(VI)=3:1, c0=11.11-18.52 µmol/L (3.0-5.0 mg/L)), current density

257

(b) (pH 3.0, OGLs-to-U(VI)=3:1, c0=11.11-18.52 µmol/L (3.0-5.0 mg/L)), different OGLs-to-U(VI) molar ratio (c)

258

(pH 3.0, i=0.6 mA/cm2, c0=11.11-18.52 µmol/L (3.0-5.0 mg/L)), and initial uranium concentration 0 to 55.56

259

µmol/L (0 to 15.0 mg/L) (d) (pH 3.0, i=0.6 mA/cm2, OGLs-to-U(VI)=3:1)

260

Elimination of Organic Ligand Pollution. Figure 4 shows that adding the OGLs could raise the

261

organic pollution index, with the chemical oxygen demand (CODCr) value ranging from 40 to 80

262

mg/L. Fortunately, the introduced organics would also be removed during the subsequent

263

iron-electrocoagulation process. Hydrophilic macromolecule such as Alizarin S and EDTA (with

264

hydrophilic hydroxyl and carboxyl groups, respectively) present higher precipitation efficiency

265

than the hydrophilic small molecule IDA and the hydrophobic macromolecule of PANI. The COD

266

removal efficiency with IDA, PANI, EDTA, and Alizarin S as organic ligands were 82.97%,

ACS Paragon Plus Environment

Environmental Science & Technology

Page 14 of 33

267

71.61%, 88.97%, and 86.89%, respectively. The different CODCr removal for different organic

268

ligands would be ascribed to their affinity and nucleation-promotion capacity with the flocculation

269

precursors generated in the iron-electrocoagulation system. The hydrophilic substances would be

270

easily captured and encapsulated in the crystallized ferrite species. In other words, the hydrophilic

271

groups have an intrinsic affinity for the iron hydroxides. The larger molecular weight and fine

272

hydrophilicity of Alizarin S that endows adequate flocculation reactions in iron-electrocoagulation

273

system also facilitate its uranium precipitation in U-Alizarin S chelates.

274

a)

b) COD removal efficiency (%)

120 100 80 60 40 20 0 IDA

PANI

EDTA

Alizarin S

OGLs species

275 276

Figurer 4 The COD value (a) and removal efficiency (b) during uranium iron-electrocoagulation with different

277

organic ligands species. Experimental condition: pH 6.0, current density 0.6 mA/cm2, OGLs-to-U(VI) mole ratio

278

3:1, initial uranium concentration 11.11 to 18.52 µmol/L (3.0-5.0 mg/L)

279

Mechanism of Uranium Precipitation in Iron-electrocoagulation System. The precipitated

280

flocs in iron-electrocoagulation system were collected for the following three cases under the

281

initial uranium concentration of 11.11–18.52 µmol/L (3.0–5.0 mg/L): (1) with no uranium and

282

OGLs, (2) with uranium but no OGLs, and (3) with uranium and Alizarin S as OGL. The flocs

ACS Paragon Plus Environment

Page 15 of 33

Environmental Science & Technology

283

were characterized with SEM, elemental mapping, EDS, and TEM methods for their

284

microstructure observation and elemental composition detection. XRD, FT-IR, and XPS

285

techniques were employed to explore the corresponding precipitation mechanisms. As shown in

286

Figure 5a, d, and g, the colloidal aggregates of pure iron oxides/hydroxides were flake-shaped,

287

fully crystallized nanoparticles with size of appropriately 26.2 nm. The fine crystals on the

288

surfaces were sodium sulfate granules separated out during the bulk electrolysis. Once the

289

uranium participated in the iron-electrocoagulation reactions, crystalline uranium composites were

290

observed on the surface and edge of the particles of the iron oxides and hydroxides (Figure 5b),

291

and the morphology of the precipitated flocs became disorganized with a defective lattice structure

292

and marginal fault (shown in Figure 5b, e, and h). The size of the formed nanoparticles decreased

293

to 8.6 nm. After the intercalation of Alizarin S, the SEM image (Figure 5c) showed that fine

294

nanoparticles of uranium composites were gathered on the particle surface and edge of pure iron

295

oxides and hydroxides, the lattice structure of the flocs became increasingly disordered, and the

296

size of the formed nanoparticles further decreased to 4.7 nm. Uranium composites were also found

297

as fine nanoparticles on the surface and edge of iron oxides and hydroxides when IDA, PANI, or

298

EDTA was used as organic ligands in the iron-electrocoagulation system, with the respective

299

nanoparticle size of 4.7, 2.6, and