Highly Stable Hybrid Capacitive Deionization with a MnO2 Anode and

Jan 22, 2018 - Performance degradation caused by the oxidation of carbon anodes during capacitive deionization (CDI) remains a major problem that may ...
0 downloads 5 Views 882KB Size
Subscriber access provided by READING UNIV

Letter

Highly Stable Hybrid Capacitive Deionization with a MnO Anode and a Positively Charged Cathode 2

Tingting Wu, Gang Wang, Shiyong Wang, Fei Zhan, Yu Fu, Huiying Qiao, and Jieshan Qiu Environ. Sci. Technol. Lett., Just Accepted Manuscript • DOI: 10.1021/acs.estlett.7b00540 • Publication Date (Web): 22 Jan 2018 Downloaded from http://pubs.acs.org on January 24, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 20

Environmental Science & Technology Letters

1

Highly Stable Hybrid Capacitive Deionization with a MnO2

2

Anode and a Positively Charged Cathode

3

Tingting Wu†, Gang Wang†, *, Shiyong Wang†, Fei Zhan†, Yu Fu†, Huiying Qiao†, Jieshan

4

Qiu†, ‡, *

5



State Key Lab of Fine Chemicals, School of Chemical Engineering, Liaoning Key Lab for

6

Energy Materials and Chemical Engineering, Dalian University of Technology, Dalian

7

116024, Liaoning, China.

8 9



School of Chemical Engineering and Technology, Xi’an Jiaotong University, Xi’an 710049, China.

10 11

Corresponding Author:

12

Gang Wang, *E-mail: [email protected];

13

Jieshan Qiu, *E-mail: [email protected], *Tel/Fax: +86-411-84986024

14

1 ACS Paragon Plus Environment

Environmental Science & Technology Letters

15

ABSTRACT

16

Performance degradation caused by the oxidation of carbon anodes during the operation

17

of capacitive deionization (CDI) remains a major problem that may greatly restrict its

18

practical application. To improve the cyclic stability of CDI, carbon based anode materials

19

were replaced by pseudocapacitive MnO2 in this work. The cation-selective MnO2 anode was

20

assembled with an anion-selective quaternized poly (4-vinyl pyridine) coated activated

21

carbon (AC-QPVP) cathode into a hybrid CDI cell. The cell exhibited inverted CDI

22

performance with a wide operating voltage window of 1.4 V and salt adsorption capacity

23

(SAC) of 14.9 mg/g in 500 mg/L NaCl. The SAC retention ratio of the cell can be as high as

24

95.4% after 350 adsorption-desorption cycles at 1.0/0 V while that of the CDI cell consisting

25

of activated carbon electrodes was only 15.7% after 285 cycles. The enhanced cyclic stability

26

of the hybrid CDI cell is attributed to the employment of the MnO2 anode, which avoided the

27

use and oxidation of carbon anodes.

28

2 ACS Paragon Plus Environment

Page 2 of 20

Page 3 of 20

29

Environmental Science & Technology Letters

INTRODUCTION

30

Capacitive deionization (CDI) is a promising desalination technology with the

31

advantages of low cell voltage operation, high energy efficiency and environmental

32

friendliness. CDI usually employs two porous carbon electrodes to adsorb ions from water

33

with an external electric field as the driving force.1, 2 Recently, the exploration of new CDI

34

systems3-7 and electrode materials8-10, the optimization of operational processes,11-13 the

35

advances in related theories14,

36

Nevertheless, the gradual performance degradation during the operation of CDI is still an

37

unsolved problem.16, 17

15

etc. have greatly promoted the development of CDI.

38

Although the cell voltage of CDI is usually lower than the theoretical value of water

39

electrolysis (1.23 V vs. NHE), parasitic reactions occur during the charging process and the

40

carbon anode of CDI is continually oxidized.18,

41

introduces negatively charged functional groups into the carbon surface and thus aggravates

42

co-ion expulsion.16 Moreover, it may reduce the specific capacitance of the carbon anodes. As

43

a result, salt adsorption capacity (SAC) of CDI gradually decreases during cycling. Therefore,

44

the key to inhibit the performance degradation and improve the cyclic stability of CDI is to

45

suppress the oxidation of the carbon anode. Up to now, low-cell voltage operation,20 polarity

46

reversal,17 introducing ion exchange membranes or polymers,21, 22 etc. have been attempted to

47

improve the cyclic stability of CDI. However, these methods usually have limited

48

effectiveness and may lower the SAC or increase the operational cost of CDI.

19

The oxidation of the carbon anode

49

In 2015, Gao et al. proposed inverted CDI (i-CDI) consisting of a carbon anode with net

50

negative surface charges and a carbon cathode with net positive surface charges.5 When the 3 ACS Paragon Plus Environment

Environmental Science & Technology Letters

51

cell is charged, the electrodes are polarized towards their potential of zero charge (Epzc) and

52

desorb ions. When it is discharged, ions are adsorbed to neutralize the surface charges in the

53

electrodes. I-CDI effectively avoided the negative effects of co-ion expulsion on CDI

54

performance and exhibited excellent cyclic stability during 600 adsorption-desorption cycles.

55

However, it suffers from relatively narrow operating voltage window and SAC (0.8/0 V, ~1.8

56

mg/g). In addition, oxidation of carbon anodes still occur in i-CDI, which may affect the

57

properties of carbon anodes and thus greatly reduce the SAC of i-CDI.23

58

Recently, various pseudocapacitive or battery materials have been explored as electrode

59

materials of different deionization systems.24-26 MnO2 is a low-cost and environmentally

60

friendly pseudocapacitive metal oxide and MnO2/carbon composites with different structure

61

have been used as CDI electrode materials.27-30 However, these works focused on the

62

preparation of electrode materials and few of them investigated the impact of MnO2 anode on

63

the cyclic stability of CDI. In this work, a hybrid CDI cell (MnO2//AC-QPVP) consisting of a

64

MnO2 anode and a quaternized poly (4-vinyl pyridine) coated activated carbon (AC-QPVP)

65

cathode was assembled. Due to the ion selectivity of the electrodes, MnO2//AC-QPVP

66

exhibited inverted CDI performance with a wide operating voltage window and a high SAC.

67

Moreover, as the cell avoided the use of carbon anode materials, it exhibited good cyclic

68

stability with a SAC retention ratio of 95.4% during 350 adsorption-desorption cycles at 1.0/0

69

V.

70

MATERIALS AND METHODS

71

Preparation of MnO2.

72

MnO2 was prepared by the reaction of KMnO4 with HCl.31 Typically, 3.6 g KMnO4 was 4 ACS Paragon Plus Environment

Page 4 of 20

Page 5 of 20

Environmental Science & Technology Letters

73

first dissolved in 40 mL deionized water at 85 ºC. Then 20 mL 1:1 (v/v) HCl was added into

74

the KMnO4 solution dropwise under vigorous stirring. After the addition of HCl was

75

completed, the resulting product was collected, washed with deionized water and finally dried

76

in a vacuum oven at 110 ºC for 6 h. Quaternized poly (4-vinylpyridine) coated activated

77

carbon (AC-QPVP) was prepared through polymerization, crosslinking and quaternization

78

processes, as reported in our previous work.23

79

Characterization.

80

The morphology and elemental composition of MnO2 were examined using

81

field-emission scanning electron microscopy (FESEM, FEI NOVA NanoSEM 450) equipped

82

with an energy-dispersive spectrometer (EDS), and transmission electron microscopy (FEI

83

Tecnai G20). The crystalline structure of MnO2 was characterized by X-ray diffractometer

84

(Rigaku D/Max 2400) using Cu Kα radiation (λ=1.5406 Å). To characterize the pore structure

85

of MnO2, the sample was first degassed at 150 ºC for 12 h under vacuum and then nitrogen

86

adsorption-desorption isotherms were measured using a Micromeritics 3-Flex surface

87

characterization analyzer at 77 K. Inductively coupled plasma atomic emission spectroscopy

88

(ICP-AES) was used to analyze the composition of the prepared MnO2 and determine the

89

concentration of Mn in the tank after the cyclic test of MnO2//AC-QPVP.

90

CDI tests.

91

CDI electrodes were prepared by coating the homogeneous slurry of the active material,

92

acetylene black, polyvinyl butyral (PVB) and polyvinylpyrrolidone (PVP) in a weight ratio of

93

82.5:10:6:1.5 onto graphite paper (57 cm2) followed by drying at 80 ºC overnight. The CDI

94

cell consisting of a MnO2 anode and an AC-QPVP cathode was denoted as MnO2//AC-QPVP 5 ACS Paragon Plus Environment

Environmental Science & Technology Letters

Page 6 of 20

95

while that consisting of two AC electrodes was denoted as AC//AC; the CDI cell with a

96

MnO2 anode and an AC cathode was denoted as MnO2//AC and that with an AC anode and

97

an AC-QPVP cathode was denoted as AC//AC-QPVP. A silicon gasket with the thickness of

98

~1.3 mm and two pieces of nonwoven fabric with the thickness of ~120 m were used as the

99

spacer and the separator of the CDI cells, respectively. All CDI tests were conducted under

100

constant voltage operation. In a typical cycle, the CDI cells were first charged at a certain cell

101

voltage for 5 min and then short-circuited for 5 min. Single-pass tests were conducted during

102

which 2.5 L NaCl solution in a tank was pumped continuously through the CDI cell and then

103

back to the tank. An electrochemical workstation (CHI 660D) was used to supply the voltage

104

needed. Conductivity and pH changes in the NaCl solution at the outlet of CDI cells were

105

recorded by the conductivity and pH monitor system. The salt adsorption/desorption capacity

106

(, mg/g), charge (Σ, C/g) passed during the charging and discharging processes, and charge

107

efficiency () were calculated according to eqs 1, 2 and 3, respectively:

108

 

    c0  ct 

109



110



m

 idt

(1)

(2)

m

 F  

(3)

111

where Ф refers to the flow rate of NaCl solution and is 9.2 mL/min in this work, c0 and ct

112

(mg/L) refer to the influent and effluent NaCl concentration, respectively, m is the total mass

113

of the two electrodes in a CDI cell (0.23-0.27 g in this work), i (A) is the charge current, F

114

refers to Faraday constant (96485 C/mol) and M is the molar mass of NaCl (58.5 g/mol).

115

RESULTS AND DISCUSSION 6 ACS Paragon Plus Environment

Page 7 of 20

116

Environmental Science & Technology Letters

Properties of MnO2 and AC-QPVP.

117

The morphology and surface properties of AC-QPVP have been reported in our previous

118

work.23 There are positively charged quaternary ammonium groups on the surface of

119

AC-QPVP. As a result, the AC-QPVP electrode is anion selective and its Epzc can be as

120

negative as -0.745 V vs. Ag/AgCl. The structure and morphology of the prepared MnO2 are

121

summarized in Figure S1. The obtained product is birnessite-type MnO2 with submicron

122

flower-like structure composed of highly interconnected carbon nanosheets. Its Brunauer-

123

Emmett- Teller (BET) specific surface area is 193 m2/g and the pore size distribution is

124

centered at about 8.6 nm. MnO2 can reversibly intercalate/deintercalate Na+ in the positive

125

potential range following the eqs 4.32, 33

126 127

MnO2 + Na + + e-

MnOONa

(4)

CDI performance at different cell voltages.

128

Figure 1 shows the CDI performance of AC//AC and MnO2//AC-QPVP at different cell

129

voltages in 500 mg/L NaCl. As shown in Figure 1a, AC//AC exhibits conventional CDI

130

performance, i.e. ions are adsorbed when the cell is charged and desorbed when the cell is

131

discharged. By contrast, MnO2//AC-QPVP exhibits inverted performance at different cell

132

voltages. When the cell is charged, ions are released from the electrodes into the electrolyte.

133

During this process, the MnO2 electrode is oxidized and cations in the MnO2 structure are

134

deintercalated to maintain charge balance. Simultaneously, the AC-QPVP electrode is

135

polarized towards its Epzc and desorbs Cl-. When the cell is discharged, ions are stored into

136

the electrodes during which the MnO2 electrode is reduced and intercalate Na+ while the

137

AC-QPVP electrode stays far away from its Epzc and adsorbs Cl-. ICP results indicate that K+ 7 ACS Paragon Plus Environment

Environmental Science & Technology Letters

138

exists in the prepared MnO2 and the amount is 19.9 mg/g. In addition, it has been reported

139

that a certain amount of H3O+ exists in MnO2.34 During the CDI tests, K+ and H3O+ in the

140

MnO2 structure were gradually replaced by Na+,35 which can be demonstrated by the EDS

141

results shown in Figure S2.

142

For MnO2//AC and AC//AC-QPVP, negligible changes in the effluent NaCl

143

concentration were observed (Figure S3a). However, they consumed comparable charge with

144

AC//AC and MnO2//AC-QPVP (Figure S3b), indicating their low charge efficiency. It is

145

supposed that the migration of a single kind of ion between the electrodes rather than the

146

simultaneous removal/release of sodium and chloride ions dominates in MnO2//AC and

147

AC//AC-QPVP, which results in their poor desalination performance.

148

The NaCl concentration variation range of MnO2//AC-QPVP increases steadily as the

149

cell voltage increases from 0.6 V to 1.4 V, which indicates that the operating voltage window

150

of MnO2//AC-QPVP can reach 1.4 V. From Figure 1b, it can be seen that the current density

151

of AC//AC and MnO2//AC-QPVP increases with the applied cell voltage, indicating a gradual

152

increase in the charge passed.

8 ACS Paragon Plus Environment

Page 8 of 20

Page 9 of 20

Environmental Science & Technology Letters

153 154

Figure 1. Effluent NaCl concentration profiles (a) and current density (b) of AC//AC and

155

MnO2//AC-QPVP at different cell voltages in 500 mg/L NaCl.

156

Figure 2 shows the SAC of AC//AC and MnO2//AC-QPVP according to eqs 1 and 3. As

157

the cell voltage increases from 0.6 V to 0.8, 1.0, 1.2 and 1.4 V, the SAC of MnO2//AC-QPVP

158

increases from 6.0 mg/g to 8.0, 10.0, 11.9 and 14.4 mg/g, respectively, while that of AC//AC

159

is 3.8,6.3, 9.0, 9.7 and 9.7 mg/g, respectively (Figure 2a).

9 ACS Paragon Plus Environment

Environmental Science & Technology Letters

160 161

Figure 2. SAC (a) and charge efficiency during charging (b) of AC//AC and

162

MnO2//AC-QPVP at different cell voltages in 500 mg/L NaCl. The average values of

163

triplicate experiments are shown and the error bars represent the standard deviations.

164

From Figure 2b, it can be seen that the charge efficiency of both AC//AC and

165

MnO2//AC-QPVP exhibits a downward trend as the cell voltage increases, which can be

166

attributed to aggravated parasitic reactions at high cell voltages. Nevertheless, charge

167

efficiency of MnO2//AC-QPVP stays above 0.67 and is higher than that of AC//AC at each

168

cell voltage. This can be attributed to the ion selectivity of the MnO2 and AC-QPVP

169

electrodes, which can greatly diminish co-ion expulsion. The SAC and charge efficiency

10 ACS Paragon Plus Environment

Page 10 of 20

Page 11 of 20

Environmental Science & Technology Letters

170

results indicate that the CDI performance of MnO2//AC-QPVP at different cell voltages is

171

much better than that of AC//AC.

172

The salt desorption capacity, and charge efficiency during discharging of

173

MnO2//AC-QPVP at different cell voltages are shown in Figure S4. The salt desorption

174

capacity of MnO2//AC-QPVP is approximately equal to its SAC. However, the charge

175

efficiency during discharging is above 0.81 and higher than that during charging, which is

176

because that more charge is consumed by parasitic reactions during charging.

177

Cyclic performance.

178

The cyclic performance of AC//AC and MnO2//AC-QPVP was investigated in 500 mg/L

179

NaCl at the cell voltage of 1.0/0 V. The obtained effluent NaCl concentration profiles, current

180

density and effluent pH changes during the cyclic tests are shown in Figure S5, Figure S6 and

181

Figure S7, respectively.

182

For AC//AC, the variation range of effluent NaCl concentration at the 285th cycle is

183

much smaller than that at the 5th cycle, indicating that a serious performance degradation

184

occurred (Figure S8a). As shown in Figure 3a, the SAC of AC//AC at the 5th cycle is

185

calculated to be 8.3 mg/g and falls rapidly to 1.3 mg/g at the 285th cycle. The SAC retention

186

ratio is only 15.7%. Correspondingly, the charge efficiency decreases from 0.61 at the 5th

187

cycle to 0.13 at the 285th cycle. After 288 adsorption-desorption cycles, the polarity of the

188

applied cell voltage on AC//AC was reversed. The SAC recovers to 8.2 mg/g and the charge

189

efficiency goes back to 0.49. However, significant performance degradation occurs again

190

during the continued cyclic test. The SAC declines to 5.3 mg/g and the charge efficiency

191

decreases to 0.29 at the 350th cycle. 11 ACS Paragon Plus Environment

Environmental Science & Technology Letters

192

For MnO2//AC-QPVP, the adsorption process at the 350th cycle becomes slower than

193

that at the 5th cycle, as shown in Figure S8b. Meanwhile, the current of MnO2//AC-QPVP

194

gradually decreases during the cyclic test, as shown in Figure S6. The instantaneous current

195

during charging at the 5th cycle is 0.1962 while that at the 350th cycle decreases to 0.1156 A.

196

Correspondingly, the ESR increases from 5.1  at the 5th cycle to 8.7  at the 350th cycle

197

during the cycling. These phenomena may be related to the oxidation of the conductive agent

198

(carbon black) in the anode. Despite this, most of the desalination performance of

199

MnO2//AC-QPVP was retained after 350 adsorption-desorption cycles. The SAC of

200

MnO2//AC-QPVP at the 5th cycle is calculated to be 8.7 mg/g. During the cyclic test, it

201

increases a little first as a result of the activation of the MnO2 electrode and then decreases

202

slightly to 8.3 mg/g. The SAC retention ratio is as high as 95.4%. To demonstrate the

203

reproducibility of the results, the cyclic performance of another MnO2//AC-QPVP cell is

204

provided in Figure S9. Its SAC at the 5th cycle and the 350th cycle is 8.4 mg/g and 7.6 mg/g,

205

respectively, and the SAC retention ratio is 90.5%.

12 ACS Paragon Plus Environment

Page 12 of 20

Page 13 of 20

Environmental Science & Technology Letters

206 207

Figure 3. SAC (a) and charge efficiency during charging (b) of AC//AC and

208

MnO2//AC-QPVP during 350 adsorption-desorption cycles at the cell voltage of 1.0/0 V in

209

500 mg/L NaCl.

210

Charge efficiency of MnO2//AC-QPVP maintains above 0.8 during the cyclic test and is

211

much higher than that of AC//AC. In a word, MnO2//AC-QPVP exhibited much better cyclic

212

stability than AC//AC and the i-CDI cell with a negatively charged carbon anode reported in

213

our previous work.23 The improved cyclic stability is attributed to the employment of the

214

MnO2 electrode, which avoided the use of carbon anodes and the consequent irreversible

215

carbon oxidation. 13 ACS Paragon Plus Environment

Environmental Science & Technology Letters

216

Environmental implications.

217

The concentration of Mn in the tank was tested by the ICP-AES method to evaluate the

218

influences of MnO2 on the quality of produced water. After MnO2//AC-QPVP was tested for

219

350 adsorption-desorption cycles, the concentration of Mn in the tank is 2.9 g/L, which is

220

much lower than the usually acceptable level for drinking water (100 g/L). Therefore, the

221

impact of the MnO2 electrode on the quality of the produced water is negligible. In summary,

222

this work demonstrated a novel strategy to enhance the cyclic stability of CDI by using

223

non-carbon MnO2 as the anode material of CDI, which can be extended to other

224

pseudocapacitive electrode materials and may pave the way for the large-scale industrial

225

application of CDI.

226

ASSOCIATED CONTENT

227

Supporting Information. Structure and morphology of MnO2; EDS spectra of the MnO2

228

electrodes; CDI performance of MnO2//AC and AC//AC-QPVP; salt desorption capacity, and

229

charge efficiency during discharging of MnO2// AC-QPVP; effluent NaCl concentration

230

profiles, current density and effluent pH changes of AC//AC and MnO2//AC-QPVP during

231

the cyclic tests; adsorption curves of AC//AC and MnO2//AC-QPVP at the start and end of

232

the cyclic test; changes in SAC of another MnO2// AC-QPVP cell during cycling.

233

NOTES

234

The authors declare no competing financial interest.

235

ACKNOWLEDGEMENTS

236

This work was supported by the National Natural Science Foundation of China (NSFC,

237

No. 21336001), and the Qaidam Salt Lake Chemical Joint Research Fund Project of NSFC 14 ACS Paragon Plus Environment

Page 14 of 20

Page 15 of 20

Environmental Science & Technology Letters

238

and Qinghai Province State People's Government (No. U1507103).

239

REFERENCES

240

1.

241

science and technology of water desalination by capacitive deionization. Prog. Mater. Sci.

242

2013, 58, 1388-1442.

243

2.

244

desalination via capacitive deionization: what is it and what can we expect from it? Energy

245

Environ. Sci. 2015, 8, 2296-2319.

246

3.

247

Desalination via a new membrane capacitive deionization process utilizing flow-electrodes.

248

Energy Environ. Sci. 2013, 6, 1471-1475.

249

4.

250

desalination performance of capacitive techniques. Energy Environ. Sci. 2014, 7, 3683-3689.

251

5.

252

for stable and efficient capacitive deionization using inverted adsorption-desorption behavior.

253

Energy Environ. Sci. 2015, 8, 897-909.

254

6.

255

capacitive deionization system. Environ. Sci. Technol. Lett. 2017, 4, 470-474.

256

7.

257

hexacyanoferrate electrodes for continuous cation intercalation desalination of brackish water.

258

Electrochim. Acta 2017, 255, 369-378.

259

8.

Porada, S.; Zhao, R.; van der Wal, A.; Presser, V.; Biesheuvel, P. M., Review on the

Suss, M. E.; Porada, S.; Sun, X.; Biesheuvel, P. M.; Yoon, J.; Presser, V., Water

Jeon, S. I.; Park, H. R.; Yeo, J. G.; Yang, S.; Cho, C. H.; Han, M. H.; Kim, D. K.,

Lee, J.; Kim, S.; Kim, C.; Yoon, J., Hybrid capacitive deionization to enhance the

Gao, X.; Omosebi, A.; Landon, J.; Liu, K. L., Surface charge enhanced carbon electrodes

Zhang, J.; Hatzell, K. B.; Hatzell, M. C., A combined heat- and power-driven membrane

Porada, S.; Shrivastava, A.; Bukowska, P.; Biesheuvel, P. M.; Smith, K. C., Nickel

Wang, M.; Xu, X.; Liu, Y.; Li, Y.; Lu, T.; Pan, L., From metal-organic frameworks to 15 ACS Paragon Plus Environment

Environmental Science & Technology Letters

260

porous carbons: a promising strategy to prepare high-performance electrode materials for

261

capacitive deionization. Carbon 2016, 108, 433-439.

262

9.

263

Starch derived porous carbon nanosheets for high-performance photovoltaic capacitive

264

deionization. Environ. Sci. Technol. 2017, 51, 9244-9251.

265

10. Wang, M.; Xu, X.; Tang, J.; Hou, S.; Hossain, M. S. A.; Pan, L.; Yamauchi, Y., High

266

performance capacitive deionization electrodes based on ultrathin nitrogen-doped

267

carbon/graphene nano-sandwiches. Chem. Commun. 2017.

268

11. Dykstra, J. E.; Zhao, R.; Biesheuvel, P. M.; van der Wal, A., Resistance identification and

269

rational process design in capacitive deionization. Water Res. 2016, 88, 358-370.

270

12. Tang, W. W.; He, D.; Zhang, C. Y.; Waite, T. D., Optimization of sulfate removal from

271

brackish water by membrane capacitive deionization (MCDI). Water Res. 2017, 121,

272

302-310.

273

13. Qu, Y. T.; Campbell, P. G.; Gu, L.; Knipe, J. M.; Dzenitis, E.; Santiago, J. G.; Stadermann,

274

M., Energy consumption analysis of constant voltage and constant current operations in

275

capacitive deionization. Desalination 2016, 400, 18-24.

276

14. Dykstra, J. E.; Keesman, K. J.; Biesheuvel, P. M.; van der Wal, A., Theory of pH changes

277

in water desalination by capacitive deionization. Water Res. 2017, 119, 178-186.

278

15. Hemmatifar, A.; Oyarzun, D. I.; Palko, J. W.; Hawks, S. A.; Stadermann, M.; Santiago, J.

279

G., Equilibria model for pH variations and ion adsorption in capacitive deionization

280

electrodes. Water Res. 2017, 122, 387-397.

281

16. Bouhadana, Y.; Avraham, E.; Noked, M.; Ben-Tzion, M.; Soffer, A.; Aurbach, D.,

Wu, T. T.; Wang, G.; Dong, Q.; Zhan, F.; Zhang, X.; Li, S. F.; Qiao, H. Y.; Qiu, J. S.,

16 ACS Paragon Plus Environment

Page 16 of 20

Page 17 of 20

Environmental Science & Technology Letters

282

Capacitive deionization of NaCl solutions at non-steady-state conditions: inversion

283

functionality of the carbon electrodes. J. Phys. Chem. C 2011, 115, 16567-16573.

284

17. Cohen, I.; Avraham, E.; Bouhadana, Y.; Soffer, A.; Aurbach, D., The effect of the

285

flow-regime, reversal of polarization, and oxygen on the long term stability in capacitive

286

de-ionization processes. Electrochim. Acta 2015, 153, 106-114.

287

18. Lee, J.-H.; Bae, W.-S.; Choi, J.-H., Electrode reactions and adsorption/desorption

288

performance related to the applied potential in a capacitive deionization process. Desalination

289

2010, 258, 159-163.

290

19. He, D.; Wong, C. E.; Tang, W.; Kovalsky, P.; Waite, T. D., Faradaic reactions in water

291

desalination by batch-mode capacitive deionization. Environ. Sci. Technol. Lett. 2016, 3,

292

222-226.

293

20. Cohen, I.; Avraham, E.; Bouhadana, Y.; Soffer, A.; Aurbach, D., Long term stability of

294

capacitive de-ionization processes for water desalination: the challenge of positive electrodes

295

corrosion. Electrochim. Acta 2013, 106, 91-100.

296

21. Omosebi, A.; Gao, X.; Landon, J.; Liu, K., Asymmetric electrode configuration for

297

enhanced membrane capacitive deionization. ACS Appl. Mater. Interfaces 2014, 6, 12640-9.

298

22. Gao, X.; Omosebi, A.; Holubowitch, N.; Liu, A.; Ruh, K.; Landon, J.; Liu, K.,

299

Polymer-coated composite anodes for efficient and stable capacitive deionization.

300

Desalination 2016, 399, 16-20.

301

23. Wu, T.; Wang, G.; Zhan, F.; Dong, Q.; Ren, Q.; Wang, J.; Qiu, J., Surface-treated carbon

302

electrodes with modified potential of zero charge for capacitive deionization. Water Res. 2016,

303

93, 30-7. 17 ACS Paragon Plus Environment

Environmental Science & Technology Letters

304

24. Kim, S.; Lee, J.; Kim, C.; Yoon, J., Na2FeP2O7 as a novel material for hybrid capacitive

305

deionization. Electrochim. Acta 2016, 203, 265-271.

306

25. Su, X.; Tan, K.-J.; Elbert, J.; Rüttiger, C.; Gallei, M.; Jamison, T. F.; Hatton, T. A.,

307

Asymmetric Faradaic systems for selective electrochemical separations. Energy Environ. Sci.

308

2017, 10, 1272-1283.

309

26. Kim, T.; Gorski, C. A.; Logan, B. E., Low energy desalination using battery electrode

310

deionization. Environ. Sci. Technol. Lett. 2017, 4, 444-449.

311

27. Yang, J.; Zou, L. D.; Song, H. H.; Hao, Z. P., Development of novel MnO2/nanoporous

312

carbon composite electrodes in capacitive deionization technology. Desalination 2011, 276,

313

199-206.

314

28. Hand, S.; Cusick, R. D., Characterizing the impacts of deposition techniques on the

315

performance of MnO2 cathodes for sodium electrosorption in hybrid capacitive deionization.

316

Environ. Sci. Technol .2017, 51, 12027–12034.

317

29. Zhou, F.; Gao, T.; Luo, M.; Li, H. B., Preferential electrosorption of anions by

318

C/Na0.7MnO2 asymmetrical electrodes. Sep. Purif. Technol. 2018, 191, 322-327.

319

30. Chen, B. W.; Wang, Y. F.; Chang, Z.; Wang, X. W.; Li, M. X.; Liu, X.; Zhang, L. X.; Wu,

320

Y. P., Enhanced capacitive desalination of MnO2 by forming composite with multi-walled

321

carbon nanotubes. Rsc Adv. 2016, 6, 6730-6736.

322

31. Ren, Y. M.; Yan, N.; Wen, Q.; Fan, Z. J.; Wei, T.; Zhang, M. L.; Ma, J.,

323

Graphene/delta-MnO2 composite as adsorbent for the removal of nickel ions from wastewater.

324

Chem. Eng. J. 2011, 175, 1-7.

325

32. Toupin, M.; Brousse, T.; Belanger, D., Charge storage mechanism of MnO2 electrode 18 ACS Paragon Plus Environment

Page 18 of 20

Page 19 of 20

Environmental Science & Technology Letters

326

used in aqueous electrochemical capacitor. Chem. Mater. 2004, 16, 3184-3190.

327

33. Subramanian, V.; Zhu, H. W.; Wei, B. Q., Nanostructured MnO2: Hydrothermal synthesis

328

and electrochemical properties as a supercapacitor electrode material. J. Power Sources 2006,

329

159, 361-364.

330

34. Yao, Q. F.; Xiong, Y.; Wang, H. W.; Wanga, C.; Sun, Q. F., MnO2 nanoflakes/cellulose

331

nanofibre aerogel fabricated via ultrasonication for high-performance water desalination. J.

332

Mater. Chem. A 2017, 5, 9580-9590.

333

35. Liu, Y.; Qiao, Y.; Zhang, W.; Xu, H.; Li, Z.; Shen, Y.; Yuan, L.; Hu, X.; Dai, X.; Huang,

334

Y., High-performance aqueous sodium-ion batteries with K0.27MnO2 cathode and their

335

sodium storage mechanism. Nano Energy 2014, 5, 97-104.

336

19 ACS Paragon Plus Environment

Environmental Science & Technology Letters

337

20 ACS Paragon Plus Environment

Page 20 of 20