ARTICLE

Improved Properties of Oxygen and Argon RF Plasma-Activated Polyester Fabrics Loaded with TiO2 Nanoparticles Darka Mihailovic´,† Zoran Sˇaponjic´,‡ Ricardo Molina,§ Nevena Puacˇ,| Petar Jovancˇic´,† Jovan Nedeljkovic´,‡ and Maja Radetic´*,† Textile Engineering Department, Faculty of Technology and Metallurgy, University of Belgrade, Karnegijeva 4, 11120 Belgrade, Serbia, Vincˇa Institute of Nuclear Sciences, P.O. Box 522, 11001 Belgrade, Serbia, Chemical and Biomolecular Nanotechnology Department, Institut de Quı´mica Avanc¸ada de Catalunya (IQAC), Consejo Superior de Investigaciones Cientı´ficas (CSIC), C/Jordi Girona 18-26, 08034 Barcelona, Spain, and Institute of Physics, Pregrevica 118, 11080 Zemun, Serbia

ABSTRACT The potentials of low-pressure capacitively coupled RF oxygen and argon plasmas for the activation of polyester fibers surface that can enhance the deposition of colloidal TiO2 nanoparticles were discussed. SEM and XPS analysis confirmed the plasmainduced morphological and chemical changes on the surface of polyester fibers. Oxygen and argon plasma pretreated polyester fabrics loaded with TiO2 nanoparticles provided maximum reduction of Gram-negative bacteria E. coli and UV blocking. The self-cleaning effects tested on blueberry juice stains and photodegradation of methylene blue in aqueous solution proved excellent photocatalytic activity of TiO2 nanoparticles deposited onto fiber surface. Although both plasmas significantly contributed to overall improvement of properties of such nanocomposite textile material, oxygen plasma treatment, in particular, enhanced the deposition of colloidal TiO2 nanoparticles and thus ensured superior effects. KEYWORDS: TiO2 nanoparticles • PES fabric • oxygen plasma • argon plasma

1. INTRODUCTION

T

he potentials of plasma for targeted functionalization of different textile materials were extensively studied in last two decades (1). Different plasma-chemical reactions and hence, desirable effects can be obtained by appropriate choice of plasma system and regulation of operating conditions (gas type, gas flow rate, pressure, power, exposure time) (2). Although plasma effects were explored on cellulosic fibers (1, 3-7), the major research so far has focused on imparting the enhanced wettability, dyeability, and printability as well as shrink-resistance and antipilling properties to wool fibers (1, 8-16). The strong hydrophobic nature of some synthetic fibers (polyester, polypropylene) makes adhesion, dyeing, and printing of these materials more complex. The improvement of hydrophilicity of these fibers by the action of reactive and nonpolymerizable plasmas was described in literature in detail (16-19). The latest studies opened up some new perspectives to plasma that could be utilized for engineering of durable nanocomposite textile materials (20-26). Namely, plasma can activate the surface of different natural and synthetic * Corresponding author. E-mail: [email protected]. Received for review March 15, 2010 and accepted May 21, 2010 †

University of Belgrade. Vincˇa Institute of Nuclear Sciences. § Consejo Superior de Investigaciones Cientı´ficas. | Institute of Physics. DOI: 10.1021/am100209n ‡

2010 American Chemical Society

1700

VOL. 2 • NO. 6 • 1700–1706 • 2010

fibers and hence facilitate the anchoring of metal and metal oxide nanoparticles (NPs). The modification of textile materials with TiO2 NPs seems to be a viable alternative to conventional finishing processes since small amounts of nanoparticles simultaneously can provide good antibacterial, UV protective and self-cleaning properties. However, the lack of chemical bonding between hydrophobic polyester (PES) fibers and TiO2 NPs makes the deposition of TiO2 NPs onto PES fabrics highly challenging (23). The creation of new polar functional groups and particularly carboxylic groups on the PES fiber surface is favorable for the efficient binding of colloidal TiO2 NPs. Namely, when diameter of nanocrystalline anatase TiO2 particles becomes smaller than 20 nm, the surface Ti atoms adjust their coordination environment from octahedral to more reactive pentacoordinated (square pyramidal) (27, 28). These undercoordinated defect sites provide improved binding efficiency between carboxylic groups on the fiber surface and Ti atoms. Recent studies confirmed the positive effects of plasma on the loading of PES fabrics with TiO2 NPs (22, 23). However, the research so far was oriented toward application of air and oxygen plasmas at low or atmospheric pressures, as the presence of oxygen atoms in the discharge ensure effective plasma oxidation and plasma etching. The aim of this study was to compare the potentials of extremely reactive oxygen and inert argon RF plasmas at low-pressure to activate the PES fiber surface and thus, enhance binding efficiency of the colloidal TiO2 NPs. The chemical changes on the surface of PES fibers induced by plasma treatment www.acsami.org

Published on Web 06/04/2010

2. EXPERIMENTAL SECTION Desized and bleached polyester (PES, 115 g/m2) woven fabric was cleaned in the bath containing 0.5% nonionic washing agent Felosan RG-N (Bezema) at liquor-to-fabric ratio of 50:1. After 15 min of washing at 50 °C, the fabrics were rinsed once with warm water (50 °C) for 3 min and three times (3 min) with cold water. Subsequently, the samples were dried at room temperature (24). Glow-discharge treatment of PES fabrics was performed in low-pressure capacitively coupled RF-induced (13.56 MHz) O2 and Ar plasmas. The power applied to capacitively coupled reactor was 100 W. The treatment time was 2.5 min, the gas flow rate 150 sccm while the pressure was maintained at the constant level of 0.27 mbar. It must be emphasized that our plasma system (29) cannot provide perfect evacuation of air out of the chamber and a small fraction of air remained in the chamber. The colloid consisting of TiO2 NPs was synthesized by acid hydrolysis of TiCl4. All the chemicals used for the synthesis of TiO2 colloid were analytical grade and used as received without further purification (Aldrich, Fluka). Milli-Q deionized water was used as a solvent. The colloid of TiO2 NPs was prepared in a manner analogous to the procedure proposed by Rajh et al. (30). Four milliliters of TiCl4, cooled to -20 °C, was added dropwise to 200 mL of cooled water (at 4 °C) under vigorous stirring. Obtained clear solution was kept at this temperature for 30 min. The pH value of the solution was in a range 0-1, depending on TiCl4 concentration. Slow growth of the particles was achieved by applying dialysis against 15 times higher volume of water at 4 °C for 3 days until the pH of the solution reached 3.5. Water for dialysis was changed daily. The concentration of TiO2 colloidal solution was determined from the concentration of the peroxide complex obtained after dissolving the particles in concentrated H2SO4 (31). Afterward, the colloid was thermally treated in reflux at 60 °C for 16 h. The synthesized colloid consisted of faceted, single-crystalline, anatase TiO2 NPs with an average size of about 6 nm (32). Untreated PES fabric and PES fabrics pretreated with O2 or Ar plasma were dipped into the 0.1 M TiO2 colloid (liquor-tofabric ratio of 1:20) for 5 min and dried at room temperature. After 30 min of curing at 100 °C, the fabrics were soaked twice (5 min) with deionized water and dried at room temperature. The PES fiber surface morphology before and after plasma treatment was studied by scanning electron microscopy (SEM, JEOL JSM 6460 LV). Gold layer was deposited on the samples before the analysis. The evaluation of surface chemical changes was carried out by X-ray photoelectron spectroscopy (XPS) analysis. Samples were analyzed using a PHI Model 5500 Multitechnique System with an Al KR monochromatic X-ray source operating at 350 W. The measurements were conducted under a takeoff angle of 45°. Survey scans were in the range 0-1100 eV, with pass energy of 187.85 eV. High-resolution scans were obtained on the C1s, O1s and Ti2p photoelectron peaks, with pass energy of 23.5 eV. Binding energies were referenced to the C1s photopeak position for C-C and C-H species at 285.0 eV. Surface composition was estimated after a linear background subtraction from the area of the different photoemission peaks modified by their corresponding sensitivity factors (33). www.acsami.org

The wettability of the PES fabrics was evaluated by measuring the wetting time according to TEGEWA drop test (34). The antibacterial efficiency of fabrics was quantitatively evaluated by using the Gram-negative bacterium Escherichia coli ATCC 25922. Bacterial inoculum was prepared in the Tripton soy broth (Torlak, Serbia), which was used as the growth medium for bacteria while the physiological saline solution (pH 7.0) was used as the testing medium. Bacteria were cultivated in 3 mL of Tripton soy broth at 37 °C and left overnight (late exponential stage of growth). Afterward, 70 mL of sterile physiological saline solution was added to sterile beaker (400 mL), which was then inoculated with 0.7 mL of the bacterial inoculum. The zero counts were made by removing 1 mL aliquots from the flask with inoculum, and making 1:10 and 1:100 dilutions in physiological saline solution. 0.1 mL of the 1:100 solution was put on the Tripton soy agar (Torlak, Serbia) and after 24 h of incubation at 37 °C, the zero time counts (initial number of bacterial colonies) of viable bacteria were made. One gram of the sterile PES fabric cut into small pieces was placed into the beaker (70 mL of sterile physiological saline solution inoculated with 0.7 mL of the bacterial inoculum) and shaken for 2 h under UV illumination (TL-D lamp, 18 W, Philips). Two-hour counts were made in accordance with an abovedescribed procedure. The percentage of bacteria reduction (R, %) was calculated in accordance with eq 1

R)

C0 - C 100 C0

(1)

where C0 (CFU, colony forming units) is the number of bacterial colonies on the control fabric (fabric without TiO2 NPs) and C (CFU) is the number of bacterial colonies on the PES fabric loaded with TiO2 NPs (35, 36). The UV protection factor (UPF value) of the PES fabrics was determined by UV/vis spectrophotometer Cary 100 Scan (Varian). The UV protection factor (UPF) value was automatically calculated on the basis of recorded data in accordance with Australia/New Zealand standard AS/NZS 4399:1996 using a Startek UV fabric protection application software version 3.0 (Startek Technology). Laundering durability of antibacterial and UV protective effects was examined after five washing cycles in Polycolor (Werner Mathis AG) laboratory beaker dyer at 45 rpm. The fabrics were washed in the bath containing 0.5% Felosan RG-N (Bezema) at liquor-to-fabric ratio of 40:1. After 30 min of washing at 40 °C, fabrics were rinsed once with warm water (40 °C) for 3 min and three times (3 min) with cold water. The fabrics were subsequently dried at 70 °C (35). The percentage of bacteria reduction after five washing cycles was determined according to eq 1. The self-cleaning effects were evaluated on the PES fabrics which were stained with blueberry juice. Untreated and plasma pretreated PES fabrics loaded with TiO2 NPs were cut into 5 × 5 cm2 pieces and stained with 50 µL of blueberry juice. After drying at room temperature, the fabrics were illuminated using ULTRA-VITALUX lamp (300 W, Osram) for 24 h. The lamp provided sunlike irradiation with a spectral radiation power distribution at wavelengths between 300-1700 nm. Photocatalytic activity of TiO2 NPs deposited onto the untreated and plasma pretreated PES fabrics was examined by degradation of methylene blue (MB) in aqueous solution under UV illumination. 0.5 g of PES fabric was immersed in 25 mL of MB solution (10 mg L-1, pH 5.81) and illuminated by ULTRAVITALUX lamp (300 W, Osram) for 2, 4, 6, 8, and 24 h. The MB VOL. 2 • NO. 6 • 1700–1706 • 2010

1701

ARTICLE

and deposition of TiO2 NPs were analyzed by XPS. Antibacterial activity of PES fabrics was tested on Gram-negative bacterium E. coli. The UV blocking ability was evaluated by determining the UV protection factor (UPF). The photocatalytic activity of TiO2 NPs deposited onto the PES fabrics was followed by decoloration of blueberry juice stains and methylene blue in aqueous solution under UV illumination.

ARTICLE

Table 1. Elemental Composition of the UPES, O2PES, and ArPES Fibers

FIGURE 1. SEM images of (a) UPES, (b) O2PES, and (c) ArPES fibers.

concentration was calculated on the basis of spectrophotometric measurements at 664 nm.

3. RESULTS AND DISCUSSION Plasma-induced morphological changes of PES fibers were analyzed by SEM. SEM images of untreated (UPES), O2 plasma-treated (O2PES), and Ar plasma-treated (ArPES) PES fibers are shown in Figure 1. Figure 1a reveals relatively smooth surface of the UPES fiber. Few striations are visible on the surface of the UPES fiber. Although O2 plasma treatment led to a formation of small pits and striations (Figure 1b), no significant morphological changes compared to UPES fiber can be observed. On the contrary, Ar plasma produced widened, less-uniform striations (Figure 1c). Additionally, it seems that redeposition of material that was already sputtered from the PES fiber surface during plasma 1702

VOL. 2 • NO. 6 • 1700–1706 • 2010

sample

C (at %)

O (at %)

O/C

UPES O2PES ArPES

80.6 74.1 78.0

19.4 25.9 22.0

0.24 0.35 0.28

processing occurred. Figure 1c indicates that particularly Ar plasma promoted the increase in fiber surface roughness and consequently, the specific surface area. The topographical changes are due to severe bombardment of PES fibers with energetic plasma particles. It is expected that Ar particles are primarily sputtering the surface away and hence, they induced greater topographical changes. Oxygen particles, however, participate in the chemical etching perhaps supported by ion bombardment, making the fiber surface more even. In addition to morphological properties, plasma action considerably affected the chemical composition of the PES fiber surface. The atomic compositions of PES fibers before and after plasma treatment analyzed by XPS are presented in Table 1. It is noticeable that both O2 and Ar plasma treatments induced the increase in oxygen content and decrease in carbon content on the PES fiber surface. However, the contribution of O2 plasma in the generation of oxygen-containing functionalities was more prominent. The O/C atomic ratio that was calculated on the basis of XPS peak intensities, increased by 46% after O2 plasma treatment and 17% after Ar plasma treatment. Namely, during the O2 plasma treatment, different plasma species (ions, UV photons and particularly atomic oxygen) may create radicals on the PES fiber surface through polymer scission or hydrogen abstraction (37). The abundance of highly reactive oxygen species in O2 discharge makes possible rapid reactions with generated radicals on the PES fiber surface and formation of polar oxygen-containing functional groups. The formation of new oxygen-containing functionalities on the PES fiber surface in Ar plasma was facilitated by the traces of O2/air in discharge. Even at low concentrations, oxygen is extremely reactive and high rate of its dissociation can be expected. However, Ar ions and UV photons are supposed to be the most responsible for the creation of radicals on the polymer surface (38, 39). In addition to oxygen species in discharge, generated radicals may also react with radicals in neighboring polymer chains, causing the formation of oxidized cross-linked structures on the PES fiber surface. It was suggested that cross-linking reactions obstruct the incorporation of oxygen groups (38, 39) and that can also explain lower content of oxygen on the surface of the Ar plasma treated PES fibers (Table 1). Independently of the applied gas, some of the created radicals also take part in postplasma chemical reactions with the species from surrounding environment. Hence, lower content of oxygen on the surface of the Ar plasma-treated PES fibers can also be due to weaker generation of radicals that further react with atmospheric species. Deconvolution of high-resolution C1s spectra provided more information on the content of exact oxygen-containing Mihailovic´ et al.

www.acsami.org

Table 3. Elemental Composition of the UPES, O2PES, and ArPES Fibers Loaded with TiO2NPs

Table 2. Relative Intensity Data of Deconvoluted C1s Spectra atomic ratio (%) sample

C-C, C-H 285.0 eV

C-O 286.6 eV

CdO 288.3 eV

O-CdO 289.1 eV

UPES O2PES ArPES

77.4 63.6 70.4

13.1 21.0 14.2

0.0 8.3 10.3

9.5 7.1 5.1

groups incorporated on the PES fiber surface during the O2 and Ar plasma treatments. Figure 2 shows the C1s spectra of the UPES, O2PES and ArPES fibers. The results presented in Table 2 demonstrate that C1s signal of the UPES fibers consists of three peaks at binding energies at 285.0, 286.6, and 289.1 eV, corresponding to carbon atoms in aromatic ring (C-C, C-H), methylene carbons singly bound to oxygen (C-O) and ester carbon atoms (O-CdO), respectively (38-40). In the C1s spectrum of the O2PES and ArPES fibers additional peak at 288.3 eV related to carbonyl (CdO) group appeared. This observation is in line with literature findings (41). It is also evident that plasma treatment, independently of applied gas, caused the decrease in the percentage of C-C, C-H, and O-CdO groups, and increase in the percentage of C-O groups. The results suggest that newly formed C-O groups and CdO groups are generated at the expense of C-C, C-H, and O-CdO groups (42). The wetting of PES fabrics was also a sensitive indicator of plasma-induced surface modification. The wetting time of the UPES was 208 s while the O2PES and ArPES fabrics were wetted within a second. As expected, the wetting time of plasma treated fabrics was significantly shorter. This can be attributed to increased hydrophilicity of plasma treated PES fibers, i.e., implementation of new CdO and C-O groups as well as the presence of considerable amount of O-CdO groups on the PES fibers surface. Improvement of hydrophilicity along with increased surface roughness made the PES fibers more accessible to hydrophilic colloidal TiO2 NPs. The effect of plasma action on the deposition of TiO2 NPs onto PES fabrics was evaluated by XPS. The results of XPS elemental analysis for the www.acsami.org

C (at %)

O (at %)

Ti (at %)

UPES+TiO2 O2PES+TiO2 ArPES+TiO2

79.0 59.0 56.8

19.7 31.9 37.1

1.3 9.1 6.1

untreated (UPES+TiO2), O2 plasma treated (O2PES+TiO2) and Ar plasma-treated (ArPES+TiO2) PES fibers loaded with TiO2 NPs are given in Table 3. The high-resolution XPS spectra of Ti2p photoelectron peaks for the UPES+TiO2, O2PES+TiO2, and ArPES+TiO2 fibers are shown in Figure 3. The Ti2p1/2 and Ti2p3/2 spin-orbital splitting electrons are located at binding energies of 464.2 and 458.6 eV, respectively. The Ti content on the surface of the O2PES+TiO2 and ArPES+TiO2 fibers was 7 and 4.7 times higher compared to UPES+TiO2 fabric. It is interesting to note that air plasma treated PES fabrics examined in our previous work, contained almost equal amount of Ti (8.9%) than the O2PES+ TiO2 fabric (9.1%) (43). O1s high-resolution spectra of the UPES+TiO2, O2PES+ TiO2 and ArPES+TiO2 fibers are presented in Figure 4. The results in Table 4 demonstrate that O1s signal contain three peaks corresponding to TiO2 (529.8 eV), CdO (531.6 eV), and C-O (532.9 eV). The existence of the peak at 529.8 eV clearly confirms the presence of TiO2 NPs on the surface of both PES fibers. Overall XPS results proved that plasma activation of the PES fibers surface positively affected the deposition of TiO2 NPs. The antibacterial activity of the UPES+TiO2, O2PES+TiO2 and ArPES+TiO2 was examined against Gram-negative bacterium E. coli. The results of bacteria reduction are presented in Table 5. The control UPES fabric provided bacterial reduction of approximately 1 order of magnitude due to adsorption of E. coli on the PES fabric surface (44). The UPES+TiO2 fabric did not reach the desired level of antibacterial efficiency (R ) 99.9%), because the number of bacterial colonies decreased only by 1 order of magnitude compared to control UPES fabric. On the contrary, O2PES+

FIGURE 3. High-resolution spectra of Ti2p photoelectron peaks for the UPES+TiO2, O2PES+TiO2, and ArPES+TiO2 fibers. VOL. 2 • NO. 6 • 1700–1706 • 2010

1703

ARTICLE

FIGURE 2. High-resolution spectra of C1 photoelectron peaks for the UPES, O2PES, and ArPES fibers.

sample

ARTICLE

Table 6. UPF Values of PES Fabric Loaded with TiO2 NPs

FIGURE 4. High-resolution O1s spectra of the UPES+TiO2,O2PES+TiO2 and ArPES+TiO2 fibers.

Table 4. Relative Intensity Data of the Deconvoluted O1s Spectra of the UPES+TiO2, O2PES+TiO2, and ArPES+TiO2 Fibers atomic ratio (%) sample

TiO2 529.8 eV

CdO 531.6 eV

C-O 532.9 eV

UPES+TiO2 O2PES+TiO2 ArPES+TiO2

18.6 70.4 42.0

36.9 13.8 35.8

44.5 15.8 22.2

Table 5. Antibacterial Efficiency of PES Fabrics Loaded with TiO2 NPs

sample UPES UPES+TiO2 UPES O2PES+TiO2 UPES ArPES+TiO2 UPES O2PES+TiO2 UPES ArPES+TiO2

initial number of bacterial colonies (CFU)

no. of bacterial colonies (CFU)

3.7 × 105 4.2 × 105 3.6 × 105 After washing 4.2 × 105 6.5 × 105

1.5 × 105 1.3 × 104 9.0 × 104