Incorporation of Cadmium and Nickel into Ferrite Spinel Solid Solution

Dec 19, 2017 - A feasible treatment technique based on the investigated mechanism of CNF formation was developed, involving thermal treatment of waste...
3 downloads 13 Views 2MB Size
Subscriber access provided by UNIV OF NEW ENGLAND ARMIDALE

Article

Incorporation of Cadmium and Nickel into Ferrite Spinel Solid Solution: XRD and EXAFS Study Minhua Su, Changzhong Liao, Ting-Shan Chan, Kaimin Shih, Tangfu Xiao, Diyun Chen, Lingjun Kong, and Gang Song Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b04350 • Publication Date (Web): 19 Dec 2017 Downloaded from http://pubs.acs.org on December 19, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 31

Environmental Science & Technology

TOC ART

ACS Paragon Plus Environment

Environmental Science & Technology

Page 2 of 31

1

Incorporation of Cadmium and Nickel into Ferrite Spinel Solid Solution: XRD

2

and EXAFS Study

3

Minhua Su a, c, Changzhong Liao b, c, Tingshan Chan d, Kaimin Shih c*, Tangfu Xiao e, Diyun Chen a*,

4

Lingjun Kong a, c, Gang Song a

5

a

6 7

Guangdong Provincial Key Laboratory of Radionuclides Pollution Control and Resources, School of Environmental Science and Engineering, Guangzhou University, Guangzhou 510006, China

b

Guangdong Key Laboratory of Integrated Agro-environmental Pollution Control and Management,

8

Guangdong Institute of Eco-environmental Science & Technology, Guangzhou, 510650, China

9

c

Department of Civil Engineering, The University of Hong Kong, Pokfulam Road, Hong Kong,

10

Hong Kong SAR, China d

11

National Synchrotron Radiation Research Center, Hsinchu Science Park, Hsinchu, Taiwan

12

e

13

Education, School of Environmental Science and Engineering, Guangzhou University, Guangzhou,

14

510006, China

Key Laboratory for Water Quality Security and Conservation of the Pearl River Delta, Ministry of

15 16 17 18 19 20 21 22 1/30

ACS Paragon Plus Environment

Page 3 of 31

Environmental Science & Technology

23

ABSTRACT: The feasibility of incorporating Cd and Ni in hematite was studied by investigating

24

the interaction mechanism for the formation of CdxNi1−xFe2O4 solid solutions (CNFs) from CdO,

25

NiO, and α-Fe2O3. XRD results showed that the CNFs crystallized into spinel structures with

26

increasing lattice parameters as the Cd content in the precursors was increased. Cd2+ ions were found

27

to occupy the tetrahedral sites, as evidenced by Rietveld refinement and EXAFS analyses. The

28

incorporation of Cd and Ni into ferrite spinel solid solution strongly relied on the processing

29

parameters. The incorporation of Cd and Ni into the CNFs was greater at high x values (0.7 < x ≤ 1.0)

30

than at low x values (0.0 ≤ x ≤ 0.7). A feasible treatment technique based on the investigated

31

mechanism of CNF formation was developed, involving thermal treatment of waste sludge

32

containing Cd and Ni. Both of these metals in the waste sludge were successfully incorporated into a

33

ferrite spinel solid solution, and the concentrations of leached Cd and Ni from this solid solution

34

were substantially reduced, stabilizing at low levels. This research offers a highly promising

35

approach for treating the Cd and Ni content frequently encountered in electronic waste and its

36

treatment residues.

37 38 39 40 41 42 43 2/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 4 of 31

44



45

Due to rapid advances in technology, the demand for electronic devices is growing significantly.1-3

46

Ni-Cd batteries, as portable power sources, are widely utilized in cordless electric utensils, cordless

47

telephones, airplane engine starters, electric and hybrid electric vehicles, and communicational

48

distribution systems.4-6 At the end-of-life of these products, numerous spent Ni-Cd batteries are

49

generated, most of which are disposed of directly.2, 4, 7 This causes severe environmental pollution

50

because of both the large quantity of these batteries and their high contents of Cd and Ni.8-10 Most

51

compounds of Cd and Ni are highly toxic, and the release of these metals into the environment poses

52

extreme risks to human health and the ecosystem. In view of the toxicological significance of Cd and

53

Ni, special care in the disposal of Ni-Cd batteries is now mandatory in many places.11 However,

54

conventional techniques, including pyrometallurgical and hydrometallurgical process, often fail to

55

satisfy the increasingly stringent standards.9,

56

friendly technologies to effectively control and eliminate the release of Cd and Ni from this type of

57

electronic waste and its treatment residues is of great importance.

INTRODUCTION

12

Developing novel, reliable, and environmentally

58 59

Recent research has demonstrated a promising strategy to effectively and reliably convert

60

metal-containing wastes into a variety of robust crystalline products.13, 14 The incorporation of these

61

waste-borne metals into widely available ceramic matrices (e.g., alumina, hematite, and kaolinite,

62

etc.) under thermal treatment has been studied mechanistically.13-16 The metal leachability of the

63

stabilized products can be substantially reduced, achieving the detoxification of hazardous metals in

64

the waste stream. This is mainly attributed to the irreversible crystallographic transformation 3/30

ACS Paragon Plus Environment

Page 5 of 31

Environmental Science & Technology

65

occurring in the mineral phases during the sintering process. Cd-Ni ferrite solid solutions have a

66

wide variety of applications in industry and their properties and synthesis have attracted strong

67

interest.17, 18 For instance, in one study, Cd-Ni ferrite solid solutions were synthesized through a

68

typical ceramic manufacturing process involving the sintering of finely milled oxides in compacted

69

forms at high temperatures.19 Other processes, such as double sintering and co-precipitation, are also

70

commonly used in the fabrication of ferrite solid solutions.20, 21 These methods offer a technically

71

feasible approach to incorporating Cd and Ni into a Fe-rich precursor under thermal conditions.

72 73

Owing to its relatively low cost and wide availability, hematite (α-Fe2O3) is known as a feasible

74

matrix for the immobilization of various hazardous metals in waste.17, 22, 23 In this work, α-Fe2O3 was

75

used to incorporate Cd and Ni into spinel structures. The incorporation reaction pathways through

76

the sintering of CdO + NiO + α-Fe2O3 mixtures at various temperatures were studied by X-ray

77

diffraction (XRD) and extended X-ray absorption fine structure (EXAFS) techniques in detail. The

78

incorporation parameters (i.e., sintering temperature and time) for the formation of CdxNi1−xFe2O4

79

spinel solid solutions were systematically investigated, and were then used to optimize the

80

processing parameters for stabilizing waste sludge containing Cd and Ni. Furthermore, the chemical

81

durability of ferrite spinel solid solutions should be evaluated via leaching experiments under acidic

82

conditions (e.g., pH 4.0) to reflect the metal stabilization effect. Constant-pH leaching tests (CPLTs)

83

can avoid the change of leaching behavior due to the corresponding change of leaching solution pH

84

and were adopted to evaluate the metal stabilization effects of the final products.

85 4/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 6 of 31

86



87

Materials and Sample Preparation. A series of experiments was designed and performed to probe

88

the optimal conditions for Cd and Ni to be incorporated by hematite (α-Fe2O3). The optimum

89

processing parameters, i.e., sintering temperature and time, for preparing the single-phase

90

CdxNi1−xFe2O4 solid solution samples (CNFs) were systematically investigated. The as-received

91

cadmium oxide (CdO, Fisher Scientific), nickel oxide (NiO, Fisher Scientific), and hematite

92

(α-Fe2O3, Sigma-Aldrich) were used as the reaction precursors. All of the precursor materials were

93

of analytical grade, and used without further purification. The mineralogical compositions of these

94

materials were confirmed by X-ray diffraction (XRD), as shown in the Supporting Information

95

Figure S1. The reaction precursors (i.e., CdO, NiO, and α-Fe2O3) were mixed by ball-milling for 1.0

96

h with different stoichiometric molar ratios of Cd/Ni. The ball milling was conducted in a planetary

97

ball mill consisting of four tungsten carbide grinding jars (100 mL each) at a rotation speed of 500

98

rpm. Sequentially, the mixtures were dried in a vacuum oven at 105 °C for 24 h, and then further

99

homogenized by extended mortar grinding for 10 min in an agate mortar. Before thermal treatment,

100

the dried mixtures were compacted into 20-mm-diameter circular pellets under an axial pressure of

101

250 MPa. For the incorporation reaction, a well-control thermal treatment scheme at the targeted

102

temperature was applied. In most cases, the dwell time was fixed at 3 h for sintering temperatures

103

ranging from 700 to 950 °C. CdxNi1−xFe2O4 solid solutions with x values of 0.0, 0.1, 0.3, 0.5, 0.7, 0.9,

104

and 1.0 were then prepared by sintering.

EXPERIMENTAL SECTION

105

5/30

ACS Paragon Plus Environment

Page 7 of 31

Environmental Science & Technology

106

XRD Analysis. After cooling to room temperature, the sintered pellets were ground into fine

107

powders for phase transformation analysis by XRD. The step-scanned XRD pattern of each powder

108

sample was recorded at room temperature by a Bruker D8 Advance X-ray powder diffractometer

109

equipped with Cu Kα1,2 X-ray radiation (λ = 1.54059 Å) and a LynxEye detector. The scanning angle

110

2θ ranged from 20° to 120° with a step size of 0.02° and a scanning speed of 0.5 s per step. Phase

111

identification was executed by matching the experimental XRD patterns with those retrieved from

112

the standard powder diffraction database of the International Centre for Diffraction Data (ICDD,

113

PDF-2 Release 2008). The Rietveld refinement of the crystal structures was performed via the

114

TOPAS V4.0 program (Bruker AXS, Karlsruhe).

115 116

EXAFS Measurements and Analysis. The Cd K-edge extended X-ray absorption fine structure

117

(EXAFS) spectra of the CNFs were collected at Beam Line 01C at the National Synchrotron

118

Radiation Research Center (NSRRC) of Taiwan, with the storage ring operated at 1.5 GeV and 300

119

mA. The EXAFS spectra were recorded in transmission mode, with all ion chambers filled with

120

argon. The EXAFS data were analyzed using Athena and Artemis software.24

121 122

Characterization and Treatment of SNCB Sludge. Waste sludge enriched in Cd and Ni was

123

collected from spent Ni-Cd batteries (SNCBs) dried at 105 °C for 24 h in a vacuum oven (the

124

resulting sample being denoted SNCBS-105). Ball milling was carried out to homogenize

125

SNCBS-105 for sample analysis and immobilization. The mineral phases of SNCBS-105 were

126

identified by XRD (Figure S2). Graphite (C, ICDD PDF No. 26-1079), cadmium hydroxide 6/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 8 of 31

127

(Cd(OH)2, ICCD PDF No. 71-2137), and theophrastite (Ni(OH)2, ICCD PDF No. 73-1520) were the

128

major crystalline phases identified. SNCBS-105 was further calcined at 600 °C for 12 h to achieve

129

decarbonization (removal of graphite),25, 26 and the resulting sample was denoted SNCBS-600. In

130

SNCBS-600, only cadmium oxide (CdO, ICDD PDF No. 75-0594) and nickel oxide (NiO, ICDD

131

PDF No. 89-5881) were detected by XRD. The elemental composition of SNCBS-600 was probed

132

by scanning electron microscopy–energy-dispersive X-ray spectroscopy (SEM-EDX) (Hitachi S4800

133

FEG SEM) and by inductively coupled plasma–optical emission spectrometry (ICP-OES) (ICP-OES

134

800, Perkin Elmer) through the digestion method using aqua regia. The EDX results are summarized

135

in Figure S3. In the digestion method, 20 mL aqua regia was slowly added into 1 g of SNCBS-600

136

powder, boiled for 1 h, cooled, and diluted with doubly distilled deionized water, and the metal

137

concentrations were then measured by an ICP-OES 800 (Perkin Elmer). Cd and Ni were found to be

138

the two major elements in SNCBS-600, and the molar ratio of Cd/Ni was about 1.1. To immobilize

139

the Cd and Ni in SNCBS-600, mixtures of SNCBS-600 and hematite with a Cd/Fe molar ratio of

140

~1:3 (with excess hematite available for Cd and Ni incorporation) were prepared. The treatment for

141

SNCBs was conducted via an identical homogenization and palletization process as for the CNFs.

142

The final products after sintering were subjected to CPLT to evaluate the stabilization of Cd and Ni

143

in the CNF solid solutions, compared with the untreated SNCBS-600.

144 145

Constant-pH Leaching Test (CPLT). The leachability of single-phase Cd-bearing samples (i.e.,

146

CdO, CdFe2O4, and CdxNi1−xFe2O4), Ni-bearing samples (i.e., NiO and NiFe2O4), the SNCBS-600

147

sintered product, and the untreated SNCBS-600 sample was assessed by the constant-pH leaching 7/30

ACS Paragon Plus Environment

Page 9 of 31

Environmental Science & Technology

148

test (CPLT) method with a leaching fluid of pH 4.0 HNO3 solution.27 During the leaching process,

149

the pH value was continually monitored by a pH meter and kept at 4.0 ± 0.1 by adding 1 M HNO3

150

aqueous solution in volumes ranging from 10 to 20 µL for each adjustment. The CPLT was

151

performed the controlled room temperature (i.e., 25 ± 1 °C), using 500 mL of leaching fluid and 0.5

152

g of powders with mechanical stirring throughout each test. At 10 min intervals, 5 mL leachate

153

together with suspended solids was sampled and filtered through a 0.2 µm syringe filter. The leached

154

metal concentrations were determined by an ICP-OES 800 (Perkin Elmer) with a calibration range of

155

10–2000 ppb (R2 > 0.9995).

156 157



158

Formation of CdxNi1−xFe2O4 Spinel Solid Solutions. As the composition of metals in waste

159

streams can fluctuate, the relative incorporation of Cd and Ni depends critically on the Cd/Ni molar

160

ratio. Previous experiments performed at temperatures of 700-950 °C showed that 950 °C was a

161

preferred temperature for Cd and Ni incorporation, and the observed weight loss of CdO was

162

insignificant. Figure 1(a) depicts the XRD patterns of the samples sintered at 950 °C for 3 h. The

163

predominant product phase in the sintered samples of CdO + NiO + α-Fe2O3 exhibited characteristic

164

Bragg reflections of the Fd-3m cubic spinel group. Both Cd and Ni were able to be

165

crystallographically incorporated into the Cd-Ni ferrite spinel solid solutions after thermally reacting

166

with hematite. No other oxidation state of Cd during the incorporation process was observed. As the

167

proportion of Ni increased (Figure 1(a)), the diffraction signals of residual reactants (i.e., NiO and

168

α-Fe2O3) became more intense in the sintered samples. This implied different incorporation abilities

RESULTS AND DISCUSSION

8/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 31

169

of Cd and Ni, which might have been due to the difference in the required activation energies. With a

170

greater amount of Ni, a higher energy input was required to overcome the high activation barrier for

171

the formation of the final products.28 For a solid-state reaction, the driving force for mass transfer is

172

related to the difference in chemical potential, and therefore Gibbs free energy, between the reactants

173

and products.29 The standard Gibbs free energy of formation for CdFe2O4 is greater than that of

174

NiFe2O4 by +6.98 kJ/mol (Text S2),30, 31 indicating that the reaction between CdO and α-Fe2O3 is

175

energetically favored over that between NiO and α-Fe2O3 in spinel structure formation. Therefore, at

176

a sintering temperature of 950 °C, Cd had a much greater affinity for incorporation into spinel than

177

did Ni.

178 179

Given optimized processing parameters, thermal treatment schemes can achieve complete phase

180

transformation in solid-state reactions. Elevating the sintering temperature can stimulate the

181

incorporation reaction, and intensive grinding together with an extended sintering time can enhance

182

the homogeneity and crystallinity of the products.28, 29, 32 Thus, we performed a multi-stage sintering

183

process in an effort to achieve the full incorporation of Cd and Ni into the Cd-Ni ferrite spinel solid

184

solutions. The multi-stage sintering process included homogenization, grinding, drying, pelletizing,

185

and multi-stage heat treatment. The heat treatment consisted of the following stages: first round,

186

sintering at 950 °C for 3 h; second round, sintering at 975 °C for 12 h; third and fourth rounds, both

187

sintering at 1000 °C for 12 h. For each sample, the fired pellet was ground into powder and then

188

re-pelletized at 250 MPa for the next cycle of sintering. All of the final products obtained by

189

sintering the CdxNi1−xFe2O4 (0 ≤ x ≤ 1) samples were identified as single-phase Cd-Ni ferrite spinel 9/30

ACS Paragon Plus Environment

Page 11 of 31

Environmental Science & Technology

190

solid solutions, as inferred from their XRD patterns’ containing no secondary crystalline phases

191

(Figure 2(a)). Thus, a series of CdxNi1−xFe2O4 spinel solid solutions was successfully produced. The

192

overall reaction is expressed in Eq. 1. The formation reactions for the CdFe2O4 and NiFe2O4 phases

193

are given in Eqs. 2 and 3, respectively.

194 195

xCdO + (1-x)NiO + α-Fe2O3 (hematite) → CdxNi1-xFe2O4

(1)

196

CdO + α-Fe2O3 (hematite) → CdFe2O4

(2)

197

NiO + α-Fe2O3 (hematite) → NiFe2O4

(3)

198 199

As shown in Figure 2(a), the diffraction peaks of the single-phase CNFs were shifted toward lower

200

2θ values as x was increased from 0.0 to 1.0. This indicates that the lattice parameters increased as

201

the Cd content was increased and the Ni content was decreased. Rietveld refinement allowed

202

accurate determination of the lattice parameters of the CNFs, as given in Figure 2(b). The lattice

203

parameters measured here were in good agreement with those found in previous studies.17, 33 The

204

increase of the lattice parameter from 8.3420(3) Å to 8.7072(1) Å (Table S1) as x increased from 0.0

205

to 1.0 in CdxNi1−xFe2O4 corresponds well with Vegard’s law.34 Linear fitting of the data generated

206

the following relationship between the lattice parameter (y) and the x value: y = 0.36513x + 8.3439

207

(R2 = 0.9996). The crystal radius of Cd (r (Cd2+) = 0.97 Å) is larger than that of Ni (r (Ni2+) = 0.72 Å)

208

in the CdxNi1-xFe2O4 solid solution structure.35 This was the cause of the increasing lattice

209

parameters of the products with higher loading of Cd, as observed in Figure 2(b). Therefore, the

10/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 12 of 31

210

sintered products can be expected to expand when both Cd and Ni are fully incorporated into the

211

CNFs.

212 213

To reveal the formation mechanism of these CNFs, it is important to determine which sites are

214

occupied by the cations. EXAFS spectroscopy can offer the structural information of many elements,

215

including bond distances and coordination numbers at molecular level.36-37 Figure 3 shows the fitting

216

results of the EXAFS data acquired at the Cd K-edge of three CdxNi1−xFe2O4 samples (x = 0.5, 0.9,

217

and 1.0), all of which are closely consistent with the spinel structure. In general, the octahedral

218

environments in spinel structures contain three major Fourier peaks (at ~2 Å, ~3 Å, and ~3.5 Å),

219

while only two peaks (at ~ 2 Å and ~ 3.5 Å) appear for the tetrahedral environments.38 The absence

220

of peaks at 3.0 Å in all of the Fourier forms of the EXAFS spectra for CdxNi1−xFe2O4 (x = 0.5, 0.9,

221

and 1.0) indicates that the Cd2+ ions exclusively occupied the tetrahedral sites (8a sites). Furthermore,

222

we note that NiFe2O4 is an inverse spinel in which all of the Ni2+ ions occupy the octahedral sites.

223

Therefore, the most reasonable basis for Rietveld refinement was to assume that all Ni2+ occupied

224

octahedral sites while all Cd2+ occupied tetrahedral sites. During the Rietveld analysis, an attempt to

225

allocate Cd atoms into octahedral sites was also conducted, but not surprisingly this obtained a very

226

low level of occupancy. The profiles calculated on the assumption that Cd2+ ions occupy 8a sites and

227

Ni2+ ions occupy 16d sites (Tables S2–6) agreed very closely with the experimental data (Tables S2–

228

6 and Figures S4–8).

229

11/30

ACS Paragon Plus Environment

Page 13 of 31

Environmental Science & Technology

230

Leachability of CdxNi1−xFe2O4 Spinel Solid Solutions. To verify the stabilization of Cd and Ni

231

after the formation of the CNFs, the inherent leachability of CdxNi1−xFe2O4 was assessed by CPLT at

232

pH 4.0. For comparison, the as-received CdO and NiO, and samples of CdFe2O4 spinel and NiFe2O4

233

spinel synthesized in-house, were also tested by CPLT under the same acidic condition (pH = 4.0).

234

All of the leaching samples were ball-milled into powder. The congruent dissolution of CdO,

235

CdFe2O4, NiFe2O4, and CdxNi1−xFe2O4 in an acidic aqueous solution can be described as:

236 237

CdO + 2H  → Cd   + H O

238



CdFe O + 8H  → Cd   + 2Fe  + 4H O

239



NiFe O + 8H  → Ni  + 2Fe   + 4H O

240

 

Cd Ni Fe O + 8H  → xCd   + 1 − xNi  + 2Fe  + 4H O

(4) (5) (6) (7)

241 242

Figure 4 shows the 120 min CPLT results of the tested phases. The leachates of CdO and NiO

243

contained very high concentrations of Cd and Ni, revealing that both oxides were highly vulnerable

244

to proton-mediated dissolution. In contrast, the levels of Cd leached from CdFe2O4 and Ni leached

245

from NiFe2O4 were observed to be very low. Furthermore, in the CdxNi1−xFe2O4 leachates, both the

246

Cd and Ni concentrations were much lower still than those in the CdFe2O4 or NiFe2O4 leachates. The

247

solid solutions with lower Cd and Ni loading produced leachates with substantially decreased

248

concentrations of those metals (Figure 4). It can be seen that the concentrations of Cd and Ni in the

249

CdxNi1−xFe2O4 leachates were three and two orders of magnitude smaller than those derived from

250

CdO and NiO, respectively. This indicates that the phase transformation of Cd and Ni into solid 12/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 14 of 31

251

solutions markedly reduced their leachability, suggesting a promising strategy for processing

252

industrial waste by adding sufficient Fe to stabilize their Cd and Ni content.

253 254

SNCB Waste Sludge. Cd-Ni-bearing waste sludge was collected from SNCBs. To fully remove

255

graphite, which can affect the stabilization process and the product texture, the SNCBS-105 sample

256

was further pretreated at 600 °C for 12 h. The elemental composition of SNCBS-600 was analyzed

257

by energy-dispersive X-ray spectroscopy (EDX) (Figure S3). The peaks in the spectrum

258

corresponded well to the characteristic signals of cadmium (Cd), nickel (Ni), cobalt (Co), sodium

259

(Na), and potassium (K). Both Na and K were from the alkaline electrolytes in the batteries. The Co

260

content was from an additive to improve the electrical conductivity of the electrodes. The metal

261

contents (i.e., Cd, Ni, Co, Na and K) in SNCBS-600 were quantified by acid digestion and ICP-OES.

262

Table S7 lists the weight percentages and the molar fractions of those five metals. The Ni (19.07 ±

263

1.05 wt.%) and Cd (40.13 ± 1.86 wt.%) contents were relatively high. The molar ratio of Cd/Ni was

264

around 1.1, just above the range of x values in the CdxNi1−xFe2O4 spinel solid solutions.

265 266

SNCB Sludge Stabilization. The successful production of acid-resistant CNFs enabled the design of

267

a stabilization strategy for Cd- and Ni-bearing waste. Figure 5(a) shows the XRD patterns of samples

268

of SNCBS-600 + hematite sintered for 3 h at temperatures ranging from 700 °C to 950 °C. The

269

incorporation reaction was initiated at 700 °C, as reflected by the characteristic Bragg reflection

270

positions corresponding to the typical ferrite spinel structure. As the sintering temperature increased,

271

the diffraction signals of CdO and NiO significantly declined, indicating that both Cd and Ni were 13/30

ACS Paragon Plus Environment

Page 15 of 31

Environmental Science & Technology

272

transformed into the new spinel phase. Upon further increasing the treatment temperature to 950 °C,

273

the ferrite spinel solid solution came to significantly dominate the final product composition. Eq. 8

274

describes the incorporation reaction.

275 276

SNCB Sludge + Hematite (α-Fe2O3) → Ferrite Spinel Solid Solution

(8)

277 278

Based on the results in Figure 5(a), the optimal temperature for the incorporation of Cd and Ni by

279

hematite is 950 °C. Repeated grinding and thermal treatment are known to assist the full

280

incorporation of metals. To assist the full incorporation of Cd and Ni by hematite, the sample of

281

SNCBS-600 + hematite fired for at 950 °C for 12 h was further subjected to additional grinding

282

followed by sintering at 1050 °C for 6 h. As observed from Figure 5(b), the resulting product

283

consisted mainly of the Cd-Ni-Fe spinel phase after this thermal treatment. The lattice parameter of

284

the Cd-Ni-Fe spinel was estimated to be 8.52175(1) Å, and was related to x by the relationship y =

285

0.36513x + 8.34392.

286 287

The stabilization of Cd and Ni in the CNF was evaluated by leaching the final sintered product

288

(obtained by heat treatment at 950 °C for 12 h followed by 1050 °C for 6 h) under CPLT conditions

289

at pH 4.0 for 120 min. During the CPLT, 13 aliquots were taken over the 120 min period, and three

290

independent replicates were conducted for each leaching experiment. The measured concentrations

291

of all of the metals (Cd, Ni, Co, K, Na, and Fe) in the leachates of the sintered SNCBS-600 +

292

hematite mixtures (a ferrite spinel solid solution) are shown in Figure 6. Compared with the 14/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 16 of 31

293

untreated SNCBS-600, the sintered sludge products exhibited a higher resistance to strong acid

294

attack. The leachability of the sintered product of SNCB-600 was slightly higher than those of the

295

CdxNi1−xFe2O4 samples prepared in this study. This was likely due to the surface area of the sintered

296

SNCBS-600 (7.39 m2/g) being greater than those of the CdxNi1−xFe2O4 samples (ranging from 1.78

297

to 1.96 m2/g) (Table S8). In addition to Cd and Ni, the Co and K concentrations in the leachates also

298

decreased significantly after sintering, potentially indicating the transformation of Co and K into

299

more stable crystal structures.39-40 K has been reported to strongly stabilize defect spinel structures

300

by a potassium-substituted magnetite oxidation process.39 Moreover, the KFe11O17 and NaFeO2

301

phases were formed herein after sintering (Figure 5). NaFeO2 is highly soluble in aqueous (Eq. 9) or

302

acidic media.42 The exchange of Na ions for protons might also have led to the leaching-out of Na

303

from the sintered product, causing the high Na concentration in the leachates. The substantial

304

reduction of the leaching of metals (e.g., Cd and Ni) from the waste sludge of the SNCBs after

305

sintering can be attributed to the successful formation of ferrite spinel solid solutions.

306 NaFeO2 + H2O → NaOH + Fe(OH)3

307

(9)

308 309



310

Wastes containing cadmium and nickel pose a severe threat to the environment. Stabilizing cadmium

311

and nickel by incorporating them into crystalline products is an effective approach to detoxify

312

hazardous wastes. In this study, a series of single-phase CdxNi1−xFe2O4 solid solutions was prepared,

313

and demonstrated considerable resistance to strong acid attack. Both Cd and Ni were incorporated

ENVIRONMENTAL IMPLICATIONS

15/30

ACS Paragon Plus Environment

Page 17 of 31

Environmental Science & Technology

314

in large quantities into the Cd-Ni ferrite spinel structure at 950 °C. The optimal experimental

315

parameters for the incorporation of Cd and Ni into ferrite spinel solid solutions via a solid-state

316

reaction were determined systematically, and the stability of these solutions in an acidic

317

environment was confirmed. The EXAFS results further revealed that Cd2+ ions occupied the

318

tetrahedral sites (8a sites) while Ni2+ occupied the octahedral sites (16d sites) in the CdxNi1−xFe2O4

319

solid solutions. This information provides an important basis for stabilizing waste bearing Cd and

320

Ni (e.g., SNCB sludge derived from spent Cd-Ni batteries) and a guide to the optimal use of the

321

final products. The major metals in the tested SNCB sludge were Cd, Ni, Co, K, and Na. The SNCB

322

sludge was further sintered with hematite to produce a spinel solid solution capable of incorporating

323

the hazardous metals Cd and Ni. The CPLT results showed a substantial reduction of the

324

leachability of hazardous metals in the final treated products, compared with the untreated SNCB

325

sludge.

326 327



328

Supporting Information. Seven tables and nine figures report the surface area of the samples used for

329

CPLT, the metal contents of SNCBS-600, the diffraction patterns and electron micrographs of the

330

used chemicals and sintered products, and the Rietveld refinement results of the CdxNi1−xFe2O4

331

samples. Two method descriptions are given, providing the standard Gibbs free energy of cadmium

332

ferrite and nickel ferrite.

ASSOCIATED CONTENT

333 334 16/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 18 of 31

335



336

This work was supported by the Research Grants Council of Hong Kong (17212015, 17257616,

337

C7044-14G, and T21-771/16R), National Natural Science Foundations of China (51708143,

338

41372364, U1501231, U1612442), the Project of Radioactive Pollution Control and Resource Reuse

339

Key Laboratory (2012A061400023), and Guangzhou University's Training Program for Excellent

340

New-recruited Doctors (YB201710), High Level University Construction Project (Regional Water

341

Environment Safety and Water Ecological Protection), GDAS' Special Project of Science and

342

Technology Development (2017GDASCX-0834). Use of facilities from the National Synchrotron

343

Radiation Research Center (NSRRC) of Taiwan is gratefully acknowledged.

ACKNOWLEDGMENTS

344 345

Competing financial interests

346

The authors declare no competing financial interests.

347 348

References

349

1.

350

and electronic equipment in China: A review. Waste Manage. Res. 2014, 32(4), 254-269; DOI

351

10.1177/0734242X14525824.

352

2.

353

mechanical treatment. Waste Manage. 2011, 31(6) 1292-1299; DOI 10.1016/j.wasman.2011.01.006.

354

3.

355

developing countries. Waste Manage. Res. 2007, 25(6) 489-501; DOI 10.1177/0734242X07082028.

He, Y.; Xu, Z. The status and development of treatment techniques of typical waste electrical

Huang, K.; Li, J.; Xu, Z. Enhancement of the recycling of waste Ni-Cd and Ni-MH batteries by

Osibanjo, O.; Nnorom, I. The challenge of electronic waste (E-waste) management in

17/30

ACS Paragon Plus Environment

Page 19 of 31

Environmental Science & Technology

356

4.

Pistoia, G.; Wiaux, J.-P.; Wolsky, S. Used battery collection and recycling; Elsevier Science,

357

2001.

358

5.

359

from sulfate solutions of spent nickel–cadmium batteries using mixtures of D2EHPA and Cyanex

360

302. J. Power Sources 2014, 247(0) 127-133; DOI http://dx.doi.org/10.1016/j.jpowsour.2013.08.063.

361

6.

362

needs (ANL/ESD/10-7). Argonne National Laboratory, 2010.

363

7.

364

Innovation and Skills (BIS), London, U.K., 2014;

365

www.gov.uk/government/uploads/system/uploads/attachment_data/file/341262/bis_14_989_Amende

366

d_Batteries_Directive_3.pdf

367

8.

368

processes

369

10.1016/j.jpowsour.2003.12.026.

370

9.

371

batteries for the preparation of C/Ni and C/Ni/Pd layered electrodes for energy sources. Process Saf.

372

Environ 2015, 93, 139-146; DOI https://doi.org/10.1016/j.psep.2014.02.007.

373

10. Rogulski, Z.; Czerwiński, A. Used batteries collection and recycling in Poland. J. Power Sources

374

2006, 159 (1), 454-458; DOI 10.1016/j.jpowsour.2006.02.034.

375

11. Plachy, J. Cadmium recycling in the United States in 2000; U.S. Geological Survey:  Reston,

376

VA, 2003.

Babakhani, A.; Rashchi, F.; Zakeri, A.; Vahidi, E. Selective separation of nickel and cadmium

Sullivan, J. L.; Gaines, L. A review of battery life-cycle analysis: State of knowledge and critical

Implementation of the amended batteries directive 2013/56/EU; Department for Business,

Bernardes, A.; Espinosa, D. C. R.; Tenório, J. S. Recycling of batteries: A review of current and

technologies.

J.

Power

Sources

2004,

130

(1-2),

291-298;

DOI

Skowroński, J. M.; Rozmanowski, T.; Osińska, M. Reuse of nickel recovered from spent Ni-Cd

18/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 20 of 31

377

12. Santos, V. E. O.; Celante, V. G.; Lelis, M. F. F.; Freitas, M. B. J. G. Chemical and

378

electrochemical recycling of the nickel, cobalt, zinc and manganese from the positives electrodes of

379

spent Ni-MH batteries from mobile phones. J. Power Sources 2012, 218 (12), 435-444; DOI

380

https://doi.org/10.1016/j.jpowsour.2012.07.024.

381

13. Shih, K.; White, T.; Leckie, J. O. Spinel formation for stabilizing simulated nickel-laden sludge

382

with aluminum-rich ceramic precursors. Environ. Sci. Technol. 2006, 40 (16), 5077-5083; DOI

383

10.1021/es052324z.

384

14. Shih, K.; White, T.; Leckie, J. O. Nickel stabilization efficiency of aluminate and ferrite spinels

385

and their leaching behavior. Environ. Sci. Technol. 2006, 40 (17), 5520-5526; DOI

386

10.1021/es0601033.

387

15. Tang, Y. Shih, K. Wang, Y. Chong, T. C. Zinc stabilization efficiency of aluminate spinel

388

structure and its leaching behavior. Environ. Sci. Technol. 2011 45 (24), 10544-10550; DOI

389

10.1021/es201660t.

390

16. Lu, X.; Shih, K. Phase transformation and its role in stabilizing simulated lead-laden sludge in

391

aluminum-rich

392

https://doi.org/10.1016/j.watres.2011.07.015.

393

17. Nikumbh, A.; Nagawade, A.; Gugale, G.; Chaskar, M.; Bakare, P. The formation, structural,

394

electrical, magnetic and Mössbauer properties of ferrispinels, Cd1−xNixFe2O4. J. Mater. Sci. 2002, 37

395

(3), 637-647; DOI https://doi.org/10.1023/A:1013790129045.

396

18. Belavi, P.; Naik, L. Structural and elastic properties of Cd1− xNixFe2O4 ferrites. In Physics of

397

Semiconductor Devices; Springer International Publishing: Switzerland, 2014; pp 659-662.

ceramics.

Water

Res.

2011,

45

(16),

5123-5129;

DOI

19/30

ACS Paragon Plus Environment

Page 21 of 31

Environmental Science & Technology

398

19. Mouallem-Bahout, M.; Bertrand, S.; Peña, O. Synthesis and characterization of Zn1−xNixFe2O4

399

spinels prepared by a citrate precursor. J. Solid State Chem. 2005, 178 (4), 1080-1086; DOI:

400

10.1016/j.jssc.2005.01.009.

401

20. Desai, R.; Mehta, R.; Upadhyay, R.; Gupta, A.; Praneet, A.; Rao, K. Bulk magnetic properties of

402

CdFe2O4

403

https://doi.org/10.1007/s12034-007-0035-4.

404

21. Gadkari, A.; Shinde, T.; Vasambekar, P. Influence of rare-earth ions on structural and magnetic

405

properties of CdFe2O4 ferrites. Rare Metals 2010, 29 (2) 168-173; DOI 10.1007/s12598-010-0029-z.

406

22. Cornell, R. M.; Schwertmann, U. The Iron Oxides: Structure, Properties, Reactions,

407

Occurrences and Uses, 2nd, ed.; Wiley-VCH Verlag GmbH & Co. KGaA, Germany, 2003.

408

23. Pappu, A.; Saxena, M.; Asolekar, S. R. Solid wastes generation in India and their recycling

409

potential

410

DOI :10.1016/j.buildenv.2006.04.015.

411

24. Ravel, B.; Newville, M. ATHENA, ARTEMIS, HEPHAESTUS: data analysis for X-ray

412

absorption spectroscopy using IFEFFIT. J. Synchrotron Radiat. 2005, 12 (4), 537-541; DOI

413

10.1107/S0909049505012719.

414

25. Contescu, C. I.; Azad, S.; Miller, D.; Lance, M. J.; Baker, F. S.; Burchell, T. D. Practical aspects

415

for characterizing air oxidation of graphite. J. Nucl. Mater. 2008, 381 (1-2) 15-24; DOI

416

10.1016/j.jnucmat.2008.07.020.

417

26. Luo, X.; Jean-Charles, R.; Yu, S. Effect of temperature on graphite oxidation behavior. Nucl.

418

Eng. Des. 2004, 227 (3), 273-280; DOI 10.1016/j.nucengdes.2003.11.004.

in

in

nano-regime.

building

Bull.

materials.

Mater.

Build.

Sci.

2007,

Environ.

30

2007,

(3),

42

197-203;

(6),

DOI

2311-2320;

20/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 22 of 31

419

27. Su, M.; Liao, C.; Chuang, K.-H.; Wey, M.-Y.; Shih, K. Cadmium stabilization efficiency and

420

leachability by CdAl4O7 monoclinic structure. Environ. Sci. Technol. 2015, 49 (24), 14452–14459;

421

DOI 10.1021/acs.est.5b02072.

422

28. Yang, S.; Kim, K.; Baek, J.-I.; Kim, J.-W.; Lee, J. B.; Ryu, C. K.; Lee, G. Spinel Ni(Al,Fe)2O4

423

solid solution as an oxygen carrier for chemical looping combustion. Energ. Fuel. 2012, 26 (7)

424

4617-4622; DOI dx.doi.org/10.1021/ef300712u.

425

29. Rahaman, M. N. Ceramic Processing and Sintering, 2nd ed.; Marcel Dekker, Inc.: New York,

426

2003.

427

30. Zhang, J.; Shi, J.; Gong, M. Synthesis of magnetic nickel spinel ferrite nanospheres by a reverse

428

emulsion-assisted hydrothermal process. J. Solid State Chem. 2009, 182 (8), 2135-2140; DOI

429

https://doi.org/10.1016/j.jssc.2009.05.032.

430

31. Knacke, O.; Zimmermann, E. Thermal dissociation of CdO and CdFe2O4. Z. Anorg. Allg. Chem.

431

1993, 619 (10), 1790-1792; DOI 10.1002/zaac.19936191027.

432

32. Awano, M.; Takagi, H.; Kuwahara, Y. Grinding effects on the synthesis and sintering of

433

cordierite. J. Am.Ceram. Soc. 1992, 75 (9), 2535-2540; DOI 10.1111/j.1151-2916.1992.tb05608.x.

434

33. Wolska, E.; Riedel, E.; Wolski, W. The evidence of Cd2+xFe3+1− x[Ni2+1− xFe3+1+x]O4 cation

435

distribution based on X-ray and Mössbauer data. Physica Status Solidi A 1992, 132 (1), K51-K56;

436

DOI 10.1002/pssa.2211320137.

437

34. Denton, A. R.; Ashcroft, N. W. Vegard’s law. Phys. Rev. A 1991, 43 (6), 3161-3164; DOI

438

10.1103/PhysRevA.43.3161.

439

35. Pauling, L. The Nature of The Chemical Bond. Cornell university press: New York, 1960. 21/30

ACS Paragon Plus Environment

Page 23 of 31

Environmental Science & Technology

440

36. Yu, S.; Wang, X.; Yang, S.; Sheng, G.; Alsaedi, A.; Hayat, T.; Wang, X. Interaction of

441

radionuclides with natural and manmade materials using XAFS technique. Sci. Chi. Chem. 2017, 60

442

(2), 170; DOI 10.1007/s11426-016-0317-3.

443

37. Wang, X.; Yang, S.; Shi, W.; Li, J.; Hayat, T.; Wang, X. Different interaction mechanisms of

444

Eu(III) and 243Am(III) with carbon nanotubes studied by batch, spectroscopy technique and

445

theoretical

446

10.1021/acs.est.5b02679.

447

38. Nordhei, C.; Ramstad, A. L.; Nicholson, D. G. Nanophase cobalt, nickel and zinc ferrites:

448

synchrotron XAS study on the crystallite size dependence of metal distribution. Phys. Chem. Chem.

449

Phys. 2008, 10 (7), 1053-1066; DOI 10.1039/b711918f.

450

39. Gillot, B.; Laarj, M.; Maachi, B.; Rousset, A. Thermal stability and reactivity in oxygen of

451

potassium ferrites with spinel structure. J. Therm. Anal. 1990, 36 (2), 645-656; DOI

452

https://doi.org/10.1007/BF01914517.

453

40. Pullar, R. C. Hexagonal ferrites: A review of the synthesis, properties and applications of

454

hexaferrite

455

http://dx.doi.org/10.1016/j.pmatsci.2012.04.001.

456

41. Henderson, C. M. B.; Charnock, J. M.; Plant, D. A. Cation occupancies in Mg, Co, Ni, Zn, Al

457

ferrite spinels: a multi-element EXAFS study. J. Phys.: Condens. Matter 2007, 19 (7) 076214; DOI

458

10.1088/0953-8984/19/7/076214.

459

42. Henglein, F. A. Chemical Technology; Elsevier Science, 2013.

calculation.

ceramics.

Environ.

Prog.

Sci.

Technol.

Mater.

Sci.

2015,

2012,

49

57

(19),

(7),

11721-11728;

1191-1334;

DOI

DOI

460 22/30

ACS Paragon Plus Environment

Environmental Science & Technology

461

Page 24 of 31

Captions of Figures

462 463

Figure 1. XRD patterns of the sintered samples of (a) NiO + α-Fe2O3, (b) 0.1CdO + 0.9NiO +

464

α-Fe2O3, (c) 0.3CdO + 0.7NiO + α-Fe2O3, (d) 0.5CdO + 0.5NiO + α-Fe2O3, (e) 0.7CdO + 0.3NiO +

465

α-Fe2O3, (f) 0.9CdO + 0.1NiO + α-Fe2O3, and (g) CdO + α-Fe2O3 for the formation of CdxNi1−xFe2O4

466

spinel (x = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9, and 1.0) at 950°C for 3 h. H is for hematite (α-Fe2O3, ICDD

467

PDF No. 89-0597); N is for bunsenite (NiO, ICDD PDF No. 71-1179); S0, S1, S3, S5, S7, S9, and

468

S10 are for the newly formed spinel in the (a)–(g) sintered samples, respectively.

469 470

Figure 2. (a) XRD patterns of the single-phase Cd-Ni-Fe spinel solid solutions (CdxNi1−xFe2O4, x =

471

0.0, 0.1, 0.3, 0.5, 0.7, 0.9, and 1.0), and (b) lattice parameters of CdxNi1−xFe2O4 spinel solid solutions,

472

refined from the XRD patterns presented in Figure 2a with the Rietveld refinement method, showing

473

a linear increase of the lattice parameters of the single-phase CdxNi1−xFe2O4 products as x increased.

474 475

Figure 3. EXAFS data acquired at the Cd K-edge of CdxNi1−xFe2O4 samples (x = 0.5, 0.9, and 1.0).

476

Solid line: experimental data, dotted line: best fit.

477 478

Figure 4. Contents of (a) Cd and (b) Ni in the leachates of CdO, NiO, CdFe2O4, NiFe2O4, and

479

CdxNi1−xFe2O4 after 120 min of CPLT.

480

23/30

ACS Paragon Plus Environment

Page 25 of 31

Environmental Science & Technology

481

Figure 5. XRD patterns of (a) the SNCBS-600 +α-Fe2O3 mixtures sintered at temperatures ranging

482

from 700°C to 950°C for 3 h, showing that both Cd and Ni were incorporated into the ferrite spinel

483

solid solution, and (b) the sintered product of SNCBS-600 + α-Fe2O3 after a treatment scheme to

484

incorporate Cd and Ni into the ferrite spinel solid solution. A is for sodium iron oxide (NaFeO2,

485

ICDD PDF No. 76-0243); C is for cadmium oxide (CdO, ICDD PDF No. 75-0594); H is for hematite

486

(α-Fe2O3, ICDD PDF No. 89-0597); K is for potassium iron oxide (KFe11O17, ICDD PDF No.

487

25-0652); N is for bunsenite (NiO, ICDD PDF No. 71-1179); and S is for the ferrite spinel solid

488

solution formed after sintering the mixture of SNCBS-600 and hematite.

489 490

Figure 6. Concentrations of (a) Cd, (b) Ni, (c) Co, (d) K, (e) Na, and (f) Fe in the leachates of the

491

untreated and sintered SNCB sludge (SNCBS-600). The sintered SNCB sludge was thermally

492

reacted with hematite (α-Fe2O3) at 950°C for 12 h followed by another sintering process at 1050°C

493

for 6 h.

494 495 496 497 498 499 500 501 24/30

ACS Paragon Plus Environment

Environmental Science & Technology

502

Table and Figures

503

Including six figures in six pages

Page 26 of 31

504

505 506

Figure 1. XRD patterns of the sintered samples of (a) NiO + α-Fe2O3, (b) 0.1CdO + 0.9NiO +

507

α-Fe2O3, (c) 0.3CdO + 0.7NiO + α-Fe2O3, (d) 0.5CdO + 0.5NiO + α-Fe2O3, (e) 0.7CdO + 0.3NiO +

508

α-Fe2O3, (f) 0.9CdO + 0.1NiO + α-Fe2O3, and (g) CdO + α-Fe2O3 for the formation of CdxNi1−xFe2O4

509

spinel (x = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9, and 1.0) at 950°C for 3 h. H is for hematite (α-Fe2O3, ICDD

510

PDF No. 89-0597); N is for bunsenite (NiO, ICDD PDF No. 71-1179); S0, S1, S3, S5, S7, S9, and

511

S10 are for the newly formed spinel in the (a)–(g) sintered samples, respectively. 25/30

ACS Paragon Plus Environment

Page 27 of 31

Environmental Science & Technology

512

513

514 515

Figure 2. (a) XRD patterns of the single-phase Cd-Ni-Fe spinel solid solutions (CdxNi1−xFe2O4, x =

516

0.0, 0.1, 0.3, 0.5, 0.7, 0.9, and 1.0), and (b) lattice parameters of CdxNi1−xFe2O4 spinel solid solutions,

517

refined from the XRD patterns presented in Figure 2a with the Rietveld refinement method, showing

518

a linear increase of the lattice parameters of the single-phase CdxNi1−xFe2O4 products as x increased. 26/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 28 of 31

519

520 521

Figure 3. EXAFS data acquired at the Cd K-edge of CdxNi1−xFe2O4 samples (x = 0.5, 0.9, and 1.0).

522

Solid line: experimental data, dotted line: best fit.

523

27/30

ACS Paragon Plus Environment

Page 29 of 31

Environmental Science & Technology

524

525 526

Figure 4. Contents of (a) Cd and (b) Ni in the leachates of CdO, NiO, CdFe2O4, NiFe2O4, and

527

CdxNi1−xFe2O4 after 120 min of CPLT.

528 529 28/30

ACS Paragon Plus Environment

Environmental Science & Technology

Page 30 of 31

530

531 532

Figure 5. XRD patterns of (a) the SNCBS-600 +α-Fe2O3 mixtures sintered at temperatures ranging

533

from 700°C to 950°C for 3 h, showing that both Cd and Ni were incorporated into the ferrite spinel

534

solid solution, and (b) the sintered product of SNCBS-600 + α-Fe2O3 after a treatment scheme to

535

incorporate Cd and Ni into the ferrite spinel solid solution. A is for sodium iron oxide (NaFeO2,

536

ICDD PDF No. 76-0243); C is for cadmium oxide (CdO, ICDD PDF No. 75-0594); H is for hematite

537

(α-Fe2O3, ICDD PDF No. 89-0597); K is for potassium iron oxide (KFe11O17, ICDD PDF No.

538

25-0652); N is for bunsenite (NiO, ICDD PDF No. 71-1179); and S is for the ferrite spinel solid

539

solution formed after sintering the mixture of SNCBS-600 and hematite.

29/30

ACS Paragon Plus Environment

Page 31 of 31

Environmental Science & Technology

540

541

542 543

Figure 6. Concentrations of (a) Cd, (b) Ni, (c) Co, (d) K, (e) Na, and (f) Fe in the leachates of the

544

untreated and sintered SNCB sludge (SNCBS-600). The sintered SNCB sludge was thermally

545

reacted with hematite (α-Fe2O3) at 950°C for 12 h followed by another sintering process at 1050°C

546

for 6 h.

547 30/30