Integrating Zeolite-Type Chalcogenide with Titanium Dioxide

Department of Chemistry and Biochemistry, California State University Long Beach, 1250 Bellflower Boulevard, Long Beach, California 90840, United Stat...
1 downloads 0 Views 1MB Size
Article Cite This: Langmuir XXXX, XXX, XXX-XXX

pubs.acs.org/Langmuir

Integrating Zeolite-Type Chalcogenide with Titanium Dioxide Nanowires for Enhanced Photoelectrochemical Activity Chengyu Mao,†,‡,⊥ Yanxiang Wang,‡ Wei Jiao,‡,§ Xitong Chen,‡ Qipu Lin,‡ Mingli Deng,§ Yun Ling,§ Yaming Zhou,§ Xianhui Bu,*,∥ and Pingyun Feng*,†,‡ †

Materials Science and Engineering Program, University of California, Riverside, California 92521, United States Department of Chemistry, University of California, Riverside, California 92521, United States § Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Department of Chemistry, Fudan University, Shanghai 200433, China ∥ Department of Chemistry and Biochemistry, California State University Long Beach, 1250 Bellflower Boulevard, Long Beach, California 90840, United States ‡

S Supporting Information *

ABSTRACT: Developing photoanodes with efficient visiblelight harvesting and excellent charge separation still remains a key challenge in photoelectrochemical water splitting. Here zeolite-type chalcogenide CPM-121 is integrated with TiO2 nanowires to form a heterostructured photoanode, in which crystalline CPM-121 particles serve as a visible light absorber and TiO2 nanowires serve as an electron conductor. Owing to the small band gap of chalcogenides, the hybrid electrode demonstrates obvious absorption in visible-light range. Electrochemical impedance spectroscopy (EIS) shows that electron transport in the hybrid electrode has been significantly facilitated due to the heterojunction formation. A >3-fold increase in photocurrent is observed on the hybrid electrode under visible-light illumination when it is used as a photoanode in a neutral electrolyte without sacrificial agents. This study opens up a new avenue to explore the potential applications of crystalline porous chalcogenide materials for solar-energy conversion in photoelectrochemistry.

1. INTRODUCTION

The quest for efficient solar-energy conversion into chemical energy has stimulated worldwide interest in artificial photosynthesis research13,14 since the first discovery of TiO2 photocatalyst four decades ago.15 Despite their strong optical absorption, advantageous band edge positions, high stability toward photocorrosion, low toxicity, and abundance, the efficiency of metal oxide photocatalysts is limited by the large band gap and severe charge recombination.16 In comparison, heterometallic chalcogenides are known to consist of environmentally benign elements and exhibit tunable gaps in the visible-light range. As such, they are well-suited for solar-energy harvest.17−19 As photovoltaic materials, high solar-energy conversion efficiency has been achieved in solar cell devices by employing various quaternary chalcogenides such as Cu 2 ZnSnS 4 (CZTS), Cu 2 ZnSnSe 4 (CZTSe), and CuInxGa1−xSe4 (CIGS).20 However, for photocatalytic reactions, hole-induced oxidative photocorrosion represents a significant hindrance for the practical application of metal chalcogenide photocatalysts.21 Moreover, low surface area of

Heterometallic chalcogenides are among the most advanced solid-state materials and have been widely investigated in recent years.1,2 By combining synthetic and structural concepts from metal chalcogenide chemistry and nanoporous solids, a number of highly stable porous chalcogenides with structural and functional diversity have been developed.3 Compared to the well-developed crystalline porous zeolites, which are at the center of many industrial revolutions like petroleum refining and gas separation,4 chalcogenides possess favorable electronic band structures in semiconducting5,6 instead of insulating range, and their atomic and electronic structures can be conveniently tuned through either direct synthesis or postsynthetic modifications by varying cluster composition, type, and size, intercluster connectivity, or doping clusters with heteroatoms.7 Moreover, thanks to the size-tunable building blocks in chalcogenides such as supertetrahedral clusters,8 a pore size much larger than that in zeolites can be achieved, which makes porous chalcogenides ideal as host frameworks for guest molecules.9 Such integration between unique electronic properties10 and porosity makes chalcogenides promising candidates for many important applications.11,12 © XXXX American Chemical Society

Received: July 12, 2017 Revised: October 2, 2017

A

DOI: 10.1021/acs.langmuir.7b02403 Langmuir XXXX, XXX, XXX−XXX

Article

Langmuir

Figure 1. (A) PXRD patterns of FTO-TiO2 and FTO-TiO2-CPM-121. (B) Adamantane cage in CPM-121. (C, D) SEM image and EDX spectra of FTO-TiO2-CPM-121.

situ formed on the vertically aligned TiO2 substrate grown on the fluorine-doped tin oxide (FTO) current collector. The porous crystalline CPM-121 serves as a visible-light absorber and could provide more active sites due to its porosity and high surface area. Simultaneously, TiO2 nanowires work as an electron conductor to transfer electrons to the FTO current collector. The in situ formed heterojunction between the chalcogenide cluster and TiO2 nanowires could facilitate the charge-separation process and offer a much-improved charge transfer compared to clusters deposited by postsynthetic electrophoresis or spin-coating, reported previously.34−36 The as-fabricated hybrid photoanode shows a significantly enhanced photocurrent compared to either TiO2 photoanode or CPM121 photoanode directly deposited on FTO, demonstrating the synergetic effect of both components.

many previously reported chalcogenides also limits the available surface-active sites. Integrating merits of different types of materials by forming hybrid structures could provide a feasible pathway to circumvent some limitations of single-component photocatalysts.22−24 For instance, chalcogenides can be anchored onto a wide band gap photocatalyst to form a heterojunction.25 Electrons generated under visible-light irradiation in the conduction band (CB) of chalcogenides can be effectively transferred into the conduction band of the other photocatalyst, which allows for a more efficient solar-light absorption and photogenerated electron−hole separation. TiO2 nanowire photoanode sensitized with CdS quantum dots (QDs) or shells is a classic example of heterostructured photoelectrode for photoelectrochemical (PEC) water splitting.26,27 More recently, reduced graphene oxide28 (RGO) sheets, which can offer excellent electron mobility and high optical transparency,29,30 are widely used as an electron acceptor to promote charge separation. In our own work, by integrating RGO sheets and OCF-40-ZnGaSnS chalcogenide (OCF stands for organically directed chalcogenide frameworks) T4 supertetrahedral clusters (T4 means there are 4 metal sites along the edge of the tetrahedron), we were able to fabricate a hybrid material31 using a two-step approach. The resulting hybrid exhibited enhanced photoelectrochemical performance and much improved photostability. Despite these aforementioned advances, hybridizing heterometallic chalcogenide clusters with wide band gap materials as photoanode for visible-light photoelectrochemical reactions without sacrificial agent has not been explored so far.32 Here, we first report the fabrication of heterostructural photoanode by integrating TiO2 with a zeolite-type chalcogenide denoted CPM-121-ZnGeGaS, or simply CPM-12133 (CPM stands for crystalline porous materials), and its use for visible-light photoelectrochemical reactions in neutral electrolyte without any sacrificial agents. CPM-121-ZnGeGaS was in

2. EXPERIMENTAL SECTION Materials Synthesis. To integrate zeolite-type chalcogenide CPM121-ZnGeGaS with TiO2, TiO2 nanowires were first grown on a substrate using a hydrothermal method. A clean FTO substrate with conductive side facing down was immersed into the autoclave filled with a solution of hydrochloric acid and Ti(IV) isopropoxide. The autoclave was put in a preheated 200 °C oven for 90 min. Afterward, FTO substrate covered with TiO2 nanowires was recovered from the autoclave, dried overnight first, and annealed in air at 400 °C for 1 h. CPM-121-ZnGeGaS was then fabricated on FTO-TiO2. A slurry containing GeO2, Zn(NO3)2·6H2O, Ga(NO3)3·xH2O, sulfur, and 3 mL of N-(2-aminoethyl) morpholine (AEM) was first stirred overnight until no aggregates existed. The as-obtained slurry was dropped onto the TiO2 side of FTO-TiO2 by using a glass rod. FTOTiO2 was held vertically to remove extra slurry. The process was repeated for 3−5 times until the whole FTO-TiO2 surface was covered by the slurry uniformly. The FTO-TiO2 was then moved into an empty autoclave. The vessel was then sealed and heated at 190 °C for 1 week. After cooling to room temperature, the FTO was recovered and the yellow crystals were grown on the TiO2 surface. Characterization. The X-ray diffraction (XRD) patterns were measured using a Bruker D8 Advance powder diffractometer with Cu Kα emission. Scanning electron microscopy (SEM) images and B

DOI: 10.1021/acs.langmuir.7b02403 Langmuir XXXX, XXX, XXX−XXX

Article

Langmuir

Figure 2. (A) UV−vis spectra and (B) Tauc plots of FTO-TiO2-CPM-121 and FTO-TiO2. energy-dispersive X-ray spectroscopy (EDX) were obtained using a Nova Nano-SEM450 equipped with Oxford Instruments Aztec energydispersive spectroscopy detector. Optical properties were investigated by a SHIMADZU UV-3150 UV−vis scanning spectrophotometer equipped with an integration sphere. Photoelectrochemical Characterization. Photoelectrochemical study was performed in a three-electrode configuration with samples as a working electrode, Pt as a counter electrode, and Ag/AgCl as a reference electrode. A 150 W xenon lamp coupled with a 420 nm cutoff filter was applied as the visible-light source, and 0.5 M Na2SO4 aqueous solution at pH = 6.3 was employed as the electrolyte. A Solartron 1287 electrochemistry interface coupled with a Solartron 1260 impedance/gain-phase analyzer was used to collect the data. The gaseous product on the cathode was collected by electrolytedisplacement method and analyzed by a gas chromatograph (Shimadzu GC-8A) equipped with a thermal conductivity detector (TCD). Stability test was also performed in 0.5 M Na2SO4 solution at 1.23 V vs reversible hydrogen electrode (RHE) with a 455 nm cutoff filter.

and S in EDX spectra (Figure 1D) further verified the formation of CPM-121. Moreover, the elemental mapping (Figure S3) revealed that those signals only came from the locations where the octahedral crystals were formed. More specifically, S and Ge elements were homogeneously distributed on the octahedral-shaped crystals while Ti signals were coming from the nanowires. Given the small amount of Zn and Ga in the chalcogenide cluster, their signals were not strong in the elemental mapping. Powder samples prepared in the autoclave were also examined by powder X-ray diffraction. Their crystallinity and purity were further verified by comparing the X-ray diffraction pattern obtained from the powders and that simulated from single-crystal data (Figure S4). The optical properties of the heterostructural electrodes as well as FTO-TiO2 were investigated by UV−vis absorbance spectra.38 As shown in Figure S5A, crystalline CPM-121 powder showed strong absorption in the entire range of wavelengths, making it an ideal light absorber for efficient solarenergy harvest. The band gap was determined to be 1.94 eV from its corresponding Tauc plot (Figure S5B). On the other hand, Figure 2A showed that TiO2 nanowires grown on FTO current collector only demonstrated a strong absorbance below 420 nm, consistent with its intrinsic large band gap of 2.97 eV. When the TiO2 photoelectrode was integrated with the chalcogenide crystals, an obvious absorption in the visiblelight region was observed. Furthermore, the light absorption in the UV region was also enhanced. The results confirmed the effectiveness of the heterostructure for light harvest and suggested that the hybrid electrode may absorb more photons to generate electrons and holes and thus enhance the photoelectrochemical activity. Tauc plot of the heterostructured photoelectrode in Figure 2B revealed two distinct band gaps at 2.99 and 1.84 eV, corresponding to the band gap of rutile TiO2 and CPM-121, respectively. An X-ray photoelectron spectroscopy valence band (XPS-VB) spectrum was also collected for CPM-121 (Figure S6), and the valence band maximum was determined to be at 0.56 eV. Conduction band minimum of rutile and CPM-121 could then be estimated using their measured band gap, which were at −1.12 and −1.28 eV, respectively.39 As a result, a type-II gap could be formed between rutile and CPM-121 to facilitate charge transport. The slight deviation of the band gap from each individual component may be the result of strong interfacial interaction between the two components. The visible-light-driven photoelectrochemical activity of the hybrid electrode was studied here. The transient photocurrents of the FTO-TiO2-CPM-121, FTO-TiO2, and CPM-121 crystals deposited directly on the FTO by electrophoresis were

3. RESULTS AND DISCUSSION Rutile TiO2 nanowires were grown on FTO by a hydrothermal method.37 Both powder X-ray diffraction (PXRD) and SEM characterizations (Figure 1A and Figure S1A) confirmed the formation of TiO2 nanowires. Energy-dispersive X-ray spectroscopy (EDX) collected at the same spot as the SEM images reveals that the nanowires are composed of Ti and O (Figure S1B). With its high chemical stability, TiO2 nanowires could serve as the backbone during the following solvothermal reactions, and crystallized chalcogenide clusters can be grown on its surface. The crystallization of Ge/Sn chalcogenide zeotypes induced by a small amount of divalent metal ions was systematically investigated in our previous study. Built of supertetrahedral T2 clusters, the as-obtained CPM-121 crystals could be simplified into a noninterpenetrated superdiamond, and its adamantane cage is depicted in Figure 1B. The detailed procedure for CPM-121 formation on the TiO2 backbone by the reaction of Zn(NO3)2·6H2O, Ga(NO3)3·xH2O, GeO2, and S with the assistance of N-(2-aminoethyl) morpholine (AEM) template is described in the Experimental Section and Supporting Information. As shown in the SEM image of Figure S2, TiO2 nanowires kept their original morphology after its recovery from the autoclave while octahedral-shaped crystals in a few micrometers were obtained on TiO2 surfaces. From a larger-scale SEM image in Figure 1C, uniformly distributed octahedral crystals with a narrow size distribution were observed on the TiO2 substrate. Diffraction peaks ascribed to CPM-121 were also spotted in the PXRD pattern of the asobtained sample (Figure 1A) in addition to those signals coming from TiO2 substrate. The signatures from Zn, Ge, Ga, C

DOI: 10.1021/acs.langmuir.7b02403 Langmuir XXXX, XXX, XXX−XXX

Article

Langmuir

Figure 3. (A) Transient photocurrents and (B) linear sweep voltammetry of FTO-TiO2-CPM-121, FTO-TiO2, and CPM-121 deposited on the FTO electrode.

FTO-TiO2-CPM-121 showed a nearly 2-fold enhancement in photocurrent density, up to 59.6 μA/cm2. On the other hand, CPM-121 only exhibited an inferior photoelectrochemical performance and a much smaller photocurrent of 12.2 μA/ cm2 at 1.23 V vs RHE. To gain further insight into the charge-transport behaviors of all samples, electrochemical impedance spectroscopy (EIS) measurements were performed on the electrodes studied above. A Mott−Schottky plot was generated based on the capacitance derived from the impedance at different applied potentials of FTO-TiO2-CPM-121 (Figure S9) as well. The positive slope in the linear part of the Mott−Schottky plot described the behavior of an n-type semiconductor, which was working as a photoanode in the photoelectrochemical cell. The semicircle in the as-obtained Nyquist plots was associated with the chargetransfer process, and a smaller arc corresponds to smaller impedance and a better charge separation. As shown in Figure 4A, FTO-TiO2-CPM-121 photoanode exhibited a much smaller

recorded in Figure 3A during repeated on/off illumination cycles at 1.0 V vs RHE. The RHE potential was converted from the saturated Ag/AgCl reference electrode using ERHE = E(Ag/AgCl) + 0.57 V. All samples exhibited prompt and reproducible responses toward light illumination, with photocurrents decreasing to almost zero upon irradiation interruption and fully recovering upon light switching on. The spike observed upon irradiation was due to the rapid effect upon power excitation, and then it quickly returned to the steady state. The photocurrent of FTO-TiO2-CPM-121 reached 55 μA/cm2 upon visible-light illumination, whereas FTO-TiO2 is only 16 μA/cm2. The >3-fold enhancement in photocurrent confirmed the synergistic effect of the heterostructure, where CPM-121 acts as an efficient visible-light absorber while TiO2 substrate contributed to the electron transfer and suppressed charge recombination. The gaseous product generated on the counter electrode (Pt) was collected by electrolyte displacement and analyzed by gas chromatography, and the results are presented in Figure S10. Signals from air were used as a reference. Only a prominent H2 peak was identified from the gaseous product on the cathode side and confirmed as the product of the photoelectrochemical reaction. Action spectra of photocurrents of FTO-TiO2-CPM-121 and FTO-TiO2 were also obtained by measuring the photocurrents under each 20 nm wavelength interval from 300 to 600 nm. The spectra in Figure S8 further demonstrated that the hybrid electrode has a superior activity in both UV and visible-light range due to the synergistic effect between the small band gap CPM-121 and TiO2 nanowires, which was consistent with their optical properties and the photocurrent measurements discussed above. Although CPM-121 powder demonstrated strong light adsorption in the entire light range, it only exhibits a limited photocurrent of 1.4 μA/cm2 upon visible-light illumination. The poor photoelectrochemical performance should be ascribed to the difficult electron transport between the directly deposited crystals and the current collector, which could lead to severe photoexcited electron−hole pairs recombination. Note that the photocurrent achieved by the FTO-TiO2-CPM-121 here was even >2 times higher than that by Pt-loaded CPM-120 photoanode with sacrificial agent.33 This superior performance by FTO-TiO2-CPM-121 hybrid electrode may result from more efficient charge separation owing to the heterojunction formation, as well as the enhanced light harvesting. This result was further confirmed by the linear sweep voltammetry (LSV) in Figure 3B, where FTO-TiO2 only achieved a photocurrent of 30.5 μA/cm2 at 1.23 V vs RHE. In contrast, FTO-TiO2-CPM121 also exhibited a substantially higher photocurrent over the entire potential range. At the same 1.23 V applied voltage,

Figure 4. (A) Nyquist plot of FTO-TiO2-CPM-121, FTO-TiO2, and (B) CPM-121 deposited on the FTO electrode.

radius than FTO-TiO2, further proving the advantageous charge separation upon heterojunction formation in the asfabricated photoanode. The equivalent circuit shown in Figure S11 was employed to further analyze the Nyquist plot, where Rs stands for a series resistance, Rct stands for charge-transfer resistance, CPE stands for a constant phase element for imperfect capacitance, and Ws is Nernst diffusion impedance. While Rs did not change much between FTO-TiO2 and FTOTiO2-CPM-121(from 46.9Ω to 40.3Ω), Rct decreased significantly from 11 891Ω to 1 889Ω, proving the beneficial charge transfer in the hybrid material. Meanwhile, CPM-121 powder deposited on FTO current collector had a significantly larger semicircle (Figure 4B), suggesting the poor electron transport within the electrode and consistent with our observations in photoelectrochemical tests. The photocurrent of FTO-TiO2CPM-121 in the presence and the absence of H2O2 under AM D

DOI: 10.1021/acs.langmuir.7b02403 Langmuir XXXX, XXX, XXX−XXX

Langmuir



1.5 illumination was measured to estimate the hole-injection yield. Because the injection yield becomes 100% when H2O2 is in the electrolyte, the charge-injection yield into water can be estimated by dividing two photocurrents. As shown in Figure S12, the hole-injection yield rises steeply for FTO-TiO2-CPM121 and remains close to 100% at high potentials. Stability test was also performed on FTO-TiO2-CPM-121, and the result is displayed in Figure S13. The as-fabricated photoanode exhibited a steady activity, with 90% photocurrent remaining after 30 min of visible-light illumination.

ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acs.langmuir.7b02403. Experimental details, XRD patterns, SEM, EDX, UV−vis spectra, Mott−Schottky plot, and GC profile (PDF)



REFERENCES

(1) Shi, Y.; Wan, Y.; Zhao, D. Ordered mesoporous non-oxide materials. Chem. Soc. Rev. 2011, 40 (7), 3854−3878. (2) Kershaw, S. V.; Susha, A. S.; Rogach, A. L. Narrow bandgap colloidal metal chalcogenide quantum dots: synthetic methods, heterostructures, assemblies, electronic and infrared optical properties. Chem. Soc. Rev. 2013, 42 (7), 3033−87. (3) Feng, P.; Bu, X.; Zheng, N. The Interface Chemistry between Chalcogenide Clusters and Open Framework Chalcogenides. Acc. Chem. Res. 2005, 38 (4), 293−303. (4) Zhao, D.; Feng, J.; Huo, Q.; Melosh, N.; Fredrickson, G. H.; Chmelka, B. F.; Stucky, G. D. Triblock Copolymer Syntheses of Mesoporous Silica with Periodic 50 to 300 Angstrom Pores. Science 1998, 279 (5350), 548−552. (5) Dehnen, S.; Brandmayer, M. K. Reactivity of Chalcogenostannate Compounds: Syntheses, Crystal Structures, and Electronic Properties of Novel Compounds Containing Discrete Ternary Anions [MII4(μ4Se)(SnSe4)4]10- (MII = Zn, Mn). J. Am. Chem. Soc. 2003, 125 (22), 6618−6619. (6) Ewing, S. J.; Vaqueiro, P. Synthesis and characterization of inorganic-organic hybrid gallium selenides. Inorg. Chem. 2014, 53 (17), 8845−7. (7) Wu, T.; Zhang, Q.; Hou, Y.; Wang, L.; Mao, C.; Zheng, S. T.; Bu, X.; Feng, P. Monocopper doping in Cd-In-S supertetrahedral nanocluster via two-step strategy and enhanced photoelectric response. J. Am. Chem. Soc. 2013, 135 (28), 10250−3. (8) Corrigan, J. F.; Fuhr, O.; Fenske, D. Metal Chalcogenide Clusters on the Border between Molecules and Materials. Adv. Mater. 2009, 21 (18), 1867−1871. (9) Zheng, N.; Bu, X.; Feng, P. Synthetic design of crystalline inorganic chalcogenides exhibiting fast-ion conductivity. Nature 2003, 426 (6965), 428−432. (10) Staszak-Jirkovsky, J.; Malliakas, C. D.; Lopes, P. P.; Danilovic, N.; Kota, S. S.; Chang, K.-C.; Genorio, B.; Strmcnik, D.; Stamenkovic, V. R.; Kanatzidis, M. G.; Markovic, N. M. Design of active and stable Co-Mo-Sx chalcogels as pH-universal catalysts for the hydrogen evolution reaction. Nat. Mater. 2016, 15 (2), 197−203. (11) Regulacio, M. D.; Han, M. Y. Multinary I-III-VI2 and I2-II-IV-VI4 Semiconductor Nanostructures for Photocatalytic Applications. Acc. Chem. Res. 2016, 49 (3), 511−9. (12) Gao, M. R.; Xu, Y. F.; Jiang, J.; Yu, S. H. Nanostructured metal chalcogenides: synthesis, modification, and applications in energy conversion and storage devices. Chem. Soc. Rev. 2013, 42 (7), 2986− 3017. (13) Hisatomi, T.; Kubota, J.; Domen, K. Recent advances in semiconductors for photocatalytic and photoelectrochemical water splitting. Chem. Soc. Rev. 2014, 43 (22), 7520−35. (14) Lewis, N. S.; Nocera, D. G. Powering the planet: Chemical challenges in solar energy utilization. Proc. Natl. Acad. Sci. U. S. A. 2006, 103 (43), 15729−15735. (15) Fujishima, A.; Honda, K. Electrochemical Photolysis of Water at a Semiconductor Electrode. Nature 1972, 238 (5358), 37−38. (16) Chen, X.; Shen, S.; Guo, L.; Mao, S. S. Semiconductor-based Photocatalytic Hydrogen Generation. Chem. Rev. 2010, 110 (11), 6503−6570. (17) Liu, Y.; Kanhere, P. D.; Ling Wong, C.; Tian, Y.; Feng, Y.; Boey, F.; Wu, T.; Chen, H.; White, T. J.; Chen, Z.; Zhang, Q. Hydrazinehydrothermal method to synthesize three-dimensional chalcogenide framework for photocatalytic hydrogen generation. J. Solid State Chem. 2010, 183 (11), 2644−2649. (18) Shim, Y.; Young, R. M.; Douvalis, A. P.; Dyar, S. M.; Yuhas, B. D.; Bakas, T.; Wasielewski, M. R.; Kanatzidis, M. G. Enhanced Photochemical Hydrogen Evolution from Fe4S4-Based Biomimetic Chalcogels Containing M2+ (M = Pt, Zn, Co, Ni, Sn) Centers. J. Am. Chem. Soc. 2014, 136 (38), 13371−13380. (19) Dilsaver, P. S.; Reichert, M. D.; Hallmark, B. L.; Thompson, M. J.; Vela, J. Cu2ZnSnS4−Au Heterostructures: Toward Greener Chalcogenide-Based Photocatalysts. J. Phys. Chem. C 2014, 118 (36), 21226−21234.

4. CONCLUSIONS In summary, we have rationally designed a heterostructured photoanode consisting of heterometallic zeolite-type chalcogenide CPM-121 and TiO2 nanowires for efficient solar-energy conversion. The crystalline porous chalcogenides act as a visible-light absorber to generate electrons and holes upon irradiation, while the TiO2 nanowire serves as the scaffold for chalcogenide formation and facilitates the electron transfer during the photoelectrochemical reactions. The interface formed between two components significantly promotes charge separation and reduces the electrochemical impedance. As a result, a profoundly enhanced photoelectrochemical activity in the neutral electrolyte is realized under visible-light illumination on the hybrid electrode. Given the richness of compositional and topological variations in crystalline porous chalcogenide materials and their tunable optical and electronic properties, this study opens up a new avenue to explore their potential applications for solar-energy conversion in photoelectrochemistry.



Article

AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected]. *E-mail: [email protected]. ORCID

Yun Ling: 0000-0002-6956-4504 Yaming Zhou: 0000-0003-2720-9536 Xianhui Bu: 0000-0002-2994-4051 Pingyun Feng: 0000-0003-3684-577X Present Address

⊥ C.M.: Energy and Transportation Science Division, Oak Ridge National Laboratory, One Bethel Valley Road, P.O. Box 2008, Oak Ridge, TN 37831, United States.

Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS This research was supported by the National Science Foundation (DMR-1506661, P.F.). W.J. thanks the financial support of Fudan University and the NSFC (51402314, W.J.) E

DOI: 10.1021/acs.langmuir.7b02403 Langmuir XXXX, XXX, XXX−XXX

Article

Langmuir (20) Chung, I.; Lee, B.; He, J.; Chang, R. P. H.; Kanatzidis, M. G. Allsolid-state dye-sensitized solar cells with high efficiency. Nature 2012, 485 (7399), 486−489. (21) Yu, X.; Shavel, A.; An, X.; Luo, Z.; Ibáñez, M.; Cabot, A. Cu2ZnSnS4-Pt and Cu2ZnSnS4-Au Heterostructured Nanoparticles for Photocatalytic Water Splitting and Pollutant Degradation. J. Am. Chem. Soc. 2014, 136 (26), 9236−9239. (22) Li, R.; Hu, J.; Deng, M.; Wang, H.; Wang, X.; Hu, Y.; Jiang, H. L.; Jiang, J.; Zhang, Q.; Xie, Y.; Xiong, Y. Integration of an inorganic semiconductor with a metal-organic framework: a platform for enhanced gaseous photocatalytic reactions. Adv. Mater. 2014, 26 (28), 4783−8. (23) Zhuang, T.-T.; Liu, Y.; Sun, M.; Jiang, S.-L.; Zhang, M.-W.; Wang, X.-C.; Zhang, Q.; Jiang, J.; Yu, S.-H. A Unique Ternary Semiconductor-(Semiconductor/Metal) Nano-Architecture for Efficient Photocatalytic Hydrogen Evolution. Angew. Chem., Int. Ed. 2015, 54, 11495−11500. (24) Li, H.; Zhou, Y.; Tu, W.; Ye, J.; Zou, Z. State-of-the-Art Progress in Diverse Heterostructured Photocatalysts toward Promoting Photocatalytic Performance. Adv. Funct. Mater. 2015, 25 (7), 998−1013. (25) Wang, G.; Yang, X.; Qian, F.; Zhang, J. Z.; Li, Y. Double-sided CdS and CdSe quantum dot co-sensitized ZnO nanowire arrays for photoelectrochemical hydrogen generation. Nano Lett. 2010, 10 (3), 1088−92. (26) Ai, G.; Li, H.; Liu, S.; Mo, R.; Zhong, J. Solar Water Splitting by TiO2/CdS/Co-Pi Nanowire Array Photoanode Enhanced with Co-Pi as Hole Transfer Relay and CdS as Light Absorber. Adv. Funct. Mater. 2015, 25 (35), 5706−5713. (27) Qin, N.; Liu, Y.; Wu, W.; Shen, L.; Chen, X.; Li, Z.; Wu, L. Onedimensional CdS/TiO2 nanofiber composites as efficient visible-lightdriven photocatalysts for selective organic transformation: synthesis, characterization, and performance. Langmuir 2015, 31 (3), 1203−9. (28) da Silva, A. G. M.; Rodrigues, T. S.; Correia, V. G.; Alves, T. V.; Alves, R. S.; Ando, R. A.; Ornellas, F. R.; Wang, J.; Andrade, L. H.; Camargo, P. H. C. Plasmonic Nanorattles as Next-Generation Catalysts for Surface Plasmon Resonance-Mediated Oxidations Promoted by Activated Oxygen. Angew. Chem. 2016, 128, 7227−7231. (29) Xiang, Q.; Yu, J.; Jaroniec, M. Synergetic effect of MoS2 and graphene as cocatalysts for enhanced photocatalytic H2 production activity of TiO2 nanoparticles. J. Am. Chem. Soc. 2012, 134 (15), 6575−8. (30) Chang, K.; Mei, Z.; Wang, T.; Kang, Q.; Ouyang, S.; Ye, J. MoS2/Graphene Cocatalyst for Efficient Photocatalytic H2 Evolution under Visible Light Irradiation. ACS Nano 2014, 8 (7), 7078−7087. (31) Hou, Y.; Wu, T.; Wang, L.; Feng, P. Integration of supertetrahedral cluster with reduced graphene oxide sheets for enhanced photostability and photoelectrochemical properties. Sci. China: Chem. 2013, 56 (4), 423−427. (32) Jiang, F.; Gunawan; Harada, T.; Kuang, Y.; Minegishi, T.; Domen, K.; Ikeda, S. Pt/In2S3/CdS/Cu2ZnSnS4 Thin Film as an Efficient and Stable Photocathode for Water Reduction under Sunlight Radiation. J. Am. Chem. Soc. 2015, 137, 13691−13697. (33) Lin, Q.; Bu, X.; Mao, C.; Zhao, X.; Sasan, K.; Feng, P. Mimicking High-Silica Zeolites: Highly Stable Germanium-and TinRich Zeolite-Type Chalcogenides. J. Am. Chem. Soc. 2015, 137, 6184− 6187. (34) Zheng, J. W.; Bhattcahrayya, A.; Wu, P.; Chen, Z.; Highfield, J.; Dong, Z.; Xu, R. The Origin of Visible Light Absorption in Chalcogen Element (S, Se, and Te)-Doped Anatase TiO2 Photocatalysts. J. Phys. Chem. C 2010, 114 (15), 7063−7069. (35) Sheng, P.; Li, W.; Tong, X.; Wang, X.; Cai, Q. Development of a high performance hollow CuInSe2 nanospheres-based photoelectrochemical cell for hydrogen evolution. J. Mater. Chem. A 2014, 2 (44), 18974−18987. (36) Krbal, M.; Prikryl, J.; Zazpe, R.; Sopha, H.; Macak, J. M. CdScoated TiO2 nanotube layers: downscaling tube diameter towards efficient heterostructured photoelectrochemical conversion. Nanoscale 2017, 9 (23), 7755−7759.

(37) Hwang, Y. J.; Hahn, C.; Liu, B.; Yang, P. Photoelectrochemical Properties of TiO2 Nanowire Arrays: A Study of the Dependence on Length and Atomic Layer Deposition Coating. ACS Nano 2012, 6 (6), 5060−5069. (38) Lin, J.; Zhang, Q.; Wang, L.; Liu, X.; Yan, W.; Wu, T.; Bu, X.; Feng, P. Atomically precise doping of monomanganese ion into coreless supertetrahedral chalcogenide nanocluster inducing unusual red shift in Mn2+ emission. J. Am. Chem. Soc. 2014, 136 (12), 4769− 79. (39) Nguyen-Phan, T.-D.; Luo, S.; Vovchok, D.; Llorca, J.; Graciani, J.; Sanz, J. F.; Sallis, S.; Xu, W.; Bai, J.; Piper, L. F. J.; Polyansky, D. E.; Fujita, E.; Senanayake, S. D.; Stacchiola, D. J.; Rodriguez, J. A. Visible Light-Driven H2 Production over Highly Dispersed Ruthenia on Rutile TiO2 Nanorods. ACS Catal. 2016, 6 (1), 407−417.