LiFePO4 Anchored on Pristine Graphene for Ultrafast Lithium Battery

Jun 18, 2018 - Here we report a kind of LFP/G composites in which LiFePO4 nanoparticles ... The mixture was annealed at 700 °C for 5 h in N2 atmosphe...
4 downloads 0 Views 2MB Size
Subscriber access provided by - Access paid by the | UCSB Libraries

Article 4

LiFePO Anchored on Pristine Graphene for Ultrafast Lithium Battery Haijian Tian, Xiaoli Zhao, Jiajia Zhang, Mengxiong Li, and Hongbin Lu ACS Appl. Energy Mater., Just Accepted Manuscript • DOI: 10.1021/acsaem.8b00721 • Publication Date (Web): 18 Jun 2018 Downloaded from http://pubs.acs.org on June 22, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

LiFePO4 Anchored on Pristine Graphene for Ultrafast Lithium Battery Haijian Tian,‡ Xiaoli Zhao,‡ Jiajia Zhang, Mengxiong Li, Hongbin Lu*

State Key Laboratory of Molecular Engineering of Polymers, Collaborative Innovation Center of Polymers and Polymer Composite, Materials and Department of Macromolecular Science, Fudan University, Shanghai 200433, China

Keywords: lithium iron phosphates, graphene, cathode material, lithium ion batteries, defect free, coupling

Abstract Defects make a difference in the performance of graphene or other carbonaceous materials when used as conductive additives in electrodes. Reduced graphene oxide (rGO) has been widely used in lithium iron phosphate cathode (LiFePO4) to promote electron transport and improve lithium storage. Though the defects in rGO or GO induce strong coupling between LiFePO4 nanoparticles and conductive sheets, they inevitably impair the in-plane carrier mobility and thus the conductivity throughout the electrode. In this work, LiFePO4 was robustly anchored on pristine graphene with the assistance of branched polyethyleneimine. The pristine graphene used here features with high crystallinity and anti-restacking merit. The resulting composite

1 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 26

electrodes reveal excellent rate performance: a specific capacity of 143 mAh g-1 at 10 C (1.7 A g-1) and 137 mAh g-1 at 20 C (3.4 A g-1).

1. Introduction Electric vehicles (EVs) have been intensively explored for decades for their advantages with respect to reducing the fossil fuel consumption and the air pollution caused by vehicle exhaust. An EV uses electric energy storage devices. In this regard, lithium ion batteries (LIBs) are deemed among the best options because of the high energy density, good cyclic stability, and low toxicity.1 For LIBs, high-performance cathode materials are still one of the greatest challenges.2 Lithium iron phosphates (LiFePO4) has proved to be ideal cathode materials for LIBs, especially due to its low toxicity, low cost, environmentally benignity, and safety performance.3-9 However, limited rate capability or power density remains its prominent drawback. In particular, hour-long charging time is far inferior to that of gasoline, which largely limits the commercial utilization of LiFePO4. The low rate performance of LiFePO4 primarily arises from its inefficient lithium ion diffusivity and electron migration.10, 11 To deal with these issues, many efforts have been paid to three strategies: scaling down the LiFePO4 particles, metal doping and carbon coating.12, 13

Graphene has manifested great potential in boosting the electrochemical performance of LiFePO4 cathodes, owing to the high specific surface area and superior electrical conductivity.14-18 In the previous studies, reduced graphene oxide (rGO) was usually used,19-29 due to its feasibility in a scalable production of graphene derivatives.30 Zhou 2 ACS Paragon Plus Environment

Page 3 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

et al. reported a scalable spray-drying strategy to prepare graphene-coated LiFePO4.15 Nevertheless, defects in rGO considerably impair its role as conductive additives. Hu et al. observed the cathode capability from electrochemically exfoliated graphene in LiFePO4/graphene composite and ascribed the beyond the theoretical capability to the redox active site induced in the electrochemical exfoliation process.31 However, the rate performance of the composite was also impaired by the reaction on defects of graphene as well as the decreased electrical conductivity, for example, delivering a capacity of 125 mAh g-1 at 10 C, only 60% of that at 0.1 C.

By comparison, pristine graphene contains fewer defects, promising for better electrical conductive additives than rGO or other graphene derivatives.32-34 In the previous study, we have proposed a non-dispersible strategy for production of few-defect graphene in a facile and scalable manner.32 The resulting graphene exhibits both anti-restacking merit and high lattice integrity, beneficial for the optimization of LiFePO4 cathodes and other active nanoparticles.

Here we report a kind of LFP/G composites in which LiFePO4 nanoparticles are in-situ grown on pristine graphene. The interaction between LiFePO4 precursors and graphene are effectively enhanced by branched polyethyleneimine (PEI). To further increase the electrical conductivity of the cathode, a carbon layer was coated through a simple mixing-pyrolysis method. The composite shows superior rate performance, with 143 mAh g−1 at 10 C (1.7 A g-1) and 137 mAh g−1 at 20 C (3.4 A g-1). In another

3 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 26

word, it can be charged within 5.5 min with a capacity efficiency of 93%, and 172 s with ∼ 89%.

2. Experimental Section 2.1 Materials

H3PO4 (85 wt % aqueous solution, AR), LiOH⋅H2O (AR), FeSO4⋅7H2O (AR), glucose (AR), ethylene glycol (EG, AR), N-methyl-2-pyrrolidone (NMP, AR), and L-ascorbic acid (AR) were obtained from Sinopharm Chemical Reagent Co., Ltd. PEI (branched, M = 600 Da, 99 %) was obtained from Alfa Aesar.

2.2 Synthesis of LFP/G composite Graphene was prepared through a sonication method as previously reported,32 which consists mainly of single-layered graphene nanosheets and can be well suspended in NMP for months. The Graphene/NMP dispersion was first substituted with the EG-water binary solvent by cycles of centrifugation, decanting and redispersion. Then PEI was put into the graphene dispersion under magnetic stirring, to obtain the PEI-modified graphene. The weight ratio of graphene and PEI was 3:10.

The preparation of LFP/G starts from a solvothermal method using LiOH⋅H2O, H3PO4 and FeSO4⋅7H2O with a molar ratio of 2.7:1:1 in the presence of PEI-modified graphene. An EG-water binary solvent (the volume ratio of EG to water was 3:1) was used as the solvent. H3PO4 and LiOH⋅H2O were dissolved into the EG-water binary solvent subsequently with an interval time of half an hour. After stirring for an hour, 4 ACS Paragon Plus Environment

Page 5 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

FeSO4⋅7H2O and L-ascorbic acid (with a Fe/ascorbic acid molar ratio of 1:0.18) were added to the suspension quickly. The suspension was sealed and stirred for 10 min before transferred into a Teflon-lined autoclave, and then kept in 200 oC oven for 10 hours. The precipitate was obtained by centrifugation and washed for five times with water and ethanol, followed by drying at 60 oC in a vacuum oven for 2 hours. The dried powder was mixed with glucose (glucose/LiFePO4: 0.1/1 (w/w)). The mixture was annealed at 700 °C for 5 hours in N2 atmosphere.

As a control experiment, the electrode material was prepared without graphene. Other synthesis conditions were kept. The obtained electrode material was denoted as LFP.

2.3 Characterization

The crystalline structure of LFP/G composite and LFP was analyzed by powder X-ray diffraction (XRD) on a Rigaku D/max−2550 V XRD system over a 2θ range of 10– 70° at 8 kW (40 kV, 200 mA). The carbon contents of LFP and LFP/G were determined by thermal gravimetric analysis (TGA) on a Mettler Toledo TGA instrument from 100 to 700 Celsius degree at a heating rate of 10 Celsius degree per minute in air. The morphologies of LFP/G composite and LFP were observed by field-emission scanning electron microscopy (FESEM) on a Zeiss-Ultra55 microscope and high-resolution transmission electron microscopy (HRTEM) on a JEM-2100F microscope.

2.4 Electrochemical Tests

5 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 26

LFP/G and LFP were loaded in coin cells (CR2016) for electrochemical testing. Active material, acetylene black, and polyvinylidene fluoride with a mass ratio of 8:1:1 were added to NMP to form a slurry and then spread uniformly on a piece of Al foil with the loading density of 1 mg cm-2 (dry mass). The test cell used a Celgard 2400 membrane as the separator and lithium metal foil as the counter electrode. The electrolyte solution was 1M LiPF6 in a mixed solvent of ethylene carbonate, dimethyl carbonate, and diethyl carbonate (1:1:1 by volume). The cell was assembled in an Ar-filled M Braun glove box with both water moisture and oxygen contents kept ≤1 ppm.

The galvanostatic charge-discharge measurement was performed at different currents within a potential range of 2.3–3.8 V (vs. Li+/Li) on a LAND CT2001A battery test system

(LANHE,

electrochemical

Wuhan,

impedance

China). Cyclic voltammetry (CV) curves and spectra

(EIS)

were

collected

on

a

CHI660E

electrochemical working station (Chenhua, Shanghai, China). CV was scanned over a potential range of 2.5–4.2 V. The scan rates were 0.1, 0.2, 0.5, 1.0, and 2.0 mV s-1, respectively. EIS was tested in the frequency range of 105 to 10−2 Hz with an amplitude potential of 5 mV at open circuit voltage.

6 ACS Paragon Plus Environment

Page 7 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

3. Results and Discussion Scheme 1. Synthesis of LFP/G.

The preparation process of LFP/G is illustrated in Scheme 1. Compared with GO or rGO, the graphene used here has fewer oxygen-containing groups with an oxygen content of 5.9 atom% with hydroxyl (-OH) as the primary oxygen-containing group. The single layer graphene percentage is >90% and lateral size ranges from 0.5-5 µm.32 Branched PEI, with abundant amine end groups, is an ideal crosslinking agent to the graphene and the precursors and negatively charged nanoparticles.35, 36 PEI associates with the graphene through the hydrogen bonding between amine groups and hydroxyl groups. The protonated PEI attracts phosphate anion groups around. This helps the deposition of Li3PO4 and Fe3(PO4)2 on the graphene. Following a “dissolution–nucleation–crystallization” mechanism,37 LiFePO4 nanoplatelets were formed in-situ on PEI modified graphene during the solvothermal process. Note that the restacking of graphene is well inhibited due to the electrostatic repulsion of the

7 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

adsorbed cationic PEI. It is noteworthy that the hydroxyl density on the graphene is too low to absorb the precursor or the LiFePO4 nanoparticle, blocking the direct growth of LiFePO4 on graphene. As shown in Figure S1a, for the sample synthesized without PEI, the white LiFePO4 nanoplatelets were separated out from the graphene suspension after centrifugation. In contrast, the presence of PEI enables LiFePO4 and graphene to effectively couple together, giving a clean supernatant after centrifugation (Figure S1b).

Impurities, like Fe2P and Li+−Fe2+ anti-site defects, strongly affect the LiFePO4 performance.38, 39 The crystalline structure of the synthesized LFP/G and LFP were checked by XRD (Figure 1). All the peaks in the two XRD profiles were assigned to those of the standard olivine LiFePO4 with the space group Pnma (JCPDS 83-2092), indicating that PEI and graphene do not influence the phase purity of LiFePO4.

Figure 1. XRD profiles of LFP/G (a) and LFP (b). The standard diffraction profile (c) is indexed from the space group Pnma.

The morphologies of LFP/G and LFP were examined by SEM and TEM (Figure 2). The synthesized LiFePO4 nanoplatelets are mainly rectangular in shape, with about 8 ACS Paragon Plus Environment

Page 8 of 26

Page 9 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

150~200 nm in length, 50~100 nm in width, and 20~30 nm in height. The nanoplatelets severely aggregated, which hinders an efficient ion diffusion and conductive additives incorporation. In contrast, for LFP/G, LiFePO4 nanoplatelets are well dispersed on graphene, demonstrating the advantage of graphene as a growing substrate. Acidic environment favors the developing of (100)-oriented LiFePO4 nanoplatelets.37, 40-43

He et al. proposed that at low pH value, LiFePO4 crystal prefers to absorb anions

which favors the developing of (100) facet; at high pH value, LiFePO4 prefers to absorb ethylene glycol or water molecules, which favors the developing of (010) facet.40 In this work, the acidic environment was generated by the H3PO4 excess to LiOH (i.e., molar ratio LiOH / H3PO4=2.7:1) and the addition of ascorbic acid. HRTEM was used to analyze the oriented growth of the LiFePO4 nanocrystal. Revealed by the fringe spacing (Figure 3), LiFePO4 nanoplatelets in LFP and LFP/G share the predominant (100) face exposed. Carbon content was calculated from TGA,44 as shown in Figure S2. LFP/G contained 3.5 wt% carbon and LFP 2 wt%. The graphene content here was about 1.5 wt%, rather small compared with those reported in the literatures.19, 45

9 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 26

Figure 2. SEM (a, c) and TEM (b, d) images of LFP (a, b) and LFP/G (c, d).

Figure 3. HRTEM and their corresponding FFT (right) images of (a) LFP and (b) LFP/G composite.

10 ACS Paragon Plus Environment

Page 11 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Electrochemical performances of LFP/G and LFP were evaluated by galvanostatic charge-discharge measurements. Figure 4a shows typical charge and discharge profiles of LFP/G and LFP at a low rate of 0.2 C (0.034 A g-1). The discharge capacity of LFP/G (∼154 mAh g−1) is slightly smaller than that of LFP (∼156 mAh g−1). This is attributed to that the carbon content in LFP/G (3.5 wt%) is higher than that in LFP (2 wt%), as the specific capacities here were calculated based on the total mass of LFP or LFP/G.

For the galvanostatic measurement at 0.2 C, LFP/G shows less polarization, revealed by a smaller potential difference between the charge and discharge plateaus (24 mV) than LFP (38 mV) (Figure 4a, the inset). This indicates the electrochemical kinetics of LFP/G is better than that of LFP.

The electrochemical performances of LFP are highly related to the exposed crystal facet.17-19, 21, 23, 26, 45-47 (100) facet-oriented LiFePO4 nanoplatelets were reported to be of good rate performance, delivering a discharge capacity of about 122 mAh g−1 at 20 C.43 Here LFP shows comparable rate performance, with a discharge capacity of 129 mAh g−1 at 10 C, and 120 mAh g−1 at 20 C (Figure 4b). With the assistant of highly conductive pristine graphene network, the rate performance is greatly enhanced. LFP/G delivers a discharge capacity of 143 mAh g-1 at 10 C (10.8% higher than LFP), and 137 mAh g−1 at 20 C (14% higher than LFP). The rate performance of LFP/G cathode (10 C/ 0.2 C=93%) is better than those using rGO (68-88%).14, 15, 18, 19, 21-23, 45, 47, 48, 49

The capacity at 10 C of LFP/G is comparable with the reported best results 11 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

with complex preparation processing (147-162 mAh g-1).25,

Page 12 of 26

50, 51

A comparison is

given in Table S1.

Good rate performance asks for shorter charging time while keeping a good capacity retention. For LFP/G, it took 5.0 minutes to complete a galvanostatic charge process at 10 C, and another 0.5 minutes in the subsequent constant voltage charging process (Figure S3). The capacity retention reaches ∼ 93% (based on the capacity at 0.2 C) under a total charging time of 5.5 minutes. Moreover, when the charge rate was increased to 20 C, the capacity retention can still reach ~89% with a charging time of 172 s (Figure S4). Also, the cycling stability of LFP/G is obviously better than LFP. Figure 4c shows their cycling performances at 10 C (1.7 A g-1). LFP/G retains 90% of the initial capacity after 500 cycles, while LFP only 80%.

12 ACS Paragon Plus Environment

Page 13 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Figure 4. Electrochemical properties of LFP/G and LFP. (a) Galvanostatic charge and discharge profiles at 0.2 C. (b) Rate performance at current densities from 0.2 C to 20 C. (c) Cycling performance and Coulombic efficiency at 10 C in 500 cycles.

CV scan was implemented to further study their electrochemical properties (Figure 5). Figure 5a shows the CV curves at a low scan rate of 0.1 mV s−1 over a potential range of 2.5–4.2 V (versus Li+/Li). For LFP/G and LFP, there are only a pair of 13 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 26

oxidation/reduction peaks, indicating the two-phase charge/discharge reaction of LiFePO4 and FePO4.52 Compared with LFP, LFP/G shows a higher peak current intensity and a smaller potential difference between the charging and discharging peaks (146 mV), demonstrating the improved electrode kinetics and reversibility.53 Figure 5b and 5c show the CV curves at scan rates from 0.1 to 2.0 mV s−1. The potential separation between the oxidation and reduction peaks increases with the scan rate, indicating the polarization increases with charge/discharge current densities. For both cells, it was found that the peak current densities (Ip/mass, in the unit of A g-1) were proportional to the square root of scan rate v (Figure 5b and 5c, the inset). This indicates the oxidation/reduction reaction is reversible.54 Randles−Sevcik equation describes the relationship between Ip/mass and v as follows:53, 55 Ip/mass = 2.69×105n3/2AD1/2v1/2C

(1)

where n is the number of electrons transferred per molecule (here n=1), and A is the active surface area per unit mass of the electrode (cm2 g-1), and C is the initial concentration of lithium ions in LiFePO4 crystal (mol cm-3) which is deemed to be the same for LFP and LFP/G, and D is the Li+ diffusion coefficient (cm2 s-1).

From Eq. 1, we can conclude that the electrochemical reaction in the cathode is more efficient in the electrode when the slope of the plot of Ip and v1/2 is larger.22, 45 We analyzed the Ip at the discharge process (Figure 5). LFP/G shows a slope of 4.0, larger than that of LFP (3.3) (Figure 5b and 5c, inset), which agrees with the rate performance in Figure 4b. 14 ACS Paragon Plus Environment

Page 15 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Figure 5. Normalized CV curves. (a) Comparison of the LFP and LFP/G at the low scan rate of 0.1 mV s−1. (b, c) CV curves of LFP (b) and LFP/G composite (c) at different scan rates (v) from 0.1 to 2.0 mV s−1. The insets are the corresponding plots of extracted Ip/mass and v1/2.

To gain an intuitive understanding of the lithium ion transport kinetics and the involved resistances, EIS measurement was carried out (Figure 6). The charging or 15 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 26

discharging state affects the EIS results.10, 56 Here EIS was implemented at 50% of discharge state, which is in the discharge plateaus region.57 The obtained Nyquist plots consisted of a depressed semicircle in the high-middle frequency region and a straight line with a slope of ~1 in the low-frequency region. The semicircle reflects the charge transfer resistance (Rct) at the electrolyte-electrode interface. The straight line is related to the Warburg diffusion element (Zw) of lithium ions in the solid electrode.10 Rct for LFP and LFP/G were found to be 62.7 and 52.4 Ω, analyzed by ZView program based on the equivalent circuit in Figure 6a, respectively.58, 59 The decreased Rct value indicates that the charge transfer is improved in LFP/G composite. LFP/G also displays a smaller ohm resistance Rs (3.43Ω) than LFP (3.82 Ω). Besides, the lithium ion diffusion coefficient D can be calculated as follows:60

D = R2T2/(2A2n4F4C2σw2)

(2)

in which R is the gas constant, and T is the absolute temperature (300 K here), and F is the Faraday constant, and A, n, and C are given in Eq. 1, and σw is the Warburg impedance coefficient (ohm Hz1/2) related to real part of impedance Z'. In the low-frequency range, Z' can be written as,57, 58

Z' = Rs + Rct +(2π)-1/2σwf (−1/2)

(3)

where f is the frequency and Rs is the ohm resistance. Thus σw can be calculated from the plot of Z' and f

(-1/2)

. Figure 6b shows that the slope of the plot of LFP was 2.8

times that of LFP/G. Thus AD1/2 of LFP/G is 2.8 times that of LFP. Note that in the 16 ACS Paragon Plus Environment

Page 17 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

CV results analyzed by Randles−Sevcik equation, the fitted AD1/2 is 1.2 times that of LFP (Figure 5b,c). Both results indicate a superior electrochemical kinetics of LFP/G to LFP. This can be attributed to that the high-speed electron pathway of the graphene network, which also effectively reduces the aggregation of LiFePO4 nanoplatelets and thus increases their accessible surface area and improves the ion diffusion.

Figure 6. (a) Nyquist plots and the corresponding fitting plots. The inset is the applied equivalent circuit. (b) The plots of Z' and f (-1/2). The slopes of the linearly fitted curves are 6.61 and 2.36 for LFP and LFP/G, respectively.

4. Conclusions

17 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 26

In summary, the strongly coupled LiFePO4-pristine-graphene composite has been prepared through a solvothermal method. With the assistance of branched PEI, (100) facet-oriented LiFePO4 nanoplatelets in situ grow on pristine graphene with high crystalline integrity. The 3D graphene conductive network pronouncedly decreases the internal resistance of the electrode and enhance its electrochemical kinetics. As a result, LFP/G delivers a specific capacity of 143 mAh g−1 at 10 C, and 137 mAh g−1 at 20 C. So far as we know, LFP/G holds the highest capacity retention of 93% (10 C / 0.2 C). The composite can be charged within 5.5 minutes with a capacity efficiency of 93%, and 172 s of ∼ 89%. LFP/G promises for industrial production of cathode materials in EVs.

ASSOCIATED CONTENT

Supporting Information.

SI 1. Centrifugation results showing the association between LiFePO4 and graphene

SI 2. TGA profiles

SI 3,4. Fast charging profiles. The following file is available free of charge. (pdf)

AUTHOR INFORMATION

18 ACS Paragon Plus Environment

Page 19 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Corresponding Author *Email: [email protected]

Author Contributions ‡These authors contributed equally.

ACKNOWLEDGEMENT This work was supported by the 973 project (2011CB605702), Shanghai key basic research project (14JC1400600) and the National Science Foundation of China (51173027).

REFERENCES (1) Tang, Y. X.; Zhang, Y. Y.; Li, W. L.; Ma, B.; Chen, X. D. Rational Material Design for Ultrafast Rechargeable Lithium-Ion Batteries. Chem. Soc. Rev. 2015, 44, 5926-5940. (2) Myung, S. T.; Amine, K.; Sun, Y. K. Nanostructured Cathode Materials for Rechargeable Lithium Batteries. J. Power Sources 2015, 283, 219-236. (3) Wang, Y.; He, P.; Zhou, H. Olivine LiFePO4: Development and Future. Energy Environ. Sci. 2011, 4, 805-817. (4) Park, O. K.; Cho, Y.; Lee, S.; Yoo, H.-C.; Song, H.-K.; Cho, J. Who Will Drive Electric Vehicles, Olivine or Spinel? Energy Environ. Sci. 2011, 4, 1621-1633. (5) Wang, J.; Sun, X. Olivine LiFePO4: The Remaining Challenges for Future Energy Storage. Energy Environ. Sci. 2015, 8, 1110-1138. (6) Eftekhari, A. LiFePO4/C Nanocomposites for Lithium-Ion Batteries. J. Power Sources 2017, 343, 395-411. (7) Chen, C. J.; Zhang, Y.; Li, Y. J.; Kuang, Y. D.; Song, J. W.; Luo, W.; Wang, Y. B.; Yao, Y. G.; Pastel, G.; Xie, J.; Hu, L. B. Highly Conductive, Lightweight, Low-Tortuosity Carbon Frameworks as Ultrathick 3D Current Collectors. Adv. Energy Mater. 2017, 7, 8. 19 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 26

(8) Liu, Y. L.; Liu, J.; Wang, J. J.; Banis, M. N.; Xiao, B. W.; Lushington, A.; Xiao, W.; Li, R. Y.; Sham, T. K.; Liang, G. X.; Sun, X. L. Formation of Size-Dependent and Conductive Phase on Lithium Iron Phosphate During Carbon Coating. Nat. Commun. 2018, 9, 8. (9) Jokar, A.; Desilets, M.; Lacroix, M.; Zaghib, K. Mesoscopic Modeling and Parameter Estimation of a Lithium-Ion Battery Based on LiFePO4/Graphite. J. Power Sources 2018, 379, 84-90. (10) Prosini, P. P.; Lisi, M.; Zane, D.; Pasquali, M. Determination of the Chemical Diffusion Coefficient of Lithium in LiFePO4. Solid State Ionics 2002, 148, 45-51. (11) Chung, S. Y.; Bloking, J. T.; Chiang, Y. M. Electronically Conductive Phospho-Olivines as Lithium Storage Electrodes. Nat. Mater. 2002, 1, 123-128. (12) Deng, S. X.; Wang, H.; Liu, H.; Liu, J. B.; Yan, H. Research Progress in Improving the Rate Performance of LiFePO4 Cathode Materials. Nano-Micro Lett. 2014, 6, 209-226. (13) Doeff, M. M.; Wilcox, J. D.; Kostecki, R.; Lau, G. Optimization of Carbon Coatings on LiFePO4. J. Power Sources 2006, 163, 180-184. (14) Ding, Y.; Jiang, Y.; Xu, F.; Yin, J.; Ren, H.; Zhuo, Q.; Long, Z.; Zhang, P. Preparation of Nano-Structured LiFePO4/Graphene Composites by Co-Precipitation Method. Electrochem. Commun. 2010, 12, 10-13. (15) Zhou, X. F.; Wang, F.; Zhu, Y. M.; Liu, Z. P. Graphene Modified LiFePO4 Cathode Materials for High Power Lithium Ion Batteries. J. Mater. Chem. 2011, 21, 3353-3358. (16) Xu, H.; Chang, J.; Sun, J.; Gao, L. Graphene-Encapsulated LiFePO4 Nanoparticles with High Electrochemical Performance for Lithium Ion Batteries. Mater. Lett. 2012, 83, 27-30. (17) Tian, Z.; Liu, S.; Ye, F.; Yao, S.; Zhou, Z.; Wang, S. Synthesis and Characterization of LiFePO4 Electrode Materials Coated by Graphene. Appl. Surface Sci. 2014, 305, 427-432. (18) Ding, B.; Ji, G.; Sha, Z.; Wu, J. S.; Lu, L.; Lee, J. Y. Dual-Carbon Network for the Effective Transport of Charged Species in a LiFePO4 Cathode for Lithium-Ion Batteries. Energy Technol-Ger 2015, 3, 63-69. (19) Wang, B.; Wang, S.; Liu, P.; Deng, J.; Xu, B. H.; Liu, T. F.; Wang, D. L.; Zhao, X. S. Growth of LiFePO4 Nanoplatelets with Orientated (010) Facets on Graphene for 20 ACS Paragon Plus Environment

Page 21 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

Fast Lithium Storage. Mater. Lett. 2014, 118, 137-141. (20) Wu, G.; Ran, R.; Zhao, B.; Sha, Y.; Su, C.; Zhou, Y.; Shao, Z. 3d Amorphous Carbon and Graphene Co-Modified LiFePO4 Composite Derived from Polyol Process as Electrode for High Power Lithium-Ion Batteries. Journal of Energy Chemistry 2014, 23, 363-375. (21) Ha, S. H.; Lee, Y. J. Core-Shell LiFePO4/Carbon-Coated Reduced Graphene Oxide Hybrids for High-Power Lithium-Ion Battery Cathodes. Chem. Eur. J. 2015, 21, 2132-2138. (22) Tang, H.; Si, Y.; Chang, K.; Fu, X.; li, B.; Shangguan, E.; Chang, Z.; Yuan, X.-Z.; Wang, H. Carbon Gel Assisted Low Temperature Liquid-Phase Synthesis of CLiFePO4/Graphene Layers with High Rate and Cycle Performances. J. Power Sources 2015, 295, 131-138. (23) Wu, K. P.; Hu, G. R.; Du, K.; Peng, Z. D.; Cao, Y. B. Improved Electrochemical Properties of LiFePO4/Graphene/Carbon Composite Synthesized from FePO4·2H2O/Graphene Oxide. Ceram. Int. 2015, 41, 13867-13871. (24) Yu, F.; Zhang, L.; Lai, L.; Zhu, M.; Guo, Y.; Xia, L.; Qi, P.; Wang, G.; Dai, B. High Electrochemical Performance of LiFePO4 Cathode Material via in-situ Microwave Exfoliated Graphene Oxide. Electrochim. Acta 2015, 151, 240-248. (25) Zhang, K.; Lee, J. T.; Li, P.; Kang, B.; Kim, J. H.; Yi, G. R.; Park, J. H. Conformal Coating Strategy Comprising N-Doped Carbon and Conventional Graphene for Achieving Ultrahigh Power and Cyclability of LiFePO4. Nano Lett. 2015, 15, 6756-6763. (26) Lim, J.; Gim, J.; Song, J.; Dang Thanh, N.; Kim, S.; Jo, J.; Mathew, V.; Kim, J. Direct Formation of LiFePO4/Graphene Composite Via Microwave-Assisted Polyol Process. J. Power Sources 2016, 304, 354-359. (27) Oh, J.; Lee, J.; Hwang, T.; Kim, J. M.; Seoung, K. D.; Piao, Y. Dual Layer Coating Strategy Utilizing N-Doped Carbon and Reduced Graphene Oxide for High-Performance LiFePO4 Cathode Material. Electrochim. Acta 2017, 231, 85-93. (28) Wu, Z. S.; Xue, L. L.; Ren, W. C.; Li, F.; Wen, L.; Cheng, H. M. A Lif Nanoparticle‐Modified Graphene Electrode for High‐Power and High‐Energy Lithium Ion Batteries. Adv. Funct. Mater. 2012, 22, 3290-3297. (29) Wu, Z. S.; Ren, W. C.; Wen, L.; Gao, L. B.; Zhao, J. P.; Chen, Z. P.; Zhou, G. M.; Li, F.; Cheng, H. M. Graphene Anchored with Co3O4 Nanoparticles as Anode of Lithium Ion Batteries with Enhanced Reversible Capacity and Cyclic Performance. 21 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 26

ACS Nano 2010, 4, 3187-3194. (30) Fan, X.; Peng, W.; Li, Y.; Li, X.; Wang, S.; Zhang, G.; Zhang, F. Deoxygenation of Exfoliated Graphite Oxide under Alkaline Conditions: A Green Route to Graphene Preparation. Adv. Mater. 2008, 20, 4490-4493. (31) Hu, L. H.; Wu, F. Y.; Lin, C. T.; Khlobystov, A. N.; Li, L. J. Graphene-Modified LiFePO4 Cathode for Lithium Ion Battery Beyond Theoretical Capacity. Nat. Commun. 2013, 4, 7. (32) Dong, L.; Chen, Z.; Zhao, X.; Ma, J.; Lin, S.; Li, M.; Bao, Y.; Chu, L.; Leng, K.; Lu, H.; Loh, K. P. A Non-Dispersion Strategy for Large-Scale Production of Ultra-High Concentration Graphene Slurries in Water. Nat. Commun. 2018, 9. (33) Parvez, K.; Wu, Z. S.; Li, R. J.; Liu, X. J.; Graf, R.; Feng, X. L.; Müllen, K. Exfoliation of Graphite into Graphene in Aqueous Solutions of Inorganic Salts. J. Am. Chem. Soc. 2014, 136, 6083-6091. (34) Wu, Z. S.; Zheng, Y. J.; Zheng, S. H.; Wang, S.; Sun, C. L.; Parvez, K.; Ikeda, T.; Bao, X. H.; Klaus, M.; Feng, X. L. Stacked-Layer Heterostructure Films of 2d Thiophene Nanosheets and Graphene for High-Rate All-Solid-State Pseudocapacitors with Enhanced Volumetric Capacitance. Adv. Mater. 2017, 29, 1602960. (35) Gao, X.; Li, Y.; Zhang, Q.; Li, S.; Chen, Y.; Lee, J.-M. Polyethyleneimine-Assisted Synthesis of High-Quality Platinum/Graphene Hybrids: The Effect of Molecular Weight on Electrochemical Properties. J. Mater. Chem. A 2015, 3, 12000-12004. (36) Li, J.; Zhou, P.; Li, F.; Ma, J.; Liu, Y.; Zhang, X.; Huo, H.; Jin, J.; Ma, J. Shape-Controlled Synthesis of Pd Polyhedron Supported on Polyethyleneimine-Reduced Graphene Oxide for Enhancing the Efficiency of Hydrogen Evolution Reaction. J. Power Sources 2016, 302, 343-351. (37) Wang, L.; He, X. M.; Sun, W. T.; Wang, J. L.; Li, Y. D.; Fan, S. S. Crystal Orientation Tuning of LiFePO4 Nanoplates for High Rate Lithium Battery Cathode Materials. Nano Lett. 2012, 12, 5632-5636. (38) Arnold, G.; Garche, J.; Hemmer, R.; Strobele, S.; Vogler, C.; Wohlfahrt-Mehrens, A. Fine-Particle Lithium Iron Phosphate LiFePO4 Synthesized by a New Low-Cost Aqueous Precipitation Technique. J. Power Sources 2003, 119, 247-251. (39) Chen, J. J.; Whittingham, M. S. Hydrothermal Synthesis of Lithium Iron Phosphate. Electrochem. Commun. 2006, 8, 855-858. 22 ACS Paragon Plus Environment

Page 23 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

(40) Huang, X. K.; He, X. M.; Jiang, C. Y.; Tian, G. Y. Morphology Evolution and Impurity Analysis of LiFePO4 Nanoparticles via a Solvothermal Synthesis Process. RSC Adv. 2014, 4, 56074-56083. (41) Dokko, K.; Koizumi, S.; Nakano, H.; Kanamura, K. Particle Morphology, Crystal Orientation, and Electrochemical Reactivity of LiFePO4 Synthesized by the Hydrothermal Method at 443 K. J. Mater. Chem. 2007, 17, 4803-4810. (42) Li, Z.; Zhu, K.; Li, J.; Wang, X. Morphological and Orientational Diversity of LiFePO4 Crystallites: Remarkable Reaction Path Dependence in Hydrothermal/Solvothermal Syntheses. CrystEngComm 2014, 16, 10112-10122. (43) Li, Z.; Peng, Z.; Zhang, H.; Hu, T.; Hu, M.; Zhu, K.; Wang, X. 100-Oriented LiFePO4 Nanoflakes toward High Rate Li-Ion Battery Cathode. Nano Lett. 2016, 16, 795-799. (44) Belharouak, I.; Johnson, C.; Amine, K. Synthesis and Electrochemical Analysis of Vapor-Deposited Carbon-Coated LiFePO4. Electrochem. Commun. 2005, 7, 983-988. (45) Wang, B.; Liu, A.; Abdulla, W. A.; Wang, D.; Zhao, X. S. Desired Crystal Oriented LiFePO4 Nanoplatelets in Situ Anchored on a Graphene Cross-Linked Conductive Network for Fast Lithium Storage. Nanoscale 2015, 7, 8819-8828. (46) Bi, H.; Huang, F.; Tang, Y.; Liu, Z.; Lin, T.; Chen, J.; Zhao, W. Study of LiFePO4 Cathode Modified by Graphene Sheets for High-Performance Lithium Ion Batteries. Electrochim. Acta 2013, 88, 414-420. (47) Wei, W.; Gao, S.; Yang, Z.; Guo, L. Porous Micro-Spherical LiFePO4/Graphene Nanocomposites for High-Performance Li Ion Battery Cathode Materials. RSC Adv. 2014, 4, 56701-56706. (48) Tian, X.; Zhou, Y.; Tu, X.; Zhang, Z.; Du, G. Well-Dispersed LiFePO4 Nanoparticles Anchored on a Three-Dimensional Graphene Aerogel as High-Performance Positive Electrode Materials for Lithium-Ion Batteries. J. Power Sources 2017, 340, 40-50. (49) Wei, X.; Guan, Y.; Zheng, X.; Zhu, Q.; Shen, J.; Qiao, N.; Zhou, S.; Xu, B. Improvement on High Rate Performance of LiFePO4 Cathodes Using Graphene as a Conductive Agent. Appl. Surface Sci. 2018, 440, 748-754. (50) Kang, B.; Ceder, G. Battery Materials for Ultrafast Charging and Discharging. Nature 2009, 458, 190-193. 23 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 26

(51) Li, J.; Zhang, L.; Zhang, L.; Hao, W.; Wang, H.; Qu, Q.; Zheng, H. In-Situ Growth of Graphene Decorations for High-Performance LiFePO4 Cathode through Solid-State Reaction. J. Power Sources 2014, 249, 311-319. (52) Padhi, A. K.; Nanjundaswamy, K. S.; Goodenough, J. B. Phospho-Olivines as Positive-Electrode Materials for Rechargeable Lithium Batteries. J. Electrochem. Soc. 1997, 144, 1188-1194. (53) Cho, Y. D.; Fey, G. T. K.; Kao, H. M. The Effect of Carbon Coating Thickness on the Capacity of LiFePO4/C Composite Cathodes. J. Power Sources 2009, 189, 256-262. (54) Yu, D. Y. W.; Fietzek, C.; Weydanz, W.; Donoue, K.; Inoue, T.; Kurokawa, H.; Fujitani, S. Study of LiFePO4 by Cyclic Voltammetry. J. Electrochem. Soc. 2007, 154, A253-A257. (55) Yu, L.; Liu, J.; Xu, X.; Zhang, L.; Hu, R.; Liu, J.; Yang, L.; Zhu, M. Metal– Organic Framework-Derived NiSb Alloy Embedded in Carbon Hollow Spheres as Superior Lithium-Ion Battery Anodes. ACS Appl. Mater. Inter. 2017, 9, 2516-2525. (56) Feng, L.; Xu, X.; Shui, M.; Zheng, W.; Shu, J.; Hui, L.; Xu, L.; Chen, L.; Ren, Y. The Potential Dependent Electrochemical Impedance Spectroscopy and Lithium Diffusion Kinetics of LiFePO4. Solid State Ionics 2014, 265, 49-54. (57) Wang, G. L.; Ma, Z. P.; Shao, G. J.; Kong, L. X.; Gao, W. M. Synthesis of LiFePO4@Carbon Nanotube Core-Shell Nanowires with a High-Energy Efficient Method for Superior Lithium Ion Battery Cathodes. J. Power Sources 2015, 291, 209-214. (58) Zheng, F.; Yang, C.; Ji, X.; Hu, D.; Chen, Y.; Liu, M. Surfactants Assisted Synthesis and Electrochemical Properties of Nano- LiFePO4/C Cathode Materials for Low Temperature Applications. J. Power Sources 2015, 288, 337-344. (59) Zhang, J. L.; Nie, N.; Liu, Y. Y.; Wang, J.; Yu, F.; Gu, J. J.; Li, W. Boron and Nitrogen Codoped Carbon Layers of LiFePO4 Improve the High-Rate Electrochemical Performance for Lithium Ion Batteries. ACS Appl. Mater. Inter. 2015, 7, 20134-20143. (60) Ho, C.; Raistrick, I. D.; Huggins, R. A. Application of Ac Techniques to the Study of Lithium Diffusion in Tungsten Trioxide Thin-Films. J. Electrochem. Soc. 1980, 127, 343-350.

24 ACS Paragon Plus Environment

Page 25 of 26 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Energy Materials

25 ACS Paragon Plus Environment

ACS Applied Energy Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 26

TOC

LiFePO4 anchored on pristine graphene was prepared with the assistance of branched polyethyleneimine. The composite delivers a specific capacity of 143 mAh g−1 at 10 C (1.7 A g−1), and 137 mAh g−1 at 20 C (3.4 A g−1). It retains a capacity retention of ∼ 89% when charged in 172 s.

26 ACS Paragon Plus Environment