Magnetization and resistance switchings induced by electric field in epitaxial Mn:ZnO/BiFeO3 multiferroic heterostructures at room temperature Dong Li, Wanchao Zheng, Dongxing Zheng, Junlu Gong, Liyan Wang, Chao Jin, Peng Li, and Haili Bai ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.5b11265 • Publication Date (Web): 26 Jan 2016 Downloaded from http://pubs.acs.org on February 1, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Magnetization and Resistance Switchings Induced by Electric Field in Epitaxial Mn:ZnO/BiFeO3 Multiferroic Heterostructures at Room Temperature

Dong Li, Wanchao Zheng, Dongxing Zheng, Junlu Gong, Liyan Wang, Chao Jin, Peng Li, and Haili Bai*

Tianjin Key Laboratory of Low Dimensional Materials Physics and Preparing Technology, Institute of Advanced Materials Physics, Faculty of Science, Tianjin University, Tianjin 300072, PRC

*

Author to whom all correspondence should be addressed. E-mail: [email protected]

−1−

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT

Electric field induced reversible switchings of the magnetization and resistance were achieved at room temperature in epitaxial Mn:ZnO(110)/BiFeO3(001) heterostructures. The observed modulation of magnetic moment is ~500% accompanying with a coercive field varying from 43 to 300 Oe and a resistive switching ratio up to ~104% with the applied voltages of ±4 V. The switching mechanisms in magnetization and resistance are attributed to the ferroelectric polarization reversal of the BiFeO3 layer under applied electric fields, combined with the reversible change of oxygen vacancy concentration at the Mn:ZnO/BiFeO3 interface.

PACS: 75.70.Cn, 75.50.Pp, 75.85.+t

Keywords: magnetization reversal, multiferroic heterosutructures, magnetoelectric coupling effect, bismuth ferrite, zinc oxide films

−2−

ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

 INTRODUCTION

Multiferroic materials have been proposed to meet the demands for higher memory speed and density with low energy assumption in next generation information technologies and systems.1−5 The converse magnetoelectric (ME) effect makes it possible to control magnetism with electric fields rather than electric currents or magnetic fields, thus achieving electric-writing and magnetic-reading.6 ME coupling in single-phase multiferroics is often too weak and only occurs in very low temperatures, which severely limits its practical application. Up to now, many efforts especially which combines room temperature ferromagnetic (FM) and ferroelectric (FE) materials have been made to explore new possibilities of electrical tunable magnetization in thin film systems.3 For instance, to achieve electric-field control of magnetization in multiferroic materials or structures, ME effects are mainly studied in the exchange bias (EB), strain or charge mediated couplings of transition metal and oxide ferromagnets to ferroelectrics or multiferroics.7−12 To date, electric field control of magnetism by exchange coupling has been accomplished in CoFe/BiFeO3 and La0.7Sr0.3MnO3/BiFeO3 structures.8–10 Even so, the applied in-plane electric field in the CoFe/BiFeO3 structure is unfavorable for high density storage, and the blocking temperature (100 K) of exchange bias in the La0.7Sr0.3MnO3/BiFeO3 structure is much lower than room temperature. In strain mediated FM-FE systems, the piezoelectric strain of the FE layer −3−

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

can be transferred to the FM layer, which would result in converse ME effects.11, 12 But the induced strain effect is hard to retain without continuous voltage. Remnant polarization as a dual effect offers the possibility of nonvolatile and reversible switching of magnetization and resistance in the charge-mediated ME systems.13, 14 Charge carriers are repelled or attracted by ferroelectric polarization, which will change the charge-related magnetic and electronic transport properties. BiFeO3 (BFO) is one of the most potential lead-free ferroelectric materials and the only room-temperature multiferroic material.9, 15 The discovery of its high remnant polarization in thin films has attracted much close attention for its great potential applications in nonvolatile memory and spintronics.16−20 Recently, tetragonal-like BiFeO3 (T-BFO) films have been unveiled a giant polarization up to 150 µC/cm2, which is related to its large axial ratio ( c / a ≈ 1.24 ).21, 22 T-BFO films can be fabricated in highly strained films (e.g.