Mapping Nanoscale Hotspots with Single-Molecule Emitters

Nov 22, 2017 - Fabricating nanocavities in which optically active single quantum emitters are precisely positioned is crucial for building nanophotoni...
1 downloads 20 Views 1MB Size
Download PDF
Subscriber access provided by READING UNIV

Communication

Mapping nanoscale hotspots with single-molecule emitters assembled into plasmonic nanocavities using DNA origami Rohit Chikkaraddy, V A Turek, Nuttawut Kongsuwan, Felix Benz, Cloudy Carnegie, Tim Van De Goor, Bart de Nijs, Angela Demetriadou, Ortwin Hess, Ulrich F Keyser, and Jeremy J. Baumberg Nano Lett., Just Accepted Manuscript • DOI: 10.1021/acs.nanolett.7b04283 • Publication Date (Web): 22 Nov 2017 Downloaded from http://pubs.acs.org on November 22, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Nano Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Mapping nanoscale hotspots with single-molecule emitters assembled into plasmonic nanocavities using DNA origami Rohit Chikkaraddy1, V. A. Turek1, Nuttawut Kongsuwan2, Felix Benz1, Cloudy Carnegie1, Tim van de Goor1, Bart de Nijs1, Angela Demetriadou2, Ortwin Hess2, Ulrich F. Keyser1, and Jeremy J. Baumberg1 1

NanoPhotonics Centre, Cavendish Laboratory, Department of Physics, JJ Thompson Avenue, University of Cambridge, Cambridge, CB3 0HE, United Kingdom 2 Blackett Laboratory, Prince Consort Road, Imperial College London, London SW7 2AZ, UK

KEYWORDS: Single-molecule, DNA origami, Plasmonics, Nanocavities, Nano-assembly, Purcell factor, Strong coupling, and SERS.

ABSTRACT. Fabricating nanocavities in which optically-active single quantum emitters are precisely positioned, is crucial for building nanophotonic devices. Here we show that self-assembly based on robust DNA-origami constructs can precisely position single molecules laterally within sub-5nm gaps between plasmonic substrates that support intense optical confinement. By placing single-molecules at the center of a nanocavity, we show modification of the plasmon cavity resonance before and after bleaching the chromophore, and obtain enhancements of ≥ 4×103 with high quantum yield (≥ 50%). By varying the lateral position of the molecule in the gap, we directly map the spatial profile of the local density of optical states with a resolution of ±1.5 nm. Our approach introduces a straightforward non-invasive way to measure and quantify confined optical modes on the nanoscale. Coherent coupling of light and single-molecules at room temperature is one of the fundamental goals of nano-optics that would enable widespread adoption as a building block of nanophotonic devices. Over the past decade many constructs have been designed to enhance the coupling of single-emitters, such as planar interfaces,1 near-field probes,2 photonic crystals,3,4 microcavities5 and metal nanostructures.6–8 Improved optical coupling results in Purcell enhancement of the emission rate, enhancing efficiency and both spatial and temporal mode-matching of single photon emission.9–11 Further improvement eventually leads to the strong-coupling regime where nonlinearities can reach the single photon level, an essential characteristic for many quantum devices. So far however most single-emitter strong-coupling required cooling of the system12–15 increasing cost and complexity. For room temperature nano-optics, plasmonic nanocavities have gained tremendous interest due to their enhanced field confinements.7,16–18 Integrating optically-active materials (such as molecules, quantum dots, monolayer semiconductors, or diamond vacancy centers) into these cavities is of great

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

importance to access the desired coherent interaction between optical field and exciton. Either the cavity must be fabricated around randomly located emitters such as quantum dots or nitrogen-vacancy centres,14,19,20 or emitters are randomly located inside the cavity.21 In realizing the promising hopes for molecules in plasmonic cavities, the major hurdles are: (i) robust assembly of plasmonic nanocavities with reliable nanogaps (200 µW/µm2, strong SERS signatures are identified at 1500 cm-1 corresponding to cytosine, and at 1000 cm-1 and 730 cm-1 corresponding to adenine of DNA-origami. When a single-Cy5 is present at the center of the gap the emission from the NPoM is strongly enhanced (Fig. 2h, orange). Different NPoM constructs show only minor variations in peak emission wavelength and widths (Fig. S12a). The emission of Cy5 coupled to the plasmon mode enhances the decay rates and modifies the energy levels giving larger surface-enhanced fluorescence linewidths in comparison with the ensemble emission of molecules in solution (Fig. 2h, yellow).

ACS Paragon Plus Environment

Page 6 of 14

Page 7 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 3. Emission from NPoM with single-Cy5. (a) Time-series emission spectra from a NPoM with single-Cy5 at the gap center. Inset: extracted variation in peak - and intensity (dot size) as a function of time. (b) Scattering spectra from the NPoM before (.=0 s) and after bleaching (.=30 s) the single-Cy5, with initial emission spectrum (orange). (c) Intensity over time extracted from fluorescence microscopy images (shown in inset) for single-Cy5 in NPoM (top) and ensemble Cy5 embedded in DNAo on glass (bottom). (d) Emission intensity as a function of pump power in five individual NPoMs, and for comparison a typical DNAo on glass.

Time series scans of the emission from NPoMs containing a single Cy5 show variations in peak position and intensity on timescales of seconds (Fig. 3a and Fig. S12b). The emission suddenly bleaches after a certain time, leaving only weak ILS and SERS from the NPoM (.>21 s in Fig. 3a) which is the same for the DNAo without Cy5 (Fig. 2h, grey). This confirms the presence of only one Cy5 molecule in each NPoM, as previously demonstrated for single emitters within DNAo inside plasmonic dimers.43,45 Scattering spectra obtained from the NPoM before (Fig. 3b, bottom) and after (Fig. 3b, top) the bleaching of the single-Cy5 show the expected collapse in the splitting. Intensity traces from fluorescence microscopy images of NPoMs also show these step-like features, in complete contrast to ensemble Cy5s on glass which show the gradual irreversible bleaching of molecules. We note that chemically binding Cy5 to DNA stands has

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

been shown to increase the photo-stability of the molecules.61 The average bleaching time of Cy5-DNAo on glass is /̅1 =8.5 s, whereas in these NPoMs we find /̅1 > 13 s, giving an additional two-fold increase in photo-stability. With NPoMs providing local intensity enhancements of 2345 ~ 2500 in the gap (Fig. 1c) and /1 ∝ 1/2345 , the photobleaching is actually suppressed by more than three orders of magnitude.62 The total number of photons emitted from the single dye in each NPoM before it bleaches is estimated to be 4×106, resulting in enhancement of total photon counts by factors >1000 times compared to each Cy5 in DNAo on glass. This enhancement results from combined effects of enhanced radiative emission rates, better light collection from the NPoM antenna, and suppressed bleaching rates.46,63 These behaviors fully corroborate our evidence for single molecule emission. To estimate the emission enhancement of Cy5 molecules in NPoMs we performed emission experiments for different pump powers (Fig. S13). Emission from an ensemble of Cy5 molecules on glass exhibits saturation and bleaching at >100 µW/µm2 (Fig. 3d, black curve). The emission is now integrated over a range of wavelengths (curly bracket Fig. 2h) and normalized to the counts from Cy5s in DNAo on glass considering the excitation and collection efficiencies (Suppl.Info. S14), to give the enhancement factor (EF). We find the radiative emission rate (67 /6 ) is enhanced by EF > 2×103. The coupling strength estimated from this single-Cy5 enhancement10 using + =  6 Γ (1 + 2!/Γ )/4 (with radiative linewidth ℏ/6 =1 ns64) gives values  ~50 meV which agree with those from the cavity linewidth in scattering (Fig. 2g). The emission intensity from a Cy5 coupled to a single NPoM shows linear scaling with excitation power density in the range 4-400 µW/µm2 (Fig. 3d). We estimate photon populations in the NPoM < 0.1, well below the critical cavity photon population65 for non-linear effects Γ+ / (2+ )~2. Pumping at higher excitation power densities instead gives irreversible photobleaching of the Cy5, before saturation of the excited state population can be reached. All subsequent measurements are thus conducted at excitation power densities of 50 µW/µm2. At these powers we do not see the collapse of the DNA origami core as seen in prior work45,66,67 at >500 µW/µm2.

ACS Paragon Plus Environment

Page 8 of 14

Page 9 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

Figure 4. Mapping the LDOS. Experimental variation in enhancement of emission intensity from NPoMs when laterally displacing the position of single dye molecule (orange dots). Normalized to the emission of a single Cy5 in DNAo on glass, grey box indicates standard error, statistical variations in emission intensity shown as violin plots. Solid red line is Gaussian fit to the experimental data. Theoretically calculated emission enhancements are shown for vertical (900) dipole (solid blue) and slanted dipole (450) (dashed blue). Calculated quantum efficiency for vertical dipole is shown as dashed grey line.

The EF is measured for >100 individual NPoMs for different assembled origamis. In successive designs, the spatial position  of the single-Cy5 is systematically scanned laterally within the gap (Fig. 4). As the Cy5 is moved towards the center of the gap (=0) the emission intensity increases monotonically, evidencing that the centre of the NP on the DNAo is correctly defined within ±1 nm, and that the optical field in the gap has a spatial fullwidth Δ:;5< = 6.5±2 nm. This measured intensity profile is similar to that from simulations Δ ~8 nm for facets = = 55° based on the numerical aperture of the objective.

ASSOCIATED CONTENT Supporting Information. AUTHOR INFORMATION Corresponding Author * Prof Jeremy J Baumberg, [email protected] Notes The authors declare no competing financial interest. ACKNOWLEDGMENT We acknowledge financial support from EPSRC Grants EP/G060649/1, EP/K028510/1, EP/L027151/1, ERC Grant LINASS 320503 and ERC Consolidator Grant (DesignerPores 67144). R.C. acknowledges support from the Dr. Manmohan Singh scholarship from St. John’s College. F.B. acknowledges support from the Winton Programme for the Physics of Sustainability. REFERENCES (1) (2) (3)

Lee, K. G.; Chen, X. W.; Eghlidi, H.; Kukura, P.; Lettow, R.; Renn, A.; Sandoghdar, V.; Götzinger, S. Nat. Photonics 2011, 5 (3), 166–169. Taminiau, T. H.; Stefani, F. D.; Segerink, F. B.; Hulst, N. F. van. Nat. Photonics 2008, 2 (4), 234–237. Lodahl, P.; Floris van Driel, A.; Nikolaev, I. S.; Irman, A.; Overgaag, K.; Vanmaekelbergh, D.; Vos, W. L. Nature 2004, 430 (7000), 654–657.

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(4) (5) (6) (7) (8) (9) (10) (11) (12) (13) (14) (15) (16) (17) (18) (19) (20) (21) (22) (23) (24) (25) (26) (27) (28) (29) (30) (31) (32) (33) (34)

Page 12 of 14

Englund, D.; Fattal, D.; Waks, E.; Solomon, G.; Zhang, B.; Nakaoka, T.; Arakawa, Y.; Yamamoto, Y.; Vučković, J. Phys. Rev. Lett. 2005, 95 (1), 013904. Pelton, M.; Santori, C.; Vuc̆ković, J.; Zhang, B.; Solomon, G. S.; Plant, J.; Yamamoto, Y. Phys. Rev. Lett. 2002, 89 (23), 233602. Pelton, M. Nat. Photonics 2015, 9 (7), 427–435. Schuller, J. A.; Barnard, E. S.; Cai, W.; Jun, Y. C.; White, J. S.; Brongersma, M. L. Nat. Mater. 2010, 9 (3), 193–204. Novotny, L.; van Hulst, N. Nat. Photonics 2011, 5 (2), 83–90. Purcell, E. M. Phys. Rev. 1946, 69 (11–12), 681. Khitrova, G.; Gibbs, H. M.; Kira, M.; Koch, S. W.; Scherer, A. Nat. Phys. 2006, 2 (2), 81–90. Noda, S.; Fujita, M.; Asano, T. Nat. Photonics 2007, 1 (8), 449–458. Moerner, W. E.; Orrit, M. Science 1999, 283 (5408), 1670–1676. Yoshie, T.; Scherer, A.; Hendrickson, J.; Khitrova, G.; Gibbs, H. M.; Rupper, G.; Ell, C.; Shchekin, O. B.; Deppe, D. G. Nature 2004, 432 (7014), 200–203. Hennessy, K.; Badolato, A.; Winger, M.; Gerace, D.; Atatüre, M.; Gulde, S.; Fält, S.; Hu, E. L.; Imamoğlu, A. Nature 2007, 445 (7130), 896–899. Fushman, I.; Englund, D.; Faraon, A.; Stoltz, N.; Petroff, P.; Vučković, J. Science 2008, 320 (5877), 769–772. Zhang, R.; Zhang, Y.; Dong, Z. C.; Jiang, S.; Zhang, C.; Chen, L. G.; Zhang, L.; Liao, Y.; Aizpurua, J.; Luo, Y.; Yang, J. L.; Hou, J. G. Nature 2013, 498 (7452), 82–86. Zhu, W.; Crozier, K. B. Nat. Commun. 2014, 5, 5228. Takase, M.; Ajiki, H.; Mizumoto, Y.; Komeda, K.; Nara, M.; Nabika, H.; Yasuda, S.; Ishihara, H.; Murakoshi, K. Nat. Photonics 2013, 7 (7), 550–554. Park, H.-G.; Barrelet, C. J.; Wu, Y.; Tian, B.; Qian, F.; Lieber, C. M. Nat. Photonics 2008, 2 (10), 622– 626. Akselrod, G. M.; Argyropoulos, C.; Hoang, T. B.; Ciracì, C.; Fang, C.; Huang, J.; Smith, D. R.; Mikkelsen, M. H. Nat. Photonics 2014, 8 (11), 835–840. Chikkaraddy, R.; de Nijs, B.; Benz, F.; Barrow, S. J.; Scherman, O. A.; Rosta, E.; Demetriadou, A.; Fox, P.; Hess, O.; Baumberg, J. J. Nature 2016, 535 (7610), 127–130. Aravind, P. K.; Metiu, H. Surf. Sci. 1983, 124 (2), 506–528. Ciracì, C.; Hill, R. T.; Mock, J. J.; Urzhumov, Y.; Fernández-Domínguez, A. I.; Maier, S. A.; Pendry, J. B.; Chilkoti, A.; Smith, D. R. Science 2012, 337 (6098), 1072–1074. Benz, F.; Schmidt, M. K.; Dreismann, A.; Chikkaraddy, R.; Zhang, Y.; Demetriadou, A.; Carnegie, C.; Ohadi, H.; Nijs, B. de; Esteban, R.; Aizpurua, J.; Baumberg, J. J. Science 2016, 354 (6313), 726–729. Benz, F.; de Nijs, B.; Tserkezis, C.; Chikkaraddy, R.; Sigle, D. O.; Pukenas, L.; Evans, S. D.; Aizpurua, J.; Baumberg, J. J. Opt. Express 2015, 23 (26), 33255. Benson, O. Nature 2011, 480 (7376), 193–199. Kufer, S. K.; Puchner, E. M.; Gumpp, H.; Liedl, T.; Gaub, H. E. Science 2008, 319 (5863), 594–596. Krishnan, M.; Mojarad, N.; Kukura, P.; Sandoghdar, V. Nature 2010, 467 (7316), 692–695. Hu, M.; Ou, F. S.; Wu, W.; Naumov, I.; Li, X.; Bratkovsky, A. M.; Williams, R. S.; Li, Z. J. Am. Chem. Soc. 2010, 132 (37), 12820–12822. Zheng, Y.; Soeriyadi, A. H.; Rosa, L.; Ng, S. H.; Bach, U.; Gooding, J. J. Nat. Commun. 2015, 6, 8797. Álvarez-Puebla, R. A.; Contreras-Cáceres, R.; Pastoriza-Santos, I.; Pérez-Juste, J.; Liz-Marzán, L. M. Angew. Chem. Int. Ed. 2009, 48 (1), 138–143. Taylor, R. W.; Lee, T.-C.; Scherman, O. A.; Esteban, R.; Aizpurua, J.; Huang, F. M.; Baumberg, J. J.; Mahajan, S. ACS Nano 2011, 5 (5), 3878–3887. Seeman, N. C. J. Theor. Biol. 1982, 99 (2), 237–247. Chen, J.; Seeman, N. C. Nature 1991, 350 (6319), 631–633.

ACS Paragon Plus Environment

Page 13 of 14

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Nano Letters

(35) (36)

(37)

(38) (39) (40) (41) (42) (43) (44) (45) (46) (47) (48) (49) (50) (51)

(52) (53) (54) (55)

(56)

(57) (58)

Rothemund, P. W. K. Nature 2006, 440 (7082), 297–302. Andersen, E. S.; Dong, M.; Nielsen, M. M.; Jahn, K.; Subramani, R.; Mamdouh, W.; Golas, M. M.; Sander, B.; Stark, H.; Oliveira, C. L. P.; Pedersen, J. S.; Birkedal, V.; Besenbacher, F.; Gothelf, K. V.; Kjems, J. Nature 2009, 459 (7243), 73–76. Kershner, R. J.; Bozano, L. D.; Micheel, C. M.; Hung, A. M.; Fornof, A. R.; Cha, J. N.; Rettner, C. T.; Bersani, M.; Frommer, J.; Rothemund, P. W. K.; Wallraff, G. M. Nat. Nanotechnol. 2009, 4 (9), 557–561. Hung, A. M.; Micheel, C. M.; Bozano, L. D.; Osterbur, L. W.; Wallraff, G. M.; Cha, J. N. Nat. Nanotechnol. 2010, 5 (2), 121–126. Tørring, T.; V. Voigt, N.; Nangreave, J.; Yan, H.; V. Gothelf, K. Chem. Soc. Rev. 2011, 40 (12), 5636– 5646. Voigt, N. V.; Tørring, T.; Rotaru, A.; Jacobsen, M. F.; Ravnsbæk, J. B.; Subramani, R.; Mamdouh, W.; Kjems, J.; Mokhir, A.; Besenbacher, F.; Gothelf, K. V. Nat. Nanotechnol. 2010, 5 (3), 200–203. Gopinath, A.; Miyazono, E.; Faraon, A.; Rothemund, P. W. K. Nature 2016, 535 (7612), 401–405. Ke, Y.; Lindsay, S.; Chang, Y.; Liu, Y.; Yan, H. Science 2008, 319 (5860), 180–183. Acuna, G. P.; Möller, F. M.; Holzmeister, P.; Beater, S.; Lalkens, B.; Tinnefeld, P. Science 2012, 338 (6106), 506–510. Holzmeister, P.; Pibiri, E.; Schmied, J. J.; Sen, T.; Acuna, G. P.; Tinnefeld, P. Nat. Commun. 2014, 5, 5356. Simoncelli, S.; Roller, E.-M.; Urban, P.; Schreiber, R.; Turberfield, A. J.; Liedl, T.; Lohmüller, T. ACS Nano 2016, 10 (11), 9809–9815. Pellegrotti, J. V.; Acuna, G. P.; Puchkova, A.; Holzmeister, P.; Gietl, A.; Lalkens, B.; Stefani, F. D.; Tinnefeld, P. Nano Lett. 2014, 14 (5), 2831–2836. Bidault, S.; Devilez, A.; Maillard, V.; Lermusiaux, L.; Guigner, J.-M.; Bonod, N.; Wenger, J. ACS Nano 2016, 10 (4), 4806–4815. Douglas, S. M.; Marblestone, A. H.; Teerapittayanon, S.; Vazquez, A.; Church, G. M.; Shih, W. M. Nucleic Acids Res. 2009, 37 (15), 5001–5006. Bell, N. A. W.; Engst, C. R.; Ablay, M.; Divitini, G.; Ducati, C.; Liedl, T.; Keyser, U. F. Nano Lett. 2012, 12 (1), 512–517. Kongsuwan, N.; Demetriadou, A.; Chikkaraddy, R.; Benz, F.; Turek, V. A.; Keyser, U. F.; Baumberg, J. J.; Hess, O. ArXiv161202611 Phys. 2016. Nijs, B. de; Bowman, R. W.; Herrmann, L. O.; Benz, F.; Barrow, S. J.; Mertens, J.; Sigle, D. O.; Chikkaraddy, R.; Eiden, A.; Ferrari, A.; Scherman, O. A.; Baumberg, J. J. Faraday Discuss. 2015, 178 (0), 185–193. Benz, F.; Chikkaraddy, R.; Salmon, A.; Ohadi, H.; de Nijs, B.; Mertens, J.; Carnegie, C.; Bowman, R. W.; Baumberg, J. J. J. Phys. Chem. Lett. 2016, 7 (12), 2264–2269. Thacker, V. V.; Herrmann, L. O.; Sigle, D. O.; Zhang, T.; Liedl, T.; Baumberg, J. J.; Keyser, U. F. Nat. Commun. 2014, 5, ncomms4448. Tserkezis, C.; Esteban, R.; Sigle, D. O.; Mertens, J.; Herrmann, L. O.; Baumberg, J. J.; Aizpurua, J. Phys. Rev. A 2015, 92 (5), 053811. Chikkaraddy, R.; Zheng, X.; Benz, F.; Brooks, L. J.; de Nijs, B.; Carnegie, C.; Kleemann, M.-E.; Mertens, J.; Bowman, R. W.; Vandenbosch, G. A. E.; Moshchalkov, V. V.; Baumberg, J. J. ACS Photonics 2017, 4 (3), 469–475. Kleemann, M.-E.; Mertens, J.; Zheng, X.; Cormier, S.; Turek, V.; Benz, F.; Chikkaraddy, R.; Deacon, W.; Lombardi, A.; Moshchalkov, V. V.; Vandenbosch, G. A. E.; Baumberg, J. J. ACS Nano 2017, 11 (1), 850–855. De Liberato, S. Phys. Rev. Lett. 2014, 112 (1), 016401. Bamgbelu, A.; Wang, J.; Leszczynski, J. J. Phys. Chem. A 2010, 114 (10), 3551–3555.

ACS Paragon Plus Environment

Nano Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(59) (60) (61) (62) (63) (64) (65) (66) (67) (68) (69)

Vietz, C.; Kaminska, I.; Sanz Paz, M.; Tinnefeld, P.; Acuna, G. P. ACS Nano 2017, 11 (5), 4969–4975. Mertens, J.; Kleemann, M.-E.; Chikkaraddy, R.; Narang, P.; Baumberg, J. J. Nano Lett. 2017, 17 (4), 2568–2574. Altman, R. B.; Terry, D. S.; Zhou, Z.; Zheng, Q.; Geggier, P.; Kolster, R. A.; Zhao, Y.; Javitch, J. A.; Warren, J. D.; Blanchard, S. C. Nat. Methods 2012, 9 (1), 68–71. Cang, H.; Liu, Y.; Wang, Y.; Yin, X.; Zhang, X. Nano Lett. 2013, 13 (12), 5949–5953. Wientjes, E.; Renger, J.; Cogdell, R.; van Hulst, N. F. J. Phys. Chem. Lett. 2016, 7 (9), 1604–1609. Resch-Genger, U.; Grabolle, M.; Cavaliere-Jaricot, S.; Nitschke, R.; Nann, T. Nat. Methods 2008, 5 (9), 763–775. Vahala, K. J. Nature 2003, 424 (6950), 839–846. Urban, A. S.; Fedoruk, M.; Nedev, S.; Lutich, A.; Lohmueller, T.; Feldmann, J. Adv. Opt. Mater. 2013, 1 (2), 123–127. Pillers, M. A.; Lieberman, M. J. Vac. Sci. Technol. B Nanotechnol. Microelectron. Mater. Process. Meas. Phenom. 2014, 32 (4), 040602. Kusch, P.; Mastel, S.; Mueller, N. S.; Morquillas Azpiazu, N.; Heeg, S.; Gorbachev, R.; Schedin, F.; Hübner, U.; Pascual, J. I.; Reich, S.; Hillenbrand, R. Nano Lett. 2017, 17 (4), 2667–2673. Rotenberg, N.; Kuipers, L. Nat. Photonics 2014, 8 (12), 919–926.