Mechanism for Photopromoted Release of Vanadium from Vanadium

Subscriber access provided by READING UNIV

Article

The mechanism for photo-promoted release of vanadium from vanadium titano-magnetite Xingyun Hu, Xianjia Peng, and Linghao Kong Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b05707 • Publication Date (Web): 30 Jan 2018 Downloaded from http://pubs.acs.org on January 31, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 30

Environmental Science & Technology

1

The mechanism for photo-promoted release of vanadium from vanadium

2

titano-magnetite

3

Xingyun Hua,b, Xianjia Penga,b,c*, Linghao Konga,b

4

a

5

Eco-Environmental Sciences, Chinese Academy of Sciences, Beijing 100085, China

6

b

7

for Eco-Environmental Sciences, Chinese Academy of Sciences, Beijing 100085, China

8

c

9

*

National Engineering Laboratory for Industrial Wastewater Treatment, Research Center for

Beijing Key Laboratory of Industrial Wastewater Treatment and Resource Recovery, Research Center

University of Chinese Academy of Sciences, Beijing 100190, China Corresponding author: Xianjia Peng, Tel: +86-10-62849198, E-mail: [email protected]

10

11

TOC

12

1 ACS Paragon Plus Environment


13

Abstract

14

The release of V from vanadium titano-magnetite, a predominant natural source of V, was studied

15

under light irradiation. The release rate of V from vanadium titano-magnetite was accelerated by light

16

irradiation, and the oxidation of V was detected. The essence of the photo-promoted release of V is

17

that the immobile low valence V is transformed to the mobile V(V) by photo-induced active species

18

generated from the photocatalysis process of magnetite. Among the photo-induced active species, •OH

19

and H2O2 were recognized as the most important oxidizing agents. Not only can they directly convert

20

the immobile low-valence V to the mobile V(V), but also initiate Fenton reaction, which produce more

21

•OH and then further promotes the oxidation of low-valence V. In addition, a conceptual model of the

22

photo promoted release of V was proposed. This study, as part of a broader study of the release

23

behavior of V, can improve the understanding of the pollution problem about V, as well as the fate and

24

environmental geochemistry cycling of V in natural environment.


Page 2 of 30

Page 3 of 30


25

1 INTRODUCTION

26

Vanadium (V) has been suggested to be a potentially hazardous pollutant in the same class as

27

mercury (Hg), lead (Pb) and arsenic (As). As an emerging contaminant, the release and mobilization

28

processes of V have yet to be studied as much as those of Hg, Pb and As, although its economic

29

importance is growing.1,2 Consequently, the understanding of V pollution and its environmental

30

geochemistry cycling is still superficial. Vanadium has three different oxidation states, V(III), V(IV) and

31

V(V), and V(V) is the most toxic and mobile one among them, which means that the redox behavior of V

32

can govern the mobility and geochemical cycling of V in the environment. 3-5 However, previous

33

studies on the release kinetics of V from important vanadium containing ores, i.e., vanadium

34

titano-magnetite (VTM) and stone coal only obtained the release rate and amount of V under different

35

simulated environmental conditions, but the redox of V in the release process was not involved.

36

Thus, it is a necessity to develop a better understanding of the redox of V in its release process from

37

natural vanadium-containing minerals.

6-8

38

Sunlight is recognized as a significant trigger factor on the redox behavior of valence-variable

39

elements. Some studies have shown that light promoted the release of Sb and Cd from valentinite,

40

stibnite and cadmium sulfide through the oxidation of Sb(III) and/or S(-II) by photo-induced active

41

oxidants from the photocatalysis of minerals themselves.9-12 Vanadium titano-magnetite (VTM), as a

42

predominant natural source of V, contained three oxidation states of V, i.e., V(III), V(IV) and V(V).

43

The photochemistry of titano-magnetite and the UV-Fenton reactions mediated by titano-magnetite

44

have been investigated in the catalytical degradation of environmental pollutants. Once it is exposed to

45

light irradiation, the photo-induced oxidants or reductants may be generated from the photocatalysis of

46

VTM. 13-16 Magnetite and titanium dioxide as the famous semiconducting materials, usually present as 3 ACS Paragon Plus Environment


47

a base unit in the VTM deposits; especially magnetite is very sensitive to light irradiation. Thus, it can

48

be hypothesized that under the light irradiation, the immobile V(III) and V(IV) may be oxidized to V(V)

49

which is soluble and mobile, and thereby the release behavior of V from VTM may be promoted.

50

The purpose of the present study is to investigate whether the simulated sunlight irradiation

51

influences the release of V from VTM or not, and if so, how the light irradiation influences the release

52

behavior of V. Firstly, a preliminary experiment was conducted under the simulated sunlight

53

irradiation to verify the promotion effect of light on the release rate and amount of V. Subsequently,

54

the mechanism of photo-prompted release of V was investigated through the identification of key

55

active species, addition of H2O2 and free radical scavengers, and the removal of dissolved oxygen. The

56

study on the redox and release mechanism of V from its predominant source, vanadium titanium

57

magnetite, under light irradiation, as part of a broader study of the release behavior of V, can deepen

58

the understanding of the fate and environmental geochemistry cycling of V in the environment, and

59

then further improve the awareness of emerging pollution problem of V.

60

2 MATERIALS AND METHODS

61

2.1 Materials

62

Vanadium titano-magnetite certified reference material [GBW(E)070130] was purchased from

63

Jinan ZhongBiao Science and Technology Ltd. (Jinan, China). Its dominant component was

64

characterized as magnetite (Fe3O4, PDF#19-0629) by X-ray diffraction (XRD) (Fig. S1a). No

65

diffraction peak for V and Ti compounds was identified by XRD, because of relatively minor amounts

66

of V and Ti (< 3% by weight percent). Magnetite (Fe3O4) with hyperfine field of 48.70 T (tetrahedral

67

site A, isomer shifts 0.331 mm/s) and 45.36 T (octahedral site B, isomer shifts 0.603mm/s) and


Page 4 of 30

Page 5 of 30


68

ilmenite with isomer shifts 1.07–1.10 mm/s were found in the VTM by Mössbauer spectra of 57Fe (Fig.

69

S1b). In addition, chemical method was used to separate V(III), V(IV) and V(V) based on their

70

different solubility characteristics in acidic and basic solution (Supporting information). The content

71

of V(III), V(IV) and V(V) in the VTM were determined as 2.2 mg/g, 1.17 mg/g and 1.3 mg/g,

72

respectively. Its specific surface area is 1.56 m2/g and the point of zero charge (PZC) is pH 6.3 (Fig.

73

S1c).

74

Fe3O4 with a specific surface area of 2.74 m2/g, was purchased from Shanghai Macklin

75

Biochemical Co., Ltd. It has the same crystal structure as magnetite contained in the VTM (Fig. S1a).

76

Other chemicals which had a purity of analytical grade or better were purchased from Sinopharm

77

Chemical Reagent Co. Ltd. (Shanghai, China). All aqueous solutions were prepared using deionized

78

water (18.2 MΩ/cm at 25 °C) from a Milli-Q water purification device.

79

2.2 Experimental Methods

80

A 500-mL beaker with 1.5 g VTM powder and 350 mL of aqueous solution was used to study the

81

release of V in the VTM solution under the light irradiation. A 500W long-arc xenon lamp (35 cm×1

82

cm) (Shanghai Jiguang Special Lighting Appliance Factory, China) with a lamp cover was placed 50

83

cm above the beaker to irradiate light. Its spectral power distribution mainly ranged from 400 nm to

84

800 nm (Fig. S2). The suspension was exposed to visible light irradiation with an ultraviolet cutoff

85

glass filter (λ > 400 nm) above the beaker. The light intensity received by the liquid level was detected

86

as 43,000±1000 Lux, closing to the received solar light intensity on sunny days on the earth. Because

87

the lamp was calorigenic, the reactions require the use of cooling water to keep it at room temperature.

88

At selected time intervals, 0.5 mL aqueous samples were taken and filtered through 0.22 µm

89

polyethersulfone membrane filters (ANPEL Laboratory Technologies lnc., China) for analysis. The



Page 6 of 30

90

sorption of V on the membrane filters can be negligible. As controls, the dissolution of Fe3O4 both in

91

the dark and under light irradiation at pH 4.0 and 6.5 were also investigated.

92

To test the release of V from VTM at different pH values, solutions with pH 2.5, pH 4.0, pH 6.5

93

and pH 9.0 were prepared using diluted hydrochloric acid and/or 5 mmol/L carbonates-bicarbonate

94

buffers. The different pH values were selected to simulate the pH of acid mine drainage (pH 2-4)

95

and natural waters (pH 6-9). The ionic strength of the solution was adjusted to 0.05 mol/L using NaCl.

96

The pH of the solutions was measured at the beginning and at the end of the experiments. To check the

97

effect of dissolved oxygen, anoxic environment was created for the feed solution using a gas purging

98

tube. To exclude oxygen (O2) from the solutions, high purity nitrogen (N2, 99.99%) was input into the

99

feed solution for approximately 2 h before the reaction and insufflation was sustained throughout the

100

irradiation. To determine the effect of H2O2 on the release of V, 30 µmol/L H2O2 was added in the feed

101

solution.

17

102

To identify whether precipitation between aqueous Fe3+ and V5+ occurred in the VTM suspension

103

at pH 2.5, dissolved Fe3+ (25 mg/L) and V5+ (20 mg/L) were prepared individually and then blended in

104

a series of 10 mL centrifuge tubes. At selected time intervals, 5 mL aqueous samples were taken from

105

each centrifuge tube and filtered using 0.22 µm polyethersulfone membrane filters for analysis.

106

2.3 Analytical Methods

107

2.3.1 Characterization of vanadium titano-magnetite

108

The characterization methods of VTM including X-ray diffraction (XRD),

57

Fe Mössbauer

109

measurement, zero zeta potential, Brunauer-Emmett-Teller (BET) N2-adsorption and ultraviolet visible

110

diffuse reflection spectrum (UV-vis DRS) are described in detail in the Supporting Information.

111

2.3.2 Analysis of V, Fe and Ti in the aqueous solution


Page 7 of 30


112

The total V, Fe and Ti were determined by inductively coupled plasma optical emission

113

spectroscopy (ICP-OES, NexION300, PerkinElmer Inc., USA) with a detection limit of 10 µg/L.

114

Some aqueous samples need to be diluted with Milli-Q water to fit in the working range (0 – 20 mg/L,

115

R2≥0.9990). Dissolved V(V) was measured by phosphortungstate spectrophotometric method on an

116

ultraviolet visible light spectrophotometer (DR600, HACH Co. Ltd., USA).

117

analyzed in acid solution at pH 1 by electron paramagnetic resonance (EPR) on an A300 electron spin

118

resonance spectrometer (Bruker Corporation, Germany) at approximately 9.40 GHz at room

119

temperature. The concentration of Fe(II) was measured colorimetrically using 1,10-phenanthroline on

120

an ultraviolet visible light spectrophotometer (DR600, HACH Co. Ltd., USA).

121

2.3.3 Analysis of hydroxyl free radical

18

Vanadyl (IV) was

122

The measurement of hydroxyl free radical was performed on a Bruker EleXsys E500 electron

123

paramagnetic resonance spectrometer (Germany) at room temperature (25 °C ± 1) using 300 mmol/L

124

dimethyl pyridine N-oxide (DMPO) as a capture reagent. Typical instrument settings were: sweep

125

width 100.0 G, power attenuation 13.0 dB, modulation amplitude 2 G and sweep time 40 s. The EPR

126

signals of the irradiated samples for 2 min at pH 2.5, pH 4.0, pH 6.5 and pH 9.0 were recorded. The

127

results for samples in the dark at the above corresponding pH values were obtained as the controls.

128

2.3.4 Analysis of hydrogen peroxide

129

Concentration of hydrogen peroxide (H2O2) was measured by an ultraviolet visible light

130

spectrophotometer (DR600, HACH Co. Ltd., USA) at 400 nm with the help of the yellow complex

131

formed with potassium titanyl oxalate dehydrate and H2O2 in quartz cuvettes of 1 cm path length.19

132

The method has a 0.1 mg/L (approximately 3.0 µmol/L) detection limit.

133

2.4 Estimation of release rate of V



Page 8 of 30

134

For all the experiments, the mobilized mass of V in aqueous solutions is plotted as a function of

135

time. The average release rates of V are calculated from the cumulative migrated amount (mg) of Vtot

136

in the solution at certain reaction time (Eq. 1). Note that we do not convert these release rates of V

137

into dissolution rates of the VTM, since the ideal chemical equation of V and the precise stoichiometry

138

of V in the VTM are difficult to be determined. Specifically, the secondary precipitation of V at pH 2.5

139

was recognized as undissolved V, which is not involved in the calculation of release kinetics. r=

140

[ ]

141

3 RESULTS AND DISCUSSION

142

3.1 The release of V from VTM under light irradiation

(1)

143

To determine the effect of light irradiation on the release behavior of V from VTM, preliminary

144

experiments were conducted in the dark and under light irradiation, respectively, for 120 min. The

145

release amount of V with the time in the VTM suspension are showed in Fig. 1. It can be clearly seen

146

that light irradiation accelerates the release of total V at pH 2.5, pH 4.0 and pH 6.5. Accordingly, the

147

average release rates of V increased from 6.1×10−3 mg/min in the dark to 9.1×10−3 mg/min under light

148

irradiation at pH 2.5, from 5.3×10−3 mg/min to 9.9×10−3 mg/min at pH 4.0, and from 7.6×10−3 mg/min

149

to 1.4×10−2 mg/min at pH 6.5. While, little promotion effect of the light irradiation at pH 9.0 was

150

found on the release of V. Above results indicated that the light irradiation promoted the release rate

151

and amount of V in the VTM suspension at pH 2.5-6.5.

152

Furthermore, at pH 4.0-9.0, only V(V) was detected in the VTM suspension in the dark and under

153

light irradiation, while, at pH 2.5, both V(IV) and V(V) were detected. It is known that V occurs in III,

154

IV and V oxidation states in the VTM, and the higher oxidation states of V corresponds to the more


Page 9 of 30


155

soluble and mobile ability. Thus, it can be speculated that the light irradiation can accelerate the

156

release of V through the oxidation of immobile V(III) or V(IV) to more soluble and mobile V(V). To

157

verify that light irradiation can promote the oxidative dissolution of V(III) and V(IV), an approximate

158

dissolution experiment of V2O3 and VO2 in the presence of pure Fe3O4 at pH 4.0 and pH 6.5 in the

159

dark and under light irradiation were performed. It can be found that light irradiation greatly promoted

160

the release of V from VO2 and V2O3 at pH 4.0 and pH 6.5 (Fig. S3). The average release rate of V in

161

the VO2 suspension increased from 9.8×10−4 mg/min at pH 4.0 and 8.4 × 10−4 mg/min at pH 6.5 in the

162

dark to 3.8×10−3 mg/min and 3.4×10−3 mg/min under light irradiation, respectively. The average

163

release rate of V from the dissolution of V2O3 increased from 5.9×10−4 mg/min at pH 4.0 and 3.5×10−4

164

mg/min at pH 6.5 in the dark to 2.2×10−3 mg/min and 2.0×10−3 mg/min under light irradiation,

165

respectively, and all released V in the solution existed in the form of V(V). The result indicated that

166

light irradiation could promote the oxidative dissolution of V(III) and V(IV) in the presence of Fe3O4.

167

Probably, the specific chemical states of V in VTM are different from that in V2O3 and VO2, or they

168

may not be the good surrogates for simulating the reactions of V in VTM, but it still valued for

169

understanding the photo-promoted release mechanism of V in VTM.

170

Thus, analogically, in the VTM suspension under light irradiation, the essence of photo-promoted

171

release of V is assumed to be the oxidation of immobile V(IV) or V(III) to soluble and mobile V(V) by

172

some photo-induced active species generated from the photocatalysis process of magnetite or titanium

173

dioxide. The UV-Vis diffuse reflection spectrum of pure Fe3O4 in Fig. S4 showed the same excellent

174

optical absorptivity as VTM in ultraviolet and visible region (200-800 nm). As we have known,

175

magnetite can be regarded as a compound containing ferrous oxide and ferric oxide (FeO·Fe2O3). The

176

energy gap (Eg) of FeO and Fe2O3 are 2.4 eV and 2.2 eV, respectively, while corresponding valence



177

band edges are 2.23 eV and 2.48 eV, respectively, with respect to the normal hydrogen electrode

178

(NHE), 16 which are above the valence band edges of semiconductor that could react with H2O/OH- to

179

form hydroxyl radical (1.99 eV). In addition, in the photochemical experiment of the pure Fe3O4

180

suspension at pH 2.5, 4.0, 6.5 and 9.0, obvious signals of •OH were detected (Fig. S5), suggesting the

181

occurrence of photocatalysis process of magnetite. While, when compared with Fe3O4, the effect of

182

photochemistry of titanium dioxide on the oxidation of V(IV) or V(III) can be neglected in the studied

183

system, because of its low content in the VTM and the optical absorptivity in ultraviolet region

184

(190-380 nm). Besides, the standard electrode potential of Fe(III)/Fe(II), V(IV)/V(III) and V(V)/V(IV)

185

at 298 K are 0.771 eV, 0.337 eV and 0.991 eV individually, so the redox reaction between Fe and V of

186

different oxide state will happen, further influence the release behavior of V. According to above

187

speculation, major reactions that may occur in the VTM suspension under light irradiation have been

188

listed in Table 1. The photo-oxidants described above may be in the form of •OH, •O2−, •OOH and

189

H2O2. Furthermore, the generated H2O2 can trigger the homogeneous or heterogeneous Fenton reaction,

190

producing more •OH to oxidize V(III) or V(IV). 20, 21 Subsequently, to verify above hypothesis, the key

191

active species were identified and their effects on the release behavior of V were discussed.

192

3.2 Identification and evaluation of major photo-oxidants

193

3.2.1 •OH and H2O2

194

The signal of •OH-DMPO in the VTM suspension at pH 2.5-9.0 was detected by EPR under light

195

irradiation in Fig. 2. However, a slight signal of •OH-DMPO was also detected in control groups,

196

which is attributed to the strong light adsorption ability of VTM. In the measured process by EPR,

197

some light induced the photochemical reaction. The redox potential of •OH was concluded as 1.9-2.8

198

eV in acidic and basic solution, so it can oxidize V(III) and V(IV) to V(V) (the redox potential of


Page 10 of 30

Page 11 of 30


199

V(IV)/V(III) and V(V)/V(IV) are 0.337 eV and 0.991 eV, respectively). The •OH probably generated

200

from three ways: (1) The photo-induced (hvb+) can be captured on the magnetite surface undergoing a

201

charge transfer with adsorbed water molecules (H2O) or with surface-bound hydroxide species (OH−)

202

to generate active hydroxyl free radicals (•OH) as shown in Eq. 3. (2) Fenton reaction initiated by

203

H2O2 generated under light irradiation, which resulted in more •OH producing (Eqs. 6, 8). Because the

204

magnetite contains both Fe(II) and Fe(III), which are the crucial cations for the initiation of Fenton

205

reaction. (3) The photolysis of Fe(OH)2+ (Eq. 7). At pH 2.5, approximately 50 µg/L Fe(III) was

206

detected in the VTM suspensions. While, in the individual light irradiation experiment for 50 µg/L

207

Fe(III) aqueous solution at pH 2.5, no signal of •OH-DMPO was detected. Thus, the sources of •OH

208

from the photolysis of Fe(OH)2+ could be excluded. The first two ways were deemed to be the

209

important sources of •OH, and they were co-occurring in the VTM suspension under light irradiation,

210

especially the photo-induced Fenton process. The content of Fe(II) in the VTM solid after the reaction

211

under light irradiation and/or H2O2 conditions dropped by 2%-5% than that in the fresh VTM solid,

212

meanwhile, the content of Fe(III) in the VTM solid after the reaction increased proportionately (Table

213

S1). These results indicated that heterogeneous Fenton reaction was initiated under light irradiation

214

(Eq. 8). From Fig. S6, the added H2O2 at pH 2.5-9.0 was decomposed at different levels, so it can be

215

argued that extra •OH would be generated rapidly because of the Fenton reaction (Eq. 8). In addition,

216

at pH 2.5, 4.7 mg/L Fe(II) ions was detected under light irradiation, while no Fe ions were detected at

217

pH 4.0-9.0, which illustrated that Fenton reaction also happened at pH 2.5. That is why the amount of

218

•OH at pH 2.5 was much higher than that at pH 4.0-9.0. Thus, the photo-induced Fenton reaction was

219

identified as the most important source of •OH.

220

So, in the VTM suspension under light irradiation, •OH and H2O2 are always concomitant



221

because of the Fenton reaction, it is almost impossible to distinguish their effect on the release of V. To

222

verify their effect on the release of V at pH 2.5-9.0, H2O2 was added at a dosage of 30 µmol/L in the

223

dark. Most H2O2 was transformed to •OH by Fe(II) quickly, meaning that both the concentration of

224

•OH and H2O2 increased correspondingly (Fig. S6). The EPR patterns for the addition of H2O2

225

indicated that extra •OH was generated (Figs. 2a-2d). From Figs. 3a-3d, after adding H2O2, the average

226

release rate of V increased from 6.1×10-3 mg/min to 9.9×10-3 mg/min at pH 2.5, from 4.6×10−3 mg/min

227

to 1.4×10−2 mg/min at pH 4.0 and from 7.6×10−3 mg/min to 1.4×10−2 mg/min at pH 6.5, respectively.

228

The release rate of V at pH 9.0 was accelerated from 3.5×10−2 to 3.9×10−2 mg/min at the first 30 min

229

and then reached a solubility equilibrium. In this situation, there still were undecomposed H2O2 in the

230

solution, thus, the result verified the combined importance of •OH and H2O2 on the promotion of V

231

release. It is known that redox potential of ·OH/H2O and H2O2/H2O are 2.27 eV and 1.35 eV,

232

respectively. Therefore, hydroxyl radical will provide stronger oxidizability than H2O2 in a

233

concomitant system. However, in the VTM suspension under light irradiation, no H2O2 was detected.

234

It is probable that the generated H2O2 was transformed to •OH instantly through Fenton reaction

235

(Eqs.8, 9, 11, 12). It should be noted that the importance of individual •OH on the promoted release of

236

V was verified through the addition of H2O2 instead of free-radical scavengers, that is because the

237

common free radical masking agents were found to had a remarkable effect on the release of V in the

238

VTM suspension. The previous studies have verified the importance of •OH and H2O2 on the oxidation

239

of SbIII, and promotion release of Sb from Sb2O3 and Sb2S3 through photocatalytic process of Sb2O3

240

and Sb2S3 themselves. 9-11

241

3.2.2 •O2− and •OOH

242

In the photocatalysis process of magnetite, the photo-induced electrons (ecb−) can be captured by the


Page 12 of 30

Page 13 of 30


243

dissolved oxygen (O2) to produce superoxide free radicals (•O2−) (Eq. 4). Furthermore, the •O2−

244

becomes •OOH through a protonation process, and then two of the •OOH can form H2O2 (Eqs. 5, 6).

245

From the EPR patterns in Fig. 2, the signals of •OOH-DMPO were found at pH 4.0-9.0, which

246

indirectly indicated that there were •O2− or H2O2 in the VTM suspension ((Eqs. 5, 6, 9, 11, 15). Due to

247

the existence of abundant Fe(II) and Fe(III) in the VTM suspension, the generated H2O2 in this

248

reaction pathway will transform into •OH again through Fenton reaction. The end-product in this

249

pathway is still •OH. It was found that the removal of dissolved oxygen from the VTM suspension

250

under light irradiation slightly lowered the release rate and amount of V (Fig. 4). The release rate of V

251

decreased from 9.2×10-3 mg/min to 8.1×10-3 mg/min at pH 2.5, from 9.9×10-3 mg/min to 8.4×10-3

252

mg/min at pH 4.0 and from 1.3×10-2 mg/min to 1.2×10-2 mg/min at pH 6.5, respectively. The result

253

suggests that this reaction pathway also played a role in the release of V. And many previous studies

254

have also verified the generation of •O2− and its oxidizing ability to metals or refractory organics in the

255

heterogeneous photocatalysis reaction system. 9, 11, 22, 23

256

3.3 The mechanism of photo promoted release of V

257

Based on above experimental results, •OH and H2O2 are the most significant intermediate products

258

from the photocatalytic and Fenton reactions. Thus, the effect mechanism of •OH and H2O2 on the

259

release of V was discussed emphatically in the subsequent section. Because of the different solution

260

characteristics in the VTM suspension at pH 2.5 and pH 4.0-9.0, the promotion mechanism at pH 2.5

261

and pH 4.0-9.0 was discussed individually.

262

3.3.1 The release of V in the VTM suspension at pH 2.5

263

In the dark, 0.5 mg/L V(IV), 2.0 mg/L V(V), 7.0 mg/L Fe(II) and 0.05 mg /L Fe(III) were detected

264

at 120 min in the VTM suspension. While under light irradiation, the corresponding concentration of



265

Fe(II) and V(V) decreased to 4.5 mg/L and 0.2 mg/L, respectively, but the concentration of V(IV)

266

increased to 3.5 mg/L. It can be inferred in the VTM suspension that the redox reaction between Fe(II)

267

and V(V) and the precipitation reaction between Fe(III) and V(V) occurred. The XRD of solid product

268

at pH 2.5 apart from VTM (Fig. S1a) verified the generation of ferric vanadate. Thus, the decrease of

269

V(V) concentration was ascribed to the redox reaction with Fe(II) and precipitation reaction with

270

Fe(III) (Eqs. 8, 10, 21). However, the concentration of V(IV) in the solution was higher than the

271

computation value according to Eqs. 19 and 21. It can be inferred that, under light irradiation, the

272

photo-induced active species restricted the precipitation of Fe(III) and V(V) or increased the

273

dissolution of ferric vanadate precipitation, and then improved the release rate and amount of V.

274

To verify the inference, the precipitation experiment between Fe(III) and V(V), and dissolution

275

experiment of ferric vanadate precipitation at pH 2.5 were conducted individually under light

276

irradiation. From Figs. 5a and 5b, the concentration of Fe(III) and V(V) decreased with time, and the

277

decreased mole ratio of them were estimated to be approximately 1, indicating that precipitation

278

reaction between them occurred (Fig. S7a). However, in the presence of light or/and H2O2, the

279

concentration of Fe(III) and V(V) was higher than those in the absence of light and H2O2 and some

280

Fe(II) ions were detected at different levels (Fig. 5c), which indicated that the generation of H2O2

281

partly induced the reductive of Fe(III) (Eqs. 11, 12), inhibiting the formation of ferric vanadate

282

precipitation under light irradiation (Fig. S7b).

283

In the as-prepared ferric vanadate aqueous solution, it can be found that the concentration of Fe(III)

284

and V(V) increased during the first 60 min and then decreased from 60 min to120 min (Figs. 5d and

285

5e). This illustrated that in the presence of light or/and H2O2, ferric vanadate dissolved during the first

286

60 min because of the reduction of part of Fe(III) (Fig. 5f) contained in the ferric vanadate


Page 14 of 30

Page 15 of 30


287

precipitation by H2O2 (Eqs. 11, 12), releasing V and Fe gradually to a certain degree. Subsequently,

288

dissolved Fe(II) was oxidized to Fe(III) again by H2O2 or the other oxidants, and then V(V) and Fe(III)

289

precipitated again from 60 min to120 min. Anyway, under light irradiation, the dissolution of ferric

290

vanadate precipitation was initiated.

291

In summary, above two groups of experiments can be ascribed to a series of heterogeneous Fenton

292

reactions among photo-induced H2O2, Fe(II) and Fe(III) after receiving the light irradiation. Under

293

light irradiation, continuous •OOH and H2O2 generated from the photocatalysis process of magnetite

294

could convert Fe(III) to Fe(II), not only inhibiting the formation of ferric vanadate precipitation but

295

also promoting the dissolution of pre-existing ferric vanadate precipitation, thereby the release rate and

296

amount of V at pH 2.5 increased under light irradiation.

297

3.3.2 The release of V in the VTM suspension at pH 4.0-9.0

298

In the VTM suspension at pH 4.0-9.0, neither Fe(III) nor Fe(II) was detected in the dark and

299

under light irradiation. And in the magnetite suspension at pH 4.0 - 9.0, Fe was not detected as well.

300

That is to say, in the VTM suspension at pH 4.0-9.0, only undissolved VTM solid and dissolved V(V)

301

were in the reaction system.

302

In this situation, the promotion effect of light irradiation on the release of V was attributed to the

303

oxidation of immobile V(III) or V(IV) in the VTM to soluble and mobile V(V) by the photo-induced

304

active species. The individual dissolution experiment of V2O3 and VO2 at pH 4.0 and pH 6.5 in the

305

dark and under light irradiation could indirectly verify the hypothesis. The dissolution of VO2 at pH

306

6.5 under light irradiation was selected to further investigate the importance of •OH and O2 on the

307

release of V. 0.5 mol/L isopropyl alcohol (IPA) was used to scavenge •OH; at this concentration, 99%

308

of the·•OH radicals can be scavenged by IPA.24, 25 From Fig. S8, the presence of a scavenger slowed



309

the release rate of V from 3.4×10−3 mg/min to 1.6 ×10−3 mg/min. The removal of dissolved oxygen

310

reduced the release rate of V from 3.4×10−3 mg/min to 2.5×10−3 mg/min. Furthermore, based on the

311

release rate data of V under corresponding condition, the participation ratio of •OH in the oxidative

312

release of V(IV) was estimated to be 50%, and the participation ratio of •O2− and •OOH was estimated

313

to be 26.5%. The results suggested that •OH, •O2− and •OOH played a major role in the oxidative

314

release of V(IV), and implied that other than •OH, •O2− and •OOH, the other oxidants existed.

315

According to the redox potential law, another oxidant may be Fe(III) (Eq. 20).

316

In the VTM suspension at pH 9.0, the release amount of V was much higher than those in acidic

317

solutions (Fig. 1). That is because the thermodynamic property of V(V) made it easier to be dissolved

318

in basic solution. From Figs. 1, 3 and 4, under light irradiation, H2O2 and O2 had little effect on the

319

release of V at pH 9.0 and the concentration of V reached to an equilibrium after 30 min, maybe

320

because the release amount of V under this condition had reached saturation.

321

3.3.3 Conceptual model of the photo-promoted release of V

322

The essence of photo-promoted release of V is to transform the immobile low-valence V to the

323

soluble and mobile V(V) by the photo-induced active species generated from the photocatalysis

324

process of magnetite. According to the mentioned results, a postulated mechanism of photo-promoted

325

release of V was proposed in Fig. 6 and the main reaction pathways were marked with bold solid lines.

326

The magnetite contained in the VTM received light with sufficient energy irradiation (hv > Eg),

327

and an electron (ecb−) from its valence band jumped to the conduction band with the concomitant

328

generation of a hole (hvb+) in the valence band (Eq. 2). Then the hvb+ was captured on the VTM surface

329

undergoing a charge transfer with adsorbed water molecules (H2O) to generate active hydroxyl free

330

radicals (•OH) (Eq. 3). The ecb− was captured by the dissolved oxygen to produce •O2− (Eq. 4).


Page 16 of 30

Page 17 of 30


331

Furthermore, the •O2− became •OOH through a protonation process, and then two •OOH formed

332

hydrogen peroxide (H2O2) (Eqs. 5, 6). Furthermore, the generated H2O2 could trigger Fenton reactions,

333

producing more •OH (Eq. 8).

334

In the VTM suspensions at pH 2.5, the ultimate photo-induced active species •OH and/or H2O2

335

improved the release rate and amount of V through inhibiting the formation or promoting the

336

dissolution of ferric vanadate precipitation (Eqs. 11, 12). In the VTM suspension at pH 4.0-9.0, the

337

promotion effect was attributed to the transformation of low-valence V in the VTM to the soluble and

338

mobile V(V) by above species. In a word, it is the combined effect of photocatalytic process and

339

Fenton reaction of VTM that promoted the release of V.

340

4 ENVIRONMENTAL SIGNIFICANCE

341

Titanomagnetite deposits are the primary source of V in the world. In China, an estimated 40% of

342

V production is from vanadiferous slag from the smelting of vanadium titanium magnetite. As the

343

most important base of V production in the world, the giant Panzhihua vanadium titanium magnetite

344

deposit provides 64% of V for China. Extensive mining and smelting activities have had major

345

environmental impacts in mines or nearby regions, resulting in abnormally elevated concentrations of

346

V in the water and soil near mines or smelting sites.26-30 When these minerals are exposed to water

347

environment under solar light irradiation, the release rate of V can be accelerated and the release

348

amount of V increased by the photocatalysis process of magnetite. Low toxic and immobile V(III) and

349

V(IV) are oxidized to high toxic and mobile V(V) during the process, which enhanced the

350

environmental risk of V. As the starting point of biogeochemistry cycle of V, this study on the

351

dissolution of the most important V containing minerals helps us to understand the pollution problem



352

of V. This study, as a part of broader study on the release behavior of V, is a premise that helps us to

353

understand the migration and transformation behavior of V in the presence of the other important

354

factors, such as natural organic ligands, in natural environment. To clarify the fate and environmental

355

geochemistry cycle of V in the environment, further studies are needed.

356

In addition, magnetite naturally doped with V is an immense resource of (photo)catalyst and

357

greatly influence the geochemical processes of organic pollutants through initiating the homogeneous

358

or/and heterogeneous Fenton reaction, producing more free radicals. Thereby, a wide range of element

359

or compounds are oxidized and some geochemically and environmentally important reactions,

360

including the photooxidation of phenol, polychlorinated biphenyls, sulfur-containing organic

361

compounds, and nitro gen-containing organic compounds are initiated.16, 25, 31

362

ACKNOWLEDGEMENTS

363

This work was supported by the National Natural Science Foundation of China (No. 21607166,

364

41641034 and 41473113) and the National Water Pollution Control and Treatment Science and

365

Technology Major Project (No. 2015ZX07205-003).

366

Supporting Information

367

Eight figures and one table relate to characterization of VTM, the spectral power distribution of light

368

source, the release amount of V from VO2 and V2O3 in the presence of Fe3O4, EPR signals intensity

369

for free radicals in the pure Fe3O4 suspension, the decomposition efficiency of 30 µmol/L H2O2 at

370

different pH values and the relative content of Fe(II) and Fe(III) in the fresh and reacted VTM

371

supplied as Supporting Information.


Page 18 of 30

Page 19 of 30


372

REFERENCES

373

1.

S. Vanadium, recent advancements and research prospects: A review. Environ. Int. 2015, 80, 79-88.

374 375

2.

Moskalyk, R.R.; Alfantazi, A.M. Processing of vanadium: a review. Miner. Eng. 2003, 16 (9), 793-805.

376 377

Imtiaz, M.; Rizwan, M.S; Xiong, S.; Li, H.; Ashraf, M.; Shahzad, S.M.; Shahzad, M.; Rizwan, M.; Tu,

3.

Crans, D.; Amin, S.; Keramidas, A. Chemistry of relevance to vanadium in the environment. In:

378

Nriagu, J. (Ed.), Vanadium in the Environment. Part 1: Chemistry and Biochemistry. John Wiley

379

and Sons, New York, 1998, pp. 73-96.

380

4.

Lett. 1984, 23, 227-231.

381 382

5.

Nechay, B.R.; Nanning, L.B.; Nechay, P.S.E.; Post, R.L.; Branthan, J.J.; Macara, I.G.; Kubena, L.F.; Philip, T.D.; Nielsen, F.H. Role of vanadium in biology. Fred Proc. 1986, 45, 123-132.

383 384

Llobet, J.M.; Domingo, J.L. Acute toxicity of vanadium compounds in rats and mice. Toxicol.

6.

Hu, X.; Yue, Y.; Peng, X. Release kinetics of vanadium from vanadium titano-magnetite: The

385

effects of pH, dissolved oxygen, temperature and foreign ions. J. Environ. Sci. 2017,

386

doi.org/10.1016/j.jes.2017.07.001. In Press.

387

7.

Hu, X.; Yue, Y.; Peng, X. Release kinetics of vanadium from vanadium (III, IV and V) oxides:

388

Effect

389

https://doi.org/10.1016/j.jes.2017.08.006. In Press.

390

8.

393

pH,

temperature

and

oxide

dose.

J.

Environ.

Sci.

2017,

DOI:

Hu, X.; Yue, Y.; Peng, X. Organic ligand induced release of vanadium from the dissolution of stone coal oxide ore. Environ. Sci. Poll. Res. 2017, DOI: 10.1007/s11356-017-0342-2. In Press.

391 392

of

9.

Hu, X.; Kong, L.; He, M. Kinetics and mechanism of photopromoted oxidative dissolution of antimony trioxide. Environ. Sci. Technol. 2014, 48(24), 14266-14272. 19 ACS Paragon Plus Environment


394 395 396 397 398 399

10. Kong, L.; He, M. Mechanisms of Sb(III) photooxidation by the excitation of organic Fe(III) complexes. Environ. Sci. Technol. 2016, 50 (13), 6974–6982. 11. Hu, X.; He, M; Kong, L. Photopromoted oxidative dissolution of stibnite. Appl. Geochem. 2015, 61, 53-61. 12. Davis, A.P.; Hsieh, Y.H.; Huang, C.P. Photo-oxidative dissolution of CdS(s): the effect of complexing agents. Chemosphere, 1995, 31(4), 3093-3104.

400

13. Zhong, Y.; Liang, X.; Zhong, Y.; Zhu, J.; Zhu, S.; Yuan, P.; He, H.; Zhang, J. Heterogeneous

401

UV/Fenton degradation of TBBPA catalyzed by titanomagnetite: Catalyst characterization,

402

performance and degradation products. Water Res, 2012, 46(15), 4633-4644.

403

14. Liang, X.; Zhong, Y.; Zhu, S.; Zhu, J.; Yuan, P.; He, H.; Zhang, J. The decolorization of Acid

404

Orange II in non-homogeneous Fenton reaction catalyzed by natural vanadium–titanium

405

magnetite. J. Hazard. Mater., 2010. 181(1-3), 112-120.

406

15. Costa, R.C.C.; Lelis, M.F.F.; Oliveira, L.C.A.; Fabris, J.D.; Ardisson, J.D.; Rios, R.R.V.A.; Silva,

407

C.N.; Lago, R.M. Novel active heterogeneous Fenton system based on Fe3−xMxO4 (Fe, Co, Mn,

408

Ni): the role of M2+ species on the reactivity towards H2O2 reactions, J. Hazard. Mater. 2006,

409

129,171-178.

410 411 412 413

16. Xu, Y.; Schoonen, M. A.A. The absolute energy positions of conduction and valence bands of selected semiconducting minerals. Am. Mineral. 2000, 85, 543-556. 17. Akcil, A.; Koldas, S. Acid Mine Drainage (AMD): causes, treatment and case studies. J. Clean. Product. 2006, 14, 1139-1145.

414

18. Yue, Y.; Wang, X.; Hu, X.; Peng, X. Improvement determination of the oxidovanadium (Ⅳ) and

415

total vanadium in the solution by modified phosphorus-tungsten-vanadium spectrophotometry.


Page 20 of 30

Page 21 of 30

416 417 418


Chinese Journal of Analysis Laboratory, 2017, 36, 362-367. 19. Sellers, R.M. Spectrophotometric determination of hydrogen-peroxide using potassium titanium (IV) oxalate. Analyst, 1980, 105, 950-954.

419

20. Liang, X.; Zhu, S.; Zhong, Y.; Zhu, J.; Yuan, P.; He, H.; Zhang, J. The remarkable effect of

420

vanadium doping on the adsorption and catalytic activity of magnetite in the decolorization of

421

methylene blue. Appl. Catal. B: Environ. 2010, 97(1-2), 151-159.

422 423

21. Wu, R.C.; Qu, J.H. Removal of azo dye from water by magnetite adsorption–Fenton oxidation, Water Environ. Res. 2004, 76, 2637–2642.

424

22. Hansard, S. P., Easter, H. D., Voelker, B. M. Rapid reaction of nanomolar Mn(II) with superoxide

425

radical in seawater and simulated freshwater. Environ. Sci. Technol., 2011, 45 (7), 2811–2817.

426

23. Huang, W., Brigante, M., Wu, F., Mousty, C., Hanna, K., Mailhot, G. Assessment of the Fe(III)–

427

EDDS complex in Fenton-like processes: from the radical formation to the degradation of

428

bisphenol A. Environ. Sci. Technol., 2013, 47 (4), 1952-1959.

429

24. Brezonik, P. L.; Fulkerson-Brekken, J. Nitrate-induced photolysis in natural waters: Controls on

430

concentrations of hydroxyl radical photo intermediates by natural scavenging agents. Environ. Sci.

431

Technol. 1998, 32, 3004-3010.

432

25. Buxton, G. V.; Greenstock, C. L.; Helman, W. P.; Ross, A. B. Critical-review of rate constants for

433

reactions of hydrated electrons, hydrogen-atoms and hydroxyl radicals (·OH/·O−) in aqueous

434

solution. J. Phys. Chem. Ref. Data 1988, 17, 513-886.

435 436

26. Huang, J.H.; Huang, F.; Evans, L.; Glasauer, S. Vanadium: Global (bio)geochemistry. Chem. Geol. 2015, 417, 68-89.

437

27. Teng, Y.; Ni, S.; Zhang, C.; Wang, J.; Lin, X.; Huang, Y. Environmental geochemistry and

438

ecological risk of vanadium pollution in Panzhihua mining and smelting area, Sichuan, China. 21 ACS Paragon Plus Environment


439

Chin. J. Geochem. 2006, 25(4), 379-385.

440

28. Teng, Y.; Yang, J.; Wang, J.; Song, L. Bioavailability of V extracted by EDTA, HCl, HOAC,

441

and NaNO3 in topsoil in the Panzhihua Urban Park, located in Southwest China. Biol. Trace

442

Elem. Res. 2011, 144, 1394-1404.

443

29. Panichev, N.; Mandiwana, K.L.; Moema, D.; Molatlhegi, R.; Ngobeni, P. Distribution of

444

vanadium (V) species between soil and plants in the vicinity of vanadium mine. J. Hazard. Mater.

445

2006, 137, 649-653.

446

30. Połedniok, J.; Buhl, F. Speciation of vanadium in soil. Talanta 2003, 59, 1-8.

447

31. Spikes, J.D. Selective photooxidation of thiols sensitized by aqueous suspensions of cadmium

448

sulfide. Photochem. Photobio. 1981, 34, 549-556.

449


Page 22 of 30

Page 23 of 30


450

The captain of figures

451

Fig.1 The release amount of V from the dissolution of vanadium titano-magnetite at different pH: (a)

452

At pH 2.5, (b) At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

453

Fig. 2 Electron spin resonance signals intensity for free radicals under different conditions: (a) At pH

454

2.5, (b) At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

455

Fig. 3 The release amount of V in the presence of 30 µmol/L H2O2 at different pH: (a) At pH 2.5, (b)

456

At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

457

Fig.4 The release amount of V under the anoxic condition at different pH: (a) At pH 2.5, (b) At pH 4.0,

458

(c) At pH 6.5 and (d) At pH 9.0.

459

Fig. 5 The effect of H2O2 on the concentration of V, Fe(III) and Fe(II) at pH 2.5: (a-c) in the formation

460

of ferric vanadate: the initial concentration of V(V) and Fe(III) are 20 and 25 mg/L, respectively; (d-f)

461

in the dissolution of ferric vanadate

462

Fig. 6 Conceptual model for photo-promoted release of V from vanadium titano-magnetite

463



464

Page 24 of 30

The list of figures

465 4.0

5.0 Control Light

V Concentration (mg/L)

3.5

(a) pH 2.5

Control Light

4.5

(b) pH 4.0

4.0

3.0

3.5 2.5

3.0

2.0

2.5

1.5

2.0

1.0

r=9.1x10 mg/min

1.5

0.5

r=6.1x10-3 mg/min

1.0

-3

r=9.9x10-3 mg/min r=5.3x10-3 mg/min

0.5 0

20

40

60

80

100

120

0

20

40

60

80

100

120

100

120


6 Control Light

5

(c) pH 6.5

(d) pH 9.0

Control Light

10 9

4 8 3 7 2 6

r=1.4x10-2 mg/min 1

r=7.6x10-3 mg/min 5 0

466

20

40

60

80

100

120

0

20

40

60

80

Time (min)

Time (min)

467

Fig.1 The release amount of V from the dissolution of vanadium titano-magnetite at different pH: (a)

468

At pH 2.5, (b) At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

469


Page 25 of 30


470

Offset Y values

2.0

+ H2O2

(a) pH 2.5

+ H2O2

(b) pH 4.0 0.16

1.5

0.12 + Light + Light

1.0

0.08 0.04

0.5

Control

Control 0.00

0.0 3460

Offset Y values

0.16

3480

3500

3520

3540

+ H2O2

(c) pH 6.5

3460

3560 0.16

0.12

3480

3500

3520

3540

3560

+ H2O2

(d) pH 9.0

0.12 + Light

+ Light

0.08

0.08

0.04

Control

0.00

0.04 Control 0.00

3460

3480

3500

3520

3540

3560

3460

3480

3500

3520

3540

3560

X [G]

X [G]

471 472

Fig. 2 Electron spin resonance signals intensity for free radicals under different conditions: (a) At pH

473

2.5, (b) At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

474 475



4.0

7 Control H2 O2

3.5 V Concentration (mg/L)

Page 26 of 30

Control H2 O2

(a) pH 2.5 6

3.0

(b) pH 4.0

5

2.5 4 2.0 3

1.5 1.0

r=9.9x10-3 mg/min

0.5

-3

2

0

20

40

60

80

100


1

r=6.1x10 mg/min 120

0

20

40

60

80

100

120


7 Control H2 O2

6

(c) pH 6.5

9

5 4

8

3

7

2

r=3.5x10-2 mg/min for 30 min

r=7.6x10-3 mg/min 0

20

40

60

80

100

r=3.9x10-2 mg/min for 30 min

6

r=1.4x10-2 mg/min 1

476

(d) pH 9.0

Control H2 O2

10

5 120

0

20

Time (min)

40

60

80

100

120

Time (min)

477 478

Fig. 3 The release amount of V in the presence of 30 µmol/L H2O2 at different pH: (a) At pH 2.5, (b)

479

At pH 4.0, (c) At pH 6.5 and (d) At pH 9.0.

480 481


Page 27 of 30


4.0

4.5 Light N2


3.5

(a) pH 2.5

3.0

3.5

2.5

3.0

2.0

2.5

1.5

2.0

1.0


0.5 0

20

40

60

Light N2

4.0

80

100

(b) pH 4.0

1.5

r=9.9x10-3 mg/min

1.0

r=8.4x10-3 mg/min

120

0

20

40

60

80

100

120


6 Light N2

5

(c) pH 6.5

Light N2

10

(d) pH 9.0

9 4 8 3 7 2 1

r=4.9x10-2 mg/min for 30 min r=4.9x10-2 mg/min for 30 min

6


5 0

482

20

40

60

80

100

120

0

20

Time (min)

40

60

80

100

120

Time (min)

483

Fig.4 The release amount of V under the anoxic condition at different pH: (a) At pH 2.5, (b) At pH 4.0,

484

(c) At pH 6.5 and (d) At pH 9.0.



Page 28 of 30

485

Control

Light

H2O2

Light+H2O2 0.5

20 Fe(III) Concentration (mg/L)


(b)

12 10 8 6

(c) Fe(II) Concentration (mg/L)

(a)

14

18 16 14 12 10

0.4 0.3 0.2 0.1 0.0

4

0

20

40

60

8

80 100 120

3.5

0

20

40

2.0

1.5

0

20

40

60

1.5

1.0

0.5

Time (min)

40

60

80 100 120

(f)

0.15 0.10 0.05 0.00

0.0

80 100 120

20

0.20 Fe(II) Concentration (mg/L)

2.0

1.0

486

Fe(III) Concentration (mg/L)


2.5

0

80 100 120

(e)

(d) 3.0

60

0

20

40

60

80 100 120

Time (min)

0

20

40

60

80 100 120

Time (min)

487

Fig. 5 The effect of H2O2 on the concentration of V, Fe(III) and Fe(II) at pH 2.5: (a-c) in the formation

488

of ferric vanadate: the initial concentration of V(V) and Fe(III) are 20 and 25 mg/L, respectively; (d-f)

489

in the dissolution of ferric vanadate.

490


Page 29 of 30


491 492

Fig. 6 Conceptual model for photo-promoted release of V from the dissolution of vanadium

493

titano-magnetite.



494

Table 1 Probable chemical reactions in the vanadium titano-magnetite solution under light irradiation

Equation Reactions for VTM in the light irradiation

2

Fe O s Fe O h + Fe O e

3

h + H O/OH →∙ OH + H

4

e + O →∙ O

5

H +∙ O →∙ OOH

6

2 ∙ OOH → O + H O

7

FeOH ∙ OH + Fe

Fenton Reactions 8

H O + FeII → FeIII + OH +∙ OH

9

∙ OH + H O → H O +∙ OOH

10

∙ OH + FeII → FeIII + OH

11

H O + FeIII → FeII + H +∙ OOH

12

∙ OOH + FeIII → FeII + H + O Redox reactions of V

13

V + O + H O → VO + H

14

VO + H O ↔ VOOH + H

15

VOOH + O → VO +∙ OOH

16

VO +∙ OOH + H O → VO + H O + H

17

VO + H O → VO +∙ OH + H

18

VO +∙ OH → VO +H

19

VO + 2H → VO + Fe + H O + Fe

20

VO + Fe + H O → VO + 2H + Fe

21

Fe + VO + H O → FeVO s

495


Page 30 of 30

Mechanism for Photopromoted Release of Vanadium from Vanadium

Recommend Documents