Article

High-yield Harvest of Nanofibers/Mesoporous Carbon Composite by Pyrolysis of Waste Biomass and Its Application for High Durability Electrochemical Energy Storage Wu-Jun Liu, Ke Tian, Yan-Rong He, Hong Jiang, and Han-Qing Yu Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/es504184c • Publication Date (Web): 05 Nov 2014 Downloaded from http://pubs.acs.org on November 10, 2014

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

Environmental Science & Technology

High-yield Harvest of Nanofibers/Mesoporous Carbon Composite by Pyrolysis of Waste Biomass and Its Application for High Durability Electrochemical Energy Storage

Wu-Jun Liu, Ke Tian, Yan-Rong He, Hong Jiang*, Han-Qing Yu Department of Chemistry, University of Science and Technology of China, Hefei 230026, China



Corresponding author: Dr. Hong Jiang

E-mail: [email protected]

1 ACS Paragon Plus Environment

Environmental Science & Technology

1

ABSTRACTS

2

Disposal and recycling of the large scale biomass waste is of great concern.

3

Themochemically converting the waste biomass to functional carbon nanomaterials and bio-

4

oil is an environmentally-friendly apporach by reducing greenhouse gas emissions and air

5

pollution caused by open burning. In this work, we reported a scalable, “green” method for

6

the synthesis of the nanofibers/mesoporous carbon composites through pyrolysis of the

7

Fe(III)-preloaded biomass, which is controllable by adjustment of temperature and additive of

8

catalyst. It is found that the coupled catalytic action of both Fe and Cl species is able to

9

effectively catalyze the growth of the carbon nanofibers on the mesoporous carbon and form

10

magnetic nanofibers/mesoporous carbon composites (M-NMCCs). The mechanism for the

11

growth of the nanofibers is proposed as an in-situ vapor deposition process, and confirmed by

12

the XRD and SEM results. M-NMCCs can be directly used as electrode materials for

13

electrochemical energy storage without further separation, and exhibit favorable energy

14

storage performance with high EDLC capacitance, good retention capability, and excellent

15

stability and durability (more than 98% capacitance retention after 10,000 cycles).

16

Considering that biomass is a naturally abundant and renewable resource (over billions tons

17

biomass produced every year globally) and pyrolysis is a proven technique, M-NMCCs can

18

be easily produced at large scale and become a sustainable and reliable resource for clean

19

energy storage.

2 ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

20

Environmental Science & Technology

TOC Art

21 22 23 24

25 26 27 28 29 30

3 ACS Paragon Plus Environment

Environmental Science & Technology

31

INTRODUCTION

32

With the increasing of agricultural/industrial production or consumption, the generation

33

of waste biomass has been greatly accelerated.1 For example, in China, it is estimated to

34

generate more than 2.4 billion tons of waste biomass in the year 2010, an increase of 18.1%

35

over the previous year.2 The waste biomass will be an abundantly available resources,

36

whereas if mishandled, it will become a major source of environmental pollution. For instance,

37

the energy contained in the biomass waste of China is amount to that of one billion of

38

standard coal, while the fertilizer value of the nitrogen (N) and phosphorus (P) is more than

39

that of the total chemical fertilizer produced in China. However, due to the lack of facilities,

40

high labor costs, low economic benefit, and tough environmental regulations, it is not

41

economically friendly to recycle the solid waste.3 Instead, most of the biomass waste are

42

currently open burnt directly in many developing countries, causing serious environmental

43

pollution. For example, the incineration of biomass waste will result in serious air pollution

44

due to the emission of heavy metals, particulate matters (e.g., PM 2.5), and dioxin-like

45

compounds during the combustion process.4-7 Therefore, it urgently needs to develop an

46

environmentally friendly and economically feasible technology for recycling the large scale

47

biomass waste.

48

Fast pyrolysis, an thermochemical decomposition process of lignocellulosic biomass

49

under anoxic conditions at an ultrahigh heating-up rate, has been heavily studied and

50

commercially used in recent years8-10 (see Table S1 of Supporting Information (SI)). In a

51

pyrolysis process, not only the renewable liquid fuel, but also the tons of biochar has been

52

produced and has not found its value-added utilization. On the other hand, different

53

carbonaceous materials, such as nanotubes and graphene, have been massively produced and

54

found their application in separation, energy sorage, drug deliver, and bioimaging.11,12 For

55

instance, carbonaceous materials are the most widely used electrical double layer capacitors

56

(EDLC).13-15 Due to the more favorable cycle durability and electrical conductivity of the 4 ACS Paragon Plus Environment

Page 4 of 29

Page 5 of 29

Environmental Science & Technology

57

different carbonaceous materials have led to their use in almost 100% of commercial

58

supercapacitors since 1960th.16 Conventional synthetic routes of cabon nanomaterials, such as

59

chemical vapor deposition, and arc discharge synthesis, etc., usually need tedious and

60

expensive synthesis paths as well as organic solvent and electrochemical treatment, which

61

limit their large-scale production and commercialization.17-19 Although some researchers

62

developed facile methods to prepare carbon nanomaterials by pyrolyzing silk and feathers,12,20

63

using the complicated lignocellulosic biomass which contains ligin, cellulose, semicellulose,

64

and ash to prepare carbon nanomaterials have not been found to date.

65

Recently, we found that the functionalized carbonaceous materials could be formed in

66

the pyrolysis of lignocellulosic biomass by adjusting the pyrolysis temperature.21,22 It is

67

envisioned that we can develop a conceptually new method for in-situ growth of carbon fibers

68

by catalytically reducing and depositing certain volatile low-molecular-weight organic

69

compounds on the carbonaceous skeletons. In addition, the morphology and properties of as-

70

prepared carbon composites could be tunable via deliberated adjustment of temperature and

71

selection of catalysts. Thus, the main objective of this study is to (1) demostrate a new

72

approach to synthesize magnetic nanofiber/mesoporous carbon composites (M-NMCCs) in

73

one-pot by catalytic pyrolysis of lignocellulosic biomass with FeCl3, (2) evaluate the energy

74

storage performance of M-NMCCs, and (3) reveal the formation mechanism of M-NMCCs.

75 76

EXPERIMENTAL SECTION

77 78

Materials. The biomass (sawdust, a naturally abundant lignocellulosic biomass waste) used in

79

this work was collected from a local timber treatment plant in Hefei, China. Before used, the

80

biomass was first washed several times with distilled water to remove the impurity particles

81

and then dried at 378 K overnight. The dried biomass was then crushed by a high-speed rotary

82

cutting mill, and the produced particles with the particle size smaller than 0.12 mm (120 5 ACS Paragon Plus Environment

Environmental Science & Technology

83

mesh) were screened for further use. The proximate analysis and elemental composition of the

84

biomass was analyzed and shown in our previous work.23

85

The precursor for the magnetic carbon nanofibers (M-NMCCs) was the Fe(III)-preloaded

86

biomass, which was prepared in a biosorption process using sawdust as adsorbent at ambient

87

temperature. Briefly, 10.0 g of sawdust and 1,000 mL of FeCl3 solution with a concentration

88

of 10 mmol L–1 were mixed in a flask and shaken in a constant temperature oscillator at 200

89

rpm for 300 min. Afterwards, the water in the mixture was evaporated under reduced pressure,

90

and the solid residue was dried at 378 K overnight and sieved again to collect the particles

91

with size smaller than 120 mesh, and the Fe-preloaded biomass with Fe content of

92

approximately 1.0 mmol g–1 was obtained. For comparison, the Fe(III) preloaded biomass

93

with other Fe source (e.g., Fe2(SO4)3 and Fe(NO3)3) and other metal preloaded biomass (e.g.,

94

CuCl2 and NiCl2) were prepared in the same way.

95

Synthesis of the M-NMCCs. The M-NMCCs were directly synthesized by fast

96

pyrolysis of the Fe-loaded biomass under N2 flow. The fast pyrolysis experiments were

97

performed in a pyrolyzed reactor described in our previous work.23 Briefly, A 4.0 g portion of

98

the Fe-preloaded biomass sample was first placed in the feed pipe under a 400 mL min–1 of N2

99

flow, which was maintained for 20 min to remove air from the pyrolysis system. Once the

100

temperature rose to the setting value (873-1073 K), the Fe-loaded biomass sample was

101

inserted into the quartz tubular reactor with a piston for pyrolysis. The volatiles produced in

102

the pyrolysis process were swept out by the N2 flow (200 mL min–1), and condensed by cold

103

ethanol to obtain bio-oil. When the fast pyrolysis process was accomplished, the solid residue

104

in the heating zone was maintained for another one hour for further carbonization. Finally, the

105

reactor was moved out of the heating zone and cooled in the N2 flow (200 mL min–1) to room

106

temperature, and the M-NMCCs were obtained.

107

Characterizations. The structural features of the M-NMCCs were investigated by

108

nitrogen adsorption-desorption isotherms, which were carried out at 77 K on a Micromeritics 6 ACS Paragon Plus Environment

Page 6 of 29

Page 7 of 29

Environmental Science & Technology

109

Gemini apparatus (ASAP 2020 M+C, Micromeritics, USA). The surface morphology of the

110

M-NMCCs was analyzed by SEM (Sirion 200, FEI electron optics company, USA) coupled

111

with energy dispersive X-ray spectroscopy (EDX, INCA energy, UK) and TEM (JEOL-2100F,

112

Japan). The surface composition and chemical state of the M-NMCCs were studied by X-ray

113

photoelectron spectroscopy (XPS). XRD analysis of the M-NMCCs was carried out in an 18

114

kW rotating anode X-ray diffractometer (MXPAHF, Rigaku, Japan) using nickel-filtered Cu

115

Kα radiation source (30 kV/160 mA, λ=0.154056 nm). The Raman analysis of the M-NMCCs

116

was performed in a Laser Raman spectrometer (LabRamHR, HORIBA Jobin Yvon, France).

117

The radiation source was a laser operating at a wavelength of 514 nm and a power of 25 mW.

118

Energy Storage Performance of the M-NMCCs. The electrochemical tests were

119

conducted on a CHI 760D electrochemical workstation at room temperature in a three-

120

electrode system, in which the Ag/AgCl electrode was used as a reference electrode, platinum

121

wire was used as a counter electrode, and 0.5 mol L–1 of K2SO4 solution served as electrolyte.

122

The work electrode was prepared by loading a slurry which consisted of 80 wt% active

123

material (e.g., M-NMCCs), 10 wt% of conducting agent (carbon black), and 10 wt% of binder

124

(polytetrafluoroethylene (PTFE) in methanol) on a nickel foam and dried at 353 K for 30 min.

125

The determination and calculation of specific capacitance were described in Supporting

126

Information (SI). The electrochemical impedance spectroscopy (EIS) of the material was

127

analyzed in a frequency range of 0.01 to 100,000 Hz, at the open circuit voltage with an

128

alternate current amplitude of 5 mV.

129 130

RESULTS AND DISCUSSION

131 132

Effects of Temperature on the Structure and Composition of M-NMCCs. Pyrolysis

133

temperature is a primary factor influencing the microstructure and morphology of M-NMCCs.

134

Representative images of the M-NMCCs prepared at different temperatures are shown in 7 ACS Paragon Plus Environment

Environmental Science & Technology

135

Fig.S1 (623–773 K) and Fig. 1a-c (873–1073 K). As shown in Figures S1a, b, the nanofiber

136

structure could not be formed at low pyrolysis temperatures (e.g., 623 and 673 K), while as

137

the temperature was increased to 773 K, some small nanofiber structure was found in Fig. S1c.

138

When the temperature was further increased to 873–1073 K, the nanofiber structure

139

continuously grew to several micrometers long, suggesting that a high temperature was

140

favorable to the growth of the nanofiber structure. The high coverage SEM images of the M-

141

NMCCs are presented in Fig.S2, which shows that the carbon nanofibers tightly covered on

142

the mesoporous carbon surface.

143

Fig. 2a shows the Raman spectra of the M-NMCCs. The peaks around wavenumber of

144

1355 and 1592 cm–1 are the characteristic D (defect) and G (graphitic) bands of carbon,

145

respectively. The D band (~1355 cm–1) is attributed to the breathing mode of κ-point phonons

146

of A1g symmetry, which reflects the disorder degree of the carbon materials, while the G band

147

is ascribed to the E2g phonon of sp2 carbon atoms and reflects the graphitization degree of the

148

carbon materials.24 For the M-NMCCs in this work, the intensity of D bands (ID) decreased

149

with the increasing temperature, while the intensity of G bands (IG) increased with the

150

increasing temperature. The high IG/ID value of the M-NMCCs-1073 indicates that the carbon

151

nanofibers growing at a higher temperature had a greater graphitization degree, which is

152

confirmed by the X-Ray Diffraction (XRD) results.

153

The texture features of the M-NMCCs, e.g., surface area and pore structure, were

154

analyzed by the nitrogen adsorption-desorption method. As shown in Fig. 2b, the nitrogen

155

sorption isotherms of the M-NMCCs-873 and M-NMCCs-973 exhibited a typical IV type

156

pattern according to the IUPAC classification,25 confirming the presence of mesopores in

157

these materials. Strangely, differing from most of the porous materials reported

158

previously,16,26 the adsorption and desorption branches of the M-NMCCs-873 and M-

159

NMCCs-973 did not close completely in the relatively low pressures region. These

160

observations were mainly resulted from the presence of a large amount of micropores in the 8 ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

Environmental Science & Technology

161

materials, which trended to be collapsed under high-vacuum conditions in the nitrogen

162

adsorption-desorption process. Similar results were also reported previously.27,28 Differing

163

from the M-NMCCs-873 and M-NMCCs-973, the isotherm of the M-NMCCs-1073 exhibited

164

a classic IV type pattern with an H2 type hysteresis loops, implying the presence of some

165

macropores with non-uniform size and shape.29 With the nitrogen quantity adsorbed at

166

different relative pressures, the surface properties (e.g., surface area, pore volume and size) of

167

the M-NMCCs were calculated and are shown in Table S2. The Brunauer, Em-mett and Teller

168

(BET) surface areas of the M-NMCCs decreased from 421.4 to 360.0 m2 g–1 with an increase

169

in the pyrolysis temperature. The micropore area and volume were dominant in the M-

170

NMCCs-873 and M-NMCCs-973, but significantly decreased in the M-NMCCs-1073,

171

indicating that a high pyrolysis temperature is favorable to the growth of the pore size and

172

volume.

173

The transformation of the Fe species in the pyrolysis process was monitored by XRD

174

(Fig. 2c). The pattern of the M-NMCCs-873 shows 7 peaks at 2θ of 30.1°, 35.7°, 37.1°, 43.2°,

175

53.6°, 56.9°, and 62.7°, which are attributed to the Fe3O4 lattice planes (JCPDS, 19-0629).

176

For the M-NMCCs-973, the new peak at 2θ of 40.6° is assigned to the Fe3C (201) lattice

177

plane (JCPDS, 35-0772). With a further increase in the pyrolysis temperature to 1073 K, the

178

Fe3O4 crystalline phase disappeared, but metallic Fe and Fe3C crystalline were formed.

179

Furthermore, a strong peak due to graphitic carbon (2θ=26.1°) was observed for the M-

180

NMCCs-1073, indicating the formation of the graphitic carbon at high temperatures with the

181

catalysis of the Fe species.30

182

With the XRD results, the transformation of the Fe species in the pyrolysis process can

183

be explained by Eqs. 1–4: Fe3+ was initially hydrolyzed to some amorphous Fe species (e.g.,

184

Fe(OH)3 and FeO(OH)) at 623 K (XRD pattern a in Fig. S3); The amorphous Fe species were

185

then transformed to Fe2O3 at 673 K (XRD pattern b in Fig. S3), which was further reduced to

186

Fe3O4 under mesothermal conditions (e.g., 773–973 K) by the reducing components (e.g., H2, 9 ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 29

31,32

187

CO, and amorphous carbon) formed in the biomass pyrolysis process.

188

metallic Fe was attributed to the further reduction of the Fe3O4 by the amorphous carbon

189

formed during biomass pyrolysis process, while the formation of Fe3C was mainly due to the

190

partial dissolution of carbon atoms into metallic Fe.33 The energy-dispersive X-ray (EDX)

191

spectroscopy reveals that there was 3.79 atom% of Fe in the material, but there were no

192

nanoparticles of Fe species (e.g., Fe, Fe3C, and Fe3O4) in the SEM images (Fig.S4), the

193

possible reason may be that the Fe species were coated by the in situ grown carbon nanofibers.

The formation of

194

Fe3++3H2O →Fe(OH)3+3H+

(1)

195

Fe(OH)3→FeO(OH) →Fe2O3

(2)

196

3Fe2O3+4H2(CO, C)→2Fe3O4+4H2O(CO2, CO)↑

(3)

197

Fe3O4+4C →3Fe+4CO ↑

(4)

198

Effects of Catalysis on the Growing of the Nanofibers. As shown in Fig. 3, the Fe(III)-

199

preloaded biomass was pyrolyzed to produce bio-oil, a renewable liquid as fuel or source of

200

chemicals,8, 34 meanwhile to obtain M-NMCCs. It is a rapid, cost-effective, organic solution

201

free, and readily-scalable route to prepare M-NMCCs. Another important factor affcting the

202

formation of M-NMCCs was the catalyst, and numerous studies were undertaken to prepare

203

nanofibers by catalysis and activation of metalic compounds. It is reported that iron

204

compounds can catalyze the formation of carbon nanofibers and metal chloride can activate

205

the porous carbon.35,36 However, we found that not all ferric salts and chloride can catalyze

206

the formation of M-NMCCs. The nanofibers have not formed by pyrolysis of Fe(NO3)3 and

207

Fe2(SO4)3) or CuCl2 and NiCl2 preloaded biomass (Fig.S5). Hence, it is supposed that the

208

formation of the carbon nanofiber structure was the combined catalytic effects of both Fe(III)

209

and Cl–. To verify this assumption, we pyrolyzed the Fe(NO3)3 and CuCl2 co-loaded biomass,

210

in which Fe(III) and Cl– coexisted, the produced materials exhibited carbon nanofiber

211

structure (Fig.S6). In the thermochemical reaction process without oxygen, FeCl3 can improve

212

the decomposition of celluloses and hemicelluloses into small-molecular hydrocarbons, e.g., 10 ACS Paragon Plus Environment

Page 11 of 29

Environmental Science & Technology

213

CH4, C2H4 and C2H2.37 These hydrocarbons, can deposit on the in-situ formed Fe species, e.g.,

214

Fe3O4 and Fe3C, to grow the carbon nanofibers in a way similar to the chemical vapor

215

deposition process (Fig.3). As evidenced by the transmission electron microscope (TEM)

216

images (insert in Fig. 1a-c), some Fe species nanoparticles were observed on the bottom of the

217

carbon nanofibers, suggesting the deposition and growth of the carbon nanofibers on the Fe

218

species. For Fe(NO3)3 and Fe2(SO4)3, despite of their catalysis on the carbon nanofiber growth,

219

they could not catalyze the formation of small-molecular-weight hydrocarbons, which are the

220

carbon source for the growth of carbon nanofibers. While for CuCl2 and NiCl2, they have the

221

similar effects on the catalytic formation of the small-molecular-weight hydrocarbons in

222

biomass pyrolysis process, but could not catalyze the deposition and growth of the carbon

223

nanofibers. To further confirm the vapor deposition and growth mechanism, we carried out

224

another pyrolysis experiment, in which the feedstock was the FeCl3-preloaded biochar

225

(without further release of small-molecular-weight hydrocarbons). As shown in Fig.S7,

226

though the Fe3O4, Fe, and Fe3C species could be found in the XRD patterns of the products

227

after pyrolysis, the carbon nanofiber structure could not be observed in the SEM images

228

(Fig.S8).

229

Application of the M-NMCCs for Electrochemical Energy Storage. To explore the

230

potential applications of the as-synthesized M-NMCCs, the materials were fabricated into

231

supercapacitor electrodes and characterized with cyclic voltammograms (CV) measurements.

232

Fig. 4a shows the CV curves of the M-NMCCs prepared at different temperatures. The M-

233

NMCCs-1073 exhibited almost rectangular and symmetric CVs, indicating that the dominant

234

contribution of the capacitance was originated from EDLC38,39 The specific capacitance of the

235

M-NMCCs-1073 calculated from its CV curve with a potential scan rate of 50 mV s–1 was 89

236

F g–1, much higher than those of other two M-NMCCs (17 and 24 F g–1 for the M-NMCCs-

237

873 and M-NMCCs-973, respectively). The high capacitance of the M-NMCCs-1073 was

238

mainly attributed to its abundant mesopore and macropore structure (Table S2). It is known 11 ACS Paragon Plus Environment

Environmental Science & Technology

239

that the mesopore and macropore structure can improve the infinitely fast ion transport and

240

decrease the ion “traffic jam” within the pores.40,41 As stated by Dahn et al.,42 When the pores

241

size is less than 1.5 nm in diameter, it can be fully filled by the adsorbed electrolyte ions,

242

causing ion “traffic jam”. While for the large mesopores, due to its big size, it can

243

accommodate more ions within its pore structure.43,44 As the GCD curves shown in Fig. 4d,

244

there is a plateau close to 0 V in the charged curve, suggesting that more electrolyte ions can

245

accommodate, agreeing with the above discussion well.

246

Moreover, the carbon nanofibers were found to enhance the ion diffusion in the electrode

247

and act as electronic bridges between the activated carbon particles, thus greatly improving

248

the capacitance performance of the M-NMCCs-1073.45 Furthermore, as revealed by the

249

Raman spectra (Fig. 3a), the M-NMCCs-1073 showed a higher graphitization degree,

250

endowing it with a good electronic conductivity, thus improving its capacitance

251

performance.46 We also compared the capacitance performance of the carbon materials

252

synthesized by pyrolysis of different Fe(III) (including FeCl3, Fe(NO3)3 and Fe2(SO4)3)

253

preloaded biomass (Fig. S9), the specific capacitances of the carbon materials derived from

254

Fe(NO3)3 and Fe2(SO4)3 preloaded biomass are only 19 and 21 F g–1 at scan rate of 50 mV s–1,

255

much lower than that of the carbon materials derived from FeCl3 (i.e., M-NMCCs-1073, 89 F

256

g–1 at 50 mV s–1). The main reason for this phenomenon is that there is no carbon nanofiber

257

structure in the carbon materials derived from the Fe(NO3)3 and Fe2(SO4)3 preloaded biomass

258

(Fig. S5) and cannot effectively diffuse the ions and transport the electrons between the

259

carbon particles.

260

Fig. 4b shows the CV curves of the M-NMCCs-1073 at different potential scan rates.

261

The CV curves kept the “rectangular shape” even at a potential scan rate of 100 mV s–1. With

262

a further increase in the potential scan rate to 150 and 200 mV s–1, the CV curves were

263

slightly distorted (Fig. S10), which was mainly due to the limited ion incorporation into the

264

active electrode material at high scan rates.47 The specific capacitance of the M-NMCCs-1073 12 ACS Paragon Plus Environment

Page 12 of 29

Page 13 of 29

Environmental Science & Technology

265

was up to 128 F g–1 at a potential scan rate of 2 mV s–1 (Fig. 4c), and the capacitance per

266

surface area reached 0.36 F m–2, much higher than those of many other electric double-layer

267

capacitances reported previously (Table S3).

268

When the potential scan rate was continuously increased to 10 and then to 200 mV s–1,

269

the specific capacitance decreased to 101 and 54 F g–1, respectively. Such a decrease in the

270

specific capacitance was universal, which was possibly caused by the insufficient time

271

available for ion diffusion and transport inside the pores in the materials.19,48 Indeed, at a

272

potential scan rate of 200 mV s–1, the distortion of the rectangular shape of the CV curve was

273

clearly observed (Fig. S11, SI), which is a characteristic of ion diffusion and transport being

274

restricted on the EDLC electrode surface.48 To further understand the ion diffusion and

275

transport characteristic of the M-NMCCs-1073 at different scan rates, the Trasatti’s method

276

was used to analyze the contribution of the total charge stored, which was described by the

277

following equation (Eq.5):

278

q = q0 + k ( v -0.5 )

(5)

279

where q (F/g) is the total stored charge involved in the slow access of electrolyte ions into the

280

electrode materials, v (mV/s) is the scan rate, q0 is the stored charge related to the accessible

281

outer surface, k is a constant, and the kv-0.5 is the stored charge controlled by diffusion. The

282

values of k and q0 can be obtained by plotting the v-0.5 dependence of the total stored charge.

283

Based on the above analysis, the stored charge controlled by the diffusion (kv-0.5) as a

284

function of the scan rates was presented in the insert of Fig. 4c, which further confirmed that

285

with the increasing of the scan rate, the diffusion of the ions into the electrode materials is

286

greatly restrained, thus causing the decrease of the specific capacitance. A small hump was

287

also observed at 0.4–0.6 V (vs Ag/AgCl) of the CV curves (Fig.4b), which can be attributed

288

to pseudocapacitive contribution of the redox process of remained Fe compounds.49,50 As

289

shown in the XRD patterns (Fig. 2c), the main Fe species remained in the carbon nanofibers 13 ACS Paragon Plus Environment

Environmental Science & Technology

Page 14 of 29

290

are Fe3O4 and Fe3C, which are very stable and hard to be released from composites after acid

291

treatment.51

292

To further evaluate the capacitance performance of the M-NMCCs-1073, galvanostatic

293

charge/discharge (GCD) experiments were carried out at different current densities in a three-

294

electrode system. As shown in the GCD curves (Fig. 4d), the discharging curves show a small

295

Ohmic drop of at its start, which is attributed to the present of internal resistance in the

296

electrode materials.52 This internal resistance, as analyzed by the electrochemical impedance

297

spectroscopy, was 1.26 Ω. The specific capacitance was 99.1 F g–1 at a current density of 0.5

298

A g–1, and decreased to 72.0 F g–1 with an increase in the current density to 6.0 A g–1. About

299

72.6% of the specific capacitance was retained when the current density was increased from

300

0.5 to 6.0 A g–1. The reason for a decrease in capacitance is that the effective interactions

301

between the ions and the electrode materials become deficient with the increase in current

302

density. 53

303

The energy and power densities of the M-NMCCs-1073 were calculated by the following

304

equations (Eqs. 6 and 7)[52]

305

1 E= × Cm × (∆V ) 2 2

306

P=

(6)

E ∆t

(7)

307

where E (J g–1) is the energy density, Cm (F) is the specific capacitance deduced from the

308

GCD curves, P is the power density (W g–1), ∆V (V) is the potential change within the

309

discharge time ∆t (s). A Ragone plot is presented in Fig. 4e for the M-NMCCs-1073, which

310

shows that the energy density for the electrode material is about 11.3 Wh/kg at a current

311

density of 0.5 A g–1, and still keeps at 8.0 Wh/kg at a high current density of 6 A g–1. Note

312

that for the state-of-the-art of current electrochemical energy storage devices, the

313

specifications of the energy density are 70-100 and 5-8 wh/kg for the lithium ion batteries and

14 ACS Paragon Plus Environment

Page 15 of 29

Environmental Science & Technology

314

commercial carbon supercapacitors, respectively,54,55 electrodes materials from this work

315

could deliver energy densities slightly better than those of state-of-the-art commercial carbon

316

supercapacitors.

317

The capacitive behavior of the M-NMCCs-1073 was further investigated by the

318

electrochemical impedance spectroscopy (EIS), in which the transport characteristics of the

319

charge carriers within the electrode material were illuminated. The EIS spectrum of the M-

320

NMCCs-1073 electrode was presented in Fig. 4f, and an equivalent circuit (lower inset of

321

Fig.3f) was proposed to fit the spectrum.56 This equivalent circuit was composed of Rs, a

322

resistor accounting for the solution resistance between the reference electrode (Ag/AgCl) and

323

the working electrode (M-NMCCs-1073); Rict, an electrode-electrolyte interfacial charge

324

transfer resistor; Zw, a finite length Warburg diffusion element including the encountered

325

impedances when the electrolyte ions diffuse from the bulk to the electrode-electrolyte

326

interfaces; Rect, a reaction electron transfer resistor accounting for the electron transfer

327

resistance involved in the redox reactions; Cdlc, a capacitor accounting for the electrical

328

double layers formed on the surfaces of the composite electrode in contact with the

329

electrolyte; and Cp, a capacitor accounting for the psudocapacitance generated from the

330

Faradaic redox reactions of the electrode material.

331

As shown in Fig. 4f, a semicircle was found at decreasing frequency, which was more

332

clearly observed from the upper inset of Fig. 4f, indicating that the composite interfacial

333

impedance and psudocapacitance impedance were non-negligible.57 An ‘onset’ frequency can

334

be defined as the highest frequency where the impedance begins to be dominated by the

335

capacitive behavior (i.e., the Nyquist plot starts to go vertical), which reflects the highest

336

frequency to achieve most of the capacitance.38 The ‘onset’ frequency of the M-NMCCs-1073

337

is 89 Hz, higher than many other carbon supercapacitors (e.g., 50 Hz),38 indicating the fast

338

electrolyte ion transfer in the electrode material.

15 ACS Paragon Plus Environment

Environmental Science & Technology

Page 16 of 29

339

One of the most important advantages for the EDLC electrode material is its durability

340

and stability. The long term cycle performance of the M-NMCCs-1073 was evaluated by the

341

CV measurements at a potential scan rate of 50 mV s–1 (Fig. 4g). The specific capacitance still

342

remained at about 87.4 F g–1 after 10,000 cycles, more than 98% retention of the initial

343

capacitance (89.1 F g–1), indicating an excellent durability of the M-NMCCs-1073 used as a

344

supercapacitive electrode material. Furthermore, the rectangle shape of CV curves remained

345

unchanged even after 10,000 times of CV scan, showing the favorable stability of the

346

materials.

347

Environmental Implications. Energy storage in supercapacitors is mainly based on the

348

diffusion and transport of electrolyte ions on the surface of electrode materials.58 The

349

complicated porous structures and disordered texture of porous carbon often limits the

350

electron transfer efficiency and results in a poor electrical conductivity, thus greatly limiting

351

the performance of the supercapacitors.59 An effective method for this problem is to

352

composite the highly conductive carbon frame, e.g., carbon nanotubes and nanofibers, on

353

porous activated carbon, in which the carbon nanotubes/nanofibers can act as a structural

354

frame and an electron collector to improve the electron transfer in the electrochemical energy

355

storage

356

nanofibers/mesoporous carbon composites have much better performance in EDLC energy

357

stroage due to the synergistic effects of nanofibers and mesoporous carbon in which the

358

mesoporous carbon can offer more accessible surface area and pore structure for the migration

359

and diffusion of the electrolyte ions, thus improving the electrochemical energy storage

360

performance.61 Therefore, in this study, about 45%-50% of the initial biomass feedstock can

361

be converted to nanofibers/mesoporous carbon composites, all of which could be used as

362

supercapacitors.

process.60

Whereas,

compared

to

the

pure

carbon

nanofibers,

the

363

Though the specific capacitance of the as-synthesis is releative lower than those of

364

conventional porous carbon based materials, its excellent stability and durability (more than 16 ACS Paragon Plus Environment

Page 17 of 29

Environmental Science & Technology

365

98% capacitance retention after 10,000 cycles) can make them find its applications in many

366

consumer pocket electronics. Considering that biomass is a naturally abundant and renewable

367

resource (over billions tons biomass produced every year globally) and pyrolysis is a proven

368

technique, the M-NMCCs can be easily produced at large scale and become a sustainable and

369

reliable resource for clean energy storage. In addition, a notable observation is that the

370

aggregation of the carbon nanofibers was avoided in pyrolysis, which might be one of the

371

factors responsible for the high performance of M-NMCCs. Besides, we also found that both

372

the yield and quality of bio-oil derived from the FeCl3 proloaded biomass have been improved

373

(Table S4 and Fig.S11), which is beneficial to the large-scale application of this technology.

374 375

Supporting Information

376

Tables S1-S4 and Figures S1-S11 is provided as supporting information for this manuscript.

377

This material is available via the Internet at http://pubs.acs.org

378 379 380

ACKNOWLEDGEMENTS

381

This work is sponsored by the Key Special Program on the S&T for the Pollution Control and

382

Treatment of Water Bodies (No.2012ZX07103-001), National 863 Program (2012AA063608-

383

01), National Key Technology R&D Program of the Ministry of Science and Technology

384

(2012BAJ08B00).

385

REFERENCE

386 387 388 389

(1) Marshall, R. E.; Farahbakhsh, K. Systems approaches to integrated solid waste management in developing countries. Waste Manage. 2013, 33, 988-1003. (2) 2010, the state of the environment in China (in Chinese). Department of Environmental Protection, People's Republic of China 2011. 17 ACS Paragon Plus Environment

Environmental Science & Technology

390 391

(3) Alston, S. M.; Arnold, J. C. Environmental impact of pyrolysis of mixed WEEE plastics part 2: Life cycle assessment. Environ. Sci. Technol. 2011, 45, 9386-9392.

392

(4) Tian, H.; Gao, J.; Lu, L.; Zhao, D.; Cheng, K.; Qiu, P. Temporal trends and spatial

393

variation characteristics of hazardous air pollutant emission inventory from municipal solid

394

waste incineration in China. Environ. Sci. Technol. 2012, 46, 10364-10371.

395

(5) Sakai, S.-I.; Hayakawa, K.; Takatsuki, H.; Kawakami, I. Dioxin-like PCBs released

396

from waste incineration and their deposition flux. Environ. Sci. Technol. 2001, 35, 3601-3607.

397

(6) Cheng, H.; Hu, Y. China needs to control mercury emissions from municipal solid

398

waste (MSW) incineration. Environ. Sci. Technol. 2010, 44, 7994-7995.

399

(7) Alvim-Ferraz, M. C. M.; Afonso, S. A. V. Incineration of different types of medical

400

wastes:  emission factors for particulate matter and heavy metals. Environ. Sci. Technol. 2003,

401

37, 3152-3157.

402 403

(8) Huber, G. W.; Iborra, S.; Corma, A. Synthesis of transportation fuels from biomass:  Chemistry, catalysts, and engineering. Chem. Rev. 2006, 106, 4044-4098.

404

(9) Hu, B.; Wang, K.; Wu, L.; Yu, S.-H.; Antonietti, M.; Titirici, M.-M. Engineering

405

carbon materials from the hydrothermal carbonization process of biomass. Adv. Mater. 2010,

406

22, 813-828.

407 408 409 410

(10) Zhou, C.-H.; Xia, X.; Lin, C.-X.; Tong, D.-S.; Beltramini, J. Catalytic conversion of lignocellulosic biomass to fine chemicals and fuels. Chem. Soc. Rev. 2011, 40, 5588. (11) Simon, P.; Gogotsi, Y. Materials for electrochemical capacitors. Nat. Mater. 2008, 7, 845-854.

411

(12) Li, W; Zhang, Z.; Kong, B.; Feng, S.; Wang, J.; Wang, L.; Yang, J.; Zhang, F.; Wu, P.;

412

Zhao, D. Simple and green synthesis of nitrogen-doped photoluminescent carbonaceous

413

nanospheres for bioimaging. Angew. Chem. Int. Ed. 2013, 52, 8151-8155.

18 ACS Paragon Plus Environment

Page 18 of 29

Page 19 of 29

Environmental Science & Technology

414

(13) Noked, M.; Okashy, S.; Zimrin, T.; Aurbach, D. Composite carbon nanotube/carbon

415

electrodes for electrical double-layer super capacitors. Angew. Chem. Int. Ed. 2012, 51, 1568-

416

1571.

417

(14) Wang, L.; Mu, G.; Tian, C.; Sun, L.; Zhou, W.; Yu, P.; Yin, J.; Fu, H. Porous graphitic

418

carbon nanosheets derived from cornstalk biomass for advanced supercapacitors.

419

ChemSusChem 2013, 6, 880-889.

420

(15) Wen, Z.; Wang, X.; Mao, S.; Bo, Z.; Kim, H.; Cui, S.; Lu, G.; Feng, X.; Chen, J.

421

Crumpled nitrogen-doped graphene nanosheets with ultrahigh pore volume for high-

422

performance supercapacitor. Adv. Mater. 2012, 24, 5610-5616.

423 424

(16) Xie, K.; Qin, X.; Wang, X.; Wang, Y.; Tao, H.; Wu, Q.; Yang, L.; Hu, Z. Carbon nanocages as supercapacitor electrode materials. Adv. Mater. 2012, 24, 347-352.

425

(17) Li, X.; Cai, W.; An, J.; Kim, S.; Nah, J.; Yang, D.; Piner, R.; Velamakanni, A.; Jung,

426

I.; Tutuc, E.; Banerjee, S. K.; Colombo, L.; Ruoff, R. S. Large-area synthesis of high-quality

427

and uniform graphene films on copper foils. Science 2009, 324, 1312-1314.

428

(18) Volotskova, O.; Levchenko, I.; Shashurin, A.; Raitses, Y.; Ostrikov, K.; Keidar, M.

429

Single-step synthesis and magnetic separation of graphene and carbon nanotubes in arc

430

discharge plasmas. Nanoscale 2010, 2, 2281-2285.

431

(19) Wei, L.; Sevilla, M.; Fuertes, A. B.; Mokaya, R.; Yushin, G. Hydrothermal

432

carbonization of abundant renewable natural organic chemicals for high-performance

433

supercapacitor electrodes. Adv. Energy Mater. 2011, 1, 356-361.

434

(20) Gao, L.; Hu, H.; Sui, X.; Chen, C.; Chen Q. One for Two: Conversion of Waste

435

Chicken Feathers to Carbon Microspheres and (NH4)HCO3. Environ. Sci. Technol., 2014, 48,

436

6500-6507.

437

(21) Liu, W.-J.; Jiang, H.; Tian, K.; Ding, Y.-W.; Yu, H.-Q. Mesoporous carbon stabilized

438

MgO nanoparticles synthesized by pyrolysis of MgCl2 preloaded waste biomass for highly

439

efficient CO2 capture. Environ. Sci. Technol. 2013, 47, 9397-9403. 19 ACS Paragon Plus Environment

Environmental Science & Technology

440 441

(22) Liu, W.-J.; Tian, K.; Jiang, H.; Yu, H.-Q. Facile synthesis of highly efficient and recyclable magnetic solid acid from biomass waste. Sci. Rep. 2013, 3, 2419.

442

(23) Liu, W.-J.; Zeng, F.-X.; Jiang, H.; Yu, H.-Q. Total recovery of nitrogen and

443

phosphorus from three wetland plants by fast pyrolysis technology. Bioresour. Technol. 2011,

444

102, 3471-3479.

445 446 447 448

(24) Zhao, Q.; Wagner, H. D. Raman spectroscopy of carbon–nanotube–based composites. Phil. Transac. Royal Soc. London. Ser. A 2004, 362, 2407-2424. (25) Rouquerol, J.; Rouquerol, F.; Sing, K. Adsorption by Powders and Porous Solids, Academic Press, London, 1999.

449

(26) Su, F.; Poh, C. K.; Chen, J. S.; Xu, G.; Wang, D.; Li, Q.; Lin, J.; Lou, X. W. Nitrogen-

450

containing microporous carbon nanospheres with improved capacitive properties. Energy

451

Environ. Sci. 2011, 4, 717-724.

452

(27) Xing, R.; Liu, N.; Liu, Y.; Wu, H.; Jiang, Y.; Chen, L.; He, M.; Wu, P. Novel solid

453

acid catalysts: sulfonic acid group-functionalized mesostructured polymers. Adv. Func. Mater.

454

2007, 17, 2455-2461.

455

(28) Meng, Y.; Gu, D.; Zhang, F.; Shi, Y.; Yang, H.; Li, Z.; Yu, C.; Tu, B.; Zhao, D.

456

Ordered mesoporous polymers and homologous carbon frameworks: Amphiphilic surfactant

457

templating and direct transformation. Angew. Chem. Int. Ed. 2005, 44, 7053-7059.

458

(29) Valente, J. S.; Tzompantzi, F.; Prince, J.; Cortez, J. G. H.; Gomez, R. Adsorption and

459

photocatalytic degradation of phenol and 2,4 dichlorophenoxiacetic acid by Mg–Zn–Al

460

layered double hydroxides. Appl. Catal. B 2009, 90, 330-338.

461

(30) Maldonado-Hódar, F. J.; Moreno-Castilla, C.; Rivera-Utrilla, J.; Hanzawa, Y.;

462

Yamada, Y. Catalytic graphitization of carbon aerogels by transition metals. Langmuir 2000,

463

16, 4367-4373.

464 465

(31) Patwardhan, P. R.; Brown, R. C.; Shanks, B. H. Product distribution from the fast pyrolysis of hemicellulose. ChemSusChem 2011, 4, 636-643. 20 ACS Paragon Plus Environment

Page 20 of 29

Page 21 of 29

Environmental Science & Technology

466

(32) Gong, F.; Ye, T.; Yuan, L.; Kan, T.; Torimoto, Y.; Yamamoto, M.; Li, Q. Direct

467

reduction of iron oxides based on steam reforming of bio-oil: a highly efficient approach for

468

production of DRI from bio-oil and iron ores. Green Chem. 2009, 11, 2001.

469

(33) Prakash, R.; Mishra, A. K.; Roth, A.; Kubel, C.; Scherer, T.; Ghafari, M.; Hahn, H.;

470

Fichtner, M. A ferrocene-based carbon-iron lithium fluoride nanocomposite as a stable

471

electrode material in lithium batteries. J. Mater. Chem. 2010, 20, 1871-1876.

472 473

(34) Mohan, D.; Pittman, C. U.; Steele, P. H. Pyrolysis of wood/biomass for bio-oil: A critical review. Energy Fuels 2006, 20, 848-889.

474

(35) Singh, C.; Quested, T.; Boothroyd, C. B.; Thomas, P.; Kinloch, I. A.; Abou-Kandil, A.

475

I.; Windle, A. H. Synthesis and characterization of carbon nanofibers produced by the floating

476

catalyst method. J. Phys. Chem. B 2002, 106, 10915-10922.

477 478

(36) Tang, N.; Zhong, W.; Gedanken, A.; Du, Y. High magnetization helical carbon nanofibers produced by nanoparticle catalysis. J. Phys. Chem. B 2006, 110, 11772-11774.

479

(37) Edye, L. A.; Richards, G. N.; Zheng, G. Transition metals as catalysts for pyrolysis

480

and gasification of biomass. In Clean Energy from Waste and Coal, American Chemical

481

Society: 1992; Vol. 515, pp 90-101.

482

(38) Li, Z.; Zhang, L.; Amirkhiz, B. S.; Tan, X.; Xu, Z.; Wang, H.; Olsen, B. C.; Holt, C.

483

M. B.; Mitlin, D. Carbonized chicken eggshell membranes with 3D architectures as high-

484

performance electrode materials for supercapacitors. Adv. Energy Mater. 2012, 2, 431-437.

485

(39) Reddy, A. L. M.; Shaijumon, M. M.; Gowda, S. R.; Ajayan, P. M. Multisegmented

486

Au-MnO2/carbon nanotube hybrid coaxial arrays for high-power supercapacitor applications.

487

J. Phys. Chem. C 2009, 114, 658-663.

488

(40) Portet, C.; Yushin, G.; Gogotsi, Y. Electrochemical performance of carbon onions,

489

nanodiamonds, carbon black and multiwalled nanotubes in electrical double layer capacitors.

490

Carbon 2007, 45, 2511-2518.

21 ACS Paragon Plus Environment

Environmental Science & Technology

491 492 493 494

(41) Miller, J. R.; Outlaw, R. A.; Holloway, B. C. Graphene double-layer capacitor with ac line-filtering performance. Science 2010, 329, 1637-1639. (42) Dahn, J.; Zheng, T.; Liu, Y.; Xue, J. Mechanisms for lithium insertion in carbonaceous materials. Science 1995, 270, 590-593.

495

(43) Zhou, H.; Zhu, S.; Hibino, M.; Honma, I.; Ichihara, M., Lithium storage in ordered

496

mesoporous carbon (CMK-3) with high reversible specific energy capacity and good cycling

497

performance. Adv. Mater. 2003, 15, 2107-2111.

498 499 500 501 502 503

(44) Wu, Y.-P.; Wan, C.-R.; Jiang, C.-Y.; Fang, S.-B.; Jiang, Y.-Y. Mechanism of lithium storage in low temperature carbon. Carbon 1999, 37, 1901-1908. (45) Gryglewicz, G.; Śliwak, A.; Béguin, F. Carbon nanofibers grafted on activated carbon as an electrode in high-power supercapacitors. ChemSusChem 2013, 6, 1516-1522. (46) Miller, J. R.; Simon, P. Electrochemical capacitors for energy management. Science

2008, 321, 651-652.

504

(47) Chen, L.-F.; Zhang, X.-D.; Liang, H.-W.; Kong, M.; Guan, Q.-F.; Chen, P.; Wu, Z.-Y.;

505

Yu, S.-H. Synthesis of nitrogen-doped porous carbon nanofibers as an efficient electrode

506

material for supercapacitors. ACS Nano 2012, 6, 7092-7102.

507 508

(48) Conway, B. E. Electrochemical Supercapacitors, Vol. 1, Kluwer Academic/Plenum Publishers , New York, USA 1999. .

509

(49) Mu, J.; Chen, B.; Guo, Z.; Zhang, M.; Zhang, Z.; Zhang, P.; Shao, C.; Liu, Y. Highly

510

dispersed Fe3O4 nanosheets on one-dimensional carbon nanofibers: Synthesis, formation

511

mechanism, and electrochemical performance as supercapacitor electrode materials.

512

Nanoscale 2011, 3, 5034-5040.

513

(50) Li, B.; Wang, Y. Facile fabrication and electrochemical performance of flower-like

514

Fe3O4@C@layered double hydroxide (LDH) composite. J. Mater. Chem. A 2014, 2, 8758-

515

876

22 ACS Paragon Plus Environment

Page 22 of 29

Page 23 of 29

516

Environmental Science & Technology

(51) Liu, W.J.; Tian, K.; Jiang, H.; Yu, H.Q. Facile synthesis of highly efficient and

517

recyclable

518

doi:10.1038/srep02419.

519 520

magnetic

solid

acid

from

biomass

waste.

Sci.

Rep.

2013,

3:2419,

(52) Yan, J.; Khoo, E.; Sumboja, A.; Lee, P. S. Facile coating of manganese oxide on tin oxide nanowires with high-performance capacitive behavior. ACS Nano 2010, 4, 4247-4255.

521

(53) Jafri, R. I.; Mishra, A. K.; Ramaprabhu, S. Polyaniline–MnO2 nanotube hybrid

522

nanocomposite as supercapacitor electrode material in acidic electrolyte. J. Mater. Chem.

523

2011, 21, 17601-17605.

524 525 526 527

(54) John, R.; Miller, A. F. B. Electrochemical capacitors: Challenges and opportunities for real-World applications. Electrochem. Soc. Interface 2008, 17, 53-57. (55) Zhai, Y.; Dou, Y.; Zhao, D.; Fulvio, P. F.; Mayes, R. T.; Dai, S. Carbon materials for chemical capacitive energy storage. Adv. Mater. 2011, 23, 4828-4850.

528

(56) Lin, Y.-H.; Wei, T.-Y.; Chien, H.-C.; Lu, S.-Y. Manganese oxide/carbon aerogel

529

composite: an outstanding supercapacitor electrode material. Adv. Energy Mater. 2011, 1,

530

901-907.

531

(57) Yang, L.; Cheng, S.; Ding, Y.; Zhu, X.; Wang, Z. L.; Liu, M. Hierarchical network

532

architectures of carbon fiber paper supported cobalt oxide nanonet for high-capacity

533

pseudocapacitors. Nano Lett. 2011, 12, 321-325.

534

(58) Chmiola, J.; Yushin, G.; Gogotsi, Y.; Portet, C.; Simon, P.; Taberna, P.-L. Anomalous

535

increase in carbon capacitance at pore sizes less than 1 nanometer. Science 2006, 313, 1760-

536

1763.

537 538 539 540

(59) Zhang, L. L.; Zhao, X. Carbon-based materials as supercapacitor electrodes. Chem. Soc. Rev. 2009, 38, 2520-2531. (60) Bordjiba, T.; Mohamedi, M.; Dao, L. H. New class of carbon-nanotube aerogel electrodes for electrochemical power sources. Adv. Mater. 2008, 20, 815-819.

23 ACS Paragon Plus Environment

Environmental Science & Technology

541 542

(61) Fernandez, J.; Tennison, S.; Kozynchenko, O.; Rubiera, F.; Stoeckli, F.; Centeno, T. Effect of mesoporosity on specific capacitance of carbons. Carbon 2009, 47, 1598-1604.

543 544

24 ACS Paragon Plus Environment

Page 24 of 29

Page 25 of 29

Environmental Science & Technology

545 546

Figure Captions

547 548

Figure 1. SEM and TEM (insert) images of the M-NMCCs: (a) M-NMCCs-873; (b) M-

549

NMCCs-973; and (c) M-NMCCs-1073.

550 551

Figure 2. (a) Raman spectra of the M-NMCCs; (b) nitrogen adsorption-desorption isotherms

552

of the M-NMCCs; and (c) XRD patterns of the M-NMCCs.

553 554

Figure 3. Schematic and mechanism illustration of the synthesis of the magnetic carbon

555

nanofiber from the lignocellulosic biomass waste.

556 557

Figure 4. Electrochemical performance of the M-NMCCs in a three-electrode system. (a)

558

Cyclic voltammograms (CV) curves of M-NMCCs synthesized at different temperature

559

(potential scan rate: 50 mV s-1); (b) CV curves of the M-NMCCs-1073 at different potential

560

scan rate; (c) Specific capacitances of the M-NMCCs-1073 at different potential scan rate; (d)

561

Galvanostatic charge-discharge curves of M-NMCCs-1073 at different current densities; (e)

562

Ragone plots of the M-NMCCs-1073; (f) Electrochemical impedance spectra (Nyquist plot)

563

of the M-NMCCs-1073, the upper inset is an enlargement of the high-frequency region of the

564

Nyquist plot, and the lower inset is the proposed equivalent circuit. (g) Long term cycling

565

performance of M-NMCCs-1073 (potential scan rate: 50 mV s-1).

566

25 ACS Paragon Plus Environment

Environmental Science & Technology

Figure 1

26 ACS Paragon Plus Environment

Page 26 of 29

Page 27 of 29

Environmental Science & Technology

Figure 2

27 ACS Paragon Plus Environment

Environmental Science & Technology

mechanism

Figure 3

28 ACS Paragon Plus Environment

Page 28 of 29

Page 29 of 29