Microstructured Silicon–Graphite Composite Anode for High

5 days ago - With the ever-increasing demand for lithium-ion batteries (LIBs) with higher energy density, tremendous attention has been paid to design...
0 downloads 0 Views 1MB Size
Subscriber access provided by UNIV OF NEW ENGLAND ARMIDALE

Article

Nano/Micro-Structured Silicon-Graphite Composite Anode for High-Energy Density Li-Ion Battery Peng Li, Jang-Yeon Hwang, and Yang-Kook Sun ACS Nano, Just Accepted Manuscript • DOI: 10.1021/acsnano.9b00169 • Publication Date (Web): 13 Feb 2019 Downloaded from http://pubs.acs.org on February 14, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 25 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Nano

Nano/Micro-Structured Silicon-Graphite Composite Anode for High-Energy Density Li-Ion Battery Peng Lia, Jang-Yeon Hwanga and Yang-Kook Suna* a Department

of Energy Engineering, Hanyang University, Seoul 133-791, Republic of Korea

* Corresponding author. E-mail: [email protected]

ABSTRACT: With the ever-increasing demand for lithium ion batteries (LIBs) with higher energy density, tremendous attention has been paid to design various silicon active materials as alternative electrodes due to its high theoretical capacity (ca. 3579 mAh g-1). However, replacing the commercially utilized graphite totally with silicon is still insurmountable owing to bottlenecks such as low electrode loading and insufficient areal capacity. Thus, in this study, we turn eyes back on enhanced graphite electrode through the cooperation of modified silicon via a facile and scalable blending process. The modified nano/micro-structured silicon with boron doping and carbon nanotube wedging (B-Si/CNT) can provide improved stability (88.2% retention after 200 cycles at 2000 mA g-1) and high reversible capacity (approximately 2426 mAh g-1), while the graphite can act as a tough framework for high loading. Owing to the synergistic effect, the resultant B-Si/CNTgraphite composite (B-Si/CNT@G) shows an high areal capacity of 5.2 mAh cm-2 and excellent cycle retention of 83.4 % over 100 cycles even with ultra-high active mass loading of 11.2 mg cm2,which

could significantly surpass the commercially used graphite electrode. Notably, the

composite also exhibits impressive application in Li-ion full battery using 2 mol% Al-doped full concentration gradient Li[Ni0.76Co0.09Mn0.15]O2 (Al2-FCG76) as cathode with excellent capacity retention of 82.5% even after 300 cycles and an outstanding energy density (8.0 mWh cm-2) based 1 ACS Paragon Plus Environment

ACS Nano 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

on the large mass loading of cathode (12.0 mg cm-2).

KEYWORDS: silicon, graphite, electrode loading, areal capacity, lithium ion battery

To address global climate change issues, electric vehicles, hybrid electric vehicles, and energy storage systems equipped with lithium-ion batteries (LIBs) are intensively used nowadays.1 Graphite has been used as the most common active material for negative electrodes in commercially available LIBs because of its low potential, abundant reserves, and good stability.2 However, its limited theoretical capacity (372 mAh g−1) still falls short of the energy density and capability required to meet ever-growing demands and cannot surpass the excellent mileage of internal combustion vehicles (approximately 400 miles).3,4 Thus, the development of advanced anodes with high Li+ storage capacity at low working voltage has long been pursued to overcome this limitation and realize high energy and power density. To date, various active materials with higher theoretical capacities have been proposed to replace graphite, e.g., silicon, tin, and germanium.3 Owing to its high theoretical gravimetric capacity (ca. 4200 mAh g-1 at 415 °C in the form of Li22Si5; 3579 mAh g-1 at room temperature in the form of Li15Si4), relatively low redox voltage (