Model Transient Networks from Strongly Hydrogen-Bonded Polymers

Sep 17, 2009 - The reversible junctions in transient networks typically contain areas of hydrophobic associations,(7-10) hydrogen bonding,(11-17) meta...
8 downloads 11 Views 3MB Size
9072

Macromolecules 2009, 42, 9072–9081 DOI: 10.1021/ma901668w

Model Transient Networks from Strongly Hydrogen-Bonded Polymers Kathleen E. Feldman,† Matthew J. Kade,‡ E. W. Meijer,§ Craig J. Hawker,*,‡,† and Edward J. Kramer*,†,^ † Materials Department, University of California, Santa Barbara, California 93106, ‡Department of Chemistry and Biochemistry, University of California, Santa Barbara, California 93106, §Laboratory of Macromolecular and Organic Chemistry, Eindhoven University of Technology, Eindhoven, The Netherlands, and ^ Department of Chemical Engineering, University of California, Santa Barbara, California 93106

Received July 28, 2009; Revised Manuscript Received August 28, 2009

ABSTRACT: Random copolymers consisting of n-butyl acrylate backbones with quadruple hydrogenbonding side chains based on 2-ureido-4[1H]-pyrimidinone (UPy) have been synthesized via controlled radical polymerization and postpolymerization functionalization. Through this synthetic strategy high UPy monomer content (15 mol %) can be reached while maintaining low polydispersity and excellent control over molecular weight, providing model reversible networks with well-defined molecular architecture. Despite low Tgs and a lack of entanglements or crystallinity, these materials behave as thermoplastic elastomers through the strong but reversible association of UPy groups. Bulk properties such as the plateau modulus, tensile modulus, and relaxation time scale are primarily determined by the average distance between UPy’s along the chain. Starting from a difunctional initiator, triblock copolymers can also be synthesized containing a homopolymer midblock and random copolymer end blocks, effectively concentrating the hydrogen-bonding groups near the chain ends. By controlling both the average composition and distribution of UPy’s along the polymer chain, macroscopic material properties such as stiffness and resistance to creep can be independently tuned.

Introduction Thermoplastic elastomers (TPEs) encompass a broad class of materials that can be processed, for example, by molding or extrusion, at elevated temperatures yet are elastomeric at ambient temperature. Typically such behavior arises through a phaseseparated microstructure in which “hard” domains are bridged by “soft” rubbery chains; when a stress is applied to the material, the hard domains serve to pin the polymer chains and prevent macroscopic deformation, while the rubbery chains provide elasticity through the connectivity of the network. Transient networks, in which the junctions can be reversibly broken and re-formed, are interesting from both fundamental and applied standpoints; many reversibly associating polymers have been synthesized for use as rheological property modifiers or physical gels, and numerous theories have been presented1-6 to describe their equilibrium and dynamic properties. The reversible junctions in transient networks typically contain areas of hydrophobic associations,7-10 hydrogen bonding,11-17 metal-ligand interactions,18,19 or ionic associations.20,21 In many cases such junctions are poorly defined aggregates with unknown association strength and kinetics, but in a few transient network materials bulk properties have been directly correlated to defined polymer microstructure or well-characterized reversible interactions leading to important insights into the properties of these systems. In an early series of papers, Stadler and Freitas11,22-24 studied the rheological behavior of polybutadienes lightly modified with double-hydrogen-bonding phenylurazole groups, finding that even with light substitution along the backbone the storage modulus plateau was broadened and shifted to lower frequencies (although the overall network properties were primarily dictated by the highly entangled polymer backbone and the crystallization of the phenyl urazole side chains). More *To whom correspondence should be addressed. E-mail: hawker@ mrl.ucsb.edu (C.J.H.); [email protected] (E.J.K.). pubs.acs.org/Macromolecules

Published on Web 09/17/2009

recently, reversible networks based on metal-ligand coordination have been synthesized and the macroscopic material properties directly related to the coordination dynamics;25-28 in this case it was found that formation of a strong network required not just a high association constant but also slow dynamics of the reversible bond. Additionally, supramolecular gels based on hydrogen bonding in ionic liquids have been demonstrated and their rheological properties related to the strength and number of hydrogen bonds as well as stoichiometry of donor and acceptor units.29,30 To broaden the scope and applicability of supramolecular polymer chemistry, many new strongly hydrogen-bonding moieties have been synthesized31-37 and incorporated into networkforming materials.12-15,38-41 The strength and specificity of multiple-hydrogen-bonded (MHB) groups vary widely, from weakly complementary pyridine-phenol pairs42 to extremely strong, self-complementary 6-H-bonded dimers.31 The 2-ureido4[1H]-pyrimidinone (UPy) group first reported by Sijbesma et al.12 was developed as a synthetically accessible, exceptionally strong (Kdim = 6  107 M-1 in CDCl3) quadruple-hydrogenbonded dimer in order to create highly thermally responsive polymeric materials. By attaching UPy’s to both ends of short, low-Tg oligomers, materials were produced which, at low temperature, bonded end to end to give high molecular weight polymer chains. On heating, the bonds between the oligomers dissociate and the material flows like a liquid. A number of other telechelic, UPy-based materials have been demonstrated to show similar behavior;43-46 although useful, they generally rely on crystallization of the UPy dimers into long stacks to achieve mechanical stability, similar to the crystallization typically seen in segmented polyurethane thermoplastic elastomers. Later work showed that the nature of the linker joining the UPy group to the polymer chain dramatically affects the macroscopic properties. When an additional urea or urethane is present near the UPy group, lateral hydrogen bonding between dimers is enhanced, r 2009 American Chemical Society

Article

which results in the crystallization of the dimers into long stacks.39 Alternately, bulky substituents near UPy’s prevent such crystallization while linear alkyl chains enhance it.40 In both cases, the presence of crystalline stacks (rather than simple pairwise UPy-UPy association) was shown to be crucial for network formation and good mechanical properties. Examples of UPy-based segmented TPEs have also been presented in which the MHB groups comprise the “hard” segments of longer chains,47,48 and several groups have also begun to incorporate UPy groups into higher molecular weight polymers as side chains via random copolymerization of a UPy-functional alkene15 or methacrylate monomer.14,38,49,50 Although the low solubility of the UPy methacrylate monomer limited its incorporation to 10 mol % or less, a higher degree of control over the bulk properties can be achieved via this route by varying any number of parameters including the concentration of UPy’s in the chain, the total molecular weight, and the type of comonomer. In particular, it has been demonstrated that the melt viscosity and adhesive properties of random copolymers of n-butyl acrylate and UPy-methacrylate14 together with the creep compliance of random copolymers of ethylhexyl methacrylate and UPy-methacrylate49 can be widely varied by the concentration of UPy’s along the backbone. Although prior work has addressed the question of how the overall concentration of UPy monomer in random copolymers affects the bulk properties, most of the materials studied were synthesized via conventional radical polymerization leading to poor control over the chain architecture, molecular weight, and polydispersity. In this work we demonstrate a new synthetic strategy involving postpolymerization functionalization which allows well-defined precursor polymers to be prepared via atom transfer radical polymerization (ATRP) of n-butyl acrylate and a Boc-protected amine functional monomer. This allows for architectural control and higher incorporation of UPy’s in the final polymers as well as effective control over the chain length and repeat unit distribution. By keeping the primary chain length below the entanglement molecular weight, the effects of the reversible interaction on the dynamics can be isolated from those due to reptation, in contrast with most prior examples of bulk transient networks. As a result, new questions about these materials, such as the relative importance of backbone molecular weight and overall concentration of UPy’s, can be addressed. Additionally, we show that by controlling the distribution of UPy’s along the chain through a triblock-like architecture it is possible to greatly improve the utility of such materials while minimizing the amount of functional monomer required. Experimental Section Methods. All synthetic procedures were performed under an inert atmosphere of dry nitrogen unless stated otherwise. N,NDimethylformamide (DMF) was dried over 4 A˚ molecular sieves. tert-Butyl 6-hydroxyhexylcarbamate was prepared as reported by Forbes et al.51 Tris[2-(dimethylamino)ethyl]amine (Me6TREN) was prepared as reported by Queffelec et al.52 2(1-Imidazolylcarbonylamino)-6-methyl-4-[1H]-pyrimidinone was prepared as reported by Keizer et al.53 Ethane-1,2-diyl bis(2-bromo-2-methylpropanoate) was synthesized as reported by Matyjaszewski et al.54 n-Butyl acrylate was purified by passing over neutral alumina. Acryloyl chloride was distilled prior to use. All other chemicals were obtained from Aldrich and used as received. Analytical TLC was performed on commercial Merck plates coated with silica gel GF254 (0.24 mm thick). 1H NMR (500 MHz) and 13C NMR (125 MHz) were performed on a Bruker AVANCE500 spectrometer at room temperature. Proton chemical shifts are reported in ppm downfield from tetramethylsilane (TMS). The following splitting patterns are designated as s,

Macromolecules, Vol. 42, No. 22, 2009

9073

singlet; d, doublet; t, triplet; q, quartet; b, broad; m, multiplet; and dd, double doublet. Carbon chemical shifts are reported downfield from TMS using the resonance of the deuterated solvent as the internal standard. Size exclusion chromatography was carried out at room temperature on a Waters chromatograph connected to a Waters 410 differential refractometer and six Waters Styragel columns (five HR-5 μm and one HWM-20 μm) using THF as eluent (flow rate: 1 mL/min). A Waters 410 differential refractometer and a 996 photodiode array detector were employed. The molecular weights of the polymers were calculated relative to linear polystyrene standards. Fourier transformed infrared spectroscopy was performed using a PerkinElmer Spectrum One spectrometer equipped with a Universal ATR accessory. Spectra are the sum of 16 scans acquired at a resolution of 4 cm-1. Electrospray ionization time-of-flight (ESI-TOF) data were obtained on a Micromass QTOF2 quadrupole/time-of-flight tandem mass spectrometer. Differential scanning calorimetry data were acquired on a TA Instruments Q2000 modulated DSC at a heating rate of 5 C. Data presented are from the second heating after a single cycle from -75 to 100 C. Rheological measurements were performed on an ARES rheometer from TA Instruments. Most samples were measured using a 25 mm cone and plate geometry (cone angle 0.1 rad), but for high-modulus materials it was necessary to use 8 mm parallel plates with a gap of 0.7 mm. Strain sweeps were performed at each temperature to ensure that measurements were made in the linear viscoelastic regime. Synthesis. 6-(tert-Butoxycarbonylamino)hexyl Acrylate (t-BocAHA). tert-Butyl 6-hydroxyhexylcarbamate (20 g, 92 mmol) and triethylamine (20 mL, 138 mmol) in dry methylene chloride (100 mL) were stirred at 0 C. Acryloyl chloride (8.2 mL, 101 mmol) was added dropwise via syringe. The mixture was allowed to warm to room temperature and stirred overnight. Water was added (100 mL) to dissolve salts and hydrolyze any remaining acryloyl chloride, and the mixture stirred for 30 min. The organic layer was separated and washed with 1 N HCl (1  50 mL), NaHCO3 (saturated, 1  50 mL), and brine (1  50 mL) and dried over sodium sulfate. The crude mixture was separated by flash column chromatography eluting with 1% methanol in methylene chloride to give a clear viscous oil (22.2 g, 89%). 1H NMR (CDCl3): d = 6.30 (dd, 1H), 6.04 (dd, 1H), 5.75 (dd, 1H), 4.65 (br, 1H), 4.07 (t, 2H), 3.03 (br, 2H), 1.60 (m, 2H), 1.42 (m, 2H), 1.36 (s, 9H), 1.34-1.25 ppm (m, 4H). 13C NMR (CDCl3): 166.2, 156.0, 130.4, 128.5, 78.8, 64.4, 40.4, 29.9, 28.4, 26.4, 25.6 ppm. FTR-IR (ATR): ν = 3364.9, 2932.9, 2860.9, 1710.0, 1692.7, 1636.5, 1619.4, 1516.3 cm-1. ESI-MS (m/z): calcd: 294.17 (M þ Naþ); found: 294.17 (M þ Naþ), 310.14 (M þ Kþ). Poly(n-butyl acrylate-r-Boc-aminohexyl acrylate). n-Butyl acrylate (3.24 g, 25.3 mmol), 6-(tert-butoxycarbonylamino)hexyl acrylate (0.726 g, 2.70 mmol), methyl 2-bromopropionate (31 mg, 1.9 mmol), and Me6TREN (60 mg, 1.9 mmol) were sparged in a round-bottom flask with nitrogen for 10 min. CuBr (27 mg, 1.9 mmol) was added under flowing nitrogen. The flask was sealed and placed in a 70 C oil bath for 45 min, then the polymerization was quenched by opening the flask to air and diluting with methylene chloride. The reaction mixture was washed with water (3  50 mL), 0.1 M EDTA (3  50 mL), and brine (1  50 mL), then dried over sodium sulfate, and evaporated. Residual monomer was removed by heating the polymer under high vacuum at 50 C overnight to give P(nBA-r-t-Boc-AHA), Mn 24 600 g/mol, PDI 1.21 (THF GPC). 1H NMR (CDCl3): 4.68, 4.02, 3.10, 2.32, 1.90, 1.60, 1.43, 1.37, 0.93 ppm. 13C NMR (CDCl3): 174.5, 155.97, 79.0, 64.5, 41.4, 40.5, 36.3, 35.4, 30.6, 30.0, 28.4, 26.4, 25.6, 19.1, 13.7 ppm. FTR-IR (ATR): ν = 3391.3, 2932.9, 2933.8, 5869.4, 1723.6, 1636.6, 1516.4 cm-1. Poly(n-butyl acrylate-r-aminohexyl acrylate) (TFA Salt). P(nBA-r-t-Boc-AHA) (3.00 g) was dissolved in 25 mL of

9074

Macromolecules, Vol. 42, No. 22, 2009 Scheme 1. Synthesis of P(nBA-r-UPyA)

methylene chloride. TFA (25 mL) was added, and the mixture was stirred overnight. Solvent and excess TFA were removed by a rotavap, and residual TFA was removed by coevaporation with methanol followed by heating to 50 C under high vacuum overnight to give P(nBA-r-AHA). 1H NMR (CDCl3): 7.77, 4.02, 3.04, 2.32, 1.90, 1.60, 1.37, 0.93 ppm. 13C NMR (CDCl3): 174.7, 64.7, 41.5, 40.0, 36.2, 35.2, 30.5, 28.1, 27.1, 25.7, 25.1, 19.0, 13.6 ppm. FTR-IR (ATR): ν = 2960.3, 2938.0, 2873.9, 1726.5, 1677.5, 1524.6 cm-1. Poly(n-butyl acrylate-r-UPy acrylate). P(nBA-r-AHA) (3.00 g) was dissolved in dry DMF (25 mL). Triethylamine (3 equiv per amine) and 2-(1-imidazolylcarbonylamino)-6-methyl4-[1H]-pyrimidinone (1.5 equiv per amine) were added, and the mixture was heated to 100 C overnight. Excess DMF was removed by a rotavap, and the polymer was precipitated into methanol to give P(nBA-r-UPyA). 1H NMR (CDCl3): 13.13, 11.87, 10.17, 5.82, 4.02, 3.25, 2.32, 1.90, 1.60, 1.37, 0.93 ppm. Limited solubility of UPy-functional polymers in CDCl3 precluded the acquisition of reliable 13C NMR spectra. FTR-IR (ATR): ν = 2957.6, 2932.4, 2872.7, 1729.3, 1698.4, 1661.8, 1586.2, 1524.6, 1448.2 cm-1. ABA Triblock Copolymers. Triblock copolymers were prepared by a similar method to the random copolymers as shown in Scheme 2. The midblock of PnBA was first polymerized using a difunctional initiator with 2 equiv of CuBr/Me6TREN complex and purified by precipitation from acetone into cold methanol. The random copolymer end blocks were then poly merized from the PnBA macroinitiator via the procedure described previously, followed by deprotection of the Boc groups and functionalization with CDI-activated methylisocytosine.

Results and Discussion Synthesis of Side-Chain UPy-Functionalized Polymers. Initial attempts at the synthesis of random copolymers from UPy-functional monomers met with limited success. A UPybased acrylic monomer was synthesized, and random copolymers with n-butyl acrylate could be prepared at low UPy incorporation (