Nanosize Effects, Physicochemical Properties, And Catalytic Oxidation

Jan 26, 2009 - Characterization data prove that the redox-precipitated system ... also accounting for the better stability of the redox-precipitated s...
0 downloads 0 Views 2MB Size
2822

J. Phys. Chem. C 2009, 113, 2822–2829

Nanosize Effects, Physicochemical Properties, And Catalytic Oxidation Pattern of the Redox-Precipitated MnCeOx System Francesco Arena,*,†,‡ Giuseppe Trunfio,† Barbara Fazio,§ Jacopo Negro,† and Lorenzo Spadaro‡ Dipartimento di Chimica Industriale e Ingegneria dei Materiali, UniVersita` degli Studi di Messina, Salita Sperone 31 c.p. 29, I-98166 S. Agata (Messina), Italy, Istituto CNR-ITAE “Nicola Giordano”, Salita S. Lucia 5, I-98126 S. Lucia (Messina), Italy, and Istituto di Processi Chimico-Fisici del CNR (CNR-IPCF) di Messina, Salita Sperone Contrada Papardo, I-98158 Faro Superiore (Messina), Italy ReceiVed: July 31, 2008; ReVised Manuscript ReceiVed: December 9, 2008

A series of nanostructured MnCeOx catalysts with superior textural and redox properties in comparison to coprecipitated systems was synthesized via the “redox-precipitation” route (Chem. Mater. 2007, 19, 2269). Characterization data prove that the redox-precipitated system consists of uniformly sized (d ≈ 20 nm) spherical nanoparticles ensuring large surface area (120-260 m2/g) and pore volume (0.5-0.6 cm3/g), and a regular pore size distribution in a wide range of Mn/Ce ratios (1/3 to 3/1). The lack of long-range crystalline order and a homogeneous chemical composition signal that Mn and Ce oxides form composite nanodomains with a molecular dispersion of the active phase. Superior MnOx accessibility, strong MnOx-CeO2 interaction, and higher average oxidation number of both Mn and Ce ions strongly promote the reactive surface oxygen availability and the CO oxidation activity in the range of 323-423 K, also accounting for the better stability of the redox-precipitated system under reaction conditions. Introduction The urgent need to mitigate the harmful impact of anthropic activities on the environment is pressing the implementation of catalytic processes for effective waste detoxification. However, the extensive use of noble-metal catalysts represents to date a major drawback to the economical feasibility of present technologies. A major scientific concern, focused on low-cost catalyst formulations, allowed ascertaining the performance of MnCeOx systems for environmental applications, including wet air oxidation (CWAO) of toxic and biorefractory pollutants in wastewaters,1-7 total oxidation of volatile organic compounds (VOCs),8-14 and CO,15,16 and selective reduction (SCR) of NOx.16,17 Structure, dispersion, and chemical composition influence the catalytic pattern of the MnCeOx system having a superior activity generally associated with higher oxidation states (>+3) of Mn ions,4,5,8,9,11,16-22 while stability and lifetime mostly rely on type and dispersion of MnOx phases and strength of the oxide-supportinteraction.4,15-17 Thenspecialsynthesisroutes5-17,23-25 and adjustments in composition4-6,19-26 were adopted for tuning the catalytic pattern of the title system. For instance, Qi and Yang reported that the sol-gel method promotes the NOx SCR activity,17 while a modified coprecipitation route enhances the VOC combustion functionality of MnOx-CeO2 catalysts.8 Further, Larachi et al. found an optimum Mn/Ce atomic ratio and a promoting effect of K on the phenol CWAO activity,4,21 while Abecassis-Wolfovich et al. related a high chlorophenol CWAO performance of “nanocasted” MnCeOx catalysts to very large surface area and presence of a Mn5O8 phase.6 Likewise, the redox-precipitation route enhances the CWAO activity of * Corresponding author, [email protected]. † Dipartimento di Chimica Industriale e Ingegneria dei Materiali, Universita` degli Studi di Messina. ‡ Istituto CNR-ITAE “Nicola Giordano”. § Istituto di Processi Chimico-Fisici del CNR (CNR-IPCF) di Messina.

the MnCeOx system, owing to markedly better surface texture and active phase dispersion.5,23-25 Overall, such improved catalytic pattern depends on peculiar features of nanostructured materials since, besides a much higher surface area, a particle size smaller than 10 nm enables unprecedented electronic properties that strongly accelerate redox reactions.6,15,23-29 Therefore, this paper addresses the effects of preparation method and composition on the textural, redox, and catalytic properties of the MnCeOx system. Experimental data show that the redox-precipitation route leads to nanostructured systems with higher surface area, uniform pore size distribution, and molecular-like oxide dispersion, greatly promoting the surface oxygen mobility and the CO oxidation activity of MnCeOx catalysts. Experimental Methods Catalyst Preparation. MnCeOx catalysts with Mn/Ce atomic ratio (x/y) ranging between 1/3 and 3/1 (MxCy-R) were obtained via the redox-precipitation route,5,23-25 consisting of titrating the KMnO4 precursor (≈10 g/L) with an aqueous solution of Ce3+-Mn2+ salts at constant pH (8.0 ( 0.2)

MnO4- + 3e- + 2H2O f MnO2 V + 4HO-

(1)

Mn2+ + 4HO- f MnO2 V + 2e- + 2H2O

(2)

Ce3+ + 4HO- f CeO2 V + e- + 2H2O

(3)

After titration, the solids were filtered, washed, and dried at 373 K (16 h) and further calcined (4 h) in air at 673 K (MxCyR4). A coprecipitated MnCeOx sample (Mn/Ce, 1) calcined at 673 K (M1C1-P4) was taken as reference.4,5,22-25 The list of samples with the relative notation and main physicochemical properties is given in Table 1. Catalyst Characterization. Surface area (SA) and pore size distribution (PSD) were obtained from N2 physisorption mea-

10.1021/jp8068249 CCC: $40.75  2009 American Chemical Society Published on Web 01/26/2009

Nanostructured MnCeOx Catalysts

J. Phys. Chem. C, Vol. 113, No. 7, 2009 2823

TABLE 1: List of Catalysts and Main Physicochemical Properties Mn/Cea catalyst

preparation method

des.

exptl

Mn (wt %)

M1C3-R M1C3-R4 M3C4-R M3C4-R4 M1C1-R M1C1-R4 M3C2-R M3C2-R4 M2C1-R M2C1-R4 M3C1-R M3C1-R4 M1C1-P4

redox-precipitation

0.33

0.34

9.3

Tcalcd (K) 673

redox-precipitation

0.75

0.71

16.7

redox-precipitation

1.00

0.95

20.5

redox-precipitation

1.50

1.44

26.6

redox-precipitation

2.00

2.12

32.7

redox-precipitation

3.00

2.76

36.8

coprecipitation

1.00

1.00

21.2

673 673 673 673 673 673

a Mn/Ce atomic ratio from design and XRF measurements, respectively. measurements.

surements (77 K), using an ASAP 2010 (Micromeritics Instruments) static adsorption device. Isotherms were elaborated by the BET method for SA calculation, while micro- and mesopore distributions were obtained by Horvath-Kavazoe and BJH methods, respectively. Scanning electron microscopy (SEM) analyses were performed using a field emission ZEISS Supra 25 microscope, working with an accelerating voltage of 5-10 kV, after Ptsputtering of the samples. Transmission electron microscopy (TEM) analysis was performed using a PHILIPS CM12 microscope on catalyst samples ultrasonically dispersed in isopropanol and deposited over a thin carbon film supported on a standard copper grid. Micro-Raman spectra were taken at room temperature in back-scattering geometry, using a He-Ne laser excitation source (λ, 632.8 nm) focused onto the sample with a microscope (50×). An incident power of 0.5 mW was used to avoid thermal laserinduced effects. The signal was collected by the microscope, dispersed by a HR460 monochromator (Horiba-Jobin Yvon), and detected by a charge-coupled device array sensor (77 K) with a resolution of ca. 3 cm-1. X-ray photoelectron spectroscopy (XPS) data were obtained using a Physical Electronics GMBH PHI 5800-01 spectrometer operating with monochromatized Al KR radiation with a power beam of 350 W. The pass energy for determination of the oxidation state and concentration of surface species were 11.0 and 58.0 eV, respectively. The BE regions of C 1s (280-300 eV), Mn 2p (635-680 eV) and Ce 3d (870-935 eV) were investigated, taking the C1s line (284.8 eV) of adventitious carbon as reference. X-ray diffraction (XRD) analysis was performed by a Philips X-Pert diffractometer operating with Ni β-filtered Cu KR radiation (40 kV; 30 mA) and a scan rate of 0.05 deg/min. Reactive surface oxygen availability (RSOA) measurements in the range 293-423 K were carried out in continuous mode using a 10% CO/He mixture as carrier gas (30 stp mL min-1). A catalyst sample (≈30 mg) was loaded into a quartz microreactor, heated in a 10% O2/He flow to 423 K (10 K/min), and then kept under isothermal conditions for 30 min. After the sample was allowed to cool to room temperature, the reactor was switched in the CO/He carrier and heated to 323, 373, or 423 K, manitaining isothermal conditions until the end of CO2 formation (reduction step). Thereafter, oxygen treatment (oxidation step) in the 10% O2/He flow at the same temperature was performed. Three reduction-oxidation cycles were run on each sample to address the catalyst stability.

b

SA (m2/g)

PV (cm3/g)

APD b (nm)

Mn/Ce c

259 168 239 169 226 154 208 157 206 140 185 117 101

0.31 0.28 0.53 0.47 0.61 0.49 0.62 0.45 0.59 0.50 0.52 0.46 0.24

4.3 5.1 6.0 7.2 8.5 11.7 9.7 14.3 10.4 16.7 12.4 18.3 9.4

n.d. 0.58 n.d. 1.00 1.32 1.33 n.d. 1.80 n.d. 2.69 n.d. 3.42 0.40

Average pore diameter.

c

Mn/Ce atomic ratio from XPS

Figure 1. Influence of the Mn/Ce atomic ratio on surface area (SA) and average pore diameter (APD) of dried and calcined “redoxprecipitated” catalysts.

Catalyst Testing. Kinetic measurements of CO oxidation in the range of 323-423 K were performed using a linear quartz microreactor (dint, 4 mm) loaded with a catalyst sample (dp, 0.03-0.05 mm) of 0.03-0.1 g diluted with 0.5 g of SiC (dp, 0.3-0.5 mm). A CO/O2/He mixture in the molar ratio 2/1/22 was fed at the rate of 0.1 stp L/min to ensure differential conversion levels (i.e.,