New Insights into the Stability of Silver Sulfide ... - ACS Publications

Jun 13, 2017 - School of Sciences, Zhejiang Sci-Tech University, Hangzhou 310018, China. ‡. Institute of Quality and Standard of Agro-Products, Zhej...
0 downloads 0 Views 643KB Size
Subscriber access provided by EAST TENNESSEE STATE UNIV

Article

New Insights into the Stability of Silver Sulfide Nanoparticles in Surface Water: Dissolution through Hypochlorite Oxidation Lingxiangyu Li, Zhenlan Xu, Andreas Wimmer, Qinghua Tian, and Xin Ping Wang Environ. Sci. Technol., Just Accepted Manuscript • Publication Date (Web): 13 Jun 2017 Downloaded from http://pubs.acs.org on June 14, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 26

Environmental Science & Technology

1

New Insights into the Stability of Silver Sulfide Nanoparticles in Surface Water: Dissolution through

2

Hypochlorite Oxidation

3 4

Lingxiangyu Li,*,† Zhenlan Xu,§ Andreas Wimmer,‡ Qinghua Tian† and Xinping Wang†

5 6



School of Sciences, Zhejiang Sci-Tech University, Hangzhou 310018, China

7

§

Institute of Quality and Standard of Agro-Products, Zhejiang Academy of Agricultural Sciences, Hangzhou

8

310021, China

9



10

Division of Analytical Chemistry, Department of Chemistry, Technical University of Munich, Garching

85748, Germany

11 12

Corresponding Author:

13



14

E-mail: [email protected]

15

Tel: +86 571 86843228

16

Fax: +86 571 86843600

Dr. Lingxiangyu Li

17 18 19 20 21 22 23 1

ACS Paragon Plus Environment

Environmental Science & Technology

24

TOC

25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 2

ACS Paragon Plus Environment

Page 2 of 26

Page 3 of 26

Environmental Science & Technology

44

ABSTRACT

45

Silver sulfide nanoparticles (Ag2SNPs) are considered to be stable in the environment due to the extreme low

46

solubility of Ag2S (Ksp: 6.3×10-50). Little is known about the stability of Ag2SNPs in surface water disinfected

47

with aqueous chlorine, one of the globally most used disinfectants. Our results suggested that both uncoated

48

and polyvinylpyrrolidone (PVP)-coated Ag2SNPs (100 µg/L) underwent dissolution in surface water

49

disinfected with aqueous chlorine at a dose of 4 mg/L, showing the highest dissolved silver ion concentrations

50

of 22.3 and 10.5 µg/L within 45 min, respectively. The natural organic matter (NOM) and dissolved oxygen

51

(DO) posed effects on the Ag2SNPs dissolution by chlorine; NOM accelerated Ag2SNPs dissolution while DO

52

reduced the rate and extent of Ag2SNPs dissolution. We further demonstrated that Ag2SNPs dissolution was

53

primarily attributed to active oxidative substances including hydroxyl radical and H2O2 originating from the

54

hypochlorite oxidation. Additionally, water containing Ag2SNPs disinfected with hypochlorite showed stronger

55

interference on the zebra fish (Danio rerio) embryo hatching than Ag2SNPs and hypochlorite on their own.

56

This work documented that Ag2SNPs could undergo dissolution in surface water through hypochlorite

57

oxidation, posing potential risks to aquatic organisms, and therefore showed new insights into the stability of

58

Ag2SNPs in natural environment.

59 60 61 62 63 64 65 66 3

ACS Paragon Plus Environment

Environmental Science & Technology

67

INTRODUCTION

68

The occurrence of silver sulfide nanoparticles (Ag2SNPs) in natural environment was primarily attributed to

69

sulfidation of silver nanoparticles (AgNPs), being one of the most promising engineered nanomaterials used in

70

products all over the world.1,2 Laboratory and field studies have shown that AgNPs could be converted almost

71

entirely to Ag2SNPs in the wastewater treatment system, along with a buildup of Ag2SNPs in sewage sludge.3,4

72

Thus, measurable levels of Ag2SNPs have been observed in sewage sludge and even surface water.5-7

73

Previous studies showed good stability of Ag2SNPs in soil and compost even over a six months period.8,9

74

Furthermore, sulfidation has been considered as natural antidote for AgNPs toxicity because several reports

75

documented that Ag2SNPs posed substantially reduced toxicity to aquatic organisms and microorganisms

76

compared to that of AgNPs due to the negligible solubility of Ag2S.10,11 In a recent study, nevertheless, we

77

observed that Ag2SNPs could undergo dissolution in the aquatic environment containing ferric ions through the

78

hydroxyl radical formed during reduction of Fe(III) to Fe(II) in the light ,12 indicating that the stability of

79

Ag2SNPs might be overestimated in past studies. More recently, Kaegi et al.13 reported that oxidation of

80

Ag2SNPs in wastewater effluent by ozone resulted in a substantial increase in acute toxicity to green algae.

81

Therefore, it is essential to investigate the stability of Ag2SNPs under various environmental conditions to gain

82

comprehensive understanding of its risks to human and environmental health.

83

Chlorination has been widely applied for drinking water disinfection, which was found to degrade organic

84

pollutants rapidly, along with the formation of disinfection by-products (DBPs).14,15 To date, however, little is

85

known about the stability of Ag2SNPs during water disinfection with free chlorine such as aqueous chlorine,

86

one of the globally most used disinfectants. Potential dissolution of Ag2SNPs would pose risks, in particular

87

when the levels of silver-based nanoparticles (e.g., Ag2SNPs) in surface water gradually increase.6,7,16

88

Moreover, high chlorine doses and long contact times are required in some cases.17 In recent, it has been

89

reported that exposure to aqueous chlorine can affect the oxidation of AgNPs in water.18 Accordingly, can Ag+ 4

ACS Paragon Plus Environment

Page 4 of 26

Page 5 of 26

Environmental Science & Technology

90

be remobilized from Ag2SNPs by aqueous chlorine? How can Ag2SNPs dissolution occur in the surface water

91

disinfected with free chlorine? More importantly, what is the impact that Ag2SNPs dissolution has on aquatic

92

organisms?

93

Herein, the primary aim of this work was to investigate the stability of Ag2SNP in surface water disinfected

94

with aqueous chlorine at safe levels recommended by the United States Environmental Protection Agency (U.S.

95

EPA).19 Two types of Ag2SNP, namely uncoated Ag2SNPs (U-Ag2SNPs) and polyvinylpyrrolidone

96

(PVP)-coated Ag2SNPs (P-Ag2SNPs), were comprehensively examined. We investigated the Ag2SNPs

97

dissolution in the presence of hypochlorite under different conditions, and proposed the potential pathway of

98

Ag2SNPs dissolution by hypochlorite on the basis of experimental data. We further explored the toxicity of

99

Ag2SNPs dissolution to zebra fish (Danio rerio) embryo development to evaluate the impact of aqueous

100

chlorine disinfection on the risk of Ag2SNPs in the aquatic environment.

101

MATERIALS AND METHODS

102

Materials. In this study the reagents except for the natural organic matter (NOM) were purchased from

103

Sigma-Aldrich (St. Luis, USA). The NOM (2R101N) from the Suwannee River was acquired from the

104

International Humic Substance Society (Denver, USA). Ultrapure water from a Direct-Q-system (Millipore,

105

Billerica, USA) with a resistivity of 18.2 MΩ/cm was used for preparation of all solutions. The P-Ag2SNPs

106

with an average size of 57.2 ± 5.3 nm were prepared as described in our previous study.20 The U-Ag2SNPs

107

with an average size of 107.8 ± 19.5 nm (on the basis of size measurement through TEM images, n = 156)

108

were prepared by reaction of AgNO3 with NaSH in aqueous solution.21 Here the hydrodynamic size of

109

U-Ag2SNPs was 201.2 ± 17.3 nm by using dynamic light scattering (DLS, Malvern Zetasizer Nano-ZS90),

110

with a polydispersity index of 0.609. In brief, an aqueous solution of NaSH (50 mL, 1 mM) was added to

111

AgNO3 solution (50 mL, 2 mM) under vigorous stirring. The transparent AgNO3 solution turned bright yellow

112

immediately. After 3 min, the reaction mixture gradually turned tawny. After 30 min of mixing, precipitate was 5

ACS Paragon Plus Environment

Environmental Science & Technology

113

observed at the bottom of the vessel. The precipitate was concentrated by using centrifugation (9384 g, 30 min)

114

and purified by using ultrapure water for three cycles. Following 30 min of ultrasonication (KQ-600E, 40 kHz,

115

600 W) at about 0oC (ice-water mixture), the U-Ag2SNPs stock solution was stored at 4oC for later use. The

116

U-Ag2SNPs and P-Ag2SNPs should undergo ultrasonication (KQ-600E, 40 kHz, 600 W) for 30 min at 0oC to

117

disperse NPs before use.

118

Effect of Chlorine Disinfection on the Stability of Ag2SNPs in Surface Water. River, lake, and landscape

119

water samples were collected manually in Hangzhou city, Zhejiang, China. Briefly, river water was taken from

120

the Qiantang River. Lake water was collected from the West Lake, and landscape water was from a fountain in

121

front of the labrary on the campus of Zhejiang Sci-Tech University. The landscape water originated from an

122

effluent of a wastewater treatment plant to save water resource. All samples were collected in 500 mL

123

polyvinyl chloride (PVC) containers, which were rinsed threefold with the sample before collection. Samples

124

were filtered through a 0.45 µm glass fiber filter (Pall Corporation, Michigan, USA) and stored at 4oC until use.

125

The basic characterization of surface water is shown in the Table S1 (Supporting Information). The total silver

126

concentrations of surface water were all below 0.1 µg/L (limit of detection) based on inductively coupled

127

plasma mass spectrometry (ICP-MS, Agilent 8800, USA) measurement. The dissolved organic carbon (DOC)

128

concentration of samples was determined with a TOC-L total organic carbon analyzer (Shimadzu, Germany),

129

showing the DOC concentrations of river, lake and landscape water were 3.6 ± 0.1, 3.0 ± 0.1 and 2.7 ± 0.2

130

mg/L (Table S1), respectively. The samples were spiked with stock Ag2SNPs and NaClO, leading to

131

concentrations of 100 µg/L Ag2SNPs and 4 mg/L free chlorine respectively, followed by stirring (100 rpm) at

132

room temperature. A chlorine dose of 4 mg/L was used due to the recommendation for drinking water

133

chlorination by the U.S. EPA.19 Afterward, a sample of 4 mL was taken from each bottle at certain intervals

134

(e.g., 0, 0.5, 8, 20, 30, 45, 60 and 120 min). Centrifugal filtration (Amicon Ultra-4, 3kD, Millipore) at 9384 g

135

for 8 min was used to collect the dissolved silver ions released from Ag2SNPs followed by ICP-MS 6

ACS Paragon Plus Environment

Page 6 of 26

Page 7 of 26

Environmental Science & Technology

136

measurement to observe the dissolution of Ag2SNPs in surface water disinfected by hypochlorite. To validate

137

the centrifugal filtration at 9384 g for 8 min, the recovery efficiency of 100 µg/L AgNO3 solution is 95.7 ±

138

1.9%, suggesting negligible loss of the analyte during the centrifugal filtration (9384 g, 8 min). All

139

experiments were performed in triplicate.

140

Effect of NOM and DO on the Ag2SNPs Dissolution by Aqueous Chlorine. The P-Ag2SNP and U-Ag2SNP

141

stock solutions were diluted with ultrapure water in glass bottles (100 mL) followed by adding NaClO stock

142

solution (40 mg/L) prepared by sodium hypochlorite solution with an available chlorine content of 4.00-4.99%.

143

Finally, different volumes of NaClO stock solution were added to Ag2SNPs solution, yielding 0.1, 1 and 4

144

mg/L NaClO with 100 µg/L Ag2SNPs respectively. The homogenized mixtures (pH: ~8) were stirred (100

145

rpm) at room temperature. At each time interval (0, 0.5, 8, 20, 30, 45, 60 and 120 min), a 4-mL aliquot of the

146

aqueous sample was taken from each bottle. The dissolved silver ions collected with centrifugal filtration at

147

9384 g for 8 min were quantified using ICP-MS. All experiments were performed in triplicate.

148

The effect of NOM on the dissolution of Ag2SNPs by chlorine was investigated. A NOM stock solution with

149

the determined content of 100 mg/L DOC was prepared dissolving the dry powder in ultrapure water, followed

150

by filtration using a 0.45 µm membrane syringe. ICP-MS measurement confirmed no silver impurities (< 0.1

151

µg/L) in the NOM. Different volumes of the so prepared NOM stock solution were added to P-Ag2SNP and

152

U-Ag2SNP solutions based on the desired DOC concentrations (2 and 10 mg/L). Afterward, NaClO stock

153

solution was added to the mixture of Ag2SNPs and NOM, followed by stirring, sampling and silver ions

154

measurement as mentioned above.

155

To examine the role of dissolved oxygen (DO) in the dissolution of Ag2SNPs by hypochlorite, experiments

156

using (99.999%) N2-purged (4 h) deoxygenated ultrapure water for preparing mixtures of Ag2SNPs and

157

hypochlorite were performed in a glove box with N2 headspace. Then, a 4-mL aliquot of an aqueous sample

158

was taken from each bottle at intervals (0, 0.5, 8, 20, 30, 45, 60 and 120 min), followed by centrifugal filtration 7

ACS Paragon Plus Environment

Environmental Science & Technology

159

and silver ions measurement.

160

Chlorine Measurement. In the present study, concentrations of ClO- were measured applying the DPD

161

(N,N-diethyl-p-phenylenediamine) method as developed by Garg et al.18 In brief, 50 mM phosphate buffer was

162

prepared by mixing 75 mM NaH2PO4 and 25 mM Na2HPO4, and 6 mM DPD stock solution was prepared by

163

dissolving 30 mg DPD in 30 mL of 50 mM H2SO4 solution. Then, 300 µL of the phosphate buffer and 100 µL

164

of the DPD stock solution were added to 2.6 mL of each sample, followed by vortexing for 5 seconds. The

165

mixture was measured at 551 nm using a UV-visible spectrophotometer (UV-1800, Shimadzu). Considering

166

potential DPD oxidation caused by other oxidants in the sample, 100 µL of a 1.5 mM glycine was firstly added

167

to 2.5 mL of each sample to remove ClO-,18,22 followed by 300 µL of phosphate buffer and 100 µL of DPD

168

stock solution. The slight changes in the absorbance of samples with glycine were observed during the

169

Ag2SNPs dissolution (Figure S1). The concentrations of ClO- in samples were calculated according to the

170

absorbance of a prepared NaClO calibration.

171

Effect of Radical Scavengers on the Dissolution of Ag2SNPs by Chlorine. To examine the contribution of

172

active oxidative substances to the dissolution of Ag2SNPs by chlorine, effects of radical scavengers including

173

tertiary butyl alcohol (TBA), catalase, and superoxide dismutase (SOD) on the Ag2SNPs dissolution were

174

investigated. Here TBA (20 mM), catalase (1000 U/mL) and SOD (1000 U/mL) stock solutions were added to

175

the mixture of Ag2SNPs (100 µg/L) and hypochlorite (4 mg/L) to yield 2 mM TBA, 300 U/mL catalase and

176

300 U/mL SOD, respectively. These mixtures were stirred (100 rpm) at room temperature, and samples were

177

collected at intervals (0, 0.5, 8, 20, 30, 45, 60 and 120 min), followed by determination of silver ions using

178

centrifugal filtration and ICP-MS.

179

Toxicity of Ag2SNPs Dissolution to Zebra Fish (Danio rerio) Embryos. Zebra fish (Danio rerio) were

180

cultured at 25ºC and a photoperiod of 14 h light and 10 h dark. The embryos were collected, counted, and

181

rinsed several times in ultrapure water to remove any residue on the embryo surface. Twenty healthy embryos 8

ACS Paragon Plus Environment

Page 8 of 26

Page 9 of 26

Environmental Science & Technology

182

[~4 hour postfertilization (hpf)] were incubated in each well of 12-well transparent plates (NEST Biotech,

183

USA). 3 mL of Ag2SNPs (100 µg/L), dispersion, NaClO (4 mg/L) solution, or mixture of Ag2SNPs and NaClO

184

were added to each well. Throughout the whole exposure period (3 d), solutions were changed every 24 h and

185

the development status of embryos was observed to assess the embryo mortality and hatching rate. Three

186

replicate trials were conducted in this study.

187

RESULTS AND DISCUSSION

188

Effect of Chlorine Disinfection on the Stability of Ag2SNPs in Surface Water. The effect of chlorine

189

disinfection on the stability of Ag2SNPs in environmental water was investigated by spiking hypochlorite into

190

surface water with 100 µg/L Ag2SNPs. Dissolution of Ag2SNPs was observed (Figure 1); both P-Ag2SNPs and

191

U-Ag2SNPs rapidly released silver ions within the first 45 min, showing the highest silver ion concentrations

192

of 22.3 ± 2.1 and 10.5 ± 1.3 µg/L, respectively. This suggests that hypochlorite for surface water disinfection at

193

the dose recommended by the U.S. EPA could result in Ag2SNPs dissolution. Moreover, compared to

194

U-Ag2SNPs, P-Ag2SNPs showed a higher rate and extent of dissolution (Table S2 and Figure 1), implying that

195

P-Ag2SNPs likely underwent dissolution by hypochlorite in surface water. For example, the highest rate

196

constant of P-Ag2SNPs dissolution was 1.02 min-1, which is much higher than that of U-Ag2SNPs (0.60 min-1)

197

(Table S2). Also, the highest rate constants of P-Ag2SNPs and U-Ag2SNPs were observed in the river sample

198

(Table S2), which might be related to the NOM, since the river water showed the highest DOC level(Table S1).

199

To comprehensively understand the Ag2SNPs dissolution by hypochlorite, the kinetics, potential pathways and

200

impact were further investigated.

201

Dissolution Kinetics of Ag2SNPs by Chlorine. Both P-Ag2SNPs and U-Ag2SNPs showed negligible

202

dissolution in the absence of hypochlorite (Figure 1 and Figure 2A,B), while a measurable amount of silver

203

ions was observed in the presence of aqueous chlorine (Figure 2), even at hypochlorite concentrations of 0.1

204

mg/L, far lower than the chlorine disinfection dose recommended by the U.S. EPA. This suggests that 9

ACS Paragon Plus Environment

Environmental Science & Technology

205

hypochlorite is a key factor controlling the dissolution of Ag2SNPs. The time-resolved content of silver ions

206

was highly dependent on the concentration of hypochlorite; the higher the concentration of hypochlorite, the

207

larger the extent of Ag2SNPs dissolution (Figure 2A,B). Besides this extent, the dissolution rate of Ag2SNPs

208

also increased with the increase in the initial hypochlorite concentration (Figure 2A,B). Moreover, the amount

209

of dissolved silver rapidly increased again when a second equivalent of hypochlorite was added to the solution

210

(Figure S2), demonstrating the key role of hypochlorite in the Ag2SNPs dissolution. At a dose of 4 mg/L

211

hypochlorite 15.3 ± 2.5 and 17.1 ± 1.1 µg/L silver ions (120 min) were measured for P-Ag2SNPs and

212

U-Ag2SNPs, respectively, being an order of magnitude higher than that at dose of 0.1 mg/L hypochlorite.

213

As shown in Figure 2, P-Ag2SNPs show faster dissolution rates compared to U-Ag2SNPs, which may be

214

attributed to the hydrophilic characterization of PVP. A previous study has already documented that

215

hydrophilic coating could affect the dissolution dynamics and particularly accelerate the dissolution rate of

216

nanoparticles.23 Also, the fast dissolution rates of P-Ag2SNPs may be related to their small size, since generally

217

small size of NPs would undergo dissolution fast compared to big NPs.24 Accordingly, the time scale to reach

218

the dissolution equilibrium was shorter for P-Ag2SNPs compared to U-Ag2SNPs; the amount of released silver

219

ions from P-Ag2SNPs remained constant after a rapid increase within the first 45 min, while U-Ag2SNPs

220

dissolution reached equilibrium at 60 min. Also, the molar ratio of ClO- to Ag2S was 30 to reach equilibrium of

221

P-Ag2SNPs dissolution, while great excess of ClO- was needed for U-Ag2SNPs (Figure 2C). However, the

222

amount of silver ions released from P-Ag2SNPs was comparable to that of U-Ag2SNPs at the same

223

concentration of hypochlorite (Figure 2).

224

Similarly, NOM posed effects to the dissolution of Ag2SNP by hypochlorite (Figure S3); the dissolution rate

225

increased with increasing concentration of NOM, being likely attributed to the electron transfer-mediating role

226

of NOM, which has been proven to be able to accelerate electron transfer as electron shuttle mediators.25

227

Moreover, the increasing rate of Ag2SNP dissolution in the presence of NOM may be related to the stability of 10

ACS Paragon Plus Environment

Page 10 of 26

Page 11 of 26

Environmental Science & Technology

228

Ag+ by NOM due to formation of Ag+-NOM complex. A recent study on dissolution of sulfidized AgNPs

229

showed that fulvic acid from the Pony lake accelerated the dissolution of partly-sulfidized AgNPs through

230

formation of very stable complexs with Ag+.26 On the other hand, the extent of U-Ag2SNPs dissolution was

231

greatly reduced by the presence of NOM, which is consistent with previous studies on that adsorption of NOM

232

reduces dissolution of nanoparticles due to the increased colloidal stability.27

233

Pathway of Ag2SNPs dissolution by ClO-. Here we demonstrated that both P-Ag2SNPs and U-Ag2SNPs

234

could undergo dissolution in aqueous environment even with a lower dose of chlorine than recommended by

235

the U.S. EPA. The chlorine-dependent dissolution of Ag2SNPs was influenced by DO; both extent and rate of

236

dissolution dramatically increased with the decreasing concentration of DO (Figure 3), which is in contrast to

237

the general consensus presenting that dissolution of metal-based NPs is accelerated by DO.28,29 Here, DO

238

suppressed the dissolution of Ag2SNPs, which might be attributed to the production of O2 during Ag2SNPs

239

dissolution by chlorine. As shown in Figure 4A, the concentration of DO gradually increases in the solution. In

240

a recent study on AgNPs dissolution by chlorine, effect of O2 was dependent on the molar ratio of AgNP to

241

OCl-; at [AgNP]/[ClO-] > 4, the dissolution of AgNPs was completely inhibited under deoxygenated condition,

242

while little effect of O2 removal was observed on the AgNPs dissolution at [AgNP]/[ClO-] ≈ 1.18 Also, the pH

243

value gradually decreased during Ag2SNPs dissolution (Figure 4B), indicating that OH- is consumed during the

244

Ag2SNPs dissolution by ClO-. In general, hypochlorite oxidation is initiated by a single-electron oxidation,30

245

resulting in the occurrence of ClO• radical which was observed applying spin-trap EPR using the stable spin

246

adduct formed with 5,5-dimethyl-1-pyrroline N-oxide (DMPO) in this study (Figure S4). The ClO• radical can

247

react with OH- to form H+, Cl- and superoxide radical anions,31,32 resulting in the decrease of the solution’s pH

248

value. Accordingly, the free Cl- concentration increased within the first 10 min, followed by the gradual

249

decrease (Figure 4C), which might be attributed to the formation of [AgClx]-(x-1) complexes due to the

250

occurrence of silver ions in the solution with sufficient Cl-.33 11

ACS Paragon Plus Environment

Environmental Science & Technology

251

Sulfate was detected (ICS-1000, DIONEX) when Ag2SNPs underwent dissolution through hypochlorite

252

(Figure 4D), suggesting the sulfur element of Ag2SNPs underwent oxidation to form the SO42- during Ag2SNPs

253

dissolution by hypochlorite . A recent study reported that O3-induced Ag2SNPs oxidation occurred, along with

254

the release of silver ions and sulfate formation.13 As shown in Figure 4E, the concentration of ClO- rapidly

255

decreases from 4.7 to 4.0 mg/L in the initial time, and then gradually increases to 4.3 mg/L, keeping constant

256

along with the time. This suggests a ClO- depletion at first, followed by formation during the Ag2SNPs

257

dissolution process. Hydroxyl radical and Cl- could form ClO- in the presence of DO through several reaction

258

steps as described in previous studies.34

259

Additionally, the hydroxyl radical can oxidize most redox-sensitive elements in the solution because of its

260

extremely high oxidation ability (standard reduction potential: 2.8 V).35 Here, we postulated that highly active

261

oxidative substances like the hydroxyl radical and H2O2 may induce the dissolution of Ag2SNPs. To investigate

262

whether the dissolution of Ag2SNPs by hypochlorite is primarily attributed to these active substances, the

263

effect of radical scavengers such as TBA, SOD and catalase on the Ag2SNPs dissolution was examined.

264

As shown in Figure 4F, the extent of Ag2SNPs dissolution is significantly influenced by 2 mM TBA; the

265

amount of released silver ions is reduced from 15.3 ± 2.5 to 10.8 ± 0.1 µg/L, demonstrating that the hydroxyl

266

radical contributes to the Ag2SNPs dissolution. Furthermore, we observed that the amount of silver ions was

267

negligible after addition of SOD or catalase (Figure 4F), which suggests that the Ag2SNPs dissolution was

268

completely inhibited by SOD and catalase. Taken together, this indicates that active oxidative substances, in

269

particular the hydroxyl radical and H2O2, might primarily contribute to the Ag2SNPs dissolution. The

270

generation of superoxide radical and H2O2 during the hypochlorite oxidation has been demonstrated in

271

previous studies.36,37 Here, the occurrence of H2O2 in the Ag2SNPs solution with ClO- was confirmed by using

272

visual observation and instrumental analysis (Figures S5 and S6).

273

On the basis of these findings, we proposed that the Ag2SNPs dissolution process was mainly attributed to 12

ACS Paragon Plus Environment

Page 12 of 26

Page 13 of 26

Environmental Science & Technology

274

highly active oxidative substances formed during the hypochlorite oxidation (Figure 5). We thus postulated

275

that the dissolution of Ag2SNPs through hypochlorite oxidation may primarily proceed through the following

276

equations.

277

ClO-

278

ClO• + OH-

279

O2•- + H2O + ClO-

280

Ag2S H2O2/•OH

281

ClO• + e

(1)

H+ + Cl- + O2•-

(2)

H2O2 + •OH + Cl- + O2

(3)

Ag+ + SO42-

(4)

According to previous studies, hypochlorite oxidation was initiated by a single-electron oxidation, forming

282

ClO• radical (eq 1),30 followed by generation of superoxide radical anion through reactions between water and

283

ClO• radical, along with the occurrence of H+ and Cl- (eq 2).31,32 In general, superoxide radical anion could

284

further undergo reactions to form hydroxyl radical, O2, H2O2 and water. Here, we proposed that the superoxide

285

radical anion underwent interactions with hypochlorite in water to yield H2O2, O2 and •OH in the solution (eq

286

3).38,39 And then the H2O2 together with hydroxyl radical primarily contributed to the Ag2SNPs dissolution

287

with a simultaneous oxidation of the sulfide to sulfate (eq 4). Evidently, our data supported the proposed

288

mechanism that Ag2SNPs dissolution was primarily attributed to the hypochlorite oxidation.

289

Environmental Implications. Sulfidation has been widely considered as natural antidote for metallic NPs; the

290

toxicity of AgNPs to aquatic organisms and microbes could be dramatically reduced by sulfidation due to the

291

negligible dissolution of Ag2SNPs in previous studies.10,11 In general, ionic silver primarily controls the

292

toxicity of particles containing silver.40 The dissolution, therefore, potentially affects the hazard of Ag2SNPs,

293

which should be taken into account when assessing their risks to aquatic ecosystems. In the present study,

294

Ag2SNPs underwent dissolution by hypochlorite at a dose recommended by the U.S. EPA, indicating potential

295

risks to aquatic organisms. Indeed, Ag2SNPs dissolution completely inhibited zebra fish embryos from

296

hatching (Figure 6); higher than 90% embryos were dead in the first 24 h when exposed to Ag2SNPs in the 13

ACS Paragon Plus Environment

Environmental Science & Technology

297

presence of hypochlorite, which interferes embryos hatching by directly affecting their viabilities, showing a

298

large reduction in the survival rate. In contrast, all embryos hatched when exposed to either P-Ag2SNPs or

299

U-Ag2SNPs alone (Figure 6), suggesting that the safety of Ag2SNPs is dependent on their stability.

300

The rapid increase of silver ions released from Ag2SNPs by hypochlorite indicates that acute toxicity may

301

occur in the effluent of water disinfection by aqueous chlorine, in particular when the level of Ag2SNPs in

302

surface water is rapidly increasing due to the erosion of soils receiving a large amount of sewage sludge with

303

high concentrations of Ag2SNPs.5,41 Our findings provided robust evidence that stability and safety of

304

Ag2SNPs was likely overestimated in previous studies. Clearly, researchers should raise attention to the risk of

305

potential transformations, especially the dissolution of Ag2SNPs in surface water disinfected by aqueous

306

chlorine.

307 308

ASSOCIATED CONTENT

309

Supporting Information

310

Additional details of results are included. It includes the basic characterization of surface water (Table S1), the

311

rate constant (k) of Ag2SNPs (100 µg/L) dissolution in surface water disinfected with hypochlorite (Table S2),

312

the changes in the absorbance of samples with glycine through the Ag2SNPs dissolution (Figure S1), the effect

313

of ClO- on the P-Ag2SNPs dissolution, and a second equivalent of ClO- was added after 120 h (Figure S2),

314

effect of NOM on the dissolution of Ag2SNPs by hypochlorite (Figure S3), ClO• radical EPR signal observed

315

from NaClO solution (Figrue S4), and the visual observation and instrumental analysis confirmed the

316

occurrence of H2O2 through the Ag2SNPs dissolution by hypochlorite (Figures S5 and S6). This material is

317

available free of charge via the internet at http://pubs.acs.org.

318 319 14

ACS Paragon Plus Environment

Page 14 of 26

Page 15 of 26

Environmental Science & Technology

320

AUTHOR INFORMATION

321

Corresponding Author

322



323

Notes

324

The authors declare no competing financial interest.

E-mail: [email protected]

325 326

ACKNOWLEDGEMENTS

327

We thank the Zhejiang Province of Natural Science Foundation (2015C32039, LQ16B070003) and Science

328

Foundation of Zhejiang Sci-Tech University (17062003-Y) for financial support. The authors thank Miss Xiaoxi

329

Yang (Research Center for Eco-Environmental Sciences, Chinese Academy of Sciences) for providing the

330

zebra fish embryo. The authors also thank the anonymous reviewers for their valuable comments and

331

suggestions on this work.

332 333

REFERENCES

334

1. Lowry, G. V.; Espinasse, B. P.; Badireddy, A. R.; Richardson, C. J.; Reinsch, B. C.; Bryant, L. D.; Bone, A.

335

J.; Deonarine, A.; Chae, S.; Therezien, M.; Colman, B. P.; Hsu-Kim, H.; Bernhardt, E. S.; Matson, C. W.;

336

Wiesner, M. R. Long-term transformation and fate of manufactured Ag nanoparticles in a simulated large

337

scale freshwater emergent wetland. Environ. Sci. Technol. 2012, 46, 7027-7036.

338

2. Colman, B. P.; Espinasse, B.; Richardson, C. J.; Matson, C. W.; Lowry, G. V.; Hunt, D. E.; Wiesner, M. R.;

339

Bernhardt, E. S. Emerging contaminant or an old toxin in disguise? silver nanoparticle impacts on

340

ecosystems. Environ. Sci. Technol. 2014, 48, 5229-5236.

341 342

3. Kaegi, R.; Voegelin, A.; Sinnet, B.; Zuleeg, S.; Hagendorfer, H.; Burkhardt, M.; Siegrist, H. Behavior of metallic silver nanoparticles in a pilot wastewater treatment plant. Environ. Sci. Technol. 2011, 45, 15

ACS Paragon Plus Environment

Environmental Science & Technology

343 344 345 346 347 348

3902-3908. 4. Kent, R. D.; Oser, J. G.; Vikesland, P. J. Controlled evaluation of silver nanoparticle sulfidation in a full-scale wastewater treatment plant. Environ. Sci. Technol. 2014, 48, 8564-8572. 5. Kim, B.; Park, C.; Murayama, M.; Jr. Hochella, M. F. Discovery and characterization of silver sulfide nanoparticles in final sewage sludge products. Environ. Sci. Technol. 2010, 44, 7509-7514. 6. Li, L.; Hartmann, G.; Döblinger, M.; Schuster, M. Quantification of nanoscale silver particles removal and

349

release from municipal wastewater treatment plants in Germany. Environ. Sci. Technol. 2013, 47,

350

7317-7323.

351

7. Li, L.; Stoiber, M.; Wimmer, A.; Xu, Z.; Lindenblatt, C.; Helmreich, B.; Schuster, M. To what extent can

352

full-scale wastewater treatment plant effluent influence the occurrence of silver-based nanoparticles in

353

surface waters? Environ. Sci. Technol. 2016, 50, 6327-6333.

354

8. Sekine, R.; Brunetti, G.; Donner, E.; Khaksar, M.; Vasilev, K.; Jämting, A. K.; Scheckel, K. G.; Kappen, P.;

355

Zhang, H.; Lombi, E. Speciation and lability of Ag-, AgCl-, and Ag2S-nanoparticles in soil determined by

356

X-ray absorption spectroscopy and diffusive gradients in thin films. Environ. Sci. Technol. 2015, 49,

357

897-905.

358

9. Lombi, E.; Donner, E.; Taheri, S.; Tavakkoli, E.; Jämting, A. K.; McClure, S.; Naidu, R.; Miller, B. W.;

359

Scheckel, K. G.; Vasilev, K. Transformation of four silver/silver chloride nanoparticles during anaerobic

360

treatment of wastewater and post-processing of sewage sludge. Environ. Pollut. 2013, 176, 193-197.

361

10. Reinsch, B. C.; Levard, C.; Li, Z.; Ma, R.; Wise, A.; Gregory, K. B.; Jr. Brown, G. E.; Lowry, G. V.

362

Sulfidation of silver nanoparticles decrease Escherichia coli growth inhibition. Environ. Sci. Technol. 2012,

363

46, 6992-7000.

364 365

11. Levard, C.; Hotze, E. M.; Colman, B. P.; Dale, A. L.; Truong, L.; Yang, X. Y.; Bone, A. J.; Jr. Brown, G. E.; Tanguay, R. L.; Di Giulio, R. T.; Bernhardt, E. S.; Meyer, J. N.; Wiesner, M. R.; Lowry, G. V. Sulfidation of 16

ACS Paragon Plus Environment

Page 16 of 26

Page 17 of 26

366

Environmental Science & Technology

silver nanoparticles: natural antidote to their toxicity. Environ. Sci. Technol. 2013, 47, 13440-13448.

367

12. Li, L.; Zhou, Q.; Geng, F.; Wang, Y.; Jiang, G. Formation of nanosilver from silver sulfide nanoparticles in

368

natural waters by photoinduced Fe(II, III) redox cycling. Environ. Sci. Technol. 2016, 50, 13342-13350.

369 370

13. Thalmann, B.; Voegelin. A.; von Gunten, U.; Behra, R.; Morgenroth, E.; Kaegi, R. Effect of ozone treatment on nano-sized silver sulfide in wastewater effluent. Environ. Sci. Technol. 2015, 49, 10911-10919.

371

14. Wu, Z.; Fang, J.; Xiang, Y.; Shang, C.; Li, X.; Meng, F.; Yang, X. Roles of reactive chlorine species in

372

trimethoprim degradation in the UV/chlorine process: kinetics and transformation pathways. Water Res.

373

2016, 104, 272-282.

374 375 376 377 378

15. Wybraniec, S.; Starzak, K.; Pietrykowski, Z. Chlorination of betacyanins in several hypochlorous acid systems. J. Agric. Food Chem. 2016, 64, 2865-2874. 16. Sun, T., Gottschalk, F., Hungerbühler, K., Nowack, B. Comprehensive probabilistic modelling of environmental emissions of engineered nanomaterials. Environ. Pollut. 2014, 185, 69-76. 17. Zong, W., Sun, F., Sun, X. Evaluation on the generative mechanism and biological toxicity of

379

microcystin-LR disinfection by-products formed by chlorination. J. Hazard. Mater. 2013, 252, 293-299.

380

18. Garg, S.; Rong, H.; Miller, C. J.; Waite, T. D. Oxidative dissolution of silver nanoparticles by chlorine:

381 382 383 384

implications to silver nanoparticle fate and toxicity. Environ. Sci. Technol. 2016, 50, 3890-3896. 19. EPA. Basic information about disinfectants in drinking water: chloramine, chlorine and chlorine dioxide. 2013. 20. Li, L.; Wang, Y.; Liu, Q.; Jiang, G. Rethinking stability of silver sulfide nanoparticles in the aquatic

385

environment: photoinduced transformation of Ag2S-NPs in the presence of Fe(III). Environ. Sci. Technol.

386

2016, 50, 188-196.

387 388

21. Xiong, S.; Xi, B.; Zhang, K.; Chen, Y.; Jiang, J.; Hu, J.; Zeng, H. Ag nanoprisms with Ag2S attachment. Sci. Rep. 2013, 3, 1-9. 17

ACS Paragon Plus Environment

Environmental Science & Technology

389

22. Peskin, A. V.; Midwinter, R. G.; Harwood, D. T.; Winterbourn, C. C. Chlorine transfer between glycine,

390

taurine, and histamine: reaction rates and impact on cellular reactivity. Free Radical Biol. Med. 2004, 37,

391

1622-1630.

392

23. Pokhrel, L. R.; Dubey, B.; Scheuerman, P. R. Impacts of select organic ligands on the colloidal stability,

393

dissolution dynamics, and toxicity of silver nanoparticles. Environ. Sci. Technol. 2013, 47, 12877-12885.

394

24. Zhang, H.; Chen, B.; Banfield, J. F. Particle size and pH effects on nanoparticle dissolution. J. Phy. Chem.

395 396 397 398

C 2010, 114, 14876-14884. 25. Kang, S.; Choi, W. Oxidative degradation of organic compounds using zero-valent iron in the presence of natural organic matter serving as an electron shuttle. Environ. Sci. Technol. 2009, 43, 878-883. 26. Collin, B.; Tsyusko, O. V.; Starnes, D. L.; Unrine, J. M. Effect of natural organic matter on dissolution and

399

toxicity of sulfidized silver nanoparticles to Caenorhabditis elegans. Environ. Sci.: Nano 2016, 3, 728-736.

400

27. Gunsolus, I. L.; Mousavi, M. P. S.; Hussein, K.; Bühlmann, P.; Haynes, C. L. Effects of humic and fulvic

401

acids on silver nanoparticle stability, dissolution, and toxicity. Environ. Sci. Technol. 2015, 49, 8078-8086.

402

28. Zhang, W.; Yao, Y.; Li, K.; Huang, Y.; Chen, Y. Influence of dissolved oxygen on aggregation kinetics of

403 404 405 406 407 408

citrate-coated silver nanoparticles. Environ. Pollut. 2011, 159, 3757-3762. 29. Fabrega, J.; Luoma, S. N.; Tyler, C. R.; Galloway, T. S.; Lead, J. R. Silver nanoparticles: behaviour and effects in the aquatic environment. Environ. Int. 2011, 37, 517-531. 30. Spasojević, M.; Krstajić, N.; Spasojević, P.; Ribić-Zelenović, L. Modelling current efficiency in an electrochemical hypochlorite reactor. Chem. Eng. Res. Des. 2015, 93, 591-601. 31. Ozawa, T.; Miura, Y.; Ueda, J. Oxidation of spin-traps by chlorine dioxide (ClO2) radical in aqueous

409

solutions: first ESR evidence of formation of new nitroxide radicals. Free Radical Bio. Med. 1996, 20,

410

837-841.

411

32. Macounová, K. M.; Simic, N.; Ahlberg, E.; Krtil, P. Electrochemical water-splitting based on hypochlorite 18

ACS Paragon Plus Environment

Page 18 of 26

Page 19 of 26

412 413

Environmental Science & Technology

oxidation. J. Am. Chem. Soc. 2015, 137, 7262-7265. 33. Fargašová, A.; Prucek, R.; Ranc, V.; Panáček, A.; Kvítek, L.; Zbořil, R. Influence of various chloride ion

414

concentrations on silver nanoparticle transformations and effectiveness in surface enhanced Raman

415

scattering for different excitation wavelengths. RSC Adv. 2015, 5, 9737-9744.

416

34. Saran, M.; Beck-Speier, I.; Fellerhoff, B.; Bauer, G. Phagocytic killing of microorganisms by radical

417

processes: consequences of the reaction of hydroxyl radicals with chloride yielding chlorine atoms. Free

418

Radical Biol. Med. 1999, 26, 482-490.

419

35. Cheng, D., Yuan, S., Liao, P., Zhang, P. Oxidizing impact induced by mackinawite (FeS) nanoparticles at

420

oxic conditions due to production of hydroxyl radicals. Environ. Sci. Technol. 2016, 50, 11646-11653.

421

36. Behar, D; Czapski, G.; Rabani, J.; Dorfman, L. M.; Schwarz, H. A. Acid dissociation constant and decay

422 423 424 425 426

kinetics of the perhydroxyl radical. J. Phys. Chem. 1970, 74, 3209-3213. 37. Rees, M. D.; Hawkins, C. L.; Davies, M. J. Hypochlorite and superoxide radicals can act synergistically to induce fragmentation of hyaluronan and chondroitin sulphates. Biochem. J. 2004, 381, 175-184. 38. Burns, J. M.; Craig, P. S.; Shaw, T. J.; Ferry, J. L. Multivariate examination of Fe(II)/Fe(III) cycling and consequent hydroxyl radical generation. Environ. Sci. Technol. 2010, 44, 7226-7231.

427

39. Tokumura, M.; Morito, R.; Hatayama, R.; Kawase, Y. Iron redox cycling in hydroxyl radical generation

428

during the photo-Fenton oxidative degradation: dynamic change of hydroxyl radical concentration. Appl.

429

Catal. B-Environ. 2011, 106, 565-576.

430

40. Ivask, A.; ElBadawy, A.; Kaweeteerawat, C.; Boren, D.; Fischer, H.; Ji, Z.; Chang, C. H.; Tolaymat, T.;

431

Telesca, D.; Zink, J. I.; Cohen, Y.; Holden, P. A.; Godwin, H. A. Toxicity mechanisms in Escherichia coli

432

vary for silver nanoparticles and differ from ionic silver. ACS Nano 2014, 8, 374-386.

433

41. Wang, P.; Menzies, N. W.; Dennis, P. G.; Guo, J.; Forstner, C.; Sekine, R.; Lombi, E.; Kappen, P.; Bertsch,

434

P. M.; Kopittke, P. M. Silver nanoparticles entering soils via the wastewater-sludge-soil pathway pose low 19

ACS Paragon Plus Environment

Environmental Science & Technology

435

risk to plants but elevated Cl concentrations increase Ag bioavailability. Environ. Sci. Technol. 2016, 50,

436

8274-8281.

437 438 439 440 441 442 443 444 445 446 447 448 449 450 451 452 453 454 455 456 457 20

ACS Paragon Plus Environment

Page 20 of 26

Page 21 of 26

Environmental Science & Technology

458 459

Figure 1. Dissolution kinetics of Ag2SNPs (100 µg/L) in surface waters by aqueous chlorine (4 mg/L). (A)

460

P-Ag2SNPs. (B) U-Ag2SNPs. Statistic analysis for dissolution rates of Ag2SNPs in the presence of

461

hypochlorite at the initial 8 min showed that the highest rate was observed in the river water among the

462

different surface water samples.

463 464 465 466 467 468 469 470 471 472 473 474 475 476 477 21

ACS Paragon Plus Environment

Environmental Science & Technology

478

479 480

Figure 2. Dissolution of Ag2SNPs by aqueous chlorine. (A) Effect of hypochlorite concentrations on the

481

dissolution kinetics of P-Ag2SNPs. (B) Effect of hypochlorite concentrations on the dissolution kinetics of

482

U-Ag2SNPs. (C) Dissolution of Ag2SNPs by different molar ratios of ClO- to Ag2S. It should be noted that the

483

amount of silver ion was measured after Ag2SNPs (100 µg/L) mixed with different amount of NaClO for 120

484

min, since the dissolution has been equilibrium after 120 min on the basis of our data.

485 486 487 488 489 490 491 492

22

ACS Paragon Plus Environment

Page 22 of 26

Page 23 of 26

Environmental Science & Technology

493 494

Figure 3. Effect of DO on the dissolution of Ag2SNPs by aqueous chlorine. Here the concentrations of

495

Ag2SNPs and NaClO were 100 µg/L and 4 mg/L, respectively. (A) P-Ag2SNPs. (B) U-Ag2SNPs.

496 497 498 499 500 501 502 503 504 505 506 507 508 509 510 511 23

ACS Paragon Plus Environment

Environmental Science & Technology

512

513

514 515

Figure 4. Experimental data to support the proposed mechanism of Ag2SNPs dissolution by chlorine. (A) DO.

516

(B) pH. (C) Free Cl- concentration. (D) SO42- concentration. (E) ClO- concentration. (F) Effect of radical

517

scavengers on the Ag2SNPs dissolution by chlorine. The concentrations of P-Ag2SNPs and NaClO were

518

simultaneously amplified by 8 folds for the cases A and B (namely concentrations of P-Ag2SNPs and NaClO

519

were 800 µg/L and 32 mg/L, respectively) to measure the changes of DO and pH. Similarly, for the case of D,

520

the concentrations of P-Ag2SNPs and NaClO were simultaneously amplified by 24 folds (namely 2.4 and 96

521

mg/L for P-Ag2SNPs and NaClO, respectively) to measure the SO42- changes. The other cases of C, E and F,

522

the concentrations of P-Ag2SNPs and NaClO were 100 µg/L and 4 mg/L, respectively.

523 24

ACS Paragon Plus Environment

Page 24 of 26

Page 25 of 26

Environmental Science & Technology

524 525

Figure 5. Pictorial summary of the proposed pathway of Ag2SNPs dissolution through hypochlorite oxidation.

526 527 528 529 530 531 532 533 534 535 536 537 538 539 540 541 542 543

25

ACS Paragon Plus Environment

Environmental Science & Technology

544 545

Figure 6. Toxicity of NaClO (4 mg/L), Ag2SNPs (100 µg/L), and Ag2SNPs with NaClO to zebra fish (Danio

546

rerio) embryos.

26

ACS Paragon Plus Environment

Page 26 of 26