New Superior PLASTICIZERS derived from ALFOL ALCOHOLS
N-Hexyl Octyl Decyl ester plasticizers made with ALFOL 610 Alcohol. For the first time, these properties are available to you in each of several economical plasticizers from leading plasticizer manufacturers*
Compare the performance advantages of ALFOL 610 Phthalate with those of leading branch-chain plasticizers shown in table below.
Higher Plasticizing Efficiency Low Volatility Superior Long-Term Flexibility at Elevated Temperatures Excellent Low Temperature Flexibility Very Low Plastisol Viscosities: At Low Shear Rates At High Shear Rates
Ask your plasticizer supplier for samples of new plasticizers manufactured from CONOCO ALFOL Alcohols. Write to us for Alfol Technical Bulletin AL-9»
ALFOL 610 Phthalate
DOP
DIOP
DIDP
Plasticizer Level ( p h r ) t o provide 100% modulus at 1500 psi
47.5
50
51.5
55
% Wt. Loss after 7 days @ 100°C
4.6
11.2
9.3
2.1
% Retention of Elongation after 7 days @ 100°C
93
60
65
96
Low Temp. Flex. (Tf), °C
-35
-26
-23
-27
Brookfield Viscosity 10 RPM, cps (after 2 hours)
4600
9900
9400
9300
Severs Viscosity (after 2 hours) 500 sec-i, cps 1000 sec-l, cps
3000 4000
8000 12000
—
V CONOCO PETROCHEMICALS
24000 Off-Scale
CONTINENTAL OIL COMPANY PETROCHEMICAL DEPARTMENT CEN-505 630 Fifth Avenue, New York 20, N.Y. • 212 JUdson 6-2510 © 1962. Continental Oil Company