NiOx Nanoflower Modified Cotton Fabric for UV Filter and Gas

Mar 2, 2019 - Differential scanning calorimeter trace for bare and surface modified cotton fabrics .... functional textiles for UV blocking and gas se...
30 downloads 0 Views 1MB Size
Subscriber access provided by University Library of Southern Denmark

Energy, Environmental, and Catalysis Applications

NiOx Nanoflower Modified Cotton Fabric for UV Filter and Gas Sensing Applications Dinesh Kumar Subbiah, Jayanth Babu Karanam, Apurba Das, and John Bosco Balaguru Rayappan ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.9b04682 • Publication Date (Web): 14 May 2019 Downloaded from http://pubs.acs.org on May 14, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

ACS Applied Materials & Interfaces

NiOx Nanoflower Modified Cotton Fabric for UV Filter and Gas Sensing Applications

2

1Dinesh

Kumar Subbiah, 1K. Jayanth Babu, 2Apurba Das and 1John Bosco Balaguru Rayappan*

3

1Centre

for Nanotechnology & Advanced Biomaterials (CeNTAB) and

4

School of Electrical & Electronics Engineering (SEEE),

5

SASTRA Deemed to be University, Thanjavur 613 401, India

6 7

2Depatment

of Textile Technology, Indian Institute of Technology Delhi, New Delhi – 110 016 [email protected]

8 9 10 11 12 13 14 15 16 17 18 19 20 21 22

* Corresponding author

23

Prof. John Bosco Balaguru Rayappan, Ph.D.

24

Centre for Nanotechnology & Advanced Biomaterials (CeNTAB) &

25

School of Electrical & Electronics Engineering

26

SASTRA Deemed to be University

27

Thanjavur – 613 401

28

India

29

Phone: +91 4362 264 101; Ext: 2255

30

Fax: +91 4362 264120

31

E-mail: [email protected] 1 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 28

32

Abstract

33

Integration of multifunctional nanomaterials with textiles could be a significant value addition to the bright

34

future of the growing technology “Technical Textiles”. Development of textiles with anti-electromagnetic

35

radiation and in particular anti-ultraviolet features could be one of the best solutions to the ozone depletion

36

induced ultraviolet pollution of the environment, which is a major concern in the context of surging skin cancer

37

cases. In this background, multifunctional nanoflower structured partially hydroxide nickel oxide (NiOx) was

38

grown on cotton fabric using chemical bath deposition technique for the development of UV filter and flexible

39

gas/chemical sensor. X-ray diffraction patterns of bare and NiOx modified cotton fabrics confirmed the micro

40

and poly-crystalline nature respectively. Field emission scanning electron microscopic images revealed the

41

growth of 3D green button chrysanthemum flower-like morphology on the surface of cotton fabric. In-

42

addition, X-ray photoelectron spectra revealed the presence of Ni, carbon, oxygen elements in the NiOx

43

modified cotton cellulose. The increase in hydrophobic nature of surface treated fabric was observed using

44

Goniometer. Differential scanning calorimeter trace for bare and surface modified cotton fabrics exhibited an

45

endothermic behavior at the characteristic onset temperature. The results of thermogravimetric analysis

46

revealed the enhanced thermal stability of up to 800ºC for the surface treated fabric compared to bare cotton.

47

Further, Ultraviolet Protection Factor (UPF) of the NiOx nanoflower modified cotton fabric was measured

48

using an in-vitro method following the AATCC 183:2004 standard using UV transmittance analyzer. The

49

enhanced absorbance of ultraviolet rays at 388 nm resulted in the UPF of 2000. The chemical/gas sensing

50

features of the surface modified textile samples were investigated using the home-made gas testing chamber.

51

NiOx modified fabric showed a selective response of 12431 towards trimethylamine at room temperature.

52 53

Keywords: Technical textiles, NiOx Nanostructures, UV filter, Gas sensor

54 55 2 ACS Paragon Plus Environment

Page 3 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

56

ACS Applied Materials & Interfaces

1. Introduction

57

In the last few decades, researchers and scientists have focused on the reasons leading to depletion of ozone

58

layer, resultant elevation of ultraviolet radiation (UVR) and its threat. UV spectrum lies between 290 and 400

59

nm and it has a total incident of 8%1 on the earth’s surface. Even though, UVR has less proportion compared

60

to visible and IR radiation, its higher energy compared with other radiations2 is a major concern. Excessive

61

exposure to UVR can cause several adverse effects such as eye damage, skin cancer3, suppression of immune

62

system4, sunburn5, tanning6, genetic damage to cells7 and aging of the skin3. Centers for Disease Control and

63

Prevention has predicted a steep increase in the number of skin cancer cases to 1.9 million by 20208. As a

64

consequence, governments9 and researchers have started exploring the development of technical textiles to

65

protect UVR induced skin cancer cases.

66

On the other hand, detection of toxic gases and volatile organic compounds (VOCs) in the working ambient

67

is a concern in the context of growing industrial sectors. Especially, emission of VOCs from industries10 like

68

paint11 have serious implications on the environment12. For this instance, Trimethylamine (TMA), which is a

69

short-chain tertiary aliphatic amine, an air pollutant emitted from chemical industries, fishery industries and

70

exhaust from vehicles13,14 need to be monitored and controlled. Inhalation of TMA leads to neuro and heart

71

diseases15,16,17.

72

In this context, development of wearable suits by modifying the surface of textiles with nanomaterials has

73

gained a significant momentum. For these kinds of modifications, suitable fabrics have been identified based

74

on the unique factors such as fiber structure, type of fabric, configuration of warp and weft of thread18–20. In

75

particular, nanostructured inorganic materials have been used for the manufacturing of multifunctional fabrics

76

due to their tunable electrical, mechanical, thermal, chemical, optoelectronic and magnetic properties21–26.

77

Further, adding various functionalities to the fabrics by the process of surface modification have enabled the

78

fabrication of smart textiles for UV-blocking27, self-cleaning28, gas sensing29, water repellent30, anti-

79

microbial31, flame-retardant32 applications. 3 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 80 5 6 81 7 8 82 9 10 11 83 12 13 84 14 15 85 16 17 86 18 19 20 87 21 22 88 23 24 89 25 26 27 90 28 29 91 30 31 92 32 33 34 93 35 36 94 37 38 95 39 40 41 96 42 43 97 44 45 98 46 47 99 48 49 50 100 51 52 101 53 54 102 55 56 57 103 58 59 60

Page 4 of 28

Nanostructured metal oxide materials like ZnO33, WO334, TiO235, NiO33 have been used for fabricating functional textiles for UV blocking and gas sensing applications. Mohamed Rehan et al.,36 developed in-situ incorporated ZnO and Ag nanoparticles on cellulose for enhancing UV blocking characteristics. The developed fiber exhibited an UPF of 442. Ibrahim et al.,37 prepared multifunctional cotton fabrics modified with ZnO, ZrO and TiO2 nanoparticles using padding technique to study flame retardant, antibacterial and UV blocking functions. TiO2 modified fabrics showed UV blocking factor of 101. Wang et al.,27 embedded dumbbell shaped ZnO on cotton fabric via dip-pad-cure method and revealed that the curing temperature (170℃) plays an important role in-turn better UPF of 786.7. TiO2 incorporated cotton fabrics employing ultrasonic acoustic method exhibited self-cleaning and anti-microbial properties with a UPF of 63.13. Jiang et al.,38 deposited aluminum-doped ZnO (AZO) on polyester fabric using magnetron sputtering and also evaluated UPF (362), water repellency and infrared emissivity with respect to the thickness of modified fabrics. Tungsten oxide modified polyester fabrics prepared using two-roll padding technique achieved a UPF of 108.1 in the UVB region39. Our group has recently developed nanostructured ZnO modified cotton fabrics using sol-gel and seed layer enhanced sol-gel technique for UV filter and gas sensing applications. This fabric showed a UPF of 378 with a selective detection of acetaldehyde vapour at room temperature29. In similar line, another wide bandgap metal oxide material namely NiO/NiOx with high electrocatalytic activity has been considered for the fabrication of multifunctional cotton fabrics. NiOx has been considered as a UV blocking candidate due to its wide bandgap40, large refractive index33, tunable catalytic41 and environment friendly features42. Interestingly the four different phases of NiOx namely α-Ni(OH)2, β-NiOOH, β-Ni(OH)2 and γNiOOH have motivated us to modify the cotton fabric to enhance the UV protection capability employing chemical bath technique. Since, metal hydroxide is one of the promising candidates for gas sensing applications43 and in particular 3D flower-like nanostructures have been an interesting candidate for sensing applications because of its enhanced surface area, different energy levels, enormous number of interior contact sites, multiple scattering points or 4 ACS Paragon Plus Environment

Page 5 of 28 1 2 3 4 104 5 6 105 7 8 106 9 10 11 107 12 13 108 14 15 109 16 17 110 18 19 20 111 21 22 112 23 24 113 25 26 27 114 28 29 115 30 31 116 32 33 34 117 35 36 118 37 38 119 39 40 120 41 42 43 121 44 45 122 46 47 123 48 49 50 124 51 52 125 53 54 126 55 56 57 127 58 59 60

ACS Applied Materials & Interfaces

junctions44 and tunable transport properties suitable for variety of applications involving surface phenomena45, the sensing characteristics of 3D green button chrysanthemum flower-like NiOx modified cotton fabric were investigated and reported.

2. Experimental section 2.1 Materials A white colored cotton cellulose fabric (warp and weft count of 40x40 picks per inch) was brought from Department of Textile Technology Delhi, Indian Institute of Technology, New Delhi. Sodium hydroxide (NaOH), nickel (II) sulfate hexahydrate (NiSO4.6H2O), potassium persulfate (K2S2O8) were procured from Alfa-Aesar, USA. Ammonium hydroxide solution (30-33% of NH3 in H2O) was purchased from Sigma Aldrich, USA.

2.2 Synthesis of NiOx flowers on cotton fabric 2.2.1 Pretreatment of cotton fabric Mercerisation technique46 was adopted to remove the impurities and additives such as fats, waxes, pectin, proteins, coloring, moistures and mineral from textile surface. Pretreatment promotes the oxidation / reduction rate of metal oxide compounds and increase the absorbance rate on the surface of cotton substrates. 1 M of sodium hydroxide pellets were dissolved in 200 mL of deionized water and maintained at 90°C. Cotton fabric was cut in to samples of 20 cm x 20 cm size and treated with preheated NaOH solution. Then the NaOH treated samples were washed thoroughly with doubly-deionized water and dried at 120°C for 2 h in a hot air oven prior to deposition.

5 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 128 5 6 129 7 8 130 9 10 11 131 12 13 132 14 15 133 16 17 134 18 19 20 135 21 22 136 23 24 137 25 26 27 138 28 29 139 30 31 140 32 33 34 141 35 36 142 37 38 143 39 40 144 41 42 43 145 44 45 146 46 47 48 147 49 50 148 51 52 149 53 54 150 55 56 57 151 58 59 60

Page 6 of 28

2.2.2 Chemical bath deposition of NiOx on pretreated cotton fabric 150 mL of 0.5 M nickel sulfate hexahydrate and 0.09 M potassium persulfate were mixed at room temperature. 11.24 mL of ammonium hydroxide solution (30-35%) was added to the prepared precursor solution under vigorous stirring condition. As the end of reaction process, the colour of the solution was changed from light green to dark blue and solution became viscous47. This could be due to the replacement of ammonia with the coordinated water molecules in the precursor solution48. The treated cotton cellulose samples were dipped into the prepared precursor solution. The dipped cotton fabric was kept undisturbed for 96 h and then it was dried at 80±6°C for 1 h using hot air oven. Then the dried samples were washed several times with deionized water and dried at room temperature for further analysis.

2.3 Methods XRD patterns were recorded in the diffraction angle ranging from 5° to 80° on a D8 Focus X-ray Diffractometer, Bruker, Germany with Cu Kα radiation. The crystallite size of NiOx modified fabric was estimated using the Debye-Scherrer formula as given in Eq. 1, 𝐷 = 𝑘𝜆(𝛽𝑐𝑜𝑠ϴ) ―1

(1)

where, λ represents the wavelength (λ = 1.5406 Å) of the incident X-ray, k is the shape factor constant (0.89), βℎ𝑘𝑙 represents the full width at half- maximum of the diffraction peak, and θ denotes the diffraction angle. Field Emission Scanning Electron Microscope (JSM6701F, JEOL, Japan) was used to observe the morphological features of unmodified and modified fabrics. Fourier Transform Infra-red (FTIR) (Alpha-T, Bruker, Germany) spectrometer was used to examine the functional groups of the bare and surface modified samples in the wavenumber range of 400-4000 cm-1. Thermogravimetric analyzer (SDT Q600, TA Instruments, USA) was used under the nitrogen atmosphere in the temperature range of 30 and 800°C at a heat flow rate of 10°C min-1 for observing the thermal stability of the modified samples. Differential Scanning Calorimeter (DSC 214 Polyma, NETZSCH, USA) was used in the temperature range of 298 to 673 K at a 6 ACS Paragon Plus Environment

Page 7 of 28 1 2 3 4 152 5 6 153 7 8 9 154 10 11 155 12 13 14 156 15 16 157 17 18 158 19 20 21 159 22 23 160 24 25 161 26 27 162 28 29 30 163 31 32 164 33 34 165 35 36 37 166 38 39 167 40 41 42 43 168 44 45 46 169 47 48 170 49 50 51 171 52 53 172 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

heating rate of 10 K min-1 for studying the exothermic or endothermic behaviour of the surface modified textile samples. The percentage change in latent heat of fusion was calculated using the Eq. 2, % 𝑐ℎ𝑎𝑛𝑔𝑒 𝑖𝑛 𝑙𝑎𝑡𝑒𝑛𝑡 ℎ𝑒𝑎𝑡 𝑜𝑓 𝑓𝑢𝑠𝑖𝑜𝑛 =

[∆𝐻𝑁𝑖𝑂𝑥 𝑚𝑜𝑑𝑖𝑓𝑖𝑒𝑑 𝑓𝑎𝑏𝑟𝑖𝑐 ― ∆𝐻𝐶𝑜𝑛𝑡𝑟𝑜𝑙𝑙𝑒𝑑 𝑓𝑎𝑏𝑟𝑖𝑐] [∆𝐻𝐶𝑜𝑛𝑡𝑟𝑜𝑙𝑙𝑒𝑑 𝑓𝑎𝑏𝑟𝑖𝑐]

(2)

where, ∆Htreated cotton fabric and ∆Hcontrolled fabric are the latent heat of fusion of treated and controlled cotton samples respectively. Surface area and porosity analyzer (ASAP 2020, Micrometrics, USA) was used to measure the adsorption isotherms and specific surface area of bare and NiOx modified fabrics. Stiffness analyzer (WIRA Instruments, UK) was used to measure the stiffness of the bare and NiOx modified fabrics. Analytical balance instrument (Amkette Analysis Ltd, India) under ASTM D3776 M-Option 3:2017 was used to measure the weight of the bare and NiOx cotton cellulose. Static water contact angle measurement was carried out on standard goniometer equipment integrated with high-resolution camera and imaging software (Model 250, Rame-Hart Instruments, USA) using 30 µL distilled water droplet. X-ray photoelectron spectrometer (Model K-Alpha, Thermo Scientific, USA) was utilized to analyze the surface of the modified fabric. UV transmittance analyzer (UV2000F, Labsphere Inc., USA) under AATCC 183:2010 standard was used to measure the Ultraviolet Protection Factor (UPF) of the modified fabrics in the wavelength range of 280-410 nm. The computerized formula for the calculation of UPF value is given as follows (Eq. 3,4): 𝑈𝑃𝐹 =

𝑛𝑚 Σ400 280 𝑛𝑚 𝐸𝜆𝑆𝜆Δ𝜆

(3)

𝑛𝑚 Σ400 280 𝑛𝑚 𝐸𝜆𝑆𝜆T𝜆Δ𝜆 𝜆

𝑃𝑒𝑟𝑐𝑒𝑛𝑡 𝑈𝑉 𝑡𝑟𝑎𝑛𝑠𝑚𝑖𝑠𝑠𝑖𝑜𝑛 =

∑𝜆2𝑇(𝜆) 1

(𝜆2 ― 𝜆1)

(4)

where, 𝐸𝜆 denotes to the relative erythemal spectral effectiveness, 𝑆𝜆 relates the solar spectral irradiance, 𝛥𝜆is the measured wavelength interval (280 nm ≤ λ ≤ 400 nm), 𝑇𝜆 denotes the average spectral transmittance and λ is the wavelength of radiation. Room temperature chemical/gas sensing performance of the modified fabrics was investigated using a homemade gas sensing unit integrated with high resistance electrometer (Keithley

7 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 173 5 6 174 7 8 9 175 10 11 176 12 13 14 177 15 16 178 17 18 179 19 20 180 21 22 181 23 182 24 25 183 26 27 184 28 29 30 185 31 32 186 33 187 34 35 188 36 37 189 38 39 40 190 41 42 191 43 44 192 45 46 193 47 48 49 194 50 51 195 52 53 196 54 55 197 56 57 198 58 59 60

Page 8 of 28

6517B, USA)49. Sensing response of the nanostructured modified cotton fabric can be calculated by using Eq. 5, 𝑅𝑎

𝑆 = 𝑅𝑔

(𝑖𝑓 𝑅𝑎 ≫ 𝑅𝑔)

(5)

where, Ra and Rg is the resistance of the sensing material in an ambient air atmosphere and analyte atmosphere respectively.

3. Results and discussion 3.1 Physical characteristics

Fig. 1. Photographs of (a) bare and (b) NiOx modified cotton fabrics.

The photographs of bare (White Color) and NiOx modified (Dark Blue Color) cotton fabrics are shown in Fig. 1. The weight of bare and modified fabrics was measured using the standard test method (ASTM D3776 M-Option 3:2017 standard). The weight of NiOx modified fabric (10.02 (oz/yd2)) was increased by 1.77 oz/yd2 with reference to the bare cotton sample (8.25 oz/yd2). This trend is well within the allowed standard of 2.5 to 13.8 (oz/yd2)50. Bending modulus of the cotton fabric was estimated by the cantilever method using stiffness analyzer (WIRA Instruments, UK). Stiffness of the surface modified cotton fabric was increased to 37.5 mm with reference to 32.5 mm for the bare sample.

8 ACS Paragon Plus Environment

Page 9 of 28 1 2 3 4 199 5 6 200 7 8 201 9 10 11 202 12 13 203 14 15 204 16 17 205 18 19 20 206 21 22 207 23 24 208 25 26 209 27 28 210 29 30 31 211 32 33 212 34 35 213 36 37 38 214 39 40 215 41 42 216 43 44 45 217 46 47 218 48 49 219 50 51 220 52 53 54 221 55 56 222 57 58 59 60

ACS Applied Materials & Interfaces

3.2 Crystal phase

Fig. 2. XRD patterns of (a) bare and (b) NiOx modified cotton fabrics.

XRD patterns of bare and NiOx grown cotton fabric samples are shown in Fig. 2. The bare cotton fabric exhibited microcrystalline cellulose structure (Fig. 2(a)) with diffraction peaks corresponding to (110), (110), (200) and (004) planes at 2θ = 14.5°, 16.1°, 22.2° and 33.6° respectively. The observed microcrystalline cellulose structure of bare cotton fabric is in good agreement with the standard JCPDS card no. [03-0226]51. The strong crystalline peak at 2θ = 22.2º denotes the presence of intermolecular hydrogen bonding52. The occurrence of crystal plane (004) could be attributed to the characteristic signatures of microcrystalline cellulose, which is in agreement with the results observed by Wang et al53. Fig. 2(b) shows the XRD pattern of NiOx modified fabric with diffraction planes of (001), (120), (002), (031), (230), (004) and (300) at 2θ= 18.9°, 21.1°, 23.4°, 36.8°, 40.6°, 47.8°, 59.70° respectively. The observed XRD pattern is in good aggreement with the standard JCPDS card no. [14-0117], [40-1179], [22-0444] corresponding to hexagonal, orthorhombic and hexagonal cubic structure of Ni(OH)2, α-3Ni(OH)2.2H2O and Ni2O3H respectively54. The presence of (200) and (004) planes in the NiOx modified fabric (Fig. 2(b)) confirmed the deposition of Ni2O3H on microcrystalline cotton cellulose. Though polycrystalline natured Ni2O3H structure was observed from Fig. 2(b), the crystallinity was observed to be very less in comparison to the bare cotton fabric. This could be due 9 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 223 5 6 224 7 8 225 9 10 11 226 12 13 14 227 15 16 228 17 18 229 19 20 230 21 22 23 231 24 25 232 26 27 233 28 29 30 234 31 32 235 33 34 236 35 36 237 37 38 238 39 40 41 239 42 43 240 44 45 241 46 47 48 242 49 50 243 51 52 244 53 54 245 55 56 57 58 59 60

Page 10 of 28

to the increased distance between the molecular chains (O-H) and damaged crystallite sites of Ni-O metal complexes influenced by interfacial gradient forces acting between the metal oxide matrix and the surface of cotton23. The formation of Ni2O3H phase could be due to the role of oxidization agent as it partially hydrolyzed nickel oxide (NiOx) for catalytic process55. The diffraction peak at 2θ = 6.3° might be due to the inherent presence of montmorillonite (MMT)56,57 in the cotton cellulose and the same has been suppressed after the modification of cotton surface with NiOx. Major peak found at 22.2° with an increased intensity and decreased fullwidth half maximum might be due to the increase in crystallite size with secondary wall cellulose. Absence of change in the crystallinity of (002) plane after hydrolysis revealed the presence of active amorphous region in cotton cellulose58. XRD pattern showed that nanoparticles are localized on the inward construction of the absorbent fabric. The observed peak shift after the modification of nanoparticles might be due to the interfacial forces playing between the nickel nanoparticles and cotton cellulose23. The average crystallite size of NiOx modified cotton fabric from (300) plane was 40 nm.

3.3 Morphological analysis and growth mechanism (a)

(b)

Fig. 3. FE-SEM images of (a) bare and (b) NiOx modified cotton fabrics. 10 ACS Paragon Plus Environment

Page 11 of 28 1 2 3 4 246 5 6 247 7 8 248 9 10 11 249 12 13 250 14 15 251 16 17 252 18 19 20 253 21 22 254 23 24 255 25 26 27 256 28 29 257 30 31 258 32 33 34 259 35 36 260 37 38 261 39 40 262 41 42 43 263 44 45 264 46 47 48 265 49 50 266 51 52 267 53 54 55 268 56 57 58 59 60

ACS Applied Materials & Interfaces

FE-SEM images of bare and NiOx modified cotton fabrics are shown in Fig. 3(a & b). The bare cotton fabrics showed the ordered arrangement of cellulose structure whereas NiOx modified cotton fabrics showed the growth of 3D green button chrysanthemum flower like structure on the cotton fabric. The formation of this structure on the cotton fibers mainly depends on the concentration of precursor solution with suitable oxidizing agents and growth duration. Growth of NiOx on the cotton fabric could be realized through the following mechanism: (i)

Potassium persulfate (K2S2O8) in the precursor acts as a strong oxidizing /structure directing agent and it generates more active sites on the surface of the cotton fabric. S2O82- ions from K2S2O8 react with Ni(OH)2 and gets oxidized. Composition of Ni decides the transformation of Ni(H2O)62+ to Ni(NH3)62+ as it depends on the concentration of ammonium hydroxide in the precursor solution. As the pretreated cotton fabric was dipped in to the precursor solution, Ni2+ ions from precursor solution get bonded with 𝑂𝐻 ― ions and lead to the formation of homogeneous Ni(OH)2. As an initial growth stage, the Ni nucleation sites from Ni(OH)2 get uniformly distributed over the surface of cotton fabrics.

(ii)

As a next stage, it was reduced to NiOOH as a sequence of color indication observed during the CBD process. As the Ni2+ nucleation sites grew further, the degree of supersaturation increases as a function of growth duration. This results in the formation of nickel oxy-hydroxide or nickel oxide hydroxide or nickel hydroxide. The possible formation reactions are given in equations (6–10) as reported by S.-Y. Han et al.,55

𝑁𝑖𝑆𝑂4 + 𝑥𝐾2𝑆2𝑂8― + 2(1 + 𝑥)𝑂𝐻 ― →𝑁𝑖𝑂1 + 𝑥 + 𝑥𝐾2𝑆𝑂4 + (1 + 𝑥)𝑆𝑂24 ― + (1 + 𝑥)𝐻2𝑂 𝑁𝑖𝑂1 + 𝑥 + 2𝑥/3𝑁𝐻3→𝑁𝑖𝑂 + 𝑥/3𝑁2 + 𝐻2𝑂

(6) (7)

𝑁𝑖2 + + 2𝑂𝐻 ― →𝑁𝑖(𝑂𝐻)2

(8)

𝑁𝑖(𝑂𝐻)2 + 𝑆2𝑂8― →2𝑁𝑖𝑂𝑂𝐻 + 2𝑆𝑂24 ― + 2𝐻 +

(9)

(or) 11 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 269 5 6 270 7 8 271 9 10 11 272 12 13 273 14 15 274 16 17 18 275 19 20 276 21 22 277 23 24 278 25 26 27 279 28 29 280 30 31 281 32 33 282 34 35 283 36 37 38 284 39 40 285 41 42 286 43 44 45 287 46 47 288 48 49 289 50 51 52 290 53 54 291 55 56 292 57 58 59 60

(10)

𝑁𝑖𝑂𝑂𝐻 + 𝐻2𝑂→𝑁𝑖(𝑂𝐻)2 +𝑂𝐻 (iii)

Page 12 of 28

Further the negatively charged cotton cellulose surface enhanced the binding nature of Ni2+ ions inturn facilitates the growth of 3D green button chrysanthemum flower like structure under drying temperature of 353 K (Fig. 4). The petals of flower were grown on the surface of each thread spreading in all the directions59.

Fig. 4. Schematic representation for the growth process of the NiOx on cotton cellulose.

At the beginning of growth process, primary source of Ni2+ ions dissolved in potassium persulfate was immediately hydrolyzed. During the interaction with ammonium hydroxide, the generated Ni(OH)2 nuclei having electrostatic driving force and minimized surface energy of cotton cellulose promoted the growth of nanosheets60,61. It is a well-known fact that the higher saturation level benefits the formation and enhancement of nucleation sites, while lower one facilitates the crystal growth. When the reaction time was extended gradually, further nucleation and assembly process enhanced the growth of nanosheets and lead to the formation of nanostructured NiOx 3D green button chrysanthemum flower on cotton fabric. This might be due the gradual self-orientation of nanosheets with lower surface energy. Specific surface area of bare and NiOx modified cotton cellulose was determined from N2 adsorption using Brunauer-Emett-Teller (BET) method (Fig. 5). NiOx modified cotton cellulose showed higher adsorption value of 8.1 cm3/g than bare cotton cellulose (2.6 cm3/g). Subsequently, the specific surface area of the bare and NiOx modified cotton cellulose found to be 2.64 and 3.46 m2/g respectively. The uniform NiOx nanoflower on cotton cellulose resulted in the 12 ACS Paragon Plus Environment

Page 13 of 28 1 2 3 4 293 5 6 294 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 295 26 27 296 28 29 297 30 31 298 32 299 33 34 300 35 36 301 37 302 38 39 303 40 41 304 42 305 306 43 308 307 44 45 309 310 46 47 311 48 49 313 312 50 51 314 52 53 54 315 55 56 316 57 58 59 60

ACS Applied Materials & Interfaces

increased surface area62. Further, to test the possibility of post processing of NiOx modified fabrics with dying, the surface modified samples were dyed with methylene blue and confirmed the same with functional analysis

using FTIR spectrometer (Fig. S1) and presented in supplementary information.

Fig. 5. N2 adsorption-

desorption isotherm of

(a) bare and (b) NiOx

modified cotton fabrics.

3.4

Contact

angle

measurement

13 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 317 5 6 318 7 8 319 9 10 11 320 12 13 321 14 15 322 16 17 323 18 19 324 20 21 325 22 23 24 326 25 26 327 27 28 328 29 30 31 329 32 33 330 34 35 331 36 37 38 332 39 40 333 41 42 334 43 44 335 45 46 47 336 48 49 337 50 51 338 52 53 54 339 55 56 340 57 58 59 60

Page 14 of 28

Fig. 6. Contact angle measurement of NiOx modified cotton cellulose.

To determine the wettability nature of bare and NiOx modified cotton fabrics, water contact angle measurement was carried out and the observed result for NiOx modified cloth is shown in Fig. 6. The water contact angle (CA) on NiOx modified cotton fabric was found to be 85.6°, which confirmed the increase in hydrophobic nature with reference to hydrophilic bare cotton fabric. The 3D green button chrysanthemum flower like structure of NiOx modified cotton fabric promotes the water repelling affinity at the edges of cellulose due to the influence of surface roughness63,64. Air plays a vital role in between the solid/liquid interface, which results in tramping of air occurred in-between the NiOx modified cotton fabric and water droplet65.

3.5 Thermogravimetric analysis

Fig. 7. Thermogravimetric analysis of (a) bare and (b) NiOx modified cotton fabrics. 14 ACS Paragon Plus Environment

Page 15 of 28 1 2 3 4 341 5 6 342 7 8 343 9 10 11 344 12 13 345 14 15 346 16 17 347 18 19 20 348 21 22 349 23 24 350 25 26 27 351 28 29 352 30 31 353 32 33 34 354 35 36 355 37 38 39 356 40 41 357 42 43 358 44 45 46 359 47 48 360 49 50 361 51 52 53 362 54 55 363 56 57 58 59 60

ACS Applied Materials & Interfaces

Thermogravimetric analysis (TGA) of the bare and modified cotton fabrics are shown in Fig. 7. This analysis was used to estimate the weight loss rate and thermal stability of the cotton fabrics. TGA of the bare cotton cellulose (Fig. 7(a)) comprises of three stages with respect to temperature. In the first stage, (below 275°C) there was an initial weight loss, which could be attributed to the dehydration of the cotton cellulose. Significant weight loss in the second stage (275 to 400°C) might be due to the degradation of crystalline region of bare cotton cellulose (char pyrolysis). With further increase in temperature, the bare cotton entered into the third stage namely pyrolysis region, where the complete sample was burnt. TGA analysis of NiOx modified fabric (Fig. 7(b)) comprises of two stages; first stage (20-275°C) revealed the evaporation of half of water molecules in the crystalline region66 and in the second stage (275-700°C), a sudden drop of weight loss was observed, which might be attributed to the removal of remaining water molecules and thermo oxidative decomposition of NiOx. After 700°C and up to 800°C, the weight percentage was started decreasing slowly and indicated the removal of the hydroxyl group present in cotton cellulose without any additional phases67. Thus, NiOx modified cotton fabric exhibited better thermal stability than bare cotton cellulose. Thermal degradation of NiOx modified fabric process can be represented by Eqn. (11), 𝑁𝑖2 + + 2𝑂𝐻 ―

𝑅𝑇

(11)

𝑁𝑖(𝑂𝐻)2

3.6 Differential scanning calorimetry

15 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 364 5 6 365 7 366 8 367 9 10 368 11 12 369 13 14 15 370 16 17 371 18 19 372 20 21 373 22 23 24 374 25 26 375 27 28 376 29 30 31 377 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 28

Fig. 8. Differential scanning calorimetry thermogram of bare and NiOx modified fabrics.

Fig. 8 shows the differential scanning calorimetry thermogram of bare and NiOx modified cotton fabrics at a controlled and constant heating rate. Bare and NiOx modified samples showed an intense endothermic behavior throughout the thermograph. Both the samples exhibited the endothermic peaks at 64.5 and 76.4ºC, which are attributed to the carboxyl group and elimination of bounded water compounds in cotton fabrics respectively68. A second endothermic peak at 126.9ºC corresponds to NiOx modified fabric, which could be due to the evaporation of solvents and partial decomposition of nickel group presented in the cotton cellulose 69.

Also, the peaks at 368.8 and 312ºC confirmed the final decomposition of cellulose crystal phase present

in the cotton fabrics68.

16 ACS Paragon Plus Environment

Page 17 of 28 1 2 3 4 378 5 6 7 379 8 9 380 10 11 381 12 13 14 382 15 16 383 17 18 384 19 20 385 21 22 23 386 24 25 387 26 27 388 28 29 30 389 31 32 390 33 34 391 35 36 37 392 38 393 39 394 40 41 395 42 396 43 397 44 45 46 398 47 48 399 49 50 400 51 52 53 401 54 55 402 56 57 58 59 60

ACS Applied Materials & Interfaces

3.7 X-ray photoelectron spectroscopy

Fig. 9. XPS (a) survey, (b) carbon 1s, (c) Ni 2p, and (d) Oxygen 1s spectra of the NiOx modified cotton cellulose. To investigate the NiOx modified surface on cotton fabric, XPS analysis was carried out and the survey spectra (Fig. 9(a)) confirmed the presence of various states of nickel, carbon and oxygen elements. Survey spectra showed the characteristic existence of NiO with Ni (2s, 2p, 2d, 3s & 3p), O (1s) and core level C 1s. Auger transition characteristics were also observed for Ni (LMM and O KLL). The C 1s peak was deconvoluted into two components (Fig. 9(b)) namely C-O/C-O-C and C=O/O-C=O at 285.4 and 288.5 eV70 respectively. Presence of Ni2+ and Ni3+ (Fig. 9(c)) was confirmed through the spin-orbit coupling of Ni 2p spectra. Ni 2p 17 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 403 5 6 404 7 8 405 9 10 11 406 12 13 407 14 15 408 16 17 409 18 19 20 410 21 22 411 23 24 412 25 26 27 413 28 29 414 30 31 415 32 33 34 416 35 36 417 37 38 418 39 40 419 41 42 43 420 44 45 421 46 47 422 48 49 50 423 51 52 424 53 54 425 55 56 57 426 58 59 60

Page 18 of 28

spectra was observed with Ni 2p3/2 and Ni 2p1/2 peaks at the binding energy range of 850-865 eV and 870885 eV71 respectively. In the present case, Ni 2p3/2 and Ni 2p1/2 peaks were observed at 856.5 and 874.2 eV respectively55. The shake-up satellites correspond to Ni2+ 2p3/2 and Ni3+ 2p1/2 were observed at 862 and 879.5 eV respectively. O 1s peak at 531.9 eV confirmed the appearance of oxygen in defect states in the adsorbed oxygen or hydroxide or oxygen crystal (Fig. 9(d)).

3.8 UV blocking property In electromagnetic spectrum, UV region has been classified into three bands such as UV-C (200-290 nm), UV-B (290-320 nm) and UV-A (320-400 nm) respectively. Whereas, UV-A and UV-B rays are considered to be harmful due to the maximum possibility of penetrating the skin surface and causing several human illnesses. The UV radiation blocking property of the NiOx modified fabrics depends on the type, thickness, inter-pore yarn size, color of the fabric and existence of UV absorbing agent18–20. An UPF rating represents the amount of UV rays is being blocked by the material. A fabric with a UPF rating of 50 would only allow 1/50th of the hazardous rays on its surface to pass through it, and hence UV rays exposure will be reduced by a factor of 50. Based on the UPF rating, fabrics quality can be classified as bad (50) respectively72. The UV blocking measurement of NiOx nanostructured fabric was tested as per the AATCC 183:2010 using UV transmittance analyzer. UPF measurement was carried out in the wavelength range of 290 to 450 nm for 5 times at different locations on the NiOx modified cotton fabric and the mean value was found to be 2000. When the surface modified NiOx fabric was kept in ambient atmosphere, oxygen molecules from the atmosphere adsorb the electrons from the conduction band of NiOOH and forms O2- depletion layer on the modified surface. Under UV exposure, photo-activated electron and hole pairs are generated. Subsequently, the photogenerated holes reacts with chemisorbed oxygen ions and release oxygen molecules. The chemisorption of oxygen species and reaction with photoactivated holes progressing continuously, which effectively block the UV rays. The redox reaction of the nickel oxide hydroxide modified 18 ACS Paragon Plus Environment

Page 19 of 28 1 2 3 4 427 5 6 428 7 8 429 9 10 11 430 12 13 431 14 15 432 16 17 433 18 19 20 434 21 22 435 23 24 436 25 26 27 437 28 29 438 30 31 439 32 33 34 440 35 36 441 37 38 442 39 40 443 41 42 444 43 445 44 45 446 46 447 47 48 49 448 50 51 449 52 53 450 54 55 451 56 57 58 59 60

ACS Applied Materials & Interfaces

fabric under UV illumination is expressed in the Eq. (12) 𝑁𝑖𝑂𝑂𝐻 + 𝑒 ― ↔𝑁𝑖𝑂 + 𝑂𝐻 ―

(12)

Also, the 3D green button chrysanthemum flower-like structure of NiOx modified cotton fabric promotes more active sites, which facilitates the multiple scattering and reflection phenomena44 in-turn enhance the UV filtering capacity. This enhanced UPF factor could be due to the influence of thickness, deeper coloration and NiOx nanoparticles present in the cotton fabric73. The UV-A and UV-B blocking capacity of NiOx modified fabrics were observed to be 99.90% and 99.93% respectively.

3.9 Gas sensing studies 3.9.1 Selectivity

Fig. 10. Selectivity of NiOx modified fabric towards 100 ppm of acetaldehyde, ammonia, formaldehyde, methanol, ethanol, isopropanol and trimethylamine vapours.

Selectivity of NiOx modified fabric was studied towards different gases such as trimethylamine, ammonia, ethanol, methanol, isopropanol, formaldehyde and acetaldehyde in which it showed selective response of 12431 towards 100 ppm of trimethylamine at room temperature as shown in Fig. 10. This selective response might be due to the lower bond dissociation energy of trimethylamine (351.456 kJ.mol-1) in comparison with 19 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 452 5 6 453 7 8 454 9 10 11 455 12 456 13 14 15 457 16 17 458 18 19 459 20 21 22 460 23 24 461 25 26 462 27 28 29 463 30 31 464 32 33 465 34 35 466 36 37 38 467 39 40 468 41 42 469 43 44 470 45 46 471 47 472 48 49 473 50 51 52 474 53 54 475 55 56 476 57 58 59 60

Page 20 of 28

other gases such as acetaldehyde (364 kJ.mol-1), ethanol (436 kJ.mol-1), formaldehyde (364 kJ.mol-1), methanol (436.8 kJ.mol-1) and ammonia (368 kJ.mol-1). Also, trimethylamine has weaker interaction with NiOx than other gases due to its Gibbs free energy ( △ 𝑓𝐺 ⋄ )13.

3.9.2 Transient studies

(c)

Fig. 11. (a) Transient resistance characteristics towards 100 ppm of trimethylamine vapour, (b) transient response of NiOx modified fabric towards various concentration from 2-200 ppm and (c) response and recovery times trend towards 100 ppm of trimethylamine. Transient response of the NiOx modified cotton fabrics was studied as a function of increasing concentration of trimethylamine from 2-200 ppm as shown in Fig. 11(a & b). The response was increased as a function of increasing concentration of trimethylamine. This behaviour could be due to the excessive presence of chemisorbed oxygen species on the surface of NiOx surface. The response and recovery times of the NiOx 20 ACS Paragon Plus Environment

Page 21 of 28 1 2 3 4 477 5 6 478 7 8 479 9 10 11 480 12 13 481 14 15 482 16 17 483 18 19 20 484 21 22 485 23 24 486 25 26 27 487 28 29 488 30 31 489 32 33 34 490 35 36 491 37 38 39 492 40 41 493 42 43 494 44 45 495 46 47 48 496 49 50 497 51 52 498 53 54 55 499 56 57 58 59 60

ACS Applied Materials & Interfaces

modified cotton fabrics were found to be 215 and 138 s respectively. Response and recovery times as a function of concentration are shown in Fig. 11(c).

3.9.3 Sensing mechanism The gas sensing mechanism of metal oxide materials modified cotton surface is based on the model of electron transfer dynamic during oxygen adsorption and desorption processes, which result in the change in surface resistance of the sensing element. When the surface modified cotton fabric is exposed to atmosphere, oxygen molecules get chemisorbed on the surface by trapping electrons from the conduction band of n-type semiconducting NiOx74. This interaction leads to the formation of surface charge region with O2- ions in-turn increases the surface resistance of the modified cotton fabric. The observed steady state surface resistance was fixed as the baseline resistance (Ra) for the sensing studies. The oxygen sorption reaction is given in Eqns. (13 & 14), (13)

𝑂2(𝑎𝑡𝑚𝑜𝑠𝑝ℎ𝑒𝑟𝑒)⇋ 𝑂2 (𝑎𝑑𝑠) 𝑂2 (𝑎𝑑𝑠) + 𝑒(―𝑁𝑖𝑂𝑥𝑠𝑢𝑟𝑓𝑎𝑐𝑒)⇋ 𝑂2 ― (ads) + ℎ +

(14)

In the presence of reducing type trimethylamine vapour, its interaction with NiOx modified cotton surface following the reaction given Eqn. (15) resulted in the decrease in its surface resistance from the base line value. During this interaction, electrons released by the target vapour resulted in the desorption of oxygen molecules in-turn increased the number of electrons in the conduction band of NiOx. The resultant steady state resistance is denoted as Rg and the sensing response was calculated using Eqn. 5. The gas-solid interaction scheme12 is shown in Eq. (15), ― →2𝑁2↑ + 12𝐶𝑂2↑ + 18𝐻2𝑂↑ + 21𝑒 ― 4(𝐶𝐻3)3𝑁 + 21𝑂2(𝑎𝑑𝑠)

(15)

4 Conclusion 21 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 500 5 6 501 7 8 502 9 10 11 503 12 13 504 14 15 505 16 17 506 18 19 20 507 21 22 508 23 24 509 25 26 27 510 28 29 511 30 31 512 32 33 34 513 35 36 514 37 38 515 39 40 516 41 42 517 43 44 518 45 519 46 47 520 48 521 49 522 50 523 51 52 524 53 525 54 55 526 56 527 57 58 59 60

Page 22 of 28

The surface modification process of cotton fabric with NiOx nanostructures was successfully accomplished using chemical bath deposition technique. The 3D green button chrysanthemum flower-like nanostructured NiOx modified cotton fabric exhibited a UPF of 2000. The developed multifunctional fabric showed a selective sensing response of 12431 towards trimethylamine at room temperature. The nanostructured cotton cellulose has good thermal stability and showed an increased hydrophobicity than the unmodified fabrics. This will ensure that the developed technical fabric can be used as protective suit against gas leaks, harmful UV rays, flame retardant and hydrophobic screens.

Acknowledgments The authors are grateful to Nano Mission, Department of Science & Technology, New Delhi for the funding support (SR/NM/NT- 1039/2015) and one of the authors Mr. S. Dinesh Kumar thanks Council of Scientific and Industrial Research, New Delhi for Senior Research Fellowship (09/1095(0035)/18-EMR-1). We also acknowledge SASTRA Deemed University, Thanjavur for extending infrastructure support to carry out the study.

References (1)

Gibson, J. H. UVB Radiation; 2004.

(2)

Strobel, N. Electromagnetic radiation http://www.astronomynotes.com/light/s3.htm.

(3)

Berneburg, M.; Surber, C. Children and Sun Protection. Br. J. Dermatol. 2009, 161 (SUPPL. 3), 33– 39. https://doi.org/10.1111/j.1365-2133.2009.09447.x.

(4)

Sobolewski, P. S.; Krzyścin, J. W.; Jarosławski, J.; Wink, J.; Lesiak, A.; Narbutt, J. Controlling Adverse and Beneficial Effects of Solar UV Radiation by Wearing Suitable Clothes - Spectral Transmission of Different Kinds of Fabrics. J. Photochem. Photobiol. B Biol. 2014, 140, 105–110. https://doi.org/10.1016/j.jphotobiol.2014.07.009.

(5)

Kaplan, L. A. Suntan, Sunburn, and Sun Protection. J. Wilderness Med. 1992, 3 (2), 173–196. https://doi.org/10.1580/0953-9859-3.2.173.

(6)

Rojas, J.; Londoño, C.; Ciro, Y. The Health Benefits of Natural Skin Uva Photoprotective Compounds Found in Botanical Sources. International Journal of Pharmacy and Pharmaceutical 22 ACS Paragon Plus Environment

Page 23 of 28 1 2 3 4 528 5 529 6 7 530 8 531 9 10 532 11 533 12 13 534 14 535 15 16 536 17 537 18 538 19 20 539 21 540 22 23 541 24 542 25 26 543 27 544 28 545 29 30 546 31 547 32 548 33 34 549 35 550 36 551 37 38 552 39 553 40 41 554 42 555 43 44 556 45 557 46 558 47 48 559 49 560 50 561 51 52 562 53 563 54 55 564 56 565 57 58 59 60

ACS Applied Materials & Interfaces

Sciences. 2016, pp 13–23. (7)

Environmental Effects of Ozone Depletion and Its Interactions with Climate Change: Progress Report, 2009. Photochem. Photobiol. Sci. 2010, 9 (3), 275–294. https://doi.org/10.1039/b923342n.

(8)

Kruss-scientific. Contact Angle https://www.kruss-scientific.com/services/educationtheory/glossary/contact-angle/ (accessed Nov 24, 2018).

(9)

Jain, S. k. Future of Technical Textiles. CITI. pp 1–38.

(10)

Vijayakumar, Y.; Mani, G. K.; Reddy, M. V. R.; Rayappan, J. B. B. Nanostructured Flower like V2O5 Thin Films and Its Room Temperature Sensing Characteristics. Ceram. Int. 2015, 41 (2), 2221–2227. https://doi.org/10.1016/j.ceramint.2014.10.023.

(11)

Muniyandi, I.; Mani, G. K.; Shankar, P.; Rayappan, J. B. B. Effect of Nickel Doping on Structural, Optical, Electrical and Ethanol Sensing Properties of Spray Deposited Nanostructured ZnO Thin Films. Ceram. Int. 2014, 40 (6), 7993–8001. https://doi.org/10.1016/j.ceramint.2013.12.150.

(12)

Arun Kumar, K. L.; Durgajanani, S.; Jeyaprakash, B. G.; Balaguru Rayappan, J. B. Nanostructured Ceria Thin Film for Ethanol and Trimethylamine Sensing. Sensors Actuators, B Chem. 2013, 177, 19–26. https://doi.org/10.1016/j.snb.2012.10.107.

(13)

Sivalingam, D.; Gopalakrishnan, J. B.; Rayappan, J. B. B. Structural, Morphological, Electrical and Vapour Sensing Properties of Mn Doped Nanostructured ZnO Thin Films. Sensors Actuators, B Chem. 2012, 166–167, 624–631. https://doi.org/10.1016/j.snb.2012.03.023.

(14)

Längkvist, M.; Coradeschi, S.; Loutfi, A.; Balaguru Rayappan, J. B. Fast Classification of Meat Spoilage Markers Using Nanostructured ZnO Thin Films and Unsupervised Feature Learning. Sensors (Switzerland) 2013, 13 (2), 1578–1592. https://doi.org/10.3390/s130201578.

(15)

Pereira, J.; Porto-Figueira, P.; Cavaco, C.; Taunk, K.; Rapole, S.; Dhakne, R.; Nagarajaram, H.; Câmara, J. S. Breath Analysis as a Potential and Non-Invasive Frontier in Disease Diagnosis: An Overview. Metabolites 2015, 5 (1), 3–55. https://doi.org/10.3390/metabo5010003.

(16)

last Visited 1 March 2019.

(17)

HAZARD SUMMARY IDENTIFICATION REASON FOR CITATION HOW TO DETERMINE IF YOU ARE BEING EXPOSED; 2003.

(18)

Wilson, C. A.; Bevin, N. K.; Laing, R. M.; Niven, B. E. Solar Protection — Effect of Selected Fabric and Use Characteristics on Ultraviolet Transmission. Text. Res. J. 2008, 78 (2), 95–104. https://doi.org/10.1177/0040517508089660.

(19)

Ghazi, S.; Couteau, C.; Paparis, E.; Coiffard, L. J. M. Interest of External Photoprotection by Means of Clothing and Sunscreen Products in Young Children. J. Eur. Acad. Dermatology Venereol. 2012, 26 (8), 1026–1030. https://doi.org/10.1111/j.1468-3083.2011.04139.x.

(20)

Cherif, C. Textile Materials for Lightweight Constructions; Cherif, C., Ed.; Springer Berlin Heidelberg: Berlin, Heidelberg, 2016. https://doi.org/10.1007/978-3-662-46341-3.

(21)

Dalavi, D. S. Synthesis and Characterization of Nanostructured NiO Thin Films and Their Electrochromic Properties, 2012. https://doi.org/10.1002/masy.200551124. 23 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 566 5 567 6 568 7 8 569 9 570 10 571 11 572 12 13 573 14 574 15 575 16 576 17 18 577 19 578 20 21 579 22 580 23 24 581 25 582 26 27 583 28 584 29 30 585 31 586 32 587 33 34 588 35 589 36 590 37 38 591 39 592 40 593 41 42 594 43 595 44 596 45 46 597 47 598 48 599 49 50 600 51 601 52 602 53 54 603 55 604 56 57 58 59 60

Page 24 of 28

(22)

Fasaki, I.; Koutoulaki, A.; Kompitsas, M.; Charitidis, C. Structural, Electrical and Mechanical Properties of NiO Thin Films Grown by Pulsed Laser Deposition. Appl. Surf. Sci. 2010, 257 (2), 429–433. https://doi.org/10.1016/J.APSUSC.2010.07.006.

(23)

Rajendran, V.; Dhineshbabu, N. R.; Kanna, R. R.; Kaler, K. V. I. S. Enhancement of Thermal Stability, Flame Retardancy, and Antimicrobial Properties of Cotton Fabrics Functionalized by Inorganic Nanocomposites. Ind. Eng. Chem. Res. 2014, 53 (50), 19512–19524. https://doi.org/10.1021/ie502584m.

(24)

Paravannoor, A.; Ranjusha, R.; Asha, A. M.; Vani, R.; Kalluri, S.; Subramanian, K. R. V.; Sivakumar, N.; Kim, T. N.; Nair, S. V.; Balakrishnan, A. Chemical and Structural Stability of Porous Thin Film NiO Nanowire Based Electrodes for Supercapacitors. Chem. Eng. J. 2013, 220, 360–366. https://doi.org/10.1016/j.cej.2013.01.063.

(25)

Song, J.-M.; Zhang, J.; Ni, J.-J.; Niu, H.-L.; Mao, C.-J.; Zhang, S.-Y.; Shen, Y.-H. One-Pot Synthesis of ZnO Decorated with AgBr Nanoparticles and Its Enhanced Photocatalytic Properties. CrystEngComm 2014, 16 (13), 2652. https://doi.org/10.1039/c3ce41943f.

(26)

Yuvakkumar, R.; Suresh, J.; Nathanael, A. J.; Sundrarajan, M.; Hong, S. I. Rambutan (Nephelium Lappaceum L.) Peel Extract Assisted Biomimetic Synthesis of Nickel Oxide Nanocrystals. Mater. Lett. 2014, 128, 170–174. https://doi.org/10.1016/j.matlet.2014.04.112.

(27)

Wang, R. H.; Xin, J. H.; Tao, X. M. UV-Blocking Property of Dumbbell-Shaped ZnO Crystallites on Cotton Fabrics. Inorg. Chem. 2005, 44 (11), 3926–3930. https://doi.org/10.1021/ic0503176.

(28)

Li, G.; Liu, H.; Zhao, H.; Gao, Y.; Wang, J.; Jiang, H.; Boughton, R. I. Chemical Assembly of TiO2 and TiO2@Ag Nanoparticles on Silk Fiber to Produce Multifunctional Fabrics. J. Colloid Interface Sci. 2011, 358 (1), 307–315. https://doi.org/10.1016/j.jcis.2011.02.053.

(29)

Subbiah, D. K.; Mani, G. K.; Babu, K. J.; Das, A.; Balaguru Rayappan, J. B. Nanostructured ZnO on Cotton Fabrics – A Novel Flexible Gas Sensor & UV Filter. J. Clean. Prod. 2018, 194, 372–382. https://doi.org/10.1016/j.jclepro.2018.05.110.

(30)

Farouk, A.; Sharaf, S.; Abd El-Hady, M. M. Preparation of Multifunctional Cationized Cotton Fabric Based on TiO2 Nanomaterials. Int. J. Biol. Macromol. 2013, 61, 230–237. https://doi.org/10.1016/j.ijbiomac.2013.06.022.

(31)

Dastjerdi, R.; Montazer, M. A Review on the Application of Inorganic Nano-Structured Materials in the Modification of Textiles: Focus on Anti-Microbial Properties. Colloids Surfaces B Biointerfaces 2010, 79 (1), 5–18. https://doi.org/10.1016/j.colsurfb.2010.03.029.

(32)

Mostashari, S. M.; Baghi, O.; Mostashari, S. Z. Thermogravimetric Analysis of a Cellulosic Fabric Treated With Nickel Sulfate Hexahydrate As a Flame-Retardant. Cellul. Chem. Technol. 2009, 43 (1–3), 95–98.

(33)

Shannon, R. D.; Shannon, R. C.; Medenbach, O.; Fischer, R. X. Refractive Index and Dispersion of Fluorides and Oxides. J. Phys. Chem. Ref. Data 2002, 31 (4), 931–970. https://doi.org/10.1063/1.1497384.

(34)

Rao, M. C.; Hussain, O. M. Optical Properties of Vacuum Evaporated WO3 Thin Films. Res. J. Chem. Sci. 2011, 1 (7), 76–80. 24 ACS Paragon Plus Environment

Page 25 of 28 1 2 3 4 605 5 606 6 607 7 8 608 9 609 10 610 11 12 611 13 612 14 613 15 16 614 17 615 18 616 19 20 617 21 618 22 619 23 24 620 25 621 26 27 622 28 623 29 30 624 31 625 32 626 33 34 627 35 628 36 37 629 38 630 39 40 631 41 632 42 633 43 44 634 45 635 46 636 47 637 48 49 638 50 639 51 52 640 53 641 54 642 55 56 643 57 58 59 60

ACS Applied Materials & Interfaces

(35)

Rana, M.; Hao, B.; Mu, L.; Chen, L.; Ma, P. C. Development of Multi-Functional Cotton Fabrics with Ag/AgBr-TiO2 Nanocomposite Coating. Compos. Sci. Technol. 2016, 122, 104–112. https://doi.org/10.1016/j.compscitech.2015.11.016.

(36)

Rehan, M.; Abdel-Wahed, N. A. M.; Farouk, A.; El-Zawahry, M. M. Extraction of Valuable Compounds from Orange Peel Waste for Advanced Functionalization of Cellulosic Surfaces. ACS Sustain. Chem. Eng. 2018, 6 (5), 5911–5928. https://doi.org/10.1021/acssuschemeng.7b04302.

(37)

Ibrahim, N. A.; Eid, B. M.; El-Aziz, E. A.; Abou Elmaaty, T. M.; Ramadan, S. M. Multifunctional Cellulose-Containing Fabrics Using Modified Finishing Formulations. RSC Adv. 2017, 7 (53), 33219–33230. https://doi.org/10.1039/c7ra05403c.

(38)

Jiang, S.; Xu, J.; Miao, D.; Peng, L.; Shang, S.; Zhu, P. Water-Repellency, Ultraviolet Protection and Infrared Emissivity Properties of AZO Film on Polyester Fabric. Ceram. Int. 2017, 43 (2), 2424– 2430. https://doi.org/10.1016/j.ceramint.2016.11.032.

(39)

Azeem, A.; Ashraf, M.; Munir, U.; Sarwar, Z.; Abid, S.; Iqbal, N. Synthesis of Tungsten Oxide Nanorod, Its Application on Textile Material, and Study of Its Functional Properties. J. Nanotechnol. 2016, 2016. https://doi.org/10.1155/2016/3942613.

(40)

Li, X.; Li, D.; Xu, J.; Jin, H.; Jin, D.; Peng, X.; Hong, B.; Li, J.; Yang, Y.; Ge, H.; et al. MesoporousStructure Enhanced Gas-Sensing Properties of Nickel Oxides Nanowires. Mater. Res. Bull. 2017, 89, 280–285. https://doi.org/10.1016/j.materresbull.2017.02.009.

(41)

Zheng, Y.; Zhu, B.; Chen, H.; You, W.; Jiang, C.; Yu, J. Hierarchical Flower-like Nickel(II) Oxide Microspheres with High Adsorption Capacity of Congo Red in Water. J. Colloid Interface Sci. 2017, 504, 688–696. https://doi.org/10.1016/j.jcis.2017.06.014.

(42)

Teng, B.; Shi, J.; Yao, C. Facile, Highly Efficient and Environmentally Friendly Transesterification Mediated by Platinum Dioxide and Nickel Oxide under Essentially Neutral Conditions. Green Chem. 2018, 20 (11), 2465–2471. https://doi.org/10.1039/c8gc00500a.

(43)

Montazer, M.; Harifi, T. Nanofinishing of Textile Materials; 2018.

(44)

Liu, P.; Ng, V. M. H.; Yao, Z.; Zhou, J.; Lei, Y.; Yang, Z.; Lv, H.; Kong, L. B. Facile Synthesis and Hierarchical Assembly of Flowerlike NiO Structures with Enhanced Dielectric and Microwave Absorption Properties. ACS Appl. Mater. Interfaces 2017, 9 (19), 16404–16416. https://doi.org/10.1021/acsami.7b02597.

(45)

Li, S. J.; Guo, W.; Yuan, B. Q.; Zhang, D. J.; Feng, Z. Q.; Du, J. M. Assembly of Ultrathin NiOOH Nanosheets on Electrochemically Pretreated Glassy Carbon Electrode for Electrocatalytic Oxidation of Glucose and Methanol. Sensors Actuators, B Chem. 2017, 240, 398–407. https://doi.org/10.1016/j.snb.2016.09.002.

(46)

John, M. J.; Anandjiwala, R. D. Surface Modification and Preparation Techniques for Textile Materials. Surf. Modif. Text. 2009, 1–25. https://doi.org/10.1533/9781845696689.1.

(47)

Alhebshi, N. a; Rakhi, R. B.; Alshareef, H. N. Conformal Coating of Ni(OH)2 Nanoflakes on Carbon Fibers by Chemical Bath Deposition for Efficient Supercapacitor Electrodes. J. Mater. Chem. A 2013, 1 (47), 14897. https://doi.org/10.1039/c3ta12936e.

(48)

Antonio Bianchi and Alessandro Bencini University of Florence, I. SYNTHESIS AND 25 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 644 5 645 6 7 646 8 647 9 648 10 11 649 12 650 13 14 651 15 652 16 17 653 18 654 19 655 20 21 656 22 657 23 658 24 659 25 26 660 27 661 28 662 29 30 663 31 664 32 665 33 34 666 35 667 36 37 668 38 669 39 40 670 41 671 42 43 672 44 673 45 674 46 47 675 48 676 49 50 677 51 678 52 679 53 54 680 55 681 56 682 57 58 59 60

Page 26 of 28

SPECTROSCOPY OF TRANSITION METAL COMPLEXES. In INORGANIC AND BIOINORGANIC CHEMISTRY; Vol. II. (49)

Shankar, P.; Rayappan, J. B. B. Racetrack Effect on the Dissimilar Sensing Response of ZnO Thin Film—An Anisotropy of Isotropy. ACS Appl. Mater. Interfaces 2016, 8 (37), 24924–24932. https://doi.org/10.1021/acsami.6b05133.

(50)

Part II: Textile Fabrics. In Textile Research Journal; Book, Mcgraw-hill, 1950; Vol. 20, pp 844–857. https://doi.org/10.1177/004051755002001204.

(51)

Wittwer, R. A.; Dorn, B.; Jossi, W.; van der Heijden, M. G. A. Supplementary Information. Sci. Rep. 2017, 7 (41911), 1–16. https://doi.org/10.1038/srep41911.

(52)

Gouda, M.; Keshk, S. M. A. S. Evaluation of Multifunctional Properties of Cotton Fabric Based on Metal/Chitosan Film. Carbohydr. Polym. 2010, 80 (2), 505–513. https://doi.org/10.1016/j.carbpol.2009.12.011.

(53)

Wang, C.; Lv, J.; Ren, Y.; Zhou, Q.; Chen, J.; Zhi, T.; Lu, Z.; Gao, D.; Ma, Z.; Jin, L. Cotton Fabric with Plasma Pretreatment and ZnO/Carboxymethyl Chitosan Composite Finishing for Durable UV Resistance and Antibacterial Property. Carbohydr. Polym. 2016, 138, 106–113. https://doi.org/10.1016/j.carbpol.2015.11.046.

(54)

Bakar, M. A.; Hamid, M. A. A.; Jalar, A.; Shamsudin, R. Transformation Nanostructured Nickel Hydroxide to Nickel Oxide Film by Aqueous Chemical Growth. AIP Conf. Proc. 2013, 1528, 359– 364. https://doi.org/10.1063/1.4803625.

(55)

Han, S.-Y.; Lee, D.-H.; Chang, Y.-J.; Ryu, S.-O.; Lee, T.-J.; Chang, C.-H. The Growth Mechanism of Nickel Oxide Thin Films by Room-Temperature Chemical Bath Deposition. J. Electrochem. Soc. 2006, 153 (6), C382. https://doi.org/10.1149/1.2186767.

(56)

Chen, G. G.; Qi, X. M.; Li, M. P.; Guan, Y.; Bian, J.; Peng, F.; Yao, C. L.; Sun, R. C. Hemicelluloses/Montmorillonite Hybrid Films with Improved Mechanical and Barrier Properties. Sci. Rep. 2015, 5 (November 2015). https://doi.org/10.1038/srep16405.

(57)

Alekseeva, O. V; Rodionova, A. N.; Bagrovskaya, N. A.; Agafonov, A. V; Noskov, A. V. Effect of the Bentonite Filler on Structure and Properties of Composites Based on Hydroxyethyl Cellulose. 2015, 2017. https://doi.org/10.1016/j.arabjc.2015.07.011.

(58)

Zhao, H.; Kwak, J. H.; Conrad Zhang, Z.; Brown, H. M.; Arey, B. W.; Holladay, J. E. Studying Cellulose Fiber Structure by SEM, XRD, NMR and Acid Hydrolysis. Carbohydr. Polym. 2007, 68 (2), 235–241. https://doi.org/10.1016/j.carbpol.2006.12.013.

(59)

Zhao, C.; Du, F.; Wang, J. Flower-like Nickel Oxide Micro/Nanostructures: Synthesis and Enhanced Electrochromic Properties. RSC Adv. 2015, 5 (48), 38706–38711. https://doi.org/10.1039/c5ra05334j.

(60)

Tian, M.; Hu, X.; Qu, L.; Zhu, S.; Sun, Y.; Han, G. Versatile and Ductile Cotton Fabric Achieved via Layer-by-Layer Self-Assembly by Consecutive Adsorption of Graphene Doped PEDOT: PSS and Chitosan. Carbon N. Y. 2016, 96, 1166–1174. https://doi.org/10.1016/j.carbon.2015.10.080.

(61)

Wang, L.; Yu, H. Synthesis, Properties and Applications of Ferrocene-Based Derivatives, Polymers and Hydrogels; SpringerBriefs in Molecular Science; Springer Singapore: Singapore, 2018. https://doi.org/10.1007/978-981-10-6062-5. 26 ACS Paragon Plus Environment

Page 27 of 28 1 2 3 4 683 5 684 6 685 7 686 8 9 687 10 688 11 12 689 13 690 14 691 15 16 692 17 693 18 694 19 20 695 21 696 22 697 23 24 698 25 699 26 27 700 28 701 29 30 702 31 703 32 704 33 34 705 35 706 36 37 707 38 708 39 709 40 41 710 42 711 43 712 44 45 713 46 714 47 715 48 49 716 50 717 51 52 718 53 719 54 720 55 56 721 57 58 59 60

ACS Applied Materials & Interfaces

(62)

Gupta, A.; Srivastava, R. Mini Submersible Pump Assisted Sonochemical Reactors: Large-Scale Synthesis of Zinc Oxide Nanoparticles and Nanoleaves for Antibacterial and Anti-Counterfeiting Applications. Ultrason. Sonochem. 2019, 52, 414–427. https://doi.org/https://doi.org/10.1016/j.ultsonch.2018.12.020.

(63)

Liu, Y.; Xin, J. H.; Choi, C. H. Cotton Fabrics with Single-Faced Superhydrophobicity. Langmuir 2012, 28 (50), 17426–17434. https://doi.org/10.1021/la303714h.

(64)

Xu, L.; Zhang, X.; Shen, Y.; Ding, Y.; Wang, L.; Sheng, Y. Durable Superhydrophobic Cotton Textiles with Ultraviolet-Blocking Property and Photocatalysis Based on Flower-Like Copper Sulfide. Ind. Eng. Chem. Res. 2018, 57 (19), 6714–6725. https://doi.org/10.1021/acs.iecr.8b00254.

(65)

Li, S.; Huang, J.; Chen, Z.; Chen, G.; Lai, Y. A Review on Special Wettability Textiles: Theoretical Models, Fabrication Technologies and Multifunctional Applications. J. Mater. Chem. A 2017, 5 (1), 31–55. https://doi.org/10.1039/c6ta07984a.

(66)

Kumar, S.; Brijeshlata; Dixit, S. Screening of Traditional Indian Spices for Inhibitory Activity of Acetylcholinesterase and Butyrylcholinesterase Enzymes. Int. J. Pharma Bio Sci. 2012, 3 (1), P59– P65. https://doi.org/10.1039/x0xx00000x.

(67)

BR, S.; XR, J. Effect of Calcination Time on Structural, Optical and Antimicrobial Properties of Nickel Oxide Nanoparticles. J. Theor. Comput. Sci. 2016, 03 (02), 0–0. https://doi.org/10.4172/2376130X.1000149.

(68)

Elbariji, S.; Pétrissans, A.; Elamine, M.; Ouzaouit, K.; Kabli, H.; Albourine, A.; Gerardin, P. Removal of Cu 2+ from Aqueous Solutions by Adsorption on Chemically Modified Cellulosic Supports. Part. Sci. Technol. 2011, 29 (4), 320–332. https://doi.org/10.1080/02726351.2010.499561.

(69)

Kolathodi, M. S.; Palei, M.; Natarajan, T. S. Electrospun NiO Nanofibers as Cathode Materials for High Performance Asymmetric Supercapacitors. J. Mater. Chem. A 2015, 3 (14), 7513–7522. https://doi.org/10.1039/c4ta07075e.

(70)

Liu, W.; Lu, C.; Wang, X.; Liang, K.; Tay, B. K. In Situ Fabrication of Three-Dimensional, Ultrathin Graphite/Carbon Nanotube/NiO Composite as Binder-Free Electrode for High-Performance Energy Storage. J. Mater. Chem. A 2015, 3 (2), 624–633. https://doi.org/10.1039/c4ta04023f.

(71)

Huang, W.; Ding, S.; Chen, Y.; Hao, W.; Lai, X.; Peng, J.; Tu, J.; Cao, Y.; Li, X. 3D NiO Hollow Sphere/Reduced Graphene Oxide Composite for High-Performance Glucose Biosensor. Sci. Rep. 2017, 7 (1), 1–11. https://doi.org/10.1038/s41598-017-05528-1.

(72)

Wang, R.; Wang, X.; Xin, J. H. Advanced Visible-Light-Driven Self-Cleaning Cotton by Au/TiO 2/SiO2 Photocatalysts. ACS Appl. Mater. Interfaces 2010, 2 (1), 82–85. https://doi.org/10.1021/am900588s.

(73)

Liu, Y.; Wang, X.; Qi, K.; Xin, J. H. Functionalization of Cotton with Carbon Nanotubes. J. Mater. Chem. 2008, 18 (29), 3454. https://doi.org/10.1039/b801849a.

(74)

Diplas, S.; Knutsen, T.; Jørgensen, S.; Gunnæs, A. E.; Våland, T.; Norby, T.; Olsen, A.; Taftø, J. An Experimental Study of the Electronic Structure of Anodically Grown Films on an Amorphous Ni78Si8B14 Alloy. Surf. Interface Anal. 2008, 40 (3–4), 826–829. https://doi.org/10.1002/sia.2748.

27 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces 1 2 3 4 722 5 723 6 7 8 724 9 10 725 11 12 726 13 14 15 727 16 17 728 18 19 729 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 28 of 28

Highlights  Synthesis and surface modification of NiOx nanoflower on cotton cellulose  Multi-functional cotton fabrics for UV blocking and selective detection of TMA at room temperature  Inorganic modified fabrics showed an enhanced Ultraviolet protection factor of 2000  TMA vapour was detected using surface modified cotton cellulose with response and recovery times of 215 and 138 s  Thermal degradation of NiOx modified fabrics was enhanced up to 800℃