Novel π-Conjugated Polymer Based on Extended Thienoquinoid

the move: promises for future solar energy technology. Angew. Chem. Int. Ed. 2012, 43, 2020-2067. [6] Bin, H.; Gao, L.; Zhang, Z. G.; Yang, Y.; Zhang,...
0 downloads 15 Views 487KB Size
Subscriber access provided by READING UNIV

Communication

Novel #-Conjugated Polymer Based on Extended Thienoquinoid Yunhao Cai, Xiaonan Xue, Guangchao Han, Zhaozhao Bi, Bingbing Fan, Tao Liu, Dongjun Xie, Lijun Huo, Wei Ma, Yuanping Yi, Chuluo Yang, and Yanming Sun Chem. Mater., Just Accepted Manuscript • DOI: 10.1021/acs.chemmater.7b04592 • Publication Date (Web): 08 Jan 2018 Downloaded from http://pubs.acs.org on January 9, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Chemistry of Materials is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 6 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

Novel π-Conjugated Polymer Based on Extended Thienoquinoid Yunhao Cai†, Xiaonan Xue†, Guangchao Han‡, Zhaozhao Bi§, Bingbing Fan†, Tao Liu†, Dongjun Xie∥, Lijun Huo,†,* Wei Ma§, Yuanping Yi, Chuluo Yang∥, and Yanming Sun†,* †

Heeger Beijing Research and Development Center, School of Chemistry and Environment, Beihang University, Beijing 100191, China ‡ Beijing National Laboratory for Molecular Science, Key Laboratory of Organic Solids, Institute of Chemistry, Chinese Academy of Sciences, Beijing 100190, China § State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China ∥

Hubei Key Lab on Organic and Polymeric Optoelectronic Materials, Department of Chemistry, Wuhan University, Wuhan 430072, China

ABSTRACT: With a fused terthiophene, dithieno[3,4-b:2’,3’d]thiophene (DTT) is a thienoquinoidal building block for conjuagted polymers. However, due to its highly extended heteroarene structure, chemical synthesis of functional DTT unit is a challenge. All known DTT-based polymer films were prepared by electrochemical polymerization approach. In this study, we firstly synthesized functional DTT monomer and DTT-based conjugated polymer, PDBT-DTT via a typical Stille coupling reaction. With another fused thiophene ring, DTT shows increased aromatic (weaker quinoid) character compared to thieno-[3,4-b]thiophene (TT) unit. Moreover, PDBT-DTT showed much higher photovoltaic performance as well as better thermal and photostability than its TT-based analogue (PDBT-TT). The results demonstrate that DTT is a potential quinoidal building block for constructing highperformance conjugated polymers.

Organic semiconductors have garnered considerable interests due to their numerous applications in organic electronics such as organic field-effect transistors (OFETs), organic light-emitting diodes (OLEDs), organic solar cells (OSCs), etc.[1-5] Significant progress has been made in this respect over the past decade with the development of π-conjugated polymers.[6-11] In most cases, high-performance conjugated polymers are designed and synthesized with a “donor-acceptor” (D-A) approach, in which electronrich and electron-deficient components are alternated in the backbone of polymers.[12-13] Quinoidal structures incorporating expanded para-quinodimethane units with electron-withdrawing groups have been widely used as the acceptor units for designing conjugated polymers.[14-16] The quinoidal molecules can possess unique properties including low band gap along with high absorption coefficients, deep highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) energy levels, near-infrared fluorescence, singlet-fission property as well as prominent charge transport ability because of their favorable planarity originating from double bonds and extended πconjugation.[17-21] Several representative conjugated polymers with quinoidal structures are shown in Figure 1.[22-26] Among these quinoidal units, thieno-[3,4-b]thiophene (TT) unit with functional groups have recently emerged as an extremely attractive electron-

withdrawing building block for conjugated polymers.[27-29] Yu et al. first applied TT unit into organic photovoltaic materials, and then developed a series of polythienothiophene-cobenzodithiophene copolymers.[30-32] From then on, intensive efforts have been dedicated toward the design of TT-based copolymers with state-of-the-art power conversion efficiencies (PCEs) over 10%.[33-34]

Figure 1. The representative π-conjugated polymers with quinoidal structures. It should be noted that in comparison with the aromatic form, the quinoid form is energetically less stable since obtaining a quinoidal structure needs to destroy the degree of aromaticity and a loss in the stabilization energy.[35-36] To achieve a chemically stable quinoidal structure, an alternative building block with enhanced aromaticity is highly desirable. Dithieno[3,4-b:2’,3’d]thiophene (DTT) (see Figure 1 for its chemical structure) is an interesting quinoidal unit where an aromatic thienothiophene moiety is fused to each thiophene ring. Despite apparent advantages of DTT unit, such as highly efficient π-electron delocalization, low electronic π→π* band gap and specific optical properties, its synthesis remains a challenge due to its highly extended heteroarene structure.[37-39]To the best of our knowledge, until now, there is no report for functional/soluble DTT derivatives. The well-studied low-bandgap poly(dithieno[3,4-b:2',3'-d]thiophene) (pDTT) polymer can be only obtained by electrochemical polymerization method (Figure 1).[40-43] In this contribution, we firstly report an efficient synthetic route for a new functional and energy level tunable DTT derivative (DTT-ester), in which the most reactive site is substituted by soluble ester group (Scheme 1). The electron deficient ester moiety

ACS Paragon Plus Environment

Chemistry of Materials

TT-E

S Sn

S

S R1

Br

S S

Sn

S

R1

Br

O R R1

S

S Br

*

O S

S S

R= 2-ethhexyl R1= n-octyl

R1

O S

n

PDBT-TT

O R

R1 DBT

R1

xi

+

*

S

S

S

*

S

6 solution film

(a)

n

DTT-E R1

0.6 PDBT-DTT

R1

Scheme 1. Synthetic route of functional DTT-E unit, PDBT-DTT and PDBT-TT: i) DCC, DMAP, ethanol; ii) chloromethyl ethyl ether, Tin(IV) chloride, 50oC, overnight; iii) Na2S, methanol; iv) NaOH, THF, 60 oC, overnight; v) Cu, quinoline; vi) LDA, 0 oC, N-formaylpiperidine, then room temperature 12 h; vii) 2ethylhexyl thioglycolate, K2CO3, DMF; viii) McPBA, ethyl acetate, -78 oC; ix) acetic anhydride, reflux, 30 min; x) NBS, DMF; xi) Pd(ph3P)4, Toluene, reflux, overnight. We tried several synthetic routes for DTT-ester unit (Scheme S1). Finally, we succeeded in obtaining the target compound by a fine molecular designing. The synthetic route was described as follows: firstly, an esterification of 3-bromothiophene-2carboxylic acid was done by introducing a soluble ethyl side chains to achieve compound 1. Compound 1 was then converted into bischloromethyl product of compound 2 with titanium (IV) chloride as catalyst under violent stirring conditions. Subsequently, ring-closing reaction of compound 2 was carried out in a methanol solution of equimolar sodium sulfide to obtain compound 3. Then compound 3 was hydrolyzed in an aqueous solution of sodium hydroxide to get compound 4 and formyl group was removed by catalystic copper power in a quinoline solution at reflux temperature with a yield of 60%. Compound 6 was synthesized by lithium diisopropylamide and N-formaylpiperidine. The

7 4

2

0

14

10 12

2

4

16

6 8 10 12 14 16 18 Bond number

DBT-TT

0.8 S

11 8

Figure 2. Plots of C−C and C=C bond lengths in DBT-DTT and DBT-TT. The red and blue arrows highlight the different units possessing contrasting bond length alternation characters. DFT calculations were performed to determine the geometric and electronic structure of PDBT-DTT using the tuned-ωB97XD functional and the 6-31G** basis set (Figure S2 and S3).[44] It has been proved that more thiophene units in β-fused thiophene could facilitate the localization of quinoidal properties on the paraquinodimethane unit.[45] As illustrated in Figure 2, the DTT unit in PDBT-DTT shows greater bond length variations than the TT unit in PDBT-TT, with obviously longer C−C and shorter C=C lengths, especially for the C13-C14 length. This result discloses that DTT exhibits slightly weaker quinoidal (stronger aromatic) character than TT.[46-47] Based on the DFT results, PDBT-DTT molecule has nearly planar backbone (Figure S4), which is favorable for charge transport.[48-49]

S

S

6 3

5 4 3

0.4

2 0.2 1 0.0

0 400

500 600 700 Wavelength(nm)

800

(b) Current (mA)

S

S

17 15

9

5

-1

Br

R1

S

S

13

DBT-DTT DBT-TT

1

4

*

S

O S

S

S R1

O R

R1

S

DBT-DTT

1.46 1.45 1.44 1.43 1.42 1.41 1.40 1.39 1.38 1.37

Absorption coefficient (10 cm )

R1 O R O

key intermediate of 7 was obtained by condensation reaction between compound 6 and 2-ethylhexyl thioglycolate in a water-free system. Compound 9 was synthesized by 3-chloroperbenzoic acid as oxidant then the target monomer of DTT was finished by a simple bromide process. In the following polymerization process, a typical Stille coupling reaction was carried out by copolymerizing DTT and DBT to obtain PDBT-DTT (Scheme 1). PDBT-DTT has good thermal stability with a decomposition temperature more than 405 oC under inert atmosphere (Figure S1).

Bond length (Å)

candecrease the HOMO level and band gap of DTT, which can lead to a better oxidative stability (Figure 1b). By incorporating dithienobenzodithiophenes (DBT) as the electron donor and DTTester as the acceptor, a novel conjugated copolymer, poly{dithieno[2,3-d:2’,3’-d’]benzo[1,2-b:4,5-b’]dithiophene-codithienothiophene}(PDBT-DTT), was synthesized. Its chemical structure is shown in Scheme 1. Compared to its TT-based analogue (PDBT-TT, see Scheme S2 for its structure), PDBT-DTT has a deeper ionization potential (IP). Moreover, the DTT unit in PDBT-DTT showed greater bond length variation than the TT unit in PDBT-TT, and with obviously longer C−C and shorter C=C lengths, suggesting that PDBT-DTT exhibits more aromatic (weaker quinoid) character than PDBT-TT. To evaluate the application in organic electronics, organic solar cells (OSCs) based on PDBT-DTT have been fabricated. As a result, PDBT-DTT showed much higher photovoltaic performance than those of PDBT-TT, regardless of the acceptor materials used. More importantly, we noticed that PDBT-DTT devices exhibit better thermal and photostability than PDBT-TT devices. The results suggested that DTT is a highly promising quinoidal unit for constructing high-performance conjugated polymers for organic electronics.

Absorbance

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 6

-2

-1 0 1 Potential (V vs Ag/Ag+)

2

Figure 3. (a) UV-vis absorption spectra of PDBT-DTT (in solution and film). (b) Cyclic voltammetry measurement of PDBTDTT (in solution). Figure 3a shows the UV−vis absorption spectra of PDBTDTT. In dilute chloroform solution, PDBT-DTT displays a maximum absorption peak at 578 nm. Compared to the peak in the solution, PDBT-DTT film shows ca. 36 nm red-shift in absorption (614 nm) with the onset value of 693 nm, corresponding to an optical band gap (Egopt) of 1.79 eV. In terms of PDBT-TT, its absorption spectra in solution and film are nearly identical with Egopt of 1.63 eV. The maximum absorption coefficient of PDBTDTT film was measured to be 50474 cm−1, and slightly higher than that of PDBT-TT, indicating its good light-absorbing capability (Figure S4). Electrochemical cyclic voltammetry (CV) was carried out to investigate the energy level of the two polymers (Figure 3b and Figure S4). The HOMO and the LUMO energy levels of PDBT-DTT and PDBT-TT are -5.42, -5.36 and -3.32, 3.36 eV, respectively (Figure 3b). Moreover, ultraviolet photoelectron spectroscopy (UPS) was performed to measure the IP of

ACS Paragon Plus Environment

Page 3 of 6

neat polymer films (Figure S5). The IP and electron affinity (EA) of PDBT-DTT and PDBT-TT are calculated to be 4.91, 4.66 and 3.12, 3.03 eV, respectively. The results agree well with the trend of open-circuit voltage (Voc) observed in OSCs and also are consistent with the DFT results. (b) PDBT-DTT:PC71BM

-2

0

80 70

PDBT-DTT:IDTPTC PDBT-TT:PC71BM

60

PDBT-TT:IDTPTC

IPCE (%)

Current density (mA cm )

(a)

-5

-10

50 40 30 20 10

-15 -0.2

0.0

0.2

0.4

0.6

0 300

0.8

400

Voltage (V )

(c) PDBT-DTT PDBT-TT

700

800

PDBT-DTT PDBT-TT

1.0

Normalized PCE

0.8 0.6 0.4 0.2 0.0 0.0

500 600 Wavelength (nm)

(d)

1.0

Normalized PCE

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

0.8 0.6 0.4 0.2

0.5

1.0

1.5 2.0 Time (h)

2.5

3.0

0.0 0.0

0.5

1.0

1.5 2.0 Time (h)

2.5

3.0

Figure 4. (a, b) J–V characteristics and the corresponding IPCE spectra of optimal PDBT-DTT and PDBT-TT-based OSCs under the illumination of AM1.5G, 100 mW cm−2. (c, d) Thermal and light stability test of PDBT-DTT:ITCPTC and PDBT-TT:ITCPTC devices.

Table 1. Photovoltaic performance of OSCs based on PDBTTT and PDBT-DTT under the illumination of AM1.5G, 100 mW cm-2. Active layer

Voc

Jsc

FF

PCE[1]

PCEmax

[mA/cm2]

[%]

[%]

[%]

PDBTDTT: PC71BM

0.84±0.01

13.5±0.1

60.7±0.7

6.9±0.1

7.01

PDBT-DTT: ITCPTC

0.79±0.01

15.6±0.1

68.2±0.8

8.6±0.2

8.74

PDBT-TT: PC71BM

0.51±0.01

10.5±0.2

56.3±0.9

3.1±0.1

3.09

PDBT-TT: ITCPTC

0.50±0.01

11.2±0.2

37.6±0.5

2.2±0.1

2.17

[1]

FF of 67% were achieved, demonstrating that PDBT-DTT is a very promising donor candidate for incorporation in various kinds of organic photovoltaic devices. In contrast, OSCs based on PDBT-TT displayed much lower photovoltaic performance. The hole and electron mobilities in PDBT-DTT:ITCPTC blend were measured as 1.58×10-3 and 2.50×10-3 cm2/Vs, respectively (Figure S8-S9 and Table S9). The high carrier mobility and balanced carrier transport are one of the main reasons of high PCEs achieved in PDBT-DTT devices. The device stability was also tested. As shown in Figure 4c and 4d, PDBT devices exhibited increased photostability and thermal stability than PDBT-TT cells, which are crucially important for industry production of OSCs. The corresponding incident photon conversion efficiency (IPCE) spectra of OSCs are shown in Figure 4b. Broad IPCE spectra from 300 to 750 nm were observed in PC71BM-based solar cells and 300-800 nm for non-fullerene-based devices. Especially for PDBTDTT:ITCPTC device, IPCE exceeds 65% from 565 to 730 nm, with a peak of 70% at 710 nm, indicative of efficient photon harvesting and charge collection. PDBT-DTT:ITCPTC device yielded a higher photocurrent. The calculated Jsc from the IPCE spectra is 15.36 mA cm−2, consistent with the value (15.60 mA cm−2) obtained from J–V measurements. The surface morphologies of the blend films were studied by using atomic force microscopy (AFM) and transmission electron microscopy (TEM) (Figure S10-S12). It can be seen from AFM and TEM images that without DIO additive, the surfaces of PDBT-DTT:PC71BM and PDBT-DTT:ITCPTC films are smooth with root-mean-square (RMS) roughness of 1.15 and 1.42 nm, respectively. With DIO additive, both of the blend films showed a better phase separation and the RMS values increased to 2.45 and 1.78 nm, which is probably another reason of high PCEs achieved in PDBT-DTT:ITCPTC devices.

The average PCE value was calculated from 10 devices for each condition.

In order to evaluate the application of PDBT-DTT in organic electronics, organic solar cells (OSCs) were fabricated with PC71BM as the acceptor initially. Chloroform was used as the host solvent and 1,8-diiodooctane (DIO) was used as the solvent additive to optimize the active layer morphology.[50] The detailed data for device optimizations are summarized in Figure S6 and S7, and Table S1-S8. Under the optimal condition, PDBT-DTT:PC71BM device showed a power conversion efficiency (PCE) of 7.01% with a short-circuit current (Jsc) of 13.60 mA cm−2, a Voc of 0.84 V, and a fill factor (FF) of 61%. Furthermore, the application of PDBT-DTT in non-fullerene OSCs has been also tested. 3,9bis(2-methylene-(3-(1,1-dicyanomethylene)-cyclopentane-1,3dione-[c]thiophen))-5,5,11,11-tetrakis(4-hexylphenyl)dithieno[2,3-d:2’,3’-d’]-s-indaceno[1,2-b:5,6-b’]dithiophene (ITCPTC) with complementary absorption with PDBT-DTT was employed as the acceptor (Scheme S3).[51] As a result, a high PCE of 8.74%, with a Jsc of 15.60 mA cm−2, a Voc of 0.79 V, and a

Figure 5. 2D GIWAXS patterns of (a) neat PDBT-DTT film, (b) neat ITCPTC film, (c) PDBT-DTT:PC71BM film, and (d) PDBTDTT:ITCPTC film. (e) Out-of-plane and in-plane linecuts of PDBT-DTT, ITCPTC and the blend films. Grazing-incidence wide-angle X-ray scattering (GIWAXS) were performed to investigate the molecular packing and orientation of the films.Figure 5 shows the 2D GIWAXS patterns and corresponding in-plane and out-of-plane linecuts. For the neat films, PDBT-DTT exhibited a preferential face-on orientation, as indicated by a conspicuous (100) lamellar diffraction peak at qxy ≈ 0.32 Å-1 (d ≈ 19.6 Å) and strong (010) π−π stacking peak at qz ≈ 1.70 Å-1 (d ≈ 3.70 Å) The face-on orientation is proved to be beneficial to vertical charge transport. Correspondingly, PDBT-DTT neat films show a high hole mobility of ~3.0×10-3 cm2/Vs (Table S9). When blending with PC71BM, PDBT-DTT showed a mixed face-on and edge-on orientation, as evidenced by the increased lamellar scattering and decreased π−π stacking in out-of-plane

ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

direction. Although the crystalline nature of PDBT-DTT was hampered by ITCPTC in the blend film, the lamellar scattering of PDBT-DTT in in-plane direction is still obvious. Together with the distinct π−π stacking peak in out-of-plane direction, PDBT-TT still showed a preferred face-on molecular orientation. As a result, PDBT-DTT:ITCPTC blend exhibited slightly higher hole and electron mobilities than those of PDBT-DTT:PC71BM films. In conclusion, we firstly synthesized functional and soluble DTT unit and DTT-containing conjugated polymer, PDBT-DTT, which has a main absorption ranging from 400 to 700 nm, a deep IP value, and a high hole mobility of ~3.0×10-3 cm2/Vs. With one more thiophene ring fused with TT unit, DTT shows increased aromatic (weaker quinoid) character than TT unit. In a preliminary evaluation of the potential of the PDBT-DTT for organic electronics, OSCs based on PDBT-DTT and different types of acceptors were fabricated. A higher photovoltaic performance and better device stability than devices based on its TT analogue were achieved. These promising results make DTT and its derivatives as attractive building blocks for developing high-performance πconjugated polymers.

[5]

ASSOCIATED CONTENT

[10]

[6]

[7]

[8]

[9]

Supporting Information Experimental details, synthesis and characterizations, device fabrication and characterizations, DFT calculation, UV absorption spectra, cyclic voltammogram measurement, UPS measurements, AFM and TEM images, SCLC measurements and device performance. This material is available free of charge via the Internet at http://pubs.acs.org. AUTHOR INFORMATION

[11]

[12]

[13]

Corresponding Author

[14]

[email protected];sunym@ buaa.edu.cn

Notes

[15]

The authors declare no competing financial interests.

ACKNOWLEDGMENT This work was financially supported by the National Natural Science Foundation of China (NSFC) (No., 21734001, 51473009, 21674007), and the International Science & Technology Cooperation Program of China (no. 2014DFA52820).

[16]

[17]

REFERENCES [1]

[2]

[3]

[4]

Liang, Y.; Feng, D.; Tsai, S.-T.; Son, H.-J.; Li, G.; Yu, L.Highly efficient solar cell polymers developed via fine-tuning of structural and electronic properties. J. Am. Chem. Soc.2009, 131, 22, 77927799. Beaujuge, P. M.; Fréchet, J. M. J. Molecular design and ordering effects in π-functional materials for transistor and solar cell applications. J. Am. Chem. Soc. 2011, 133, 20009-20029. Henson, B.; Bazan, G. C. Design strategies for organic semiconductors beyond the molecular formula. Nat. Chem. 2012, 4, 699-704. Gelinck, G.; Heremans, P.; Nomoto, K.; Anthopoulos, T. D. Organic transistors in optical displays and microelectronic applications. Adv. Mater. 2010, 22, 3778-3798.

[18]

[19]

[20]

Page 4 of 6

Mishra, A.; Bäuerle, P. Small molecule organic semiconductors on the move: promises for future solar energy technology. Angew. Chem. Int. Ed. 2012, 43, 2020-2067. Bin, H.; Gao, L.; Zhang, Z. G.; Yang, Y.; Zhang, Y.; Zhang, C.; Chen, S.; Xue, L.;Yang, C.; Xiao, M.; Li, Y. 11.4% Efficiency non-fullerene polymer solar cells with trialkylsilyl substituted 2Dconjugated polymer as donor. Nat. Commun. 2016, 7, 13651. Liu, T.; Pan, X.; Meng, X.; Liu, Y.; Wei, D.; Ma, W.; Huo, L.; Sun, X.; Lee, T. H.; Huang ,M.; Choi, H.; Kim, J. Y.; Choy, W. C.; Sun, Y. Alkyl Side-Chain Engineering in Wide-Bandgap Copolymers Leading to Power Conversion Efficiencies over 10%. Adv. Mater. 2017, 29, 1604251. Chen, Z.; Lee, M. J.; Ashraf, R. S.; Gu, Y.; Albert-Seifried, S.; Nielsen, M. M.; Schroeder, B.; Anthopoulos, T. D.; Heeney, M.; McCulloch, I.; Sirringhaus, H. High-Performance Ambipolar Diketopyrrolopyrrole-Thieno [3,2-b] thiophene Copolymer Field‐Effect Transistors with Balanced Hole and Electron Mobilities. Adv. Mater. 2012, 24, 647-652. Ji, Y.; Xiao, C.; Wang, Q.; Zhang, J.; Li, C.; Wu, Y.; Wei, Z.; Zhan, X.; Hu, W.; Wang, Z.; Janssen, R. A.; Li, W. Asymmetric Diketopyrrolopyrrole Conjugated Polymers for Field‐Effect Transistors and Polymer Solar Cells Processed from a Nonchlorinated Solvent. Adv. Mater. 2016, 28, 943-950. Hu, Z.; Huang, F.; Cao, Y.Water/alcohol soluble conjugated polymers for the interface engineering of highly efficient polymer light-emitting diodes and polymer solar cells.Chem. Commun. 2015, 51, 5572-5585. Dou, C.; Ding, Z.; Zhang, Z.; Xie, Z. Liu, J.; Wang, L. Developing Conjugated Polymers with High Electron Affinity by Replacing a C-C Unit with a B←N Unit. Angew. Chem. Int. Ed. 2015, 54, 36483652. Beaujuge, P. M.; Amb, C. M.; Reynolds, J. R. Spectral engineering in π-conjugated polymers with intramolecular donor-acceptor interactions. Acc. Chem. Res. 2010, 43 ,1396-1407. Mullen, K.; Pisula, W. Donor-Acceptor Polymers. J. Am. Chem. Soc. 2015, 137, 9503-9505. Lu, L.; Zheng, T.; Wu, Q.; Schneider, A. M.; Zhao, D.; Yu, L.Recent advances in bulk heterojunction polymer solar cells. Chem. Rev. 2015, 115, 12666-12731. Hwang, H.; Kim, Y.; Kang, M.; Lee, M.-H.; Heo, Y.-J.;Kim, D.Y.A conjugated polymer with high planarity and extended πelectron delocalization via a quinoid structure prepared by short synthetic steps. Polym. Chem. 2017, 8, 361-365. Janzen, D. E.;Ewbank, P. C.; Pappenfus, T. M.; Higuchi, H.; Filho, D. A.; Young, S. V. G.; Brédas, J.-L.; Mann, K. R. Preparation and characterization of π-stacking quinodimethane oligothiophenes. Predicting semiconductor behavior and bandwidths from crystal structures and molecular orbital calculations. J. Am. Chem. Soc. 2004, 126, 15295-15308. Ren, L.; Fan, H.; Huang, D.; Yuan, D.; Di, C. A.; Zhu, X. Dithienoindophenines: p-Type Semiconductors Designed by Quinoid Stabilization for Solar-Cell Applications. Chem. Eur. J. 2016, 22, 17136-17140. Kawata, S.; Pu, Y. J.; Saito, A.; Kurashige, Y.; Beppu, T.; Katagiri, H.; Hada, M.; Kido, J. Singlet Fission of Non-polycyclic Aromatic Molecules in Organic Photovoltaics. Adv.Mater. 2016, 28, 15851590. Takahashi, T.; Takimiya, K.; Otsubo, T.; Aso, Y. Extensive quinoidal oligothiophenes with dicyanomethylene groups at terminal positions as highly amphoteric redox molecules. J. Am. Chem. Soc. 2005, 127, 8928-8929. Zhang, C.; Zang, Y.; Gann, E.; McNeill, C. R.; Zhu, X.; Di, C. A.; Zhu, D. Two-dimensional π-expanded quinoidal terthiophenes terminated with dicyanomethylenes as n-type semiconductors for high-performance organic thin-film transistors. J. Am. Chem. Soc. 2014, 136, 16176-16184.

ACS Paragon Plus Environment

Page 5 of 6 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Chemistry of Materials

[21] Ren, L.; Liu, F.; Shen, X.; Zhang, C.; Yi, Y.; Zhu, X. Developing Quinoidal Fluorophores with Unusually Strong Red/Near-Infrared Emission. J. Am. Chem. Soc. 2015, 137, 11294-11302. [22] Lee, Y. S.; Kertesz, M.; Elsenbaumer, R. L. Importance of energetics in the design of small bandgap conducting polymers. Chem. Mater. 1990, 2, 526-530. [23] Lee, K. Poly (thieno [3, 4-b] thiophene). A new stable low band gap conducting polymer. Macromolecules 2001, 34, 5746-5747. [24] Wudl, F.; Heeger, A. J. Poly (isothianaphthene). J. Org. Chem. 1984, 49, 3382-3384. [25] Kenning, D.; Calhoun, T. R.; Funfar, M. R.; Sattler, D. J.; Rasmussen, S. C. Thieno [3,4-b] pyrazines: synthesis, structure, and reactivity. J. Org. Chem. 2002, 67, 9073-9076. [26] Bolognesi, A.; Catellani, M.; Destri, S.; Zamboni, R.; Taliani, C.Poly (dithieno [3,4-b:3′,4′-d] thiophene): a new transparent conducting polymer. J. Am. Chem. Soc, Chem. Commun. 1988, 4, 246-247. [27] Liu, F.; Fan, H.; Zhang, Z.; Zhu, X. Low-bandgap small-molecule donor material containing thieno [3,4-b] thiophene moiety for highperformance solar cells. Appl. Mater. Interfaces 2015, 8, 3661-3668. [28] Zhang, C.; Zhu, X. Thieno [3,4-b] thiophene-Based Novel SmallMolecule Optoelectronic Materials. Acc.Chem. Res. 2017, 50, 1342. [29] Liu, F.; Espejo,G. L.; Qiu, S. M.; Oliva, M.; Pina, J.; Melo, J. S. S.; Casado, J.; Zhu, X. Multifaceted regioregular oligo (thieno [3,4-b] thiophene) s enabled by tunable quinoidization and reduced energy band gap. J. Am. Chem. Soc. 2015, 137, 10357-10366. [30] Liang,Y.; Xu, Z.; Xia, J.; Tsai, S. T.; Wu, Y.; Li, G.; Ray, C.; Yu, L. For the bright future—bulk heterojunction polymer solar cells with power conversion efficiency of 7.4%. Adv. Mater .2010, 22, E135. [31] Lu, L.; Yu, L. Understanding low bandgap polymer PTB7 and optimizing polymer solar cells based on it. Adv. Mater. 2014, 26, 4413-4430 [32] Liang, Y.; Wu, Y. Tsai, S.-T.; Li, G.; Ray, C.; Yu, L. Highly efficient solar cell polymers developed via fine-tuning of structural and electronic properties. J. Am.Chem. Soc. 2009, 131, 7792-7799. [33] He, Z.; Xiao, B.; Liu, F.; Wu, H.; Yang, Y.; Xiao, S.; Wang, C.; Russell, T. P.; Cao, Y.Single-junction polymer solar cells with high efficiency and photovoltage.Nat. Photonics 2015, 9,174-179. [34] Wan, Q.; Guo, X.; Wang, Z.; Li, W.; Guo, B.; Ma, W.; Zhang, M.; Li, Y. 10.8% Efficiency Polymer Solar Cells Based on PTB7-Th and PC71BM via Binary Solvent Additives Treatment. Adv. Funct. Mater. 2016, 26, 6635-6640. [35] Casado, J.; Ortiz, R. P.; Navarrete, J. T. L.Quinoidal oligothiophenes: new properties behind an unconventional electronic structure. Chem. Soc. Rev. 2012, 41, 5672-5686. [36] Son, H. J.; He, F.; Carsten, B.; Yu, L. Are we there yet? Design of better conjugated polymers for polymer solar cells. J. Mater. Chem. 2011, 21, 18934-18945. [37] Nietfeld, J. P.; Heth, C. L.; Rasmussen, S. C. Poly (acenaphtho [1, 2-b] thieno [3,4-e] pyrazine): a new low band gap conjugated polymer. Chem.Commun. 2008,8, 981-983. [38] Cravino, H. N.; Luzzati, A. S.; Catellani, M.; Petr, A.;Dunsch, N. S. S. L. Positive and negative charge carriers in doped or photoexcited polydithienothiophenes: a comparative study using Raman, infrared,

[39] [40]

[41]

[42]

[43]

[44]

[45]

[46]

[47]

[48]

[49]

[50]

[51]

and electron spin resonance spectroscopy. J. Phys. Chem. B 2002, 106, 3583-3591. Jong, F. D.Synthesis of dithienothiophenes. J. Org. Chem. 1971, 36, 1998-2000. Neugebauer, H. Infrared signatures of positive and negative charge carriers in conjugated polymers with low band gaps. J. Electroanal. Chem. 2004, 563, 153-159. Arbizzani, C.; Cerroni, M. G.; Mastragostino, M. Polydithienothiophenes: two new conjugated materials with narrow band gap. Synthetic Metals 1997, 84, 249-250. Arbizzani, C.; Catellani, M.; Mastragostino, M.; Mingazzini, C. Nand P-doped Polydithieno [3,4-B:3′,4′-D] thiophene: A narrow band gap polymer for redox supercapacitors. Electrochim. Acta. 1995, 40, 1871-1876. Neugebauer, H.; Cravino,A.; Luzzati, S.; Catellani, M.; Petr, A.; Dunsch, L.; Sariciftci, N.S. Spectral signatures of positive and negative charged states in doped and photoexcited low band-gap polydithienothiophenes. Synthetic Met. 2003, 139, 747-750. Körzdörfer, T.; Brédas J.-L. Organic Electronic Materials: Recent Advances in the DFT Description of the Ground and Excited States Using Tuned Range-Separated Hybrid Functionals. Acc. Chem. Res. 2014, 47, 3284−3291. Liu, X.; He, B.; Anderson, C. L.; Kang, J.; Chen, T.; Chen, J.; Feng, S.; Zhang, L.; Kolaczkowski, M. A.; Teat, S. J.; Brady, M. A.; Zhu, C.; Wang, L. W.; Chen, J.; Liu, Y. para-Azaquinodimethane: a Compact Quinodimethane Variant as an Ambient Stable Building Block for High Performance Low Band Gap Polymers. J. Am. Chem. Soc. 2017, 139, 8355-8363. Ehrenfreund, E.; Cravino, A.; Neugebauer, H.; Sariciftci, N. S.; Luzzati, S.; Catellani, M. Even parity states in small band gap πconjugated polymers: polydithienothiophenes. Chem. Phys. Lett. 2004, 394, 132-136. Cravino, A.; Neugebauer, H.; Luzzati, S.; Catellani, A. M.; Sariciftci, N. S. Vibrational Spectroscopy on pDTT3 A Low Band Gap Polymer Based on Dithienothiophene. J. Phys. Chem. B 2001, 105, 46-52. Wakim, S.;Aich, B. R.;Tao, Y.;Leclerc,M. Charge transport, photovoltaic, and thermoelectric properties of poly (2, 7-carbazole) and poly (indolo [3,2-b] carbazole) derivatives. Polym. Rev. 2008, 48, 432-462. Mei, J.; Kim, D. H.; Ayzner, A. L.; Toney, M. F.; Bao, Z. Siloxaneterminated solubilizing side chains: bringing conjugated polymer backbones closer and boosting hole mobilities in thin-film transistors. J. Am. Chem. Soc. 2011, 133, 20130-20133. Lee, J. K.; Ma, W. L.; Brabec, C. J.; Yuen, J.; Moon, J. S.; Kim, J. Y.; Lee, K.; Bazan G. C.; Heeger, A. J. Processing Additives for Improved Efficiency from Bulk Heterojunction Solar Cells. J. Am. Chem. Soc. 2008, 130, 3619-3623. Xie, D.; Liu, T.; Gao, W.; Zhong, C.; Huo, L.; Luo, Z.; Wu, K.; Xiong, W.; Liu, F.; Sun, Y.; Yang, C. You have full text access to this contentA Novel Thiophene-Fused Ending Group Enabling an Excellent Small Molecule Acceptor for High-Performance Fullerene-Free Polymer Solar Cells with 11.8% Efficiency. Sol. RRL 2017, 1, 201700044.

Table of Contents ACS Paragon Plus Environment

Chemistry of Materials 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60