Optomechanical Thermometry of Nanoribbon Cantilevers Anupum Pant, Bennett E Smith, Matthew J. Crane, Xuezhe Zhou, Matthew B. Lim, Stuart Frazier, E. James Davis, and Peter J. Pauzauskie J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.8b00365 • Publication Date (Web): 12 Mar 2018 Downloaded from http://pubs.acs.org on March 12, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 24 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Optomechanical Thermometry of Nanoribbon Cantilevers Anupum Pant,†,k Bennett E. Smith,‡,k Matthew J. Crane,¶ Xuezhe Zhou,† Matthew B. Lim,† Stuart Frazier,† E. James Davis,¶ and Peter J. Pauzauskie∗,†,§ †Materials Science and Engineering Department, University of Washington, Seattle, Washington 98195-2120, United States ‡Chemistry Department, University of Washington, Seattle, Washington 98195-2120, United States ¶Chemical Engineering Department, University of Washington, Seattle, Washington 98195-2120, United States §Physical & Computational Sciences Directorate, Pacific Northwest National Laboratory, Richland, WA 99352, USA kContributed equally to this work E-mail: [email protected]

1

ACS Paragon Plus Environment

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Abstract Cadmium sulfide (CdS) nanostructures have attracted a significant amount of attention for a variety of optoelectronic applications including photovoltaic cells, semiconductor lasers, and solid-state laser refrigeration due to their direct bandgap around 2.42 eV and high radiative quantum efficiency. Nanoribbons (NRs) of CdS have been claimed to laser cool following excitation at 514 and 532 nm wavelengths by the annihilation of optical phonons during anti-Stokes photoluminescence. To explore this claim, we demonstrate a novel optomechanical experimental technique for micro-thermometry of a CdSNR cantilever using Young’s modulus as the primary temperature-dependent observable. Measurements of the cantilever’s fundamental acoustic eigenfrequency at low laser powers showed a red-shift in the eigenfrequency with increasing power, suggesting net heating. At high laser powers, a decrease in the rate of red-shift of the eigenfrequency is explained using Euler-Bernoulli elastic beam theory, considering Hookean optical-trapping force. A predicted imaginary refractive index for CdSNR based on experimental temperature measurement agrees well with a heat transfer analysis that predicts the temperature distribution within the cantilever and the time required to reach steady state (