Supporting Information Ordered CdSe Nanoparticles within Self-Assembled Block Copolymer Domains on Surfaces Shan Zou†, Rui Hong††, Todd Emrick†† and Gilbert C. Walker†* †
Department of Chemistry, University of Toronto, 80 St. George Street, Toronto, Ontario M5S 3H6, Canada †† Department of Polymer Science and Engineering,University of Massachusetts, 120 Governors Drive, Amherst, MA 01003, USA
Figure S1. AFM height and phase images of a TOPO-CdSe/PS-b-P2VP film on a Si substrate before annealing. Image size: 2000 × 2000 nm and Z-range: 20 nm, 30°.
Figure S2. AFM height and phase images of a CH2Cl2 vapour annealed PS-b-P2VP film on Si substrate. Image size: 900 × 900 nm and Z-range: 10 nm, 30°.
Figure S3. Particle center-to-center distance pair-wise correlation plot for TOPO-CdSe nanoparticles in PS-b-P2VP on Si substrates.