Letter

Para-Conjugated Dicarboxylates with Extended Aromatic Skeletons as the Highly Advanced Organic Anodes for K-ion Battery Chao Li, Qijiu Deng, Haochen Tan, Chuan Wang, Cong Fan, Jingfang Pei, Bei Cao, Zhihong Wang, and Jingze Li ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b08974 • Publication Date (Web): 04 Aug 2017 Downloaded from http://pubs.acs.org on August 5, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 17

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Para-Conjugated Dicarboxylates with Extended Aromatic Skeletons as the Highly Advanced Organic Anodes for K-ion Battery Chao Li,a Qijiu Deng,a Haochen Tan,a Chuan Wang,a Cong Fan,a* Jingfang Pei,a Bei Cao,b* Zhihong Wanga and Jingze Lia* a State Key Laboratory of Electronic Thin Films and Integrated Devices, School of Microelectronics and Solid-state Electronics, University of Electronic Science and Technology of China (UESTC), Chengdu 610054, P. R. China b State Key Laboratory of Synthetic Chemistry, Institute of Molecular Functional Materials, Department of Chemistry, The University of Hong Kong, Hong Kong 999077, P. R. China Keywords: organic anodes, para-conjugated dicarboxylates, extended aromatic skeletons, graphene, K-ion battery Abstract: A new family of the para-conjugated dicarboxylates embedding in biphenyl skeletons was exploited as the highly advanced organic anodes for K-ion battery. Two members of this family, namely potassium 1,1'-biphenyl-4,4'-dicarboxylate (K2BPDC) and potassium 4,4'-Estilbenedicarboxylate (K2SBDC), were selectively studied and their detailed redox behaviors in K-ion battery were also clearly unveiled. Both K2BPDC and K2SBDC could exhibit very clear and highly reversible two-electron redox mechanism in K-ion battery, as well as higher potassiation potentials (above 0.3 V vs. K+/K) when compared to the inorganic anodes of carbon materials recently reported. Meanwhile, the satisfactory specific and rate capacities could be realized for K2BPDC and K2SBDC. For example, the K2BPDC anode could realize the stable rate capacities of 165/143/135/99 mAh g-1 under the high current densities of 100/200/500/1000 mA g-1 respectively, after its electronic conductivity was improved by mixing a very small amount of graphene. More impressively, the average specific capacities of ~75 mAh g-1 could be maintained for the K2BPDC anode for 3000 cycles under the high current density of 1 A g-1. The rechargeable Li-ion batteries (LIBs) widely commercialized in portable electronics and/or electric vehicles gradually meet the fatal challenge that the global resources of Li element

ACS Paragon Plus Environment

1

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 17

will probably be running out. Moreover, the LIBs based on the conventional inorganic electrodes are approaching the ceiling of energy density for the limited choices of intercalation cathodes and thus hardly meet the urgently-increasing need for energy-storage requirement, particularly under the price consideration for large-scale electrical grid application.1 Alternatively, most attentions are shifted back to the second alkali element of Na-ion batteries (NIBs) due to the lowcost Na minerals (∼2.74% of Na vs. ∼0.0065% of Li in the earth’s crust) and the similar electrochemical properties. Tremendous and significant progresses have been reported in NIBs nowadays.2-4 Interestingly, K-ion batteries (KIBs) of the same alkali group are not largely considered up to now,5 despite the fact that they exhibit in principle similar advantages with NIBs but the standard redox potential of K/K+ couple (-2.94 V vs. SHE) is much lower than Na/Na+ (-2.71 V) and closer to Li/Li+ (-3.04 V) couple.6 Remarkably, the experimental measurements have shown that the redox potential of K/K+ couple in non-aqueous electrolytes could be the most negative one among all alkali-metal analogues.7 However, the apparently large radius of K+ ion (1.38 Å vs. 0.76/1.00 Å for Li+/Na+ ion) could seriously impede the further development of KIBs based on the conventional intercalation/deintercalation mechanism. Moreover, it is worth noting that the exploitation of anode materials for KIBs has priority to their cathode counterparts, since the proper anode materials can directly and effectively avoid the risk of producing highly-reactive K metal during charging/discharging processes. Currently, several inorganic cathodes8 such as KTi2(PO4)3,9 K0.25V2O5,10 K0.3MnO2,6 Prussian blue and its analogues,11-13 and very few inorganic anodes (e.g., carbon materials14-16 and K2Ti80717) have been reported for KIBs. Regretfully, the specific capacities and rate performance for these inorganic anodes in KIBs were unsatisfactory, along with the poor cell cyclability and low inserting K-ion potential (vs. K/K+).

ACS Paragon Plus Environment

2

Page 3 of 17

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Advantageously, organic compounds are gradually attracting more and more attentions as the highly promising electrode materials.18-19 Not only pure organic materials are structure contrivable, composed by abundant elements, and almost without concern for production cost, but also both LIBs and NIBs based on organic electrodes have achieved comparatively high gravimetric energy density and cell cyclability to their inorganic counterparts.20-21 Much more importantly, unlike the inorganic solid/crystal formed by covalent and/or ionic bond, the solid/crystal state of organic materials (small molecules or polymers) is mainly interacted by van der Waals forces, which strongly indicates that organic electrodes could provide more void room and low energy barrier for accommodating most metal ions without the size concern. Truly, our group and Chen’s group independently and initially unveiled that the typical representative of potassium terephthalate (K2TP) belonging to the family of para-aromatic dicarboxylates could be the highly efficient organic anode for KIBs, and satisfactory results were realized.22-23 Despite of these encouraging advancements, it is remarkable that the families of organic anodes suitable for KIBs are currently very scarce. Meanwhile, the rate capacites and cell cyclability of organic anodes in KIBs still need improving. Herein, we initially report a new family of organic anodes for KIBs based on the paraconjugated dicarboxylates of aromatic biphenyl skeleton. Compared to K2TP of only one phenyl ring, the biphenyl skeleton with larger π conjugation should be more advantageous for intermolecular electron transportation. Two typical members of this family, namely potassium 1,1'-biphenyl-4,4'-dicarboxylate

(K2BPDC)

and

potassium

4,4'-E-stilbenedicarboxylate

(K2SBDC), were selectively and fully studied. Both K2BPDC and K2SBDC could exhibit very clear and highly reversible two-electron redox mechanism in KIBs. Meanwhile, they could possess the high potassiation potentials of 0.35 and 0.55 V (vs. K+/K), respectively. After their

ACS Paragon Plus Environment

3

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 17

particle dispersion and electronic conductivity were simply improved, both the rate capacities and cell cyclability could be satisfactorily realized. For instance, the modified K2BPDC anode could achieve the average specific capacity of ~75 mAh g-1 for 3000 cycles under the high current density of 1 A g-1.

Figure 1. The chemical structures of potassium 1,1'-biphenyl-4,4'-dicarboxylate (K2BPDC) and potassium 4,4'-E-stilbenedicarboxylate (K2SBDC), and their proposed redox mechanism in K-ion battery.

The chemical structures of potassium 1,1'-biphenyl-4,4'-dicarboxylate (K2BPDC) and potassium 4,4'-E-stilbenedicarboxylate (K2SBDC) were depicted in Figure 1. Their synthesis could feasibly follow the similar procedures reported by our group,24 where the neutralization reaction between the acid precursors of 1,1'-biphenyl-4,4'-dicarboxylic acid (H2BPDC) or 4,4'-Estilbenedicarboxylic acid (H2SBDC) and the base of KOH could afford K2BPDC and K2SBDC with satisfactory yields above 80%. See synthetic details in Supporting Informaion (SI). The infrared (IR) spectra of the as-obtained K2BPDC and K2SBDC were shown in Figure S1a-b. Combined the experimental results with the simulation data calculated (Figure S1c-d), the bands located at around 1399/1403 cm-1 for K2BPDC/K2SBDC were assigned to νs (COO-) vibrations while the bands residing at 1583/1588 and 1539/1547 cm-1 were assigned to their νas (COO-) vibrations coupled with the benzene skeleton vibrations, respectively.25 At the same time, the broaden peaks in the range of 2400 to 3200 cm-1 belonging to the stretching vibrations of O-H

ACS Paragon Plus Environment

4

Page 5 of 17

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

bond in H2BPDC and H2SBDC disappeared. Furthermore, the purity and chemical structures of K2BPDC and K2SBDC were confirmed by 1H NMR spectra (Figure S2), where the distinct H signals from benzene ring (δ=7.85/7.68 ppm or δ=7.76/7.56 ppm) and alkene (δ=7.25 ppm) were clearly detected but no H signals from the residual COOH group were observed, indicating the complete conversion of H2BPDC and H2SBDC. In their X-ray diffraction patterns (Figure S3), the selected characteristic peaks for K2BPDC (2θ=6.14, 15.53 and 27.84o) and K2SBDC (2θ=5.51, 27.75 and 33.37o) were respectively reported. Since the growth of their single crystal was unsatisfactory even tremendous efforts were paid, the information about their lattice planes regarding these typical peaks was currently unavailable. Both K2BPDC and K2SBDC exhibited very impressive thermal stability, as confirmed by the high thermal decomposition temperatures (Td, corresponding to 5% weight loss in the thermogravimetric analysis) of 578 °C for K2BPDC and 542 °C for K2SBDC (Figure S4), which were significantly higher than their acid analogues of H2BPDC (300 °C) and H2SBDC (363 °C). The morphology images collected by scanning electron microscope (SEM) for the newly-prepared K2BPDC and K2SBDC were shown in Figure S5, where they exhibited the relatively uniform shape of thin slices in the size range of micrometer scale (>1 µm). The tap density of K2BPDC or K2SBDC was calculated to be around 0.7 g/cm3, which was lower than the inorganic and carbonaceous anode materials (e.g., ~1 g/cm3 for graphite) and thus could lead to the less volumetric energy density. As shown in Figure 2, the multi-scanned cyclic voltammograms (CVs) of K2BPDC and K2SBDC were initially carried out to inspect their electrochemical behaviors in K-ion half cells (see details in SI). In the 1st cathodic scan (Figure 2a), K2BPDC displayed complicated reduction behaviors, where the board potential around 0.5 V (vs. K+/K) was attributed to the irreversible formation of solid-electrolyte interface (SEI) and the potential located at 0.2 V was

ACS Paragon Plus Environment

5

ACS Applied Materials & Interfaces

the reduction of BPDC2- anion.22 Gradually, the clear and stable redox couple belonging to the organic BPDC2- anion appeared after the 1st scan, where the cathodic peak was located at ~0.35 V and the back reversible anodic peak was at ~0.97 V. Similarly, the irreversible formation of SEI for K2SBDC was observed at ~0.63 V in the 1st cathodic scan but then the clear redox behaviors from the organic SBDC2- anion expectably emerged during the 2nd scan (Figure 2b), and the reversible cathodic and anodic peaks stabilized at ~0.55 and ~1.12 V, respectively. Notably, the reduction potentials (~0.35 and ~0.55 V) for K2BPDC and K2SBDC were significantly higher than the potassiation potentials (