Biomacromolecules 2006, 7, 1393-1398

1393

Articles Patterned Protein Films on Poly(lipid) Bilayers by Microcontact Printing Eric E. Ross, James R. Joubert, Ronald J. Wysocki, Jr., Ken Nebesny, Tony Spratt, David F. O’Brien, and S. Scott Saavedra* University of Arizona, Department of Chemistry, Tucson Arizona 85721 Received September 28, 2005; Revised Manuscript Received January 24, 2006

The use of polymerized lipid bilayers as substrates for microcontact printing (µCP) of protein films was investigated. We have previously shown that vesicle fusion of bis-SorbPC, a dienoate lipid, on glass and silica substrates, followed by redox-initiated radical polymerization, produces a planar supported lipid bilayer (PSLB) that is ultrastable1a [Ross, E. E.; Rozanski, L. J.; Spratt, T.; Liu, S.; O’Brien, D. F.; Saavedra, S. S. Langmuir 2003, 19, 1752] and highly resistant to nonspecific adsorption of dissolved proteins [Ross, E. E.; Spratt, T.; Liu, S.; Rozanski, L. J.; O’Brien, D. F.; Saavedra, S. S. Langmuir 2003, 19, 1766].1b Here we demonstrate that µCP of bovine serum albumin (BSA) onto a dried poly(bis-SorbPC) PSLB from a poly(dimethylsiloxane) (PDMS) stamp produces a layer of strongly adsorbed protein, comparable in surface coverage to films printed on glass surfaces. Immobilization of proteins on poly(PSLB)s has potential applications in biosensing, and this work shows that direct µCP of proteins is a technically simple approach to create immobilized monolayers, as well as multilayers of different proteins.

Introduction Recently we reported development of ultrathin (50 mL from a direct stream). Oxidized stamps were created by placing hydrophobic (as-cast) PDMS stamps in a plasma cleaner (Harrick model PDC-3XG) at 30 W for 1 min (slight air bleed, although this was not critical), followed by rinsing with deionized water and drying with a nitrogen stream. µCP. Stamps used in protein inking and transfer experiments were incubated for 10 min with 1 mg/mL solution of protein, either bovine serum albumin (BSA, Sigma) or rhodamine-labeled BSA (Sigma) in 10 mM, pH 7.4 phosphate buffer (hereafter referred to as PBS). Stamps were then rinsed (approximately 100 mL from a directed stream) with buffer and then DI water before being dried briefly in a nitrogen stream and used immediately. Applying pressure by hand, stamps were brought into contact with poly(bis-SorbPC) films or bare substrates (glass slide or oxidized silicon wafer) so that conformal contact was made either

in air or under water for 5 s. After stamping, substrates were rinsed with water and dried with nitrogen before analysis. Fluorescence Microscopy. A Nikon Diaphot inverted epifluorescence microscope was used to collect fluorescence images of patterned protein films and substrates. Images were acquired using a liquidnitrogen-cooled CCD camera and processed using the background fluorescence intensity outside of the illuminated area for normalization. An average of three line scans from fluorescence images was used to compare fluorescence intensities from different surfaces. Atomic Force Microscopy. AFM was performed in tapping mode with a NanoScope III (Veeco). Forces between tip and sample were minimized as described in ref 1a. X-ray Photoelectron Spectroscopy. A Kratos Axis-Ultra X-ray photoelectron spectrometer was used with a monochromatic Al KR source at 1486.6 eV and a takeoff angle of 20 degrees. Peaks were fit using Kratos Vision2 software. An electron-emitting filament was used to reduce sample charging, and all spectra were corrected for charging effects by adjusting the C1s peak to 284.6 eV.

Results and Discussion Characterization of BSA Deposited by µCP on Poly(bisSorbPC). BSA adsorbs readily from solution to hydrophobic surfaces,11 including PDMS, and µCP of BSA from PDMS to oxide surfaces has been previously reported.9b Here dried poly(bis-SorbPC) bilayers were contacted with PDMS stamps inked with BSA, rinsed with buffer, and examined for evidence of protein transfer. A representative AFM image of BSA printed on a poly(bisSorbPC) PSLB in air is shown in Figure 1. Transfer occurred uniformly in the printed regions; a continuous layer of protein approximately 1.5-3 nm thick is observed, consisting of parallel lines approximately 12 µm wide separated by 15 µm gaps. The dimensions of the features correspond well to

Patterned Protein Films on Poly(lipid) Bilayers

Figure 2. AFM image and linescan of a poly(bis-SorbPC) PSLB that was stamped with uninked PDMS. The PDMS stamp had the same features as that used to stamp the PSLB in Figure 1. The image size is 70 µm × 70 µm, and the height scale is 10 nm. The dark line across the image indicates the position of the linescan. No discernible topographical features are observed, showing that the PSLB structure is not altered by stamping with PDMS.

those of the master from which the stamp was cast. The protein layer is sufficiently dense such that individual BSA molecules are not discernible, and no proteins are observed outside the printed region. AFM scans taken over very large areas (greater than 100 µm2) show that the transferred protein films are very uniform with very few defective areas. Previously, Boxer and co-workers have shown that unpolymerized lipid bilayers can be structurally altered by contact with PDMS stamps.5c Thus, the possibility must be considered that during µCP the PSLB is removed (or partially removed) and replaced with a BSA film that is adsorbed directly to the underlying glass substrate (or to the remnants of the PSLB). However, we have previously shown that poly(bis-SorbPC) PSLBs are not structurally altered when sonicated in surfactant solutions or immersed in common organic solvents, demonstrating the extreme chemical stability of these polymer films and suggesting that displacement by BSA during µCP is unlikely.1a The AFM data presented in Figure 2 provides further evidence that PDMS contact does not alter the poly(PSLB) morphology. µCP was performed as before, except that the stamp was not inked with BSA. No changes in bilayer surface topography are apparent, showing that the PSLB structure is not macroscopically altered by µCP. In another experiment (see the Supporting Information), a µCP BSA film on poly(bis-SorbPC) was sonicated in a surfactant solution, which desorbed most of the BSA. AFM imaging showed that after BSA removal, the underlying PSLB was still intact. The amount of BSA deposited by µCP on poly(bis-SorbPC) PSLBs was compared to that on clean glass surfaces using AFM.

Biomacromolecules, Vol. 7, No. 5, 2006 1395

Figure 3. (a) Schematic of an immobilization method in which a film of biotinylated BSA, deposited by µCP on a poly(bis-SorbPC) bilayer, is used to immobilize avidin. The unfilled biotin binding sites on avidin provide a means for subsequent attachment of a soluble biotinylated protein (not shown). Epifluorescence was used to image a poly(bisSorbPC) PSLB (b) and a glass substrate (c) that were printed with biotinylated BSA and then exposed to dissolved rhodamine-labeled avidin for 30 min. The avidin bound to the biotinylated BSA in the printed regions. On glass (c), a high degree of nonspecific adsorption of dissolved avidin to the unprinted regions greatly reduced the contrast between the printed and unprinted regions. The dark area in (c) is a region of the substrate that was scratched to remove adsorbed protein and illustrate the minimal contrast elsewhere. Nonspecific adsorption of dissolved avidin was minimal on the PSLB surface (b), as indicated by the lack of fluorescence emitted from the regions between the lines of printed biotinylated BSA.

The surface coverages appeared to be equivalent (see images in Supporting Information). However, determination of surface coverage by AFM is compromised by tip effects which make the apparent size of small features comparable to those of the AFM tip; thus, this method is not accurate when applied to films of high surface coverage.12 Epifluorescence microscopy was used to perform a more quantitative comparison. The results are listed in Table 1. The surface coverage of rhodamine-labeled BSA printed on poly(bis-SorbPC) PSLBs relative to that printed on glass substrates is approximately 90%, showing that µCP of BSA on these two substrates is of comparable efficiency. This finding is consistent with a study by Tan et al.,10 who showed that the wettabilities of the stamp and the substrate must be significantly different for efficient transfer in protein µCP. The contact angle of water on a poly(bis-SorbPC) bilayer is 32 degrees,1a whereas the surface of as-cast PDMS is very hydrophobic (contact angle of 112°13). Based on the data reported in ref 10, this difference is sufficient to predict that efficient transfer should be observed. When the PDMS stamp was oxidized in a plasma (a process that temporarily renders PDMS highly hydrophilic, with a water contact angle