Perovskite an - ACS Publications - American Chemical Society

Jan 4, 2017 - Key Laboratory of Optoelectronics Information Technology (Tianjin ... Instruments and Optoelectronics Engineering, Tianjin University, T...
0 downloads 0 Views 899KB Size
Subscriber access provided by GAZI UNIV

Letter

Broadband Phototransistor Based on CH3NH3PbI3 Perovskite and PbSe Quantum Dot Heterojunction Yu Yu, Yating Zhang, Zhang Zhang, Haiting Zhang, Xiaoxian Song, Mingxuan Cao, Yongli Che, Haitao Dai, Junbo Yang, Jianlong Wang, Heng Zhang, and Jianquan Yao J. Phys. Chem. Lett., Just Accepted Manuscript • DOI: 10.1021/acs.jpclett.6b02423 • Publication Date (Web): 04 Jan 2017 Downloaded from http://pubs.acs.org on January 4, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry Letters is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Broadband Phototransistor Based on CH3NH3PbI3 Perovskite and PbSe Quantum Dot Heterojunction Yu Yu,† Yating Zhang, *,† Zhang Zhang,† Haiting Zhang,† Xiaoxian Song,† Mingxuan Cao,† Yongli Che,† Haitao Dai,‡ Junbo Yang,§Jianlong Wang,† Heng Zhang,† and Jianquan Yao† †

Key Laboratory of Opto-Electronics Information Technology (Tianjin University),

Ministry of Education, School of Precision Instruments and Opto-Electronics Engineering, Tianjin University, Tianjin 300072, China; ‡

Tianjin Key Laboratory of Low Dimensional Materials Physics and Preparing

Technology, School of Science, Tianjin University Tianjin, 300072 (China); §

Center of Material Science, National University of Defense Technology Changsha

410073, (China).

1 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 21

ABSTRACT: Organic lead halide perovskites have received a huge amount of interest since emergence, because of tremendous potential applications in optoelectronic devices. Here field effect phototransistors (FEpTs) based on CH3NH3PbI3 perovskite / PbSe colloidal quantum dot heterostructure are demonstrated. The high light absorption and optoelectric conversion efficiency, due to the combination of perovskite and quantum dots, maintain the responsivities in a high level, especially at 460 nm up to 1.2 A/W. The phototransistor exhibits bipolar behaviors and the carrier mobilities are determined to be 0.147 cm2V-1s-1 for holes and 0.16 cm2V-1s-1 for electrons. The device has a wide spectral response spectrum ranging from 300 nm to 1500 nm. A short photoresponse time is less than 3 ms due to the assistance of heterojunction on the transfer of photoexcitons. The excellent performances presented in the device especially emphasize CH3NH3PbI3 perovskite-PbSe quantum dot as a promising material for future photoelectronic applications.

TOC Graphic:

2 ACS Paragon Plus Environment

Page 3 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

The broadband photodetectors have recently aroused substantial interests in plenty of fields, such as day and night monitoring, chemical/biological sensing, environmental monitoring, and optical communications

1-4

. Traditionally, broadband

detection spectrum ranges from the ultraviolet (UV)-visible to the near infrared (NIR) wavelength. Commercial photodetectors are fabricated with gallium nitride (GaN), silicon (Si) and indium-gallium-arsenide (InGaAs) for sensing UV, visible and NIR light, respectively

5, 6

. Due to lacking suitable materials with the ability to absorb

incident light over a wide range of wavelengths, the development of broadband photodetectors is restricted. As one type of promising materials for broadband photodetection, organic lead halide perovskites (CH3NH3PbX3, X=Cl, Br, I)

7-12

have been investigated due to its

ability to absorb light over a wide wavelength ranging from UV to visible and their suitable, direct bandgap with large absorption coefficients, as well as long electron-hole diffusion lengths and carrier lifetimes. Furthermore, on the basis of simple and cost-effective considerations, perovskites can be synthesized by a chemical solution-based self-assembly method semiconductors

10, 14-17

13

. Various types of hybrid

combined of perovskite have been investigated as channel

materials. For instance, the broad range of wavelengths (254 ~ 800 nm) detection, fast response (2.5 ns rise/ 30 ns fall based on a 337.1 nm irradiance laser), and device stability were reported through a perovskite photodetector by spin-coating with a Perfluorinated cyclic polymers (CYTOP) film 8. A flexible phototransistor fabricated by the active layer of CH3NH3PbI3-graphene heterojunction achieved a wide 3 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 21

photoresponse of 400 ~ 1000 nm18. Although perovskite photodetectors presented high responsivity, short photoresponse time, the detection wavelength regions are still narrow— only from UV to visible, can’t involve infrared (IR). To expand the wavelength range of operation, efforts should be devoted to design the photodetectors through the combination of perovskite and other materials with wide spectral sensitivity. Exhibiting tunable bandgap from 0.5 to 1.7 eV

19

matching

perovskite’s energy level and high air stability with organic ligands, PbSe colloidal 20-23

quantum dots (CQDs)

have a significant absorption capacity for NIR and

short-wavelength light, which perovskites can’t be access to. Ning et al.

24

implemented the excellent photo-carrier diffusion process in the perovskites, and the bright light can be emitted from infrared-bandgap quantum-tuned materials. An effective and solution-processable perovskite-PbSe phototransistor will exhibit excellent performances

25-28

extending to NIR wavelength due to the combination of

strong absorption efficiency of PbSe quantum dots and long distance carrier transmission in perovskite matrix. As our knowledge, phototransistors based on CH3NH3PbI3 perovskite / PbSe colloidal quantum dots heterostructure have never been reported. In

this

paper,

we

fabricate

CH3NH3PbI3

perovskite-PbSe

QDs

hybrid

phototransistors through solution-processed strategy. Due to the appropriate bandgap and large absorption coefficient, CH3NH3PbI3-PbSe QDs with a wide absorption wavelength from UV to infrared light are desirable for fabricating broadband photodetectors. The CH3NH3PbI3-PbSe phototransistor exhibits wide photodetection 4 ACS Paragon Plus Environment

Page 5 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

region ranging from 300 nm to 1500 nm, high sensitivity (R = 1.2 A/W), high carrier mobility (μn = 0.147 cm2V-1s-1 and μp = 0.16 cm2V-1s-1), a fast response times (rise time: 2.5 ms and fall time: 3 ms), and excellent stability and reproducibility. Therefore,

these

high

performances

indicate

that

solution-based

process

perovskite-PbSe colloidal quantum dots heterostructures have great potential for ultra-broadband photodetection applications, especially in the IR region. The phototransistor architecture was fabricated with the configuration shown in Figure 1a. For the bottom-gate configuration, a silicon wafer (n+ Si) with a 300 nm thick SiO2 layer (capacitance Cox of 11.5 nFcm-2) was used as gate electrode. A perovskite thin film with an active channel was made by two step spin-coating solution (see Supporting Information (SI) for details). Source and drain electrodes were thermally evaporated through a sophisticated shadow mask with the channel length (L = 0.1 mm) and channel width (W = 2.5 mm), respectively. Finally, a spin-coated film of PbSe Quantum dots was covered on the top. The preparation and characterization of PbSe QDs are referred to SI. Figure 1b depicts the cross-sectional scanning electron microscopy (SEM) image of the device with the scale of 500 nm. It described that the thickness of SiO2 is 300 nm, then the perovskite film grown on SiO2 has the average thickness of ~ 75 nm and the thickness of PbSe QDs film spinning on perovskite is ~ 177 nm. It is observed that the interface between CH3NH3PbI3 perovskite and PbSe QDs is clear and no intermediate layer, which is essential to obtain excellent photoelectric properties. Notably, the thickness of active layer is a key parameter. If the layer is too thin (40 nm ~70 nm for our devices) to 5 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

effectively absorb light

29

Page 6 of 21

. Meanwhile, thin perovskite films are prone to produce

pinholes, leading to inhomogeneous conduction in the channel. Furthermore, if the film is too thick (> 80 nm for our devices), and the channel are not efficaciously modulated by the bottom gate. Therefore, we utilized the optimized thickness (~75 nm) of the CH3NH3PbI3 film. The X-ray diffraction (XRD) spectrum of the perovskite film synthesized on a glass substrate is depicted in Figure 1c. From XRD spectrum, four characteristic peaks centered at 14.09°, 28.53°, 31.9°, 43.04°are assigned to

Figure 1. (a) Device schematic diagram. (b) Cross-sectional SEM image of the device with the scale of 500 nm. (c) X-ray diffraction spectrum of the 6 ACS Paragon Plus Environment

Page 7 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

CH3NH3PbI3 film, (inset: the SEM image top-view of perovskite on silicon substrate). (d) Optical absorption spectrum of hybrid including perovskite and PbSe quantum dots on glass substrate. the 110, 220, 310 and 330 planes of a tetragonal perovskite crystal structure with lattice parameter of a=b=8.849 Å, c=12.64 Å, which is consistent with literatures reported

13, 30-33

. Meanwhile, it is obvious that CH3NH3PbI3 exhibits well-defined

cuboid shapes and the surface morphologies are homogenous in the inset of Figure 1c, and few distinct pores exist in the grain boundary benefitting that light penetrates through the whole film 34. The absorption region ranges from visible to near-infrared wavelength, depicted in figure 1d, indicating that this device can be used for broadband spectrum detection. The hybrid shows two absorption peaks —‘547 nm’ and ‘1160 nm’—between 300nm and 1500 nm. For electric measurements, drain and source electrodes (ground connection) were connected with tow output ports of Keithley 2400 forming bias voltage (VDS). The drain source current (IDS) was also measured by Keithley 2400. And the gate electrode was connected with a constant voltage source HP6030A. Based on this system, the photoelectrical measurements were also performed under illumination of 405 nm, 532 nm and 808 nm lasers. Figure 2a describes the I-V characteristics of different gate voltages (0 V, ±1 V, ±2 V, ±3 V, ±4 V, ±5 V) under 808 nm laser with irradiance of 845 mW cm-2 (solid lines) and without irradiation (dashed lines). If VGS and VDS are both negative, the device operates in the hole-enhancement mode, while both are positive, the device operates in the electron-enhancement mode. Specially, at low |VGS| (Off-state), IDS 7 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 21

increases rapidly with the increase of VDS, indicating that a Schottky barrier forms in the device

35, 36

. However, at high |VGS| (ON-state), similar to traditional feild effect

transistors (FETs) with linear-to-saturation current-voltage characteristics, the device exhibits unipolar transport properties. Comparing with the condition with no irradiation, the values of |IDS| become larger. It can be understood that the photo-induced carriers can be generated under the condition of light irradiation. Therefore the enhancements of IDS are ascribed to the increase of the electron and hole concentrations. It can be indicated that the thermionic and tunneling currents dominate the vital role

35

. Figure 2b shows transfer characteristics of a bottom-gate

CH3NH3PbI3 phototransistor. The device exhibits typically ambipolar characteristics, and a “V” shape is particularly presented in the transfer curves, manifesting either electrons or holes transport in the n-type or p-type channels of the device, respectively. The mechanism can be interpreted that owing to the difference of electron potentials, some electrons are transferred from CH3NH3PbI3 to PbSe, resulting in the formation of a built-in-electric field in the surface that points toward PbSe. Accordingly, holes separated from photoexcitons generated in heterojunction tend to reside in the poverskite layer due to the assistance of the built-in electric field. Therefore, the shift toward positive VGS (shown in figure 2b) can be ascribed to the efficient photoexcitons separation and holes transport at the interface

37

. Meanwhile, in the

linear region, the relationship between field-effect mobility and gate voltage can be extracted with the equation of



I DS L , VDS CoxW VGS

(1) 8

ACS Paragon Plus Environment

Page 9 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

where L and W are the length and width of the channel, respectively, Cox is the capacitance per area. Therefore, both the electron and hole mobilities can be calculated as 0.147 cm2V-1s-1 and 0.16 cm2V-1s-1, which are larger one order of magnitude than prior studies in pristine PbSe QDs phototransistor (0.01 and 0.03 cm2V-1s-1) 38, respectively. It is attributed to the ‘quantum-dot-in-perovskite’

24

at the

interface, which PbSe QDs are effectively passivated by perovskite instead of conventional organic ligands (i.e. ethanedithiol, formic acid, hydrazine), providing a superior diffusion length.

Figure 2. Electrical properties of the perovskite phototransistor. (a) Output characteristic (IDS versus VDS at different VGS) under 808 nm laser with irradiance of 845 mW/cm2 (solid lines) and in the darkness (dashed lines). (b) Transfer characteristics (IDS versus VGS) of the device under light condition or not at VDS= -0.5 V, respectively. In order to investigate wide spectral response, the dark currents and photocurrents are measured by varying the wide range of wavelengths under the same irradiation. Photoresponsivity (R) is calculated by

9 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

R

I D S I i ll u I d a r k  , P Ee  S

Page 10 of 21

(2)

where Iillu and Idark represent the drain current under illumination and in the darkness. P, Ee and S are power density, irradiance and the effective channel area, respectively. The photoresponsivity and detectivity with the relationship of wavelength in the device is shown in figure 3a. The device exhibits a broadband photoresponse (300 nm ~ 1500 nm) and is suitable for visible light to near-infrared light photodetection, which is determined by the absorption curve of hybrid film in Figure 1 d. The maximum R is calculated to 1.2 A/W at 300 nm, and other key parameters characterizing photodetector’s performance, such as the detectivity (D*), the noise equivalent power (NEP), the gain (G) can be given as

NEP  A1 2 D and G 

39

12

D  RA1 2 (2eI DS )

,

h R , respectively, where R, A, e, IDS are the responsivity, e

the channel area of the device, the charge of an electron, and the dark current, respectively. Particularly, if maximum photoresponsivity (R) is set to 1.2 A/W at 300 nm, and the detectivity has been obtained and impressive high value of 3.3×107 Jones, indicating that the proposed device is extremely sensitive to incident illumination. The NEP and G of the device (shown in Figure S5) are 1.5×10-11 W/Hz and 4.96, respectively. Meanwhile, the phototransistor exhibits stability and reproducibility in the progress of on-off cycles shown in the inset of Figure 3a. Comparing with different photocurrents excited by different wavelength lights at the same power density, the photocurrents excited by 405 nm light, 532 nm and 808 nm are ~ 5 μA, ~ 2.3 μA, and ~ 1 μA, respectively. It is reasonable since the photocurrent generation needs to match the basic condition, that is, the incident photo energy must 10 ACS Paragon Plus Environment

Page 11 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

be larger than the energy gap. Only these incident photos with enough photon energy can excite electrons from the valance band maximum (VBM) to the conduction band minimum (CBM), generating the photocurrent if the VDS is applied. Therefore, more electrons and photoexcitons can be excited with larger incident photo energy lights in the short wavelength and contribute more to photocurrent. It indicates that electrons must pass through the Schottky barrier to transport. Under the irradiation of larger energy light in the shorter wavelength, Schottky barrier for built-in potential is reduced, leading to a huge enhancement in the density of free carrier, which in turn results in easier carriers transport and tunneling, thus, to greatly enhanced photocurrents. Figure 3b exhibits the photocurrent and responsivity (R) of the device with the relation of irradiance (Ee), in which the photocurrent increases linearly with Ee at low light irradiance, while it deviates below this linearity at higher light irradiation. It is concluded that with larger irradiance more photoexcitons and electrons can be excited, leading to the decrease of built in potential of the Schottky barrier, which have a higher probability to overpass the Schottky barrier, and then linearly enhanced photocurrents are generated during the process of the carriers flow to the external circuit. However, for higher light irradiances, some photoexcitons remained in the trap states

11

of perovskite, thus cannot be converted to the photocurrent, leading to

the saturation of photocurrent. As for R, the R decreases if Ee increases in a reciprocal function of R  a 1  (

Ee n ) , where a and b are constants and n is a logistic fitting b

parameter. Based on the theory 40-42 11 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

R(

e T0 1 ) h Tr 1  ( P )n P0

Page 12 of 21

(3)

where e is the charge of single electron, hν is the single photon energy, T0 is the carrier lifetime, Tr is the carrier transfer time, P0 is the excitation intensity where the surface states are fully filled, and n is a phenomenological fitting parameter. The red solid line in the inset of figure 3b is the best fit to the data obtained by equation (3) from which P0 = 2.42×10-6 W, and n = 0.54 have been deduced.

Figure 3. (a) The photoresponsivity (R) and detectivity (D*) of the device with the relationship of wavelength ranging from 300 nm to 1500 nm at VDS = 2 V and VGS = 0 V. (Inset: Switching behavior of the perovskite phototransistor at the irradiance of 50 mW/cm2 under various illuminations of 405 nm, 532 nm, and 808 nm.) (b) R and photocurrent with the relationship of Ee, and the red solid line accounts for the reciprocal function fitting. Photoresponse speed determining the capability of a photodetector to follow a fast-switching optical signal is another key factor for photodetector. In order to highlight the photoresponse of the device during IR spectrum, initially we exploit 12 ACS Paragon Plus Environment

Page 13 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

pump laser with an illumination wavelength of 808 nm — below the absorption edge of PbSe (shown in figure 1 d). Figure 4a shows drain current response of the device with light irradiance of 845 mW/cm2, exhibiting stable and reproducible photoresponse. The drain current quickly increases rapidly once the light is turned on and then decreases as the light switch is off. It indicates that the increased charge intensity will lower the effective barrier height upon illumination, which allows easier charge tunneling and transportation than that of device in darkness. Figure 4b depicts the time-photocurrent response of the device. The rise and decay times of the photocurrent are ~ 2.5 ms and 3 ms, respectively. Recently, using pristine perovskite, Li et al. reported switching times of phototransistors are ~ 6.5 and 6.0 μs. It is reasonable that the speed is probably confined by the lower charger mobility of the PbSe QDs layer (carrier mobilities ~ 0.03 (hole) cm2V-1s-1 and ~ 0.01 (electron) cm2V-1s-1) and some photo carriers remain trapped in the perovskite channel, leading to the increasement of carrier lifetime

7

. To demonstrate the groundbreaking

improvements obtained by this hybrid, we fabricated another two kinds of phototransistors, with similar method and CH3NH3PbI3 perovskite as the only active layer (Figure S3, Supporting Information) or PbSe quantum dots as the active layer (Figure S4, Supporting Information). To compare with characteristics based on CH3NH3PbI3 perovskite and PbSe QDs alone, several key parameters are list in Table 1.

13 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 21

Figure 4. Photoresponse characteristics of perovskite phototransistor under irradiation with red light (λ=808 nm). (a) Current response of the device with a red light irradiance of 845 mW/cm2. (b) Time dependent photocurrent responses, indicating that a rise time of 2.5 ms and a fall time of 3 ms. Table 1 Comparison in device performance of CH3NH3PbI3 / PbSe hybrid FEpTs with its single counterparts. Device

CH3NH3PbI3 PbSe CH3NH3PbI3 / PbSe

Charge mobility [cm2V-1s-1]

Spectral coverage [nm]

Rise / fall time

0.29 / 0.38

300~730



0.01 / 0.03

300~1500

10.9s / 8.3s

0.147 / 0.16

300~1500

2.5 ms / 3ms

to 808 nm

The working principle of this phototransistor is schematically depicted in Figure 5. Upon light illumination, the photocurrents can be generated under the condition that incident photon energy must be larger than bandgap of perovskite, which is 1.5 eV 43, that is, 826 nm in wavelength. While for PbSe, the bandgap is 0.95 eV, that is, 1.3 μm 14 ACS Paragon Plus Environment

Page 15 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

in wavelength. Only these incident photons with larger energy (hν > 1.5 eV, that is, wavelength < 826 nm) can excite electrons from the valance band maximum (VBM) to the conduction band minimum (CBM) in the perovskite, generating the photocurrent if the drain voltage is applied. Given the CBM of PbSe is lower than that of perovskite, photo-generated electrons can roll down to the CBM of PbSe. However, the VBM of perovskite is larger than that of PbSe, so, the photo-generated holes in PbSe can be energetically transferred to perovskite. Due to the larger hole mobility in perovskite, the holes drift faster in perovskite than that in PbSe, and can be rapidly collected by the electrodes. And the charges transfer at the PbSe / perovskite interface, leading to the formation of depletion layer. And the depletion layer assists in the charge separation

14

. Meanwhile, three occasions need to discuss due to different

energy gaps (Eg) of perovskite and PbSe. If hν is larger than 1.5 eV, shown in figure 5a, electron-hole pairs are generated in perovskite and PbSe films, and the electrons (holes) are transferred to PbSe (perovskite) film, which lowers (raises) the Fermi level of PbSe (perovskite) and reduces the Schottky barriers, resulting in the high photocurrent. While hν is larger than 0.95 eV smaller than 1.5 eV, shown in figure 5b, electron-hole pairs can be excited only in PbSe film. Therefore, the photocurrents become small. And if hν is smaller than 0.95 eV, none electron-hole pairs are generated so the photocurrent approximately equals dark current.

15 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 21

Figure 5. Electronic band structure and working principle of the CH3NH3PbI3-PbSe bilayer phototransistor under the illumination of (a) hν > 1.5 eV and (b) 0.95 eV < hν < 1.5 eV. In summary, broadband phototransistors based on CH3NH3PbI3 perovskite-PbSe colloidal quantum dots heterostructures were manufactured in a cost-effective, solution-processed strategy. The phototransistor exhibits bipolar behaviors and a wide spectral response ranging from 300 nm to 1500 nm. Particularly, the phototransistor is photoresponsive to the UV (405 nm), VIS (532 nm) and NIR (808 nm) irradiations, and presents stability and reproducibility in the progress of ON-OFF cycles. Carrier mobilities of CH3NH3PbI3-PbSe heterojunction photodetector are measured as 0.147 cm2V-1s-1 for holes and 0.16 cm2V-1s-1 for electrons. It is worth mentioning that the fast rise and decay times of the photocurrent are ~ 2.5 ms and 3 ms, respectively. Therefore, these results indicate that solution-based process perovskite-PbSe colloidal quantum dots heterostructures have great potential applications for ultra-broadband photodetection, especially in the IR region.

16 ACS Paragon Plus Environment

Page 17 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

Phototransistor Fabrication: The CH3NH3PbI3 perovskite thin film with an active channel made by two step spin-coating solution (see Supporting Information (SI) for details) was deposited onto a silicon wafer (n+ Si) covered with a 300 nm thick SiO2 layer. As source and drain electrodes, Au was thermally evaporated through a sophisticated shadow mask at a rate of 1 Å s−1 in the pressure of 3.8×10-4 Pa. The detail process of spin-coated film of PbSe QDs was referred to Ref [44]. All the measurements were performed in air at room temperature. ACKNOWLEDGMENTS We thank the National Natural Science Foundation of China (No. 61271066) and the Foundation of Independent Innovation of Tianjin University (No. 0903065043). AUTHOR INFORMATION Corresponding Author *E-mail:[email protected]

Notes The authors declare no competing financial interest. ASSOCIATED CONTENT Supporting Information. The characterizations and synthesis of CH3NH3PbI3 perovskite and PbSe QDs, characteristics of CH3NH3PbI3 perovskite and PbSe QDs phototransistors, and stability of the CH3NH3PbI3 perovskite / PbSe QDs FEpTs. REFERENCES 17 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(1)

(2)

(3) (4)

(5)

(6) (7)

(8)

(9)

(10)

(11)

(12)

(13)

(14)

Page 18 of 21

Hu, X.; Zhang, X.D.; Liang, L.; Bao, J.; Li, S.; Yang, W.L.; Xie, Y. High-Performance Flexible Broadband Photodetector Based on Organolead Halide Perovskite. Adv. Funct. Mater. 2014, 24, 7373-7380. Pawbake, A.S.; Waykar, R.G.; Late, D.J.; Jadkar, S.R. Highly Transparent Wafer-Scale Synthesis of Crystalline Ws2 Nanoparticle Thin Film for Photodetector and Humidity-Sensing Applications. ACS Appl. Mat. Interfaces 2016, 8, 3359-3365. Mueller, T.; Xia, F.N.A.; Avouris, P. Graphene Photodetectors for High-Speed Optical Communications. Nat. Photonics 2010, 4, 297-301. Huo, N.; Yang, S.; Wei, Z.; Li, S.-S.; Xia, J.-B.; Li, J. Photoresponsive and Gas Sensing Field-Effect Transistors Based on Multilayer Ws2 Nanoflakes. Sci. Rep. 2014, 4, 5209. Yuang, R.-H.; Chyi, J.-I.; Lin, W.; Tu, Y.-K. High-Speed Ingaas Metal-Semiconductor-Metal Photodetectors with Improved Responsivity and Process Yield. Opt. Quantum Electron. 1996, 28, 1327-1334. Monroy, E.; Omnès, F.; Calle, F. Wide-Bandgap Semiconductor Ultraviolet Photodetectors. Semicond. Sci. Technol. 2003, 18, R33. Li, F.; Ma, C.; Wang, H.; Hu, W.; Yu, W.; Sheikh, A.D.; Wu, T. Ambipolar Solution-Processed Hybrid Perovskite Phototransistors. Nature Communications 2015, 6, 8238. Guo, Y.; Liu, C.; Tanaka, H.; Nakamura, E. Air-Stable and Solution-Processable Perovskite Photodetectors for Solar-Blind Uv and Visible Light. J. Phys. Chem. Lett. 2015, 6, 535-539. Deng, H.; Yang, X.K.; Dong, D.D.; Li, B.; Yang, D.; Yuan, S.J.; Qiao, K.K.; Cheng, Y.B.; Tang, J.; Song, H.S. Flexible and Semitransparent Organolead Triiodide Perovskite Network Photodetector Arrays with High Stability. Nano Lett. 2015, 15, 7963-7969. He, M.H.; Chen, Y.; Liu, H.; Wang, J.L.; Fang, X.S.; Liang, Z.Q. Chemical Decoration of Ch3nh3pbi3 Perovskites with Graphene Oxides for Photodetector Applications. Chem. Commun. 2015, 51, 9659-9661. Dong, R.; Fang, Y.J.; Chae, J.; Dai, J.; Xiao, Z.G.; Dong, Q.F.; Yuan, Y.B.; Centrone, A.; Zeng, X.C.; Huang, J.S. High-Gain and Low-Driving-Voltage Photodetectors Based on Organolead Triiodide Perovskites. Adv. Mater. 2015, 27, 1912-1918. Spina, M.; Nafradi, B.; Tohati, H.M.; Kamaras, K.; Bonvin, E.; Gaal, R.; Forro, L.; Horvath, E. Ultrasensitive 1d Field-Effect Phototransistors: Ch3nh3pbi3 Nanowire Sensitized Individual Carbon Nanotubes. Nanoscale 2016, 8, 4888-4893. Im, J.H.; Jang, I.H.; Pellet, N.; Gratzel, M.; Park, N.G. Growth of Ch3nh3pbi3 Cuboids with Controlled Size for High-Efficiency Perovskite Solar Cells. Nat. Nanotechnol. 2014, 9, 927-932. Ma, C.; Shi, Y.; Hu, W.; Chiu, M.-H.; Liu, Z.; Bera, A.; Li, F.; Wang, H.; Li, L.-J.; Wu, T. Heterostructured Ws2/Ch3nh3pbi3 Photoconductors with 18 ACS Paragon Plus Environment

Page 19 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(15)

(16)

(17)

(18)

(19)

(20)

(21)

(22)

(23) (24)

(25)

(26)

Suppressed Dark Current and Enhanced Photodetectivity. Adv. Mater. 2016, 28, 3683-3689. Li, D.; Dong, G.F.; Li, W.Z.; Wang, L.D. High Performance Organic-Inorganic Perovskite-Optocoupler Based on Low-Voltage and Fast Response Perovskite Compound Photodetector. Sci. Rep. 2015, 5, 7902. Wang, Y.S.; Zhang, Y.P.; Lu, Y.; Xu, W.D.; Mu, H.R.; Chen, C.Y.; Qiao, H.; Song, J.C.; Li, S.J.; Sun, B.Q., et al. Hybrid Graphene-Perovskite Phototransistors with Ultrahigh Responsivity and Gain. Adv. Opt. Mater. 2015, 3, 1389-1396. Spina, M.; Lehmann, M.; Nafradi, B.; Bernard, L.; Bonvin, E.; Gaal, R.; Magrez, A.; Forro, L.; Horvath, E. Microengineered CH3NH3PbI3 Nanowire/Graphene Phototransistor for Low-Intensity Light Detection at Room Temperature. Small 2015, 11, 4824-4828. Dang, V.Q.; Han, G.-S.; Trung, T.Q.; Duy, L.T.; Jin, Y.-U.; Hwang, B.-U.; Jung, H.-S.; Lee, N.-E. Methylammonium Lead Iodide Perovskite-Graphene Hybrid Channels in Flexible Broadband Phototransistors. Carbon 2016, 105, 353-361. Yang, S.Y.; Zhao, N.; Zhang, L.; Zhong, H.Z.; Liu, R.B.; Zou, B.S. Field-Effect Transistor-Based Solution-Processed Colloidal Quantum Dot Photodetector with Broad Bandwidth into near-Infrared Region. Nanotechnology 2012, 23, 5826-5831. Zhang, D.Y.; Gan, L.; Cao, Y.; Wang, Q.; Qi, L.M.; Guo, X.F. Understanding Charge Transfer at Pbs-Decorated Graphene Surfaces toward a Tunable Photosensor. Adv. Mater. 2012, 24, 2715-2720. Wang, H.W.; Li, Z.X.; Fu, C.J.; Yang, D.; Zhang, L.; Yang, S.Y.; Zou, B.S. Solution-Processed Pbse Colloidal Quantum Dot-Based near-Infrared Photodetector. IEEE Photonics Technol. Lett. 2015, 27, 612-615. Hu, W.J.; Henderson, R.; Zhang, Y.; You, G.J.; Wei, L.; Bai, Y.B.; Wang, J.K.; Xu, J. Near-Infrared Quantum Dot Light Emitting Diodes Employing Electron Transport Nanocrystals in a Layered Architecture. Nanotechnology 2012, 23, 1-6. H. Sargent, E. Infrared Quantum Dots. Adv. Mater. 2005, 17, 515-522. Ning, Z.; Gong, X.; Comin, R.; Walters, G.; Fan, F.; Voznyy, O.; Yassitepe, E.; Buin, A.; Hoogland, S.; Sargent, E.H. Quantum-Dot-in-Perovskite Solids. Nature 2015, 523, 324-328. Dirin, D.N.; Dreyfuss, S.; Bodnarchuk, M.I.; Nedelcu, G.; Papagiorgis, P.; Itskos, G.; Kovalenko, M.V. Lead Halide Perovskites and Other Metal Halide Complexes as Inorganic Capping Ligands for Colloidal Nanocrystals. J. Am. Chem. Soc. 2014, 136, 6550-6553. Haruyama, J.; Sodeyama, K.; Han, L.; Tateyama, Y. Termination Dependence of Tetragonal Ch3nh3pbi3 Surfaces for Perovskite Solar Cells. J. Phys. Chem. Lett. 2014, 5, 2903-2909.

19 ACS Paragon Plus Environment

The Journal of Physical Chemistry Letters

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(27)

(28)

(29) (30)

(31)

(32) (33)

(34)

(35)

(36)

(37)

(38)

(39) (40)

Page 20 of 21

Buin, A.; Pietsch, P.; Xu, J.; Voznyy, O.; Ip, A.H.; Comin, R.; Sargent, E.H. Materials Processing Routes to Trap-Free Halide Perovskites. Nano Lett. 2014, 14, 6281-6286. Chen, Z.; Gu, Z.-G.; Fu, W.-Q.; Wang, F.; Zhang, J. A Confined Fabrication of Perovskite Quantum Dots in Oriented Mof Thin Film. ACS Appl. Mat. Interfaces 2016, 8, 28737-28742. Liu, M.Z.; Johnston, M.B.; Snaith, H.J. Efficient Planar Heterojunction Perovskite Solar Cells by Vapour Deposition. Nature 2013, 501, 395-398. Zhao,Y.X.; Zhu, K. CH3NH3Cl-Assisted One-Step Solution Growth of CH(3)NH(3)Pbl(3): Structure, Charge-Carrier Dynamics, and Photovoltaic Properties of Perovskite Solar Cells. J. Phys. Chem. C 2014, 118, 9412-9418. Baumann, A.; Vath, S.; Rieder, P.; Heiber, M.C.; Tvingstedt, K.; Dyakonov, V. Identification of Trap States in Perovskite Solar Cells. J. Phys. Chem. Lett. 2015, 6, 2350-2354. Park, N.G. Perovskite Solar Cells: An Emerging Photovoltaic Technology. Mater. Today 2015, 18, 65-72. Xie, J.; Liu, Y.; Liu, J.; Lei, L.; Gao, Q.; Li, J.; Yang, S. Study on the Correlations between the Structure and Photoelectric Properties of Ch3nh3pbi3 Perovskite Light-Harvesting Material. J. Power Sources 2015, 285, 349-353. Chen, J.Y.; Bai, Y.L.; Nie, C.H.; Zhao, S.F. Strong Magnetoelectric Effect of Bi4ti3o12/Bi5ti3feo15 Composite Films. J. Alloys Compd. 2016, 663, 480-486. Choi, W.; Cho, M.Y.; Konar, A.; Lee, J.H.; Cha, G.B.; Hong, S.C.; Kim, S.; Kim, J.; Jena, D.; Joo, J., et al. High-Detectivity Multilayer MoS2 Phototransistors with Spectral Response from Ultraviolet to Infrared. Adv. Mater. 2012, 24, 5832-5836. Shaikh, P.A.; Shi, D.; Retamal, J.R.D.; Sheikh, A.D.; Haque, M.A.; Kang, C.-F.; He, J.-H.; Bakr, O.M.; Wu, T. Schottky Junctions on Perovskite Single Crystals: Light-Modulated Dielectric Constant and Self-Biased Photodetection. J. Mater. Chem. C 2016, 4, 8304-8312. Dang, V.Q.; Han, G.S.; Trung, T.Q.; Duy, L.T.; Jin, Y.U.; Hwang, B.U.; Jung, H.S.; Lee, N.E. Methylammonium Lead Iodide Perovskite-Graphene Hybrid Channels in Flexible Broadband Phototransistors. Carbon 2016, 105, 353-361. Liu, Y.; Gibbs, M.; Puthussery, J.; Gaik, S.; Ihly, R.; Hillhouse, H.W.; Law, M. Dependence of Carrier Mobility on Nanocrystal Size and Ligand Length in Pbse Nanocrystal Solids. Nano Lett. 2010, 10, 1960-1969. Li, J.H.; Niu, L.Y.; Zheng, Z.J.; Yan, F. Photosensitive Graphene Transistors. Adv. Mater. 2014, 26, 5239-5273. Guo, W.H.; Xu, S.G.; Wu, Z.F.; Wang, N.; Loy, M.M.T.; Du, S.W. Oxygen-Assisted Charge Transfer between Zno Quantum Dots and Graphene. Small 2013, 9, 3031-3036.

20 ACS Paragon Plus Environment

Page 21 of 21

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry Letters

(41)

(42)

(43) (44)

Dang, V.Q.; Trung, T.Q.; Kim, D.I.; Duy, L.T.; Hwang, B.U.; Lee, D.W.; Kim, B.Y.; Toan, L.D.; Lee, N.E. Ultrahigh Responsivity in Graphene-Zno Nanorod Hybrid Uv Photodetector. Small 2015, 11, 3054-3065. Soci, C.; Zhang, A.; Xiang, B.; Dayeh, S.A.; Aplin, D.P.R.; Park, J.; Bao, X.Y.; Lo, Y.H.; Wang, D. Zno Nanowire Uv Photodetectors with High Internal Gain. Nano Lett. 2007, 7, 1003-1009. Park, N.-G. Perovskite Solar Cells: An Emerging Photovoltaic Technology. Mater. Today 2015, 18, 65-72. Zhang, Y.; Cao, M.; Song, X.; Wang, J.; Che, Y.; Dai, H.; Ding, X.; Zhang, G.; Yao, J. Multiheterojunction Phototransistors Based on Graphene–Pbse Quantum Dot Hybrids. J. Phys. Chem. C 2015, 119, 21739-21743.