pH- and GSH-Sensitive Hyaluronic Acid-MP Conjugate Micelles for

Jul 25, 2018 - File failed to load: https://cdn.mathjax.org/mathjax/contrib/a11y/accessibility-menu.js .... Center for Advanced Pharmaceutics and Drug...
0 downloads 0 Views 3MB Size
Subscriber access provided by UNIV OF DURHAM

Article

pH- and GSH-sensitive hyaluronic acid-MP conjugate micelles for intracellular delivery of doxorubicin to colon cancer cells and cancer stem cells Tilahun Ayane Debele, Lu-Yi Yu, Cheng-Sheng Yang, Yao-An Shen, and Chun-Liang Lo Biomacromolecules, Just Accepted Manuscript • DOI: 10.1021/acs.biomac.8b00856 • Publication Date (Web): 25 Jul 2018 Downloaded from http://pubs.acs.org on July 25, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

pH- and GSH-sensitive hyaluronic acid-MP

2

conjugate micelles for intracellular delivery of

3

doxorubicin to colon cancer cells and cancer stem

4

cells

5

Tilahun Ayane Debele†, Lu-Yi Yu†, Cheng-Sheng Yang†, Yao-An Shen⊥ and Chun-Liang Lo†,∥,

6

‡,*

7

† Department of Biomedical Engineering, National Yang-Ming University, Taipei 112, Taiwan

8

∥Center for Advanced Pharmaceutics and Drug Delivery Research, National Yang-Ming

9

University, Taipei 112, Taiwan

10



11

University, Taipei 112, Taiwan

12

⊥Department of Pathology and Sidney Kimmel Comprehensive Cancer Center, Johns Hopkins

13

Medical Institutions, Baltimore, MD 21205, USA

14

[*] To whom correspondence and reprint requests should be addressed.

15

Prof. C.L. Lo, E-mail: [email protected], Fax: + 886-2-2821-0847

Biomedical Engineering Research and Development Center (BERDC), National Yang-Ming

16

1 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 46

17

Abstract

18

A dual-sensitive polymeric drug conjugate (HA-SS-MP) was synthesized by conjugating

19

hydrophobic 6-mercaptopurine (MP) to thiolated hyaluronic acid (HA) as the carrier and ligand

20

to deliver doxorubicin (Dox) to parental colon cancer and colon cancer stem cells. Due to the

21

amphiphilic nature of HA-SS-MP, it was self-assembled in the aqueous media and Dox was

22

physically encapsulated in the core of the micelles. The particle size and the zeta potential of the

23

micelle were analyzed by dynamic light scattering (DLS), and the morphology of the micelle

24

was investigated using transmission electron microscopy (TEM). Drug release study results

25

revealed more drug release at pH 5.0 in the presence of GSH than that at the physiological pH

26

value. The cytotoxicity of free Dox was slightly greater than that of Dox-loaded HA-SS-MP

27

micelles. In vitro cytotoxicity of HA-SS-MP and Dox-loaded HA-SS-MP micelles was greater

28

for cancer stem cells (HCT116-CSCs) than for parental HCT116 colon cancer cells and L929

29

normal fibroblast cells. The MTT and flow cytometry results confirmed that free HA

30

competitively inhibited Dox-loaded HA-SS-MP uptake. Similarly, flow cytometry result

31

revealed anti-CD44 antibody competitively inhibited cellular uptake of Rhodamine B

32

isothiocyanate conjugated micelles which strengthen the synthesized micelle is up taken via

33

CD44 receptor. Cell cycle analysis revealed that free drugs and Dox-loaded HA-SS-MP arrested

34

parental HCT116 colon cancer cells at the S phase, while cell arrest was observed at the G0G1

35

phase in HCT116-CSCs. In addition, ex vivo biodistribution study showed that Dox-loaded HA-

36

SS-MP micelles were accumulated more in the tumor region than in any other organ.

37

Furthermore, the in vivo results revealed that Dox-loaded HA-SS-MP micelles exhibited more

38

therapeutic efficacy than the free drugs in inhibiting tumor growth in BALB/C nude mice.

39

Overall, the results suggested that the synthesized micelles could be promising as a stimuli 2 ACS Paragon Plus Environment

Page 3 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

40

carrier and ligand for delivering Dox to colon cancer cells and also to eradicate colon cancer

41

stem cells.

42

Keywords: Hyaluronic acid, Dual sensitive micelle, CD44, colon cancer stem cell

43



44

Cancer has become one of the most dreadful public health problems, causing deaths throughout

45

the world.1, 2 Among the various cancers, colon cancer is the third leading cause of cancer-related

46

mortality in men and women worldwide.3 Although there are several treatment strategies, colon

47

cancer is rarely cured completely due to its recurrence properties.4 Several researchers have

48

demonstrated that this is due to cancer stem cells (a small population of cancer cells) that possess

49

self-renewal and differentiation abilities to generate a new tumor population.5 Cancer stem cells

50

(CSCs) are highly resistant to standard conventional chemotherapy due to different cellular

51

processes, including rapid drug efflux, enhanced repair of damaged DNA, overexpression of

52

detoxifying enzymes, and antiapoptotic proteins.6-8 Hence, several researchers have

53

demonstrated that designing specific therapies targeting CSCs can enhance the survival of

54

patients with cancer, primarily those with drug resistance.9,

55

targeting CSCs is the use of nanocarriers that can regulate drug delivery and release the drug

56

more efficiently.11 Furthermore, nanocarriers can effectively inhibit multiple types of CSCs,

57

including colon cancer stem cells, by targeting specific markers (ALDH, CD44, CD90, and

58

CD133) using targeting ligands on the surface of nanocarriers, which can enhance selectivity and

59

internalization of drugs by CSCs.12-14 Thus, it is very essential to design an agent that can

60

promote the killing of both parental cancer cells and CSCs.

Introduction

10

One of the recent strategies

3 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 46

61

In recent years, nano-sized ( 97%), 6-mercaptopurine, doxorubicin (Dox),

109

glutathione (GSH, 99%, Roche), anhydrous dimethyl sulfoxide (DMSO), 1-ethyl-3-(3-

110

dimethylaminopropyl) carbodiimide hydrochloride (EDC), N-hydroxysuccinimide (NHS) and

111

dialysis bag are all purchased from Sigma-Aldrich (St Louis, MO, USA). All other reagents were

112

analytical grade and used without further purification. Water used in all the experiments was

113

purified using an AquaMax-Ultra water purification system (Younglin Co., Anyang, Korea).

114

Synthesis of HA-SS-MP conjugates

115

HA-SS-MP conjugates were prepared in two separate steps. In the first step, thiolated HA were

116

synthesized using L-cysteine by simple modification of our previous methods.33 Briefly, 500 mg

117

of HA (1.32 mmol of carboxyl group) were dissolved in the reagent grade distilled water (20 mL,

118

pH 5.3) and an excess amount of EDC/NHS (2.64 mmol each) were added to activate the

119

carboxyl group of HA and stirred for 6 h at room temperature. Then, 5 mL aqueous solution of

120

L-cysteine (2.64 mmol) was added to form thiolated HA. After 24 h reaction, resulting HA-Cys

121

conjugates were extensively dialyzed against deionized (D.I.) water (MWCO 6-8kDa) for 48 h,

122

within 6 h D.I. exchange, followed by deep freeze and lyophilization. The HA-Cys conjugates

123

(sponge-like products) were stored at 4

124

200 mg of HA-Cys conjugates were dissolved in 25 mL of co-solvents (reagent grade

125

water/DMSO) and three times molar excess of 6-mercaptopurine (MP) (3.96 mmol) was added

126

to form HA-SS-MP. Then, 5 mL of H2O2 (2mM) was added drop wise and the reactants solution

until used for the characterization. On the second step,

6 ACS Paragon Plus Environment

Page 7 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

127

were stirred at room temperature for 24 h. HA-SS-MP prodrug was acquired by extensive

128

dialysis (MWCO 6-8KDa) against DMSO, water/DMSO (1:1, v/v) for 24 h and then D.I. water

129

for the other 48 h followed by deep freezing and lyophilization. 1H-NMR and FTIR were used to

130

confirm thiolated HA and HA-SS-MP formation. In addition, GPC analysis was performed using

131

a shodex OHpack SB-803 column (8mm ID x 300mm L and 9 µm, particle size) to confirm

132

thiolated HA and HA-SS-MP formation. A serious of dextrane polysaccharide (5.2, 11.6, 23.8,

133

48.6 and 148kDa) was used to calculate the molecular weight of polymers. The analysis was

134

carried out using acetonitrile and distilled water (20:80v/v ratio, respectively) as a mobile phase

135

at a flow rate of 1 mL/min.

136

Doxorubicin loading and preparation of HA-SS-MP micelles.

137

Doxorubicin (Dox) loaded HA-SS-MP micelles were prepared using dialysis (solvent exchange)

138

method. Briefly, 20 mg HA-SS-MP, 10mg Dox, and 30µL triethylamine were dissolved in 20

139

mL of DMSO/dH2O. The solution was stirred at room temperature for 4 h and then dialyzed

140

against DMSO for 24 h to remove unloaded Dox and also against D.I water for the other 48 h in

141

order to remove the DMSO and to obtain the Dox-loaded HA-SS-MP micelles. The micellar

142

size, zeta potential, and polydispersity index were determined by DLS measurements using a

143

Malvern Zetasizer Nano S apparatus equipped with a 4.0 mW laser operating at λ = 633 nm and

144

a scattering angle of 90°. All measurements were performed at 25

145

from the average of three measurements. The morphology of micelles was analyzed using

146

transmission electron microscopy (TEM, with a JEOLJEM-2000EX instrument at a voltage of

147

200 kV). Samples were prepared by drop-casting HA-SS-MP and Dox loaded HA-SS-MP

148

solutions onto carbon-coated copper grids and then air-drying at room temperature.

149

Phosphotungstate (PTA) was used as the negative staining via sequential two-droplet methods.

and the data were obtained

7 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 46

150

The critical micelle concentration (CMC) of the micelles was determined by a fluorescent

151

spectroscopic method with pyrene as a fluorescence probe.

152

Determination of drug loading of micelles.

153

To determine the drug loading and encapsulation efficiency, 5mg of the freeze-dried micelles

154

were dispersed in 5 mL of PBS (at pH 5.0 in the presence of 10mM GSH) and shook in a water

155

bath at 37

156

spectroscopy at 480 nm using calibration curve from 0.78125 to 400 µg/mL (0.78125, 1.5625,

157

3.125, 6.25, 12.5, 25, 50, 100, 200 and 400 µg/mL). The percentage of drug loading (DL) and

158

encapsulation efficiency (EE) were calculated by the following equations:

159

DL ( wt %) =

for 6 h to release loaded drugs. The Dox concentration was measured by UV-VIS

weight of Dox in the micelle ×100 weight of the Dox − loaded − micelle

160 161

GSH-Responsiveness of Dox loaded HA-SS-MP micelles

162

The GSH responsive behavior of Dox loaded HA-SS-MP micelles was investigated in the

163

presence of GSH using DLS measurement. In brief, an equal volume of GSH (10mM) was

164

mixed with Dox loaded HA-SS-MP micelles solution at different pH values. Then, the solution

165

was incubated on a shaking table at 37

166

DLS at a different time of intervals and change in the morphology also investigated using TEM.

167

and the size change of the micelles was measured by

In vitro release of Dox and MP from the micelles

168

In vitro release behaviors of Dox and MP were investigated in PBS buffer (100 mM, pH 7.4 and

169

5.0) in the presence and absence of 10 mM GSH solution. Briefly, 2 mL of Dox loaded HA-SS-

170

MP solution was transferred to dialysis tubing (MWCO = 6-8 KDa). The dialysis tubing was

8 ACS Paragon Plus Environment

Page 9 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

171

immersed into 10 mL of PBS buffers (100 mM, pH 7.4 and 5.0) in the presence and absence of

172

10 mM GSH solution and kept on a shaking table at 37 . At predetermined time intervals, 2 mL

173

of external buffer solution was withdrawn and replaced with 2 mL of fresh PBS or PBS with 10

174

mM GSH. The amount of released Dox and MP were determined by UV−VIS spectroscopy at

175

480 nm and HPLC, respectively. The HPLC experiments were conducted on the HPLC, C18 (5

176

µm, 150 mm × 4.6 mm i.d) instruments with UV detection at 325 nm. For 6-MP, the mobile

177

phase was a mixture of acetonitrile and methanol at a volume ratio of 20:80 and flow rate of 1.0

178

mL/min. 20 µL of the sample were injected and the drug was detected at 325 nm.

179

In vitro stability and protein adsorption of Dox loaded HA-SS-MP micelles

180

The in vitro stability and protein adsorption of Dox loaded HA-SS-MP were investigated in PBS

181

and protein solutions.34, 35 Briefly, 2 mL (2 mg/mL) of Dox-loaded HA-SS-MP micelle solution

182

were mixed with equal volume of each solution (i.e. 10% (v/v) FBS, 100 mM PBS at pH 7.4 and

183

1wt% fibrinogen). The suspensions were constantly mixed using a sonicator at 37

184

size was measured using DLS at 0, 6, 24 and 48 h.

and particle

185

In vitro cytotoxicity of thiolated HA, HA-SS-MP, Free Dox, Free MP and Dox loaded

186

HA-SS-MP

187

The in vitro cytotoxicity of thiolated HA, HA-SS-MP, Dox loaded HA-SS-MP, free MP and free

188

Dox were evaluated against parental colon cancer cells (HCT116-PC) and L929 fibroblast

189

normal cells using MTT assay. Briefly, all the cells were seeded at a density of 2.5

190

per well in 96-well plates and incubated for 24 h to allow cell attachment. The cells were then

191

incubated in a concentration gradient at 37

192

concentration of: 500, 250, 125, 62.5 and 31.25 µg/mL for each), free Dox and free MP (at Dox

193

and MP concentration of 25, 12.5, 6.25, 3.125 and 1.5625µg/mL) and Dox-loaded HA-SS-MP

104 cells

with thiolated HA and HA-SS-MP (at

9 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 46

194

(at Dox concentration of 25, 12.5, 6.25, 3.125 and 1.5625µg/mL for each). After 48 h incubation,

195

the cells were washed with PBS and new medium were added with 20 µl MTT (5 mg/m1) and

196

further incubated for 4 h. The medium in each well was removed and 100 µl DMSO was added

197

to dissolve the internalized purple formazan crystals. The absorbance was measured at the test

198

wavelength (570 nm) and reference wavelength (633 nm) using an enzyme-linked

199

immunosorbent assay (ELISA) reader (Power Wave XS, BioTek, Winooski, VT). Similarly Dox

200

loaded HA-SS-MP cytotoxicity was investigated for cancer stem cells (HCT116-CSCs). The

201

relative cell viability (%) was calculated using the following equation: absorbance of test cells − absorbance of reference ×100 absorbance of controlled cells − absorbance of reference

202

Cell viability (%) =

203

Cellular uptake and competitive inhibition study

204

Parental HCT116 cells and HCT116-CSCs were grown in McCoy’s 5A and DMEM modified

205

medium, respectively, at 37

206

were seeded and grown in a six well plate at a density of 4 × 104 cells/well and incubated at 37

207

under 5% CO2 for 24 h. Cellular uptake competitive inhibition of Dox loaded HA-SS-MP and

208

HA-SS-MP-Rhodamine B isothiocyanate were investigated using flow cytometry after

209

incubating for 1 h at 37

210

respectively. Fluorescence histograms were recorded with a BD FACS Calibur flow cytometer

211

(Becton Dickinson, USA) and analyzed using Cell Quest software.

212

and 5% CO2 according to reported protocol. Briefly, the cells

in the presence and absence of free HA and anti-CD44 antibody

Cell cycle analysis

213

Parental cancer cells and cancer stem cells were treated with HA-SS-MP (500µg/mL), free MP,

214

free Dox and Dox-MP (at the Dox and MP concentrations of 20 and 2 µg/ml, respectively) and

10 ACS Paragon Plus Environment

Page 11 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

215

Dox loaded HA-SS-MP micelles (at Dox concentration of 20µg/mL) for cell cycle analysis.

216

Briefly, cells (1104 cells/well) were seeded on 6-well plates and co-cultured with HA-SS-MP,

217

free MP, free Dox, Dox-MP and Dox loaded HA-SS-MP for 24 h. After incubation, cells were

218

washed three times by PBS, collected by trypsinization, fixed on iced ethanol for 24 h and then

219

centrifuged at 1000 rpm for 5 min to separate suspension and cell pellets. The cell pellets were

220

finely washed by PBS and stained by PI/Triton X-100/ RNAase solution for 30 min at 37

221

FACS Calibur flow cytometer and ModFit LT software were applied for cell cycle analysis.

222

. BD

In vivo biodistribution study

223

Female BALB/C nude mice (6 - 8 weeks of age, 20 g) were obtained from National Yang-Ming

224

University, and kept in filter-topped cages with standard rodent chow and water available ad

225

libitum, with a 12 h light/dark cycle. The experiment protocol was approved by the ethical

226

committee of animal experiment of National Yang-Ming University. Briefly, 2.5 × 106 HCT116

227

colon cancer cells were subcutaneous seeded by inoculation in the front armpit of BALB/C nude

228

mice. After 4 weak of tumor growth (> 500 mm3), Rhodamine B isothiocyanate conjugated Dox-

229

HA-SS-MP (100 µL) was intravenously (i.v.) injected into the tail vein of tumor bearing

230

BALB/C nude mice. The ex vivo fluorescent scans were performed by scarifying mice after 18 h

231

of post-injection using the IVIS imaging system series 50 with an excitation band filter at 563

232

nm and an emission at 581 nm.

233

Ex vivo anti-tumor efficacy study

234

Similar to the above protocols, after 3 weeks of tumor growth (~200 mm3), Dox-loaded HA-SS-

235

MP or free drugs (Dox + MP) were injected via the lateral tail vein at a dose of 5 mg/kg (for each

236

Dox and MP) every 7 days for a total of 3 injections. Vernier caliper was used to measure the

237

tumor sizes every 2 days and volume was measured using the formula: V = L × W ×W × 0.5, 11 ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 46

238

wherein L and W represent the tumor dimension at the longest and widest point, respectively.

239

Relative tumor volumes were calculated as V/V0 (V0-volume when the treatment was initiated).

240

In addition, relative body weights percent were calculated as W/W0×100 (W0-body weight when

241

the treatment was initiated).

242

Statistical analysis

243

Data are represented as the mean ± standard deviation. All results are representative of at least

244

three sets of independent experiments with samples performed in duplicate or triplicate in each

245

experiment. The significances of the differences were determined using Student's t-test, one

246

tailed, for each paired experiment. *p-value < 0.05 was considered statistically significant in all

247

cases. *p< 0.05, ** p< 0.01, *** p< 0.001.

248

249

12 ACS Paragon Plus Environment

Page 13 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

250

 Results and discussion

251

Synthesis and characterization of HA-SS-MP conjugates

252

Today, smart nanocarrier systems have been synthesized for targeted cancer therapy to overcome

253

the adverse effects of drugs on normal cells and to enhance its therapeutic efficacy in the region

254

of interest. In this study, HA-based dual-sensitive polymeric drug conjugates were designed and

255

synthesized with the properties of both targeting and drug delivery against colon cancer cells and

256

cancer stem cells. The HA shell permits a dual function, both as a ligand (i.e., targeting CD44 as

257

a ligand to enhance receptor-mediated endocytosis to internalize nanoparticles) and allowing the

258

conjugation of L-Cys via amide linkage as a spacer to conjugate the hydrophobic MP to form the

259

polymer–drug conjugate. The synthesized HA-SS-MP forms a micelle by a solvent exchange

260

method due to its amphiphilic nature, which in turn enables the encapsulation of Dox anticancer

261

drugs in its hydrophobic core. The micelles can respond in the cancer cell cytoplasm due to

262

excess GSH levels. Similarly, a micelle can respond to a low pH value due to the pKa value of

263

the conjugated MP to thiolated HA. Hence, during disulfide cleavage that occurs after the cell

264

internalization of the micelles into endosomes, Dox and MP are released. As shown in Scheme

265

1, the activated HA carboxyl groups were covalently coupled with the amine groups of L-Cys

266

through the amide linkage to form thiolated HA based on the EDC/NHS chemical approach.

267

Then, the HA-SS-MP conjugates were synthesized via the disulfide linkage between thiolated

268

HA and 6-MP in the presence of H2O2. The synthesis of HA-SS-MP conjugates was confirmed

269

via 1H-NMR (Figure 1), FTIR (Figures S1a and S1b) spectra, and GPC (Figure S2). The 1H-

270

NMR spectrum (Figure 1) demonstrated the presence of both HA and L-Cys, which indicated

271

the successful formation of thiolated HA. The

272

monosaccharide units of HA (H-1 from

1

H-NMR peaks of the major repeating

D-glucuronic

acid and H-1 from N-acetyl-D13

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 46

273

glucosamine) were found at 4.35 and 4.55 ppm, respectively. The other protons of HA

274

disaccharide units (H-2, H-3, H-4, H-5, and H-6) were found at approximately 3.2–3.9 ppm.36

275

Furthermore, the proton signal of the acetyl groups of HA was found at 1.9 ppm. After thiolation

276

with L-Cys, the new 1H-NMR spectrum was observed at 2.8–3.08 ppm in the HA–Cys conjugate.

277

The degree of thiolation was determined by considering the ratio of the integral of the HA

278

methyl proton peak (at ~1.9 ppm) to that of the protons of L-Cys (at ~2.85 ppm). The degree of

279

thiolation was calculated as 95.52%. Similarly, the 1H-NMR spectrum of HA-SS-MP showed the

280

successful conjugation of MP to thiolated HA via a disulfide bond. The 1H-NMR spectrum of

281

HA-SS-MP showed signals at 8.3–8.41 ppm, which could be assigned to the MP moiety. The

282

degree of substitution was approximately 13.33%, as calculated by comparing the integrals of

283

signals at 7.3–7.41 ppm for MP and 2.85 ppm for methylene protons of L-Cys. Moreover, the

284

degree of substitution was confirmed by UV-VIS measurement (about 12%) after excess GSH

285

treatment at 333 nm, which was almost similar to the 1H-NMR results. Similar to previous

286

reports, the percentage of MP conjugation with thiolated HA was low, which is due to the low

287

reactivity and the low thiol content of MP.29, 37 The chemical structures of the thiolated HA and

288

HA-SS-MP were further confirmed using FTIR (Figures S1a and S1b). All major characteristic

289

peaks of HA–Cys and HA-SS-MP were observed within the range of 3600–500 cm−1. Several

290

major peaks were observed at 3325 cm−1 (HA hydroxyl stretching), 2883–2915 cm−1 (C-H

291

stretching), 1620 cm−1 (amide carbonyl, C=O), 1549 cm−1 (amide, N-H), 1350–1400 cm−1

292

(aromatic, C-N and C=C stretching of MP), and 1027 cm−1 (C-H bending), all of which

293

confirmed the formation of thiolated HA and HA-SS-MP conjugates. In addition, the synthesis

294

of HA–Cys and HA-SS-MP conjugates was further confirmed by GPC analysis. The result

295

(Figure S2) revealed that the retention times of HA, HA–Cys, and HA-SS-MP conjugates were

14 ACS Paragon Plus Environment

Page 15 of 46 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

296

5.69, 5.14, and 4.92 min, respectively. The decrement in the retention time after the formation of

297

the HA conjugates confirmed the successful formation of thiolated HA and HA-SS-MP,

298

supporting the NMR and FT-IR results.

299

Preparation and characterization of HA-SS-MP micelles

300

Due to their amphiphilic nature, the HA-SS-MP conjugates could self-assemble into micelles in

301

an aqueous solution. The micellization behavior of HA-SS-MP was confirmed by measuring the

302

CMC value using pyrene as a fluorescent probe. The CMC value of the amphiphilic HA-SS-MP

303

conjugates was determined using the excitation intensity ratio of I334/I338 vs a prodrug

304

concentration (Log C). As the concentration of HA-SS-MP increased and reached the CMC

305

value, the hydrophobic pyrene molecules were preferentially solubilized in the core of the

306

micelles, by which the intensity ratio decreased. As shown in Figure S3a, the CMC value of the

307

amphiphilic HA-SS-MP conjugates was determined to be