Photochemistry of Hydrochar: Reactive Oxygen Species Generation

Sep 11, 2017 - In this study, we systematically investigate the photochemistry of hydrochar and check its effects on the sulfadimidine degradation. Di...
1 downloads 18 Views 3MB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Photochemistry of Hydrochar: Reactive Oxygen Species Generation and Sulfadimidine Degradation Na Chen, Yahui Huang, Xiaojing Hou, Zhihui Ai, and Lizhi Zhang Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.7b02740 • Publication Date (Web): 11 Sep 2017 Downloaded from http://pubs.acs.org on September 11, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 28

Environmental Science & Technology

1

Photochemistry of Hydrochar: Reactive Oxygen Species

2

Generation and Sulfadimidine Degradation

3

Na Chen, Yahui Huang, Xiaojing Hou, Zhihui Ai, and Lizhi Zhang*

4

Key Laboratory of Pesticide & Chemical Biology of Ministry of Education, Institute of

5

Environmental & Applied Chemistry, College of Chemistry, Central China Normal University,

6

Wuhan 430079, People’s Republic of China

7

* To whom correspondence should be addressed. E-mail: [email protected].

8

Phone/Fax: +86-27-6786 7535

9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24

1 ACS Paragon Plus Environment

Environmental Science & Technology

Page 2 of 28

25

ABSTRACT Biochar, mainly including pyrochar produced via pyrolysis of biomass at moderate

26

temperatures of 350−700 oC and hydrochar formed by hydrothermal carbonization in a range of

27

150-350 oC, have received increasing attention because of their significant environmental impacts. It

28

is known that pyrochar can generate reactive oxygen species even in the dark owing to the presence

29

of persistent free radicals, but hydrochar is far less studied. In this study, we systematically

30

investigate the photochemistry of hydrochar and check its effects on the sulfadimidine degradation.

31

Different from pyrochar derived from the same biomass, hydrochar could generate much more H2O2

32

and •OH under daylight irradiation, which could enhance the sulfadimidine degradation rate by 6

33

times than in the dark. Raman spectroscopy, Fourier transform infrared spectroscopy, electron

34

paramagnetic resonance, and X-ray photoelectron spectroscopy were employed to elucidate this

35

interesting phenomenon. Characterization results revealed that the higher reactive oxygen species

36

generation ability of hydrochar under solar light irradiation was attributed to its abundant

37

photoactive surface oxygenated functional groups. This study clarifies the differences of pyrochar

38

and hydrochar on organic pollutants degradation, and also sheds light on environmental effects of

39

hydrochar.

40 41

Keywords: Hydrochar; Photochemistry; Reactive oxygen species; Sulfadimidine; Oxygenated

42

functional groups

43

Introduction

44

Biochar, as one of the refractory carbon materials, has received increasing attention because of their

45

significant environmental impacts and outstanding agricultural application potential.1-3 For instance,

46

the utilization of biochar may increase carbon storage in soil, mitigate soil nitrous oxide emissions,

47

and raise agricultural productivity.4-8 Furthermore, biochar is regarded as a “super sorbent” because 2 ACS Paragon Plus Environment

Page 3 of 28

Environmental Science & Technology

48

of its high specific surface areas and unique surface chemistry properties (e.g., enriched

49

O-containing groups and highly electronically polarized graphitized carbon surfaces), being used to

50

immobilize toxic heavy metal ions and adsorb persistent pollutants, and thus promising for the

51

contaminated soil and groundwater remediation.9-12 Generally, pyrolysis and hydrothermal carbonization can be used to convert biomass into biochar.4,

52 53

13

54

(pyrochar) in a reactor at moderate temperatures (e.g., 350−700 oC) with limited oxygen.13 Pyrochar

55

has been intensively studied as a sorbent to remove heavy metal ions (e.g., Cu(II) and Pb(II)) and

56

persistent organic contaminants (e.g., polycyclic aromatic hydrocarbons and polychlorinated

57

biphenyls).14-19 Recently, some new properties of pyrochar were explored. For instance, Zhou’s group

58

found that pyrochar could catalyze hydrogen peroxide or persulfate to produce reactive oxygen

59

species (ROS) for the phenolic compounds degradation, which was ascribed to the presence of

60

persistent free radicals (PFRs) generated during the pyrolysis of biomass.20 Meanwhile, Qu and his

61

co-workers reported that dissolved fractions of black carbon released from pyrochar could directly

62

generate singlet oxygen (1O2) and superoxide (O2-) under sunlight irradiation.21 In contrast, little

63

information is available on another kind of biochar produced via hydrothermal carbonization (HTC).

64

HTC is often used to mimic the natural coal formation under geothermal conditions,22 and becomes

65

a novel thermal chemical technique for converting the wet biomass to solid carbonaceous materials

66

(hydrochar) at self-generated pressure and relatively lower temperature with using water as an

67

environmental friendly reaction medium.23 In comparison with pyrochar, hydrochar is far less studied.

68

Recently, Yu’s group reported that the photoactivity of hydrochar could be improved with iodine

69

doping and explained this phenomenon with the semiconductor photocatalysis mechanism.24

70

However, the photochemical environmental effects of hydrochar on organic pollutants degradation

71

still remain mysterious, and its potential in environmental remediation needs to be explored. 3

Pyrolysis is a traditional process to thermally decompose biomass into carbon-rich solid product

ACS Paragon Plus Environment

Environmental Science & Technology 72

Meanwhile, HTC process is quite dissimilar from pyrolysis, which might result in the chemical

73

structures and properties of hydrochar different from those of pyrochar.4 For example, pyrochar with

74

higher stability in soil exhibits a higher potential for carbon sequestration than hydrochar, while

75

hydrochar may act as a mid-term fertilizer by slowing the release of plant-available nutrient to soils.25

76

Sun and co-workers found that hydrochar could adsorb more bisphenol A, 17a-ethinyl estradiol, and

77

phenanthrene than pyrochar.26 In despite of these advances, we still lack a systematic comparison

78

between hydrochar and pyrochar derived from the same biomass on the degradation of organic

79

contaminants in the dark and under solar light irradiation, and thus fail to evaluate their environmental

80

effects and pollutant removal performances.

81

In this study, we prepare hydrochar and pyrochar with two common biomass (fallen-leaves and

82

woodchips), and then compare their performances on the removal of sulfadimidine (SM2) in the dark

83

and under solar light irradiation, aiming to check the differences between hydrochar and pyrochar

84

derived from the same biomass for ROS generation and organic pollutants degradation under different

85

conditions, especially under solar light irradiation.

86 87

Experimental Section

88

Chemicals and Materials. Acetic acid (≥ 99.5%), methanol (≥ 99.5%), ethanol (≥ 99.7%),

89

potassium acid phthalate (≥ 99.8%), benzoic acid (≥ 99.5%), tert-butanol (TBA, ≥ 98.0%) and nitric

90

acid (65%-68%) were all purchased from Sinopharm Chemical Reagent Co., Ltd. China.

91

Sulfadimidine (≥ 98.0%) was purchased from TCI (Shanghai) Development Co., Ltd.

92

P-hydroxyphenylacetic acid (PHPA, ≥ 99.0%), horseradish peroxidase (POD, specific activity

93

of >100 units mg−1), catalase from bovine liver (CAT, specific activity of 2000-5000 units mg−1),

94

superoxide dismutase (SOD, specific activity of ≥ 2500 units mg−1) were purchased from Aladdin

95

Chemistry Co., Ltd. China. Acetonitrile and methanol were of HPLC grade (≥ 99.9%) and obtained 4 ACS Paragon Plus Environment

Page 4 of 28

Page 5 of 28

Environmental Science & Technology

96

from Merck KGaA. All chemicals were used as received without any further purification. Deionized

97

water was used throughout the experiments.

98

Biochar Preparation. Leaves and wood sticks were collected from Platanus acerifolia in the

99

campus of Central China Normal University in October. Before the hydrothermal carbonization and

100

pyrolysis processes, the collected fallen-leaves and woodchips were washed thoroughly to remove

101

the dust and then dried in the air for 24 hours. Then, the dried feedstock was carefully smashed by a

102

pulverizer to pass through a 400-mush sieve. The passed powders were called as “fallen-leaves” and

103

“woodchips”, respectively. For the synthesis of hydrochar, 7 g of biomass powder was added in 50

104

mL of deionized water with magnetic stirring for 2 hours at room temperature. The mixture was

105

subsequently transferred into a 80 mL Teflon−lined stainless steel autoclave and heated in an electric

106

oven at 200 oC for 5 hours. After cooling to room temperature, the solid was collected, washed with

107

deionized water and dried at 60 oC before use. The samples derived from fallen-leaves and

108

woodchips were called as HTC-F and HTC-W, respectively. For the pyrolysis of biomass, the tube

109

furnace was first heated with a temperature increase of 3 oC/min from 20 oC to 450 oC, and then kept

110

at 450 oC for 3 hours. The whole pyrolysis process was continuously purged with high-purity argon.

111

After natural cooling to the room temperature, the products were collected and donated as PC-F

112

(fallen-leaves) and PC-W (woodchips), respectively. All the biochar samples were stored in the dark

113

before use. The preparation procedures were illustrated in supporting information (Scheme S1).

114

Materials Characterizations. The element contents of biochar samples were characterized by

115

element analysis (vario EL cube, Elementar, Germany) (SI Table S1). The morphology of biochar

116

samples was characterized by scanning electron microscopy (SEM, TESCAN MIRA 3, Czech) (SI

117

Figure

118

(Brunauer-Emmett-Teller) nitrogen adsorption isotherms at 77 K (SI Figure S2 and Table S2). The

119

persistent free radicals of biochar powder were detected by an electron paramagnetic resonance 5

S1).

The

specific

surface

area

of

biochar samples was analyzed

ACS Paragon Plus Environment

by BET

Environmental Science & Technology 120

(EPR) spectrometer (Bruker E500, Germany) at room temperature according to previous reports (SI

121

Text S1).20,

122

USA) equipped with a 532 nm laser excitation source. The Fourier transform infrared (FT-IR)

123

spectra of biochar samples were collected by a Nicolet iS50 FT-IR spectrometer (Thermo, USA) in

124

the region of 800-4000 cm-1 with the resolution of 2 cm-1. The C and O bonding states on the surface

125

of biochar samples were obtained by using an X-ray photoelectron spectroscopy (Thermal scientific,

126

ESCALAB 250Xi) (SI Text S2).

27, 28

The biochar samples were characterized by DXR Raman Microscope (Thermo,

127

Photodegradation of Sulfadimidine. Batch experiments were conducted in 100 mL containers

128

with constant magnetic stirring. Briefly, 5 mg of biochar powder were dispersed into 50 mL of SM2

129

solution (250 µg L-1). The initial pH value of the solution was adjusted to 7.2 ± 0.1 at 25 °C by dilute

130

H2SO4 and NaOH aqueous solutions. The dark reaction was performed in the container covered with

131

aluminum foil. For the light reaction, the solutions were irradiated from the top by a daylight lamp (a

132

domestic fluorescent lamp, Foshan Electrical And Lighting Co., Ltd., China) with the output energy

133

of 40 W at a distance of 0.1 m. The irradiation intensity was 3.82 mW/cm2, which was much weaker

134

than that of solar light (66.20 mW/cm2 in May, Wuhan, Hubei Province, China), as detected by the

135

optical power meter (PLS-MW2000, Beijing Perfect Light Co., Ltd., China). The wavelength of

136

daylight lamp was in the range of 300 -750 nm, as measured by a grating spectrometer (WGD-8/8A)

137

(SI Figure S3). The light reaction temperature was maintained at 25 ± 0.1°C with a water circulating

138

system (SI Scheme S2). Control experiments without biochar powder were conducted under the

139

same conditions. 2 mL of removal solutions were sampled and then filtered through 0.22 µm nylon

140

syringe filter for the subsequent analysis. The nylon syringe filter was used to take 10 mL of SM2

141

solution (250 µg L-1) for the adsorption saturation before the degradation solution sampling, which

142

could prevent the further adsorption of SM2 on the nylon syringe filter. 1 mL of sample solution was

143

used to determine the concentration of SM2 by high performance liquid chromatography (HPLC, 6 ACS Paragon Plus Environment

Page 6 of 28

Page 7 of 28

Environmental Science & Technology

144

Ultimate 3000, Thermo), another 1 mL was used to quantify the amount of generated H2O2. For the

145

•OH measurement, we replaced the SM2 solution with a benzoic acid aqueous solution (10 mmol L-1,

146

the initial pH 7.2 ± 0.1 at 25 °C) and conducted the experiment under the same conditions as those of

147

SM2 removal experiments.

148

Analytical Methods. The production of hydrogen peroxide (H2O2) was monitored according to a

149

modified p-hydroxyphenylacetic acid (POHPAA) emission method.29 Fluorescent dimmer (FD), the

150

reaction product of H2O2 with POHPAA fluorescence reagent, emits strong fluorescence at 409 nm

151

when excited at 315 nm. The fluorescence reagent was prepared by dissolving 2.7 mg of

152

para-hydroxyphenylacetic acid and 1 mg of horseradish peroxidase in 10 mL of potassium hydrogen

153

phthalate buffer solution (8.2 g L-1). For the H2O2 concentration detection, 50 µL of fluorescence

154

reagent was added in 1 mL of sample and diluted with 1 mL of deionized water, after the next 10 min

155

of reaction, 1 mL of NaOH (0.1 mol L-1) was added to quench the reaction. The resulting solutions

156

were then measured with the fluorescence spectrophotometer (FL1008M018, Cary, USA).

157

Benzoic acid (BA) was used as a probe molecule to detect the production of hydroxyl radical

158

(•OH). The products of this reaction are p-hydroxybenzoic acid (p-HBA), m-HBA and o-HBA with

159

the ratio of 1.2: 2.3: 1.7.30 The p-HBA could be easily determined by high performance liquid

160

chromatography (HPLC, LC-20AT, Shimadzu) with a SB-C18 reverse phase column. The initial

161

concentration of BA was 10 mM. The injection volume was 10 µL. The mobile phase contained 30%

162

acetonitrile and 70% water. The flow rate was 1 mL min−1 and the detection wavelength was 270 nm

163

(SI Text S3).

164

The concentration of SM2 was monitored by HPLC. The injection volume was 100 µL. The eluent

165

contained 75% of 0.75% (w/w) acetic acid and 25% acetonitrile. The flow rate was 0.8 mL min−1.

166

The UV detector was set as 275 nm and the column temperature was maintained at 35 °C.

167

The SM2 photodegradation intermediates were identified by liquid chromatography-mass 7 ACS Paragon Plus Environment

Environmental Science & Technology 168

spectrometry with tandem mass spectrometry (LC-MS/MS, TSQ Quantum MAX, Thermo, USA).

169

The detailed pre-treatment method and analysis procedures were provided in supporting information

170

(Text S4).

171 172

Results and discussions

173

Sulfadimidine Removal and Reactive Oxygen Species Generation of Hydrochar. We first

174

compared the SM2 removal capacities of hydrochar in the dark and under daylight irradiation. As

175

shown in Figure 1a, only 19.8% of SM2 was removed by HTC-F within 6 days in the dark,

176

suggesting the slight adsorption of SM2 on HTC-F. Interestingly, 72% of SM2 was removed over

177

HTC-F within 6 days under daylight irradiation, indicating that hydrochar was daylight responsive.

178

Control experimental results revealed that the self-clean of SM2 was negligible either in the dark or

179

under daylight irradiation. Both of SM2 removal curves obeyed pseudo-first-order kinetic equation

180

(Figure 1b), while the apparent SM2 removal rate constants under daylight (0.2120 d-1) was almost 6

181

times that (0.0344 d-1) in the dark. We therefore assumed that hydrochar might be excited by

182

daylight to generate ROS for the enhanced SM2 degradation.

183

To verify this assumption, we thus determined the generation of H2O2 and •OH in different

184

systems, and found that the concentration of H2O2 under daylight irradiation increased to a

185

maximum value of 350 µg L−1 in the first three days and then decreased from the fourth day, while

186

the generation of H2O2 was negligible in the dark (Figure 2a). Similar phenomena were also

187

observed for the •OH generation (Figure 2b). The •OH formation quantum yields (Φ•OH) of

188

hydrochar at λ0 = 300 nm was calculated according to a previous report.31 The Φ•OH of hydrochar

189

was calculated to be (6.2 ± 0.22) × 10-5, higher than those (Suwannee River humic acid Φ•OH = (3.01

190

± 0.12) × 10-5, Suwannee River fulvic acid Φ•OH = (4.29 ± 0.14) × 10-5, and Pony lake fulvic acid

191

Φ•OH =(4.56 ± 0.16) × 10-5) of many reported DOM.32 Subsequently, we utilized EPR technique with 8 ACS Paragon Plus Environment

Page 8 of 28

Page 9 of 28

Environmental Science & Technology

192

DMPO as a spin-trapping agent to check the superoxide anion free radical (•O2-) generation in

193

different systems (SI Figure S4a). No signal could be observed in the dark, but a strong four-line

194

EPR spectrum with the relative intensities of 1 : 1 : 1 : 1, a typical pattern of superoxide anion free

195

radical adducted to DMPO, was recorded after 50 min of daylight irradiation. These results

196

confirmed that hydrochar could transfer electron to dissolved oxygen under daylight to form •O2-,

197

which further reacted with H+ to produce H2O2. The final pH of SM2 solution under daylight

198

irradiation increased to 7.9 ± 0.2 at 25 °C, indicative of the H+ consumption during the SM2

199

photodegradation with hydrochar. Under daylight irradiation, H2O2 could easily convert to •OH for

200

the SM2 degradation. We employed the EPR technique with 2, 2, 6, 6-tetramethylpiperidine (TEMP)

201

as a spin trapping agent to check the singlet oxygen (1O2) generation in different systems (SI Figure

202

S5), and did not observe any triplet signals in the dark or after 50 min of daylight irradiation, ruling

203

out that hydrochar could transfer energy to molecular oxygen to form singlet oxygen. To evaluate the

204

contributions of different ROS to the photo-degradation of SM2 on hydrochar, a series of trapping

205

experiments were then carried out with adding different kinds of excess scavengers (TBA for •OH

206

and CAT for H2O2) everyday.33 As shown in Figure 2c, this daily addition of TBA and CAT inhibited

207

80% and 88% of SM2 degradation, respectively. Meanwhile, the degradation rates of SM2 were also

208

reduced by the presence of scavengers (Figure 2d). Therefore, we conclude that molecular oxygen

209

can be activated by hydrochar under daylight irradiation to generate plenty of ROS for the enhanced

210

SM2 degradation.

211

To estimate the ROS generation ability of hydrochar in the natural system, we carried out the SM2

212

removal experiments under natural solar light in the campus of Central China Normal University

213

(8:30-14:30, 11/7/2017). The corresponding solar irradiation intensity was monitored by an optical

214

power meter (SI Figure S6). It was interesting to find that 69% of SM2 could be removed with

215

HTC-F within 6 hours under solar light irradiation (SI Figure S7a), and the concentration of H2O2 9 ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 28

216

reached as high as 433.3 µg L-1 in 6 hours (SI Figure S7b), about 7 times that under daylight lamp.

217

Therefore, hydrochar is very promising for the degradation of organic pollutants under solar light

218

irradiation. Subsequently, we employed LC-MS/MS to detect the intermediates and products to

219

understand the degradation pathway of sulfadimidine (1) in detail. Six degradation intermediates,

220

including 4-aminophenol (2), 4,6-dimethylpyrimidin-2-amine (3), N-(4,6-Dimethyl-2-pyrimidinyl)

221

-4-(hydroxyamino)benzenesulfonamide

222

methylpyrimidine-4-carboxylic acid (6) were identified (SI Figure S8). The mass charge ratios (m/z)

223

of all these detected intermediates of SM2 were consistent with those reported in the literatures,34

224

which were summarized in Table S3 (Supporting Information). On the basis of these intermediates,

225

we proposed a possible degradation pathway of SM2 (SI, Scheme S3).

(4),

2-aminopyrimidine

-4,5,6-triol

(5),

2-amino-6-

226

The Role of Hydrochar on the ROS Generation under Daylight. Recently, it was reported that

227

dissolved black carbon could generate ROS (e. g. 1O2, O2−) under sunlight.21 As aforementioned,

228

hydrochar could induce molecular oxygen activation to generate ROS under daylight irradiation.

229

However, the roles of dissolved and undissolved hydrochar on the ROS generation were unclear,

230

which were disclosed by a series of separating experiments (SI Text S5 and Scheme S4). As shown

231

in Figure 3a, the removal of undissolved hydrochar completely inhibited the degradation of SM2,

232

indicating that undissolved hydrochar was responsible for the photo-degradation of SM2.

233

Subsequently, we fractionated the dissolved hydrochar form water extracts of bulk hydrochar

234

according to the previous reported method, 35 and compared the performances of dissolved and

235

undissolved hydrochar on the SM2 degradation and the ROS generation under daylight irradiation

236

(SI Text S6 and Scheme S5). As expected, the undissolved hydrochar could efficiently degrade SM2

237

within 6 days under daylight irradiation, while the SM2 degradation by the dissolved hydrochar was

238

not observed (Figure 3b), confirming that undissolved hydrochar accounted for the SM2

239

degradation. It was found that undissolved hydrochar could generate H2O2 and •OH under daylight 10 ACS Paragon Plus Environment

Page 11 of 28

Environmental Science & Technology

240

irradiation, but the generation of ROS by dissolved hydrochar was negligible (Figure 3c and Figure

241

3d), confirming that undissolved hydrochar play a dominated role in the SM2 photodegradation and

242

the ROS generation.

243

Comparative Study of Pyrochar and Hydrochar. For comparison, we examined the ability of

244

pyrochar to generate ROS and degrade SM2 in the dark and under daylight irradiation. It was found

245

that PC-F could remove 50% of SM2 within 6 days under daylight irradiation, significantly lower

246

than that (72%) of HTC-F. In the dark, the SM2 removal efficiency of PC-F was 40% within 6 days,

247

which was obviously higher than that (20%) of HTC-F (Figure 4a). All of the removal curves were

248

calculated to obey pseudo-first-order kinetics equations (Figure 4b). The apparent SM2 removal rate

249

constant (0.2120 d-1) of HTC-F was about 2 times that (0.1026 d-1) of PC-F under daylight

250

irradiation. On the contrary, the apparent SM2 dark removal rate constant (0.0848 d-1) of PC-F was

251

calculated to be about 2.5 times that (0.0344 d-1) of HTC-F. The rate constants normalized with

252

specific surface area were also calculated (SI Table S4), which indicated that the SM2 removal

253

efficiency was not only ascribed to their specific surface area. Further separating experiments

254

revealed that the SM2 removal in case of PC-F was also attributed to undissolved pyrochar (SI

255

Figure S11).

256

As the SM2 removal was involved with both adsorption and degradation processes, we first

257

compared the adsorption ability of hydrochar and pyrochar with the oxygen trapping experiments by

258

continuously purging high-purity argon gas with a flow rate of 1.0 L min-1 for 30 min before the

259

reaction and during the whole SM2 removal experiments. As shown in Figure S12, the SM2 removal

260

efficiency of PC-F was 40% within 6 days in the presence of molecular oxygen, while the SM2

261

removal efficiency decreased to 29% in the absence of molecular oxygen, indicating that 11% of

262

SM2 was degraded via molecular oxygen activation induced by PC-F, while 29% of SM2 was

263

removed via the adsorption of PC-F. Differently, the absence of molecular oxygen did not 11 ACS Paragon Plus Environment

Environmental Science & Technology 264

significantly reduce the SM2 removal efficiency of HTC-F, suggesting that 19.8% of SM2 removal

265

was completely attributed to the adsorption of HTC-F. These comparisons revealed that pyrochar

266

had a much stronger adsorbing ability than hydrochar, and also confirmed that pyrochar could

267

generate ROS for the SM2 degradation in the dark. Subsequently, we compared the generation of

268

H2O2 and •OH over HTC-F and PC-F in the dark or under daylight irradiation. As expected, some

269

H2O2 was generated by PC-F in the dark (approximately 60 µg L−1 in the first two days), but not

270

generated by HTC-F under the same conditions (Figure 4c). While, the maximum concentration of

271

H2O2 generated over HTC-F was about 2 times that over PC-F under daylight irradiation (Figure 4c).

272

Similar phenomena were observed in the case of •OH (Figure 4d). We therefore conclude that

273

hydrochar possess the higher ROS generation and SM2 degradation ability than pyrochar under

274

daylight irradiation, but its ROS generation and SM2 degradation abilities were lower than those of

275

pyrochar in the dark.

276

Many types of biomass, such as plant residual, animal waste and sewage sludge, could be used for

277

the biochar preparation.36, 37 Among them, plant residuals (e.g. woodchips, crop straw and corn

278

stover), with hemicellulose, cellulose and lignin as the main components, were commonly used to

279

produce biochar.13, 23 To check whether the type of plant residuals can affect the ROS generation and

280

the SM2 degradation by the resulting hydrochar and pyrochar in the dark and under daylight

281

irradiation, we thus prepared different biochar with other feedstock instead of fallen-leaves for

282

comparison (SI Figure S13). It was found that biochar derived from woodchips was similar with

283

biochar derived from fallen-leaves on the ROS generation and the SM2 degradation under daylight

284

irradiation.

285

Several studies reported that persistent free radicals (PFRs) generated during pyrolysis of biomass

286

could transfer electrons to O2, which further convert to H2O2 and •OH.27, 38, 39 We therefore attributed

287

the traces of ROS generated by pyrochar in the dark to the presence of PFRs, and employed electron 12 ACS Paragon Plus Environment

Page 12 of 28

Page 13 of 28

Environmental Science & Technology

288

paramagnetic resonance (EPR) technique to compare the amounts of PFRs generated by pyrochar

289

and hydrochar. As expected, obvious singlet EPR signals were observed in the two kinds of

290

pyrochars derived from fallen-leaves and woodchips, which were much stronger than those of

291

hydrochar (Figure 5). This comparison confirmed that pyrochar contained much more PFRs than

292

hydrochar. It was known that the type of PFRs highly depended on the g factor of EPR signals. For

293

instance, PFRs with a g factor larger or smaller than 2.0040 were arisen from oxygen-centered such

294

as semiquinone radical anions or carbon-centered radicals such as aromatic radicals, respectively. If

295

carbon-centered and oxygen-centered radicals coexisted, the corresponding g factor was in the range

296

of 2.0030-2.0040.28 We found that the singlet EPR signals generated by pyrochar was similar with

297

that of hydrochar, which could be assigned to oxygen-centered radicals, although the EPR signal

298

intensity of pyrochar was much stronger than that of hydrochar. To verify whether the ROS

299

generation in the dark was dependent on the PFRs, we changed the amount of PFRs in pyrochar by

300

an organic solvent extracting technique (SI Text S7),20 and found that the amount of PFRs in PC-F

301

and PC-W significantly decreased after methanol extraction (SI Figure S14). The H2O2 generation

302

ability of pyrochar after extraction (PC-F-MeOH and PC-W-MeOH) were further examined in the

303

dark. As shown in Figure S15 (Supporting information), the PFRs decrease significantly inhibited

304

the H2O2 generation, confirming that PFRs was responsible for the ROS generation in the dark.

305

It was reported that carboxylated single-walled carbon nanotubes (SWCNT) could more

306

efficiently generate ROS (•O2-, 1O2 and •OH) under solar or UVA light irradiation than pristine

307

SWCNTs.40,

308

(hydrochar and pyrochar) might be related to the amount of oxygenated functional groups (OFGs),

309

especially their surface carboxyl groups. To validate this hypothesis, Raman spectroscopy was first

310

employed to characterize OFGs on the surface of pyrochar and hydrochar.42-44 As shown in Figure 6a,

311

both hydrochar and pyrochar had peaks at D and G bands, indicating the presence of graphitic 13

41

We therefore hypothesized that the photo-generated ROS ability of biochar

ACS Paragon Plus Environment

Environmental Science & Technology

Page 14 of 28

312

carbon in the two kinds of biochar. The value of ID/IG was in the order of hydrochar > pyrochar,

313

reflecting that hydrochar possessed more abundant defects and functional groups than pyrochar.

314

FTIR was then used to gain more information of functional groups on the surface of pyrochar and

315

hydrochar (SI, Table S5 and Figure 6b).42, 44-50 The peak of hydrochar at 3420 cm-1, being mainly

316

ascribed to OH stretching of H-bonded hydroxyl groups, was much stronger than that of pyrochar.

317

Meanwhile, a more clear characteristic peak at 1710 cm-1, which was ascribed to C=O stretching of

318

carboxyl groups, was observed for hydrochar.42, 48 The broad band of hydrochar at 1160-1030 cm-1,

319

representing the C-O stretching of aliphatic, was more distinct than that of pyrochar.42,

320

Furthermore, hydrochar was of more CH3 carbon, as evidenced by its stronger absorbance at

321

2923-2853 cm-1, whereas pyrochar with weak absorbance at this broad band possessed less CH3

322

moieties, consistent with the relatively higher carbonation degree of pyrochar.45, 50 These above

323

results revealed that hydrochar possessed more oxygenated functional groups including hydroxyl

324

groups, ether groups, and carboxyl groups. XPS was further used to characterize OFGs on the

325

surface of different biochar samples. As shown in Figure 6c-f, C 1s spectra could be deconvoluted

326

into three peaks and the deconvolution of O 1s spectra produced two peaks (Table S6 supporting

327

information).3, 47, 51 Table 1 summarizes the relative percentages of surface oxygen element and

328

OFGs (C-O and O-C=O) on pyrochar and hydrochar. For hydrochar, the oxygen contents related to

329

OFGs were calculated to be 37.8% for HTC-F and 31.3% for HTC-W, respectively. These two

330

values were significantly higher than those (18.8% for PC-F and 26.1% for PC-W) of pyrochar.

331

These obvious differences strongly confirmed that hydrochar possessed more surface OFGs.

332

Moreover, the content of O-C=O in hydrochar was relatively higher, suggesting that there was more

333

carboxyl groups in hydrochar, consistent with the FTIR data (Figure 6b).

48, 49

334

To verify whether the ROS generation under daylight irradiation was dependent on the surface

335

OFGs of hydrochar, we changed the concentration of OFGs on the hydrochar surface with the 14 ACS Paragon Plus Environment

Page 15 of 28

Environmental Science & Technology

336

oxidation and thermal treatments, respectively (SI Text S7).52 It was found that the surface OFGs,

337

especially carboxyl groups, significantly increased after the oxidation treatment, while disappeared

338

after thermal treatment (SI, Figure S16a and Figure S17a). We thus examined the H2O2 generation

339

ability of hydrochar after the oxidation and thermal treatments under daylight irradiation (SI, Figure

340

S16b and Figure S17b). As expected, the increase of OFGs concentration efficiently promoted the

341

H2O2 generation, while the removal of OFGs completely inhibited the H2O2 generation, validating

342

that OFGs accounted for the ROS generation under daylight irradiation. Therefore, the better ROS

343

generation and SM2 degradation performances of hydrochar under daylight were attributed to its

344

abundant surface OFGs. On the basis of these results, we proposed a possible mechanism of

345

photochemical ROS generation with hydrochar (SI Text S8 and Scheme S6). Similar with dye

346

sensitized semiconductor photocatalysis systems,53 the OFGs on hydrochar surface may serve as a

347

photosensitizer, and hydrochar particles functioned as an electron shuttle.54,

348

photoexcitation of surface OFGs, the excited electrons transfer from the OFGs to the electron

349

acceptor (e.g. O2) adsorbed on the surface of hydrochar particles, generating different ROS.

350

Environmental application. In this study, we have demonstrated that hydrochar particles in aquatic

351

environment could efficiently generate ROS via oxygen molecular activation for the SM2

352

degradation under daylight irradiation. Moreover, hydrochar with more photoactive surface OFGs

353

could generate much more ROS than pyrochar under daylight irradiation, although pyrochar was

354

able to produce trace of ROS even in the dark owing to the presence of PFRs. The higher

355

photochemical ROS generation ability of hydrochar suggests that it is very promising for

356

environmental remediation under solar light irradiation. Therefore, these findings shed light on

357

photochemical environmental effects of hydrochar, and also play a significant role in estimating the

358

performance of different biochar on environmental remediation.

55

Along with the

359

15 ACS Paragon Plus Environment

Environmental Science & Technology 360

AUTHOR INFORMATION

361

Corresponding Author

362

*Phone/Fax: +86-27-6786 7535; e-mail: [email protected].

363

Notes

364

The authors declare no competing financial interest.

Page 16 of 28

365 366

ACKNOWLEDGEMENTS

367

This work was supported by Natural Science Funds for Distinguished Young Scholars (Grant

368

21425728), National Science Foundation of China (Grant 51472100), the 111 Project (Grant

369

B17019), Self−Determined Research Funds of CCNU from the Colleges’ Basic Research and

370

Operation of MOE (Grant CCNU14Z01001), excellent doctorial dissertation cultivation grant from

371

Central China Normal University (Grant 2016YBZZ037), and the CAS Interdisciplinary Innovation

372

Team of the Chinese Academy of Sciences.

373 374

ASSOCIATED CONTENT

375

Supporting Information

376

Preparation and characterization of biochar samples; EPR and XPS analysis method; quantification

377

of hydroxyl radicals; pre-treatment method and analysis procedure for LC-MS/MS detection;

378

separating, modification and fractionation procedures of biochar samples; possible photochemical

379

mechanism of hydrochar; the diagram of photo-reaction setup; mass spectra and structural formula

380

and m/z values of SM2 and its degradation intermediates; possible sulfadimidine photodegradation

381

pathway; BET surface area of biochar samples; spectrum of daylight lamp; EPR signals of •O2- ,

382

•OH and 1O2; H2O2 generation and SM2 degradation by hydrochar under solar light; O2 trapping

383

experiments; ROS generation and SM2 degradation by biochar derived from woodchips. 16 ACS Paragon Plus Environment

Page 17 of 28

Environmental Science & Technology

384 385

REFERENCE:

386

(1) Cochrane, M. A. Fire science for rainforests. Nature 2003, 421, 913-919.

387

(2) Cheng, C.-H.; Lehmann, J.; Engelhard, M. H. Natural oxidation of black carbon in soils:

388

Changes in molecular form and surface charge along a climosequence. Geochim. Cosmochim. Acta

389

2008, 72, 1598-1610.

390

(3) Amin, F. R.; Huang, Y.; He, Y.; Zhang, R.; Liu, G.; Chen, C. Biochar applications and modern

391

techniques for characterization. Clean Technol. and Environ. Policy 2016, 18, 1457-1473.

392

(4) Kambo, H. S.; Dutta, A. A comparative review of biochar and hydrochar in terms of production,

393

physico-chemical properties and applications. Renew. Sust. Energ. Rev. 2015, 45, 359-378.

394

(5) Cayuela, M. L.; van Zwieten, L.; Singh, B. P.; Jeffery, S.; Roig, A.; Sánchez-Monedero, M. A.

395

Biochar's role in mitigating soil nitrous oxide emissions: A review and meta-analysis. Agric.

396

Ecosyst. Environ. 2014, 191, 5-16.

397

(6) Tang, J.; Zhu, W.; Kookana, R.; Katayama, A. Characteristics of biochar and its application in

398

remediation of contaminated soil. J. Biosci. Bioeng. 2013, 116, 653-659.

399

(7) O.West, T.; Marland, G. A synthesis of carbon sequestration, carbon emissions, and net carbon

400

flux in agriculture: comparing tillage practices in the United States. Agr. Ecosyst. Environ. 2002, 91,

401

217-232.

402

(8) Schmidt, M. W. I.; Noack, A. G. Black carbon in soils and sediments: Analysis, distribution,

403

implications, and current challenges. Global Biogeochem. Cy. 2000, 14, 777-793.

404

(9) Koelmans, A. A.; Jonker, M. T.; Cornelissen, G.; Bucheli, T. D.; Van Noort, P. C.; Gustafsson,

405

O. Black carbon: the reverse of its dark side. Chemosphere 2006, 63, 365-377.

406

(10) Chen, Z.; Chen, B.; Chiou, C. T. Fast and slow rates of naphthalene sorption to biochars

407

produced at different temperatures. Environ. Sci. Technol. 2012, 46, 11104-11111. 17 ACS Paragon Plus Environment

Environmental Science & Technology 408

(11) Han, L.; Ro, K. S.; Sun, K.; Sun, H.; Wang, Z.; Libra, J. A.; Xing, B. New Evidence for High

409

Sorption Capacity of Hydrochar for Hydrophobic Organic Pollutants. Environ. Sci. Technol. 2016,

410

50,13274-13282.

411

(12) Ji, L.; Wan, Y.; Zheng, S.; Zhu, D. Adsorption of tetracycline and sulfamethoxazole on crop

412

residue-derived ashes: implication for the relative importance of black carbon to soil sorption.

413

Environ. Sci. Technol. 2011, 45, 5580-5586.

414

(13) Liu, W. J.; Jiang, H.; Yu, H. Q. Development of Biochar-Based Functional Materials: Toward a

415

Sustainable Platform Carbon Material. Chem. Rev. 2015, 115, 12251-12285.

416

(14) Jonker, M. T. O.; Koelmans, A. A. Sorption of Polycyclic Aromatic Hydrocarbons and

417

Polychlorinated Biphenyls to Soot and Soot-like Materials in the Aqueous Environment:

418

Mechanistic Considerations. Environ. Sci. Technol. 2002, 36, 3725-3734.

419

(15) Luo, L.; Lou, L.; Cui, X.; Wu, B.; Hou, J.; Xun, B.; Xu, X.; Chen, Y. Sorption and desorption of

420

pentachlorophenol to black carbon of three different origins. J. Hazard. Mater. 2011, 185, 639-646.

421

(16) Qiu, Y.; Cheng, H.; Xu, C.; Sheng, G. D. Surface characteristics of crop-residue-derived black

422

carbon and lead(II) adsorption. Water Res. 2008, 42, 567-574.

423

(17) Regmi, P.; Garcia Moscoso, J. L.; Kumar, S.; Cao, X.; Mao, J.; Schafran, G. Removal of copper

424

and cadmium from aqueous solution using switchgrass biochar produced via hydrothermal

425

carbonization process. J. Environ. Manage. 2012, 109, 61-69.

426

(18) Rivera-Utrilla, J.; Gomez-Pacheco, C. V.; Sanchez-Polo, M.; Lopez-Penalver, J. J.;

427

Ocampo-Perez, R. Tetracycline removal from water by adsorption/bioadsorption on activated

428

carbons and sludge-derived adsorbents. J. Environ. Manage. 2013, 131, 16-24.

429

(19) Teixido, M.; Pignatello, J. J.; Beltran, J. L.; Granados, M.; Peccia, J. Speciation of the ionizable

430

antibiotic sulfamethazine on black carbon (biochar). Environ. Sci. Technol. 2011, 45, 10020-10027.

431

(20) Fang, G.; Gao, J.; Liu, C.; Dionysiou, D. D.; Wang, Y.; Zhou, D. Key role of persistent free 18 ACS Paragon Plus Environment

Page 18 of 28

Page 19 of 28

Environmental Science & Technology

432

radicals in hydrogen peroxide activation by biochar: implications to organic contaminant

433

degradation. Environ. Sci. Technol 2014, 48, 1902-1910.

434

(21) Fu, H.; Liu, H.; Mao, J.; Chu, W.; Li, Q.; Alvarez, P. J.; Qu, X.; Zhu, D. Photochemistry of

435

Dissolved Black Carbon Released from Biochar: Reactive Oxygen Species Generation and

436

Phototransformation. Environ. Sci. Technol. 2016, 50, 1218-1226.

437

(22) Reza, M. T.; Andert, J.; Wirth, B.; Busch, D.; Pielert, J.; Lynam, J. G.; Mumme, J.

438

Hydrothermal Carbonization of Biomass for Energy and Crop Production. Appl. Bioenerg. 2014, 1,

439

11-29.

440

(23) Jain, A.; Balasubramanian, R.; Srinivasan, M. P. Hydrothermal conversion of biomass waste to

441

activated carbon with high porosity: A review. Chem. Eng. J. 2016, 283, 789-805.

442

(24) Hu, Z.; Shen, Z.; Yu, J. C., Converting Carbohydrates to Carbon-Based Photocatalysts for

443

Environmental Treatment. Environ. Sci. Technol. 2017, 51, 7076-7083.

444

(25) Gronwald, M.; Vos, C.; Helfrich, M.; Don, A. Stability of pyrochar and hydrochar in

445

agricultural soil - a new field incubation method. Geoderma 2016, 284, 85-92.

446

(26) Sun, K.; Ro, K.; Guo, M.; Novak, J.; Mashayekhi, H.; Xing, B. Sorption of bisphenol A,

447

17alpha-ethinyl estradiol and phenanthrene on thermally and hydrothermally produced biochars.

448

Bioresource Technol. 2011, 102, 5757-5763.

449

(27) Fang, G.; Liu, C.; Gao, J.; Dionysiou, D. D.; Zhou, D. Manipulation of persistent free radicals in

450

biochar to activate persulfate for contaminant degradation. Environ. Sci. Technol. 2015, 49,

451

5645-5653.

452

(28) Liao, S.; Pan, B.; Li, H.; Zhang, D.; Xing, B. Detecting free radicals in biochars and determining

453

their ability to inhibit the germination and growth of corn, wheat and rice seedlings. Environ. Sci.

454

Technol. 2014, 48, 8581-8587.

455

(29) Huang, X. P.; Hou, X. J.; Zhao, J. C.; Zhang, L. Z. Hematite facet confined ferrous ions as high 19 ACS Paragon Plus Environment

Environmental Science & Technology 456

efficient Fenton catalysts to degrade organic contaminants by lowering H2O2 decomposition

457

energetic span. Appl. Catal. B: Environ. 2016, 181, 127-137.

458

(30) Joo, S. H.; Feitz, A. J.; Sedlak, D. L.; Waite, T. D. Quantification of the Oxidizing Capacity of

459

Nanoparticulate Zero-Valent Iron. Environ. Sci. Technol. 2005, 39, 1263-1268.

460

(31)Liu, J.; Liu, Y.; Liu, N.; Han, Y.; Zhang, X.; Huang, H.; Lifshitz, Y.; Lee, S. T.; Zhong, J.;

461

Kang, Z., Water splitting. Metal-free efficient photocatalyst for stable visible water splitting via a

462

two-electron pathway. Science 2015, 347, 970-974.

463

(32) Zhang, D.; Yan, S.; Song, W. Photochemically induced formation of reactive oxygen species

464

(ROS) from effluent organic matter. Environ. Sci. Technol. 2014, 48, 12645-12653.

465

(33) Wang, L.; Cao, M. H.; Ai, Z. H.; Zhang, L. Z. Dramatically enhanced aerobic atrazine

466

degradation with Fe@Fe2O3 core-shell nanowires by tetrapolyphosphate. Environ. Sci. Technol.

467

2014, 48, 3354-3362.

468

(34) Yang, B.; Mao, X.; Pi, L.; Wu, Y.; Ding, H.; Zhang, W., Effect of pH on the adsorption and

469

photocatalytic degradation of sulfadimidine in Vis/g-C3N4 progress. Environ. Sc. Pollut. Res. Int.

470

2017, 24, 8658-8670.

471

(35) Qu, X.; Fu, H.; Mao, J.; Ran, Y.; Zhang, D.; Zhu, D. Chemical and structural properties of

472

dissolved black carbon released from biochars. Carbon 2016, 96, 759-767.

473

(36) Cantrell, K. B.; Hunt, P. G.; Uchimiya, M.; Novak, J. M.; Ro, K. S. Impact of pyrolysis tem

474

perature and manure source on physicochemical characteristics of biochar. Bioresource Technol.

475

2012, 107, 419-428.

476

(37) Park, J.; Lee, Y.; Ryu, C.; Park, Y. K. Slow pyrolysis of rice straw: analysis of products

477

properties, carbon and energy yields. Bioresource Technol. 2014, 155, 63-70.

478

(38) Balakrishna, S.; Lomnicki, S.; McAvey, K. M.; Cole, R. B.; Dellinger, B.; Cormier, S. A.

479

Environmentally persistent free radicals amplify ultrafine particle mediated cellular oxidative stress 20 ACS Paragon Plus Environment

Page 20 of 28

Page 21 of 28

Environmental Science & Technology

480

and cytotoxicity. Part. Fibre Toxicol. 2009, 6, 11-25.

481

(39) Lomnicki, S.; Truong, H.; Vejerano, E.; Dellinger, B. Copper Oxide-Based Model of Persistent

482

Free Radical Formation on Combustion-Derived Particulate Matter. Environ. Sci. Technol. 2008, 42,

483

4982–4988.

484

(40) Chen, C.-Y.; Jafvert, C. T. The role of surface functionalization in the daylight-induced

485

production of reactive oxygen species by single-walled carbon nanotubes in water. Carbon 2011, 49,

486

5099-5106.

487

(41) Qu, X.; Alvarez, P. J.; Li, Q. Photochemical transformation of carboxylated multiwalled carbon

488

nanotubes: role of reactive oxygen species. Environ. Sci. Technol. 2013, 47, 14080-14088.

489

(42) Chia, C. H.; Gong, B.; Joseph, S. D.; Marjo, C. E.; Munroe, P.; Rich, A. M. Imaging of

490

mineral-enriched biochar by FTIR, Raman and SEM–EDX. Vib. Spectrosc. 2012, 62, 248-257.

491

(43) Jorio, A.; Cancado, L. G. Perspectives on Raman spectroscopy of graphene-based systems: from

492

the perfect two-dimensional surface to charcoal. Phys. Chem. Chem. Phys. 2012, 14, 15246-15256.

493

(44) Kim, P.; Johnson, A.; Edmunds, C. W.; Radosevich, M.; Vogt, F.; Rials, T. G.; Labbé, N.

494

Surface Functionality and Carbon Structures in Lignocellulosic-Derived Biochars Produced by Fast

495

Pyrolysis. Energ. Fuel. 2011, 25, 4693-4703.

496

(45) Mukome, F. N.; Zhang, X.; Silva, L. C.; Six, J.; Parikh, S. J. Use of chemical and physical

497

characteristics to investigate trends in biochar feedstocks. J. Agric. Food. Chem. 2013, 61,

498

2196-2204.

499

(46) Odeh, A. O. Oualitative and quantitative ATR-FTIR analysis and its application to coal char of

500

different ranks. J. Fuel Chem. Technol. 2015, 43, 129-137.

501

(47) Qian, L.; Chen, B. Interactions of aluminum with biochars and oxidized biochars: implications

502

for the biochar aging process. J. Agric. Food. Chem. 2014, 62, 373-380.

503

(48) Keiluweit, M.; Nico, P. S.; Johnson, M. G.; Kleber, M. Dynamic Molecular Structure of Plant 21 ACS Paragon Plus Environment

Environmental Science & Technology

Page 22 of 28

504

Biomass-Derived Black Carbon (Biochar). Environ. Sci. Technol. 2010, 44, 1247-1253.

505

(49) Fuertes, A. B.; Arbestain, M. C.; Sevilla, M.; Maciá-Agulló, J. A.; Fiol, S.; López, R.; Smernik,

506

R. J.; Aitkenhead, W. P.; Arce, F.; Macías, F. Chemical and structural properties of carbonaceous

507

products obtained by pyrolysis and hydrothermal carbonisation of corn stover. Aust. J. Soil Res.

508

2010, 48, 618-626.

509

(50) Kang, S.; Li, X.; Fan, J.; Chang, J. Characterization of Hydrochars Produced by Hydrothermal

510

Carbonization of Lignin, Cellulose, d-Xylose, and Wood Meal. Ind. Eng. Chem. Res. 2012, 51,

511

9023-9031.

512

(51) Singh, B.; Fang, Y.; Cowie, B. C. C.; Thomsen, L. NEXAFS and XPS characterisation of

513

carbon functional groups of fresh and aged biochars. Org. Geochem. 2014, 77, 1-10.

514

(52)Cuervo, M. R.; Asedegbega-Nieto, E.; Díaz, E.; Ordóñez, S.; Vega, A.; Dongil, A. B.;

515

Rodríguez-Ramos, I. Modification of the adsorption properties of high surface area graphites by

516

oxygen functional groups. Carbon 2008, 46, 2096-2106.

517

(53)Cho, Y.; Choi, W., Visible light-induced reactions of humic acids on TiO2. J. Photoch. Photobio.

518

A 2002, 148, 129-135.

519

(54)Kappler, A.; Wuestner, M. L.; Ruecker, A.; Harter, J.; Halama, M.; Behrens, S., Biochar as an

520

Electron Shuttle between Bacteria and Fe(III) Minerals. Environ. Sci. Technol. Let. 2014, 1, 339-344.

521

(55)Cayuela, M. L.; van Zwieten, L.; Singh, B. P.; Jeffery, S.; Roig, A.; Sánchez-Monedero, M. A.,

522

Biochar's role in mitigating soil nitrous oxide emissions: A review and meta-analysis. Agr. Ecosyst.

523

Environ. 2014, 191, 5-16.

524 525 526 527

22 ACS Paragon Plus Environment

Page 23 of 28 528

Environmental Science & Technology

Figure Captions

529 530

Figure 1. (a) Time profiles of the SM2 removal under different conditions. (b) Plots of -ln(C/C0)

531

versus time for SM2 removal under different conditions. The initial concentrations of SM2 and

532

HTC-F were 250 µg L−1 and 100 mg L-1, respectively.

533 534

Figure 2. ROS generation in different systems during the SM2 degradation: (a) H2O2 generation; (b)

535

•OH generation. (c) Profiles of SM2 photodegradation with adding different kinds of scavengers 23 ACS Paragon Plus Environment

Environmental Science & Technology

Page 24 of 28

536

(TBA for •OH, CAT for H2O2); (d) SM2 photodegradation rate constant with adding different kinds

537

of scavengers. The initial concentrations of SM2, HTC-F and BA were 250 µg L−1, 100 mg L-1 and

538

10 mM, respectively.

539 540

Figure 3. (a) Time profiles of SM2 degradation in hydrochar separating experiments. The dash line

541

was the boundary of hydrochar before and after separation. (b) Profiles of SM2 photodegradation

542

with dissolved, bulk, rest hydrochar, respectively. ROS generation with different fractions of

543

hydrochar during the SM2 degradation: (c) H2O2 generation; (d) •OH generation. The initial

544

concentrations of SM2 and the three kinds of HTC-F were 250 µg L−1 and 100 mg L-1, respectively.

24 ACS Paragon Plus Environment

Page 25 of 28

Environmental Science & Technology

545 546

Figure 4. (a) Time profiles of the SM2 degradation with hydrochar and pyrochar under different

547

conditions. (b) Plots of -ln(C/C0) versus time for SM2 degradation in different systems. ROS

548

generation in different system during the SM2 degradation: (c) H2O2 generation; (d) •OH generation.

549

The initial concentrations of SM2 and the biochar samples were 250 µg L−1 and 100 mg L-1,

550

respectively.

551 552

Figure 5. EPR signals detected in different biochar samples: (a) hydrochar and pyrochar derived

553

from fallen-leaves; (2) hydrochar and pyrochar derived from woodchips. 25 ACS Paragon Plus Environment

Environmental Science & Technology

Page 26 of 28

554 555

Figure 6. (a) Raman spectra of different biochar samples. (b) FTIR spectra of different biochar

556

sampels. XPS C1s spectra of biochar samples derived from (c) fallen-leaves and (d) woodchips, O1s

557

spectra of biochar samples derived from (e) fallen-leaves and (f) woodchips.

558 559 560

26 ACS Paragon Plus Environment

Page 27 of 28

Environmental Science & Technology

561

Table 1. The relative percentages of surface oxygen element and OFGs (C-O and O-C=O) on

562

pyrochar and hydrochar. C 1s

O 1s O/C (%)

C-C (%)

C-O (%)

O-C=O (%)

C-O (%)

O-C=O (%)

HTC-F

46.7

34.4

18.9

60.4

39.6

37.8

HTC-W

56.8

27.7

15.5

69.9

30.1

31.3

PC-F

75.9

15.7

8.4

85.1

14.9

18.8

PC-W

83.5

11.3

5.2

81.2

18.8

26.1

563 564 565 566 567 568 569 570 571 572 573 574 575 576 577 578 579

27 ACS Paragon Plus Environment

Environmental Science & Technology 580