Polymer Dehalogenation-Enabled Fast Fabrication of N,S-Codoped

Aug 14, 2017 - Doped carbon materials (DCM) with multiple heteroatoms hold broad interest in electrochemical catalysis and energy storage but require ...
0 downloads 0 Views 1MB Size
Subscriber access provided by UNIVERSITY OF ADELAIDE LIBRARIES

Article

Polymer dehalogenation-enabled fast fabrication of N, S-codoped carbon materials for superior supercapacitor and deionization applications Yingna Chang, Guoxin Zhang, Biao Han, Haoyuan Li, Cejun Hu, Yingchun Pang, Zheng Chang, and Xiaoming Sun ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b08181 • Publication Date (Web): 14 Aug 2017 Downloaded from http://pubs.acs.org on August 15, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Polymer dehalogenation-enabled fast fabrication of N, S-codoped carbon materials for superior supercapacitor and deionization applications Yingna Chang,a Guoxin Zhang,a,d,* Biao Han,a Haoyuan Li,a Cejun Hu,b Yingchun Pang,a Zheng Chang,a,* and

Xiaoming Suna,b,c

a. State Key Laboratory of Chemical Resource Engineering, College of Science, Beijing University of Chemical Technology, Beijing, 100029, China. Email: [email protected] b. College of Energy, Beijing University of Chemical Technology, Beijing, 100029, China. c. Beijing Advanced Innovation Centre for Soft Matter Science and Engineering, Beijing University of Chemical Technology, Beijing, 100029, China. d. College of Electrical Engineering and Automation, Shandong University of Science and Technology, Qingdao 266590, China. Email: [email protected]

KEYWORDS.

Dehalogenation;

carbon

materials;

codoping;

supercapacitor;

capacitive deionization

ABSTRACT. Doped carbon materials (DCM) with multiple heteroatoms hold broad interests in electrochemical catalysis and energy storage but require several steps to fabricate, which greatly hinder their practical applications. In this study, a facile 1 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 25

strategy is developed to enable the fast fabrication of multiply doped carbon materials via room-temperature dehalogenation of polyvinyl dichloride (PVDC) promoted by KOH with the presence of different organic dopants. A N, S-codoped carbon material (NS-DCM) is demonstratively synthesized using two dopants (dimethylformamide for N doping and dimethylsulfoxide for S doping). Afterwards, the precursive room-temperature NS-DCM with intentionally overdosed KOH is submitted to inert annealing to obtain large specific surface area and high conductivity. Remarkably, NS-DCM annealed at 600 °C (named as 600-NS-DCM), with 3.0 at.% N and 2.4 at.% S, exhibits a very high specific capacitance of 427 F g-1 at 1.0 A g-1 in acidic electrolyte and also keeps ~60% of capacitance at ultrahigh current density of 100.0 A g-1.

Furthermore,

capacitive

deionization

(CDI)

measurements

reveal that

600-NS-DCM possesses a large desalination capacity of 32.3 mg g-1 (40.0 mg L-1 NaCl), and very good cycling stability. Our strategy of fabricating multiply doped carbon materials can be potentially extended to the synthesis of carbon materials with various combinations of heteroatom doping for broad electrochemical applications.

1. Introduction Doped carbon materials (DCM) have gained tremendous attention due to their broad applications in electrochemical energy conversion1-7 and storage8-14. Because of their low cost and high performance, DCM hold great potentials in practical applications. Meanwhile, their highly controllable surface properties enabled by heteroatom doping and functionalization have brought about nearly unlimited 2 ACS Paragon Plus Environment

Page 3 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

opportunities to continuously enhance their electrochemical performance.15 For instance, a N-doped ordered carbon material developed by Huang et al shows a capacitance as high as 855 F g-1, and consequently, it delivers a very high specific energy of 41.0 Wh kg-1 in aqueous electrolyte, which is highly comparable to these lead-acid batteries.12 As proved by many studies, heteroatom doping has the capability of activating stable carbon lattices, and good cooperative effects towards the activation of carbon matrix can be achieved if doping with multiple heteroatoms.16-18 For instance, nitrogen and sulfur codoped carbon spheres with a specific surface area of only ~400 m2 g-1 exhibit outstanding specific capacitance (295 F g-1 at 0.1 A g-1) and rate capability (247 F g-1 at 10 A g-1).18 However, the synthesis procedures of multiply doped carbon materials (MDCM) still required tedious steps and strict control on byproduct wastes. Therefore, the clean, scalable, and facile production of MDCM with good electrochemical performance is still challengeable.

Herein, we develop a facile strategy for the fast fabrication of MDCM via in situ doping halogenated polymer (such as polyvinyl dichloride, PVDC)-defunctionalizing carbon materials. The synthetic procedure can be done in one step by simply milling the mixture of halogenated polymer, dehalogenation agent, and dopants. As a demonstration, N, S-codoped carbon material (RT-NS-DCM) is synthesized via the dechlorination reaction between PVDC and KOH using two common solvents of dimethylformide and dimethylsulfoxide as N and S sources, respectively. After further annealing to obtain large specific surface area and high conductivity, the resulted 600-NS-DCM achieves heteroatom doping contents of 3.0 at.% N and 2.4 3 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 25

at.% S. Remarkably, it delivers a very high capacitance of 427 F g-1 at 1.0 A g-1, and also supplies 251 F g-1 (~60% of initial capacitance) at ultrahigh current density of 100.0 A g-1. Furthermore, capacitive deionization (CDI) measurements find that 600-NS-DCM achieves an absorption capacity as high as 32.3 mg g-1 in 40.0 mg L-1 NaCl and also can effectively work in concentrated salt solutions.

2. Experimental section

2.1 Materials

Polyvinyldichloride (PVDC) was obtained from Solvay (American company) through

Alibaba.

Other

reagents,

including

dimethylformide

(DMF),

dimethylsulfoxide (DMSO), sodium chloride (NaCl), concentrated sulfuric acid (H2SO4), and potassium hydroxide (KOH) of A.R. grade were all purchased from Beijing Chemical Works without any treatment.

2.2 Preparation of N, S-codoped carbon materials

Typically, for the synthesis of N, S-codoped carbon materials at room temperature, 1.00 g PVDC, 2.00 g KOH together with 1.69 mL DMSO and 10.00 mL DMF were added into a ZrO2 ball mill jar. The mixture was ball milled at 30 Hz for 2 hrs, and then the black slurry was collected and dried at 60 °C for 6 hrs to obtain solid products. The dried products were then purified by water for removing excess KOH and those by-products such as KCl. After further drying, clean codoped carbon materials (designated as RT-NS-DCM) were collected. In order to explore the 4 ACS Paragon Plus Environment

Page 5 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

potentials of DCM in capacitive applications, high temperature annealing of unwashed RT-NS-DCM was performed at 500/600/700 °C in inert atmosphere, followed by washing and drying. The resulted products were named as 500/600/700-NS-DCM, respectively. For comparison, control samples were synthesized following the protocol of 600-NS-DCM but with the absence of either DMF or DMSO, and correspondingly, the resulted control samples were named as 600-N-DCM and 600-S-DCM, respectively.

2.3 Characterizations

Scanning electron microscopy (SEM, Zeiss SUPRA55, with EDX apparatus). High resolution transmission electron microscopy (HRTEM, JEOL JEM-2100). Powder X-ray diffraction (XRD, Shimadzu XRD-6000). Raman spectroscopy (LabRAM ARAMIS, excited with a 532 nm laser). X-ray photoelectron spectroscopy (XPS, Thermo Electron ESCALAB 250). N2 adsorption/desorption isotherms (Quantachrome Autosorb-1CVP, measured at 77 K). The samples were preprocessed in a vacuum at 200 °C for 3 hrs. The desorption branches were used to calculate specific surface areas according to the Brunauer–Emmett–Teller (BET) method and pore size distributions based on the Barrett–Joyner–Halenda (BJH) method. The micropore area was calculated through t-plot of quantity of adsorbed N2 versus multilayer absorption thickness. Thermogravimetry (TG) and differential thermal analysis (DTA) (NETZSCH STA 449F3, heated at 10 °C min-1 up to 800 °C).

2.4 Electrochemical characterizations 5 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 25

Supercapacitor measurements were conducted using an electrochemical workstation (Chenhua CHI 660E) in three-electrode system. Typically, the slurry containing 85.0 wt.% NS-DCM, 10.0 wt.% carbon black, and 5.0 wt.% polytetrafluoroethylene (PTFE, Aldrich; 60 wt.% dispersion in water) binder was cast-coated onto a glassy carbon electrode (1.0 cm in diameter). The electrode was fully dried using a NIR lamp and 80°C oven. The loading mass of working electrode was ~1.0 mg cm-2. The measurements were respectively carried out in three aqueous electrolytes (6.0 M KOH, 1.0 M NaCl, or 1.0 M H2SO4), with Pt as counter electrode and Hg/HgO (or Ag/AgCl) as reference electrode. The gravimetric specific capacitances (Cs, F g-1) were calculated depending on the charge/discharge curves obtained with different current streams as shown in the equation (1):19

Cs =

I × ∆t M ×V

(1)

where I is the current density (A g-1), ∆t is the charging/discharging duration time, M equals to the loading mass of active materials, and V is the potential window (eliminating IR drop). Electrochemical impedance spectroscopy (EIS) was conducted at a 10 mV AC amplitude from 10 mHz to 100 kHz.

Capacitive deionization (CDI) measurements were following the previous paper published by our group.20 For a typical electrode fabrication, 80.0 wt.% NS-DCM, 15.0 wt.% carbon black, and 5.0 wt.% PTFE were fully mixed in ethanol, followed by sonication for 1 hr. Resulted slurry with ~100 mg solids was casted on a graphite sheet (6 cm×7 cm×0.2 cm), and then dried at 80°C overnight to obtain a solid 6 ACS Paragon Plus Environment

Page 7 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

electrode. The loading mass of electrode materials was ~2.4 mg cm-2. CDI measurements were carried out using a home-made CDI set-up consisting of a CDI cell, a peristaltic pump, a conductivity meter and an external power supply, which had been carefully described in our previous publication.20 100.0 mL NaCl aqueous solution circulated in the CDI set-up at a flow rate of 25.0 mL min-1. A series of NaCl concentrations (40, 100, 500 and 1000 mg L-1) and applied voltages (1.2, 1.4 and 1.6 V) were selected to evaluate CDI performance of electrode materials. The NaCl concentrations were calculated from the conductivities in situ collected using a conductivity meter (Leici Type 308F). The desalination capacities (W, mg g-1) were calculated according to the equation (2):20

W=

(C 0 −C ) × V m

(2)

where V is the total solution volume, and m is the total mass of electrode materials. C0 and C are the initial and final NaCl concentrations, respectively. The time-dependent accumulated ion removal rates (U, mg g-1 min-1) were given in the equation (3):20

U=

W t

(3)

where t is the operation time.

3. Results and discussions

Polymer

dehalogenation

is

a

newly

developed

strategy

for

the

time-/cost-effective fabrication of carbon materials, which can ensure the 7 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 25

room-temperature synthesis of carbon materials with high carbon contents.5-6, 21 But the defunctionalization of halogenated polymers such as polyvinyldichloride (PVDC) is hardly done even under high-temperature treatment. As confirmed by TG profile of pure PVDC in Figure S1A, heating PVDC to over 800℃ only results in a weight loss of ~50% while the initial Cl content in PVDC is ~73%, and no obvious defunctionalization of PVDC can be seen (Figure S1B). However, the defunctionalization of PVDC can be rapidly promoted at room temperature using strong alkaline such as KOH.21 Moreover, the previous reports have confirmed that N in DMF solvent could be extracted and efficiently doped into the as-formed carbon materials.21 As far as we know, DMF with amide N is normally stable, but can be decomposed into dimethylamine with secondary amine under strong alkaline promotion.

The

successful

doping

of

N

using

dopant

of

secondary

amine-dimethylamine into carbon lattice suggests that the carbon sites during or after dehalogenation are highly reactive for coupling adjacent atoms.21 Encouraged by the applicable N doping under mild conditions, therefore, we may safely envision plenteous possibilities for the room-temperature fabrication of MDCM that will not be limited by single type of heteroatoms. As demonstration, two common solvents of DMF and DMSO, which are rarely used as heteroatom sources because most of the outer electrons of their N and S atoms are sharing with C or O atoms, were selected as N and S sources for synthesizing the N, S-codoped carbon materials during PVDC dehalogenation at room temperature (named as RT-NS-DCM). The SEM image (Figure 1A) reveals amorphous morphology. EDX element mapping (Figure 1B) 8 ACS Paragon Plus Environment

Page 9 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

verifies the substantial presence and uniform distribution of N and S in addition to C and O in RT-NS-DCM. Meanwhile, Raman spectrum in Figure 1C shows that a clear graphitization band is located at ~1583 cm-1 and also a disorder band at ~1354 cm-1, confirming the successful fabrication of carbonaceous materials at room temperature. XRD profile in Figure 1D further evidences the as-formed carbon to be amorphous, which is in agreement with SEM image. In addition, the overwhelming presence of XRD signals for KCl is observed for unwashed products (Figure 1D), which evidences that the dehalogenation reaction is probably following the formula (1).

RT (CH 2CCl2 ) n + 2nKOH  → C2 n + 2nKCl + 2nH 2O

(1)

9 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 25

Figure 1 (A) SEM image and (B) element mapping of RT-NS-DCM, (C) Raman spectra of RT/600-NS-DCM, and (D) XRD profiles of RT/600-NS-DCM and unwashed RT-NS-DCM samples.

XPS technique was applied to reveal the composition and functionality of RT-NS-DCM, as shown in Figure 2. Firstly, RT-NS-DCM has a high carbon content of 76.6 at.% (Figure 2A), in which the carbon species indicated by the C1s peak at ~285 eV takes the dominant proportion (Figure 2B), revealing the high completeness of PVDC dehalogenation and carbonization under KOH promotion. It is consistent with little Cl residual in the products. Secondly, the signals for N at ~400 eV and S at ~168 eV can be clearly observed in Figure 2A. According to the detailed deconvolutions of N1s and S2p spectra (Figure 2C/D), the N species is mainly taking pyrrolic form, and S species is mainly taking sulfone form.

In order to extend the N, S-codoped carbon materials in capacitive applications, high temperature annealing was performed on unwashed RT-NS-DCM prior to electrode fabrication. According to the annealing temperature of 500/600/700 °C, the products were named as 500/600/700-NS-DCM, respectively. In Figure 1D (XRD profile) and Figure 1C (Raman spectrum), 600-NS-DCM shows little variation relative to RT-NS-DCM, which may be ascribed to the high completeness of defunctionalization and carbonization at room temperature. Similar trends of XRD profiles and Raman spectra of 500/700-NS-DCM in Figure S2C/D are also observed.

10 ACS Paragon Plus Environment

Page 11 of 25

A

B

500k

40k

C1s~76.6%

400k

Cl2p ~3.4%

N1s ~4.7%

200k

S2p ~0.6%

100k 0 700

Intensity / cps

Intensity / cps

300k

30k 20k

~68.5% ~25.4%

10k

~6.1%

RT-NS-DCM

0 600

500

400

300

200

100

294

Binding energy / eV

D Raw Fitted Baseline Pyrrolic N Pyridinic N Graphitic N

4.0k

288

285

282

279

276

2.0k

1000 900

Intensity / cps

N1s

291

Binding energy / eV

C 6.0k

C1s

Raw Fitted Baseline C-C&C=C C-O/-N/-S C=O/=N Sat. peak

O1s~14.7%

Intensity / a.u.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

800

S2p

Raw Fitted Baseline C-SOx-C

700 600 500

404

402

400

398

Binding energy / eV

396

174

172

170

168

166

164

Binding energy / eV

Figure 2 XPS measurement on RT-NS-DCM: (A) element survey, (B) C1s spectrum, (C) N1s spectrum, and (D) S2p spectrum.

Figure 3A (SEM image of 600-NS-DCM) typifies that high temperature annealing transforms RT-NS-DCM into 3D porous structure, and NS-DCM materials annealed at 500 and 700 °C also show the similar morphology (Figure S2A/B). Uneven contrast is observed through the enlarged view of TEM image in Figure 3B, which arises from the porous structure of 600-NS-DCM. HRTEM image in Figure 3C shows that 600-NS-DCM possesses a large content of micropores, which is related to the activation of intentionally overdosed KOH in unwashed RT-NS-DCM; meanwhile, both amorphous and graphitic domains are presenting. As indicated by BET measurements (Figure 3D-F), increasing annealing temperature from 500 to 700 11 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 25

°C leads the significant increasing of specific surface area (SSA), micropore area and pore volume, because KOH activation usually begins to happen at 400 °C and thereafter gets intense. In our case, 700-NS-DCM does not present so much difference in SSA (760 m2 g-1) and micropore area (611 cm2 g-1) to 600-NS-DCM (SSA of 699 m2 g-1 and micropore area of 594 cm2 g-1), which is possibly due to the insufficient KOH for activation at 700 °C. Herein, the optimized temperature for activating carbon is about 600 °C after balancing porosity and yield, as other common reports.22

Figure 3 (A) SEM image, (B) TEM image, and (C) HRTEM image of 600-NS-DCM, (D) N2 adsorption/desorption curves, (E) specific surface areas and micropore areas, and (F) pore size distributions of 500/600/700-NS-DCM.

By performing annealing, partial functionalities can be eradicated from carbon matrix, leading to the formation of highly carbonized materials with less heteroatom doping. As shown in Figure 4A and Figure S3, increasing annealing temperature 12 ACS Paragon Plus Environment

Page 13 of 25

shows obvious positive effect on further carbonization, resulting in the carbon contents of 81.4 at.% for 600-NS-DCM and 88.3 at.% for 700-NS-DCM. The N contents show little variation and stably keep at ~3.0 at.%. But the S contents sharply drops from 2.4 at.% (600-NS-DCM) to 0.8 at.% (700-NS-DCM). As revealed by the deconvolutions of C1s spectra in Figure 4B, the C1s peaks are dominantly 285 eV-centered. The N configurations of 500/600-NS-DCM are dominated by the pyrrolic N, similar to that of RT-NS-DCM. While at 700 °C, the pyrrolic N will be gradually converted into the six-atom ringed pyridinic and graphitic N (Figure 4C).5-6, 23-24

The S configurations of 500/600-NS-DCM go through similar variation of

stability by keeping minimal change of the ratios of C-S-C and C-S(=O)-C, but due to the relatively poor stability of S species at high temperature, 700-NS-DCM shows a low S content (Figure 4D).

B 90

500-NS-DCM 600-NS-DCM 700-NS-DCM

80

Intensity

Atomic percentage / %

A

20

Raw Fitted Baseline C-C/C=C C-O/C-N/C-S C=O/C=N/C=S

700-NS -DCM 600-NS -DCM 500-NS -DCM

10 0 C

O

N

290

S

288

286

284

282

Binding energy / eV Raw

12.0k 10.0k 8.0k

700-NS-DCM

Fitted

Baseline Pyridinic N Pyrrolic N Graphitic N

600-NS-DCM

6.0k 500-NS-DCM

4.0k 406 404 402 400 398 396 394 392

Binding energy / eV

D 4k Raw C-S-C

Intensity / a.u.

C Intensity / cps

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

3k

2k

Fitted Baseline C-SOx-C

700-NS-DCM

600-NS-DCM

1k 500-NS-DCM

174

171

168

165

162

159

Binding energy / eV

13 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 25

Figure 4 XPS measurements of 500/600/700-NS-DCM: (A) bar chart of element analysis, (B) C1s spectra, (C) N1s spectra and (D) S2p spectra.

Therefore, after balancing the SSA, porosity, carbonization degree and heteroatom doping level, 600-NS-DCM was firstly selected as electrode material to explore capacitive applications. After a three-electrode electrochemical system was set up, the measurements in different electrolytes of 6.0 M KOH, 1.0 M NaCl or 1.0

M H2SO4 were respectively conducted and compared. Usually, the enclosed area of CV profile is one clear indicator for qualitative measurement of capacitance. As revealed in Figure 5A, the CV profile of 600-NS-DCM collected in 1.0 M H2SO4 shows the largest enclosed area, meaning that the highest capacitance can be expected in acid electrolyte. The largest area is probably related to the pseudocapacitance provided by S and N species when absorbing H+ ions.12 The second largest area is present in 6.0 M KOH and followed by the area collected in 1.0 M NaCl. The smallest capacitance achieved in neutral electrolyte is probably due to Na+ and Cl- which are hard to provide any pseudocapacitance.25 According to the galvanic charge/discharge profiles in Figure 5B, 600-NS-DCM shows very high specific capacitances of 427 F g-1 at 1.0 A g-1 and 334 F g-1 at 10.0 A g-1 in 1.0 M H2SO4, and both the initial capacitance and rate capability of 600-NS-DCM are among the best capacitive performance ever reported as listed in Table S1.13-14, 21, 26-36 600-NS-DCM also performs well in both 6.0 M KOH and 1.0 M NaCl, respectively exhibiting 328

14 ACS Paragon Plus Environment

Page 15 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

F g-1 and 242 F g-1 at 1.0 A g-1. Remarkably, 600-NS-DCM maintains ~60% of capacitance at ultrahigh current density of 100.0 A g-1 in 1.0 M H2SO4, achieving the specific capacitance of 251 F g-1. The rate capability in 1.0 M H2SO4 is the best over the other two electrolytes (Figure 5C), which is possibly ascribed to the smallest resistance of charge transferring when absorbing H+ ions with the smallest ionic radius, as revealed by the smallest semicircle of Nyquist plot (Figure S4). While those control samples doped with single heteroatom N or S show much lower capacitances in three electrolytes, as shown in Figure S5, confirming the importance of N and S codoping in DCM. The capacitive

behaviours of 500-NS-DCM and 700-NS-DCM are similar to that of 600-NS-DCM, but their specific capacitances are relatively low (Figure S6). Moreover, cycling

stability tests are performed as shown in Figure 5D. 600-NS-DCM shows very good cycling stability at current densities of both 1.0 A g-1 and 10.0 A g-1, obtaining almost 90% of capacitance retention after 1000 cycles in 1.0 M H2SO4. The good cycling stability can be also observed in the other two

electrolytes: the capacitance retention at 10.0 A g-1 was 91% in 1.0 M NaCl and 80% in 6.0 M KOH, respectively.

15 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

B

A

1.0

1 M H2SO4

2 0

6 M KOH 1 M NaCl 1 M H2SO4

0.8

Potential / V

Current / mA

4

1 M NaCl 6 M KOH

-2

10 A/g

0.6 0.4 0.2

1 A/g

-4 0.0

C

-0.5

0.0

0.5

Potential / VRHE 6 M KOH 1 M NaCl 1 M H2SO4

-1

300

200 400 600 800

200

100

0

20

40

60

Time / s

Time / s

D

500 400

0

1.0

400

Capacitance / F g-1

-1.0

Capacitance / F g

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 25

300

200

10 A/g 1 M H2SO4 1 M NaCl 6 M KOH

100

1 A/g 1 M H2SO4

0

0

20

40

60

80

Currrent density / A g-1

100

0

200

400

600

800

1000

Cycle number / n

Figure 5 (A) CV profiles, (B) GCD curves, (C) rate capability curves, and (D) Cycling stability tests of 600-NS-DCM measured in different electrolytes of 6.0 M KOH, 1.0 M NaCl, and 1.0 M H2SO4.

600-NS-DCM with porous structure, large SSA and ultrahigh capacitance should be promising electrode materials for CDI. The desalination performance of 600-NS-DCM was tested in NaCl solution using a home-made CDI set-up. The conductivity was in situ measured to monitor the change in solution concentration. The influence of applied voltage was firstly studied in 40 mg L-1 NaCl, as shown in Figure 6A. To exclude physical adsorption, applied voltage is not supplied in the first 20 min. During this period, it is observed that the conductivity of each experiment engages very limited increase, which is probably related to trace amount of ions remaining after annealing and washing processes. Once applied voltage is supplied, the conductivity of each experiment rapidly decreases and then reaches to a plateau 16 ACS Paragon Plus Environment

Page 17 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

within 80 min. When the CV profiles of 600-NS-DCM are collected using two-electrode testing system (Figure S7), no obvious faradaic current can be observed in between 1.4 to 1.6 V in NaCl solution, indicating that the operating voltage of 1.6 V for our CDI measurements is safe to avoid the splitting of water, which is mainly due to the largely expanded stable window of neutral electrolyte. With the higher applied voltage supply, the larger ion removal rate (U) and higher desalination capacity (W) are accordingly obtained. U plotting with W at different applied voltages are respectively shown in Figure 6B. For instance, 600-NS-DCM with 1.6 V applied voltage has a desalination capacity of 32.3 mg g-1 and a maximum ion removal rate of 0.56 mg g-1 min-1, which exceed most of the currently reported values for CDI applications as listed in Table S2.20, 33, 37-53

Even with 1.4 V applied voltage, the desalination capacity still reaches 30.9 mg g-1 and the maximum ion removal rate is 0.51 mg g-1 min-1. Secondly, the cycling stability of 600-NS-DCM was measured by monitoring the conductivity changes over five adsorption/desorption cycles with 1.4 or 1.6 V (Figure 6C). Desorption processes were achieved by applying transposed voltages. For the CDI cycles with both 1.4 V and 1.6 V, the trends of conductivity can be reproducible and the conductivity retentions achieve over 98% for the first four cycles, but the abnormal trends occur at the fifth cycle which is probably related to the detachment of active materials from current collectors after long-term operations. Finally, CDI experiments with higher NaCl concentrations were performed with 1.4 V for broadening the applications of NS-DCM. As shown in Figure 6D and Figure S8A-C, with NaCl concentrations 17 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

increasing, a continual enhancement of desalination capacity can be obtained, and 600-NS-DCM exhibits the desalination capacities of 48.2, 87.2, 140.7 mg g-1 in 100, 500 and 1000 mg L-1 NaCl solutions, respectively. The corresponding maximum ion removal rates are respectively 0.99, 1.53, and 1.60 mg g-1 min-1, as revealed in Figure

S8D. These results prove that the as-formed NS-DCM electrode materials are capable of treating concentrated NaCl solutions.

A

B

100

0.7

90

incr e

0.6

80 70 60

1.2V

50

1.4V

40

U / mg g-1 min-1

Conductivity / µS cm

-1

0V

1.6V

30

asin g

time

0.5 0.4 0.3

1.2 V 1.4 V 1.6 V

0.2 0.1 0.0

-20

0

20

40

60

80

100

Time / min

0

5

10

15

20

25

30

35

W / mg g-1

D

-1

100

80

60

40 1.4 V

1.6 V

20 0

200

400

600

Time / min

800

Desalination capacity / mg g

-1

C

Conductivity / µS cm

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 25

140.7

150

1.4 V 120 87.2 90 48.2

60 30.9 30

100

1000 -1

Initial concentration of NaCl / mg L

Figure 6. CDI performance of 600-NS-DCM measured in 40.0 mg L-1 NaCl: (A) desalination curves at different applied voltages, (B) desalination rate plotting with desalination capacity at different applied voltages, (C) cycling stability tests at applied voltages of 1.4 V and 1.6 V, and (D) desalination capacities in different initial NaCl concentrations at applied voltage of 1.4 V.

18 ACS Paragon Plus Environment

Page 19 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

4. Conclusions

In conclusion, we develop a facile synthetic strategy for multiply doped carbon

materials

at

room

temperature

through

in

situ

doping

PVDC-dehalogenated carbon with multiple heteroatom sources. N, S-codoped carbon materials (NS-DCM) are demonstratively fabricated using two common solvents: DMF and DMSO, during the dehalogenation of PVDC promoted by KOH. For electrochemical applications, the room-temperature synthesized NS-DCM are submitted to annealing to gain large SSA and good conductivity. Remarkably, the resulted 600-NS-DCM exhibits a specific capacitance as high as 427 F g-1 (at 1.0 A g-1) and nearly 60% of capacitance retention at ultrahigh current density of 100.0 A g-1 in 1.0 M H2SO4, and very good cycling stability. Meanwhile, it exhibits a high efficiency and long-term stability towards CDI, achieving a desalination capacity of 32.3 mg g-1 in 40.0 mg L-1 NaCl. We believe this clean and time/cost-efficient strategy for the fabrication of multiple heteroatoms-doped carbon materials has wide application prospects in electrochemical energy conversion and storage. ASSOCIATED CONTENT

Supporting Information. TG profile of PVDC and digital image of ball-milled PVDC/DMF, SEM images, Raman spectra, XRD profiles, XPS element survey and electrochemical data of 500/700-NS-DCM, rate capability of 600-N or S-DCM, supportive CDI data, tables for the summary of capacitive and CDI performance of 19 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 25

previously reported works. These materials are available free of charge via the Internet at http://pubs.acs.org.

AUTHOR INFORMATION

Corresponding Author *[email protected], and *[email protected].

ACKNOWLEDGMENT This work was financially supported by NSFC, 973 Program (2014CB932104), and Beijing Engineering Center for Hierarchical Catalysts, the Fundamental Research Funds for the Central Universities, the Program for Changjiang Scholars and Innovative Research Team in the University, and the long-term subsidy mechanism from the Ministry of Finance and the Ministry of Education of PRC.

REFERENCES 1. Zhang, B.; Wang, H. H.; Su, H.; Lv, L. B.; Zhao, T. J.; Ge, J. M.; Wei, X.; Wang, K. X.; Li, X. H.; Chen, J. S., Nitrogen-Doped Graphene Microtubes with Opened Inner Voids: Highly Efficient Metal-Free Electrocatalysts for Alkaline Hydrogen Evolution Reaction. Nano Res. 2016, 9 (9), 2606–2615. 2. Li, J.-C.; Hou, P.-X.; Zhao, S.-Y.; Liu, C.; Tang, D.-M.; Cheng, M.; Zhang, F.; Cheng, H.-M., A 3D Bi-Functional Porous N-Doped Carbon Microtube Sponge Electrocatalyst for Oxygen Reduction and Oxygen Evolution Reactions. Energy Environ. Sci. 2016, 9, 3079-3084. 3. Tang, C.; Wang, H.-F.; Chen, X.; Li, B.-Q.; Hou, T.-Z.; Zhang, B.; Zhang, Q.; Titirici, M.-M.; Wei, F., Topological Defects in Metal-Free Nanocarbon for Oxygen Electrocatalysis. Adv. Mater. 2016, 28 (32), 6845-6851. 4. Martinez, U.; Dumont, J. H.; Holby, E. F.; Artyushkova, K.; Purdy, G. M.; Singh, A.; Mack, N. H.; Atanassov, P.; Cullen, D. A.; More, K. L., Critical Role of Intercalated Water for Electrocatalytically Active Nitrogen-Doped Graphitic Systems. Sci. Adv. 2016, 2 (3), e1501178. 5. Zhang, G.; Jin, X.; Li, H.; Wang, L.; Hu, C.; Sun, X., N-Doped Crumpled Graphene: Bottom-Up Synthesis and Its Superior Oxygen Reduction Performance. Sci. 20 ACS Paragon Plus Environment

Page 21 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

China Mater. 2016, 59 (5), 337-347. 6. Zhang, G.; Luo, H.; Li, H.; Wang, L.; Han, B.; Zhang, H.; Li, Y.; Chang, Z.; Kuang, Y.; Sun, X., ZnO-Promoted Dechlorination for Hierarchically Nanoporous Carbon as Superior Oxygen Reduction Electrocatalyst. Nano Energy 2016, 26, 241-247. 7. Wang, H.; Chen, Y.; Hou, X.; Ma, C.; Tan, T., Nitrogen-Doped Graphenes as Efficient Electrocatalysts for Selective Reduction of Carbon Dioxide to Formate in Aqueous Solution. Green Chem. 2016, 18 (11), 3250-3256. 8. Ding, Y. L.; Kopold, P.; Hahn, K.; Aken, P. A. V.; Maier, J.; Yu, Y., Facile Solid-State Growth of 3D Well-Interconnected Nitrogen-Rich Carbon Nanotube-Graphene Hybrid Architectures for Lithium-Sulfur Batteries. Adv. Funct. Mater. 2015, 26 (7), 1681-1693. 9. Sun, D.; Yan, X.; Yang, J.; Zhang, P.; Xue, Q., Hierarchically Porous and Nitrogen‐Doped Graphene‐Like Microspheres as Stable Anodes for Lithium‐Ion Batteries. ChemElectroChem 2015, 2 (8), 638-643. 10. Wang, X.; Lv, L.; Cheng, Z.; Gao, J.; Dong, L.; Hu, C.; Qu, L., High‐Density Monolith of N‐Doped Holey Graphene for Ultrahigh Volumetric Capacity of Li‐ Ion Batteries. Adv. Energy Mater. 2016, 6 (6), 1502100. 11. Zhang, Z.; Bao, J.; He, C.; Chen, Y.; Wei, J.; Zhou, Z., Hierarchical Carbon– Nitrogen Architectures with Both Mesopores and Macrochannels as Excellent Cathodes for Rechargeable Li–O2 Batteries. Adv. Funct. Mater. 2014, 24 (43), 6826– 6833. 12. Lin, T.; Chen, I. W.; Liu, F.; Yang, C.; Bi, H.; Xu, F.; Huang, F., Nitrogen-Doped Mesoporous Carbon of Extraordinary Capacitance for Electrochemical Energy Storage. Science 2015, 350 (6267), 1508-1513. 13. Xu, Y.; Tao, Y.; Zheng, X.; Ma, H.; Luo, J.; Kang, F.; Yang, Q. H., A Metal‐Free Supercapacitor Electrode Material with a Record High Volumetric Capacitance over 800 F cm−3. Adv. Mater. 2015, 27 (48), 8082-8087. 14. Zhang, T.; Zhang, F.; Zhang, L.; Lu, Y.; Zhang, Y.; Yang, X.; Ma, Y.; Huang, Y., High Energy Density Li-Ion Capacitor Assembled with All Graphene-Based Electrodes. Carbon 2015, 92, 106-118. 15. Qian, B.; Wang, G.; Zheng, L.; Dong, Q.; Wu, T.; Zhang, X.; Qiu, J., Sulfonated Graphene as Cation‐Selective Coating: A New Strategy for High‐Performance Membrane Capacitive Deionization. Adv. Mater. Interfaces 2015, 2 (16), 1500372. 16. Shi, J.; Zhou, X.; Xu, P.; Qiao, J.; Chen, Z.; Liu, Y., Nitrogen and Sulfur co-Doped Mesoporous Carbon Materials as Highly Efficient Electrocatalysts for Oxygen Reduction Reaction. Electrochim. Acta 2014, 145, 259-269. 17. Ling, Z.; Wang, G.; Zhang, M.; Fan, X.; Yu, C.; Yang, J.; Xiao, N.; Qiu, J., Boric Acid-Mediated B,N-codoped Chitosan-Derived Porous Carbons with A High Surface Area and Greatly Improved Supercapacitor Performance. Nanoscale 2015, 7 (12), 5120-5125. 18. Zhang, J.; Zhou, J.; Wang, D.; Hou, L.; Gao, F., Nitrogen and Sulfur codoped Porous Carbon Microsphere: A High Performance Electrode in Supercapacitor. Electrochim. Acta 2016, 191, 933-939. 21 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 25

19. Sevilla, M.; Fuertes, A. B., Direct Synthesis of Highly Porous Interconnected Carbon Nanosheets and Their Application as High-Performance Supercapacitors. ACS Nano 2014, 8 (5), 5069-–5078. 20. Chao, L.; Liu, Z.; Zhang, G.; Song, X.; Lei, X.; Noyong, M.; Simon, U.; Chang, Z.; Sun, X., Enhancement of Capacitive Deionization Capacity of Hierarchical Porous Carbon. J. Mater. Chem. A 2015, 3 (24), 12730-12737. 21. Zhang, G.; Wang, L.; Hao, Y.; Jin, X.; Xu, Y.; Kuang, Y.; Dai, L.; Sun, X., Unconventional Carbon: Alkaline Dehalogenation of Polymers Yields N‐Doped Carbon Electrode for High‐Performance Capacitive Energy Storage. Adv. Funct. Mater. 2016, 26 (19), 3340–3348. 22. Wu, S.; Chen, G.; Kim, N. Y.; Ni, K.; Zeng, W.; Zhao, Y.; Tao, Z.; Ji, H.; Lee, Z.; Zhu, Y., Creating Pores on Graphene Platelets by Low-Temperature KOH Activation for Enhanced Electrochemical Performance. Small 2016, 12 (17), 2376-2384. 23. Wang, L.; Zhang, G.; Han, B.; Chang, Y.; Li, H.; Wang, J.; Hu, C.; Chang, Z.; Huo, Z.; Sun, X., A two-Volt Aqueous Supercapacitor from Porous Dehalogenated Carbon. J. Mater. Chem. A 2017, 5, 6734-6739 24. Zhang, G.; Wang, J.; Qin, B.; Jin, X.; Wang, L.; Li, Y.; Sun, X., Room-Temperature Rapid Synthesis of Metal-Free Doped Carbon Materials. Carbon 2017, 115, 28-33. 25. Liu, Y.; Pan, L.; Chen, T.; Xu, X.; Lu, T.; Sun, Z.; Chua, D. H. C., Porous Carbon Spheres via Microwave-Assisted Synthesis for Capacitive Deionization. Electrochim. Acta 2015, 151, 489-496. 26. Hu, Y., A Versatile, Ultralight, Nitrogen-Doped Graphene Framework. Angew. Chem., Int. Ed. 2012, 51 (45), 11371-11375. 27. Assresahegn, B. D.; Bélanger, D., Multifunctional Carbon for Electrochemical Double‐Layer Capacitors. Adv. Funct. Mater. 2015, 25 (43), 6775-6785. 28. Ling, Z.; Wang, Z.; Zhang, M.; Yu, C.; Wang, G.; Dong, Y.; Liu, S.; Wang, Y.; Qiu, J., Sustainable Synthesis and Assembly of Biomass‐Derived B/N Co‐Doped Carbon Nanosheets with Ultrahigh Aspect Ratio for High ‐ Performance Supercapacitors. Adv. Funct. Mater. 2016, 26 (1), 111-119. 29. Xu, J.; Tan, Z.; Zeng, W.; Chen, G.; Wu, S.; Zhao, Y.; Ni, K.; Tao, Z.; Ikram, M.; Ji, H., A Hierarchical Carbon Derived from Sponge ‐ Templated Activation of Graphene Oxide for High‐Performance Supercapacitor Electrodes. Adv. Mater. 2016, 28 (26), 5222-5228. 30. Qian, B.; Wang, G.; Ling, Z.; Dong, Q.; Wu, T.; Zhang, X.; Qiu, J., Sulfonated Graphene as Cation‐Selective Coating: A New Strategy for High‐Performance Membrane Capacitive Deionization. Adv. Mater. Interfaces 2015, 2 (16), 1500372. 31. Song, B.; Choi, J. I.; Zhu, Y.; Geng, Z.; Zhang, L.; Lin, Z.; Tuan, C.-c.; Moon, K.-s.; Wong, C.-p., Molecular Level Study of Graphene Networks Functionalized with Phenylenediamine Monomers for Supercapacitor Electrodes. Chem. Mater. 2016, 28 (24), 9110-9121. 32. Wei, X.; Jiang, X.; Wei, J.; Gao, S., Functional Groups and Pore Size Distribution Do Matter to Hierarchically Porous Carbons as High-Rate-Performance Supercapacitors. Chem. Mater. 2016, 28 (2), 445-458. 22 ACS Paragon Plus Environment

Page 23 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

33. Niu, R.; Li, H.; Ma, Y.; He, L.; Li, J., An Insight into the Improved Capacitive Deionization Performance of Activated Carbon Treated by Sulfuric Acid. Electrochim. Acta 2015, 176, 755-762. 34. Guo, H.; Gao, Q., Boron and nitrogen Codoped Porous Carbon and Its Enhanced Properties as Supercapacitor. J. Power Sources 2009, 186 (2), 551-556. 35. Chen, X. a.; Chen, X.; Xu, X.; Yang, Z.; Liu, Z.; Zhang, L.; Xu, X.; Chen, Y.; Huang, S., Sulfur-Doped Porous Reduced Graphene Oxide Hollow Nanosphere Frameworks as Metal-Free Electrocatalysts for Oxygen Reduction Reaction and as Ssupercapacitor Electrode Materials. Nanoscale 2014, 6 (22), 13740-13747. 36. Wang, G.; Qian, B.; Dong, Q.; Yang, J.; Zhao, Z.; Qiu, J., Highly Mesoporous Activated Carbon Electrode for Capacitive Deionization. Sep. Purif. Technol. 2013, 103, 216-221. 37. Aslan, M.; Zeiger, M.; Jäckel, N.; Grobelsek, I.; Weingarth, D.; Presser, V., Improved Capacitive Deionization Performance of Mixed Hydrophobic/Hydrophilic Activated Carbon Electrodes. J. Phys.: Condens. Matter 2016, 28 (11), 114003. 38. Duan, X.; Liu, W.; Chang, L., Porous Carbon Prepared by Using ZIF-8 as Precursor for Capacitive Deionization. J. Taiwan Inst. Chem. Eng. 2016, 62, 132-139. 39. El-Deen, A. G.; Barakat, N. A. M.; Khalil, K. A.; Motlak, M.; Kim, H. Y., Graphene/SnO2 Nanocomposite as An Effective Electrode Material for Saline Water Desalination Using Capacitive Deionization. Ceram. Int. 2014, 40 (9), 14627-14634. 40. Huang, Z. H.; Wang, M.; Wang, L.; Kang, F., Relation between the Charge Efficiency of Activated Carbon Fiber and Its Desalination Performance. Langmuir 2012, 28 (11), 5079-84. 41. Li, G. X.; Hou, P. X.; Zhao, S. Y.; Liu, C.; Cheng, H. M., A Flexible Cotton-Derived Carbon Sponge for High-Performance Capacitive Deionization. Carbon 2016, 101 (5), 1-8. 42. Li, H.; Lu, T.; Pan, L.; Zhang, Y.; Sun, Z., Electrosorption Behavior of Graphene in NaCl Solutions. J. Mater. Chem. 2009, 19 (37), 6773-6779. 43. Li, Y.; Hussain, I.; Qi, J.; Liu, C.; Li, J.; Shen, J.; Sun, X.; Han, W.; Wang, L., N-doped Hierarchical Porous Carbon Derived from Hypercrosslinked Diblock Copolymer for Capacitive Deionization. Sep. Purif. Technol. 2016, 165, 190-198. 44. Omosebi, A.; Xin, G.; Landon, J.; Liu, K., Asymmetric Electrode Configuration for Enhanced Membrane Capacitive Deionization. ACS Appl. Mater. Interfaces 2014, 6 (15), 12640-12649. 45. Peng, Z.; Zhang, D.; Yan, T.; Zhang, J.; Shi, L., Three-Dimensional Micro/Mesoporous Carbon Composites with Carbon Nanotube Networks for Capacitive Deionization. Appl. Surf. Sci. 2013, 282 (10), 965-973. 46. Ryoo, M. W.; Kim, J. H.; Seo, G., Role of Titania Incorporated on Activated Carbon Cloth for Capacitive Deionization of NaCl Solution. J. Colloid Interface Sci. 2003, 264 (2), 414-419. 47. Tian, G.; Ling, L.; Meng, Q.; Bing, C., Preparation and Characterization of Cross-Linked Quaternised Polyvinyl Alcohol Membrane/Activated Carbon Composite Electrode for Membrane Capacitive Deionization. Desalination 2014, 354, 107–115. 48. Tuan, T. N.; Chung, S.; Lee, J. K.; Lee, J., Improvement of water softening 23 ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 25

Efficiency in Capacitive Deionization by Ultrapurification Process of Reduced Graphene Oxide. Curr. Appl. Phys. 2015, 15 (11), 1397-1401. 49. Wang, G.; Dong, Q.; Wu, T.; Zhan, F.; Zhou, M.; Qiu, J., Ultrasound-Assisted Preparation of Electrospun Carbon Fiber/Graphene Electrodes for Capacitive Deionization: Importance and Unique Role of Electrical Conductivity. Carbon 2016, 103, 311-317. 50. Wang, X. Z.; Li, M. G.; Chen, Y. W.; Cheng, R. M.; Huang, S. M.; Pan, L. K.; Sun, Z., Electrosorption of NaCl Solutions with Carbon Nanotubes and Nanofibers Composite Film Electrodes. Electrochem. Solid-State Lett. 2006, 9 (9), E23-E26. 51. Xu, X.; Li, J.; Wang, M.; Liu, Y.; Lu, T.; Pan, L., Shuttle‐Like Porous Carbon Rods from Carbonized Metal – Organic Frameworks for High ‐ Performance Capacitive Deionization. ChemElectroChem 2016, 3 (6), 993-998. 52. Yong, L.; Pan, L.; Xu, X.; Lu, T.; Zhuo, S.; Chua, D. H. C., Enhanced Desalination Efficiency in Modified Membrane Capacitive Deionization by Introducing Ion-Exchange Polymers in Carbon Nanotubes Electrodes. Electrochim. Acta 2014, 130 (4), 619-624. 53. Li, Z.; Song, B.; Wu, Z.; Lin, Z.; Yao, Y.; Moon, K.-S.; Wong, C., 3D Porous graphene with Ultrahigh Surface Area for Microscale Capacitive Deionization. Nano Energy 2015, 11, 711-718.

24 ACS Paragon Plus Environment

Page 25 of 25

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Table of Contents Graphic

25 ACS Paragon Plus Environment