Subscriber access provided by Washington University | Libraries

Article

Post-assembly fabrication of a functional multicomponent supramolecular hydrogel based on a self-sorting double network Wataru Tanaka, Hajime Shigemitsu, Takahiro Fujisaku, Ryou Kubota, Saori Minami, Kenji Urayama, and Itaru Hamachi J. Am. Chem. Soc., Just Accepted Manuscript • Publication Date (Web): 05 Mar 2019 Downloaded from http://pubs.acs.org on March 5, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1 2

Post-assembly fabrication of a functional multicomponent supramolecular hydrogel

3

based on a self-sorting double network

4 5

Wataru Tanaka1,§, Hajime Shigemitsu1,†,‡,§, Takahiro Fujisaku1, Ryou Kubota1, Saori

6

Minami2, Kenji Urayama2, Itaru Hamachi1,3*

7 8

1

9

Engineering, Kyoto University, Katsura, Kyoto 615-8510, JAPAN

Department of Synthetic Chemistry and Biological Chemistry, Graduate School of

10

2

11

Matsugasaki, Kyoto 606-8585, JAPAN

12

3

13

Technology Agency (JST), 5 Sanbancho, Chiyoda-ku, Tokyo 102-0075, JAPAN

14



15

Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871, JAPAN

16



17

of Engineering, Osaka University, 2-1 Yamadaoka, Suita, Osaka 565-0871, JAPAN

18

§

Department of Macromolecular Science and Engineering, Kyoto Institute of Technology,

Core Research for Evolutional Science and Technology (CREST), Japan Science and

Present address 1: Department of Applied Chemistry, Graduate School of Engineering,

Present address 2: Frontier Research Base for Global Young Researchers, Graduate School

These authors contributed equally to this work.

19 20

Correspondence: [email protected]

21

1 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Abstract

2

Living cells exhibit sophisticated functions because they contain numerous endogenous

3

stimuli-responsive molecular systems that independently and cooperatively act in response to

4

an external circumstance. On the other hand, artificial soft materials containing multiple

5

stimuli-responsive molecular systems are still rare. Herein, we demonstrate a unique

6

multicomponent hydrogel composed of a self-sorting double network prepared through a

7

post-assembly fabrication (PAF) protocol. The PAF protocol allowed the construction of a

8

well-ordered hydrogel with a dual-biomolecule-response to two important biomolecules

9

(adenosine triphosphate (ATP) and sarcosine). Such a hydrogel could not be prepared

10

through a one-step mixing protocol. The resultant multicomponent hydrogel responded to

11

ATP and sarcosine through a gel–sol transition behavior programmed in an AND logic gate

12

fashion. Finally, we applied the multicomponent hydrogel to a controlled release of an

13

antibody.

14

2 ACS Paragon Plus Environment

Page 2 of 28

Page 3 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

Main text

2

Stimuli-responsive supramolecular hydrogels have been used as excellent soft materials for

3

controlled drug release1, a scaffold for regenerative medicine2, and a self-supported diagnosis

4

tool3. Recently, the preparation of multicomponent hydrogels has been a promising strategy

5

to obtain hydrogels with intelligent functions4. For instance, multicomponent supramolecular

6

hydrogels consisting of an enzyme-loaded liposome enabled precise control of the drug

7

release rate by controlling the heating time5. Supramolecular hydrogels including inorganic

8

materials (mesoporous silica or layered clay), fluorescent dyes, and an enzyme were used to

9

form a unique fluorescent sensor array6. Moreover, biomarker-responsive supramolecular

10

hydrogels have been constructed by coupling chemically reactive supramolecular fibers and

11

enzymes within a gel matrix7. It has also been reported that the encapsulation of a signal

12

amplification system into the biomarker-responsive hydrogels allowed for excellent

13

improvement of the sensitivity8. Multicomponent supramolecular hydrogels involving

14

orthogonally well-ordered stimuli-response systems would lead to next generation intelligent

15

materials equipped with autonomic response to diverse environmental change like living cells,

16

supreme natural soft-materials comprising multiple components9.

17

A self-sorting double network (SDN) hydrogel is an attractive multicomponent soft

18

material10. Adams and co-workers fabricated self-sorting supramolecular nanofibers by

19

applying gradual pH changes11 and subsequently developed SDN hydrogels that could be

20

spatially resolved by UV light12. Smith and co-workers also reported a phototunable SDN

21

hydrogel containing a phototriggered acid generator13. We recently demonstrated hydrogels

22

with unique adaptive functions that directly rely on the orthogonality of the SDN hydrogel14.

23

An SDN requires a delicate balance of the noncovalent interactions between both the intra3 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

and interfiber components, which is very difficult to control under aqueous conditions15.

2

Therefore, there is a limited variety of SDN hydrogels. An SDN should provide an excellent

3

platform to realize well-ordered stimuli-responsive systems.

4

Herein, we demonstrate a powerful post-assembly fabrication (PAF) strategy for

5

the construction of a multicomponent SDN hydrogel with a dual-stimuli-responsive system

6

(Figure 1a). A unique biomolecule-responsive multicomponent hydrogel was successfully

7

prepared through the PAF protocol from the original SDN hydrogel. Naked eye observation,

8

confocal laser scanning microscopy (CLSM) imaging, and rheological analysis revealed that

9

the SDN in the clear hydrogel was well-retained even after the dropwise addition of Ca2+ ions

10

and sarcosine oxidase (SOx) (i.e. additional components for acquiring a biomolecule

11

response) to the original SDN hydrogel; whereas an inhomogeneous suspension containing

12

disordered aggregates was obtained by a one-step mixing protocol of the components. The

13

multicomponent hydrogel prepared by PAF undergoes a macroscopic gel–sol transition in

14

response to two distinct biomolecules, ATP and sarcosine, in the AND logic gate fashion16,

15

which allowed for the controlled release of an antibody, a pharmaceutically important

16

protein.

4 ACS Paragon Plus Environment

Page 4 of 28

Page 5 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1 2

Figure 1. (a) Schematic representation of the post-assembly fabrication (PAF) strategy for

3

the construction of a multicomponent hydrogel based on a self-sorting double network (SDN).

4

The additional components (sarcosine oxidase (SOx) and Ca2+ ions) are sequentially added to

5

the SDN hydrogel composed of Phos-cycC6 and BPmoc-F3. The multicomponent

6

(Phos-cycC6/BPmoc-F3/Ca2+/SOx) hydrogel exhibits designed functions (i.e. gel–sol

7

transition in AND logic gate fashion by ATP and sarcosine). (b) Chemical structures of the

8

self-sorting hydrogelator pair, Phos-cycC6 and BPmoc-F3.

9

5 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

The strategy for development of a multicomponent hydrogel by post-assembly

2

fabrication (PAF)

3

The appropriate combination of additional components can equip an SDN hydrogel with new

4

functions without perturbing the orthogonal double fiber networks17. However, the

5

components may compromise the orthogonal self-assembly property of the SDN pair in a

6

one-step mixing protocol and the resultant material would not exhibit the designed functions

7

derived from the well-ordered SDN. Our PAF strategy for the construction of a

8

multicomponent hydrogel is illustrated in Figure 1a. In the PAF strategy, additional

9

components were sequentially mixed with the SDN hydrogel after the formation of the

10

self-sorting nanofibers. Therefore, the kinetically stable well-ordered SDN can be retained

11

after the addition of the components without the generation of disordered co-assembled

12

structures11,12.

13

The sophisticated functionalization of the original properties of the SDN requires

14

an elaborate design that can effectively interact the additional components with the fibers.

15

We employed Phos-cycC6 and BPmoc-F3 as a gelator pair, which have been previously

16

demonstrated to orthogonally self-assemble (Figure 1b)15. Previous structural and

17

spectroscopic analyses showed that a few noncovalent interactions (hydrogen-bonding, π/π

18

interactions, van der Waals interactions) were distinctly present between the two gelators,

19

through which the two different fibers (Phos-cycC6 and BPmoc-F3) were orthogonally

20

formed. A coordination bond was not involved in this pair; we have previously reported that

21

the strength of the Phos-cycC6 hydrogel was modulated by Ca2+ ions18. It has already been

22

revealed that the hybridization of BPmoc-F3 hydrogel and sarcosine oxidase (SOx) affords

23

the gel–sol transition response to sarcosine, a biomarker of prostate cancer (Figure S1)7b, 19. 6 ACS Paragon Plus Environment

Page 6 of 28

Page 7 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

Therefore, we decided to use Ca2+ ions and SOx as additional components that may

2

functionalize Phos-cycC6 and BPmoc-F3, respectively, in the PAF protocol.

3 4

PAF of ATP-responsive hydrogel based on single Phos-cycC6 fibers

5

According to our previous report, a viscous solution containing Phos-cycC6 fibers showed

6

Ca2+ ions-induced hydrogelation through a coordination bond with the phosphate head groups

7

(Figure 2a)18. The resultant Phos-cycC6/Ca2+ hydrogel was weakened (the gel–sol transition)

8

by addition of ethylenediaminetetraacetic acid (EDTA), a Ca2+ ion chelator. These results let

9

us expect that ATP (Figure S2) could also be used instead of EDTA as a biologically relevant

10

Ca2+ ion chelator to tune the strength of the Phos-cycC6/Ca2+ hydrogel because of its

11

sufficient affinity for the Ca2+ ions (the dissociation constant (Kd): 170 µM)20.

12

7 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2

Figure 2. (a) Schematic representation of the preparation of Phos-cycC6/Ca2+ hydrogel by

3

PAF. (b) Photo of Phos-cycC6/Ca2+ hydrogels (20 µL) on a flat glass slide 2 h after the

4

addition of nucleotide derivatives (ATP, ADP, AMP, and UTP). Conditions: [Phos-cycC6] =

5

0.2 wt% (3.2 mM), [Ca2+] = 1.3 mM, 100 mM MES buffer (pH 7.0), 25 °C. (c) Time-course

6

CLSM images and (d) fluorescent recovery profiles of Phos-cycC6 fibers stained with

7

Alexa546-cycC6 after photobleaching. Conditions: [Phos-cycC6] = 0.1 wt% (1.6 mM),

8

[Alexa546-cycC6] = 4.0 µM, [Ca2+] = 4.9 mM, [ATP] = 49 mM, 100 mM MES buffer (pH

9

7.0), room temperature (rt). Scale bar: 1 µm. (e) Diffusion coefficients of Phos-cycC6 fibers

10

determined by FRAP experiments (n = 5) with or without Ca2+ ions and ATP. The data

11

represent the mean ± standard deviation (s.d).

12 13 14

First, we confirmed the ATP response of the Phos-cycC6/Ca2+ hydrogel. A

15

Phos-cycC6/Ca2+ hydrogel was prepared through the PAF protocol (Figure 2a). A 100 mM

16

aqueous MES buffer solution (pH 7.0) was added to a powder of Phos-cycC6 and subsequent

17

heating yielded a clear solution in which the gelator was completely dissolved (see 8 ACS Paragon Plus Environment

Page 8 of 28

Page 9 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

supporting information for the detailed protocol). After incubation at 25 °C for 1 h to form a

2

dispersed solution of Phos-cycC6 fibers, Ca2+ ions were added to afford a clear

3

Phos-cycC6/Ca2+ hydrogel (Phos-cycC6: 0.20 wt% (3.2 mM), Ca2+: 1.3 mM) (Figure S3). In

4

this manuscript, we define the gel or sol state by the tube inversion test (visual confirmation

5

of fluidity of the samples). We also tested a one-step mixing protocol, that is, mixing of two

6

components (Phos-cycC6 and Ca2+ ions) followed by heating/cooling. However, we failed to

7

prepare a hydrogel but obtained an inhomogeneous suspension containing a large amount of

8

precipitate (Figure S4). This result indicated that the PAF process was indispensable for the

9

formation of the Phos-cycC6/Ca2+ hydrogel.

10

We examined the ATP-response of the Phos-cycC6/Ca2+ hydrogel. The hydrogel

11

changed to the sol state 2 h after the addition of ATP, as we expected (Figure 2b, S3). The

12

minimal concentration of ATP for the gel–sol transition was 3.2 mM (2.5 equivalents of the

13

Ca2+ ions). Adenosine diphosphate (ADP) and uridine triphosphate (UTP) similarly induced

14

the gel–sol transition (the minimal concentration of ADP and UTP was 16 mM (12.5 eq.) and

15

3.2 mM (2.5 eq.), respectively); whereas adenosine monophosphate (AMP) could not induce

16

the gel–sol transition at 16 mM (12.5 eq.) (Figure 2b, S2). It was clear that the order of the

17

minimal concentration of these nucleotide derivatives for the transition corresponded well

18

with their affinity to the Ca2+ ions (Kd of ATP: 170 µM, ADP: 1.51 mM, AMP: 17.4 mM,

19

UTP: 195 µM)20, implying that the gel–sol transition was caused by the removal of the Ca2+

20

ions from the Phos-cycC6/Ca2+ network, probably by the oligophosphate groups of these

21

nucleotides. In contrast, a Phos-cycC6 hydrogel without Ca2+ ions (8.1 mM, the same as the

22

critical gelation concentration (CGC)) retained the gel state even upon ATP addition (24 mM,

23

3.0 eq. of Phos-cycC6) (Figure S5). These results clearly revealed that coordination of Ca2+ 9 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

ions can afford an ATP response in the original Phos-cycC6 network through the PAF

2

protocol.

3

The impact of Ca2+ ions on the Phos-cycC6 fibers was evaluated by CLSM

4

imaging after staining with an appropriate fluorescence probe, Alexa546-cycC6 (Figure

5

S6)15b. As shown in Figure S7, the Ca2+ ions did not significantly alter the morphologies of

6

the Phos-cycC6 fibers, suggesting that the Ca2+ ions hardly disturbed the fiber network.

7

Unfortunately, we could not obtain direct evidence of the interaction of the Ca2+ ions with the

8

fibers by CLSM imaging. Therefore, we carefully evaluated the fluidity of the Phos-cycC6

9

fibers with/without Ca2+ ions using the fluorescence recovery after photobleaching (FRAP)

10

technique21. Time-lapse CLSM images of the stained Phos-cycC6 fibers after photobleaching

11

and the fluorescence recovery profiles are shown in Figure 2c and 2d, respectively. The

12

diffusion coefficients of the Phos-cycC6 fibers in the absence and presence of Ca2+ ions were

13

(3.0 ± 1.8) × 10–2 and (0.16 ± 0.06) × 10–2 µm2/s, respectively (Figure 2e). These results

14

indicated that the Ca2+ ions suppressed the fluidity of the Phos-cycC6 fibers owing to

15

coordination bonding between the Ca2+ ions and the phosphate head groups of the

16

Phos-cycC6 fiber surface. The decreased diffusion coefficient of Phos-cycC6 fibers was

17

recovered to (1.5 ± 0.4) × 10–2 µm2/s by the addition of ATP owing to the removal of the

18

Ca2+ ions from the Phos-cycC6 fibers (Figure 2e). These FRAP experiments explained the

19

macroscopic gel–sol transition of the Phos-cycC6/Ca2+ hydrogel resulting from the addition

20

of ATP.

21

10 ACS Paragon Plus Environment

Page 10 of 28

Page 11 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

PAF of a multicomponent (Phos-cycC6/BPmoc-F3/Ca2+/SOx) hydrogel with a

2

dual-stimuli-responsive system

3

With the two biomolecule-responsive hydrogels (ATP-responsive system: Phos-cycC6/Ca2+,

4

sarcosine-responsive system: BPmoc-F3/SOx) in hand, we hybridized the two systems

5

through the PAF protocol (Figure 3a). Utilizing the self-sorting feature of the original SDN

6

pair, we initially prepared a template SDN using Phos-cycC6 and BPmoc-F3. A mixed

7

suspension of Phos-cycC6 and BPmoc-F3 powders in aqueous 100 mM MES buffer (pH 7.0)

8

was heated until the powders dissolved. The solution was incubated for 1 h at 25 ºC to give

9

an SDN hydrogel (Phos-cycC6: 0.20 wt% (3.2 mM), BPmoc-F3: 0.075 wt% (1.2 mM), the

10

CGC of Phos-cycC6 and BPmoc-F3 are 0.5 wt% and 0.05 wt%7b, respectively). Subsequently,

11

an aqueous solution of SOx was added and then a Ca2+ ion solution was added dropwise to

12

the hydrogel, which afforded a well-ordered Phos-cycC6/BPmoc-F3/Ca2+/SOx hydrogel

13

(hereinafter, referred to as “multicomponent hydrogel”) (Figure 3b)22.

11 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 28

1 2

Figure 3. (a) Schematic representation of the preparation of the multicomponent

3

(Phos-cycC6/BPmoc-F3/Ca2+/SOx)

4

multicomponent hydrogel. (c) CLSM images of Phos-cycC6/BPmoc-F3 (left) and

5

multicomponent

6

Alexa546-cycC6 (red) and BP-OG (green). The Pearson’s correlation coefficients are shown

7

in the upper right of the images. Scale bar: 20 µm. Conditions: ((b) and (c)) [Phos-cycC6] =

8

0.2 wt% (3.2 mM), [Alexa546-cycC6] = 4.0 µM, [BPmoc-F3] = 0.075 wt% (1.2 mM),

9

[BP-OG] = 4.0 µM, [Ca2+] = 1.3 mM, [SOx] = 0.5 mg/mL (7.7 µM), 100 mM MES buffer

10

(pH 7.0), 25 °C (b), 30 °C (c). (d) Rheological properties of the Phos-cycC6/BPmoc-F3/SOx

11

hydrogels at an angular frequency of 10 rad/s with or without Ca2+ ions. Conditions:

12

[Phos-cycC6] = 0.20 wt% (3.2 mM), [BPmoc-F3] = 0.30 wt% (4.7 mM), [SOx] = 2.0 mg/mL

13

(30 µM), [Ca2+] = 3.2 mM, 100 mM MES buffer (pH 7.0), 25 °C. (e) Fluorescent recovery

14

profiles of Phos-cycC6 fibers stained with Alexa546-cycC6 after photobleaching in

hydrogel

by

PAF.

(Phos-cycC6/BPmoc-F3/SOx/Ca2+)

(b)

(right)

12 ACS Paragon Plus Environment

Optical hydrogels

image

of

stained

the with

Page 13 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

Phos-cycC6/BPmoc-F3/SOx hydrogels with or without Ca2+ ions. (f) Diffusion coefficients

2

of Phos-cycC6/BPmoc-F3/SOx hydrogel with or without Ca2+ ions determined by FRAP

3

experiments (n = 8). The data represent the mean ± s.d. Conditions: ((e) and (f))

4

[Phos-cycC6] = 0.1 wt% (1.6 mM), [Alexa546-cycC6] = 4 µM, [BPmoc-F3] = 0.1 wt% (1.6

5

mM), [BP-OG] = 4 µM, 0.5 mg/mL (7.7 µM), [Ca2+] = 4.9 mM, 100 mM MES buffer (pH

6

7.0), rt.

7 8

The influence of the additional components (SOx and Ca2+ ions) on the

9

orthogonality of the fiber networks was confirmed by in situ CLSM imaging using

10

fluorescent probes, Alexa546-cycC6 and BP-OG (Figure S6)15b. As shown in Figure S9, the

11

CLSM images of the single-fiber networks revealed that the two probes could selectively

12

stain Phos-cycC6 and BPmoc-F3 fibers, respectively, even in the presence of SOx and Ca2+

13

ions. The CLSM images of the SDN hydrogel without SOx and Ca2+ ions clearly showed that

14

BPmoc-F3 and Phos-cycC6 formed into well-entangled self-sorting nanofiber networks

15

(Figure 3c (left), Pearson’s correlation coefficient23, 24: 0.11). The orthogonality of the double

16

network remained intact upon sequential addition of SOx and Ca2+ ions (Figure 3c (right),

17

Pearson’s correlation coefficient: 0.16), suggesting that both SOx and Ca2+ ions did not have

18

crucial impact on the orthogonal fiber networks of BPmoc-F3 and Phos-cycC6 (Figure 3c,

19

S10).

20

The effect of the Ca2+ ions on the Phos-cycC6/BPmoc-F3/SOx hydrogel was

21

evaluated in more detail with dynamic viscoelastic measurement and FRAP analysis. The

22

storage modulus (G’) of Phos-cycC6/BPmoc-F3/SOx hydrogel was increased from 5.5 kPa to

23

22.9 kPa by the addition of Ca2+ ions, indicating that the Ca2+ ions were bound to the

24

Phos-cycC6 fibers and stabilized the hydrogel (Figure 3d, S11, S12). The Ca2+ ions can not

25

only bind to Phos-cycC6, but to BPmoc-F3 fibers in this multicomponent hydrogel. However 13 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

it is conceivable that the Ca2+ ions were mainly bound to Phos-cycC6 fibers, because the

2

carboxylic acid groups of BPmoc-F3 have a smaller affinity to Ca2+ ions than the phosphate

3

group of Phos-cycC6 (Kd of carboxylic acid: 250 mM, phosphate group: 32 mM)25, 26. The

4

FRAP experiments showed that the diffusion coefficient of the Phos-cycC6 fibers in the

5

Phos-cycC6/BPmocF3/SOx hydrogel was decreased from (3.8 ± 2.2) × 10–2 µm2/s to (0.72 ±

6

0.10) × 10–2 µm2/s by the addition of Ca2+ ions (Figure 3e, 3f, S13). This suggested that a

7

sufficient amount of Ca2+ ions bound to the Phos-cycC6 fibers in this multicomponent

8

hydrogel.

9

As a control experiment, we conducted a one-step mixing protocol for the

10

preparation of this multicomponent hydrogel (Figure 4a). The powders of two gelators

11

(Phos-cycC6 and BPmoc-F3) and Ca2+ ions were mixed in a buffer solution, followed by

12

heating of the mixture and subsequent incubation at 25 °C. This one-step mixing protocol did

13

not afford hydrogels but resulted in an inhomogeneous suspension containing precipitates

14

(Figure 4a). The CLSM observation of this suspension showed co-assembled spherical

15

aggregates together with fibers that were selectively stained with BP-OG (Figure 4b). Given

16

the spherical aggregates were stained by both the fluorescent probes, Phos-cycC6 and

17

BPmoc-F3 were randomly mixed in the presence of Ca2+ ions during the one-step mixing

18

protocol, resulting in undesired mixtures. It was apparent that hybridization of SOx should be

19

performed without heating to avoid thermal denaturation (The enzyme activity of the SOx

20

was completely lost at 45 °C for 10 min incubation27). Overall, it was concluded that the PAF

21

protocol was invaluable for preparing a well-ordered multicomponent hydrogel.

14 ACS Paragon Plus Environment

Page 14 of 28

Page 15 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1 2

Figure 4. (a) Schematic representation of the one-step mixing protocol and an optical image

3

of the obtained inhomogeneous suspension. (b) CLSM images of the inhomogeneous

4

suspension prepared by a one-step mixing protocol. Left, middle, and right images show

5

Alexa546-cycC6, BP-OG, and the merged channels, respectively. Scale bar: 20 µm.

6

Conditions: [Phos-cycC6] = 0.2 wt% (3.2 mM), [Alexa546-cycC6] = 4 µM, [BPmoc-F3] =

7

0.075 wt% (1.2 mM), [BP-OG] = 4 µM, [Ca2+] = 1.3 mM, 100 mM MES buffer (pH 7.0),

8

25 °C (a), rt (b).

9

15 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Controlled protein release from the multicomponent hydrogel in AND logic gate fashion

2

by ATP and sarcosine

3

Because the two biomolecule-responsive systems were hybridized in a hydrogel through the

4

PAF protocol, it was rationally expected that each fiber in the multicomponent hydrogel

5

responds to the corresponding stimuli, that is Phos-cycC6/Ca2+ to ATP and BPmoc-F3/SOx

6

to sarcosine. Therefore, the multicomponent hydrogel should exhibit a gel–sol transition in

7

response to ATP and sarcosine in an AND logic gate fashion (Figure 5a)16. Indeed, when

8

only one stimulus, either ATP or sarcosine, was added to the multicomponent hydrogel, the

9

gel–sol transition did not occur because the single gel fiber network remained intact (Figure

10

5a, S14)28. Conversely, the addition of both ATP and sarcosine induced the gel–sol transition

11

(in an AND logic gate fashion). As shown in Figure S11, S12 and S15, the rheological

12

properties supported the response behavior observed by the naked eye. The initial G’ value of

13

the multicomponent hydrogel was 22.9 kPa, which decreased to 8.6 kPa or 5.4 kPa after the

14

addition of ATP or sarcosine, respectively. Furthermore, the concurrent addition of the two

15

molecules significantly decreased the G’ value to 1.9 kPa (Figure S11, S12, S15)29. These

16

results indicated that the two biomolecule-responsive systems independently work in the

17

multicomponent hydrogel.

16 ACS Paragon Plus Environment

Page 16 of 28

Page 17 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1 2

Figure 5. (a) AND logic gate-type response (gel–sol transition) of the multicomponent

3

hydrogel to ATP and sarcosine. (b) Schematic representation of controlled Fl-IgG release

4

experiments from the multicomponent hydrogel. (c) Photos of the multicomponent hydrogels

5

encapsulating Fl-IgG before and after addition of ATP and/or sarcosine. The photos were

6

taken under UV light in a dark room. (d) Fl-IgG release profiles from the multicomponent

7

hydrogel under various conditions (n = 3). The data represent the mean ± s.d. Conditions: (a)

8

[Phos-cycC6] = 0.2 wt% (3.2 mM), [BPmoc-F3] = 0.075 wt% (1.2 mM), [SOx] = 0.5 mg/mL

9

(7.7 µM), [Ca2+] = 1.3 mM, [ATP] = 9.7 mM, [Sarcosine] = 3.5 mM, 100 mM MES buffer

10

(pH 7.0), 25 °C. ((c) and (d)) [Phos-cycC6] = 0.2 wt% (3.2 mM), [BPmoc-F3] = 0.075 wt%

11

(1.2 mM), [SOx] = 1.0 mg/mL (15 µM), [Ca2+] = 1.3 mM, [Fl-IgG] = 133 nM, [ATP] = 9.7

12

mM

13

V(gel) : V(buffer) = 1: 4.5, 100 mM MES buffer (pH 7.0), rt.

(buffer),

[Sarcosine]

=

14

17 ACS Paragon Plus Environment

3.5

mM

(buffer),

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Finally, the AND-type gel–sol response was applied to the controlled release of an

2

antibody embedded in the multicomponent hydrogel (Figure 5b). The multicomponent

3

hydrogel encapsulating fluorescein-labeled immunoglobulin G (Fl-IgG: 133 nM) was

4

prepared in a quartz cell and then an aqueous buffer solution was poured on the hydrogel.

5

Subsequently, ATP and/or sarcosine were added to the supernatant aqueous solution. The

6

Fl-IgG release rates from the hydrogel to the aqueous solution were evaluated by the

7

fluorescence intensities of the aqueous buffer solution (Figure 5c, 5d, S19). Without any

8

stimuli, the Fl-IgG release was very slow (Release rate: 16 ± 6% for 12 h), indicating the

9

efficient Fl-IgG retention of the multicomponent hydrogel. A similar slow release of 24 ± 4%

10

and 15 ± 1% was observed 12 h after the addition of the single stimulus, ATP or sarcosine,

11

respectively. Although the mesh-size of the multicomponent hydrogel network should be

12

expanded through modulation of the one-fiber network by the corresponding stimulus, the

13

impact on the Fl-IgG release was not so crucial. In contrast, an enhanced Fl-IgG release was

14

observed in the presence of both ATP and sarcosine; 83 ± 5% of Fl-IgG was released from

15

the multicomponent hydrogel after 12 h, as shown in Figure 5c, d. The release rate of Fl-IgG

16

was 3.5 and 5.5-fold larger than those using the single stimulus, ATP and sarcosine,

17

respectively, which clearly implied that the AND logic gate mode of antibody release was

18

accomplished in response to ATP and sarcosine in this multicomponent hydrogel. These

19

results suggested that the release rate of FL-IgG was mainly controlled by the state (gel or

20

sol) of the embedded matrix in this case, rather than the rheological properties. Conversely,

21

the inhomogeneous suspension prepared by the one-step mixing protocol showed an

22

immediate release of Fl-IgG even in the absence of any stimuli (Figure S20), revealing that

23

the PAF protocol was essential for such a sophisticated functionalization. 18 ACS Paragon Plus Environment

Page 18 of 28

Page 19 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

Conclusion

2

A unique multicomponent hydrogel composed of a dual-biomolecule-responsive system was

3

prepared through a post-assembly fabrication (PAF) protocol. The programmed hybridization

4

allowed us to produce a hydrogel with a designer AND logic gate mode gel–sol transition in

5

response to two biologically important molecules (ATP and sarcosine). Such a well-ordered

6

multicomponent hydrogel was not obtained with a simple one-step mixing protocol. To the

7

best of our knowledge, this is the first multicomponent hydrogel based on an SDN whose

8

function was positively modified by PAF. This fabrication method relying on the self-sorting

9

and PAF protocol should be more powerful for the development of novel intelligent materials,

10

including more multiple components. We believe that this strategy could open up next

11

generation smart materials for a variety of applications such as therapy, diagnosis, drug

12

delivery systems, and regenerative medicine.

13

19 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Associated content

2

Methods

3

The materials, instruments, experimental methods and syntheses of the compounds are

4

described in supporting information. The experimental conditions (concentration, pH and

5

temperature) are described in the figure captions.

6 7

Author information

8

Corresponding author

9

*E-mail: [email protected]

10

ORCID

11

Hajime Shigemitsu: 0000-0002-3104-049X

12

Ryou Kubota: 0000-0001-8112-8169

13

Itaru Hamachi: 0000-0002-3327-3916

14

Acknowledgements

15

This work was supported by a Grant-in-Aid for Scientific Research on Innovative Areas

16

“Chemistry for Multimolecular Crowding Biosystems” (JSPS KAKENHI Grant 17H06348),

17

the Japan Science and Technology Agency (JST) Core Research for Evolutional Science and

18

Technology (CREST), and JST ERATO Grant Number JPMJER1802 to I.H., and by a

19

Grant-in-Aid for Young Scientists (JSPS KAKENHI Grant 18K14333) to R.K. H.S.

20

acknowledge JSPS Research Fellowships for Young Scientists (16J10716). The authors

21

acknowledge financial support from The Mitsubishi Foundation.

22

Competing financial interests

23

The authors declare no competing financial interests.

24

20 ACS Paragon Plus Environment

Page 20 of 28

Page 21 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

References

2

1.

(a) Li, J.; Kuang, Y.; Gao, Y.; Du, X.; Shi, J.; Xu, B. D-Amino Acids Boost the

3

Selectivity and Confer Supramolecular Hydrogels of a Nonsteroidal Anti-Inflammatory

4

Drug (NSAID). J. Am. Chem. Soc. 2013, 135, 542-545. (b) Webber, M. J.; Matson, J.

5

B.; Tamboli, V. K.; Stupp, S. I. Controlled release of dexamethasone from peptide

6

nanofiber gels to modulate inflammatory response. Biomaterials. 2012, 33, 6823-6832.

7

(c) Koutsopoulos, S.; Unsworth, L. D.; Nagai, Y.; Zhang, S. Controlled release of

8

functional proteins through designer self-assembling peptide nanofiber hydrogel

9

scaffold. Proc. Natl. Acad. Sci. U.S.A. 2009, 106, 4623-4628.

10

2.

(a) Alakpa, E. V.; Jayawarna, V.; Lampel, A.; Burgess, K. V.; West, C. C.; Bakker, S. C.

11

J.; Roy, S.; Javid, N.; Fleming, S.; Lamprou, D. A.; Yang, J.; Miller, A.; Urquhart, A. J.;

12

Frederix, P. W. J. M.; Hunt, N. T.; Péault, B.; Ulijn, R. V.; Dalby, M. J. Tunable

13

supramolecular hydrogels for selection of lineage-guiding metabolites in stem cell

14

cultures. Chem. 2016, 1, 298–319. (b) Webber, M. J.; Appel, E. A.; Meijer, E. W.;

15

Langer, R. Supramolecular biomaterials. Nat. Mater. 2016, 15, 13–26.

16

3.

17 18

peptide/protein array using supramolecular hydrogel. Nat. Mater. 2004, 3, 58-64. 4.

19 20

Kiyonaka, S.; Sada, K.; Yoshimura, I.; Shinkai, S.; Kato, N.; Hamachi, I. Semi-wet

Draper, E. R.; Adams, D. J. How should multicomponent supramolecular gels be characterized? Chem. Soc. Rev. 2018, 47, 3395-3405.

5.

Boekhoven, J.; Koot, M.; Wezendonk, T. A.; Eelkema, R.; van Esch, J. H. A self

21

assembled delivery platform with post-production tunable release rate. J. Am. Chem. Soc.

22

2012, 134, 12908–12911.

21 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

6.

(a) Ikeda, M.; Yoshii, T.; Matsui, T.; Tanida, T.; Komatsu, H.; Hamachi, I.;

2

Montmorillonite–supramolecular hydrogel hybrid for fluorocolorimetric sensing of

3

polyamines. J. Am. Chem. Soc. 2011, 133, 1670–1673. (b) Wada, A.; Tamaru, S.; Ikeda,

4

M.; Hamachi, I. MCM–Enzyme–supramolecular hydrogel hybrid as a fluorescenec

5

sensing material for polyanions of biological significance. J. Am. Chem. Soc. 2009, 131,

6

5321–5330.

7

7.

(a) Ikeda, M.; Tanida, T.; Yoshii, T.; Hamachi, I. Rational molecular design of

8

stimulus-responsive supramolecular hydrogel based on dipeptides. Adv. Mater. 2011, 23,

9

2819–2822. (b) Ikeda, M.; Tanida, T.; Yoshii, T.; Kurotani, K.; Onogi, S.; Urayama, K.;

10

Hamachi, I. Installing logic-gate responses to a variety of biological substances in

11

supramolecular hydrogel–enzyme hybrids. Nat. Chem. 2014, 6, 511–518. (c) Shigemitsu,

12

H.; Fujisaku, T.; Onogi, S.; Yoshii, T.; Ikeda, M.; Hamachi, I. Preparation of

13

supramolecular hydrogel-enzyme hybrids exhibiting biomolecule-responsive gel

14

degradation. Nat. protocol. 2016, 11, 1744-1756.

15

8.

Yoshii, T.; Onogi, S.; Shigemitsu, H.; Hamachi, I. Chemically reactive supramolecular

16

hydrogel coupled with a signal amplification system for enhanced analyte sensitivity. J.

17

Am. Chem. Soc. 2015, 137, 3360–3365.

18

9.

Shigemitsu, H.; Hamachi, I. Design strategies of stimuli-responsive supramolecular

19

hydrogels relying on structural analyses and cell-mimicking approaches. Acc. Chem. Res.

20

2017, 50, 740–750.

21

10. (a) Raeburn, J.; Adams, D. J. Multicomponent low molecular weight gelators. Chem.

22

Commun. 2015, 51, 5170–5180. (b) Buerkle L. E.; Rowan, S. J. Supramolecular gels

23

formed from multi-component low molecular weight species. Chem. Soc. Rev. 2012, 41, 22 ACS Paragon Plus Environment

Page 22 of 28

Page 23 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

6089–6102. (c) Cross, E. R.; Sproules, S.; Schweins, R.; Draper, E. R.; Adams, D. J.

2

Controlled tuning of the properties in optoelectronic self-sorted gels. J. Am. Chem. Soc.

3

2018, 140, 8667–8670.

4

11. Morris, K. L.; Chen, L.; Raeburn, J.; Sellick, O. R.; Cotanda, P.; Paul, A.; Griffiths, P.

5

C.; King, S. M.; O’Reilly, R. K.; Serpell, L. C.; Adams, D. J. Chemically programmed

6

self-sorting of gelator networks. Nat. Commun. 2013, 4, 1480.

7 8 9

12. Draper, E. R.; Eden, E. G. B.; McDonald, T. O.; Adams, D. J. Spatially resolved multicomponent gels. Nat. Chem. 2015, 7, 848–852. 13. (a) Cornwell, D. J.; Daubney. O. J.; Smith, D. K. Photopatterned multidomain gels:

10

multi-component

self-assembled

11

1,3:2,4-Dibenzylidene-D-sorbitol derivatives. J. Am. Chem. Soc. 2015, 137, 15486–

12

15492. (b) Hirst, A. R.; Escuder, B.; Miravet, J. F.; Smith, D. K. High-tech applications

13

of

14

regenerative medicine to electronic devices. Angew. Chem. Int. Ed. 2008, 47, 8002–

15

8018.

self-assembling

hydrogels

supramolecular

based

nanostructured

on

partially

gel-phase

self-sorting

materials:

from

16

14. Shigemitsu, H.; Fujisaku, T.; Tanaka, W.; Kubota, R.; Minami, S.; Urayama, K.;

17

Hamachi, I. An adaptive supramolecular hydrogel comprising self-sorting double

18

nanofibre networks. Nat. Nanotechnol. 2018, 13, 165–172.

19

15. (a) Boekhoven, J.; Brizard, A. M.; Stuart, M. C. A.; Florusse, L.; Raffy, G.; Guerzo, A.

20

D.; van Esch, J. H. Bio-inspired supramolecular materials by orthogonal self-assembly

21

of hydrogelators and phospholipids. Chem. Sci. 2016, 7, 6021–6031. (b) Onogi, S.;

22

Shigemitsu, H.; Yoshii, T.; Tanida, T.; Ikeda, M.; Kubota, R.; Hamachi, I. In situ

23

real-time imaging of self-sorted supramolecular nanofibres. Nat. Chem. 2016, 8, 23 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

743-752. (c) Kubota, R.; Liu, S.; Shigemitsu, H.; Nakamura, K.; Tanaka, W.; Ikeda, M.;

2

Hamachi, I. Imaging-Based Study on Control Factors over Self-Sorting of

3

Supramolecular Nanofibers Formed from Peptide- and Lipid-type Hydrogelators.

4

Bioconjugate Chem. 2018, 29, 2058-2067.

5

16. (a) Tregubov, A. A.; Nikitin, P. I.; Nikitin, M. P. Advanced Smart Nanomaterials with

6

Integrated Logic-Gating and Biocomputing: Dawn of Theranostic Nanorobots. Chem.

7

Rev. 2018, 118, 10294−10348. (b) Badeau, B. A.; Comerford, M. P.; Arakawa, C. K.;

8

Shadish, J. A.; DeForest, C. A. Engineered modular biomaterial logic gates for

9

environmentally triggered therapeutic delivery. Nat. Chem. 2018, 10, 251–258.

10

17. (a) Sangiambut, S.; Channon, K.; Thomson, N. M.; Sato, S.; Tsuge, T.; Doi, Y.;

11

Sivaniah, E. A robust route to enzymatically functional, hierarchically self-assembled

12

peptide frameworks. Adv. Mater. 2013, 25, 2661–2665. (b) Khan, S.; Sur, S.; Dankers, P.

13

Y. W.; da Silva, R. M. P.; Boekhoven, J.; Poor, T. A.; Stupp, S. I. Post-assembly

14

functionalization of supramolecular nanostructures with bioactive peptides and

15

fluorescent proteins by native chemical ligation. Bioconjugate Chem. 2014, 25, 707−717.

16

(c) DiMaio, J. T. M.; Raymond, D. M.; Nilsson, B. L.; Display of functional proteins on

17

supramolecular peptide nanofibrils using a split-protein strategy. Org. Biomol. Chem.

18

2017, 15, 5279-5283.

19

18. Komatsu, H.; Matsumoto, S.; Tamaru, S.; Kaneko, K.; Ikeda, M. and Hamachi, I.

20

Supramolecular hydrogel exhibiting four basic logic gate functions to fine-tune

21

substance release. J. Am. Chem. Soc. 2009, 131, 5580–5585.

22

19. BPmoc-F3/SOx hydrogel was fabricated by addition of SOx to a BPmoc-F3 hydrogel.

23

Because SOx can produce hydrogen peroxide (H2O2) during oxidation of sarcosine, the 24 ACS Paragon Plus Environment

Page 24 of 28

Page 25 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

H2O2-sensitive BPmoc-F3 was decomposed by addition of sarcosine (Figure S1). We

2

confirmed the response of the BPmoc-F3/SOx hydrogel to sarcosine at room

3

temperature. As shown in Figure S1b, the BPmoc-F3/SOx hydrogel changed to the sol

4

state 2 h after addition of sarcosine (3 eq. of BPmoc-F3). The high performance liquid

5

chromatography (HPLC) analysis revealed that 90% of BPmoc-F3 molecules were

6

decomposed and the resultant BPmoc-F3 concentration was below the critical gelation

7

concentration (0.05 wt%) (Figure S1c).

8 9

20. Walaas, E. Stability Constants of Metal Complexes with Mononucleotides. Acta. Chem. Scand. 1958, 12, 528-536.

10

21. (a) Tamaru, S.; Ikeda, M.; Shimidzu, Y.; Matsumoto, S.; Takeuchi, S.; Hamachi, I.

11

Fluidic supramolecular nano- and microfibres as molecular rails for regulated movement

12

of nanosubstances. Nat. Commun. 2010, 1, 20. (b) Thompson, N. L.; Burghardt, T. P.;

13

Axelrod, D. Measuring surface dynamics of biomolecules by total internal reflection

14

fluorescence with photobleaching recovery or correlation spectroscopy. Biophys. J. 1981,

15

33, 435–454. (c) Jayaraman, K.; Okamoto, K.; Son, S. J.; Luckett, C.; Gopalani, A. H.;

16

Lee, S. B.; English, D. S. Observing capillarity in hydrophobic silica nanotubes. J. Am.

17

Chem. Soc. 2005, 127, 17385–17392.

18 19

22. The SDN (Phos-cycC6/BPmoc-F3) hydrogel did not show swelling/contraction behaviors by the addition of SOx and Ca2+ ions (Figure S8).

20

23. The Pearson’s correlation coefficient indicates the degree of the linear correlation

21

between the two different channel images. In most case, if gelators are orthogonally

22

self-assembled, the values of Pearson’s correlation coefficients show lower than 0.3.

25 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

24. Dunn, K. W.; Kamocka, M. M.; and McDonald, J. H. A practical guide to evaluating

2

colocalization in biological microscopy. Am. J. Physiol. Cell Physiol. 2011, 300,

3

C723−C742.

4

25. (a) Saha, A.; Saha, N.; Ji, L.; Zhao, J.; Gregáň, F.; Sajadi, S. A. A.; Song, B.; Sigel, H.

5

Stability of metal ion complexes formed with methyl phosphate and hydrogen phosphate.

6

J. Biol. Inorg. Chem. 1996, 1, 231-238. (b) Smith, R. M.; Martell, A. E. Critical stability

7

constants, enthalpies and entropies for the formation of metal complexes of

8

aminopolycarboxylic acids and carboxylic acids. Sci. Total. Environ. 1987, 64, 125-147.

9

26. The Kd values of acetic acid and methyl phosphate in aqueous solution at an ionic

10 11 12 13 14

strength of 0.1 M and 25 °C were referred. 27. Suzuki, M.; Purification and Some Properties of Sarcosine Oxidase from Corynebacterium sp. U-96. J. Biochem. 1981, 89, 599-607 28. The multicomponent hydrogel did not show swelling/contraction behaviors after the addition of ATP or sarcosine (Figure S14).

15

29. To evaluate the gel-sol transition more quantitatively, we tried to measure the

16

rheological property of the multicomponent hydrogel under the same condition with the

17

tube inversion test (Figure S16-18). The multicomponent hydrogel showed rheological

18

properties of gel state, i.e., frequency-independent G’ (Figure S17a), and G’ >> G’’ (G’

19

= 1082 Pa, G’’ = 174 Pa, Figure S18). On the other hand, the viscous solution obtained

20

after addition of both stimuli (ATP and sarcosine) showed very small G’ value (29 Pa)

21

which may be consistent with the naked eye observation. The tan δ (tan (G’’/G’)) value

22

of the viscous solution was 2.0-fold larger than that of the initial multicomponent

23

hydrogel, indicating the multicomponent hydrogel came close to the sol state by addition 26 ACS Paragon Plus Environment

Page 26 of 28

Page 27 of 28 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Journal of the American Chemical Society

1

of the both stimuli, while the G’ value is still larger than G’’. The discrepancy between

2

the rheological data (larger G’ value than G’’) and visual results would be derived from

3

the residual gel fragments in the sol.

4

27 ACS Paragon Plus Environment

Journal of the American Chemical Society 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

TOC

2

28 ACS Paragon Plus Environment

Page 28 of 28