Post-Treatment of Silicon Nanocrystals Produced ... - ACS Publications

Jan 11, 2012 - The colloidal Si-NCs and post-treated Si-NCs solutions present strong absorption edge shifts ..... İlker Doğan , Mauritius C. M. van ...
0 downloads 0 Views 958KB Size
Article pubs.acs.org/JPCC

Post-Treatment of Silicon Nanocrystals Produced by Ultra-Short Pulsed Laser Ablation in Liquid: Toward Blue Luminescent Nanocrystal Generation Sabri Alkis,†,‡ Ali K. Okyay,†,‡ and Bülend Ortaç*,† †

UNAM Institute of Materials Science and Nanotechnology and ‡Department of Electrical and Electronics Engineering, Bilkent University, Bilkent 06800 Ankara, Turkey ABSTRACT: Blue luminescent colloidal silicon nanocrystals (Si-NCs) were produced in a two-stage process. In the first step, synthesis of Si-NCs was achieved by femtosecond pulsed laser ablation of a silicon wafer, which was immersed in deionized water. The size and the structural and the chemical characteristics of colloidal Si-NCs were investigated by TEM and EDAX analyses, and it is found out that the Si-NCs are in spherical shape and the particle diameters are in the range of 5−100 nm. In the second step, ultrasonic waves and filtering chemical-free post-treatment of colloidal Si-NCs solution was performed to reduce the particle size. High-resolution TEM (HRTEM) studies on post-treated colloidal solution clearly show that small (1−5.5 nm in diameter) Si-NCs were successfully produced. Raman spectroscopy results clearly confirms the generation of Si nanoparticles in the crystalline nature, and the Raman scattering study of post-treated Si-NCs confirms the reduction of the particle size. The UV−vis absorption and photoluminescence (PL) spectroscopy studies elucidate the quantum confinement effect of Si-NCs on the optical properties. The colloidal Si-NCs and post-treated Si-NCs solutions present strong absorption edge shifts toward UV region. Broadband PL emission behavior is observed for the initial colloidal Si-NCs, and the PL spectrum of post-treated Si-NCs presents a blue-shifted broadband PL emission behavior due to the particle size reduction effect.

1. INTRODUCTION Recent reports show the staggering prospect of nanocrystal quantum dot (NQD)-based nanophosphors for light conversion and color engineering in solid-state lighting and backlighting industries. However, cadmium in efficient NQDs makes them unsuitable for use in environment friendly devices. Providing cadmium-free NQDs in amounts sufficient for the mass production of color-conversion light-emitting diodes (LEDs) is an area in which further research and development effort is needed.1 Silicon, on the other hand, is abundant in nature and environment friendly. In recent years, ultrasmall Silicon nanoparticles were shown to exhibit strong luminescence properties. Many research efforts focused on different techniques to produce Silicon nanocrystals (Si-NCs) including chemical vapor deposition (CVD), ion implantation, electrochemical etching, and laser ablation. Various techniques to obtain luminescent silicon NCs were demonstrated with limited prospects of mass production. CVD methods are widely used to investigate Silicon nanoparticles.2,3 The nanoparticles are obtained in a host matrix such as SiO2 and Si3N4, and the nanoparticles are isolated from the host matrix through selective chemical removal of the host matrix. High volume of Silicon nanoparticles production is challenging through the CVD methods because it is primarily a surface reaction. Researchers also produced silicon nanoparticles by ion-implantation © 2012 American Chemical Society

of Si species into SiO2 layers, followed by surface annealing and rapid annealing processes.4,5 Nayfeh6,7 reported a high throughput and low-cost method for producing silicon nanoparticles of diameters