Preparation of Magnetic Hollow Molecularly Imprinted Polymers for

Jun 3, 2016 - School of Chemistry and Chemical Engineering, Linyi University, Linyi, Shandong 276005, People's Republic of China. J. Agric. ... When t...
2 downloads 6 Views 2MB Size
Subscriber access provided by UNIV OF NEBRASKA - LINCOLN

Article

Preparation of Magnetic Hollow MIPs for Detection of Triazines in Food Samples Aixiang Wang, Hongzhi Lu, and Shoufang Xu J. Agric. Food Chem., Just Accepted Manuscript • DOI: 10.1021/acs.jafc.6b01197 • Publication Date (Web): 03 Jun 2016 Downloaded from http://pubs.acs.org on June 9, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Journal of Agricultural and Food Chemistry is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 29

Journal of Agricultural and Food Chemistry

Graphical abstract

Magnetic hollow molecularly imprinted polymer (M-H-MIPs) were prepared based on multi-step swelling polymerization followed by post-imprinting in-situ growth magnetic Fe3O4 nanoparticles on the surface of hollow MIPs.

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

1

Preparation of Magnetic Hollow MIPs for Detection of Triazines in Food

2

Samples

3

Aixiang Wang, Hongzhi Lu, Shoufang Xu*

4

School of Chemistry and Chemical Engineering, Linyi University, Linyi 276005,

5

China.

6 7 8

*Corresponding author

9

Tel.: +86 539 8766000; fax: +86 539 8766000.

10

E-mail address: [email protected] (S.F. Xu)

11 12 13 14 15 16 17 18 19 20 21 22

ACS Paragon Plus Environment

Page 2 of 29

Page 3 of 29

Journal of Agricultural and Food Chemistry

23

ABSTRACT

24

Novel magnetic hollow molecularly imprinted polymers (M-H-MIPs) were proposed

25

for highly selective recognition and fast enrichment of triazines in food samples.

26

M-H-MIPs were prepared based on multi-step swelling polymerization followed by

27

in-situ growth of magnetic Fe3O4 nanoparticles on the surface of hollow MIPs.

28

Transmission electron microscopy and scanning electron microscope confirmed the

29

successful immobilization of Fe3O4 nanoparticles on the surface of hollow MIPs.

30

M-H-MIPs could be separated simply using an external magnet. The binding

31

adsorption results indicated that M-H-MIPs displayed high binding capacity and fast

32

mass transfer property and class selective property for triazines. Langmuir isotherm

33

and pseudo-second-order kinetic models fitted the best adsorption models for

34

M-H-MIPs. M-H-MIPs were used to analyze atrazine, simazine, propazine and

35

terbuthylazine in corn, wheat and soybean samples. Satisfactory recoveries were in

36

the range of 80.62%-101.69% and relative standard deviation was lower than 5.2%.

37

Limits of detection from 0.16 to 0.39 µg·L-1 was obtained. When the method was

38

applied to test positive samples that were contaminated with triazines, the results

39

agree well with those obtained from accredited method. Thus, M-H-MIPs based

40

DSPE method proved to be a convenient and practical platform for detection of

41

triazines in food samples.

42 43

KEYWORDS: molecularly imprinted polymers, magnetic hollow MIPs, in-situ

44

growth, triazines, food sample

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

45

INTRODUCTION

46

Molecularly imprinted polymers (MIPs) are a kind of functional polymers which

47

display specific recognition performance to template molecules. Up to date, MIPs

48

have been applied in many field, such as enrichment/separation1-3, electrochemical or

49

optical chemical sensors4-6 and selective photocatalytic degradation7 because of their

50

outstanding selectivity, physical and thermal stability. It should be pointed out that

51

although MIPs enjoy significant benefits and diverse applications, they still

52

confronted with many problems resulted from the highly cross-linked nature of MIPs,

53

such as low binding capacity and slow mass transfer, which limiting its application in

54

rapid detection of trace targets. Many strategies, including surface molecular

55

imprinting8,9, hollow porous MIPs10,11, mesoporous MIPs12-14 and solid phase

56

synthesis method15,16 have been proposed to solve those problems. Among those novel

57

MIPs, hollow MIPs (H-MIPs) have attracted increasingly attentions based on the fact

58

that the holes on the surface and cavities in the core are benefit for mass transfer. The

59

mild preparation conditions make seed swelling polymerization becoming the most

60

commonly used method to prepare monodisperse H-MIPs.

61

In the meanwhile, magnetic MIPs (M-MIPs) are also widely applied to extract

62

targets in complicated matrix based on the fact that they can be isolated conveniently

63

from sample solutions by an external magnet

64

summarized many methods for preparing M-MIPs and the general process involves

65

preparation and surface modification of magnetic nanoparticles, followed by coating

66

MIPs. The common feature of those methods is that surface imprinting technique was

17

. In our previous work18, we have

ACS Paragon Plus Environment

Page 4 of 29

Page 5 of 29

Journal of Agricultural and Food Chemistry

67

adopted using magnetic nanoparticles as cores.

68

Magnetic hollow MIPs (M-H-MIPs) would possess the advantages of both hollow

69

polymers and magnetic separation. However, M-H-MIPs have rarely been reported

70

because the methods for preparing hollow polymers and magnetic polymers are often

71

conflicted. So if magnetic nanoparticles are used as cores, it is hard to form H-MIPs.

72

One feasible way is to immobilize magnetic nanoparticles on the surface of H-MIPs.

73

Ye et al. presented an approach to immobilize Fe3O4 nanoparticles on the surface of

74

MIPs by click reaction19. However, this method involves complicated surface

75

modification process in order to introduce clickable azide groups or alkyne groups

76

onto the surface of Fe3O4 nanoparticles or MIPs. Shi20 reported that Fe3O4 can be

77

immobilized on the surface of MIPs by using glycidilmethacrylate (GMA) as

78

co-monomers during the process of preparation MIPs. The role of GMA, which has

79

an epoxide ring, is to offer potential hydroxyl groups for in situ growth of Fe3O4

80

nanoparticles. Compared to click reaction, this method is easy to control.

81

Inspired by the above mentioned studies, M-H-MIPs for detection of four triazines

82

in food sample were prepared based on multi-step swelling polymerization followed

83

by in-situ growth of magnetic Fe3O4 nanoparticles on the surface of H-MIPs. The

84

as-prepared M-H-MIPs displayed many advantages in enrichment trace targets from

85

complicated sample matrix, such as magnetic separation ability, molecule recognition

86

ability and faster mass transfer ability. The structure of M-H-MIPs were characterized

87

by scanning electron microscopy (SEM) and transmission electron microscopy (TEM).

88

Binding capacity of M-H-MIPs, including static binding, dynamic binding and

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Page 6 of 29

89

selective recognition ability were investigated detailed. The performances of

90

M-H-MIPs for specific separation and enrichment of triazines in corn, soybean and

91

wheat samples were studied. Under optimal conditions, the recoveries of the

92

established methods were satisfactory. Moreover, M-H-MIPs were successfully

93

applied to assess triazine herbicide residues in positive food samples. And the values

94

agree with those obtained using the accredited classic method. This study provided an

95

efficient, selective, and accurate method for analyzing triazine herbicide at trace

96

abundance in multiple media.

97

EXPERIMENTAL SECTION

98 99

Materials and Chemicals. Divinylbenzene (DVB), methacrylic acid (MAA) and glycidilmethacrylate

(GMA)

were

from

Sigma-Aldrich

(Shanghai,

China).

100

FeCl3·6H2O, FeCl2·4H2O, dibutyl phthalate (DBP), benzoyl peroxide (BPO), styrene,

101

polyvinylpyrrolidone (PVP), and sodium dodecyl sulfate (SDS) were obtained from

102

Tianjin Chemical Reagents Company (Tianjin, China). Atrazine, propazine, simazine

103

and terbuthylazine were obtained from Binzhou Agricultural Technology Co., Ltd.

104

(Shandong, China). Acetonitrile (ACN) used as HPLC mobile phase was from Merck

105

(Darmstadt, Germany). Ultra-pure water (18.2 MΩ·cm-1 specific resistance) was

106

self-prepared in laboratory by Pall Cascada water system (New York, USA).

107

Stock solutions containing 100 mg·L-1 of four kinds of triazines were prepared by

108

dissolving the standards into ACN. Diluting the stock solutions with ACN to prepare

109

working solutions. Both stock and working solutions were stored in refrigerator.

110

Instruments and Analytical Methods. Transmission electron microscopy (TEM;

ACS Paragon Plus Environment

Page 7 of 29

Journal of Agricultural and Food Chemistry

111

JEOL, JEM-1230, Japan) and scanning electron microscope (SEM, Hitachi S-4800

112

FE-SEM) were employed for morphological observation. A vibration sample

113

magnetometer (VSM7307, Lake Shore, USA) was employed for the measurement of

114

magnetization in at room temperature. HPLC equipped with a C18 ODS column (250

115

mm×4.6 mm, 5 mm) and UV detector (Elite Instrument Inc., China) was used for

116

quantitative analysis of each pollutants with conditions for trizaines as follows:

117

mobile phase, ACN: water (48: 52, v/v) with flow rate at 1.0 mL·min-1; injection

118

volume 20 µL with UV detection at 220 nm; room temperature.

119

Preparation of M-H-MIPs. The process for preparation of M-H-MIPs was

120

composed of the following steps: preparation of H-MIPs; epoxide ring opening and

121

immobilization of Fe3O4 on H-MIPs. First, H-MIPs were prepared using seed

122

swelling polymerization method as our previous work11 with minor modification. The

123

specific process was as follows: 0.2 g monodispersed polystyrene seeds prepared by

124

dispersion polymerization, 0.125 g SDS and 50 mL water were mixed to form

125

homogenous emulsion, then followed by three steps swelling. 0.7 mL DBP was used

126

for the first step swelling, followed by the second step swelling with the mixture of 10

127

mL toluene, 0.344 mL MAA, 0.413 mL GMA and 0.215g atrazine, then the third step

128

swelling by 60 mg BPO and 4.0 mL DVB. After three-step swelling, polymerization

129

was carried out at 80 oC for 1 day. The polymers were washed with dichloromethane

130

and methanol to remove polystyrene seeds and template atrazine. Finally, H-MIPs

131

were prepared.

132

Then epoxide rings on the surface of H-MIPs were opened with the help of

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

133

perchloric acid. The specific process was as follows: 400 mg H-MIPs prepared above

134

were poured into 25 mL 10% perchloric acid water solution followed by stirring at 25

135

o

136

obtained.

C for 24 h. After filtration, washing and drying, H-MIPs with 1,2-diol groups were

137

At last, M-H-MIPs were prepared by coprecipitation of Fe2+ and Fe3+ on the surface

138

of H-MIPs with 1,2-diol groups according to previous literatures20. Briefly, 200 mg

139

H-MIPs with 1,2-diolgroups, 0.01 mmol FeCl2·4H2O and 0.02 mmol FeCl3·6H2O

140

were charged into 20 mL methanol/water (1/4, v/v) solution. The mixture was

141

dispersed homogeneous with the help of ultrasonic wave and then purged with N2 to

142

remove O2. After increasing the temperature to 80 oC, 3 mL NH3·H2O was dropwise

143

added, and the reaction was carried out at 80 oC in N2 atmosphere for 1 h under

144

continuously stirring. At last, M-H-MIPs were collected magnetically, washed with

145

ethanol and water repeatedly, and then dried to constant weights. Using the same

146

procedures, magnetic hollow porous non imprinted polymers (M-H-NIPs) were

147

prepared but without template atrazine.

148

Binding Property of the M-H-MIPs. Static adsorption, kinetic adsorption and

149

selective binding were carried out to characterize the specific molecular binding

150

properties of M-H-MIPs. For static adsorption capacity, 20 mg M-H-MIPs particles

151

were dispersed uniformly into 2.0 mL atrazine/ACN solution varying from 0.5 to 70

152

mg·L−1. After adsorption at room temperature for 1 day, the mixture was separated

153

and supernatant was detected by HPLC. The static binding capacity can be calculated

154

using the initial and final concentration of atrazine. Meanwhile, the dynamic binding

ACS Paragon Plus Environment

Page 8 of 29

Page 9 of 29

Journal of Agricultural and Food Chemistry

155

cure was tested by detection the temporal amount of atrazine when fixed the initial

156

concentration of atrazine at 50 mg·L−1. Selectivity adsorption ability was evaluated

157

using simazine, propazine and terbuthylazine as structural analogs while furazolidone

158

and carbendazim as control.

159

Analysis of Real Food Samples by Dispersive Solid Phase Extraction.

160

M-H-MIPs were applied to extract four triazines, including atrazine, propazine,

161

simazine and terbuthylazine, from corn, wheat and soybean samples by dispersive

162

solid phase extraction (DSPE) method. Dried corn, wheat and soybean samples were

163

purchased from local market and prepared as previous method21. Briefly, 50 g crushed

164

corn, soybean or wheat and 100 mL ACN were mixed and incubated for 8 h in order

165

to retrieve triazines herbicide. As no triazines was detected from those three samples,

166

then spiked experiment was carried out. Nine spiked samples were prepared by

167

adding the mixture standards of atrazine, simazine, propazine and terbuthylazine into

168

corn, wheat and soybean extraction solutions with the final concentration at 1.0, 5.0

169

and 50 µg·L-1, respectively. The specific process for DSPE was as follows. After

170

condition with 5.0 mL methanol, 600 mg M-H-MIPs were added into 100 mL spiked

171

solution followed by ultrasound-assisted extraction for 15 min. Then M-H-MIPs were

172

separated and washed with 5.0 mL ACN before eluted by 5.0 mL 1% acetic acid

173

acidified methanol. The eluate was concentrated with the help of nitrogen blowing,

174

and redissolved into 0.2 mL ACN for further HPLC analysis.

175

RESULTS AND DISCUSSION

176

Preparation and Characterization of M-H-MIPs. Hollow polymers have

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

177

significant advantages in increasing binding capacity and accelerating mass transfer.

178

Magnetic property is facility for rapid and efficient separation. So in this work, we

179

prepared magnetic hollow MIPs in order to integrate the separation ability of Fe3O4

180

particles and faster mass transfer ability of hollow polymer into one system. Unlike

181

embedding Fe3O4 into MIPs as core, Fe3O4 nanoparticles were immobilized on the

182

surface of H-MIPs by in situ growth method. The synthesis procedure for atrazine

183

imprinted M-H-MIPs was illustrated in Figure 1, which involved three successive

184

steps: H-MIPs preparation, epoxide ring opening and Fe3O4 immobilization. First,

185

H-MIPs were prepared by multi-step swelling polymerization as our previous work11,

186

using polystyrene as seeds, toluene as porogen, atrazine as template, MAA as

187

functional monomer and DVB as cross-linker. To facilitate the growth of magnetic

188

nanoparticles on the surface of H-MIPs, GMA was used as co-functional monomer.

189

Epoxy bond opening with the help of HClO4 provided a hydroxyl-rich

190

microenvironment on the surface of H-MIPs, in which Fe3O4 were prior to growth.

191

Then the last step was immobilization of Fe3O4 by in situ growth method based on the

192

cooperation of Fe3+ and Fe2+ under base medium in N2 atmosphere.

193

The key point throughout the preparation process is the amount of GMA. Little

194

GMA would result in insufficient hydroxyl to induce the growth of the magnetic

195

particles on the surface of hollow MIPs. On the contrary, too much GMA would cause

196

excessive magnetic particles, and the binding capacity of M-H-MIPs would be

197

reduced. In this work, optimum amount of GMA was examined using magnetic

198

property and binding capacity as evaluation index. The amount of functional

ACS Paragon Plus Environment

Page 10 of 29

Page 11 of 29

Journal of Agricultural and Food Chemistry

199

monomer MAA was fixed as 0.344 mL while changing MAA/GMA (v/v) ratio from 1:

200

0.2 to 1: 2.0. It was found that when the ratio is less than 1: 0.6, magnetic particles

201

were difficult to grow on the surface of hollow MIPs. When the ratio is greater than 1:

202

1.5, there would be a large number of magnetic particles covering the surface of the

203

polymer, which resulted in lower binding capacity. Finally, the optimum ratio of

204

MAA/GMA was 1: 1.2.

205

The preparation procedure was estimated by TEM and SEM. Figure 2 showed the

206

morphology of polystyrene seeds, H-MIPs and M-H-MIPs. Regular sphere

207

polystyrene seeds were monodispersed with diameter about 850 nm. Hollow structure

208

can be formed by multi-step swelling polymerization, which were clearly indicated by

209

Fig. 2B. The diameter of H-MIPs was about 1.8 µm and the surface of H-MIPs was

210

smooth. After immobilizing Fe3O4 nanoparticles, the surface of M-H-MIPs became

211

rough and the diameter displayed a slight increase. TEM and SEM images provided a

212

powerful evidence to confirm the successfully preparation process.

213

For the H-MIPs and M-H-MIPs, the surface area was studied using the BET

214

adsorption method. The BET surface area of M-H-MIPs was about 357 m2·g-1, which

215

was higher than H-MIPs of 271 m2·g-1. The larger BET surface area probably resulted

216

from the magnetic nanoparticles immobilized on the rough surface of M-H-MIPs.

217

The magnetic separation ability of M-H-MIPs was confirmed by magnetic

218

hysteresis loops and the dispersion/agglomeration process, which were illustrated in

219

Figure 3. The magnetic saturation of M-H-MIPs was 2.32 emu·g-1, confirming the

220

successful immobilization of magnetic nanoparticles. When applied an external

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

221

magnetic field on the outer side wall of the vials, the homogeneously dispersed

222

M-H-MIPs could adhere to the wall of vials quickly and lead to the formation of clear

223

and transparent solution. The results showed that M-H-MIPs obtained in this work

224

could be separated and collected in a simply and effectively way.

225

Binding Properties of M-H-MIPs. Binding capacity and binding rate are key

226

indexes to evaluate the performances of MIPs. So in this work, binding property

227

including static binding, dynamic binding and selective binding of M-H-MIPs were

228

evaluated in detail. First, static adsorption experiments were executed to measure the

229

adsorption capacities of M-H-MIPs using H-MIPs and M-H-NIPs as control, and the

230

results were displayed in Figure 4A. From Figure 4A we can see that the adsorption

231

capacity of M-H-MIPs and H-MIPs increased quickly with the increasing of atrazine

232

concentration until the concentration reach to 60 mg·L−1, where the adsorption

233

capacity reached an equilibrium. We also can see that the binding capacity of H-MIPs

234

was slight higher than M-H-MIPs. This was because magnetic particles didn’t

235

contribute to binding target molecules. None specific recognition site for atrazine was

236

form in NIPs because no template was used during the preparation process, so

237

M-H-NIPs displayed lower binding capacity than corresponding M-H-MIPs. The

238

adsorption capacity of M-H-MIPs (1.69 mg·g−1) was about 4 fold over that of

239

M-H-NIPs (0.37 mg·g−1) after adsorption equilibrium. The result confirmed the

240

specific recognition ability of MIPs.

241

The binding isotherms of MIPs and NIPs were evaluated using Langmuir,

242

Freundlich or Langmuir -Freundlich adsorption isotherm models, The model fitting

ACS Paragon Plus Environment

Page 12 of 29

Page 13 of 29

Journal of Agricultural and Food Chemistry

243

results revealed that Langmuir isotherm model (Eq. 1) with an R2 value of 0.9354

244

yielded the better fitting than the Freundlich isothermal equation (R2=0.8123) and the

245

Langmuir-Freundlich equation (R2=0.7234). According to Langmuir adsorption

246

model, Qmax, the maximum binding capacity, were 3.70 mg·g−1, 3.22 mg·g−1 and 0.52

247

mg·g−1 for H-MIPs, M-H-MIPs and M-H-NIPs, respectively.

248

Ce 1 1 = Ce + Qe Q max KlQ max

(1)

249

Scatchard analysis was also often employed to measure the binding isotherms. In

250

the light of Scatchard equation (Eq. 2), Scatchard plots were calculated and displayed

251

in Figure 4B. Consequently, the equilibrium dissociation constants Kd and maximum

252

binding capacities Qmax were calculated. Qmax for H-MIPs, M-H-MIPs and M-H-NIPs

253

were 2.81 mg·g-1, 2.38 mg·g-1 and 0.51 mg·g-1, respectively. Kd were 14.99 mg·L-1,

254

19.08 mg·L-1 and 23.31 mg·L-1, respectively.

255

Q Ce

=

Qmax Q − Kd Kd

(2)

256

The mass transfer properties of MIPs and NIPs can be assessed by dynamic binding

257

experiments and the kinetic curves of atrazine adsorption on M-H-MIPs, H-MIPs and

258

M-H-NIPs were illustrated in Figure 4B. It can be clearly seen that higher adsorption

259

time would lead to the greater adsorption capacity, and the rule was valid within 1h.

260

1h was enough for M-H-MIPs to reach the dynamic adsorption equilibrium,

261

demonstrating the fast adsorption process. In comparison, MIPs prepared by living

262

precipitation polymerization22 and surface imprinting method23 would take 7 h and 5 h,

263

respectively, to reach adsorption equilibrium in our previous work. Therefore, hollow

264

porous structure of M-H-MIPs facilitated the diffusion of targets to recognition sites.

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

265

Elovich, Pseudo-first-order, Pseudo-second-order and intraparticle diffusion kinetic

266

models were employed to fit the dynamic binding and the results were displayed in

267

Figure 4. The result evidenced that pseudo-second-order model, expressed as Eq. 3,

268

best fitted the dynamic adsorption with R2 higher 0.995. In the equation, Qe is the

269

equilibrium adsorption amount, Qt is the instantaneous adsorption amount at time t

270

and k2 is the adsorption constant. According to pseudo-second-order model, Qe was

271

2.17 mg·g-1, 1.86 mg·g-1 and 0.55 mg·g-1 for H-MIPs, M-H-MIPs and M-H-NIPs,

272

respectively, which agreed with the Qe of 1.9 mg·g-1, 1.53 mg·g-1 and 0.35 mg·g-1

273

from the experimental results when the initial concentration of atrazine fixed as 50

274

mg·L-1. Thus, the dynamic adsorption followed the pseudo-second-order model.

275

t 1 t = + 2 Qt k2Qe Qe

(3)

276

The cross-reactivity of the M-H-MIPs was assessed by selective binding

277

experiment while using M-H-NIPs as control. Simazine, propazine and terbuthylazine

278

were used as structural analogs while carbendazim and furazolidoneas as control. The

279

structure of involved molecules were displayed in Figure 4E. Imprinted factor (IF),

280

which defined as the ratio of QMIP to QNIP, was adopted to evaluate the selectivity of

281

the as-prepared MIPs. From Fig. 4D we can see that M-H-MIPs exhibited higher

282

binding capacity for the four triazine derivatives than the two structurally unrelated

283

compounds. It’s well known that triazine herbicides share similar structures, which

284

was hard to distinguish even using antibodies. Thus the cavities for atrazine also can

285

recognize simazine, propazine and terbuthylazine. The result implied that atrazine

286

imprinted M-H-MIPs can recognize the family of triazines. It’s a good message for

ACS Paragon Plus Environment

Page 14 of 29

Page 15 of 29

Journal of Agricultural and Food Chemistry

287

sample pretreatment because tedious work can be avoid to prepare a series of MIPs.

288

For carbendazim and furazolidone, the molecular structure were less resemblance to

289

atrazine, which resulted in the lower binding capacity. When compared the adsorption

290

capacity of six compounds onto M-H-NIPs, we can see that the values were very

291

close and lower than those in M-H-MIPs. The adsorption of M-H-NIPs was all

292

non-selective because there were no tailor-made selective recognition sites. IF,

293

calculated from Fig. 4D, ranged from 5.1 to 5.6 for simazine, propazine and

294

terbuthylazine, while the value for carbendazim and furazolidone was lower than 1.2.

295

The higher IF implied the higher selectivity property of atrazine imprinted M-H-MIPs

296

for triazine herbicides.

297

From binding experiments we can see that M-H-MIPs can achieve rapid and

298

convenience separation while they enjoy faster mass transfer property. Meanwhile,

299

atrazine imprinted M-H-MIPs displayed significant class selective recognition ability

300

for the family of trazines herbicides. So M-H-MIPs could be an ideal sorbent to

301

extract triazines from complicated samples.

302

Analytical Performance of DSPE Based on M-H-MIPs. M-H-MIPs were used as

303

adsorption sorbent to carry out dispersive solid phase extraction (DSPE) of four

304

triazine herbicides from real food samples in order to evaluate the feasibility of the

305

obtained M-H-MIPs. Various factors involved in the whole DSPE procedure

306

(condition, extraction, separation, washing and eluting), such as the amount of

307

M-H-MIPs, extraction time and elution solvent, etc., were studied in detail in order to

308

get the optimal extraction condition.

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

309

The dosage of M-H-MIPs played an important role in extraction process because

310

insufficient adsorption sites resulting from low amount of M-H-MIPs would lead to

311

lower extraction efficiency and long adsorption time. In this work, changing the

312

amount of M-H-MIPs from 300 to 900 mg while the concentration of trazines fixed at

313

100 µg·L-1 and extraction time at 30 min, the effect of amount of M-H-MIPs on

314

extraction efficiency was studied. The results (Figure S1) indicated that the recoveries

315

increased with the increasing of M-H-MIPs before reach to a plateau of 95% when 0.6

316

g M-H-MIPs were used. However, further increasing the amount of M-H-MIPs did

317

not bring significant increase in recoveries. Then as another important factor,

318

extraction time was optimized. From Figure S2 we can see that extraction efficiency

319

increased from 50.3% to 95.4% when ultrasound-assisted extraction time increased

320

from 5 to 15 min. Keeping increasing extraction time did not bring significant

321

improvement in recovery. So 15 min was enough for ultrasound-assisted extraction.

322

Another important affecting factor was the elution solvent. In addition to methanol

323

and ACN, acidified methanol were tested as eluting solvents. The result showed that

324

the elution efficiency of acid methanol was higher than other solvent (Figure S3) and

325

there was no significant difference for 90:10 and 99:1.0 (methanol: acetic acid).

326

Finally, 5×1mL of a mixture of methanol/acetic acid (99/1.0, v/v) was selected as

327

eluting solvent to promise the high recoveries of four triazine herbicides.

328

Under the above-identified optimum conditions, the linear range and limits of

329

detection (LOD) of the analytical method were further investigated and the results

330

were shown in Table 1. For the method of M-H-MIPs-DSPE coupled with HPLC, a

ACS Paragon Plus Environment

Page 16 of 29

Page 17 of 29

Journal of Agricultural and Food Chemistry

331

good linearity was derived in the range of 0.5-200 µg·L-1 for atrazine, simazine and

332

1.0-200 µg·L-1 for propazine and terbuthylazine with correlation coefficients of

333

0.9992, 0.9978, 0.9959 and 0.9962, respectively. LOD, calculated as 3S/N, were 0.16,

334

0.23, 0.31 and 0.39 µg·L-1 for atrazine, simazine, propazine, terbuthylazine,

335

respectively. Replicate analyses at spiked concentration of 100 µg·L-1 were performed

336

on the same day and on six different days to determine the intraday precision and

337

interday precision given by the relative standard deviations (RSD). The RSD of

338

intraday was 3.2−5.6% and 3.6−4.9% for interday reproducibility. Therefore, it was

339

demonstrated that this method can be applied to accurate and sensitive quantitative

340

determination of triazine in real samples.

341

To verify the recyclability of M-H-MIP-DSPE, regeneration (adsorption/

342

desorption) cycles were conducted. After M-H-MIPs were used to enrich four

343

triazines herbicides, the material could be regenerated by washing with 5 mL

344

methanol/acetic acid (90/10, v/v), 5 mL methanol and 5 mL ACN. After experienced

345

repeated 5 times regeneration, M-H-MIPs displayed good reusability and still kept the

346

high recovery with a loss of average recovery less than 5.0 % (Table S1). The result

347

indicated the stability of M-H-MIPs.

348

The methodology was applied to extract trazines from corn, wheat and soybean

349

samples. Initial analysis confirmed that those three samples were free of triazine

350

herbicides. So spiking procedure was carried out. HPLC chromatography (Figure S4)

351

for the three samples showed that four triazine compounds can be remarkably

352

concentrated while the interference substances in the real samples could be removed

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

353

after selective extraction. Although there were still some impurities after treated by

354

M-H-MIP-DSPE, they had the least impact on the quantitative determination.

355

Recovery and RSD was employed to evaluate the accuracy and the precision of the

356

method, respectively. DSPE procedure for spiked samples at three concentrations (1.0,

357

5.0 and 50 µg·L-1) in different samples were carried out and the results were displayed

358

in Table 2. The recoveries of atrazine, simazine, propazine and terbuthylazine with

359

M-H-MIP-DSPE for the spiked corn, wheat and soybean were 82.14−101.69%,

360

81.22−98.42%, 81.35−97.75% and 80.62−97.78%, respectively. The RSDs were

361

1.9−4.0%, 2.6−4.6%, 2.4−4.6% and 3.2−5.2%, respectively.

362

Furthermore, in order to demonstrate the suitability of a method for analysis of

363

real-life samples, the method was applied to test positive samples that are

364

contaminated with triazines. The corn and soybean samples contaminated ranging

365

between 5 and 20 µg·kg-1 were provided by Food Quality Supervision Bureau of

366

Linyi. The samples were analyzed using M-H-MIPs-DSPE and the results were

367

compared with those obtained from Food Quality Supervision Bureau of Linyi using

368

the National Standard Method (Table 3). From Table 3 we can see that the values in

369

our method were agree well with those obtained by accredited method. The results

370

demonstrated that M-H-MIPs-DSPE coupled with HPLC was an efficient and

371

effective methodology for selective extraction and sensitive assessment of multiple

372

triazine herbicides at a very low concentration.

373

In summary, novel M-H-MIPs were prepared by multi-step swelling polymerization

374

followed by in-situ growth of magnetic Fe3O4 nanoparticles on the surface of hollow

ACS Paragon Plus Environment

Page 18 of 29

Page 19 of 29

Journal of Agricultural and Food Chemistry

375

MIPs. M-H-MIPs showed some attractive characteristics, such as higher binding

376

capacity, faster binding kinetics, and quicker separation. M-H-MIPs were successfully

377

applied to selective purify and concentrate triazine herbicides from real samples. The

378

method proposed in this work was proved to be a simple and efficient approach for

379

selective and sensitive detection of triazines from complicated food matrices.

380 381

ACKNOWLEDGEMENTS

382

We thank NSFC (NO. 21307052), the Natural Science Foundation of Shandong

383

Province of China (ZR2013BL006).

384 385

REFERENCES

386

(1) Blasco, C.; Picó, Y. Development of an improved method for trace analysis of quinolones in

387

eggs of laying hens and wildlife species using molecularly imprinted polymers. J. Agric. Food

388

Chem. 2012, 60, 11005–11014.

389

(2) Liu, S.; Yan, H.Y.; Wang, M.Y.; Wang, L.H. Water-compatible molecularly imprinted

390

microspheres in pipette tip solid-phase extraction for simultaneous determination of five

391

fluoroquinolones in eggs. J. Agric. Food Chem. 2013, 61, 11974–11980.

392

(3) Ma, J.B.; Qiu, H.W.; Rui, Q. H.; Liao, Y.F.; Chen, Y.M.; Xu, J.; Zhan, P.P.; Zhao, Y.G. Fast

393

determination of catecholamines in human plasma using carboxyl-functionalized magnetic-carbon

394

nanotube molecularly imprinted polymer followed by liquid chromatography-tandem quadrupole

395

mass spectrometry. J. Chromatogr. A 2016, 1429, 86–96.

396

(4) Altintas, Z.; Gittens, M.; Guerreiro, A.; Thompson, K.A.; Walker, J.; Piletsky, S.; Tothill, I.E.

397

Detection of waterborne viruses using high affinity molecularly imprinted polymers. Anal. Chem.

398

2015, 87, 6801–6807.

399

(5) Wang, J.X.; Gao, L.; Han, D.L.; Pan, J.M.; Qiu, H.; Li, H.J.; Wei, X.; Dai, J.D.; Yang, J.H.;

400

Yao, H.; Yan, Y.S. Optical detection of λ-cyhalothrin by core–shell fluorescent molecularly

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

401

imprinted polymers in chinese spirits. J. Agric. Food Chem. 2015, 63, 2392–2399.

402

(6) Ahmad, R.; Griffete, N.; Lamouri, A.; Felidj, N.; Chehimi, M.M.; Mangeney, C.

403

Nanocomposites of gold nanoparticles@molecularly imprinted polymers: chemistry, processing,

404

and applications in sensors. Chem. Mater. 2015, 27, 5464–5478.

405

(7) Xu, S.F.; Lu, H.Z.; Chen, L.X.; Wang, X.C. Molecularly imprinted TiO2 hybridized magnetic

406

Fe3O4 nanoparticles for selective photocatalytic degradation and removal of estrone. RSC Adv.

407

2014, 4, 45266–45274.

408

(8) Shen, X.T.; Zhu, L.H.; Yu, H.W.; Tang, H.Q.; Liu, S.S.; Li, W.Y. Selective photocatalysis on

409

molecular imprinted TiO2 thin films prepared via an improved liquid phase deposition method.

410

New J. Chem. 2009, 33, 1673–1679.

411

(9) Bi, X.D.; Liu, Z. Facile preparation of glycoprotein-imprinted 96-well microplates for

412

enzyme-linked immunosorbent assay by boronate affinity-based oriented surface imprinting. Anal.

413

Chem. 2014, 86, 959–966.

414

(10) Gao, D.M.; Zhang, Z.P.; Wu, M.H.; Xie, C.G.; Guan, G.J.; Wang, D.P. A surface functional

415

monomer-directing strategy for highly dense imprinting of tnt at surface of silica nanoparticles. J.

416

Am. Chem. Soc. 2007, 129, 7859–7866.

417

(11) Xu, S.F.; Chen, L.X.; Li, J.H.; Qin, W.; Ma, J.P. Preparation of hollow porous molecularly

418

imprinted polymers and their application to solid-phase extraction of triazines in soil samples. J.

419

Mater. Chem. 2011, 21, 12047–12053.

420

(12) Zhang, Z.; Xu, S.F.; Li, J.H.; Xiong, H.; Peng, H.L.; Chen, L.X. Selective solid phase

421

extraction of sudan I in chilli sauce by single hole hollow molecularly imprinted polymers. J.

422

Agric. Food Chem. 2012, 60,180–187.

423

(13) Jung, B.M.; Kim, M.S.; Kim W.J.; Chang, J.Y. Molecularly imprinted mesoporous silica

424

particles showing a rapid kinetic binding. Chem. Commun. 2010, 46, 3699–3701.

425

(14) Lu, H.Z.; Xu, S.F.; Mesoporous structured estrone imprinted Fe3O4@SiO2@mSiO2 for highly

426

sensitive and selective detection of estrogens from water samples by HPLC. Talanta, 2015, 144,

427

303–311.

428

(15) Ambrosini, S.; Beyazit, S.; Haupt, K.; Bui, B.T.S. Solid-phase synthesis of molecularly

429

imprinted nanoparticles for protein recognition. Chem. Commun. 2013, 49, 6746–6748.

430

(16) Xu, J.J.; Ambrosini, S.; amahkar, E.; Rossi, T.; Haupt, K.; Bui, B.T.S. Toward a universal

ACS Paragon Plus Environment

Page 20 of 29

Page 21 of 29

Journal of Agricultural and Food Chemistry

431

method for preparing molecularly imprinted polymer nanoparticles with antibody-like affinity for

432

proteins. Biomacromolecules, 2016, 17, 345–353.

433

(17) Chen, J.X.; Lei, S.; Xie, Y.Y.; Wang, M.Z.; Yang, J.; Ge, X.W. Fabrication of

434

high-performance magnetic lysozyme-imprinted microsphere and its NIR-responsive controlled

435

release property. ACS Appl. Mater. Interfaces 2015, 7, 28606–28615.

436

(18) Xu, S.F.; Lu, H.Z.; Zheng, X.W.; Chen, L.X. Stimuli-responsive molecularly imprinted

437

polymers: versatile functional materials. J. Mater. Chem. C 2013, 1, 4406–4422.

438

(19) Xu, C.G.; Shen, X.T.; Ye, L. Molecularly imprinted magnetic materials prepared from

439

modular and clickable nanoparticles, J. Mater. Chem., 2012, 22, 7427–7433.

440

(20) Li, H.; Hu, X.; Zhang, Y.P.; Shi, S.Y.; Jiang, X.Y.; Chen, X.Q. High-capacity magnetic hollow

441

porous molecularly imprinted polymers for specific extraction of protocatechuic acid. J.

442

Chromatogr. A. 2015, 1404, 21–27.

443

(21) Hu, X.G.; Hu, Y.L.; Li, G.K. Development of novel molecularly imprinted solid-phase

444

microextraction fiber and its application for the determination of triazines in complicated samples

445

coupled with high-performance liquid chromatography. J. Chromatogr. A 2007, 1147, 1–9.

446

(22) Xu, S.F.; Li, J.H.; Chen, L.X. Molecularly imprinted polymers by reversible

447

addition-fragmentation chain transfer precipitation polymerization for preconcentration of atrazine

448

in food matrices. Talanta 2011, 85, 282–289.

449

(23) Xu, S.F.; Li, J.H.; Chen, L.X. Molecularly imprinted core-shell nanoparticles for

450

determination of trace atrazine by reversible addition-fragmentation chain transfer surface

451

imprinting. J. Mater. Chem. 2011, 21, 4346–4351.

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure caption Figure 1 The process of preparation of M-H-MIPs by in situ growth method. Figure 2 SEM (upper) and TEM (below) images of M-H-MIPs preparation process. A. polystyrene, B. H-MIPs, C. M-H-MIPs.

Figure 3 Magnetic hysteresis loops of M-H-MIPs, the insets show the dispersion and agglomeration process of the M-H-MIPs nanoparticles.

Figure 4 Binding isotherms of MIPs for atrazine in ACN, which including static adsorption experiment (A), Scatchard analysis(B), dynamic binding experiment (C), selective binding experiment (D) and chemical structure for atrazine, simazine, propazine, terbuthylazine, carbendim and

furazolidone(E). Experimental conditions

for static adsorption experiment and Scatchard analysis: V= 2.0 mL; mass of polymer, 20 mg; adsorption time, 24 h. Experimental conditions for dynamic binding experiment: V= 2.0 mL; C0= 50 mg L-1; mass of polymer, 20 mg. Experimental conditions for selective binding experiment: polymer, 20 mg; C0 = 50 mg L-1; V= 2.0 mL; adsorption time, 24 h; room temperature.

ACS Paragon Plus Environment

Page 22 of 29

Page 23 of 29

Journal of Agricultural and Food Chemistry

Figure 1

Figure 2

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Figure 3

ACS Paragon Plus Environment

Page 24 of 29

Page 25 of 29

Journal of Agricultural and Food Chemistry

Figure 4

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

ACS Paragon Plus Environment

Page 26 of 29

Page 27 of 29

Journal of Agricultural and Food Chemistry

Table 1 Linear Relations, Detection Limits and Relative Standard Deviations (RSD%, n=6) for Determination of the Four Triazines. Linear range Sample

(µg·L-1)

2

R

LOD

RSD (100 µg·L-1)

(µg·L-1)

Interday

Intraday

Atrazine

0.5-200

0.9992

0.16

3.2

3.6

Simazine

0.5-200

0.9978

0.23

3.9

4.2

Propazine

1.0-200

0.9959

0.31

4.2

4.4

Terbuthylazine

1.0-200

0.9962

0.39

5.6

4.9

ACS Paragon Plus Environment

Journal of Agricultural and Food Chemistry

Page 28 of 29

Table 2 Recoveries and Relative Standard Deviations (RSD, %) Obtained from Analysis of Corn, Wheat and Soybean Samples Spiked with Four Kinds of Triazines.

Recovery, mean±RSD (%) Sample

Compound

1.0 µg·L-1

5.0 µg·L-1

50.0 µg·L-1

Atrazine

82.14±3.6

94.58±4.0

99.87±3.2

Simazine

81.22±4.3

92.31±3.6

96.21±4.6

Propazine

81.35±4.2

90.65±4.3

95.37±4.3

Terbuthylazine

80.62±3.4

91.12±5.2

93.19±3.9

Atrazine

86.39±3.8

94.63±3.6

101.69±2.8

Simazine

84.19±4.1

94.39±4.4

98.42±2.6

Propazine

85.20±3.9

91.88±4.6

97.75±2.9

Terbuthylazine

82.57±5.1

92.78±3.8

97.78±3.3

Atrazine

84.64±2.9

93.36±2.6

98.85±1.9

Simazine

83.54±3.2

90.59±3.1

97.78±3.1

Propazine

83.56±3.7

92.17±2.4

96.05±3.4

Terbuthylazine

81.87±4.0

91.06±3.4

95.03±3.2

Corn

Wheat

Soybean

ACS Paragon Plus Environment

Page 29 of 29

Journal of Agricultural and Food Chemistry

Table 3 Results±RSD% of the Analysis of Positive Corn and Soybean Samples Using M-H-MIPs-DSPE and National Standard Method.

Sample

M-H-MIPs-DSPE

National Standard method

Atrazine (µg·kg-1)

Simazine (µg·kg-1)

Atrazine(µg·kg-1)

Simazine (µg·kg-1)

Corn 1

5.66±3.7

ND

5.46±2.9

ND

Corn 2

15.98±3.1

5.40±3.5

16.32±2.6

5.23±1.9

Soybean 1

15.48±2.9

5.32±3.6

15.23±3.2

5.21±2.9

Soybean 2

ND

8.65±3.1

ND

8.74±2.7

ND: not detected. RSD%, n=3.

ACS Paragon Plus Environment