Protein functionalised aerogel membranes (PFAMs) for gravity-driven

*Email: [email protected] / [email protected]; Phone No: +91-278- ... groups, is demonstrated for the preparation of protein functionalised aer...
0 downloads 0 Views 1MB Size
Subscriber access provided by UNIV OF DURHAM

Article

Protein functionalised aerogel membranes (PFAMs) for gravity-driven separation Nilesh Vadodariya, and Ramavatar Meena ACS Sustainable Chem. Eng., Just Accepted Manuscript • DOI: 10.1021/ acssuschemeng.8b05100 • Publication Date (Web): 01 Feb 2019 Downloaded from http://pubs.acs.org on February 3, 2019

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

1

Protein functionalised aerogel membranes (PFAMs) for gravity-driven separation

2

Nilesh Vadodariyaa,b; Ramavatar Meenaa,b*

3

aNatural

4

Institute, G. B Marg, Bhavnagar-364002 (Gujarat), India

5

bAcademy

6

Research Institute, G. B. Marg, Bhavnagar-364002 (Gujarat), India.

7

*Email: [email protected] / [email protected]; Phone No: +91-278-2567760

Products & Green Chemistry Division, CSIR-Central Salt & Marine Chemicals Research

of Scientific and Innovative Research (AcSIR)-Central Salt & Marine Chemicals

8 9

ABSTRACT

10

In this research article bovine serum albumin (BSA), a protein with a free amine (-NH2) functional

11

groups, is demonstrated for the preparation of protein functionalised aerogel membranes (PFAMs)

12

using naturally occurring genipin as a crosslinking agent. PFAMs were characterized using SEM,

13

FT-IR, Solid-UV, and TGA. PFAMs are highly stable and recyclable under aqueous conditions and

14

successfully tested for efficient separation of oil-spill as well as emulsion under gravity driven force.

15

PFAMs produced ~98 % pure water with high flux rate ranging from 430 to 605 L.m-2.h-1 at lab scale

16

separations under gravity. PFAMs were tested for the biodegradable possibility in the soil conditions.

17

This work is one of the best examples for the development of environmentally friendly porous

18

membranes using abundant seaweed biomass through crosslinking chemistry of protein.

19

KEYWORDS: Protein, Agar, Aerogel, Oil-spill and oil/water separation, Reusability

20 21 22 23 1 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 2 of 23

24

INTRODUCTION

25

Several industries including mining, textiles, foods, petrochemicals, etc. produce substantial volumes

26

of oily wastewater, which is now a common pollutant all over the world. 1, 2 According to report, a

27

mining operation produces about 140000 L of oily wastewater every day. 3 The human activities such

28

as marine transportation and oil production are another major causes of oil-leakages/spillages in

29

marine environments and ecology1,2. Numerous types of mechanical devices such as oil skimmers or

30

booms are used to purify these oil/water mixtures, but need an input of energy or high pressure to

31

operate.4 Porous materials such as sponges, 5,6 foams,7,8 and textiles,9–11 are also generally used to

32

overcome this issue, but such materials simultaneously absorb both water and oil, resulting in poor

33

separation selectivity and efficiency. The recycling/ reuse of such materials and the adsorbed oils are

34

normally difficult. Such types of materials are commonly burned in the ground, which produced

35

pollutant in the environment.12 These prior arts speaks us that development of eco-friendly, green and

36

recyclable materials technologies that can purify oil/water mixtures (including emulsions) in the

37

industry are in high demand. Recent development on this field is mainly focused on surface

38

superwettabilities

39

superoleophilicity).13–16 However, hydrophilic membranes has advantages that it cannot be easily

40

fouled by Oil during demulsification as compared to the hydrophobic and Oliophobic membrane.17,18

41

Based on the superhydrophilicity diverse membrane have been recently reported like polyacrylamide

42

(PAM) hydrogel-coated stainless steel mesh has been reported by Jiang's group in 2011, 19 Wang et.

43

al. reported stainless steel hollow fibre microfiltration membrane,20 In the recent decade, researchers

44

are focusing

45

nanowhiskers co-crosslinked Poly N-isopropylacrylamide-co-N-methylolacrylamide membranes,21

46

superhydrophilic fluorinated cellulose nanofibrils aerogel,22 superhydrophilic β-CD & Polydopamine

47

modified Poly L-Lactic acid scaffold nanofibers membrane23 for the selective separation of water

48

from oil-water mixture. Superhydrophobic and superoleophilic oil absorbent such as SiO2/Poly L-

49

Lactic acid/polystyrene hybrid nonwoven has also been reported.24

(e.g.,

superhydrophobicity,

superhydrophilicity,

superoleophobicity,

and

on the development of eco-friendly and biodegradable materials such as chitin

2 ACS Paragon Plus Environment

Page 3 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

50

Membrane-based technologies such as ultrafiltration (UF), microfiltration (MF),

51

nanofiltration (NF) and reverse osmosis (RO) have become potential candidates for such

52

separations25. UF has been successfully applied for the separation of the surfactant-stabilized oil-

53

water stable emulsion.

54

In our laboratory, we have previously reported seaweed polymer agarose-based porous

55

membrane systems for oil-water separation with flux in the range of 230-500 L m−2 h−1.26-27 These

56

prior art encourage us to utilised agar for the development of aerogel membranes for oil-water

57

separation. Furthermore, the above reports revealed that protein functionalised aerogel membranes

58

are not reported in the literature for this purpose.

59

In this study we describes a simple and eco-friendly method for the preparation of protein

60

functionalised aerogel membrane (PFAMs) through crosslinking with natural crosslinker genipin. In

61

this study a crosslinked system was developed in the form of aerogel membrane through crosslinking

62

reaction with highly water soluble protein BSA. PFAMs is composed of 100 % bio-based raw

63

materials including crosslinker and showed excellent soil degradability. In addition this work utilises

64

seaweed polymer agar (linear hydrophilic galactan) as texturing polymer which is less expensive

65

compared to agarose used in our previous studies. Flux rate and water purity were almost identical

66

with our previous reports from expensive agarose seaweed polymer. So result of this work indicates

67

that more expensive agarose polymer may be replaced by inexpensive agar polymer for designing

68

such materials. This work also opens new research areas for polymer scientist to utilised seaweed

69

polymers like agar to prepared biodegradable separation membranes for sustainable solutions.

70

PFAMs tested for sustainable separation of oil-water mixtures; organic-water mixtures and emulsion.

71

The purity of permeate water was >98 %, and water flux rate obtained up to 600 L·m−2·h−1.

72

EXPERIMENT SECTION

73

Materials

3 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 23

74

Seaweed polysaccharide agar used in this work is extracted from Indian seaweed biomass using

75

simple and cost-effective method using red seaweed Gelidella acerosa following the method reported

76

in the literature.28, 29 BSA (Sigma-Aldrich), Genipin (Challenge Bioproducts Co. Ltd., Taiwan) and

77

n-Hexane and toluene (S. D. Fine Chemicals) were purchased. Biodiesel procured from our institute

78

pilot plant and used for emulsion formation by vigorous stirring in 20:80 v/v ratio (biodiesel: water)

79

followed by addition of Sodium dodecyl sulphate (SDS). Oil-spill used in the present work was

80

collected from Alang ship breaking yard, Gujarat, India and used directly for further treatments.

81

Preparation of membrane

82

This study provides a simple, green and eco-friendly process for the preparation of protein

83

functionalised aerogel (PFAMs) membrane. For this used total polymer concentration in the range of

84

1 % (w/v) to 3 % (w/v) keeping agar: BSA ratio constant (AG : P = 8: 2 w/w) in all PFAMs. In brief,

85

1.8 g agar (AG) polymer dissolved in 80 mL distilled water under microwave heating at 100°C for 5

86

min. Separately dissolved 0.2 g BSA in 20 mL water at room temperature. BSA solution adds into

87

agar solution under stirring at 50°C followed by addition of 40 mg genipin as a crosslinker. Then the

88

mixture was heated at 80 oC in the microwave for 1 minute and gradually cooled to room temperature

89

to convert into the stable hydrogel. The appearance of bluish colored hydrogel on cooling indicates

90

cross-linking reaction and becomes dark in color within 24 to 48 h due to the high crosslinking

91

reaction of genipin with protein. In this work, the progress of blue color was observed physically up

92

to 36 h. The cross-linked hydrogel was cut to small pieces (~0.5 mm thick slices) after 36 h, and

93

lyophilised hydrogel slices to obtain the protein functionalised aerogel membranes (PFAMs), and

94

used for separation applications. The control AG aerogel was prepared by following the above process

95

without protein and genipin for comparative study.

96

PFAMs obtained with 2 % total polymer concentration (AG: P = 8: 2 w/w) with 0.01 to 0.04

97

% genipin crosslinker exhibited swelling in the range of 280 - 350 % in water. The result shows that

98

PFAMs obtained with 0.03 % and 0.04 % genipin crosslinker shows almost identical swelling (~280 4 ACS Paragon Plus Environment

Page 5 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

99

%). Figure S1b shows that PFAM obtained with 0.04 % genipin crosslinker showed the lowest

100

swelling (150 %) in oil-water mixture compared to other membranes. Hence, PFAMs obtained from

101

2 % total polymer concentration with 0.04 % genipin were tested for separation. PFAMs obtained in

102

the present study shows significantly higher swelling in water and emulsion solution may be due to

103

the more hydrophilic nature. Flux (J) of permeate and % rejection oil in permeate was calculated as

104

method reported in our previous paper.26-27

105

Membrane testing

106

The resulting membrane materials were tested for the separation of oil-water and organic-water

107

samples under gravity driven force in the laboratory using a simple funnel method. For this

108

experiment, placing wet aerogel in the neck of the funnel. Afterward oil-spill, Biodiesel/water

109

emulsion, n-hexane/water, and toluene/water feed samples were poured into the funnel. Permeation

110

rate and purity were evaluated using the following equation (1): 𝐽 = 𝐴(𝑡

111

𝑉

..........(1)

0 −𝑡𝑛 )

112

[J = flux (L·m−2·h−1); V = volume of permeate; A = effective area of the membrane used; t0 = at zero

113

time interval; tn = at interval n]

114

Membrane characterisation

115

In this work, agar solutions were prepared using microwave or autoclave ES-315 (TOMY SEIKO

116

Co., Ltd., Japan). Further, protein functionalised aerogel membranes were obtained by small slices of

117

the gel using lyophilisation (VirTis Benchtop, Freeze-dryer, United States). FTIR spectra of PFAMs

118

recorded on a PerkinElmer (Spectrum GX, USA); surface morphology and porosity of uncross-linked

119

and cross-linked PFAMs were done by scanning electron microscopy (SEM, Carl-Zeiss Leo VP 1430

120

instrument, Oxford INCA); thermogravimetric analysis (TGA) of PFAMs was carried out on Mettler

121

Toledo Thermal Analyzer, (TGA/SDTA 851e, Switzerland) under N 2 atmosphere as described in our

5 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 23

122

previous work26,

123

spectrophotometer (JAPAN).

124

RESULTS AND DISCUSSION

125

Agar used in this work is well known hydrophilic seaweed polymer extracted from the red seaweed

126

Gelidiella acerosa. Agar is chemically composed of the structure comprising a repeating unit of (1,

127

3) linked α-D-galactose (G) and (1, 4) linked β-L-3,6-anhydrogalactose(A).28, 29 It is available easily

128

in low cost and 1-2 % w/w form a strong gel in water. Figure 1 shows the preparation of protein

129

functionalised aerogel membranes (PFAMs) using hydrophilic seaweed polysaccharide “agar”.

130

Crosslinker genipin used in this study is extracted from fruits, and a well known natural crosslinker

131

with primary amine functional group. In this study protein (BSA) is gifted with free amine groups,

132

which may be available for crosslinking reaction with genipin. It results in the formation of blue

133

colored aerogels (Figure 1).

27 ;

and solid-state UV−vis spectra were recorded on Shimadzu UV-3101PC

6 ACS Paragon Plus Environment

Page 7 of 23

(a)

AG-BSA blend

After Freeze Drying

Agar

Genipin cross-linked AG-BSA blend

Micro porous Aerogel

BSA

(b) BSA Hydrogen bonding

Agar

Microwave

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

+ Genipin

Hydrogen bonding

Hydrogen bonding

134 135

Figure 1. (a) Schematic representation for the preparation of protein functionalised aerogel

136

membranes (PFAMs) [Agar(AG) and BSA(P) were mixed (9:1 w/w ratio), and add crosslinker

137

genipin to cross-link under ambient conditions hydrogel turned into blue in colour at room

138

temperature and slicing cross-linked hydrogel and subjected to freeze-drying to yield protein

139

functionalised aerogel membranes for separation]. The figure shows dark blue (cross-linked) and

140

milky-white (non-crosslinked) aerogels to illustrate the difference and (b) Reaction mechanism for

141

the crosslinked polymer.

7 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 23

BSA

Genipin

MW

Freeze Agar layer

BSA wall

Drying Agar

142 143

Figure 2. A possible mechanism for the formation of protein functionalised aerogel membranes

144

(PFAMs).

145

A possible mechanism of the formation of PFAMs has been given in Figure 2. In this

146

study, agar network is full of hydroxyl functional groups and help to form hydrogen bonding with

147

protein and water molecules. In addition, protein is full of free primary amine functional groups and

148

free to take in part in crosslinking reaction with genipin. The formation of such hydrogel network

149

through hydrogen bonding and covalent bonding is suitable for the production of porous aerogel for

150

sustainable separation. In this study naturally occurring crosslinker genipin covalently cross-linked

151

with the primary amine group of BSA (Figure F1(b)). This could be explained on the basis of color

152

changes from off-white to bluish green. Simultaneously hydroxyl groups of agar attached with protein

153

through hydrogen bonding. Such types of structural arrangement within cross-linked hydrogels may

154

results stable gel network suitable for potential use such as separation of the oil-water mixture. In

155

addition, such crosslinked hydrogel form stable gel channel inside the genipin cross-linked BSA

156

matrix on cooling. As mentioned agar a hydrophilic polymer is capable to attain high amount of water.

157

The crosslinked hydrogel after 36 h was cut into slices, and this sliced hydrogel freeze by liquid

158

nitrogen to generate ice crystal in the agar channel, which is mainly responsible for the formation of

159

microporous aerogels. Ice channel is containing hydrogel subjected to a lyophilizer for drying.

160

Sublimation of ice crystal from gel creates microporous aerogel during drying process without

161

disturbing the morphology of gel. To validate the mechanism for the formation of crosslinked aerogel

8 ACS Paragon Plus Environment

Page 9 of 23

162

membrane solid UV-spectra, FTIR, and TGA was analyzed for AG, BSA, AG-BSA blend and genipin

163

crosslinked PFAMs.

164

The appearance of dark-coloured hydrogel after crosslinking of genipin with agar-protein (AG-P)

165

blend may be due to the chemical modifications or conjugation.26, 27 & 30 This types of conjugation can

166

be confirmed using UV-Vis spectroscopy (Figure 3). Crosslinker genipin used in this study exhibited

167

a characteristic peak at 240 nm, while protein (BSA) used as amino source showed a characteristic

168

peak at 280 nm (Figure 3). Gelling polymer agar used in this study does not show any UV peak, but

169

a blend of agar polymer with protein BSA (AG-P blend) shows a broad peak at 280 nm indicates the

170

presence of BSA. The crosslinked Agar-BSA blend with genipin (AG-P-G) showed irregular

171

broadening between 240 to 300 nm but a new clear peak obtained at 590 nm due to extended

172

conjugation of genipin crosslinking in protein network. Such type of extended conjugation may be

173

mainly responsible for the development of dark-colored gel materials.26, 27 & 30 1.0

0.8

240 nm

0.6

Abs.

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

280 nm 590 nm

0.4 (d)

0.2 (c) (b)

(a) 0.0 200 300

400

500

600

700

800

Wavelength (nm)

174 175

Figure 3. UV-Vis. Spectra of (a) Genipin (b) BSA protein (c) AG-P blend (d) Genipin cross-linked

176

PFAMs.

177

After UV-Vis analysis based on colour development indicates crosslinking of genipin with

178

protein amine groups. To confirm the other possible interactions in the formation of the aerogel

179

membrane were further analysed by FTIR (Figure 4). FTIR spectrum of agar polymer shows the 9 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

180

general pattern as reported in our previous study.26-27 Figure 4 shows characteristics IR peaks at 932

181

cm-1 due to the presence of 3,6-anhydrogalactose linkage in agar. Additional two IR peaks in agar

182

spectrum at 3445 cm-1 and 1075 cm-1 are due to the stretching of –OH functional group and vibration

183

of C-O-C glycosidic linkage.28, 29 Protein (BSA) exhibit characteristics peak at 1664 cm-1 for the

184

amide I band due to C=O stretching vibrations of the peptide bond. Similarly, BSA shows peaks near

185

1533 cm-1 is due to N-H bending vibration of amide II and 1386 cm-1 is due C-N stretching

186

vibration.31 Crosslinker genipin used in this work exhibited the most characteristics IR peak at 1444

187

cm-1 due to the ring stretching mode.26-27

1684 1623 1444

(a)

932

1075

1062 932 1082 932

1409

1640

3403 3405

(e)

1725 1637

(d)

1382

3445

(c)

1533 1386

1637 1664

(b)

%T

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 23

4000 3500 3000 2500 2000 1500 1000

500

-1

Wavenumber (cm )

188 189

Figure 4. FTIR Spectra of (a) Genipin (b) BSA protein, (c) AG, (d) AG-P blend, (e) Genipin cross-

190

linked blend AG-P-G.

191

The cross-linked aerogel (AG-P-G) membrane shows a new IR band at 1409 cm−1 revealed the

192

presence of ring stretching of heterocyclic amine, in addition appearance of IR band at 1647 cm−1

193

representing C=O stretch in the crosslinked AG-P-G.26, 27 Presence of additional characteristics agar

194

and protein peaks in IR spectrum of aerogel (AG-P-G) product clearly indicates that the native

195

backbone of pure agar and protein remained intact during crosslinking through cross-linker. FTIR

196

results mainly shows noticeable change in the –OH stretching band of agar (AG) (Figure 4). As shown 10 ACS Paragon Plus Environment

Page 11 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

197

in Figure 4, -OH stretching band of AG shifted significantly from 3445 cm-1 to 3405 cm-1 on blending

198

with BSA, and remained almost (3403 cm-1) unchanged on crosslinking with genipin in the product

199

(AG-P-G). This result confirms that hydroxyl (−OH) groups present in agar network responsible for

200

hydrogen bonding interaction with N lone pair of the amide group of Protein. This may result a

201

columnar structure of aerogel membrane in which Protein walls are coated with hydrophilic polymer

202

AG.

203 204

Figure 5. SEM images of (a & a’) AG-P blend, (b & b’) Genipin cross-linked PFAMs and (c & c’)

205

after oil-water emulsion separation. 11 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

206

The morphologies of AG-P blend and Genipin cross-linked AG-P-G blend were studied using

207

Scanning Electron Microscope (SEM) as shown in Figure 5. AG-P blend aerogel exhibited highly

208

porous network ranging between 70-120 μm in sizes. This uncrosslinked hydrogel collapsed fully in

209

the presence of aqueous mixtures, and no separation is observed may be a less stable porous network

210

in this blend uncrosslinked aerogel. SEM images of the AG-P-G samples confirmed that sizes of

211

pores generated during water evaporation through lyophilisation are slightly modified and bigger in

212

the range of 100-170 μm. This could be explained on the basis of network compactness through

213

genipin crosslinking. In another way, agar-protein walls become more compact or thinner in the

214

presence of genipin crosslinker due to the formation of the stable cross-linked network. The high flux

215

rate compared to previous agarose and chitosan-based membranes due to the fabrication of larger

216

porous sizes aerogel membrane in the present study. This study revealed that less expensive agar

217

seaweed polymer could be used to modify the porosity and flux rate of the cross-linked aerogel

218

membranes. Similarly, amino functional groups containing compound may be useful to design

219

desired porosity and flux rates of the resulting aerogel membranes for oil-water separation.

100

80

% Mass

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 23

60

(d) 46.8 (c) 33.7

40

(a) 28.7 (b) 25.4

20 50 220

150

250

350

o

450

Temperature ( C)

12 ACS Paragon Plus Environment

550

Page 13 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

221

Figure 6. Thermogram of (a) AG (b) BSA protein (c) AG-P blend (d) Genipin cross-linked blend

222

AG-P-G.

223

The stability of the resulting aerogel membranes was further confirmed by thermogravimetric

224

analysis (TGA) (Figure 6). TGA results are self-explanatory that aerogel formed in this study

225

becomes more thermally stable on crosslinking with genipin. This is mainly due to the formation of

226

the stable network in the cross-linked aerogel membrane as a result of genipin crosslinking with free

227

amino groups of BSA (Scheme …). The mass loss pattren was identical in all the aerogel samples.

228

Result of TGA shows that pure agar and BSA shows higher mass losses of 71.3 % and 74.6 %

229

respectively compared to uncrosslinked and cross-linked aerogel membranes. The uncrosslinked

230

aerogel membrane of agar and BSA shows improved stability compared to individual components

231

with slightly lower mass loss (66.3 %) up to 600 ⁰C (Figure 6). The minimum mass loss (53.2 %)

232

was obtained for the cross-linked aerogel membrane may be due to the formation of stable gel network

233

through hydrogen bonding (e.g. between agar (-OH) and amine (–NH2) and carboxylic (-COOH)

234

groups of BSA) as well as covalent bonding (Scheme …). The similar observation has been found in

235

the previous study on the agarose and chitosan-based membranes.27 The wettability of the aerogel

236

membranes was tested by contact angle measurement (ESI, Figure S2). Aerogel membranes shows

237

dynamic water contact angle 78.6° to 18.5° (for control AG), 89.6° to 9.3° ( for AG-P blend), and

238

71.9° to 8.9° (for PFAMs). The lowest contact angle for PFAMs indicates more hydrophilic nature

239

of the membranes after crosslinking with genipin. This may help to permeate more water content

240

through the PFAMs. The recycled PFAMs immediately absorbed water drops (contact angle was not

241

measured) may be due to improved hydrophilic nature.

13 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

600

(e) 605

543

(c’)

523 430

400

200 98.7

0

242

pill Oil-s

97.2

97.5

98.4

After 10 min.

-1

(d’)

After 10 min. Final

-2

Initial

Initial 800 Flux (L.m .h ) % Rejection

(b’)

(a’)

(d)

Initial

(C)

After 10 min. Final

(b)

After 10 min. Final

(a)

Initial Initial

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 23

er er ater wat /wat ne/w sel/ ene a e u i x l d e o T H Bio

243

Figure 7. (a) Oil-spill wastewater collected from ship breaking yard (a’) Oil-spill waste water

244

emulsion before and after separation, (b) Biodiesel/water emulsion, (b’) biodiesel/water emulsion

245

before and after separation, (c) Toluene/water, (c’) n-Hexane/water before and after separation, (d)

246

n-Hexane/water, and (d’) Toluene/water before and after separation, (e) Flux rate and % Rejection

247

for the various oil/water mixture.

248

The results of our previous studies encourage us to utilise the resulting aerogel membrane for

249

the water purification from different types of oil/water as well as organic/water mixtures. In the

250

present study, we have successfully tested the resulting aerogel membranes for the separation

251

applications at lab scale (Figure 7a-d). Figure 7 shows the laboratory setup of gravity-driven

252

separation assembly. In brief, a coin-sized (2 cm) diameter aerogel was wetted and fix in the neck of

253

glass funnel and used for the separation of different oil/water or organic/water mixtures and emulsion

254

(Figure 7a-d). Figure 7 shows different mixtures for membrane separation includes crude oil-spill

255

(Fig.7(a), collected from ship breaking yard), biodiesel/water emulsion (Fig.7(b), prepared by

256

sonication along with a surfactant), toluene/water (Fig7(c)), and n-hexane/water (Fig. 7(d)). Figure

257

7a’-d’ shows setups for separation experiments under gravity driven force for different mixtures. 14 ACS Paragon Plus Environment

Page 15 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

258

Figure 7(e) is shown the flux rates of the water from different oil-mixtures under identical conditions

259

at room temperature. The maximum 605 L.m -2.h-1 flux was obtained for n-hexane-water mixture

260

compared to other mixtures with >97 % water rejection. This aerogel membrane shows minimum

261

flux 430 L.m-2.h-1 for biodiesel/water emulsion with >97 % water rejection. Figure 7 (e) revealed that

262

aerogel membrane of the present study also showed excellent flux 543 L.m -2.h-1 for separation of

263

water from oil-spill with high ~99 % water rejection. The mixture of toluene/water also shows

264

excellent flux 523 L.m-2.h-1. Results of this study revealed that protein functionalised aerogel

265

membrane is suitable for separation of water from the above mixtures and emulsion with high flux

266

due to large sizes of the pores fabricated during the preparation process. This separation result showed

267

that flux rate was decreased about 20 % in water-hexane and 40 % in case of oil-water after 5 h

268

(Figure S3) may be due to the changes in the surface morphology of PFAMs (SEM images, Figure

269

5). Result of SEM analysis showed that microporous size of PFAM was decreased from 70-120 μm

270

to 46-60 μm after 3 cycles (Figure 5), which may be responsible for the lower flux rate with high

271

rejection. Weight loss of PFAM was measured and found that no weight loss was observed till 3

272

cycles of reuse. In addition, PFAMs obtained in the present study shows significantly higher swelling

273

in water and emulsion solutions compared to agarose and chitosan-based membranes reported in the

274

previous work.26-27 The swelling result revealed that PFAMs are more hydrophilic in nature, which

275

may be appropriate for the higher flux of permeate through it. PFAMs was recycled and reused for

276

successive three cycles (Figure S4). Flux was decreased slightly from 430 to 404 L.m-2.h-1 in emulsion

277

(biodiesel/water), 543 to 491 L.m-2.h-1 in oil-spill, and 605 to 555 L.m-2.h-1 in n-hexane/water

278

mixtures after 3 repeat cycles (ESI, Figure S4). The control AG aerogel membrane was tested for

279

the oil-water emulsion separation. But no proper separation takes place in the control AG membrane

280

and porous morphology was destroyed significantly (ESI, Figure S5). The result of this study

281

indicates that crosslinking with genipin generate homogeneous stable porous surface morphology of

282

PFAMs essential for separation.

15 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering

283

The separation of water from the mixtures was checked by FTIR spectra (Figure 8). FTIR

284

spectrum of oil/spill shows characteristics peaks at 2925 cm -1 & 2858 cm-1 (C-H stretching), 1458

285

cm-1 (–CH2 bending). Biodiesel/water emulsion have characteristic peak at 2924 cm -1 & 2854 cm-1

286

(C-H stretching) and at 1743 cm-1 (C=O stretching). n-Hexane have characteristics peaks at 2926 cm-

287

1&

288

characteristic peak at 3029 cm-1 (C-H stretching aromatic), 2924 cm -1 (C-H stretching alkyl group)

289

and at 1500 cm-1 (C-C stretching in aromatic ring). All the characteristics peaks of oil, biodiesel, n-

290

hexane, and toluene were not obtained or disappeared in the permeate water samples obtained from

291

oil/spill, biodiesel/water emulsion, n-hexane/water and toluene/water mixtures. IR results indicate

292

efficient separation through PFAMs.

2861 cm-1 (C-H stretching) 1467 cm-1 and 1375 cm-1 (-CH2 & -CH3 bending). Toluene has a

40 30 20 10

(d) (e)

1467 1467 1375

(c)

1500

50

1743

60

2924 2852

(b)

2855

70

2924

80

1603 1458

(a)

2926 3029 2924 2861

90

1375

100

%T

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 23

(f) (g) (h)

0 4000 3500 3000 2500 2000 1500 1000

500

-1

293

Wavenumber (cm )

294

Figure 8. FTIR spectra of (a) oil-spill, (b) Biodiesel/water emulsion (c) n-Hexane, (d) Toluene, and

295

(e, f, g, and h) permeate from oil-spill/water, oil-water emulsion, n-hexane/water, and toluene/water.

296

16 ACS Paragon Plus Environment

Page 17 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

After 20 days

After 40 days

After 60 days Complete degradation 297 298

Figure 9. Biodegradation of PFAM in 60 days under normal condition in the soil.

299

As reported biodegradability and disposal of such materials including membranes in the environment

300

is another big issue. Hence, PFAMs of this study were tested for their biodegradability in soil

301

conditions (Figure 9). For soil biodegradation, the aerogel membrane placed in the soil and observed

302

at a different time interval. The weight losses of PFAM after 20 days and 40 days were ~70% and

303

~90% respectively in soil conditions. While no residue was obtained after 60 days in soil conditions

304

may be due to the complete degradation of membrane (Figure 9).

305

CONCLUSION

306

In this research paper, we have prepared protein functionalised biodegradable aerogel membranes

307

using BSA as protein. This protein functionalised aerogel membrane is highly porous and stable in

308

all the oil-water and emulsion mixtures. Use of natural crosslinker genipin makes this aerogel

309

membrane more environmentally friendly and less toxic in nature. Resulting protein functionalised

310

aerogel membranes have several potential properties with respect to their use in separation of oil-

311

water or emulsion as well as hydrocarbon-water. Protein functionalised aerogel membrane is less to

312

no toxic, easy to handle and biodegradable in soil.

313

Supporting Information

314 315

Swelling behaviour, contact angle measurement, permeate flux, recycle and reuse experiment results, oil-rejection rate with time, and SEM images of control AG.

17 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 23

316

ACKNOWLEDGEMENTS: CSIR-CSMCRI registration number-110/2018. NV & RM want to

317

acknowledge SERB (DST, EMR/2016/004944), for financial support and A&ES&CIF, CSIR-

318

CSMCRI for sample analysis.

319 320

REFERENCES

321

1.

Chen, P.-C.; Xu, Z.-K. Mineral-Coated Polymer Membranes with Superhydrophilicity and

322

Underwater Superoleophobicity for Effective Oil/Water Separation. Sci. Rep. 2013, 3, 2776,

323

DOI 10.1038/srep02776.

324

2.

Wang, L. K. Waste Chlorination and Stabilization in Advanced Physicochemical Treatment

325

Processes, ed. Wang, L. K.; Hung, Y. T. and Shammas, N. K., ISBN 978-1-59745-029-4

326

Humana Press, Totowa, NJ, 2006, pp. 403–440, DOI 10.1007/978-1-59745-029-4.

327

3.

328 329

Guerin T. F., Heavy equipment maintenance wastes and environmental management in the mining industry. J. Environ. Manage. 2002, 66(2), 185-199, DOI 10.1006/jema.2002.0583.

4.

Ventikos, N. P.; Vergetis, E.; Psaraftis, H. N.; Triantafyllou, G. A high-level synthesis of oil

330

spill response equipment and countermeasures. J. Hazard. Mater. 2004, 107, 51–58, DOI

331

10.1016/j.jhazmat.2003.11.009.

332

5.

Nguyen, D. D.; Tai, N.-H.; Lee, S.-B.; Kuo, W.-S., Superhydrophobic and superoleophilic

333

properties of graphene-based sponges fabricated using a facile dip coating method. Energy

334

Environ. Sci. 2012, 5, 7908–7912, DOI 10.1039/C2EE21848H.

335

6.

Zhu, Q.; Chu, Y.; Wang, Z.; Chen, N.; Lin, L.; Liu F.; Pan, Q., Robust superhydrophobic

336

polyurethane sponge as a highly reusable oil-absorption material. J. Mater. Chem. A 2013, 1,

337

5386–5393, DOI 10.1039/C3TA00125C.

338

7.

Calcagnile, P.; Fragouli, D.; Bayer, I. S.; Anyfantis, G. C.; Martiradonna, L.; Cozzoli, P. D.;

339

Cingolani R.; Athanassiou, A., Magnetically Driven Floating Foams for the Removal of Oil

340

Contaminants from Water. ACS Nano 2012, 6, 5413–5419, DOI 10.1021/nn3012948. 18 ACS Paragon Plus Environment

Page 19 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

341

8.

ACS Sustainable Chemistry & Engineering

Dong, X.; Chen, J.; Ma, Y.; Wang, J.; Chan-Park, M. B.; Liu, X.; Wang, L.; Huang W.; Chen,

342

P., Superhydrophobic and superoleophilic hybrid foam of graphene and carbon nanotube for

343

selective removal of oils or organic solvents from the surface of water. Chem. Commun. 2012,

344

48, 10660–10662, DOI 10.1039/C2CC35844A.

345

9.

Li, J.; Yan, L.; Zhao, Y.; Zha, F.; Wang Q.; Lei, Z., One-step fabrication of robust fabrics

346

with both-faced superhydrophobicity for the separation and capture of oil from water. Phys.

347

Chem. Chem. Phys. 2015, 17, 6451–6457, DOI 10.1039/C5CP00154D.

348

10.

Zhang J.; Seeger, S., Polyester Materials with Superwetting Silicone Nanofilaments for

349

Oil/Water Separation and Selective Oil Absorption. Adv. Funct. Mater. 2011, 21, 4699–4704,

350

DOI 10.1002/adfm.201101090.

351

11.

Zhang, L.; Zhang Z.; Wang, P., Smart surfaces with switchable superoleophilicity and

352

superoleophobicity in aqueous media: toward controllable oil/water separation. NPG Asia

353

MATER. 2012, 4, e8, DOI 10.1038/am.2012.14.

354

12.

Adebajo, M. O.; Frost, R. L.; Kloprogge, J. T.; Carmody O.; Kokot, S., Porous Materials for

355

Oil Spill Cleanup: A Review of Synthesis and Absorbing Properties. J. Porous Mater. 2003,

356

10, 159–170, DOI 10.1023/A:1027484117065.

357

13.

Wang, B.; Liang, W.; Guo, Z.; Liu, W.; Biomimetic super-lyophobic and super-lyophilic

358

materials applied for oil/water separation: a new strategy beyond nature. Chem. Soc. Rev.

359

2015, 44, 336–361, DOI 10.1039/C4CS00220B.

360

14.

361 362

separation. J. Mater. Chem. A 2014, 2, 2445–2460, DOI 10.1039/C3TA13397D. 15.

363 364

Xue, Z.; Cao, Y.; Liu, N.; Feng L.; Jiang, L., Special wettable materials for oil/water

Wang Y.; Gong, X., Special oleophobic and hydrophilic surfaces: approaches, mechanisms, and applications. J. Mater. Chem. A, 2017, 5, 3759–3773, DOI 10.1039/C6TA10474F.

16.

Ragesh, P.; Anand-Ganesh, V.; Nair, S. V.; Nair, A. S., A review on ‘self-cleaning and

365

multifunctional

366

10.1039/C4TA02542C.

materials.

J.

Mater.

Chem.

A

19 ACS Paragon Plus Environment

2014,

2,

14773–14797,

DOI

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

367

17.

Page 20 of 23

Maartensa, A.; PJacobsb, E.; Swart, P., UF of pulp and paper effluent: membrane fouling-

368

prevention and cleaning. J Memb. Sci. 2002, 209, (1), 81-92, DOI 10.1016/S0376-

369

7388(02)00266-1.

370

18.

Hua, B.;.Scott, K., Influence of membrane material and corrugation and process conditions on

371

emulsion

372

10.1016/j.memsci.2007.02.002.

373

19.

microfiltration.

J

Memb.

Sci.

2007,

294,

(1-2),

30-39,

DOI

Xue, Z.; Wang, S.; Lin, L.; Chen, L.; Liu, M.; Feng L.; Jiang, L., A Novel Superhydrophilic

374

and Underwater Superoleophobic Hydrogel‐Coated Mesh for Oil/Water Separation. Adv.

375

Mater. 2011, 23, 4270–4273, DOI 10.1002/adma.201102616.

376

20.

Wang, M.; Cao, Y.;. Xu, Z.-L; Li, Y.-X.; Xue. S.-M., Facile fabrication and application of

377

superhydrophilic stainless steel hollow fiber microfiltration membranes. ACS Sustainable

378

Chem. Eng., 2017, 5 (11), 10283-10289, DOI 10.1021/acssuschemeng.7b02300.

379

21.

Wu, J.-X.; Zhang, J.; Kang, Y.-L.; Wu, G.; Chen, S.-C.; Wang, Y.-Z., Reusable and Recyclable

380

Superhydrophilic Electrospun Nanofibrous Membranes with in-situCo-crosslinked Polymer-

381

Chitin Nanowhisker Network for Robust Oil-in-Water Emulsion Separation. ACS Sustainable

382

Chem. Eng., 2018, 6 (2), 1753–1762, DOI 10.1021/acssuschemeng.7b03102.

383

22.

Li, Y.; Liu, Y.; Liu, Y.; Lai, W.; Huang, F.; Ou A.; Qin, R.; Liu, X.; W. Xu. Ester Cross-linking

384

Enhanced Hydrophilic Cellulose Nanofibrils Aerogel. ACS Sustainable Chem. Eng., 2018, 6

385

(9), 11979–11988, DOI 10.1021/acssuschemeng.8b02284.

386

23.

Kang, Y.-L.; Zhang, J.; Wu, G.; Zhang, M. X.;. Chen, S.-C.; Wang. Y.-Z., Full-Biobased

387

Nanofiber Membranes toward Decontamination of Wastewater Containing Multiple Pollutants.

388

ACS

389

10.1021/acssuschemeng.8b01996.

390 391

24.

Sustainable

Chem.

Eng.,

2018,

6

(9),

11783–11792,

DOI

Gu, J.; Xiao, P.; Chen, P.; Zhang, L.; Wang, H.; Dai, L.; Song, L.; Huang, Y.; Zhang, J.; Chen, T., Functionalization of Biodegradable PLA Nonwoven Fabric as Superoleophilic and

20 ACS Paragon Plus Environment

Page 21 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering

392

Superhydrophobic Material for Efficient Oil Absorption and Oil/Water Separation. ACS Appl.

393

Mater. Interfaces, 2017, 9 (7), 5968–5973, DOI 10.1021/acsami.6b13547.

394

25.

Padaki, M.; Murali, R. S.; Abdullah, M.; Misdan, N.; Moslehyani, A.; Kassim, M.; Hilal, N.;

395

Ismail, A., Membrane technology enhancement in oil–water separation. A review. Desalination

396

2015, 357, 197-207, DOI 10.1016/j.desal.2014.11.023.

397

26.

Chaudhary, J. P.; Nataraj, S. K.; Gogda, A.; Meena, R., Bio-based superhydrophilic foam

398

membranes for sustainable oil–water separation. Green Chem. 2014, 16 (10), 4552-4558, DOI

399

10.1039/C4GC01070A.

400

27.

Chaudhary, J. P.; Vadodariya, N.; Nataraj, S. K.; Meena, R., Chitosan-Based Aerogel

401

Membrane for Robust Oil-in-Water Emulsion Separation. ACS Appl. Mater. Interfaces 2015, 7

402

(44), 24957-62, DOI 10.1021/acsami.5b08705

403

28.

Prasad, K; Goswami, A. M.; Meena, R,; Ramavat, B. K.; Ghosh, P. K.; Siddhanta, A. K.,

404

Superior quality agar from red alga Gelidiella acerosa (Rhodophyta, Gelidiales) from Gujarat

405

coast of India: An evaluation. Indian J. Geomarine Sci. 2006, 35(3), 268-274.

406

29.

Meena, R.; Prasad, K.; Ganesan, M,; Siddhanta, A. K., Superior quality agar from Gracilaria

407

species (Gracilariales, Rhodophyta) collected from the Gulf of Mannar, India. J. Appl. Psychol.

408

2008, 20(4), 397, DOI 10.1007/s10811-007-9272-6.

409

30.

Chhatbar, M. U.; Meena, R.; Prasad, K.; Chejara, D. R.; Siddhanta, A. K., Microwave-induced

410

facile synthesis of water-soluble fluorogenic alginic acid derivatives. Carbohydr. Res. 2011,

411

346 (5), 527-533, DOI 10.1016/j.carres.2011.01.002.

412

31.

Tang, M; Krishnamra, N.; Charoenphandhu, N.; Hoonsawat, R.; Pon-On W., Biomagnetic of

413

Apatite-Coated Cobalt Ferrite: A Core–Shell Particle for Protein Adsorption and pH-Controlled

414

Release. Nanoscale Res. Lett. 2011, 6-19, DOI 10.1007/s11671-010-9761-4.

415 416 21 ACS Paragon Plus Environment

ACS Sustainable Chemistry & Engineering 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

417

Page 22 of 23

For Table of Contents Use Only

Oil-spill

Pure Water Gen.

BSA

AG

418 419

A simple and green process for preparation of protein functionalised biodegradable aerogel

420

membranes (PFAMs) has been described. PFAMs tested for oil-spill and oil-water emulsion

421

separation.

22 ACS Paragon Plus Environment

Page 23 of 23 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Sustainable Chemistry & Engineering