Reactive Diazonium-Modified Silica Fillers for High ... - ACS Publications

Oct 11, 2016 - Institute of Chemical Technology and Engineering, Poznan University of Technology, Berdychowo 4, 60-965 Poznań, Poland. ‡. Universit...
0 downloads 0 Views 2MB Size
Subscriber access provided by CORNELL UNIVERSITY LIBRARY

Article

Reactive Diazonium-Modified Silica Fillers for High Performance Polymers Mariusz Piotr Sandomierski, Beata Strzemiecka, Mohamed Mehdi Chehimi, and Adam Voelkel Langmuir, Just Accepted Manuscript • DOI: 10.1021/acs.langmuir.6b02891 • Publication Date (Web): 11 Oct 2016 Downloaded from http://pubs.acs.org on October 17, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Langmuir is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 18

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Langmuir

2

Reactive Diazonium-Modified Silica Fillers for High Performance Polymers

3

Mariusz Sandomierski1, Beata Strzemiecka1,*, Mohamed M. Chehimi2*, Adam Voelkel1

4

1

1

5 2

6 7

Poznan University of Technology, Institute of Chemical Technology and Engineering, Berdychowo 4, 60-965 Poznań, Poland

Université Paris Est, ICMPE (UMR 7182), CNRS, UPEC, 2-8 rue Henri Dunant, 94320 Thiais, France

8

*

9

Abstract We describe a simple way of modification of three silica-based fillers with in situ generated 4-hydroxymethylbenzenediazonium salt (+N2-C6H4-CH2OH). The rationale for using a hydroxyl-functionalized diazonium salt is that it provides surface-functionalized fillers that can react with phenolic resins. The modification of silica by diazonium salts was assessed by FTIR and XPS. FTIR permitted to track benzene ring breathing and C-C. The absence of the characteristic N≡N stretching vibration at 2200-2300 cm−1 range indicates the loss of the diazonium group. XPS results indicate a higher C/Si atomic ratio after diazonium-modification of fillers as well as the presence of π−π* C1s satellite peaks characteristic of the surface-tethered aromatic species. Adhesion of aryl layers to silicas is excellent as they withstand harsh thermal and organic solvent treatments. Phenolic resins (used e.g. as binders in abrasive products) were filled with diazoniummodified silicas at 10 - 25 wt. %. The reactivity of the fillers towards phenolic resins was evaluated by determination of flow distance. After annealing at 180 °C, the diazoniummodified silica/phenolic resin composites were mechanically tested using the three-point flexural method. The flexural strength was found to be up to 35 % higher than that of the composites prepared without any diazonium salts. Diazonium-modified silica with surface bound –CH2-OH groups are thus ideal reactive filler for phenolic resins. Such filler ensures interfacial chemical reactions with the matrix and imparts robust mechanical properties to the final composites. This specialty diazonium-modified silica will find the potential application as fillers in the composites for the abrasive industry. More generally, aryl diazonium salts are unique new series of compounds for tailoring the surface properties of fillers and tuning the physicochemical and mechanical properties of polymer composites.

10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33

corresponding author: [email protected] ; [email protected]

34 35 36

Keywords: silica, aryl diazonium salt; surface modification; novolak matrix; composite interface

37 38 1 ACS Paragon Plus Environment

Langmuir

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2 3 4 5 6 7 8 9 10 11 12

Page 2 of 18

1. Introduction Phenolic resins are among the most important resins used as binders for materials containing glass, wood, metal, paper, rubber and others.1 They are most often used for the production of abrasive tools as they possess very good thermal and chemical stability, high hardness and the ability to bind abrasive grains and fillers together. Abrasive articles are complex composites consisting of abrasive particles, wetting agent (most often resole), binder (most often novolak) and filler (e.g. cryolite, potassium fluoroaluminate (PAF), pyrite). 2, 3 World production of phenolic resins is more than 6 million tons per year and it is 2 % of the world production of polymers. The main factor contributing to the wide application of phenolic resins is their ability to cure by heating. 4, 5 Phenol-formaldehyde resins are divided into resoles and novolaks. The conditions required to obtain the phenol-formaldehyde resins are shown in Table 1.

13 14

Table 1. Types of phenol-formaldehyde resins. Resin type Catalyst F/P Physical State Novolak Acidic