Recent Advances in Biodegradable Conducting Polymers and Their

May 9, 2018 - The growing importance and interests in biodegradable conducting polymers (CPs) have fuelled rapid development of this unique class of ...
5 downloads 3 Views 3MB Size
Subscriber access provided by Kaohsiung Medical University

Review

Recent Advances in Biodegradable Conducting Polymers and Their Biomedical Applications * Kenry, and Bin Liu Biomacromolecules, Just Accepted Manuscript • DOI: 10.1021/acs.biomac.8b00275 • Publication Date (Web): 09 May 2018 Downloaded from http://pubs.acs.org on May 9, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

Recent Advances in Biodegradable Conducting

2

Polymers and Their Biomedical Applications

3

Kenry, Bin Liu*

4 5

Department of Chemical and Biomolecular Engineering, National University of Singapore,

6

4 Engineering Drive 4, Singapore 117585, Singapore

7 8

KEYWORDS: Conjugated polymers; Biodegradable polymers; Biomedical imaging; Tissue

9

engineering and regenerative medicine; Biomedical implants.

10 11

ABSTRACT

12

The growing importance and interests in biodegradable conducting polymers (CPs) have fuelled rapid

13

development of this unique class of polymeric materials in recent years. Possessing both the electrical

14

conductivity of metallic conductors as well as the biodegradability of biocompatible polymers,

15

biodegradable CPs are highly sought after. In fact, they have emerged as the ideal biomaterials with

16

immense potentials to augment a wide range of practical biomedical applications. Herein, we provide

17

a broad overview on the recent advances in the development of biodegradable CPs and their

18

biomedical applications. We first introduce the fundamentals of conducting and biodegradable

19

polymers, followed by discussions on the major strategies currently used to fabricate biodegradable

20

CPs. We then highlight the potential biomedical applications of biodegradable CPs, specifically for

21

tissue engineering and regenerative medicine, biomedical imaging, as well as biomedical implants,

22

bioelectronics devices, and consumer electronics. We conclude this review article by offering our

23

perspectives on the current challenges and future opportunities facing the development and practical

24

applications of biodegradable CPs.

25

1

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

1. INTRODUCTION

2

For the past four decades since the first demonstration of conducting polymers (CPs) in the 1970s,1, 2

3

the importance and interests in this special class of organic materials have grown exponentially. With

4

an electrical conductivity approaching that of metals and inorganic semiconductor as well as the facile

5

preparation and good processability of common polymers,3 CPs have tremendous potentials for a

6

wide range of applications.4-6 The excellent in vitro and in vivo biocompatibility of CPs7-10 have

7

rendered them to be increasingly explored for various biomedical applications, particularly for tissue

8

engineering, drug delivery, bioimaging, and biosensing.11-20 More specifically, through electrical

9

stimulation, CPs are able to regulate various cellular behaviours, including cellular adhesion,

10

alignment, proliferation, differentiation, and regeneration of damaged tissues, such as skin, bone,

11

nerve, and myocardium tissues.21-26

12

While CPs have been recognized as promising biomaterials, their practical bioapplications

13

and clinical translations are still hindered by numerous limitations, notably the poor solubility and

14

non-biodegradability of conventional CPs.27,

15

environment as an implant material for tissue engineering applications, the non-biodegradability of

16

existing CPs may pose significant problems. Specifically, the inability of CPs to degrade may prolong

17

their stay in vivo, which in turn, may trigger undesirable inflammatory response. Tremendous efforts

18

have consequently been geared towards the synthesis of biodegradable electroactive polymers with

19

excellent biodegradability.29 In fact, up to date, biodegradability remains one of the greatest holy

20

grails in the development of CPs for biomedical applications.

21

28

For example, when brought into a physiological

Encouragingly, CPs with biodegradable characteristic have been progressively realized

22

through numerous design and fabrication strategies.12,

29

23

biodegradable CPs was through the blending of CPs with typical biodegradable polymers, such as

24

polylactide (PLA), polycaprolactone (PCL), and polyurethane (PU).30-33 Despite the considerable

25

breakthrough achieved via this blending technique, the biodegradability of the resultant composites

26

for practical in vivo biomedical applications is still far from satisfactory. To address this, recent years

27

have witnessed the emergence of other ingenious approaches in the preparation of biodegradable CPs.

One of the earliest attempts to realize

2

ACS Paragon Plus Environment

Page 2 of 48

Page 3 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

These include primarily the conducting oligomer-based preparation of linear, star-shaped,

2

hyperbranched, and other complex biodegradable electroactive polymeric architectures, as well as the

3

synthesis of biodegradable CPs based on modified monomers or polymers.12, 29, 34 The development of

4

these strategies have, in fact, greatly expanded the toolbox of biodegradable CPs and opened up

5

further opportunities for the practical implementation of their biomedical applications.

6

This review article seeks to provide a broad overview on the recent advances in the

7

development of biodegradable CPs and their biomedical applications. The fundamentals of

8

conducting and biodegradable polymers are first introduced, followed by discussions on the major

9

strategies currently being employed to generate biodegradable CPs. The potential biomedical

10

applications of biodegradable CPs, specifically for tissue engineering and regenerative medicine,

11

biomedical imaging, as well as biomedical implants, bioelectronics devices, and consumer electronics,

12

are then highlighted. This review article eventually concludes with a summary and perspectives on the

13

current challenges and future opportunities facing the development and practical applications of

14

biodegradable CPs.

15 16

2. FUNDAMENTALS OF CONDUCTING AND BIODEGRADABLE POLYMERS

17

CPs are synthetic macromolecules possessing highly delocalized π-conjugated backbone structure and

18

configurable side chains (Figure 1A).3,

19

polyacetylene (PA), polypyrrole (PPy), polyaniline (PANi), polythiophene (PTh), poly(3,4-

20

ethylenedioxythiophene) (PEDOT), polyfluorenes (PF), poly(p-phenylene vinylene) (PPV), poly(p-

21

phenylene) (PPP), poly(p-phenylene ethynylene) (PPE), and their derivatives (Figure 1B).

22

Structurally, the CP backbone is made of alternating single C-C, double C=C, or triple C≡C bonds,

23

where highly delocalized electrons are weakly held together by π bonds, while the overall polymeric

24

chain strength is regulated by the strong σ bonds.1, 3 In fact, the conjugated double or triple bonds

25

along their backbone are primarily responsible for the exceptional electrical conductivity displayed by

26

CPs. Furthermore, this conjugated backbone architecture endows CPs with other unique electronic

27

and photophysical properties, such as tunable electron affinity, ionization energy, as well as high

4, 35, 36

Some of the most common examples of CPs are

3

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 48

1

molar absorptivity, energy transfer efficiency, fluorescence quantum yield, and photostability. CPs

2

also have intrinsically rigid and stiff hydrophobic backbone, which in turn, can facilitate π-π stacking

3

of the polymers.

4

The electrical conductivity of CPs has been recognized to originate from the nonlinear defects

5

created during the polymerization of a monomer or during the doping process.37, 38 As a result, the

6

conductivity of CPs can be manipulated via the same doping process, in which dopant molecules are

7

deliberately introduced to remove or add electrons to the CP backbone. This doping process is

8

typically dictated by numerous factors, notably conjugation length, polymeric chain length, and

9

charge carrier length. In general, through doping, either p- or n-type dopants can be introduced to

10

endow the CPs with positive or negative charges, respectively. When a p-type dopant is introduced,

11

the polymer is oxidized and a hole charge carrier is generated. On the other hand, when an n-type

12

dopant is added, the polymer is reduced and an electron is introduced in the conduction band to create

13

an electron charge carrier. The charge carrier mobility is enhanced by the existence of the π–orbital

14

system within the CP backbone. Interestingly, it is noteworthy that undoped polymers may have

15

electrical conductivity as low as 1.0 × 10-10 – 1.0 × 10-6 S/cm similar to those of insulators and

16

semiconductors.39 However, with slight doping, this conductivity can be significantly enhanced by 10

17

or more orders of magnitude. For example, common doped CPs, such as doped PPy, PANi, PTh, and

18

PEDOT, have high electrical conductivities of 1.0 × 102 – 7.5 ×103, 3.0 ×101 – 2.0 ×102, 1.0 ×101 –

19

1.0 × 103, and 4 ×10-1 – 4 × 102 S/cm, respectively.12, 13

20

While possessing outstanding electrical property, pristine CPs may not be effectively

21

employed for biomedical applications due to their poor dispersibility in aqueous solutions.28,

22

Nevertheless, with their flexible side chains, CPs can be easily conjugated with appropriate functional

23

groups to impart them with desirable biophysical properties.

24

with water solubility by introducing hydrophilic polar side chains or charged (e.g., anionic or cationic)

25

pendant groups along their conjugated backbone. CPs can also be prepared as water-soluble

26

nanoparticles through a self-assembly process in aqueous solution, followed by the amphiphilic

27

surfactant or block copolymer-mediated stabilization. Functionalization of CPs may also be employed

28

to impart them with other biophysical properties, such as high cellular internalization and low

28, 40

4

ACS Paragon Plus Environment

40

For example, CPs can be endowed

Page 5 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

cytotoxic profile. While these outstanding biophysical properties are highly desirable, they alone are

2

not sufficient to warrant the practical biomedical applications of CPs. To fully realize the potential of

3

CPs for biomedical applications, these polymeric materials need to be biodegradable too.

4

Biodegradable polymers, which can be disintegrated into their smaller molecular components,

5

are highly desirable for in vivo biomedical applications.41-44 These polymers typically comprise

6

varying amount of biodegradable units, such as the hydrolyzable esters and hydrazones, which can be

7

directly or sequentially cleaved upon encountering external stimulations, including acidic

8

environment, high temperature, or certain enzymatic reactions.42,

9

biodegradable entities, the biodegradable polymers can be decomposed to generate non-toxic natural

10

byproducts, notably water and carbon dioxide.44 Furthermore, the biodegraded polymeric components

11

with lower molecular weights may have in principle shorter in vivo circulation time and may be

12

excreted from the body much more easily via kidney.44, 48 As such, this body clearance will ensure that

13

no undesirable inflammatory response will be elicited by the biodegradable polymers once they have

14

achieved their intended objectives in the in vivo system.

45-47

In contrast to the non-

15

With the continuous explorations into the applications of CPs for a wide range of biomedical

16

applications, particularly for controlled drug delivery, tissue engineering, and regenerative medicine,

17

the importance of biodegradability of these biomaterials has been increasingly highlighted.29

18

Unfortunately, CPs are inherently not biodegradable owing to their inert π-conjugated architecture.

19

The absence of biodegradable feature in CPs has impeded their effective in vivo bioapplications and

20

clinical translation. Continuous efforts have thus been aimed at developing CPs with biodegradable

21

characteristic, although this endeavour of developing ideal polymeric systems with both electrical

22

conductivity and biodegradability has remained a considerable challenge to date. One of the earliest

23

attempts at synthesizing biodegradable CPs have made use of common biodegradable synthetic

24

polyesters, such as polylactide (PLA), polyglycolide (PGA), polycaprolactone (PCL), their

25

copolymers poly(lactic-co-glycolic acid) (PLGA), and polyurethane (PU) (Figure 1C).30 In fact, these

26

biodegradable aliphatic polyesters are highly suitable for biomedical applications and have long found

27

practical utility, even before the discovery of CPs, due to their excellent biocompatibility and

28

biodegradability. Through direct blending of CPs with these biodegradable polymers, the first CP 5

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

composites with a certain degree of biodegradability have been successfully demonstrated. Since then,

2

more design and fabrication strategies have emerged and achieved a wide range of CPs with various

3

chemical compositions, macromolecular structures, and degrees of biodegradability.

4 5

Figure 1. Backbone and chemical structures of conducting and biodegradable polymers. (A) Conducting

6

polymer (CP) with its conjugated backbone structure which consists of alternating single and double bonds,

7

where σ bond and π bond maintains the polymeric chain strength and facilitates electron delocalization,

8

respectively. Reprinted with permission from ref.36 Copyright 2018 Wiley-VCH Verlag GmbH & Co. (B)

9

Chemical structures of common CPs, such as polyacetylene (PA), polypyrrole (PPy), polyaniline (PANi),

10

polythiophene (PTh), poly(3,4-ethylenedioxythiophene) (PEDOT), polyfluorenes (PF), poly(p-phenylene) (PPP),

11

poly(p-phenylene vinylene) (PPV), and poly(p-phenylene ethynylene) (PPE). (C) Chemical structures of

12

biodegradable polymers typically used for biomedical applications, such as polylactide (PLA), polyglycolide

13

(PGA), polycaprolactone (PCL), poly(lactic-co-glycolic acid) (PLGA), and polyurethane (PU).

6

ACS Paragon Plus Environment

Page 6 of 48

Page 7 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2 3

3. STRATEGIES TO FABRICATE BIODEGRADABLE CONDUCTING POLYMERS

4

While CPs have been known to be inherently not biodegradable and are extremely stable under

5

physiological conditions, an increasing number of studies has shown that through ingenious design

6

and fabrication approaches, this group of attractive polymers can be modified and endowed with a

7

certain degree of biodegradability.12, 29 In fact, these strategies have been utilized to generate three

8

primary types of biodegradable CPs, i.e., (1) partially biodegradable CP composites based on the

9

blends of conducting and biodegradable polymers, (2) biodegradable CPs based on conducting

10

oligomers, and (3) biodegradable CPs based on modified monomers and/or integration of degradable

11

monomer units and conjugated linkers.

12 13 14

3.1. Partially Biodegradable CP Composites based on the Blends of Conducting and Biodegradable Polymers

15

One of the earliest strategies to fabricate partially biodegradable CP composites relies on the direct

16

blending of the conducting and biodegradable polymers to generate polymeric composites (Figure 2),

17

in which CPs contribute to the electroactivity and conductivity of the composites while their

18

controlled degradability is provided by the biodegradable polymers.31-33 For example, PPy has been

19

successfully combined with various synthetic biodegradable matrices, such as PLGA, PLA, PCL, and

20

PU, to prepare partially biodegradable functional polymeric composites in the forms of nanofibers

21

(Figures 2A and 2B)30, 49 and nanoparticles (Figure 2D),50 using methods like electrospinning30, 49 and

22

emulsification.50 The integration of PPy into these biodegradable polymer composites has been noted

23

to enhance their electrical conductivity considerably. Specifically, the sheet resistance of electrospun

24

PLGA nanofibers, which intrinsically behave like insulators, could be reduced to about 9.0 × 104 – 7.4

25

× 103 Ω/square through PPy coating.30 Similarly, the incorporation of PPy nanoparticles into

26

insulating PLA nanofibers could increase the surface conductivity of the composite PPy-PLA

27

structures from less than 1.0 × 10-16 S/cm to as high as 1.0 × 10-4 S/cm.51 The increment in the content

7

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

of PPy nanoparticles in the composite PPy-PLA nanofibers was also noted to gradually increase their

2

lost weight from 14 to 24% in phosphate-buffered saline (PBS) at 37 oC over 12 weeks. In addition to

3

synthetic biodegradable polymers, PPy has been prepared directly on a silk substrate to generate a

4

biodegradable silk-PPy composite film, in which the disintegration behaviour of the composite film is

5

significantly influenced by the degradation profile of the silk substrate.52, 53 Besides PPy, other CPs,

6

such as PEDOT and PANi, have been blended or grafted with biodegradable polymers to assemble

7

partially biodegradable functional polymeric structures with improved electrical conductivity.54, 55 For

8

instance, PEDOT has been integrated with PLGA to realize biodegradable electroactive PEDOT-

9

PLGA microfibers whose overall conductivity could be enhanced up to 7.0 × 10-2 – 2.8 × 10-1 S/cm by

10

increasing the content of their polymerizable EDOT monomers (Figure 2C).54 PANi, on the other

11

hand, has been grafted to gelatin and then crosslinked with genipin to form biodegradable

12

electroactive hydrogels (GP hydrogels) with electrical conductivity ranging from 4.54 × 10-4 to 2.41 ×

13

10-4 S/cm.55 These hydrogels had favourable degradability where significant weight loss of about 50%

14

to 60% occurred after 7 to 14 d into the in vitro degradation test conducted in PBS with pH 7.4 at 37

15

o

C.

16

Direct blending of conducting and biodegradable polymers offers a simple and

17

straightforward route to achieve partially biodegradable CP composites. In fact, one of the main

18

advantages of this technique is that, by selecting appropriate types and ratios of the two polymers to

19

be blended, the conductivity and degradation rate of the eventual copolymers can be regulated for a

20

wide range of biomedical applications. For example, various partially biodegradable CP-based

21

scaffolds have been realized recently due to the flexibility of the direct blending strategy in

22

incorporating different conducting and biodegradable polymers. These polymeric composites have

23

been collectively explored for various biomedical applications, notably for tissue engineering and

24

regenerative medicine applications. However, it is important to highlight that, while this blending

25

approach incorporates the strengths and desirable features of both polymers, the resultant polymer

26

blends may not possess the original maximum conductivity and biodegradability of their individual

27

constituents. For instance, due to the inherent non-biodegradability of PPy, the amount of PPy

28

introduced into the polymer blends is typically kept to a minimum so that their overall biodegradation 8

ACS Paragon Plus Environment

Page 8 of 48

Page 9 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

behavior will not be affected. As such, while the copolymers manage to maintain their

2

biodegradability, they may not possess sufficient electrical conductivity for practical biomedical

3

applications.

4

More importantly, although the content of CPs in the polymeric blends can be minimized and

5

this may eliminate the need for biodegradability to a certain degree, the small quantity of CPs is

6

anticipated to be chemically inert and will stay in the physiological environment for an unknown

7

period of time if the partially biodegradable CP composites are introduced into the body. Clearly, the

8

blending technique does not overcome the primary challenge of achieving a complete decomposition

9

and clearance of CPs from the body after the polymeric composites have degraded. Therefore,

10

increasing efforts in recent years have been devoted to developing alternative techniques which can

11

enable the complete disintegration of biodegradable CP composites.

12 13

Figure 2. Partially biodegradable CP-based functional nanostructures prepared using the blends of

14

biodegradable and CPs. (A) Scanning electron microscopy (SEM) image of individual PPy-coated PLGA

15

nanofibers. (B) SEM image of the PPy-coated PLGA nanofibrous mesh. All scale bars represent 1 µm.

16

Reprinted from ref.30 , Copyright 2009, with permission from Elsevier. (C) Field emission SEM (FE-SEM)

17

image of the aligned PEDOT-loaded PLGA microfibers. Scale bar represents 5 µm. Reprinted from ref.54

9

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 48

1

Copyright 2012, with permission from Elsevier. (D) Transmission electron microscopy (TEM) image of the

2

PPy-coated PLGA core-shell nanoparticles. Scale bar represents 200 nm. Reproduced from ref.50

3

permission of The Royal Society of Chemistry. http://dx.doi.org/10.1039/c6ra18261e

with

4 5

3.2. Biodegradable Conducting Polymers based on Conducting Oligomers

6

To endow the conducting biodegradable polymers with better degradability and faster body clearance,

7

small-sized short chains of conducting monomers, i.e., conducting oligomers, have been increasingly

8

explored as viable alternatives to CPs as the conducting components of the electroactive

9

biodegradable copolymers.56, 57 Conducting oligomers generally possess well-defined structures as

10

well as an electroactivity and redox behaviour similar to their corresponding CPs.56-58 Nonetheless, in

11

contrast to CPs, conducting oligomers have numerous advantages, including well-confined structure,

12

higher flexibility in terms of synthesis and processing, better solubility, and capability to undergo

13

gradual degradation and renal clearance. In fact, investigations into the oligomers of pyrrole, aniline,

14

and thiophene have elucidated that, in addition to an electroactivity similar to that of their CP

15

counterparts, these oligomers can be processed and copolymerized with biodegradable polymers more

16

easily and they display a better biodegradable property. Various studies have also revealed that, in

17

contrast to the oligomers of pyrrole and thiophene, aniline oligomers, primarily aniline trimer, aniline

18

tetramer, and aniline pentamer, have a more facile and straightforward synthesis and processing

19

steps.29, 56, 58 Most significantly, these oligomers can be taken up and internalized much more easily by

20

the macrophages and subsequently excreted by kidney. Therefore, conducting oligomers have

21

emerged as a viable option for the realization of totally biodegradable and conducting polymeric

22

structures.

23

Biodegradable CPs based on conducting oligomers are typically assembled by connecting the

24

heteroaromatic oligomers with biodegradable polymeric segments via linkages, such as biodegradable

25

ester bonds, in a linear macromolecular architecture. This approach has, in fact, been largely explored

26

for the generation of biodegradable temporary scaffolds for tissue engineering applications. Similar

27

design concept based on conducting oligomers has recently been applied for the synthesis of

28

biodegradable electroactive PU film (Figure 3).59 Here, the biodegradable dopant mixture-free 10

ACS Paragon Plus Environment

Page 11 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

conducting PU elastomer (DCPU) was prepared through the chemical linking of conducting element

2

(i.e., amine-capped aniline trimer), biodegradable element (i.e., PCL), and dopant molecules (i.e.,

3

dimethylolpropionic acid (DMPA)) into a linear PU chain using 1,6-hexamethylene diisocyanate

4

(Figure 3A). The electrical conductivity of DCPU elastomer could be tuned by varying the content of

5

aniline trimer or DMPA in the PU backbone. The electrical conductivity of the dry state DCPU was

6

noted to span from 5.5 × 10-8 to 1.2 × 10-5 S/cm. The control structures fabricated without aniline

7

trimer and dopant showed low electrical conductivity of 5.5 × 10-12 and 2.7 × 10-10 S/cm, respectively.

8

In a wet state in PBS, however, the DCPU films possessed higher electrical conductivity ranging from

9

4.4 × 10-7 to 4.7 × 10-3 S/cm. These films also displayed high flexibility and elasticity, as evidenced

10

from their ease of bending and knotting (Figures 3B and 3C), and could be degraded via hydrolysis

11

and enzymatic reactions. More specifically, in vitro degradation tests on DCPU films in PBS at 37 oC

12

revealed that the films experienced hydrolytic degradation with a low degradation rate, in which the

13

remaining film mass reached about 96.6 to 98.2% after 8 weeks. Contrastingly, in a lipase/PBS

14

solution, the degradation rate of the films was significantly higher. In fact, within 14 days, the

15

remaining film mass could reach as low as 75.8%. Furthermore, using a salt leaching approach, the

16

DCPU elastomer could be transformed into a porous scaffold with tunable pore size, which is suitable

17

for numerous biomedical applications (Figures 3D and 3E).

18

Interestingly, besides typical polyesters such as PLA, PCL, and PGA, hybrid inorganic-

19

organic polymers, notably polyphosphazene and its derivatives, have been incorporated as the

20

biodegradable segment of the biodegradable CPs.60-62 These polymers are unique because they possess

21

versatile side chains which can be modified with a wide range of functional groups. This side chain

22

modification enables the facile and precise tuning of the amount of oligomers in the biodegradable

23

CPs such that their overall conductivity and biodegradability can be controlled. For instance, a

24

biodegradable electroactive CP for potential application in nerve tissue engineering was synthesized

25

by functionalizing aniline pentamer and glycine ethyl ester on polyphosphazene (PGAP copolymer).62

26

PGAP showed an electrical conductivity of approximately 2 × 10-5 S/cm. In vitro study on the

27

degradation profile of PGAP in PBS at 37 oC showed that they underwent a weight loss of about 50%

28

over 70 days. 11

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 48

1

While numerous biodegradable CPs have been demonstrated based on different conducting

2

oligomers, it is noteworthy that a large number of these copolymers are only soluble in organic

3

solvents, leading to unwanted environmental challenges.29 Copolymers with biodegradability in non-

4

toxic aqueous solution are thus highly desirable. Driven by this, recent years have seen the rapid

5

development of biodegradable electroactive copolymers based on the integration of conducting

6

oligomers with biodegradable natural polymers. Some of the examples of these include chitosan-

7

aniline pentamer-based copolymers63 and polysaccharide-aniline tetramer-based copolymers.64

8 9

Figure 3. Biodegradable conducting elastomers prepared from conducting aniline trimer. (A) Synthetic route to

10

the biodegradable dopant mixture-free conducting polyurethane elastomer (DCPU), in which the biodegradable

11

element (i.e., PCL), conducting element (i.e., aniline trimer), and dopant molecules are chemically linked into a

12

linear polyurethane chain. (B) Optical photograph of the fabricated DCPU film. (C) Optical photograph showing

13

the high flexibility of DCPU film as demonstrated through its bending and knotting. (D) Optical photograph of

14

the porous DCPU scaffold obtained using the salt leaching approach. (E) SEM image of the corresponding

15

porous DCPU scaffold with an average pore size of approximately 116 µm. Scale bar represents 100 µm.

16

Reprinted

17

https://creativecommons.org/licenses/by/4.0/ Copyright 2016 Xu et al.

from

ref.59

under

a

Creative

Commons

Attribution

18

12

ACS Paragon Plus Environment

4

International

License

Page 13 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

In addition to those with linear macromolecular architecture, conducting oligomers have been

2

progressively processed into biodegradable conducting copolymers with other macromolecular

3

architectures, notably star-shaped, hyperbranched, and crosslinked network architectures (Figure 4).34

4

Macromolecular structures of polymers have been reported to play a key role in influencing their

5

morphological feature, electrical conductivity, mechanical and thermal properties, biodegradation rate,

6

and importantly, their overall performance.65,

7

monomers and same molecular weights may exhibit different electrical conductivity and

8

biodegradability due to their different macromolecular architectures. By tuning the macromolecular

9

architectural diversity, the optimal electroactivity and biodegradability of the copolymers may be

10

achieved for specific biomedical applications. Consequently, a plethora of biodegradable CPs with

11

various macromolecular architectures have been synthesized and reported in the last few years. Some

12

examples of these are: (1) star-shaped branched biodegradable electroactive copolymers based on

13

aniline trimer and PLA,67 (2) hyperbranched biodegradable electroactive copolymers based on aniline

14

tetramer and PLA68 as well as based on aniline pentamer and PCL,66 and (3) crosslinked

15

biodegradable electroactive elastomers or hydrogels based on aniline trimer, PLLA, and PU-urea,69

16

based on aniline tetramer, chitosan, and glutaraldehyde,70 based on aniline tetramer, PLA, glycidyl

17

methacrylate, ethylene glycol dimethacrylate,71 as well as based on aniline pentamer, poly(glycerol

18

sebacate), and PU.72 These aniline oligomer-based biodegradable CPs typically display enhanced

19

electrical conductivity in the range of 10-6 to 10-4 S/cm.66, 69-71 For instance, with an increasing content

20

of aniline tetramer from 0 to 30%, the conductivity of the aniline tetramer-grafted chitosan-based

21

elastomers (DECPH films) could increase from 3.13 × 10-8 to 2.94 × 10-5 S/cm.70 At the same time,

22

this increment in aniline tetramer content from 0 to 25% led to an increasing weight loss from about 6

23

– 7% to 13 – 14% when these elastomers were immersed in buffer solutions with pH 2.1 and 7.4 for

24

48 h. Similarly, increasing the content of aniline tetramer from 10 to 40% in the hydrogels fabricated

25

from aniline tetramer, PLA, glycidyl methacrylate, and ethylene glycol dimethacrylate (DEC

26

hydrogels) could enhance their electrical conductivity from 4.69 × 10-7 to 1.05 × 10-4 S/cm.71

66

In fact, two polymers with the same amount of

13

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Altogether, due to the versatility of the conducting oligomers coupled with the wide range of

2

available biodegradable polymers and macromolecular architectures, this strategy of preparing

3

biodegradable CPs has become one of the most widely adopted approaches in recent years.

4 5

6 7

Figure 4. Different macromolecular architectures of the biodegradable CPs based on conducting oligomers: (A)

8

linear copolymer, (B) star-shaped, (C) hyperbranched copolymer, and (D) crosslinked network architectures.

9

Reprinted by permission from ref.34 Copyright 2014 Science China Press and Springer-Verlag Berlin Heidelberg.

10

https://link.springer.com/journal/11426

11 12 13

3.3. Biodegradable Conducting Polymers based on Modified Monomers and/or Integration of Degradable Monomer Units and Conjugated Linkers

14

In addition to biodegradable-conducting polymer blending and conducting oligomer-based approaches,

15

some of the more increasingly explored strategies in the development of biodegradable CPs include

16

the modification of conducting monomers and/or the integration of degradable monomer units or

17

conjugated linkers to generate bioerodible CPs.73-76 Instead of achieving partial degradation based on

18

conventional chemical bond scission, these modified CPs can be eroded gradually to realize enhanced

19

and full biodegradation. One of the earliest studies demonstrating this concept showed that pyrrole

20

monomers could be modified and then polymerized to achieve erodible PPy.73 Here, ionisable (e.g.,

21

acid) and/or hydrolysable (e.g., ester) functional groups were first introduced to the backbone of

22

pyrrole monomers to obtain β-substituted pyrrole monomers. This was followed by the oxidative

23

electrochemical and ferric chloride-mediated chemical polymerization of modified pyrrole monomers

24

to achieve erodible PPy. Conductive thin films fabricated from the acid-functionalized PPy displayed

14

ACS Paragon Plus Environment

Page 14 of 48

Page 15 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

a low average resistance of about 300 Ω. Importantly, the modified PPy was noted to be able to

2

degrade gradually under physiological conditions and mediate the proliferation and differentiation of

3

primary human cells. More clearly, at 37 oC, thin films fabricated from acid-modified PPy could

4

dissolve within 24 h in a solution with pH 8.2, although they displayed a noticeably slower dissolution

5

rate at pH 5. Similarly, pellets formed from the acid-modified PPy showed twice the erosion rate at

6

pH 7.2 than at pH 5. In fact, incubated in a solution with pH 7.2 at 37 oC, these pellets showed a mass

7

loss of 27% over 80 days. As a comparison, under the same incubation condition, the mass loss

8

exhibited by the methyl ester-functionalized PPy was only 6%. This suggests that the degradation

9

rates of these erodible CPs could be modified by introducing and tuning the amount of different

10

functional side groups.

11

Besides pyrrole-based erodible CPs, a separate study has reported the development of a

12

thiophene-based erodible CP composite for biomedical applications.74 In the study, employing a layer-

13

by-layer technique, fully erodible and electroactive polymeric films were assembled from the

14

positively

15

thienyl)ethoxypropanesulfonate) (SPT-PEI polymeric film). The synthesized multi-layered films were

16

observed to exhibit high electrical conductivity, ranging from 7.82 × 10-3 to 2.76 × 10-2 S/cm, and

17

could support muscle cell adhesion and proliferation. Significantly, these polymeric films were able to

18

undergo full degradation in an aqueous environment with physiologically relevant pH at 37 oC over

19

83 to 130 days.74 Similarly, based on thiophene monomer, a recent work has demonstrated the

20

synthesis of biodegradable fluorescent CP nanoparticles (CPNs) for biomedical imaging through the

21

integration of biodegradable imidazole units in the conjugated backbone (Figure 5).75 Here, the

22

thiophene monomer unit was first copolymerized with imidazole monomer to generate fully

23

conjugated biodegradable CPNs (Figure 5A). The thiophene monomer was then modified with either

24

methoxy (OMe) or oligoethyleneoxy (OEG) side groups in order to provide both improved stability to

25

the resultant nanoparticles in aqueous solutions as well as enhanced solubility of the degraded

26

products. The assembled CPNs were noted to undergo decomposition through an imidazole

27

degradative oxidation mechanism when exposed to reactive oxygen species (ROS), such as hydrogen

28

peroxide produced by lipopolysaccharide-activated macrophages (Figure 5B). Intriguingly, the

charged

poly(ethyleneimine)

and

the

negatively

15

ACS Paragon Plus Environment

charged

poly(ammonium(3-

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

degradation of both OMe- and OEG-functionalized CPNs could be observed as early as 11.5 h after

2

incubation with activated macrophages. In short, the degradative oxidation of imidazole could be

3

initiated by ROS, through which the CP backbone at the imidazole unit was cleaved, resulting in a

4

complete decomposition of the CPNs into soluble fragments with much lower molecular weights.

5 6

Figure 5. Synthetic and degradation processes of the imidazole-based CPNs. (A) Synthetic route to the

7

biodegradable CPNs through the Sonogashira dispersion polymerization of the monomers of thiophene with

8

imidazole. The thiophene monomer was functionalized with either methoxy (i.e., OMe for CPN P1) or

9

oligoethyleneoxy (i.e., OEG for CPN P2) side groups. (B) Degradation mechanism of the biodegradable CPNs

10

in the presence of reactive oxygen species (ROS). Reprinted from ref.75 under a Creative Commons Attribution

11

4 International License https://creativecommons.org/licenses/by/4.0/ Copyright 2017 Repenko et al.

12 13

Further to monomer modification and biodegradable unit integration, one of the more recent

14

examples has showed that fully erodible CPs can be prepared through the incorporation of degradable

15

conjugated linkers. In this work, based on imine chemistry, a fully decomposable polymer PDPP-PD

16

was synthesized as the building block of totally disintegrable transient electronics (Figure 6).76

17

Diketopyrrolopyrrole (DPP) dye, which was prepared from natural resources, was included into the

18

CP composite due to its high charge carrier mobility, ease of chemical functionalization, and excellent

19

biodegradability.76, 77 Imine bond (-C=N-), in contrast, was implemented as the conjugated linker due

20

to its high stability in an environment with neutral pH as well as its facile hydrolysis in a mildly acidic

16

ACS Paragon Plus Environment

Page 16 of 48

Page 17 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

environment.76,

78

2

succinic ester in tert-amyl acohol, followed by the attachment of branched alkyl chains (Figure 6A).

3

The addition of two aldehyde groups into the DPP monomer subsequently yielded DPP-CHO. Finally,

4

a condensation reaction between p-phenylenediamine and DPP-CHO catalyzed by p-toluenesulfonic

5

acid (PTSA) produced the biodegradable conducting PDPP-PD polymer, with an average hole

6

mobility of about 4.2 × 10-2 – 3.4 × 10-1 cm2/V.s. The CP was noted to be able to retain its stability

7

under neutral and basic conditions, but undergo decomposition both in solutions and in solid-state

8

under acidic conditions. More clearly, based on its absorption spectrum and physical color, PDPP-PD

9

solution decomposed into its monomer DPP-CHO after 10 d and it totally disintegrated after 40 days

10

under acidic condition. At the same time, the spin-coated PDPP-PD thin film experienced gradual

11

degradation after being immersed in an aqueous buffer solution with pH 4.6. The total decomposition

12

of the polymer was proposed to be driven by the acid-catalyzed imine bond hydrolyzation, followed

13

by the water-induced decomposition of DPP monomers via lactam ring hydrolyzation (Figure 6B).

DPP was first prepared via the reaction between 2-thiophenecarbonitrile and

14 15

Figure 6. Synthetic and degradation processes of the imine-based CP. (A) Synthetic route to the decomposable

16

conducting CP, i.e., PDPP-PD with the imine biodegradable linkers. (B) Proposed mechanism of PDPP-PD

17

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

decomposition through a two-step process, where this process of decomposition is initiated by imine bond

2

hydrolysis in the presence of acid, followed by the decomposition of DPP monomers via lactam ring hydrolysis.

3

Reprinted with permission from ref.76 Copyright 2017 National Academy of Sciences of the United States of

4

America.

5

It is important to highlight that, while only a limited number of studies have focused on this

6

strategy of assembling biodegradable CPs, it is possibly one of the best approaches to realize

7

polymers with both excellent electrical conductivity and full biodegradability. Therefore, it is

8

anticipated that active efforts will be progressively geared towards optimizing and enhancing this

9

polymer preparation approach in the near future.

10 11 12

4. BIOMEDICAL APPLICATIONS OF BIODEGRADABLE CONDUCTING POLYMERS

13

As a special class of polymeric materials with excellent morphological, electrical, and biological

14

properties, biodegradable CPs have demonstrated great potential for a wide range of biomedical

15

applications.29, 61, 73, 74 The unique combination of strong electroactivity and tunable biodegradability

16

has propelled active explorations into their potential biomedical applications in tissue engineering and

17

regenerative medicine, biomedical imaging, biomedical implants, bioelectronics devices, and

18

consumer electronics (Table 1).

19 20

4.1. Tissue Engineering and Regenerative Medicine

21

One of the earliest investigations into the biomedical applications of biodegradable CPs has focused

22

on their potential utility in the field of tissue engineering and regenerative medicine.33, 34, 79, 80 With

23

attractive features such as high electrical conductivity, controlled biodegradability, redox stability,

24

and three-dimensional architecture, biodegradable CPs are highly sought after for tissue engineering

25

applications. In recent years, tissue engineering and regenerative medicine have been progressively

26

seen as viable therapeutic approaches to treat physiological disorders with long-lasting and

27

devastating effects.80-82 These include bone defects, peripheral nerve injuries, and spinal cord damages.

28

To achieve its therapeutic outcomes, tissue engineering relies on the precise reconstruction of the 18

ACS Paragon Plus Environment

Page 18 of 48

Page 19 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

complex native cellular and tissue microenvironments using a wide range of strategies, including

2

biomaterials.83-88 In general, biomaterials used as scaffolds for tissue engineering and regenerative

3

medicine are expected to be highly biocompatible and have architectural and physical properties

4

similar to those of the host tissues such that these biomaterials are able to stimulate certain cellular

5

and tissue behaviours, notably cellular adhesion, proliferation, differentiation, and tissue formation.49,

6

83-86, 88

At the same time, they should be biodegradable. This is because these temporary scaffolds need

7

to decompose over time to be replaced by the newly generated cells and tissues. As a result, the

8

selection and design of biomaterials are extremely important to create the ideal artificial

9

microenvironments capable of mediating the cell-biomaterial interactions in order to achieve the

10

desired clinical outcome.

11

Over the last few decades, both natural and synthetic polymers have been widely used to

12

fabricate tissue engineering scaffolds.89-91 However, a large number of these biomaterials do not have

13

sufficient bioactivity to induce a full recovery of the tissue function. Synthetic organic CPs, such as

14

PPy, PANi, PTh, and PEDOT, have been widely evaluated more recently as biomaterial scaffolds for

15

tissue engineering application due to their outstanding electrical conductivity and biocompatibility.5, 6,

16

11, 27, 89

In fact, a wide range of cells, such as bone, muscle, and neuronal cells, has been reported to be

17

extremely responsive towards electrical stimulation.63, 68, 79, 81, 89, 92 As such, the electrical conductivity

18

of CPs serves as a potentially effective cue that enables local electrical stimulation of cells and tissues

19

for their enhanced growth and differentiation. For example, PPy has been widely reported to improve

20

neural activities, neurite extension, and axonal outgrowth.79, 92 Nevertheless, the effective applications

21

of CPs in tissue engineering and regenerative medicine are still hampered by numerous drawbacks,

22

such as their poor solubility in aqueous solutions, restricted processability, brittleness, and non-

23

biodegradability. Encouragingly, earlier attempts of using synthetic non-conducting biodegradable

24

polymers, such as PLA, PCL, and PLGA, for tissue engineering applications, coupled with the rapid

25

advances in polymer fabrication techniques, have prompted the development of integrated polymeric

26

systems comprising both electrical conductivity and biodegradability features. In one of the published

27

studies, an electrically conducting biodegradable polymeric composite was developed based on the

28

combination

of

PPy and

poly(D,

L-lactide-co-epsilon-caprolactone) 19

ACS Paragon Plus Environment

(PDLLA/CL).92

This

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

PPy/PDLLA/CL scaffold was shown to promote both the proliferation and neuronal differentiation of

2

PC12 cells as well as the regeneration of nerves in rats. In another study, a hybrid polymeric system

3

comprising biodegradable PLA/PLGA copolymer and conducting PPy doped with p-toluenesulfonate

4

was demonstrated to accelerate directed axonal growth and enhance the migration of Schwann cells

5

for an effective peripheral nerve repair.79

6

While the blends of electrically conducting and biodegradable polymers have been utilized

7

for regenerative medicine applications with considerable success, the biodegradability of the hybrid

8

composites is still largely not satisfactory. Consequently, more and more efforts have been directed

9

towards developing biodegradable CP-based tissue engineering scaffolds using oligomers.93 While

10

they typically have a good electroactivity similar to that of their polymer counterparts, oligomers have

11

tunable solubility, better processability, and biodegradability. They are more versatile as a result and

12

can be integrated or copolymerized with degradable polymers with ease, thus providing a greater

13

flexibility in terms of biodegradable conducting scaffold design. For example, a recent work has

14

highlighted the development of a biodegradable electroactive polymeric network based on the star-

15

shaped six-armed PLA and aniline trimer (PHAT polymer) for bone tissue engineering.67 PHAT was

16

noted to undergo gradual degradation with a weight loss of about 50% over 120 h. Furthermore, it

17

markedly improved the proliferation and osteogenic differentiation of C2C12 myoblasts. The use of

18

biodegradable CPs for bone tissue engineering has also been reported in one of the latest studies, in

19

which a block copolymer comprising PCL and aniline tetramer (AT-PCL polymer) was first

20

electrospun and then processed into a fibrous scaffold.94 The increasing addition of aniline tetramer

21

considerably reduced the sheet resistance of the AT-PCL composite from 2.47 × 107 to 3.0 × 106

22

Ω/square, revealing an enhanced electrical conductivity. Importantly, this polymeric composite

23

demonstrated an excellent biocompatibility and promoted the proliferation and osteogenic

24

differentiation of MC3T3-E1 precursor cells.

25

Similarly, using the electroactive aniline tetramer, a biodegradable conducting shape memory

26

polymer structure has been assembled for accelerating the myogenic differentiation of myoblasts for

27

skeletal muscle tissue regeneration (Figure 7).68 Here, the four-armed PLA was first processed to

28

acquire the ductile hyperbranched PLA (HPLA), and then copolymerized with the amino-capped 20

ACS Paragon Plus Environment

Page 20 of 48

Page 21 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

aniline tetramer to generate a range of electroactive biodegradable copolymers HPLAAT (Figure 7A).

2

The amount of aniline tetramer in the HPLAAT copolymers was fixed at 3%, 6%, 9%, and 12% and

3

the resultant copolymers were termed as HPLAAT3, HPLAAT6, HPLAAT9, and HPLAAT12,

4

respectively. The thermal stability of the different HPLAAT copolymers was then examined (Figure

5

7B). While the four-armed PLA degraded thermally at a temperature range between 210 and 290 oC,

6

the thermal degradation of HPLA occurred between 200 and 280 oC. However, the inclusion of

7

aniline tetramer into HPLA altered the thermal degradation profiles of the resultant HPLAAT

8

copolymers. In fact, all HPLAAT copolymers displayed an improved thermal stability, in which their

9

thermal degradation occurred in two phases, i.e., from 250 to 320 oC and then from 320 to 330 oC.

10

Subsequent to their thermal degradation profiles, the enzymatic degradation behaviours of all

11

polymeric structures in proteinase K solution at 37 oC were evaluated (Figure 7C). Interestingly, the

12

HPLAAT copolymers displayed a slower degradation rate than HPLA, suggesting that the inclusion

13

of aniline tetramer reduced the enzymatic degradation rate of the copolymers. More clearly, while

14

HPLA had weights of about 52 and 35% at 24 and 72 h, respectively, higher weights of 78 and 55%

15

were still retained by HPLAAT3 at the same time points. Further addition of aniline tetramer,

16

nevertheless, only led to slight decrease in the degradation rate, with similar degradation profiles

17

showed by HPLAAT6, HPLAAT9, and HPLAAT12. Eventually, the influence of the biodegradable

18

electroactive HPLAAT on the cellular behaviours of C2C12 myoblasts was assessed (Figure 7D).

19

The myoblasts were cultured on the HPLA and HPLAAT substrates for 7 days in the presence of

20

differentiation medium. It was observed that HPLAAT improved the proliferation and myogenic

21

differentiation of the myoblasts considerably as compared to HPLA. This was evident from the higher

22

amount of myotubes (in green) formed on HPLAAT than on HPLA. Quantitative evaluation of the

23

myotube maturation index, i.e., ratio of the amount of myotubes with nuclei greater than five to the

24

total amount of myotubes, further confirmed the enhanced myogenic differentiation on HPLAAT.

21

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2

Figure 7. Biodegradable CP for enhanced skeletal muscle regeneration. (A) Synthetic route to biodegradable CP,

3

i.e., hyperbranched polylactide copolymerized with aniline tetramer (HPLAAT). (B) Thermogravimetric

4

analysis (TGA) curves of different polymers, i.e., biodegradable PLA and HPLA, and biodegradable

5

electroactive HPLAAT with varying contents of aniline tetramer. (C) Decomposition profiles of HPLA and

6

HPLAAT with varying contents of aniline tetramer over time. (D) C2C12 myoblasts cultured on different

7

HPLA and HPLAAT polymeric substrates: (a) HPLA, (b) HPLAAT3, (c) HPLAAT6, (d) HPLAAT9, and (e)

8

HPLAAT12, in the presence of differentiation medium for 7 days. Tubulin and nuclei of the cells are stained in

9

green and blue, respectively. Scale bars represent 200 µm. Reprinted from ref.68 Copyright 2015, with

10

permission from Elsevier.

11 12

More recently, a study has reported the significant improvement of the myelin gene

13

expression and neurotrophin secretion of Schwann cells, via the use of conducting biodegradable

14

copolymer films, which was then utilized to enhance the peripheral nerve growth and regeneration of

15

neuronal cells (Figure 8).72 Here, the polycondensation of glycerol, sebacic acid, and aniline

16

pentamer was first employed to prepare the prepolymer poly(glycerol sebacate)-co-aniline pentamer

17

(PGSAP) (Figure 8A). The crosslinking of PGSAP with hexamethylene diisocyanate was then used 22

ACS Paragon Plus Environment

Page 22 of 48

Page 23 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

to generate the conducting PGSAP-H polyurethane films, with electrical conductivity ranging from

2

1.4 × 10-6 to 8.5 × 10-5 S/cm. Subsequent to the preparation of PGSAP-H polyurethane, the enzymatic

3

biodegradation profiles of the copolymer films were assessed in PBS in the presence of lipase enzyme

4

at 37 oC. All PGSAP-H polyurethane films displayed lower degradation rates and had lower weight

5

loss as compared to the control PGS-H film. Furthermore, with an increasing aniline pentamer content

6

from 5 to 15%, the average degradation rate of PGSAP-H polyurethane films reduced considerably

7

from 1.39 to 0.06% per hour. While PGS-H film had an average weight loss of 85% over 48 h,

8

PGSAP-H with 15% aniline pentamer still retained about 83% of its original weight after the

9

degradation process for 336 h. This suggests that the degradation rates of the PGSAP-H copolymer

10

films could be tuned by varying their amount of aniline pentamer. After establishing the degradation

11

profiles of the copolymer films, their effect on the neurite growth and elongation of PC12 cells was

12

studied. The RSC96 Schwann cells were first seeded for several days on different substrates, i.e.,

13

tissue culture polystyrene (TCP), PGS-H, and PGSAP-H, and the neurotrophin-filled media were then

14

transferred to replace the original media in which PC12 cells were cultured. The normal medium in

15

the absence of nerve growth factor (NGF) (NM) was used as negative control, whereas the normal

16

medium in the presence of NGF (NM+NGF) as well as the NGF-included medium on TCP

17

(TCP+NGF) served as positive controls. The neuronal cells were cultured for several more days in the

18

neurotrophin-filled media and their neurite outgrowth and elongation profiles were subsequently

19

analyzed (Figures 8B to 8D). Intriguingly, the neuronal cells cultured on PGSAP-H film exhibited a

20

large number of neurites with an average length of about 50 µm, which was similar to those observed

21

from the NM+NGF and TCP+NGF groups, but much longer than those found on TCP and PGS-H

22

film (Figures 8B and 8C). More clearly, the neurite lengths of the neuronal cells cultured on PGSAP-

23

H film and the positive control groups ranged from 40 to 60 µm or even beyond 60 µm, while those

24

found on TCP and PGS-H film were mostly between 0 and 40 µm (Figure 8D). Together, these

25

results show that the biodegradable conducting PGSAP-H polyurethane films could promote the

26

neurotrophin secretion of Schwann cells, which in turn, could be used to enhance the neurite growth

27

and elongation of neuronal cells.

23

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2

Figure 8. Biodegradable CP for enhanced peripheral nerve regeneration. (A) Synthetic routes to the conducting

3

poly(glycerol sebacate)-co-aniline pentamer (PGSAP) prepolymer and the biodegradable electroactive PGSAP-

4

H polyurethane films. PGSAP prepolymer was first prepared through the polycondensation of aniline pentamer,

5

glycerol, and sebacic acid. The crosslinking of the prepolymer with HDI would generate the PGSAP-H

6

polyurethane film. (B) Optical microscopy images of PC12 cells cultured on different substrates under different

7

culture conditions. The yellow arrows indicate the neurites. Scale bars represent 50 µm. (C) The corresponding

8

neurite length of PC12 cells cultured on different substrates under different culture conditions. (D) Neurite

24

ACS Paragon Plus Environment

Page 24 of 48

Page 25 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

length distribution of PC12 cells in each culture condition. * represents statistically significant difference for P

2

< 0.05. Reprinted from ref.72 Copyright 2016, with permission from Elsevier.

3 4

4.2. Biomedical Imaging

5

In recent years, explorations into the potential biomedical applications of biodegradable CPs have

6

extended beyond the field of tissue engineering and regenerative medicine into biomedical imaging.75,

7

95, 96

As one of the emerging bioapplications of biodegradable CPs, biomaging plays a central role in

8

the development of biology and medicine.97-99 This is because biomedical imaging enables the real-

9

time monitoring and elucidation of various physiological processes and pathological mechanisms.100-

10 11

102

At the same time, more precise and effective disease diagnosis and prognosis are increasingly

made possible because of the development of advanced biological imaging techniques.103, 104

12

Although a plethora of exogenous contrast agents has been developed for biomedical imaging,

13

most of these structures are largely non-biodegradable.105-108 The non-biodegradable characteristic of

14

these contrast agents may pose significant health and safety concerns as they will tend to accumulate

15

in major organs and experience an extended in vivo stay, triggering inflammatory response and other

16

adverse biological effects.109-113 This will considerably limit the in vivo imaging applications of non-

17

biodegradable exogenous contrast agents. As a result, recent efforts have been geared towards

18

developing exogenous imaging probes with high brightness and contrast, excellent biocompatibility,

19

and importantly, controlled biodegradability.

20

With their rigid hydrophobic backbone, flexible side chains, and strong intrinsic fluorescence,

21

CPs have recently been exploited as effective imaging probes capable of providing high signal-to-

22

noise ratio and excellent imaging contrast.40, 114-116 This is because the rigid hydrophobic backbone of

23

CPs can regulate their interactions with target biological entities and facilitate their cellular uptakes.

24

Also, the side chains of CPs can be easily functionalized to enhance their water dispersibility and

25

specific molecular targeting capability. Additionally, the extremely photostable intrinsic fluorescence

26

feature of CPs can be used for the long-term tracking of various cellular and physiological

27

processes.117-119 The development of biodegradable CPs lately has also fueled further the interests in

28

their biomedical imaging applications. In fact, intracellularly degradable CPs with smaller fragments 25

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

have been shown to possess enhanced selective targeting and imaging capabilities.95 Moreover, the

2

degree of biodegradability of CPs can be controlled by incorporating and varying the amount of

3

flexible degradable linkers within CPs. This has been illustrated in a recent work where a series of

4

biodegradable PPEs with controlled backbone flexibility was prepared by varying the quantity of

5

biodegradable disulfide-containing monomeric linkers integrated into the aromatic PPE backbone.120

6

Similarly, based on the disulfide-containing CPs, a recent work has demonstrated the

7

preparation, selective targeting, and enhanced localization of biodegradable CPNs into the

8

mitochondria of HeLa cancer cells (Figure 9).95 Here, biodegradable nanoparticles (i.e., CPN-1) were

9

generated based on a self-assembly process of CPs, whose backbone was modified with flexible

10

disulfide monomeric linkers (i.e., PPE-1) (Figure 9A). This backbone modification was anticipated to

11

change the self-assembly and cellular entry pathway of the CPNs. As control, CPs without degradable

12

linkers (i.e., PPE-2) and the resultant non-degradable CPNs (i.e., CPN-2) were also prepared. Both

13

CPNs were able to be internalized by HeLa cancer cells. However, in contrast to the non-degradable

14

CPN-2, CPN-1 was noted to disassemble and degrade intracellularly into conjugated oligomers with

15

low molecular weight. These fluorescent conjugated oligomers were then effectively used to label

16

mitochondria. In fact, CPN-1 displayed a high specific mitochondrial co-localization based on its high

17

Pearson’s correlation coefficient (PCC) value of 0.89, which is a quantitative metric signifying co-

18

localization. CPN-2, in contrast, displayed a low PCC value of 0.26 and a low mitochondrial co-

19

localization. Both CPNs were subsequently functionalized with hyaluronic acid (HA) to improve their

20

hydrophilicity. Similar to the unfunctionalized nanoparticles, the biodegradable CPN-1/HA and non-

21

biodegradable CPN-2/HA complexes exhibited high and low mitochondrial co-localizations,

22

respectively, based on their PCC values (i.e., 0.78 and 0.37, respectively) (Figure 9B). Fluorescence

23

spectroscopic evaluation of the mitochondria of live HeLa cancer cells was further utilized to confirm

24

the selective mitochondrial co-localization of CPN-1 (Figure 9C).

26

ACS Paragon Plus Environment

Page 26 of 48

Page 27 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2

Figure 9. Biodegradable CP for intracellular targeting and labeling application. (A) Schematic showing the

3

chemical structures of CPs PPE-1 and PPE-2 with and without biodegradable linkers, respectively, and the

4

cellular entry of their respective nanoparticles CPN-1 and CPN-2. (B) Fluorescence microscopy images

5

illustrating HeLa cancer cells incubated with CPN/HA (in green). The mitochondria of HeLa cells were stained

6

in red while their nuclei were stained in blue. Scale bars represent 20 µm. (C) Fluorescence intensity of the

7

mitochondria and cytosol of the CPN-treated HeLa cells. Reproduced from ref.95 with permission of The Royal

8

Society of Chemistry.

9 10

http://dx.doi.org/10.1039/c6cc00810k

11

In another work highlighting the biomedical imaging application of biodegradable CPs,

12

biodegradable and highly fluorescent CPNs were prepared via the integration of degradable imidazole

13

units into the backbone of fully conjugated thiophene (Figure 10).75 Specifically, the uniformly

14

distributed biodegradable CPNs were synthesized using the Sonogashira dispersion polymerization of

15

thiophene with imidazole monomers (Figure 10A). The thiophene monomer unit was complexed with

16

different side groups, either methoxy (i.e., OMe for P1) or oligoethyleneoxy (i.e., OEG for P3) side

17

groups. The nanoparticles were noted to have rough surface and uniform size of about 200 nm. As

18

controls, the thiophene monomer was also co-polymerized with benzene monomer to generate non-

19

biodegradable nanoparticles P2 and P4, with hydrodynamic diameters of 492 nm and 574 nm, 27

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

respectively. Subsequent to the nanoparticle preparation, the biodegradability of these nanoparticles,

2

particularly P1, were examined by exposing them to ROS (i.e., H2O2 in water). In accordance to

3

imidazole oxidation, the nanoparticles were anticipated to decompose after exposure to ROS (Figure

4

10B). It was observed that after exposure to 20 µM H2O2 for 48 h, the turbid nanoparticle solution

5

turned transparent. The dynamic of the biodegradation process of P1 nanoparticles was then

6

monitored using a confocal fluorescence microscopy (Figure 10C). Interestingly, the fluorescent

7

nanoparticles decomposed and disappeared completely after only 12 min. Finally, the biodegradability

8

profile of all prepared nanoparticles were evaluated in the presence of ROS-producing macrophages

9

stimulated by lipopolysaccharides in the cell culture (Figure 10D). Impressively, even at the low ROS

10

concentration produced by the activated macrophages, both P1 and P3 nanoparticles degraded with

11

the complete disappearance of their fluorescence after 11.5 h. However, the OEG-functionalized P3

12

nanoparticles were noted to have a faster degradation rate than the OMe-functionalized P1

13

nanoparticles probably due to the OEG-enhanced solubility of P3 nanoparticle fragments in solutions.

14

The non-degradable P2 and P4 nanoparticles, on the other hand, did not disintegrate over the course

15

of observation. In short, this work has illustrated that fully biodegradable CPNs at biologically

16

relevant ROS concentrations can be achieved through the incorporation of imidazole units and the

17

resultant fluorescent CPNs can be potentially used for highly sensitive biomedical imaging.

28

ACS Paragon Plus Environment

Page 28 of 48

Page 29 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2

Figure 10. Biodegradable CP for biomedical imaging application. (A) Synthetic route to degradable and non-

3

degradable CP nanoparticles (CPNs). Biodegradable CPNs P1 and P3 were obtained through the Sonogashira

4

dispersion polymerization of the monomers of thiophene with imidazole, while polymerization of the monomers

5

of thiophene with benzene resulted in non-degradable CPNs P2 and P4. The thiophene monomer was

6

functionalized with either methoxy (i.e., OMe) or oligoethyleneoxy (i.e., OEG) side groups. (B) Schematic

29

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

illustrating the reactive oxygen species (ROS)-mediated decomposition process of the imidazole-based

2

biodegradable CPNs. (C) Time-dependent decomposition process of the imidazole-based biodegradable CPNs

3

P1 exposed to H2O2 solution, as evidenced through: (a) confocal fluorescence microscopy and (b) brightfield

4

images. Scale bars represent 20 µm. (D) Evaluation of the time-dependent degradation process of the four

5

fluorescent CPNs: (a) OMe-functionalized degradable P1, (b) OMe-functionalized non-degradable P2, (c) OEG-

6

functionalized degradable P3, and (d) OEG-functionalized non-degradable P4 CPNs, in the presence of H2O2-

7

producing macrophages using confocal fluorescence microscopy. Macrophages (in blue) were treated with the

8

degradable and non-degradable OMe- and OEG-functionalized CPNs (indicated by white arrows). Scale bars

9

represent 35 µm. Reprinted from ref.75 under a Creative Commons Attribution 4 International License

10

https://creativecommons.org/licenses/by/4.0/ Copyright 2017 Repenko et al.

11 12

4.3. Biomedical Implants, Bioelectronic Devices, and Consumer Electronics

13

The synergistic combination of outstanding electrical conductivity and tunable biodegradability of

14

biodegradable CPs has also been progressively exploited for their potential applications in biomedical

15

implants, bioelectronics devices, sensors, and consumer electronics.53, 76, 121, 122 With their attractive

16

morphological and biophysicochemical properties, biodegradable CPs are poised to play a crucial role

17

in solving some of major challenges in these fields. One of these challenges revolves around the

18

health and environmental impacts of electronic devices.123, 124 With the escalating concerns on the

19

safety and toxicity of electronic devices towards human health, whether when they are used as

20

biomedical implants or after they are discarded at the end of their lifetimes, there have been growing

21

attentions on the development of transient and temporary devices which will undergo full degradation

22

over a specific period of time.125-127

23

The rise of temporary biomedical implants and their associated components in recent years is

24

a great testament to the major shift in focus in the development of electronic devices.128, 129 In general,

25

implantable biomedical devices and their associated components, such as implantable biosensors,

26

power sources, and resonators, are highly beneficial for health monitoring as well as disease diagnosis

27

and therapy.130-137 Consequently, they have found increasing healthcare and biomedical applications.

28

To realize temporary biomedical implants which will further augment the strengths of the existing

30

ACS Paragon Plus Environment

Page 30 of 48

Page 31 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

permanent implants while at the same time, addressing their long-term safety issues, active efforts

2

have been channeled towards designing a class of biomedical implants which can be degraded

3

gradually and excreted from the human body in a programmed manner at the end of their intended use.

4

This is highly desirable as a complete biodegradability will effectively minimize the need for surgical

5

removal of the implants, reduce the risks of infections, and at the same time, improve the life quality

6

of patients. Therefore, there have been intensive quests into suitable basic building blocks of the

7

various components of biodegradable implants. Interestingly, biodegradable CPs and their associated

8

composites have emerged as promising candidates for constructing biodegradable medical implants

9

and bioelectronic devices.138-140

10

For example, biodegradable CPs have been exploited for the fabrication of an all-polymer and

11

biodegradable electrical RLC resonator circuit (i.e., electrical circuit consists of resistor (R), inductor

12

(L), and capacitor (C)) driven by radio frequency.121 This RLC resonator could be potentially used for

13

constructing biodegradable biomedical implants and bioelectronic devices. Here, two different

14

blended biodegradable CP composites comprising PPy nanoparticles embedded in biodegradable

15

PLLA and PCL polymer matrices, i.e., PLLA-PPy and PCL-PPy composites, were synthesized and

16

recognized as suitable building blocks of all-polymer RLC resonators. The lowest electrical resistivity

17

of 4.3 × 10-1 and 1.6 × 10-1 Ω-cm could be achieved for PLLA-PPy and PCL-PPy, respectively, when

18

both composites were incorporated with 39% PPy. Separately, based on a silk fibroin-polypyrrole

19

(SF-PPy) composite, a recent work has demonstrated the development of a partially biodegradable

20

magnesium-air bioelectric battery.53 Architecturally, this bioelectric battery consists of a bioresorable

21

Mg alloy-based anode and a cathode made of the biodegradable SF-PPy film. It was noted that the

22

biocompatible SF-PPy film incorporated with 3.9% PPy possessed a sheet resistance in the order of 1

23

× 103 Ω/square, an electrical conductivity of about 1.1. S/cm, and a moderate oxygen reduction

24

catalytic activity. Also, after a 15-day incubation in a buffered protease solution, the SF-PPy

25

composite disintegrated with an 82% weight loss. This has further realized the vision of a

26

biodegradable implantable bioelectric battery, which can serve as an external energy source to power

27

the effective operation of implantable biodegradable electronics.

31

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Similarly, using the biocompatible and fully biodegradable silk fibroin as the flexible

2

supporting substrate, a micropatterned silk-CP biosensor has been fabricated via a photolithography

3

process (Figure 11).122 Here, a water-based photoreactive conductive ink was first prepared by

4

blending poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate) (i.e., PEDOT:PSS) with sericin

5

protein photoresist (i.e., SPP) (Figure 11A). The SPP-PEDOT:PSS ink was then coated on a fibroin

6

protein photoresist- (FPP)-coated film to initiate the fabrication process of a flexible and

7

biodegradable biosensor. This conductive ink was subsequently crosslinked to form the desired

8

micropatterns through a photomask-mediated UV light exposure and the un-crosslinked ink was

9

removed in water. In fact, the large-area PEDOT:PSS microstructures with the smallest feature size of

10

about 5 µm could be fabricated on a flexible silk fibroin sheet or glass (Figure 11B). Along with an

11

increasing content of PEDOT:PSS from 11 to 50%, the SPP-PEDOT:PSS ink displayed a reduced

12

average resistivity from 39 to 1 Ω-cm. To evaluate its biodegradability profile, the SPP-PEDOT:PSS

13

on FPP biosensor was incubated in an enzymatically active protease solution at 37 oC for a few weeks.

14

Both the SPP matrix and FPP film fully degraded in the protease solution after 4 weeks. While the

15

biocompatible PEDOT:PSS is not biodegradable, by blending it with SPP, the PEDOT:PSS

16

component of the eventual microstructures experiencing proteolytic degradation could be lost as fine

17

fibrous strands. Subsequent to confirming the biodegradability of the SPP-PEDOT:PSS on FPP film,

18

its performance as a highly selective glucose biosensor was demonstrated (Figure 11C). Glucose

19

oxidase (GOx) enzyme was first functionalized on the surface of the micropatterned silk-CP biosensor

20

to realize the glucose biosensor. The GOx-immobilized biosensor exhibited a linear response against

21

all the tested glucose concentrations as well as an excellent selectivity by detecting only glucose, but

22

not other tested sugars, including fructose, galactose, and sucrose. The sensor also had a high

23

structural stability, conformability, and could be potentially used as a wearable biosensor.

32

ACS Paragon Plus Environment

Page 32 of 48

Page 33 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2

Figure 11. Biodegradable CP for biosensing application. (A) Schematic illustrating the fabrication process of a

3

large-area conducting PEDOT:PSS microstructure on a flexible substrate. (B) Large-area PEDOT:PSS

4

microstructures fabricated on different substrates: (a) flexible silk fibroin sheets, as evidenced through optical

5

photographs, and (b-c) glass, as evidenced through: (b) optical micrograph and (c) SEM image. Scale bar

6

represents 100 µm. (C) Current variation of the microfabricated SPP-PEDOT:PSS glucose biosensor as a

7

function of glucose concentration. Inset demonstrates the high selectivity of the biosensor towards glucose, but

8

not other forms of sugars, such as fructose, galactose, and sucrose. Reprinted from ref.122 Copyright 2016, with

9

permission from Elsevier.

10 11

Beyond biomedical implants and bioelectronics device, the emerging concept of transient

12

electronics has greatly influenced consumer electronics. In fact, the development of transient

13

consumer electronics with controlled degradability has been actively emphasized in recent years due

14

to the sharp escalation in the already colossal demands in consumer electronics in the last decade.126

15

These growing demands have been partly fueled by an evolving trend in the utilization of consumer

16

electronics, particularly smartphones, tablets, and smart watches, as portable and wearable devices for

17

real-time health monitoring and other daily activities.141-143 Unfortunately, all these factors have

18

inevitably contributed to the shorter consumer electronic use lifetimes as well as the exponential

19

growth of electronic waste. As conventional consumer electronics are largely not biocompatible and 33

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2 3

biodegradable, the resultant electronic waste will certainly pose severe ecological and health issues.123, 124

To mitigate these ecological challenges, green electronics with zero footprint have been widely

promoted and explored in the last few years.125-127

4

One of the key directions in the quest to realize green electronics is to identify the most

5

suitable fundamental building blocks of these electronics. This has greatly motivated the design and

6

development of novel electroactive, biocompatible, and environmentally benign biodegradable CPs,

7

which can be prepared from natural resources and decomposed back to the environment. In one of the

8

most recent examples demonstrating this effort, biocompatible and fully disintegrable CPs (i.e.,

9

PDPP-PD) were fabricated using imine chemistry and used as a component to develop totally

10

decomposable transient thin-film transistors and organic electronics (Figure 12).76 Here, imine bond

11

was employed as a reversible conjugated linker, which is generally stable under conditions with

12

neutral pH, but can be hydrolyzed under mild acidic conditions(Figure 12A).76, 78 The biodegradable

13

conducting PDPP-PD polymer possessed an average hole mobility of about 4.2 × 10-2 – 3.4 × 10-1

14

cm2/V.s. The biodegradability profile of the imine-based PDPP-PD in the presence of acetic acid was

15

examined through changes in its absorption spectrum and solution color (Figure 12B). It was noted

16

that the peak absorbance at 680 nm reduced considerably after 3 h and disappeared after 10 days.

17

Furthermore, during this period, the originally blue PDPP-PD solution turned purple. In fact, after a

18

10-day decomposition, both PDPP-PD and its monomer DPP-CHO had similar absorption spectrum

19

and solution color. The purple PDPP-PD solution eventually turned completely transparent after 40

20

days, suggesting the full disintegration of PDPP-PD in acidic condition. In addition to the solution

21

form, the CPs were also biodegradable in a solid-state form. While a large number of the currently

22

demonstrated disintegrable organic electronics have made use of gold as their electrode material, gold

23

is generally not decomposable. In this work, instead of gold, iron was utilized as both the source-drain

24

and gate electrode material to fabricate an ultralight, fully disintegrable, and transient electronic

25

circuit (Figure 12C). Impressively, upon exposure to a mildly acidic environment, the iron electrodes

26

degraded fast within an hour (Figure 12D). Beyond 30 days, other components of the electronic

27

circuit, particularly CPs, alumina, and cellulose substrate, were noted to be fully degraded, illustrating

28

the further realization of totally biodegradable and transient electronics. 34

ACS Paragon Plus Environment

Page 34 of 48

Page 35 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2

Figure 12. Biodegradable CP for bioelectronics application. (A) Schematic of a flexible device where

3

degradable polymer PDPP-PD serves as the active component of the device. (B) Absorbance of the polymer

4

PDPP-PD undergoing degradation over time. Inset shows the optical photographs of the polymer solution before

5

and after degradation for 10 and 40 days. (C) Schematic of the structure of a totally disintegrable electronic

6

device with its individual components. (D) Optical photographs showing the degradation process of the

7

electronic device over time. Scale bars represent 5 mm. Reprinted with permission from ref.76 Copyright 2017

8

National Academy of Sciences of the United States of America.

9

35

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47

1

Page 36 of 48

Table 1. Electrical properties, biodegradability, and potential biomedical applications of some of the biodegradable CP-based structures highlighted in this article. Biodegradable CP-based Structures PPy-PLGA nanofibers PPy-PLA nanofibers PEDOT-PLGA microfibers GP hydrogels

Distinct Features of the Synthesis of Copolymers Polymer blending/coating

Electrical conductivity (S/cm) N.A.

Electrical sheet resistance (Ω/square)

Degradability Test Duration *

Potential Biomedical Applications

References

2 weeks

Weight Loss Over Test Duration * N.A.

7.4 × 103 – 9.0 × 104

Neural tissue engineering

30

Polymer blending/coating

1 × 10-6 –

N.A.

12 weeks

14 – 24%

Tissue engineering

51

N.A.

N.A.

N.A.

Neural tissue engineering

54

N.A.

21 days

50 – 60%

Tissue engineering

55

12 – 14% (hydrolytic degradation); 25% (enzymatic degradation) 50%

Tissue engineering and soft/stretchable/wearable electronics

59

Nerve tissue engineering

62 70

-4

Polymer blending/coating Polymer grafting

1 × 10 7.0 × 10-2 – 2.8 × 10-1 4.54 × 10-4 – 2.41 × 10-4

DCPU films

Aniline trimer incorporation

5.5 × 10-8 – 1.2 × 10-5 (dry state); 4.4 × 10-7 – 4.7 × 10-3 (wet state)

N.A.

PGAP films

Aniline pentamer incorporation Aniline tetramer incorporation

2 × 10-5

N.A.

8 weeks (hydrolytic degradation); 14 days (enzymatic degradation) 70 days

3.13 × 10-8 – 2.94 × 10-4

N.A.

48 h

13 – 14%

4.69 × 10-7 – 1.05 × 10-4 N.A.

N.A.

N.A.

N.A.

N.A.

24 h

~ 100%

Cardiovascular tissue engineering and controlled drug delivery Tissue engineering and drug delivery Tissue engineering

N.A.

N.A.

80 days

6 – 27%

Tissue engineering

73

7.82 × 10-3 – 2.76 × 10-2

N.A.

83 – 130 days

~ 100%

Tissue engineering

74

N.A.

N.A.

11.5 h

~ 100%

Biomedical imaging

75

N.A.

N.A.

40 days (in solution form)

~ 100% (in solution form)

Green electronic devices

76

N.A.

N.A.

120 h

50%

Bone tissue engineering

67

DECPH films

DEC hydrogels Modified PPy thin films + Modified PPy pellets SPT-PEI films

Thiophene-based CP nanoparticles PDPP-PD films #

PHAT hydrogels

Aniline tetramer incorporation β-substituted pyrrole monomer incorporation β-substituted pyrrole monomer incorporation Modified thiophene monomer incorporation Degradable imidazole unit incorporation Incorporation of imine bond as degradable conjugated linker Aniline trimer incorporation

36

ACS Paragon Plus Environment

71

73

Page 37 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47

Biomacromolecules

AT-PCL fibers HPLAAT films PGSAP-H polyurethane films SF-PPy films

1 2 3 4 5 6 7

Aniline tetramer incorporation Aniline tetramer incorporation Aniline pentamer incorporation Polymer blending/coating

3.0 × 106 – 2.47 × 107 N.A.

N.A.

N.A.

Bone tissue engineering

94

72 h

40 – 45%

Muscle tissue engineering

68

1.4 × 10-6 – 8.5 × 10-5

N.A.

96 – 336 h

17 – 80%

Peripheral nerve tissue engineering

72

1.1

1 × 103

15 days

82%

Biodegradable bioelectric battery Biosensing

53

N.A. N.A.

SPPPolymer blending/coating N.A. N.A. 4 weeks N.A. PEDOT:PSS on FPP films ^ Notes: N.A. indicates data not available. * Degradability tests here evaluated the in vitro hydrolytic and/or enzymatic degradation of biodegradable CPs at 37 oC. + Modified PPy thin films had an average resistance of about 300 Ω. # PDPP-PD films had a hole mobility of 4.2 × 10-2 – 3.4 × 10-1 cm2/V.s. ^ SPP-PEDOT:PSS films had average resistivity of about 1 – 39 Ω-cm.

37

ACS Paragon Plus Environment

122

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

5. CONCLUSIONS AND FUTURE PERSPECTIVES

2

With their highly π-conjugated molecular backbone and versatile side chains, CPs exhibit numerous

3

outstanding physicochemical properties, primarily excellent electrical conductivity, water

4

dispersibility, and biocompatibility. As emphasized in this article, while these unique organic

5

materials are increasingly sought after and have tremendous game-changing potential to augment

6

numerous applications, their translation into practical biomedical and clinical applications is still

7

restricted by many factors, with biodegradability being one of the main Achilles’ heel.

8

Biodegradability, in fact, plays a crucial role in enabling the effective in vivo biomedical applications

9

of CPs. This is because after being introduced into a physiological environment and accomplishing

10

their intended objectives, such as to serve as temporary tissue scaffolds or transient biomedical

11

implants, CPs need to be gradually degraded. Unfortunately, failure to undergo degradation will

12

undeniably lead to the accumulation and prolonged in vivo stay of CPs, potentially prompting

13

undesirable inflammatory response and consequent adverse effects. To overcome this major drawback,

14

ongoing efforts have been focused on the development of biocompatible CPs with inherent

15

biodegradable feature. While a plethora of CPs with varying degree of biodegradability has been

16

demonstrated in the last decade, there still exist major challenges, in terms of synthesis and

17

applications, which prevent these biodegradable CPs from reaching their fullest potential.

18

The first major challenge involves the synthesis of biodegradable CPs, specifically in the

19

optimization of their electrical conductivity and biodegradability. To date, it is still challenging to

20

retain the conductivity of biodegradable CPs and at the same time, ensure their biodegradability for

21

practical applications. One of the main reasons behind this obstacle is that, in contrast to those of non-

22

conjugated degradable polymers, the molecular building blocks of biodegradable fully conjugated

23

CPs are highly limited. To overcome this, one could possibly look more into diversifying the

24

macromolecular architectures and biodegradable linkers used to assemble decomposable CPs in order

25

to optimize their conductivity and biodegradability. Alternatively, one might possibly take a leaf from

26

nature in rationally identifying other more potent fundamental building blocks or biodegradable

27

linkers, similar to those previously illustrated work in identifying and employing the biodegradable

38

ACS Paragon Plus Environment

Page 38 of 48

Page 39 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1

imidazole unit75 or imine bond,76 in developing the next-generation biodegradable CPs. It is therefore

2

clear that the current library of the biodegradable CPs still needs a significant expansion in order to

3

cater to the demands of specific biomedical applications.

4

Another major challenge is associated with the biomedical applications of biodegradable CPs,

5

particularly for tissue engineering applications. Although literature has been filled with reports on the

6

applications of biodegradable CPs for enhancing the adhesion, proliferation, and differentiation of

7

electroresponsive cells and tissues, both the in vitro and in vivo biodegradation profiles of these

8

polymeric structures, are still pretty much unknown. In fact, how well the temporary CP-based

9

scaffolds degrade, either when the cells or tissues are still being supported or when they have repaired

10

themselves and regenerated, as well as how well the cells and tissues integrate with their surrounding

11

microenvironment before and after the decomposition of the temporary scaffolds, still largely remain

12

a mystery. Intriguingly, all these aspects have not been really elucidated and understood and they are

13

definitely worth the explorations.

14

Separately, an exciting emerging area of applications of biodegradable organic CPs is

15

bioelectronics and consumer electronics. The escalating demands for electronic devices with

16

enhanced performance, coupled with the shorter lifetime of electronic devices and the exponential

17

growths of non-biodegradable solid electronic waste, bring with them many ecological and

18

environmental problems. Biodegradable CPs are in a unique position and well-suited to disrupt the

19

current trend. Encouragingly, they possess tremendous potential and an enviable role to realize

20

sustainable and green electronics in order to address the emerging ecological challenges. As such, the

21

exciting opportunity available to biodegradable CPs for advancing low-cost transient electronics has

22

never been greater.

23

Overall, we foresee a bright future for the synthesis, processing, and biomedical applications

24

of biodegradable CPs. Although current challenges in realizing the full potential of biodegradable CPs

25

are aplenty, we believe that these will be overcome swiftly and steadily in the near future along with

26

the progressive advancements in the material design, synthesis, and characterization techniques. The

27

future prospect of biodegradable CPs is definitely exciting. We anticipate that, with further progress

28

in the development of this class of outstanding organic materials, biodegradable CPs are poised to 39

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

emerge as the game-changing biomaterials capable of augmenting and revolutionizing many practical

2

applications and ultimately, making a positive impact in the future.

3 4

AUTHOR INFORMATION

5

Corresponding Author

6

*Email: [email protected]. Fax: +65 6779 1936.

7 8

Author Contributions

9

The manuscript was written through contributions of all authors. All authors have given

10

approval to the final version of the manuscript.

11 12

REFERENCES

13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41

1.

2. 3.

4. 5.

6. 7. 8.

9.

10.

11.

Shirakawa, H.; Louis, E. J.; MacDiarmid, A. G.; Chiang, C. K.; Heeger, A. J., Synthesis of electrically conducting organic polymers: Halogen derivatives of polyacetylene. Journal of the Chemical Society, Chemical Communications 1977, (16), 578-580. Shirakawa, H., Nobel Lecture: The discovery of polyacetylene film: The dawning of an era of conducting polymers. Reviews of Modern Physics 2001, 73, (3), 713-718. Swager, T. M., 50th Anniversary perspective: Conducting/semiconducting conjugated polymers. A personal perspective on the past and the future. Macromolecules 2017, 50, (13), 4867-4886. Stenger-Smith, J. D., Intrinsically electrically conducting polymers. Synthesis, characterization, and their applications. Progress in Polymer Science 1998, 23, (1), 57-79. Long, Y.-Z.; Li, M.-M.; Gu, C.; Wan, M.; Duvail, J.-L.; Liu, Z.; Fan, Z., Recent advances in synthesis, physical properties and applications of conducting polymer nanotubes and nanofibers. Progress in Polymer Science 2011, 36, (10), 1415-1442. Guimard, N. K.; Gomez, N.; Schmidt, C. E., Conducting polymers in biomedical engineering. Progress in Polymer Science 2007, 32, (8), 876-921. Wang, C. H.; Dong, Y. Q.; Sengothi, K.; Tan, K. L.; Kang, E. T., In vivo tissue response to polyaniline. Synthetic Metals 1999, 102, (1), 1313-1314. Wang, X.; Gu, X.; Yuan, C.; Chen, S.; Zhang, P.; Zhang, T.; Yao, J.; Chen, F.; Chen, G., Evaluation of biocompatibility of polypyrrole in vitro and in vivo. Journal of Biomedical Materials Research Part A 2004, 68A, (3), 411-422. Ramanaviciene, A.; Kausaite, A.; Tautkus, S.; Ramanavicius, A., Biocompatibility of polypyrrole particles: an in vivo study in mice. Journal of Pharmacy and Pharmacology 2007, 59, (2), 311-315. Zhao, H.; Zhu, B.; Sekine, J.; Luo, S.-C.; Yu, H.-h., Oligoethylene-glycol-functionalized polyoxythiophenes for cell engineering: Syntheses, characterizations, and cell compatibilities. ACS Applied Materials & Interfaces 2012, 4, (2), 680-686. Ravichandran, R.; Sundarrajan, S.; Venugopal, J. R.; Mukherjee, S.; Ramakrishna, S., Applications of conducting polymers and their issues in biomedical engineering. Journal of The Royal Society Interface 2010, 7, (Suppl 5), S559-S579. 40

ACS Paragon Plus Environment

Page 40 of 48

Page 41 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

12. 13. 14.

15. 16.

17. 18. 19. 20. 21.

22.

23.

24.

25.

26.

27. 28.

29. 30. 31.

32.

Balint, R.; Cassidy, N. J.; Cartmell, S. H., Conductive polymers: Towards a smart biomaterial for tissue engineering. Acta Biomaterialia 2014, 10, (6), 2341-2353. Kaur, G.; Adhikari, R.; Cass, P.; Bown, M.; Gunatillake, P., Electrically conductive polymers and composites for biomedical applications. RSC Advances 2015, 5, (47), 37553-37567. Yang, G.; Lv, F.; Wang, B.; Liu, L.; Yang, Q.; Wang, S., Multifunctional non-viral delivery systems based on conjugated polymers. Macromolecular Bioscience 2012, 12, (12), 16001614. Zhu, C.; Liu, L.; Yang, Q.; Lv, F.; Wang, S., Water-soluble conjugated polymers for imaging, diagnosis, and therapy. Chemical Reviews 2012, 112, (8), 4687-4735. Qian, C.-G.; Zhu, S.; Feng, P.-J.; Chen, Y.-L.; Yu, J.-C.; Tang, X.; Liu, Y.; Shen, Q.-D., Conjugated polymer nanoparticles for fluorescence imaging and sensing of neurotransmitter dopamine in living cells and the brains of zebrafish larvae. ACS Applied Materials & Interfaces 2015, 7, (33), 18581-18589. Li, K.; Liu, B., Polymer-encapsulated organic nanoparticles for fluorescence and photoacoustic imaging. Chemical Society Reviews 2014, 43, (18), 6570-6597. McQuade, D. T.; Pullen, A. E.; Swager, T. M., Conjugated polymer-based chemical sensors. Chemical Reviews 2000, 100, (7), 2537-2574. Thomas, S. W.; Joly, G. D.; Swager, T. M., Chemical sensors based on amplifying fluorescent conjugated polymers. Chemical Reviews 2007, 107, (4), 1339-1386. Wu, W.; Bazan, G. C.; Liu, B., Conjugated-polymer-amplified sensing, imaging, and therapy. Chem 2017, 2, (6), 760-790. Kotwal, A.; Schmidt, C. E., Electrical stimulation alters protein adsorption and nerve cell interactions with electrically conducting biomaterials. Biomaterials 2001, 22, (10), 10551064. Sensharma, P.; Madhumathi, G.; Jayant, R. D.; Jaiswal, A. K., Biomaterials and cells for neural tissue engineering: Current choices. Materials Science and Engineering: C 2017, 77, 1302-1315. Mihic, A.; Cui, Z.; Wu, J.; Vlacic, G.; Miyagi, Y.; Li, S.-H.; Lu, S.; Sung, H.-W.; Weisel, R. D.; Li, R.-K., A Conductive polymer hydrogel supports cell electrical signaling and improves cardiac function after implantation into myocardial infarct. Circulation 2015, 132, (8), 772784. Hardy, J. G.; Li, H.; Chow, J. K.; Geissler, S. A.; McElroy, A. B.; Nguy, L.; Hernandez, D. S.; Schmidt, C. E., Conducting polymer-based multilayer films for instructive biomaterial coatings. Future Science OA 2015, 1, (4), FSO79. Mawad, D.; Mansfield, C.; Lauto, A.; Perbellini, F.; Nelson, G. W.; Tonkin, J.; Bello, S. O.; Carrad, D. J.; Micolich, A. P.; Mahat, M. M.; Furman, J.; Payne, D.; Lyon, A. R.; Gooding, J. J.; Harding, S. E.; Terracciano, C. M.; Stevens, M. M., A conducting polymer with enhanced electronic stability applied in cardiac models. Science Advances 2016, 2, (11), e1601007. Guex, A. G.; Puetzer, J. L.; Armgarth, A.; Littmann, E.; Stavrinidou, E.; Giannelis, E. P.; Malliaras, G. G.; Stevens, M. M., Highly porous scaffolds of PEDOT:PSS for bone tissue engineering. Acta Biomaterialia 2017, 62, 91-101. Qazi, T. H.; Rai, R.; Boccaccini, A. R., Tissue engineering of electrically responsive tissues using polyaniline based polymers: A review. Biomaterials 2014, 35, (33), 9068-9086. Jaymand, M.; Hatamzadeh, M.; Omidi, Y., Modification of polythiophene by the incorporation of processable polymeric chains: Recent progress in synthesis and applications. Progress in Polymer Science 2015, 47, 26-69. Guo, B.; Glavas, L.; Albertsson, A.-C., Biodegradable and electrically conducting polymers for biomedical applications. Progress in Polymer Science 2013, 38, (9), 1263-1286. Lee, J. Y.; Bashur, C. A.; Goldstein, A. S.; Schmidt, C. E., Polypyrrole-coated electrospun PLGA nanofibers for neural tissue applications. Biomaterials 2009, 30, (26), 4325-4335. Huang, Z.-M.; Zhang, Y. Z.; Kotaki, M.; Ramakrishna, S., A review on polymer nanofibers by electrospinning and their applications in nanocomposites. Composites Science and Technology 2003, 63, (15), 2223-2253. Xie, J.; MacEwan, M. R.; Schwartz, A. G.; Xia, Y., Electrospun nanofibers for neural tissue engineering. Nanoscale 2010, 2, (1), 35-44. 41

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

33. 34. 35.

36.

37.

38. 39. 40.

41.

42.

43.

44.

45.

46.

47.

48.

49. 50. 51.

52.

53.

Xue, J.; Xie, J.; Liu, W.; Xia, Y., Electrospun nanofibers: New concepts, materials, and applications. Accounts of Chemical Research 2017, 50, (8), 1976-1987. Guo, B.; Ma, P. X., Synthetic biodegradable functional polymers for tissue engineering: A brief review. Science China Chemistry 2014, 57, (4), 490-500. Moon J. H.; Kenry, Conjugated polymers for gene delivery. Conjugated Polymers for Biological and Biomedical Applications, Liu, B., Ed. John Wiley & Sons: 2018; Vol 1, pp 215-241. Kenry; Liu, B., Conductive polymer‐based functional structures for neural therapeutic applications. Conjugated Polymers for Biological and Biomedical Applications, Liu, B., Ed. John Wiley & Sons: 2018; Vol 1, pp 243-267. Gross, M.; Müller, D. C.; Nothofer, H.-G.; Scherf, U.; Neher, D.; Bräuchle, C.; Meerholz, K., Improving the performance of doped π-conjugated polymers for use in organic light-emitting diodes. Nature 2000, 405, 661-665. Tang, S.; Irgum, K.; Edman, L., Chemical stabilization of doping in conjugated polymers. Organic Electronics 2010, 11, (6), 1079-1087. Le, T.-H.; Kim, Y.; Yoon, H., Electrical and electrochemical properties of conducting polymers. Polymers 2017, 9, (4), 150. Feng, L.; Zhu, C.; Yuan, H.; Liu, L.; Lv, F.; Wang, S., Conjugated polymer nanoparticles: Preparation, properties, functionalization and biological applications. Chemical Society Reviews 2013, 42, (16), 6620-6633. Lammers, T.; Kiessling, F.; Hennink, W. E.; Storm, G., Nanotheranostics and image-guided drug delivery: Current concepts and future directions. Molecular Pharmaceutics 2010, 7, (6), 1899-1912. Tian, H.; Tang, Z.; Zhuang, X.; Chen, X.; Jing, X., Biodegradable synthetic polymers: Preparation, functionalization and biomedical application. Progress in Polymer Science 2012, 37, (2), 237-280. Gunatillake, P.; Mayadunne, R.; Adhikari, R., Recent developments in biodegradable synthetic polymers. Biotechnology Annual Review, El-Gewely, M. R., Ed. Elsevier: 2006; Vol. 12, pp 301-347. Kamaly, N.; Yameen, B.; Wu, J.; Farokhzad, O. C., Degradable controlled release polymers and polymeric nanoparticles: Mechanisms of controlling drug release. Chemical Reviews 2016, 116, (4), 2602-2663. Huynh, D. P.; Shim, W. S.; Kim, J. H.; Lee, D. S., pH/temperature sensitive poly(ethylene glycol)-based biodegradable polyester block copolymer hydrogels. Polymer 2006, 47, (23), 7918-7926. Huynh, C. T.; Kang, S. W.; Li, Y.; Kim, B. S.; Lee, D. S., Controlled release of human growth hormone from a biodegradable pH/temperature-sensitive hydrogel system. Soft Matter 2011, 7, (19), 8984-8990. Phan, V. H. G.; Thambi, T.; Duong, H. T. T.; Lee, D. S., Poly(amino carbonate urethane)based biodegradable, temperature and pH-sensitive injectable hydrogels for sustained human growth hormone delivery. Scientific Reports 2016, 6, 29978. Fredenberg, S.; Wahlgren, M.; Reslow, M.; Axelsson, A., The mechanisms of drug release in poly(lactic-co-glycolic acid)-based drug delivery systems—A review. International Journal of Pharmaceutics 2011, 415, (1), 34-52. Kenry; Lim, C. T., Nanofiber technology: Current status and emerging developments. Progress in Polymer Science 2017, 70, 1-17. Liu, M.; Xu, N.; Liu, W.; Xie, Z., Polypyrrole coated PLGA core-shell nanoparticles for drug delivery and photothermal therapy. RSC Advances 2016, 6, (87), 84269-84275. Zhou, J.-f.; Wang, Y.-g.; Cheng, L.; Wu, Z.; Sun, X.-d.; Peng, J., Preparation of polypyrroleembedded electrospun poly(lactic acid) nanofibrous scaffolds for nerve tissue engineering. Neural Regeneration Research 2016, 11, (10), 1644-1652. Romero, I. S.; Schurr, M. L.; Lally, J. V.; Kotlik, M. Z.; Murphy, A. R., Enhancing the interface in silk–polypyrrole composites through chemical modification of silk fibroin. ACS Applied Materials & Interfaces 2013, 5, (3), 553-564. Jia, X.; Wang, C.; Zhao, C.; Ge, Y.; Wallace, G. G., Toward biodegradable Mg–air 42

ACS Paragon Plus Environment

Page 42 of 48

Page 43 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

54.

55. 56. 57. 58. 59. 60. 61.

62.

63.

64.

65.

66.

67.

68.

69.

70.

71.

72.

bioelectric batteries composed of silk fibroin–polypyrrole film. Advanced Functional Materials 2016, 26, (9), 1454-1462. Feng, Z.-Q.; Wu, J.; Cho, W.; Leach, M. K.; Franz, E. W.; Naim, Y. I.; Gu, Z.-Z.; Corey, J. M.; Martin, D. C., Highly aligned poly(3,4-ethylene dioxythiophene) (PEDOT) nano- and microscale fibers and tubes. Polymer 2013, 54, (2), 702-708. Li, L.; Ge, J.; Guo, B.; Ma, P. X., In situ forming biodegradable electroactive hydrogels. Polymer Chemistry 2014, 5, (8), 2880-2890. Wei, Z.; Faul, C. F. J., Aniline oligomers – architecture, function and new opportunities for nanostructured materials. Macromolecular Rapid Communications 2008, 29, (4), 280-292. Wang, Y.; Tran Henry, D.; Kaner Richard, B., Applications of oligomers for nanostructured conducting polymers. Macromolecular Rapid Communications 2010, 32, (1), 35-49. Stejskal, J.; Trchová, M., Aniline oligomers versus polyaniline. Polymer International 2012, 61, (2), 240-251. Xu, C.; Huang, Y.; Yepez, G.; Wei, Z.; Liu, F.; Bugarin, A.; Tang, L.; Hong, Y., Development of dopant-free conductive bioelastomers. Scientific Reports 2016, 6, 34451. Potin, P.; De Jaeger, R., Polyphosphazenes: Synthesis, structures, properties, applications. European Polymer Journal 1991, 27, (4), 341-348. Qing-Song, Z.; Yu-Hua, Y.; Shi-Pu, L.; Tao, F., Synthesis of a novel biodegradable and electroactive polyphosphazene for biomedical application. Biomedical Materials 2009, 4, (3), 035008. Zhang, Q.; Yan, Y.; Li, S.; Feng, T., The synthesis and characterization of a novel biodegradable and electroactive polyphosphazene for nerve regeneration. Materials Science and Engineering: C 2010, 30, (1), 160-166. Hu, J.; Huang, L.; Zhuang, X.; Zhang, P.; Lang, L.; Chen, X.; Wei, Y.; Jing, X., Electroactive aniline pentamer cross-linking chitosan for stimulation growth of electrically sensitive cells. Biomacromolecules 2008, 9, (10), 2637-2644. Wang, Q.; He, W.; Huang, J.; Liu, S.; Wu, G.; Teng, W.; Wang, Q.; Dong, Y., Synthesis of water soluble, biodegradable, and electroactive polysaccharide crosslinker with aldehyde and carboxylic groups for biomedical applications. Macromolecular Bioscience 2011, 11, (3), 362-372. Guo, B.; Finne-Wistrand, A.; Albertsson, A.-C., Molecular architecture of electroactive and biodegradable copolymers composed of polylactide and carboxyl-capped aniline trimer. Biomacromolecules 2010, 11, (4), 855-863. Guo, B.; Finne-Wistrand, A.; Albertsson, A.-C., Enhanced electrical conductivity by macromolecular architecture: Hyperbranched electroactive and degradable block copolymers based on poly(ε-caprolactone) and aniline pentamer. Macromolecules 2010, 43, (10), 44724480. Xie, M.; Wang, L.; Ge, J.; Guo, B.; Ma, P. X., Strong electroactive biodegradable shape memory polymer networks based on star-shaped polylactide and aniline trimer for bone tissue engineering. ACS Applied Materials & Interfaces 2015, 7, (12), 6772-6781. Xie, M.; Wang, L.; Guo, B.; Wang, Z.; Chen, Y. E.; Ma, P. X., Ductile electroactive biodegradable hyperbranched polylactide copolymers enhancing myoblast differentiation. Biomaterials 2015, 71, 158-167. Chen, J.; Dong, R.; Ge, J.; Guo, B.; Ma, P. X., Biocompatible, biodegradable, and electroactive polyurethane-urea elastomers with tunable hydrophilicity for skeletal muscle tissue engineering. ACS Applied Materials & Interfaces 2015, 7, (51), 28273-28285. Guo, B.; Finne-Wistrand, A.; Albertsson, A.-C., Facile synthesis of degradable and electrically conductive polysaccharide hydrogels. Biomacromolecules 2011, 12, (7), 26012609. Guo, B.; Finne-Wistrand, A.; Albertsson, A.-C., Degradable and electroactive hydrogels with tunable electrical conductivity and swelling behavior. Chemistry of Materials 2011, 23, (5), 1254-1262. Wu, Y.; Wang, L.; Guo, B.; Shao, Y.; Ma, P. X., Electroactive biodegradable polyurethane significantly enhanced Schwann cells myelin gene expression and neurotrophin secretion for peripheral nerve tissue engineering. Biomaterials 2016, 87, 18-31. 43

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

73.

74.

75.

76.

77.

78. 79.

80.

81.

82. 83. 84. 85. 86.

87. 88. 89. 90. 91.

92.

93.

Zelikin, A. N.; Lynn, D. M.; Farhadi, J.; Martin, I.; Shastri, V.; Langer, R., Erodible conducting polymers for potential biomedical applications. Angewandte Chemie International Edition 2002, 41, (1), 141-144. Mawad, D.; Gilmore, K.; Molino, P.; Wagner, K.; Wagner, P.; Officer, D. L.; Wallace, G. G., An erodible polythiophene-based composite for biomedical applications. Journal of Materials Chemistry 2011, 21, (15), 5555-5560. Repenko, T.; Rix, A.; Ludwanowski, S.; Go, D.; Kiessling, F.; Lederle, W.; Kuehne, A. J. C., Bio-degradable highly fluorescent conjugated polymer nanoparticles for bio-medical imaging applications. Nature Communications 2017, 8, (1), 470. Lei, T.; Guan, M.; Liu, J.; Lin, H.-C.; Pfattner, R.; Shaw, L.; McGuire, A. F.; Huang, T.-C.; Shao, L.; Cheng, K.-T.; Tok, J. B. H.; Bao, Z., Biocompatible and totally disintegrable semiconducting polymer for ultrathin and ultralightweight transient electronics. Proceedings of the National Academy of Sciences 2017, 114, (20), 5107-5112. Nielsen, C. B.; Turbiez, M.; McCulloch, I., Recent advances in the development of semiconducting DPP-containing polymers for transistor applications. Advanced Materials 2013, 25, (13), 1859-1880. Belowich, M. E.; Stoddart, J. F., Dynamic imine chemistry. Chemical Society Reviews 2012, 41, (6), 2003-2024. Quigley, A. F.; Razal, J. M.; Thompson, B. C.; Moulton, S. E.; Kita, M.; Kennedy, E. L.; Clark, G. M.; Wallace, G. G.; Kapsa, R. M. I., A conducting-polymer platform with biodegradable fibers for stimulation and guidance of axonal growth. Advanced Materials 2009, 21, (43), 4393-4397. Berthiaume, F.; Maguire, T. J.; Yarmush, M. L., Tissue engineering and regenerative medicine: History, progress, and challenges. Annual Review of Chemical and Biomolecular Engineering 2011, 2, (1), 403-430. Henkel, J.; Woodruff, M. A.; Epari, D. R.; Steck, R.; Glatt, V.; Dickinson, I. C.; Choong, P. F. M.; Schuetz, M. A.; Hutmacher, D. W., Bone regeneration based on tissue engineering conceptions — A 21st century perspective. Bone Research 2013, 1, 216. Khademhosseini, A.; Langer, R., A decade of progress in tissue engineering. Nature Protocols 2016, 11, 1775. O'Brien, F. J., Biomaterials & scaffolds for tissue engineering. Materials Today 2011, 14, (3), 88-95. Yu, X.; Tang, X.; Gohil, S. V.; Laurencin, C. T., Biomaterials for bone regenerative engineering. Advanced Healthcare Materials 2015, 4, (9), 1268-1285. Lee, W. C.; Lim, C. H.; Kenry; Su, C.; Loh, K. P.; Lim, C. T., Cell-assembled graphene biocomposite for enhanced chondrogenic differentiation. Small 2015, 11, (8), 963-969. Liu, Y.; Kenry; Guo, Y.; Sonam, S.; Ki Hong, S.; Nai, M. H.; Tai Nai, C.; Gao, L.; Chen, J.; Jin Cho, B.; Lim, C. T.; Guo, W.; Loh, K. P., Large‐area, periodic, hexagonal wrinkles on nanocrystalline graphitic film. Advanced Functional Materials 2015, 25, (34), 5492-5503. Kenry; Loh, K. P.; Lim, C. T., Molecular interactions of graphene oxide with human blood plasma proteins. Nanoscale 2016, 8, (17), 9425-9441. Kenry; Lee, W. C.; Loh, K. P.; Lim, C. T., When stem cells meet graphene: Opportunities and challenges in regenerative medicine. Biomaterials 2018, 155, 236-250. Liu, X.; Ma, P. X., Polymeric scaffolds for bone tissue engineering. Annals of Biomedical Engineering 2004, 32, (3), 477-486. Kohane, D. S.; Langer, R., Polymeric biomaterials in tissue engineering. Pediatric Research 2008, 63, 487. Asti, A.; Gioglio, L., Natural and synthetic biodegradable polymers: Different scaffolds for cell expansion and tissue formation. The International Journal of Artificial Organs 2016, 37, (3), 187-205. Zhang, Z.; Rouabhia, M.; Wang, Z.; Roberge, C.; Shi, G.; Roche, P.; Li, J.; Dao, L. H., Electrically conductive biodegradable polymer composite for nerve regeneration: Electricitystimulated neurite outgrowth and axon regeneration. Artificial Organs 2007, 31, (1), 13-22. Dong, R.; Zhao, X.; Guo, B.; Ma, P. X., Biocompatible elastic conductive films significantly enhanced myogenic differentiation of myoblast for skeletal muscle regeneration. 44

ACS Paragon Plus Environment

Page 44 of 48

Page 45 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

94.

95. 96.

97. 98. 99. 100. 101.

102.

103. 104. 105. 106. 107. 108. 109.

110.

111.

112. 113. 114. 115.

116.

Biomacromolecules 2017, 18, (9), 2808-2819. Guex, A. G.; Spicer, C. D.; Armgarth, A.; Gelmi, A.; Humphrey, E. J.; Terracciano, C. M.; Harding, S. E.; Stevens, M. M., Electrospun aniline-tetramer-co-polycaprolactone fibers for conductive, biodegradable scaffolds. MRS Communications 2017, 7, (3), 375-382. Twomey, M.; Mendez, E.; Manian, R. K.; Lee, S.; Moon, J. H., Mitochondria-specific conjugated polymer nanoparticles. Chemical Communications 2016, 52, (27), 4910-4913. Liu, J.; Wang, S.; Cai, X.; Zhou, S.; Liu, B., Hydrogen peroxide degradable conjugated polymer nanoparticles for fluorescence and photoacoustic bimodal imaging. Chemical Communications 2018, 54, (20), 2518-2521. Massoud, T. F.; Gambhir, S. S., Molecular imaging in living subjects: Seeing fundamental biological processes in a new light. Genes & Development 2003, 17, (5), 545-580. Cai, W.; Rao, J.; Gambhir, S. S.; Chen, X., How molecular imaging is speeding up antiangiogenic drug development. Molecular Cancer Therapeutics 2006, 5, (11), 2624. Weissleder, R., Molecular imaging in cancer. Science 2006, 312, (5777), 1168-1171. Bading, J. R.; Shields, A. F., Imaging of cell proliferation: Status and prospects. Journal of Nuclear Medicine 2008, 49, (Suppl 2), 64S-80S. Martínez-Corral, I.; Olmeda, D.; Diéguez-Hurtado, R.; Tammela, T.; Alitalo, K.; Ortega, S., In vivo imaging of lymphatic vessels in development, wound healing, inflammation, and tumor metastasis. Proceedings of the National Academy of Sciences 2012, 109, (16), 62236228. Yao, Z.; Carballido-López, R., Fluorescence imaging for bacterial cell biology: From localization to dynamics, from ensembles to single molecules. Annual Review of Microbiology 2014, 68, (1), 459-476. Hussain, T.; Nguyen, Q. T., Molecular imaging for cancer diagnosis and surgery. Advanced Drug Delivery Reviews 2014, 66, 90-100. Chen, I. Y.; Wu, J. C., Cardiovascular molecular imaging: Focus on clinical translation. Circulation 2011, 123, (4), 425-443. Jaiswal, J. K.; Goldman, E. R.; Mattoussi, H.; Simon, S. M., Use of quantum dots for live cell imaging. Nature Methods 2004, 1, 73-78. Walling, M. A.; Novak, J. A.; Shepard, J. R. E., Quantum dots for live cell and in vivo imaging. International Journal of Molecular Sciences 2009, 10, (2), 441-491. Louie, A., Multimodality imaging probes: Design and challenges. Chemical Reviews 2010, 110, (5), 3146-3195. Hong, G.; Diao, S.; Antaris, A. L.; Dai, H., Carbon nanomaterials for biological imaging and nanomedicinal therapy. Chemical Reviews 2015, 115, (19), 10816-10906. Murphy, C. J.; Gole, A. M.; Stone, J. W.; Sisco, P. N.; Alkilany, A. M.; Goldsmith, E. C.; Baxter, S. C., Gold nanoparticles in biology: Beyond toxicity to cellular imaging. Accounts of Chemical Research 2008, 41, (12), 1721-1730. Chapman, S.; Dobrovolskaia, M.; Farahani, K.; Goodwin, A.; Joshi, A.; Lee, H.; Meade, T.; Pomper, M.; Ptak, K.; Rao, J.; Singh, R.; Sridhar, S.; Stern, S.; Wang, A.; Weaver, J. B.; Woloschak, G.; Yang, L., Nanoparticles for cancer imaging: The good, the bad, and the promise. Nano today 2013, 8, (5), 454-460. Tsoi, K. M.; Dai, Q.; Alman, B. A.; Chan, W. C. W., Are quantum dots toxic? Exploring the discrepancy between cell culture and animal studies. Accounts of Chemical Research 2013, 46, (3), 662-671. Kenry; Lim C. T., Biocompatibility and nanotoxicity of layered two‐dimensional nanomaterials. ChemNanoMat 2016, 3, (1), 5-16. Kenry, Understanding the hemotoxicity of graphene nanomaterials through their interactions with blood proteins and cells. Journal of Materials Research 2018, 33, (1), 44-57. Wu, C.; Bull, B.; Szymanski, C.; Christensen, K.; McNeill, J., Multicolor conjugated polymer dots for biological fluorescence imaging. ACS Nano 2008, 2, (11), 2415-2423. Rahim, N. A. A.; McDaniel, W.; Bardon, K.; Srinivasan, S.; Vickerman, V.; So, P. T. C.; Moon, J. H., Conjugated polymer nanoparticles for two-photon imaging of endothelial cells in a tissue model. Advanced Materials 2009, 21, (34), 3492-3496. Wu, C.; Chiu, D. T., Highly fluorescent semiconducting polymer dots for biology and 45

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55

117.

118.

119.

120.

121.

122.

123. 124. 125. 126. 127.

128.

129.

130.

131. 132. 133.

134. 135.

136.

medicine. Angewandte Chemie International Edition 2013, 52, (11), 3086-3109. Kim, B. S.-I.; Jin, Y.-J.; Lee, W.-E.; Byun, D. J.; Yu, R.; Park, S.-J.; Kim, H.; Song, K.-H.; Jang, S.-Y.; Kwak, G., Highly fluorescent, photostable, conjugated polymer dots with amorphous, glassy-state, coarsened structure for bioimaging. Advanced Optical Materials 2015, 3, (1), 78-86. Hong, G.; Zou, Y.; Antaris, A. L.; Diao, S.; Wu, D.; Cheng, K.; Zhang, X.; Chen, C.; Liu, B.; He, Y.; Wu, J. Z.; Yuan, J.; Zhang, B.; Tao, Z.; Fukunaga, C.; Dai, H., Ultrafast fluorescence imaging in vivo with conjugated polymer fluorophores in the second near-infrared window. Nature Communications 2014, 5, 4206. Piwoński, H.; Michinobu, T.; Habuchi, S., Controlling photophysical properties of ultrasmall conjugated polymer nanoparticles through polymer chain packing. Nature Communications 2017, 8, 15256. Vokatá, T.; Twomey, M.; Mendez, E.; Moon, J. H., Synthesis of biodegradable conjugated polymers with controlled backbone flexibility. Journal of Polymer Science Part A: Polymer Chemistry 2015, 53, (11), 1403-1412. Boutry, C. M.; Sun, W.; Strunz, T.; Chandrahalim, H.; Hierold, C., Development and characterization of biodegradable conductive polymers for the next generation of RF bioresonators. IEEE International Frequency Control Symposium, 1-4 June 2010; pp 258-261. Pal, R. K.; Farghaly, A. A.; Wang, C.; Collinson, M. M.; Kundu, S. C.; Yadavalli, V. K., Conducting polymer-silk biocomposites for flexible and biodegradable electrochemical sensors. Biosensors and Bioelectronics 2016, 81, 294-302. Bhutta, M. K. S.; Omar, A.; Yang, X., Electronic waste: A growing concern in today's environment. Economics Research International 2011, 2011, 474230. Perkins, D. N.; Brune Drisse, M.-N.; Nxele, T.; Sly, P. D., E-waste: A global hazard. Annals of Global Health 2014, 80, (4), 286-295. Irimia-Vladu, M.; Głowacki, E. D.; Voss, G.; Bauer, S.; Sariciftci, N. S., Green and biodegradable electronics. Materials Today 2012, 15, (7), 340-346. Irimia-Vladu, M., "Green" electronics: Biodegradable and biocompatible materials and devices for sustainable future. Chemical Society Reviews 2014, 43, (2), 588-610. Tan, M. J.; Owh, C.; Chee, P. L.; Kyaw, A. K. K.; Kai, D.; Loh, X. J., Biodegradable electronics: Cornerstone for sustainable electronics and transient applications. Journal of Materials Chemistry C 2016, 4, (24), 5531-5558. Persaud-Sharma, D.; McGoron, A., Biodegradable magnesium alloys: A review of material development and applications. Journal of Biomimetics, Biomaterials, and Tissue Engineering 2012, 12, 25-39. Kannan, M. B.; Moore, C.; Saptarshi, S.; Somasundaram, S.; Rahuma, M.; Lopata, A. L., Biocompatibility and biodegradation studies of a commercial zinc alloy for temporary miniimplant applications. Scientific Reports 2017, 7, (1), 15605. Ferguson, J. E.; Redish, A. D., Wireless communication with implanted medical devices using the conductive properties of the body. Expert Review of Medical Devices 2011, 8, (4), 427-433. Kenry; Yeo, J. C.; Lim, C. T., Emerging flexible and wearable physical sensing platforms for healthcare and biomedical applications. Microsystems & Nanoengineering 2016, 2, 16043. Yeo, J. C.; Kenry; Lim, C. T., Emergence of microfluidic wearable technologies. Lab on a Chip 2016, 16, (21), 4082-4090. Lee, S. H.; Lee, Y. B.; Kim, B. H.; Lee, C.; Cho, Y. M.; Kim, S.-N.; Park, C. G.; Cho, Y.-C.; Choy, Y. B., Implantable batteryless device for on-demand and pulsatile insulin administration. Nature Communications 2017, 8, 15032. Feiner, R.; Dvir, T., Tissue–electronics interfaces: From implantable devices to engineered tissues. Nature Reviews Materials 2017, 3, 17076. Kutbee, A. T.; Bahabry, R. R.; Alamoudi, K. O.; Ghoneim, M. T.; Cordero, M. D.; Almuslem, A. S.; Gumus, A.; Diallo, E. M.; Nassar, J. M.; Hussain, A. M.; Khashab, N. M.; Hussain, M. M., Flexible and biocompatible high-performance solid-state micro-battery for implantable orthodontic system. npj Flexible Electronics 2017, 1, (1), 7. Kenry; Geldert, A.; Zhang, X.; Zhang, H.; Lim, C. T., Highly sensitive and selective aptamer46

ACS Paragon Plus Environment

Page 46 of 48

Page 47 of 48 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Biomacromolecules

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18

137.

138. 139. 140.

141. 142. 143.

based fluorescence detection of a malarial biomarker using single-layer MoS2 nanosheets. ACS Sensors 2016, 1, (11), 1315-1321. Kenry; Geldert, A.; Lai, Z.; Huang, Y.; Yu, P.; Tan, C.; Liu, Z.; Zhang, H.; Lim Chwee, T., Single‐layer ternary chalcogenide nanosheet as a fluorescence‐based “capture‐release” biomolecular nanosensor. Small 2016, 13, (5), 1601925. Smela, E., Conjugated polymer actuators for biomedical applications. Advanced Materials 2003, 15, (6), 481-494. Rivnay, J.; Owens, R. M.; Malliaras, G. G., The rise of organic bioelectronics. Chemistry of Materials 2014, 26, (1), 679-685. Martin, D. C., Molecular design, synthesis, and characterization of conjugated polymers for interfacing electronic biomedical devices with living tissue. MRS Communications 2015, 5, (2), 131-153. Ventola, C. L., Mobile devices and apps for health care professionals: Uses and benefits. Pharmacy and Therapeutics 2014, 39, (5), 356-364. Lee, J.-H., Future of the smartphone for patients and healthcare providers. Healthcare Informatics Research 2016, 22, (1), 1-2. Garge, G. K.; Balakrishna, C.; Datta, S. K., Consumer health care: Current trends in consumer health monitoring. IEEE Consumer Electronics Magazine 2018, 7, (1), 38-46.

47

ACS Paragon Plus Environment

Biomacromolecules 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

170x167mm (96 x 96 DPI)