Red Phosphorus-Embedded Cross-Link-Structural Carbon Films as

Sep 29, 2017 - *E-mail: [email protected] (C.Z.), *E-mail: ... Red phosphorus (P) is considered to be one of the most attractive anodic materials...
0 downloads 0 Views 6MB Size
Subscriber access provided by La Trobe University Library

Article

Red Phosphorus Embedded Cross Link Structural Carbon Films as Flexible Anodes for Highly Reversible Li-Ion Storage Jiafeng Ruan, Tao Yuan, Yuepeng Pang, Xinbo Xu, Junhe Yang, Wenbin Hu, Cheng Zhong, Zi-Feng Ma, Xuanxuan Bi, and Shiyou Zheng ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.7b12556 • Publication Date (Web): 29 Sep 2017 Downloaded from http://pubs.acs.org on September 30, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

Red Phosphorus Embedded Cross Link Structural Carbon Films as Flexible Anodes for Highly Reversible Li-Ion Storage Jiafeng Ruan,a,‡ Tao Yuan,a,‡ Yuepeng Pang,a Xinbo Xu,a Junhe Yang,a Wenbin Hu,b,c Cheng Zhong,b,c* Zi-Feng Ma,d Xuanxuan Bi,e and Shiyou Zhenga* a

School of Materials Science and Engineering, University of Shanghai for Science

and Technology, Shanghai 200093, China

b

Tianjin Key Laboratory of Composite and Functional Materials, School of Material

Science and Engineering, Tianjin University, Tianjin 300072, China

c

Key Laboratory of Advanced Ceramics and Machining Technology (Ministry of

Education), Tianjin University, Tianjin 300072, China

d

Shanghai Electrochemical Energy Devices Research Center, Department of

Chemical Engineering, Shanghai Jiao Tong University, Shanghai 200240, China

e

Chemical Sciences and Engineering Division, Argonne National Laboratory, Lemont,

IL, USA

‡ Mr. Jiafeng Ruan and Dr. Tao Yuan contributed equally to this work.

KEYWORDS: Red phosphorus, Binder-free, Flexible, Anode, Li-ion battery

ACS Paragon Plus Environment

ACS Applied Materials & Interfaces

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ABSTRACT: Red phosphorus (P) is considered to be one of the most attractive anodic materials for lithium ion batteries (LIBs) due to its high theoretical capacity of 2596 mAh g-1. However, intrinsic characters such as the poor electronic conductivity and large volume expansion at lithiation impede the development of red P. Here, we design a new strategy to embed red P particles into a cross-link-structural carbon film (P-C film), in order to improve the electronic conductivity and accommodate the volume expansion. The red P/carbon film is synthesized via vapor phase polymerization (VPP) following with pyrolysis process, working as flexible binder-free anode for LIBs. High cycle stability and good rate capability are achieved by the P-C film anode. With 21 % P content in the film, it displays a capacity of 903 mAh g-1 after 640 cycles at a current density of 100 mA g-1, and 460 mAh g-1 after 1000 cycles at 2.0 A g-1. Additionally, the Coulombic efficiency reaches almost to 100 % for each cycle. The superior properties of the P-C films together with their facile fabrication make this material attractive for further flexible and high energy density LIBs applications.

ACS Paragon Plus Environment

Page 2 of 36

Page 3 of 36

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

1. INTRODUCTION

Rechargeable LIBs have been widely used as green electrical energy storage due to their relatively higher energy and power densities.1-5 Graphite anode was generally used in commercial LIBs, which suffers from limited theoretical capacity (372 mAh g-1) and restricted rate performance.6-8 Therefore, a great deal of efforts have been devoted to explore and develop alternative high capacity anode materials, such as porous amorphous carboneous materials,9-11 Phosphorus- (P-) based composites,12,13 Silicon- (Si-) based composites,14-15 transition metal oxides and nitrides,16-19 etc. Among these high capacity anode materials, P and its composites show great potential for practical applications due to its abundance, environmentally benign and they possess high theoretical specific capacity of 2596 mAh g-1 based on the reaction: 3Li+ + P + 3e- ↔ Li3P.20-22 Phosphorous has three allotropes, white P, black P, and red P.23 White P is toxic and chemically unstable, which is not suitable for the application in LIBs.24 Black P has good thermodynamic stability and conductivity, but the complex preparation process limits its large-scale applications.24-26 Among the three allotropes, red P is more chemically stable than white P, environmentally benign, and abundant, which makes it a promising candidate for the next generation high-energy anodic materials. Although red P has been reported previously in the literature as an active anodic material for LIBs,13,21 it is still plagued by low Coulombic efficiency and poor cycle life, especially at high charge/discharge rates. These obstacles arise mainly from its poor electronic conductivity (