Self-Assembled Nano-FeO(OH)/Reduced Graphene Oxide Aerogel as a Reusable Catalyst for Photo-Fenton Degradation of Phenolic Organics Renlan Liu, Yiming Xu, and Baoliang Chen Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.8b01043 • Publication Date (Web): 25 May 2018 Downloaded from http://pubs.acs.org on May 25, 2018
Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.
is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.
Page 1 of 32
Environmental Science & Technology
1
Self-Assembled Nano-FeO(OH)/Reduced Graphene Oxide Aerogel as a
2
Reusable Catalyst for Photo-Fenton Degradation of Phenolic Organics
3
Renlan Liu1,2, Yiming Xu3,4, and Baoliang Chen1,2,*
4 5
(1.Department of Environmental Science, Zhejiang University, Hangzhou, Zhejiang 310058, China; 2.
6
Zhejiang Provincial Key Laboratory of Organic Pollutant Process and Control, Zhejiang University,
7
Hangzhou Zhejiang 310058, China. 3. Department of Chemistry, Zhejiang University, Hangzhou,
8
Zhejiang 310027, China. 4. State Key Laboratory of Silica Materials, Zhejiang University, Hangzhou
9
310027, China.)
10 11 12
* Corresponding author: phone & Fax: 0086-571-88982587
13
Email:
[email protected] 14 15 16 17 18 19 20 21 22 23 1
ACS Paragon Plus Environment
Environmental Science & Technology
24
Abstract
25
Fabrication of visible-light-responsive, macroscopic photo-Fenton catalysts is crucial for
26
wastewater treatment. Here, we report a facile fabrication method for nano-FeO(OH)/reduced
27
graphene oxide aerogels (FeO(OH)-rGA) equipped with a stable macrostructure and a high
28
efficiency for catalytic degradation of phenolic organics. The structure of FeO(OH)/rGA was
29
characterized by SEM, TEM, XPS, Raman analysis. The FeO(OH) is the main constituent of
30
ferrihydrite, which dispersed in the graphene aerogel with a particle size of ~3 nm can
31
efficiently activate H2O2 to generate abundant •OH. The excellent performance of the
32
FeO(OH)/rGO aerogel was specifically exhibited by the outstanding catalyst activity,
33
sustained mineralization and eminent reaction rate for phenolic organics. A synergy effect
34
between FeO(OH) and graphene aerogel was observed, which came from the extensive
35
electron transfer channels and active sites of the 3D graphene aerogel and the
36
visible-light-activated FeO(OH) and H2O2 consistently producing •OH. The FeO(OH)/rGA
37
could be reused for 10 cycles without a reduction in the catalytic activity and had less iron
38
leaching, which guarantees that the active ingredient remains in the gel. Moreover, the
39
FeO(OH)/rGA induced photo-Fenton degradation of 4-chlorophenol under near neutral pH
40
conditions because the tight connection of FeO(OH) with the rGO aerogel results in less iron
41
leaching and prevents the generation of Fe(OH)3. The 4-chlorophenol was completely
42
removed in 80 min with a 0.074 min-1 rate constant in the FeO(OH)-rGA/H2O2 photo-Fenton
43
system under visible-light irradiation, and mineralization rate was up to 80% after six hours.
44
Oxidative •OH can continuously attack 4-chlorophenol, 2,4,6-trichlorophenol and bisphenol A
45
without selectivity. These results lay a foundation for highly effective and durable
46
photo-Fenton degradation of phenolic organics at near neutral pH and sufficient activation of
47
H2O2 for future applications.
48 2
ACS Paragon Plus Environment
Page 2 of 32
Page 3 of 32
Environmental Science & Technology
49 50
TABLE OF CONTENTS
51 52
Fe-rGA 53 54 55 56 57 58 59 60 61 62 63 64 65 66 67 68 69 70 71 72 73 3
ACS Paragon Plus Environment
Environmental Science & Technology
74
1. Introduction
75
The traditional Fenton reaction is an advanced oxidation technology used for wastewater
76
treatment, and the reaction involves a mixture of hydrogen peroxide (H2O2) and ferrous iron
77
(Fe2+) in an acidic solution to generate hydroxyl radicals (·OH) for a subsequent attack of
78
tartaric acid.1 Despite its use, the homogeneous Fenton reaction has several disadvantages,
79
such as an acidic pH (pH 420 nm) in an XPA-7 type photochemical reactor (Xujiang
180
Electromechanical Plant, Nanjing, China). The temperature was maintained at 30±2ºC by
181
circulating cooling water. For the recycling, the organic compounds were added with H2O2
182
after each cycle.
183
2.5. Analytical Methods
184
The residual concentrations of 4-CP and 2,4,6-TCP were detected by high-performance liquid
185
chromatography (HPLC, Agilent 1200 Series) equipped with an ultraviolet detector with an
186
SB-C18 (4.6×150 mm) column. The optimum mobile phase for 4-CP was a mixture of
187
methanol, water and phosphoric acid (70/20/10 by volume) at a flow rate of 1.0 mL min-1 with
188
an analytical wavelength of 279 nm. For 2,4,6-TCP detection, a mobile phase containing
189
methanol and 0.02 mol/L phosphoric acid (80:20 v/v) was used at a wavelength of 285 nm.
190
BPA was detected by an HPLC equipped with a fluorescence detector with an SB-C18
191
(4.6×150 mm) column. The mobile phase was a mixture of acetonitrile and 0.01 M
192
trifluoroacetic acid (70:30, v/v), and a wavelength of 280 nm was used. The total organic
193
carbon (TOC) was measured using a TOC-V CPH TOC analyzer (SHIMADZU). The total
194
dissolved iron in the reactive solution was detected using atomic absorption spectrometry
195
(AAS, Perkin Elmer AAnalyst 700). For the different H2O2 concentrations, the potassium
196
titanium (IV) oxalate spectrophotometric method was used at a wavelength of 385 nm.33 A
197
pseudo first-order model was applied to describe the kinetics of phenolic organics
198
photo-degration by Fe-rGA.
34,35
The first-order constant k (min-1) was determined according 8
ACS Paragon Plus Environment
Page 8 of 32
Page 9 of 32
Environmental Science & Technology
199
to the following equation: ln(C0/Ct)=kt, where Ct is the concentration of phenolic organics at
200
time t, C0 is the initial concentration of phenolic organics, k is the degradation rate constant,
201
and t is the irradiation time. Hydroxyl radicals (•OH) were measured by adding methanol as
202
scavenger and obtaining electron paramagnetic resonance (EPR) spectra with DMPO forming
203
DMPO-•OH on a Bruker A300 EPR (modulation amplitude 1.00G; microwave power 20 mW;
204
modulation frequency 9.866 GH). The intermediate products were determined by liquid
205
chromatography-mass spectrometry (LC/MS) equipped with a linear ion trap interface with an
206
HPLC and quaternary pump. More details regarding the analytical methods are available in
207
the supporting information (SI).
208 209
3. Results and discussion
210
3.1. Characterization of the FeO(OH)-rGA aerogels and rGA
211
A schematic illustration of the fabrication of FeO(OH)-rGA is presented in Figure S1. Initially,
212
Fe3+ from FeCl3 can react via electrostatic interactions, cation-π interactions or metal
213
coordination with the oxygen-containing functional groups on the GO nanosheets. Second,
214
with the addition of VcNA for the chemical reduction at 95°C, the GO will transform into a
215
reduced graphene oxide hydrogel (rGH), resulting in uniform deposition of the FeO(OH)
216
nanometer structure on rGH layers. Finally, the black FeO(OH)-rGA was obtained after the
217
freeze-drying process. The simple rGA was prepared by the same procedure without the
218
addition of Fe3+. The measured density of FeO(OH)-rGA is 14.5 mg cm-3 and can be seen in
219
Figure S2a. Meanwhile, FeO(OH)-rGA can bear weight 1,800 times more than its own weight
220
without any mechanical deformation, as shown in Figure S2b. The excellent physical and
221
mechanical performances are beneficial for its practical application. Nevertheless, excessive
222
iron loading has an adverse impact on the aerogel structure stability. 25FeO(OH)-rGA
223
presented an incomplete aerogel structure (Figure S2c). 9
ACS Paragon Plus Environment
Environmental Science & Technology
224 225
Figure 1. SEM image (a), TEM image (inset SAED image) (b), HRTEM image (c) and elemental mapping
226
(d) of FeO(OH)-rGA.
227 228
SEM and TEM techniques were used to observe the lamella and pore morphology.
229
Figure 1a displays an abundant internal pore network. FeO(OH)-rGA possesses numerous,
230
more uniform and smaller pore networks than rGA (Figure S3a), which can provide an
231
extensive transportation network for electron transfer and effective reactions with H2O2.
232
Figure 1b shows the abundant tiny particles (~3 nm) on the reduced graphene oxide (rGO)
233
layers in FeO(OH)-rGA compared with that of pure rGA (Figure S3b), and the inset SAED
234
shows the crystal diffraction with a crystal ring of FeO(OH)-rGA, implying that lattice
235
striation of the particles and suggesting the generation of smaller and uniform crystals on the
236
rGO layers. By calculation, the d-spacing values were equal to 0.223 nm and 0.127 nm, which
237
were assigned to the (112) and (220) lattice planes of ferrihydrite (FeO(OH)) (JCPDS No.
238
46-1315). Ferrihydrite can enhance the decomposition of H2O2 and the oxidation of atrazine 10
ACS Paragon Plus Environment
Page 10 of 32
Page 11 of 32
Environmental Science & Technology
239
via the Fenton reaction in solution.36 Simultaneously, the elemental mapping showed C, O,
240
and Fe elements in FeO(OH)-rGA (Figure 1d).
241
To further confirm the oxygen functional groups and iron composition in the
242
FeO(OH)-rGA aerogel, XPS was employed to analyze the FeO(OH)-rGA and rGA aerogels.
243
We analyzed the C 1s spectra of the FeO(OH)-rGA and rGA aerogels and found that the
244
functional groups, such as C-C/C=C (284.3 eV), C-O (285.5 eV), C=O (287.8 eV), and
245
O-C=C (289.7 eV), were not significantly different, as shown in Figure 2a and Figure S3(c,
246
d).37 The Fe 2p XPS spectra are shown in Figure 2b. The peaks at 711.8 eV and 725.6 eV are
247
assigned to Fe(III)2p3/2 and Fe(III)2p1/2, respectively,38 which demonstrated that the iron ions
248
were successfully loaded on the rGO layers and that a possible composition was FeO(OH).
249
These XPS results demonstrated that the addition of iron did not influence the oxygen
250
functional group contents in the rGA aerogel but increased the oxygen percentage via
251
FeO(OH) generation (Figure S3 (e, f)). Meanwhile, the EDX analysis showed that the Fe
252
mass percentage was 1.63%.
253
Raman spectroscopy is an effective tool to observe ordered and disordered defects in
254
graphene. In the Raman spectra (Figure 2c), two prominent peaks were observed at 1346 cm-1
255
(D band) and 1582 cm-1 (G band), which correspond to sp3 carbon vibrational stretching and
256
sp2 carbon vibrational stretching, respectively. The intensity ratios of the D to G bands (ID/IG)
257
for the 15FeO(OH)-rGA and rGA aerogels are 1.09 and 1.24, respectively. The decrease of
258
ID/IG ratio indicates that the FeO(OH) generation can reduce the disorder and defects of
259
graphene during the synthesis process. It is possible that the iron ions easily combine with the
260
–OH and –COOH groups of GO, and thus, small FeO(OH) crystals, which can prevent defect
261
(e.g., holes) generation, form in the presence of VcNa at 95°C and are derived from the direct
262
removal of oxygen functional groups.39 The Raman spectra are consistent with the SEM
263
morphology, which also revealed that the pore network of FeO(OH)-rGA was more uniform,
264
smaller and more plentiful than that of rGA. 11
ACS Paragon Plus Environment
Environmental Science & Technology
265 266
Figure 2. XPS spectra of C 1s (a) and Fe 2p (b) for FeO(OH)-rGA. Raman spectra of FeO(OH)-rGA and
267
rGA (c). The optical contact angle of FeO(OH)-rGA (d).
268 269
The contact angle values of FeO(OH)-rGA (Figure 2d) and rGA (Figure S4) were
270
approximately 45° and 42°, which indicated hydrophilic surfaces. These surfaces are
271
favorable for adsorbing dissolved phenolic compounds. We chose VcNa as the reducing
272
reagent for a moderate reduction process compared to that with other reducing reagents (such
273
as hydrazine hydrate) to retain a portion of the oxygen functional groups in the aerogel, as can
274
be observed in the C 1s spectra of FeO(OH)-rGA and rGA from the XPS analysis. The
275
moderate chemical reduction process of the synthesized aerogel restores the sp2 correlation of
276
the π structure of the rGO layers and forms a loose porous structure, which provides more
277
reactive reaction sites and electron transfer channels for photo-Fenton catalysis. 12
ACS Paragon Plus Environment
Page 12 of 32
Page 13 of 32
Environmental Science & Technology
278
The thermograms (TG) of 15FeO(OH)-rGA and rGA in air are shown in Figure S5. From
279
room temperature to 500ºC, rGA and 15FeO(OH)-rGA exhibit a two-stage decomposition
280
pattern. The first decomposition below 120 ºC corresponds to the loss of adsorbed water. The
281
second decomposition in the range of 120-500ºC originates from the removal of labile
282
oxygen-containing functional groups as CO2, CO, and H2O vapor. 15FeO(OH)-rGA and rGA
283
have different weight losses because crystalline FeO(OH) gradually transforms into highly
284
crystalline Fe2O3, which occupies 4.175%.
285
3.2. Photo-Fenton catalytic activity of FeO(OH)-rGA aerogel
286
Control experiments were conducted to compare the removal efficiency of 4-CP by the
287
15FeO(OH)-rGA/H2O2 system at pH 3.0 with an initial 4-CP concentration of 10 mg/L and 20
288
mM H2O2. As shown in Figure 3, 15FeO(OH)-rGA can dramatically degrade 4-CP within 80
289
min under visible-light irradiation in the 15FeO(OH)-rGA/H2O2/4-CP system, whereas
290
15FeO(OH)-rGA could not remove 4-CP, which demonstrated that 15FeO(OH)-rGA did not
291
have catalytic activity without H2O2. In addition, H2O2 could not reduce 4-CP because the
292
H2O2 direct photolysis rate constant is only 1.4×10-11 M-1 s-1.40 Most importantly, the
293
visible-light adsorption of FeO(OH)-rGO after 2 h of heating presented a dramatic increase
294
(Figure S6). This was mainly due to electron transfer between the iron center and rGO layers,
295
which mobilized the FeO(OH)-producing Fe(II) in rGO. Consequently, 4-CP could not
296
degrade without visible-light irradiation because the reaction rate constant of ferric iron with
297
H2O2 is 2×10-3 M-1 s-1,41 which falls far below that of the ferrous ion reaction with H2O2 (76
298
M-1s-1).42 Consequently, H2O2 and visible light were all essential conditions for 4-CP
299
degradation. Furthermore, the reaction rate in the initial 30 min was comparatively slow
300
because the concentration of the quinone intermediate the organics generated was limited, as
301
shown in the latter HPLC analysis. According to previous reports, the coupling of visible
302
irradiation and hydroquinone resulted in strong and universal driving forces in the Fenton
303
reaction for organic pollutant degradation and mineralization.43 As the reaction proceeded, the 13
ACS Paragon Plus Environment
Environmental Science & Technology
304
4-CP removal remarkably accelerated, and the pseudo-first-order kinetic constant (k) was
305
0.0695 min-1. Compared with other Fenton-like reactions previously reported (listed in Table
306
S1),44-50 15FeO(OH)-rGA has a high degradation activity and efficiently utilizes H2O2 with
307
less iron loading under visible-light irradiation.
308 309
Figure 3. Time evolution of 4-CP removal under different conditions (reaction conditions: C0(4-CP): 10
310
mg/L, C0(H2O2): 20 mM, pH=3, 500 W xenon lamp with a UV cutoff filter (λ > 420 nm)).
311
3.3. Influence of solution conditions on degradation of phenolic organics
312
The presence of iron in aerogels plays a vital role in their reaction activity. The
313
performance of rGA changed significantly for 4-CP in the presence of iron χFeO(OH)-rGA
314
(χ=0, 4, 8, 15) (Figure 4a) (C0(H2O2): 10 mM, pH=3). 15FeO(OH)-rGA completely removed
315
4-CP within 110 min and was more efficient than the other iron-doped rGA aerogels. The
316
removal of 4-CP increased as the iron doping increased because of the importance of iron in
317
most of the catalytic components in the photo-Fenton reaction. Consequently, the addition of
318
iron resulted in the activation of H2O2 to generate •OH radicals. Nevertheless, excessive iron
319
loading will have an adverse impact on the aerogel structure stability. The probable reason is
320
that Fe3+ could generate stable coordination compounds with GO.51 In the synthesis process,
321
the excessive iron ions turn into FeO(OH) among the rGO layers, which can greatly hinder 14
ACS Paragon Plus Environment
Page 14 of 32
Page 15 of 32
Environmental Science & Technology
322
π-π stacking between the rGO layers in the aerogel, resulting in aerogel structural collapse, as
323
shown in Figure S2c. Therefore, we chose 15FeO(OH)-rGA as the optimal aerogel ratio for
324
further study.
325 326
Figure 4. Influence of the initial iron content in FeO(OH)-rGA (a), influence of the initial solution pH (b),
327
influence of the H2O2 concentration(c) on 4-CP degradation. Effectiveness for the degradation of various
328
phenolic organics (d).
329 330
The initial pH affects not only the photocatalytic performance but also the extent of iron
331
leaching and the stability of the catalyst. In consideration of the significant influence of the
332
pH on the photo-Fenton reaction, we studied the effect of the initial pH on the degradation of
333
4-CP, as shown in Figure 4b (Catalyst: 15FeO(OH)-rGA, C0(H2O2): 10 mM). Although the
334
degradation rate of 4-CP slightly declined as the pH increased from 3 to 6, approximately 15
ACS Paragon Plus Environment
Environmental Science & Technology
335
100% of 4-CP was removed within 150 min at pH=3, 4, 5, and 6, and this removal rate is
336
evidently higher than that of other reported heterogeneous Fenton-like catalysts.52 One reason
337
for the good degradation of 4-CP at near neutral pH is that the pH of the solution changed
338
after the reaction because of the generation of low molecular weight organic acids, which
339
were detected in this study, and mineralization to form CO2, which can also transform into
340
carbonic acid, resulting in a decrease in the pH. Another reason is that FeO(OH) is
341
encapsulated by graphene layers via strong π-π interactions, which could restrain ferric iron
342
from leaching and transforming into less active Fe(OH)3. As shown in Figure S7, the color of
343
the Fe3+ solution (16.4 mg/L, pH=3) changed from colorless to yellow after heating for 2 h
344
without sediment formation, but after the 1st photo-Fenton reaction, an obvious red-brown
345
precipitation was generated after 1 h, which directly proved the homogenous Fenton-like
346
reaction is not suitable for practical applications. The special internal network structure of the
347
graphene aerogels alters the state of iron in the catalyst, and the catalyst can exist at near
348
neutral pH values and displays an excellent degradation performance that is completely
349
different from that obtained with a homogeneous Fenton system. In addition, FeO(OH)-rGA
350
has outstanding photo-Fenton performance at near neutral pH, which makes FeO(OH)-rGA a
351
good candidate for the preparation of stable catalysts for industrial wastewater treatment
352
applications without drastically adjusting the pH. Moreover, the macroscopic aerogel is easier
353
to recycle, prevents sediment production, resists corrosion and possesses longer-term
354
prospects.
355
In photo-Fenton catalytic reactions, the oxidant concentration is a crucial factor that can
356
significantly influence organic matter degradation. Figure 4c shows the 4-CP degradation was
357
accelerated as the H2O2 dosage increased from 0 to 20 mM (Catalyst: 15FeO(OH)-rGA,
358
pH=3), and the degradation rate constant (k) increased from 0.040 min under 5mM H2O2, to
359
0.069 min-1 under 10mM H2O2, and to 0.074 min-1 15mM H2O2. This is because H2O2 is the 16
ACS Paragon Plus Environment
Page 16 of 32
Page 17 of 32
Environmental Science & Technology
360
precursor in the reaction to produce •OH. However, with a higher dosage (50 mM), the k
361
value obviously decreased to 0.06 min-1, which was probably caused by the excess H2O2
362
scavenging •OH, which suppressed the 4-CP degradation. Consequently, the dosage of H2O2
363
should exists in an optimum concentration range as much as possible. The demand for H2O2 is
364
always high in the traditional Fenton reaction; hence, the consumption of H2O2 is commonly
365
high in the reaction and a supply of fresh H2O2 is constantly required. As seen in Figure S8,
366
we detected the variation in the H2O2 concentration in the photo-Fenton reaction and found
367
that the concentration of H2O2 slightly decreased as the 4-CP degraded, which was mainly
368
ascribed to the nanometer, well-dispersed FeO(OH) with a small size (~3 nm) in rGA
369
effectively activating H2O2. Comparatively, the mass percentage of transition metal iron in
370
15FeO(OH)-rGA merely was approximately 5%, which was far below that of synthetic iron
371
oxide minerals. This further confirmed that the 3D macroscopic structures can disperse
372
FeO(OH) on the graphene layers to provide sufficient catalytic sites and electron transfer
373
channels for the photo-Fenton reaction.
374
The photo-Fenton catalytic efficiency was different based on the type of organic
375
compound. We selected three phenolic organics, 4-CP, 2,4,6-TCP and BPA. These organics
376
are widely used as fungicides, herbicides, and plastic materials; considered toxic organic
377
pollutants that are harmful to human health and aquatic organisms; and regarded as priority
378
organic pollutants by the US Environmental Protection Agency (USEPA). In this study, when
379
the amount of added catalyst and H2O2 were determined, the content of •OH generated was
380
simultaneously confirmed. Consequently, the difference in the degradation kinetics among
381
4-CP, 2,4,6-TCP and BPA, which is shown in Figure 4d, was ascribed to the different
382
molecular structures. The structural formulas of 4-CP, 2,4,6-TCP and BPA are shown in
383
Figure S9. 2,4,6-TCP has three chlorine substituent connections on one benzene ring, and
384
BPA has two benzene rings connected to each other in contrast with 4-CP. The photo-Fenton 17
ACS Paragon Plus Environment
Environmental Science & Technology
385
degradation kinetics of 4-CP, 2,4,6-TCP and BPA are presented in Figure 4d (Catalyst:
386
15FeO(OH)-rGA, C0(H2O2): 20 mM, pH=3). 4-CP was completely removed within 80 min,
387
and the degradation rate constant was 0.074 min-1, which was higher than that of 2,4,6-TCP
388
and BPA. 2,4,6-TCP and BPA were completely degraded after 150 min, and the degradation
389
rate constants were 0.029 min-1 and 0.031 min-1, respectively. Based on the above results, we
390
concluded that as the number of chlorine substituents on one benzene ring and the number of
391
benzene rings increase the rate of the photo-Fenton reaction decreases. Moreover, the
392
influence of the number of benzene rings was even more significant because the structure of
393
the benzene ring is very stable and not easily oxidized into an open loop. Nonetheless, •OH
394
has a strong oxidant activity (oxidation potential=2.8 V vs NHE) and is capable of oxidizing a
395
wide range of organics in wastewater. In this study, FeO(OH)-rGA, an outstanding
396
photo-Fenton catalyst, could absolutely and rapidly degrade phenolic organics. In Figure 4,
397
degradation rate of phenolic organics at the beginning was slow, which was probably because
398
the FeO(OH)-rGA has limited sorption capacity of phenolic organics. But as the quinone
399
organics produced in the reaction may be excited under visible light, and react with H2O2 to
400
generate •OH as well. This may explain the fast degradation of 4-CP, 2,4,6-TCP and BPA after
401
a short period of irradiation time.
402
3.4. Reusability and stability of the FeO(OH)-rGA aerogel
403
The reusability and stability of photo-Fenton catalysts are crucial for practical
404
applications. FeO(OH)-rGA was stored in a reaction solution for 10 cycles, and 4-CP and
405
H2O2 were added repeatedly after each cycle under visible-light irradiation. The reusability
406
performance of FeO(OH)-rGA is shown in Figure 5a. It can be seen that 4-CP was completely
407
degraded (100%) after each cycle, and the degradation continued until the 10th cycle.
408
Moreover, the morphology and internal network of FeO(OH)-rGA after 10 cycles of
409
regeneration did not show any significant changes, as shown in Figure S10. The reusability of 18
ACS Paragon Plus Environment
Page 18 of 32
Page 19 of 32
Environmental Science & Technology
410
FeO(OH)-rGA ensures its efficient performance and stability for several cycles without losing
411
its catalytic activity; thus, it is a superior candidate for the photo-Fenton process, particularly
412
for the removal of organic contaminants.
413
The stability of the photo-Fenton catalyst was also observed by examining the iron
414
leaching, which directly indicated the stability of the catalytically active component. The total
415
iron leaching after 10 cycles is displayed in Figure 5b. The total iron concentration was 16.4
416
mg/L in FeO(OH)-rGA. The range of the total iron leaching after each cycle was
417
approximately 0.4-0.6 mg/L, which accounted for only ~2.5% of 16.4 mg/L. Moreover, the
418
total iron content in solution after each cycle did not change significantly after the first cycle,
419
as shown in the inset picture (Figure 5b). We did not detect ferrous ions in the reaction
420
solution using the 1,10-phenanthroline method at a wavelength of 510 nm with a Shimadzu
421
UV-2550 spectrophotometer.53 Comparing the EDX results of 15FeO(OH)-rGA after 10
422
cycles (Figure S10d) with that of the initial 15FeO(OH)-rGA (Figure S3f), the 0.1% drop
423
suggests that the iron loss was practically negligible. Therefore, FeO(OH)-rGA is an excellent
424
photo-Fenton catalyst for practical applications in the future.
425 426
Figure 5. The reusability (a) and stability (inset of Fe(T) variation in the first cycle) (b) of the
427
FeO(OH)-rGA aerogel after 10 cycles in the FeO(OH)-rGA/H2O2/4-CP system under visible-light
428
irradiation. (Reaction conditions: C0(4-CP): 10 mg/L, C0(H2O2): 10 mM, pH=3, 500 W xenon lamp with a
429
UV cutoff filter (λ > 420 nm)). 19
ACS Paragon Plus Environment
Environmental Science & Technology
430
3.5. Photocatalytic degradation mechanisms
431
The analysis of free radical quenching is effective for real-time identification of reaction
432
species in photo-Fenton system. Therefore, the reactive species were further distinguished by
433
adding methanol as scavenger for the •OH generated in the reaction solution.54 Methanol has
434
a high reaction rate constant with •OH, up to k=9.6 ×109 M-1 s-1.55 The results achieved after
435
the methanol addition were compared to those obtained without methanol addition and are
436
shown in Figure 6a. The results clearly revealed no degradation of 4-CP after the methanol
437
addition, which suggested that the 4-CP degradation was driven by •OH derived from
438
FeO(OH)-rGA-activated H2O2 under visible-light irradiation. To further identify the radical
439
species in the reaction, EPR with DMPO as a spin-trapping agent was used to detect •OH
440
radicals
441
•OH with an intensity ratio of 1:2:2:1 were obtained in the EPR spectra of
442
FeO(OH)-rGA/H2O2, which clearly indicated •OH was generated in the FeO(OH)-rGA/H2O2
443
system under visible-light irradiation.
48,56
after 5 min of visible-light irradiation. The typical four characteristic peaks of
444 445
Figure 6. Effect of radical scavengers on the degradation of 4-CP (a). EPR spectra of DMPO-•OH adducts
446
that formed over time with visible-light irradiation of a suspension of 15FeO(OH)-rGA/H2O2 (b).
447 448
20
ACS Paragon Plus Environment
Page 20 of 32
Page 21 of 32
Environmental Science & Technology
449
The HPLC analysis is displayed in Figure 7a and shows the visual changes in the 4-CP
450
degradation. It can be concluded that A and D are 4-CP and H2O2, respectively, at t=0, and the
451
degree of 4-CP mineralization is shown in Figure 7b. The TOC removal gradually increased
452
to 80% after 6 h of reaction. The initial TOC removal was slow within 120 min, which was
453
mainly because of the intermediate product generation, i.e., quinone organics (C and D) with
454
a higher toxicity potential.57 The molecular structure of the intermediate products was
455
determined by HPLC-MS (Figure S11). These intermediate products retained the benzene ring
456
structure, which resulted in a solution with a relatively higher TOC at the beginning of the
457
reaction. The TOC removal dramatically accelerated once the reaction continued because the
458
benzene ring of the intermediate products was persistently attacked by •OH and eventually
459
transformed into low molecular weight organic acids with toxicity decreasing, which are more
460
susceptible to oxidative degradation. The possible reaction pathway for 4-CP degradation is
461
presented in Figure S12.
462 463
Figure 7. The intermediate products generation and mineralization of 4-CP. HPLC analysis of 4-CP
464
degradation within 150 min (a). TOC removal of 4-CP within 6 h of reaction (b). (Reaction conditions:
465
C0(4-CP): 10 mg/L, C0(H2O2): 10 mM, pH=3, 500 W xenon lamp with UV cutoff filter (λ > 420 nm)).
466 467 21
ACS Paragon Plus Environment
Environmental Science & Technology
468
Based on the above analysis, a possible mechanism for phenolic organic degradation by
469
FeO(OH)-rGA with H2O2 under visible-light irradiation was proposed (Figure 8). Ferric ions
470
on the GO interface can create catalyst precursors with even and uniform distributions. Once
471
sodium ascorbate was added as a reducing agent, GO gradually transforms into rGO along
472
with recovery of the sp2 regions, which are beneficial for electron transfer between the iron
473
center and H2O2. Moreover, the ferric ions turn into nanometer FeO(OH) that is firmly fixed
474
in rGA via strong π-π interaction between the rGO layers, preventing iron leaching. In
475
addition, the nanoparticles (average size ~ 3 nm) are distributed evenly on the rGO layers,
476
improving the catalytic activity of the FeO(OH)-rGA aerogel compared with that of pure
477
Fe2O3, which has a slow reaction efficiency with H2O2 even under UV-light irradiation.58
478
FeO(OH) has a special optical activity that can easily be activated by visible light and
479
transforms to Fe(II) to activate H2O2 to produce •OH. This process is than pure H2O2 direct
480
photolysis, and an extraordinary catalytic activity is displayed for phenolic organic
481
degradation along with Fe(III)/Fe(II) catalytic cycles. Furthermore, FeO(OH)-rGA can
482
generate •OH with H2O2 under visible-light irradiation due to coupling the visible irradiation
483
and intermediate quinone organics, which have strong and universal driving forces in the
484
Fenton reaction for phenolic organic degradation and mineralization. The special
485
FeO(OH)-rGA structure allows superior degradation of phenolic organics at near neutral pH
486
values and maintains the stability of the catalyst, avoiding a negative influence from catalyst
487
aggregation.
22
ACS Paragon Plus Environment
Page 22 of 32
Page 23 of 32
Environmental Science & Technology
488 489
Figure 8. Schematic illustration of the possible hydroxyl radical generation mechanism and phenolic
490
organic mineralization in the FeO(OH)-rGA/H2O2 system under visible-light irradiation.
491 492
In this study, we employed a facile synthetic method for iron-doped-rGO aerogels as an
493
effective and original photo-Fenton catalyst. The obtained aerogel not only had a stable
494
macrostructure and lighter density but also a prominent catalytic activity for phenolic organic
495
degradation at near neutral pH values with less iron leaching after 10 cycles of consecutive
496
uses. The minimal iron leaching was mainly because the smaller FeO(OH) crystals (average
497
size ~3 nm) were immobilized and dispersed on the rGO layers, and these iron crystals
498
possess a higher catalytic activity than pure iron oxides. The sp2 regions of rGO were
499
recovered by sodium ascorbate reduction to ensure fewer defects after iron doping.
500
Consequently, this FeO(OH)-rGA aerogel is an ideal photo-Fenton catalyst that overcomes the
501
disadvantages of conventional Fenton reactions and can be applied to practical applications
502
for effective removal of organic pollutants.
503 23
ACS Paragon Plus Environment
Environmental Science & Technology
504
ASSOCIATED CONTENT
505
Supporting Information
506
LC-MS analysis and comparison of the catalytic properties of different photo-Fenton catalysts
507
(Table S-1) and Figures S1-S12 are presented. This information is available free of charge via
508
the Internet at http://pubs.acs.org.
509 510
AUTHOR INFORMATION
511
Corresponding Author
512
*Phone: 0086-574-87609508; e-mail:
[email protected] 513
Notes
514
The authors declare no competing financial interest.
515 516
ACKNOWLEDGMENTS
517
This project was supported by the National Natural Science Foundation of China (Grant
518
21425730, 21537005, and 21621005), the National Basic Research Program of China (Grant
519
2014CB441106), and the National Key Technology Support Program of China (No.
520
2015BAC02B01).
521 522
References
523
[1] Fenton, H. J. H. Oxidation of tartaric acid in presence of iron. J. Chem. Soc. Transactions.
524 525 526 527
1894, 65, 899-910. [2] Kremer, M. L. The Fenton reaction. Dependence of the rate on pH. J. Phys. Chem. A. 2003, 107, 1734-1741. [3] Lin, S. H.; Lo, C. C. Fenton process for treatment of desizing wastewater. Wat. Res. 1997, 24
ACS Paragon Plus Environment
Page 24 of 32
Page 25 of 32
528
Environmental Science & Technology
31, 2050-2056.
529
[4] Iurascu, B.; Siminiceanu, I.; Vione, D.; Vicente, M. A.; Gild, A. Phenol degradation in
530
water through a heterogeneous photo-Fenton process catalyzed by Fe-treated laponite. Wat.
531
Res. 2009, 43, 1313-1322.
532 533
[5] Dercova, K.; Branislav, V.; Tandlich, R.; Subova, L. Fenton’s type reaction in chemical pretreatment of PCBs. Chemosphere 1999, 39, 2621-2628.
534
[6] Gao, L. Z.; Zhuang, J.; Nie, J.; Zhang, J. B.; Gu, N.; Wang, T. H.; Feng, J.; Yang, S.L.;
535
Perrett, S.; Yan, X. Y. Intrinsic peroxidase-like activity of ferromagnetic nanoparticles. Nat.
536
Nanotechnol. 2007, 2, 577-583.
537 538
[7] Xu, L. J.; Wang, J. L. Fenton-like degradation of 2,4-dichlorophenol using Fe3O4 magnetic nanometerparticles. Appl. Catal. B: Environ. 2012, 123, 117-126.
539
[8] Guo, L. Q.; Chen, F.; Fan, X. Q.; Cai, W. D.; Zhang, J. L. S-doped α-Fe2O3 as a highly
540
active heterogeneous Fenton-like catalyst towards the degradation of acid orange 7 and
541
phenol. Appl. Catal. B: Environ. 2010, 96,162-168.
542 543
[9] Lin, S. S.; Gurol, M. D. Catalytic decomposition of hydrogen peroxide on iron oxide: kinetics, mechanism, and implications. Environ. Sci. Technol. 1998, 32, 1417- 1423.
544
[10] Chen, H.; Zhang, Z. L.; Yang, Z. L.; Yang, Q.; Li, B.; Bai, Z. Y. Heterogeneous
545
Fenton-like catalytic degradation of 2,4-dichlorophenoxyacetic acid in water with FeS.
546
Chem. Eng. J. 2015, 273, 481-489.
547
[11] Segura, Y.; Martinez, F.; Melero, J. A. Effective pharmaceutical wastewater degradation
548
by Fenton oxidation with zero-valent iron. Appl. Catal. B: Environ. 2013, 136, 64-69.
549
[12] Hu, M. Q.; Xu, Y. M. Visible light induced degradation of chlorophenols in the presence 25
ACS Paragon Plus Environment
Environmental Science & Technology
550
Page 26 of 32
of H2O2 and iron substituted polyoxotungstate. Chem. Eng. J. 2014, 246, 299-305.
551
[13] Ramirez, J. H.; Costa, C. A.; Madeira, L. M.; Mata, G.; Vicente, M. A.; Rojas-Cervantes,
552
M. L.; López-Peinado, A. J.; Martín-Aranda, R. M. Fenton-like oxidation of Orange II
553
solutions using heterogeneous catalysts based on saponite clay. Appl. Catal. B: Environ.
554
2007, 71, 44-56.
555
[14] Zhang, L. L.; Xu, D.; Hu, C.; Shi, Y. L. Framework Cu-doped AlPO4 as an effective
556
Fenton-like catalyst for bisphenol A degradation. Appl. Catal. B: Environ. 2017, 207,
557
9-16.
558
[15] Coelho, J. V.; Guedes, M. S.; Prado, R. G.; Tronto, J.; Ardisson, J. D.;
Pereira, M. C.;
559
Oliveira, L. C. A. Effect of iron precursor on the Fenton-like activity of Fe2O3/
560
mesoporous silica catalysts prepared under mild conditions. Appl. Catal. B: Environ.
561
2014, 144, 792-799.
562
[16] Sun, L. J.; Yao, Y. Y.; Wang, L.; Mao, Y. J.; Huang, Z. F.; Yao, D. C.; Lu, W. Y.; Chen, W.
563
X. Efficient removal of dyes using activated carbon fibers coupled with
564
8-hydroxyquinoline ferric as a reusable Fenton-like catalyst. Chem. Eng. J. 2014, 240,
565
413-419.
566
[17] Liu, Y. Y.; Jin, W.; Zhao, Y. P.; Zhang, G. S.; Zhang, W. Enhanced catalytic degradation
567
of methylene blue by α-Fe2O3/graphene oxide via heterogeneous photo-Fenton reactions.
568
Appl. Catal. B: Environ. 2017, 206, 642-652.
569
[18] Nair, R. R.; Blake, P.; Grigorenko, A. N.; Novoselov, K. S.; Booth, T. J.; Stauber, T.;
570
Peres, N. M. R.; Geim, A. K.
571
graphene. Science 2008, 320, 1308.
Fine structure constant defines visual transparency of
26
ACS Paragon Plus Environment
Page 27 of 32
572 573
Environmental Science & Technology
[19] Moser, J.; Barreiro, A.; Bachtold, A. Current-induced cleaning of graphene. Appl. Phys. Lett. 2007, 91, 163513.
574
[20] Mayorov, A. S.; Gorbachev, R. V.; Morozov, S.V.; Britnell, L.; Jalil, R.; Ponomarenko, L.
575
A.; Blake, P.; Novoselov, K. S.; Watanabe, K.; Taniguchi, T.; Geim, A. K.
576
Micrometer-scale ballistic transport in encapsulated graphene at room temperature. Nano
577
Lett. 2011, 11, 2396-2399.
578
[21] Tang, H.; Zhao, Y.; Yang, X. N.; Liu, D. M.; Shan, S.J.; Cui, F. Y. Understanding the
579
roles of solution chemistries and functionalization on the aggregation of graphene-based
580
nanometer materials using molecular dynamic simulations. J. Phys. Chem. C. 2017, 121,
581
13888-13897.
582
[22] Garacci, M.; Barret, M.; Mouchet, F.; Sarrieu, C.; Lonchambon, P.; Flahaut, E.; Gauthier,
583
L.; Silvestre, J.; Pinelli, E. Few layer graphene sticking by biofilm of freshwater diatom
584
nitzschia palea as a mitigation to its ecotoxicity. Carbon 2017, 113, 139-150.
585
[23] Sanchís, J.; Olmos, M.; Vincent, P.; Farré, M.; Barceló, D. New Insights on the influence
586
of organic co-contaminants on the aquatic toxicology of carbon nanometermaterials.
587
Environ. Sci. Technol. 2016, 50, 961-969.
588
[24] Shen, Y.; Zhu, X.; Chen, B. Size effects of graphene oxide nanosheets on the construction
589
of three-dimensional graphene-based macrostructures as adsorbents. J. Mater. Chem. A.
590
2016, 4, 12106-12118.
591
[25] Xia, W.; Qu, C.; Liang, Z.; Zhao, B.; Dai, S.; Qiu, B.; Jiao, Y.; Zhang, Q.; Huang, X.;
592
Guo, W.; Dang, D.; Zou, R.; Xia, D.; Xu, Q.; Liu, M. High-performance energy storage
593
and conversion materials derived from a single metal-organic framework/graphene 27
ACS Paragon Plus Environment
Environmental Science & Technology
594
aerogel composite. Nanometer. Lett. 2017, 17, 2788-2795.
595
[26] Liu, X.; Sun, J.; Zhang, X. Novel 3D graphene aerogel-ZnO composites as efficient
596
detection for NO2 at room temperature. Sensor Actuat B: Chem. 2015, 211, 220-226.
597
[27] Yang, T. T.; Li, R.; Long, X. H.; Li, Z. J.; Gu, Z. G.; Wang, G.; Liu, J. K. Nitrogen and
598
sulphur-functionalized multiple graphene aerogel for supercapacitors with excellent
599
electrochemical performance. Electrochim. Acta. 2016, 187, 143-152.
600
[28] Wu, T.; Chen, M.; Zhang, L.; Xu, X.; Liu, Y.; Yan, J.; Wang, W.; Gao, J. P.
601
Three-dimensional graphene-based aerogels prepared by a self-assembly process and its
602
excellent catalytic and absorbing performance. J. Mater. Chem. A. 2013, 1, 7612-7621.
603
[29] Yang, C. X.; Liu, N. S.; Zeng, W.; Long, F.; Song, Z.; Sun, J.; Li, L.; Zou, Z.; Fang, G.;
604
Xiong, L.; Gao, Y. Superelastic and ultralight electron source from modifying 3D
605
reduced graphene aerogel microstructure. Nanometer Energy 2017, 33, 280-287.
606
[30] Cui, C.; Li, S.; Qiu, Y. W.; Hu, H. H.; Li, X. Y.; Li, C.; Gao, J.; Tang, W. Fast assembly of
607
Ag3PO4 nanometerparticles within three-dimensional graphene aerogels for efficient
608
photocatalytic oxygen evolution from water splitting under visible light. Appl. Catal. B:
609
Environ. 2017, 200, 666-672.
610
[31] Wang, C.; Yang, S.; Ma, Q.; Jia, X.; Ma, P. Preparation of carbon nanometertubes/
611
graphene hybrid aerogel and its application for the adsorption of organic compounds.
612
Carbon 2017, 118, 765-771.
613 614 615
[32] Hummer, W. S.; Offerman, R. E. Preparation of graphite oxide. J. Am. Chem. Soc. 1958, 80, 1339. [33] Sellers, R. M. Spectrophotometric determination of hydrogen peroxide using potassium 28
ACS Paragon Plus Environment
Page 28 of 32
Page 29 of 32
616
Environmental Science & Technology
titanium(IV) oxalate. Analyst 1980, 105, 950-954.
617
[34] Sun, Z.; Zhang, C., Xing, L.; Zhou, Q.; Dong, W. ; Hoffmann, M. R. Uv/nitrilotriacetic
618
acid process as a novel strategy for efficient photoreductive degradation of
619
perfluorooctanesulfonate. Environ. Sci. Technol. 2018, 52, 2953-2962.
620
[35] Yu, S.; Wang, X.; Yao, W.; Wang, J.; Ji, Y.; Ai, Y.; Alsaedi, A.; Hayat, T.; Wang, X.
621
Macroscopic, spectroscopic, and theoretical investigation for the interaction of phenol
622
and naphthol on reduced graphene oxide. Environ. Sci. Technol. 2017, 51, 3278−3286.
623
[36] Barreiro, J. C.; Capelato, M. D.; Neto, L. M.; Hansen, H. C. B. Oxidative decomposition
624
of atrazine by a Fenton-like reaction in a H2O2/ferrihydrite system. Wat. Res. 2007, 41,
625
55-62.
626
[37] Wang, J.; Chen, Z.; Chen, B. Adsorption of polycyclic aromatic hydrocarbons by
627
graphene and graphene oxide nanometersheets. Environ. Sci. Technol. 2014, 48, 4817-
628
4825.
629
[38] Lv, A.; Hu, C.; Nie, Y. L.; Qu, J. H. Catalytic ozonation of toxic pollutants over magnetic
630
cobalt and manganese co-doped γ-Fe2O3. Appl. Catal. B: Environ. 2010, 100, 62-67.
631
[39] Eigler, S.; Dotzer, C.; Hirsch, A. Visualization of defect densities in reduced graphene
632
oxide. Carbon 2012, 50, 3666-3673.
633
[40] Zellner, R.; Exner, M.; Herrmann, H. Absolute OH quantum yields in the laser photolysis
634
of nitrate, nitrite and dissolved H2O2 at 308 and 351 nm in the temperature range of
635
278-353 K. J. Atm. Chem. 1990, 10, 411-425.
636
[41] Walling, C.; Goosen, A. Mechanism of the ferric ion catalyzed decomposition of
637
hydrogen peroxide. Effect of organic substrates. J. Am. Chem. Soc. 1973, 95, 2987-2991. 29
ACS Paragon Plus Environment
Environmental Science & Technology
Page 30 of 32
638
[42] Walling, C. Fenton’s reagent revisited. Acc. Chem. Res. 1975, 8, 125-131.
639
[43] Ma, J. H.; Ma, W. H.; Song, W. J.; Chen, C. C.; Tang, Y.; Zhao, J. C.; Huang, Y. P.; Xu, Y.
640
M.; Zang, L. Fenton degradation of organic pollutants in the presence of
641
low-molecular-weight organic acids: Cooperative effect of quinone and visible light.
642
Environ. Sci. Technol. 2006, 40, 618-624.
643
[44] Qiu, B. C.; Xing, M. Y.; Zhang, J. L. Stӧber-like method to synthesize ultralight, porous,
644
stretchable Fe2O3/graphene aerogels for excellent performance in photo- Fenton reaction
645
and electrochemical capacitors. J. Mater. Chem. A. 2015, 3, 12820-12827.
646
[45] Qiu, B. C.; Li, Q. Y.; Shen, B.; Xing, M. Y.; Zhang, J. L. Stöber-like method to
647
synthesize ultradispersed Fe3O4 nanometerparticles on graphene with excellent
648
Photo-Fenton reaction and high-performance lithium storage. Appl. Catal. B: Environ.
649
2016, 183, 216-223.
650
[46] Zhou, Y.; Xiao, B.; Liu, S. Q.; Meng, Z.; Chen, Z. G.; Zou, C. Y.; Liu, C. B.; Chen, F.;
651
Zhou, X. Photo-Fenton degradation of ammonia via a manganese-iron double-active
652
component catalyst of graphene-manganese ferrite under visible light. Chem. Eng. J.
653
2016, 283, 266-275.
654
[47] Boruah, P. K.; Sharma, B.; Karbhal, I.; Shelke, M. V.; Das, M. R. Ammonia-modified
655
graphene sheets decorated with magnetic Fe3O4 nanometerparticles for the photocatalytic
656
and photo-Fenton degradation of phenolic compounds under sunlight irradiation. J.
657
Hazard. Mater. 2017, 325, 90-100.
658 659
[48] Li, X. Y.; Pi, Y. H.; Wu, L. Q.; Xia, Q. B.; Wu, J. L.; Li, Z.; Xiao, J. Facilitation of the visible
light-induced
Fenton-like
excitation
of
30
ACS Paragon Plus Environment
H2O2
via
heterojunction
of
Page 31 of 32
Environmental Science & Technology
660
g-C3N4/NH2-Iron terephthalate metal-organic framework for MB degradation. Appl.
661
Catal. B: Environ. 2017, 202, 653-663.
662
[49] Nguyen, X. S.; Zhang, G. K.; Yang, X. F. Mesocrystalline Zn-doped Fe3O4 hollow sub-
663
microspheres: Formation mechanism and enhanced photo-Fenton catalytic performance.
664
ACS Appl. Mater. Interfaces. 2017, 9, 8900-8909.
665
[50] Zhao, Y. B.; Pan, F.; Li, H.; Niu, T. C.; Xu, G. Q.; Chen, W. Facile synthesis of uniform
666
α-Fe2O3 crystals and their facet-dependent catalytic performance in the photo-Fenton
667
reaction. J. Mater. Chem. A. 2013, 1, 7242-7246.
668 669
[51] Liu, R.; Zhu, X.; Chen, B. A new insight of graphene oxide-Fe(III) complex photochemical behaviors under visible light irradiation. Sci. Rep. 2017, 7, 40711.
670
[52] Xu, L. J.; Wang, J. L. Magnetic Nanometerscaled Fe3O4/CeO2 composite as an efficient
671
Fenton-like heterogeneous catalyst for degradation of 4-chlorophenol. Environ. Sci.
672
Technol. 2012, 46, 10145-10153.
673
[53] Tamura, H.; Goto, K.; Yotsuyanagi, T.; Nagayama, M. Spectrophotometric determination
674
of iron(II) with 1,10-phenanthroline in the presence of large amounts of iron(III). Talanta
675
1974, 21, 314-318.
676
[54] Lin, Y. M.; Li, D. Z.; Hu, J. H.; Xiao, G. C. Highly efficient photocatalytic degradation of
677
organic pollutants by PANI-modified TiO2 composite. J. Phys. Chem. C. 2012, 116,
678
5764-5772.
679
[55] Sun, L. Z.; Bolton, J. R. Determination of the quantum yield for the photochemical
680
generation of hydroxyl radicals in TiO2 suspensions. J. Phys. Chem. 1996, 100,
681
4127-4134. 31
ACS Paragon Plus Environment
Environmental Science & Technology
682
[56] Malka, E.; Pereshtein, I.; Lipovsky, A.; Shalo, Y. K.; Naparstek, L.; Perkas, N.; Patick, T.;
683
Lubart, R.; Nitzan, Y.; Banin, E.; Gedanken, A. Eradication of multi-drug resistant
684
bacteria by a novel Zn-doped CuO nanometercomposite. Small 2016, 9, 4069-4076.
685
[57] Miller, R. M.; Singer, G. M.; Rosen, J. D.; Bartha. R. Sequential degradation of
686
chlorophenols by photolytic and microbial treatment. Environ. Sci. Technol. 1988, 22,
687
1215-1219.
688
[58] Wang, Y.; Sun, Y.; Li, W.; Tian, W.; Irini, A. High performance of nanometerscaled Fe2O3
689
catalyzing UV-Fenton under neutral condition with a low stoichiometry of H2O2: Kinetic
690
study and mechanism. Chem. Eng. J. 2015, 267, 1-8.