Role of Ru Oxidation Degree for Catalytic Activity ... - ACS Publications

Feb 29, 2016 - Role of Ru Oxidation Degree for Catalytic Activity in Bimetallic Pt/Ru Nanoparticles ... performance of Pt/Ru bimetals was increased wi...
0 downloads 0 Views 1MB Size
Subscriber access provided by LOCK HAVEN UNIV

Article

Identify the Role of Ru Oxidation Degree for Catalytic Activity in Bimetallic Pt/Ru Nanoparticles Huanhuan Wang, Shuangming Chen, Changda Wang, Ke Zhang, Daobin Liu, Yasir A. Haleem, Xusheng Zheng, Binghui Ge, and Li Song J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.5b12267 • Publication Date (Web): 29 Feb 2016 Downloaded from http://pubs.acs.org on February 29, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

The Journal of Physical Chemistry C is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Identify the Role of Ru Oxidation Degree for Catalytic Activity in Bimetallic Pt/Ru Nanoparticles Huanhuan Wang, † Shuangming Chen,* ,† Changda Wang, † Ke Zhang, † Daobin Liu, † Yasir A. Haleem, † Xusheng Zheng, † Binghui Ge, ‡ Li Song*,† †

National Synchrotron Radiation Laboratory, CAS Center for Excellence in

Nanoscience, University of Science and Technology of China, Hefei 230029, China



Beijing National Laboratory for Condensed Mater Physics, Institute of Physics,

Chinese Academy of Sciences, Beijing 100190, China

Abstract: Understanding the intrinsic relationship between the catalytic activity of bimetallic nanoparticles and their composition and structure is very critical for further modulating their properties and specific applications in catalyst, clean energy and other related fields. Here, we prepared new bimetallic Pt-Ru nanoparticles with different Pt/Ru molar ratio via a solvothermal method. In combination with X-ray diffraction (XRD), transmission electron microscopy (TEM) coupled with energy dispersive X-ray spectroscopy (EDX), X-ray photoelectron spectroscopy (XPS) and synchrotron X-ray absorption spectroscopy (XAS) techniques; we systematically investigated the dependence of the methanol electro-oxidation activity from the obtained Pt/Ru nanoparticles with different compositions under annealing treatment. Our observations revealed

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

that the Pt-Ru bimetallic nanoparticles have a Pt-rich core and a Ru-rich shell structure. After annealed at 500 ℃, the alloying extent of Pt-Ru nanoparticles increased, and more Pt atoms appeared in the surface. Notably, the subsequent evaluations of the catalytic activity for methanol oxidation reaction proved that the electrocatalytic performance of Pt/Ru bimetals was increased with the oxidation degree of superficial Ru atoms.

Introduction

Among various kinds of fuel cells, direct methanol fuel cells (DMFCs) have been considered to be promising power sources for future energy needs due to their high energy densities, low emissions, and facile fuel distribution and storage.1-3 Pt-based catalysts are the most efficient anode catalysts for the methanol oxidation reaction (MOR) in DMFCs.4 Nevertheless, challenging issues of Pt-based catalysts such as the high cost, low abundance and poison formation are the main obstacles to the commercialization of DMFCs.5 This has led to the development of Pt-based binary metallic systems, such as PtRu, PtMo, and PtSn and ternary compounds such as PtRuW, PtRuMo, and PtRuSn.6-8 PtRu alloy nanocrystals have been recognized as being greatly efficient electrocatalysts for methanol oxidation reaction.9 The effect of PtRu structural characteristics, such as composition, degree of alloying and Ru oxidation state, on the electrocatalytic activity for methanol oxidation has been reviewed.10 Guo et al. stated that the Pt-Ru (1:1) catalyst exhibited a highest methanol oxidation current and a lower poisoning rate.11 But Selda et al. found that a 0.25 Ru/Pt ratio is optimum at room temperature.12 An optimum ratio of 10-30% Ru at room

ACS Paragon Plus Environment

Page 2 of 27

Page 3 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

temperature for methanol oxidation has also been reported.13 There is also a debate i.e. whether a PtRu bimetallic alloy or a Pt and Ru oxide mixture is the most effective methanol oxidation catalyst. Gasteiger et al. concluded that the high catalytic activity of Pt-Ru alloys for the electrooxidation of methanol is described very well by bifunctional action of the alloy surface.14 Huang et al. suggested that the presence of crystalline RuO2 is essential to have a better methanol oxidation from Pt nanoparticles.15 On the other hand, Rolison et al. found that a commercial Pt−Ru catalyst comprised of oxides of Pt and Ru could deliberately control the chemical state of Ru to form RuOxHy rather than Ru metal or particularly anhydrous RuO2 because of poor proton conduction.16 However, no unanimous conclusion has been reached till now. Therefore, understanding the intrinsic relationship between the catalytic activity of bimetallic nanoparticles and their composition and structure is very critical for further modulating their properties and specific applications in catalyst, clean energy, etc. The primary goal of the present work is to conclusively establish the relative methanol oxidation activity of bimetallic Pt-Ru nanoparticles with different compositions and annealing-treatments, using a consistent experimental approach. The catalyst samples were thoroughly characterized by physical and electrochemical technologies. Our detailed analysis of bimetal’s catalytic activity for methanol oxidation reaction revealed that the Pt/Ru nanoparticles with a Pt-rich core and Ru-rich shell structure have increased electro-oxidation of methanol with the oxidation state of Ru atoms. This study provides useful insight for understanding the

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

intrinsic relationship between catalytic property and structure/composition, thus broadening the window for designing new-generation catalysts.

Experimental section Sample preparation. In a typical procedure for PtRu, 0.0889 g Polyvinyl Pyrrolidone (PVP), 400 µL 0.2M RuCl3(aq) and 800 µL 0.1M H2PtCl6(aq) were dissolved in 38.8 mL ethylene glycol (EG) under constant magnetic stirring for 30 min. Then, mixed solution was transferred into a stainless autoclave with a 50 mL Teflon liner and heated in an oven at 200 °C for 12 h. After the autoclave was naturally cooled to room temperature, 23.68 mg acetylene black was added to the resulted black solution and continuously stirred for 30 min. The final product was gained by centrifugation, washed several times with deionized water and absolute ethanol, and dried in a vacuum oven at 60 °C for 12 h. The procedure for Pt2Ru and PtRu2 was the same as PtRu except for the molar ratio of RuCl3 and H2PtCl6 changed to 1:2 and 2:1. To investigate the influence of annealing process, the resulting PtRu powder was calcined at 500 ℃ under 100 sccm H2/Ar flow for 4h. Sample Characterization and XAFS Data Analysis. X-ray diffraction was performed on a TTR-III high-power X-ray powder diffractometer employing a scanning rate of 0.02 s-1 in a 2θ range from 30° to 90° with Cu Kα radiation. The morphology of samples was characterized by a transmission electron microscopy (TEM, JEM-2100F), equipped with energy dispersive X-ray spectroscopy (EDX). The sample for TEM was prepared by placing a drop of ultrasonically dispersed ethanol

ACS Paragon Plus Environment

Page 4 of 27

Page 5 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

solution onto a carbon-coated copper grid and allowing the solvent to be evaporated in air at room temperature. Metal concentrations were measured by inductively coupled plasma (ICP) atomic emission spectroscopy (AES) using an Atomscan Advantage Spectrometer. HAADF-STEM and EDX elemental mapping analysis were carried out in a JEOL ARM-200 microscope at 200 kV. X-ray photoelectron spectroscopy (XPS) experiments were performed at the Photoemission Endstation at the BL10B beamline in the National Synchrotron Radiation Laboratory (NSRL) in Hefei, China. This beamline is connected to a bending magnet and equipped with three gratings that cover photon energies from 100 to 1000 eV with a typical photon flux of 1×1010 photons/s and a resolution(E/∆E) better than 1000 at 244 eV. The Pt L3-edge and Ru K-edge XAFS measurements were made in transmission mode at the beamline 14W1 in Shanghai Synchrotron Radiation Facility (SSRF) and 1W1B station in Beijing synchrotron Radiation Facility (BSRF). The X-ray was monochromatized by a double-crystal Si(311) monochromator, and the energy were calibrated using a platinum metal foil for Pt L3-edge and a Ruthenium metal foil for Ru K-edge. The monochromator was detuned to reject higher harmonics. XAFS data was analyzed with WinXAS3.1 program.17 The energy thresholds were determined as the maxima of the first derivative. Absorption curves were normalized to 1, and the EXAFS signals χ(k) were obtained after the removal of pre-edge and post-edge background. The Fourier transform (FT) spectra were obtained as k3χ(k) with a Bessel window in the range 3-12.5 Å−1 for Pt L3-edge and 3.2-13.2 Å−1for Ru K-edge. Theoretical amplitudes and phase-shift functions of Pt-Pt, Ru-Ru,Pt-O and Ru-O

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

were calculated with the FEFF8.2 code18 using the crystal structural parameters of the Pt foil, Ru foil, PtO2 and RuO2.19-21 On the basis of a face-centered cubic (fcc) model, Pt-Ru bond was modeled. The S02 values were found to be 1.06 and 0.93 for Pt and Ru, respectively. Electrochemical Measurements. Electrochemical measurements were taken using a conventional three-electrode system,with a Pt mesh electrode as counter electrode, a silver/silver chloride electrode (Ag/AgCl) as the reference electrode and a 3 mm diameter glassy carbon electrode as working electrode. The working electrode was prepared by coating a small amount of catalyst ink on glassy carbon electrode. Carbon-supported PtRu catalyst (2.0mg) was dispersed into a solution containing 1 mL ethanol and 10 µL Nafion solution (5 wt %), followed by ultrasonic treatment for 30 min, and then the resultant suspension (ca. 10 µL) was pipetted onto glassy carbon electrode and dried at room temperature for 20 min. Prior to coating with catalyst ink, glassy carbon electrode was polished with alumina paste and washed with de-ionized water. Cyclic voltammetry was carried out to study the methanol oxidation reaction (MOR) at room temperature in an electrolyte containing 1.0 M KOH and 1.0 M CH3OH between -0.8 and 0.3 V (vs Ag/AgCl) at a scan rate of 50 mV/s. Prior to each cyclic voltammetry measurement, the electrolytic solution was purged with pure N2 for 30 min to remove dissolved oxygen. Results and discussion XRD and TEM Characterization. Fig. 1 shows the comparison of XRD patterns for different samples. The characteristic peaks for a face centered cubic phase (fcc)

ACS Paragon Plus Environment

Page 6 of 27

Page 7 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

were clearly observed in all samples. No additional peaks such as Pt or Ru oxides can be detected. Interestingly, the characteristic peaks shifted to higher angle with the increasing Ru percentage, indicating the contraction of the lattice parameter due to the formation of the Pt-Ru alloy. In addition, the diffraction peaks shifted to higher angles and became slightly sharper after annealing. It suggests that the annealing process can reduce the lattice parameter and slightly increased the grain size and the alloying extent of Pt/Ru nanocrystals. The particle size and corresponding histograms of size distribution of different samples are shown in Fig. 2. It can be seen that most particles of PtRu, Pt2Ru and PtRu2 are monodisperse with average size about 3~4 nm. After annealing, the particles became slightly larger in size (Fig. 2d). The compositions of the catalyst were measured by ICP-AES and EDX shown in Fig. S1 and Table S1 (Supporting Information), in which the overall chemical compositions for PtRu, Pt2Ru, and PtRu2 alloy nanoparticle electrocatalysts are well confirmed with 1:1, 2:1 and 1:2 of Pt:Ru atomic ratios. High angle annular dark field scanning transmission electron microscopy (HAADF-STEM) image and the corresponding EDX elemental mapping image of PtRu are shown in Fig. 2e and Fig. 2f. These observations reveal that the prepared PtRu particles are formed by Ru and Pt elements. EDX elemental mapping image indicates that Ru atoms have more degree of dispersion than Pt atoms. XANES and XPS Analysis. To identify the microstructure of Pt/Ru bimetals, we performed synchrotron-based X-ray absorption spectroscopy (XAS) of the samples. The X-ray absorption near edge structure (XANES) spectra of Pt L3-edge and Ru

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

K-edge were shown in Fig. 3. In Pt L3-edge of Fig. 3a, all samples exhibited more intense white line peaks than Pt foil. It is known that the Pt L3-edge white line corresponds to the excitation of 2p3/2 electrons to empty 5d orbitals,22 this means more unoccupied 5d states of Pt atoms in these Pt/Ru alloy nanoparticles in contrast to Pt foil. In general, the explanation can be ascribed to three effects: size effect, alloying effect and surface oxidation effect. However, as the Pt atoms in pure Pt nanoparticles have more d electrons than that in bulk,23 the influence of size effect can be eliminated. To clarify the alloying effect, we investigated Pt L3-edge XANES spectrum of Pt-Ru alloy, and compared it with spectrum of pure Pt. In the calculations, we modeled the Pt L3-edge XANES spectra of Pt-Ru alloy by replacing some of the twelve nearest-neighbored Pt atoms around central Pt atom with Ru atoms. As shown in Fig. 3b, it can be clearly seen that Pt/Ru alloy has a slightly weaker white line peak compared to pure Pt. That means, the alloying effect cannot cause the increase of the white line peak intensity. At last, we suggest that the increase can be attributed to surface oxidation effect. More precisely, it originates from oxidation of some surface Pt atoms. Besides, it is worth noting that the white line intensity for PtRu, Pt2Ru and PtRu2 were almost constant while PtRu-annealed exhibited a distinct increase, which can be explained by increasing oxidized Pt atoms after annealing. However, strong oxidation of Pt in these Pt-Ru alloy nanoparticles should be ruled out based on the direct comparison with bulk Pt and PtO2. For Ru K-edge XANES spectra in Fig. 3c, the Ru atoms in sample PtRu, Pt2Ru and PtRu2 were partially oxidized whereas order

ACS Paragon Plus Environment

Page 8 of 27

Page 9 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

of oxidation degree is Pt2Ru>PtRu>PtRu2. Similarly, strong oxidation of Ru should also be eliminated. Notably, there is almost no oxidation of Ru in PtRu after annealed-treatment. This means, oxidized Ru atoms in PtRu were reduced by annealing process. In order to further investigate the electronic structure of these Pt-Ru nanoparticles, XPS spectra for the Pt 4f and Ru 3d core level region for all samples were performed shown in Figure 4. As we can see in Figure 4a, The binding energies (BE) of Pt 4f7/2 for all PtRu, Pt2Ru and PtRu2 are almost same while a slight right shift to higher BE can be observed PtPu-annealed, suggesting an increase of the d-vacancy of Pt atoms.24 The Ru 3d core level region was deconvoluted shown in Figure 4b-e, as described by Roblison et al.25 The corresponding deconvoluted results are summarized in Table 2. The XPS data suggest that there are three Ru species (Ru metal, RuO2 and RuO2.xH2O) present in the surface of Pt-Ru catalyst. It is noting that the percentage of Ru-OH specie (RuO2.xH2O) and Ru-oxide increase in the following trend: Pt2Ru> PtRu>PtRu2>PtRu-annealed, consistent with the XANES analysis result. EXAFS Analysis. To further study the structure, corresponding extended X-ray absorption fine structure (EXAFS) of the samples were analyzed. The k3-weighted EXAFS signals of Pt L3-edge and Ru K-edge are shown in Fig. S2 (Supporting Information). It has been noted that EXAFS oscillations of all samples were lower in amplitude compared to that of bulk Pt and bulk Ru in both Pt L3-edge and Ru K-edge, which can be attributed to the size effect of nanoparticles. In contrast to amplitude, the phase of EXAFS oscillations of PtRu, Pt2Ru and PtRu2 were similar to bulk sample,

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

which indicates these nanoparticles are more likely to be a core-shell structure rather than an alloying structure. As the control sample, the EXAFS oscillations of PtRu-annealed were slightly phase-shifted at each edge, replying the increasing alloying extent after the annealing process. Particularly, the comparison with the EXAFS signals of standard Pt and Ru oxides further confirmed that strong oxidation of Pt and Ru could be eliminated in our samples. Fig. 5a and 5b shows the corresponding Fourier-transformed EXAFS spectra of Pt L3-edge and Ru K-edge. It is observed that Pt L3-edge for PtRu, Pt2Ru and PtRu2 exhibit similar local structure around Pt. However, there is a significant change of local structure around Pt in PtRu after annealed treatment. From Ru K-edge, we can conclude that Ru atoms in Pt2Ru have the highest oxidation degree. EXAFS data analysis was carried out by simultaneously fitting both the Pt L3-edge and Ru K-edge. The comparison of experimental and fitting data for Pt L3-edge and Ru K-edge were shown in Fig. S3-S4 (Supporting Information), and corresponding fitting parameters were summarized in Table S2 (Supporting Information). According to previously reported literature,26 we can determine atomic distribution and alloying extent in bimetallic nanoparticles based on four parameters, Pobserved(NPt-Ru/NPt-i), Robserved(NRu-Pt/NRu-i), Prandom, and Rrandom. For PtRu and PtRu-annealed samples, Prandom and Rrandom can be taken as 0.5 as the atomic ratio of Pt and Ru is 1:1. For Pt2Ru sample, Prandom and Rrandom can be taken as 0.33 and 0.67 respectively as the atomic ratio of Pt and Ru is 2:1. Conversely, Prandom and Rrandom can be taken as 0.67 and 0.33 for PtRu2. Then, alloying extents of Pt (JPt) and Ru (JRu) can

ACS Paragon Plus Environment

Page 10 of 27

Page 11 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

be calculated using following equations: JPt = (Pobserved/Prandom) × 100%

(1)

JRu = (Robserved/Rrandom) × 100%

(2)

All the calculated results based on this method are summarized in Table 1. The observed parameter relationships ∑NPt-M > ∑NRu-M and JRu, JPt < 100% indicate that all of the as-synthesized Pt-Ru nanoparticles adopt a Pt-rich core and Ru-rich shell structure. The larger JPt and JRu value in PtRu-annealed indicates the increasing extent of atomic dispersion and alloying extent after annealing process, which is in consistent with above analysis. The higher values of Robserved and JRu suggest higher alloying extent of Ru atoms than Pt. That means, most of Ru atoms were reduced and involved in alloying after annealing process. Meanwhile, some Pt atoms migrated to the surface and then oxidized by air, according to the XANES and XPS analysis. Here, we can summarize that as-grown Pt/Ru nanoparticles have a Pt-rich core and Ru-rich shell structure. After annealing process, the alloying extent of Pt/Ru nanoparticles has been increased, and more Pt atoms appeared on the surface. The structure of Pt/Ru nanoparticles are schematically shown in Fig. 5c. Catalytic performance in the methanol electro-oxidation. Cyclic voltammetry experiments were performed in N2-saturated freshly prepared 1 M KOH solution by sweeping the electrode potential from -0.8 to 0.3 V vs Ag/AgCl at a scan rate of 50 mV/s, to measure the electrochemical active surface area (ECSA) of the catalysts, as shown in Fig. S5 (Supporting Information). The integrated charge in the hydrogen adsorption/desorption peak area in the CV curves represents the total charge

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

concerning H+ adsorption, QH, and has been used to determine ECSA by employing the equation27 ECSAm /g of Pt =

chargeQ , μC/cm  210μC/cm  × electrode loading g of Pt/m 

The trend in ECSA values varied in the following order: Pt2Ru (80.71 m2/g) > PtRu (64.01 m2/g) > PtRu2 (52.08 m2/g) > PtRu-annealed (27.63 m2/g). Among these electrocatalysts, Pt2Ru was ascertained to possess the greatest electrochemical activity. Accordingly, it is rational to assume that the higher ECSA value may signify the better electrocatalyst that has more catalyst sites available for electrochemical reaction. In order to investigate the effect of Pt/Ru bimetal’s structure on their catalytic property, a methanol electro-oxidation experiment was carried out. Fig. 6a displays cyclic voltammograms (CVs) of methanol oxidation on Pt2Ru, PtRu, PtRu2 and PtRu-annealed in 1.0 M KOH containing 1.0 M CH3OH solution. Two well-defined oxidation peaks can be clearly observed, one in the forward scan is produced because of oxidation of freshly chemisorbed species coming from methanol adsorption, and the other in the reverse scan is primarily ascribed to removal of incompletely oxidized carbonaceous species formed during forward scan. As known, the oxidation peak during the forward scan can be used to evaluate the catalytic activity of the catalyst. It is estimated that the values of current density increase in the following trend: Pt2Ru> PtRu > PtRu2. This phenomenon is attributed to two probable reasons: one is increasing oxidation degree of surface Ru atoms in these samples (Pt2Ru>PtRu> PtRu2), which is consistent with the order of catalytic activity of the catalysts, while

ACS Paragon Plus Environment

Page 12 of 27

Page 13 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

the other is increasing Pt concentration in these Pt/Ru catalysts. However, with same composition, the PtRu-annealed sample with lowest oxidation degree of Ru atoms and more Pt atoms in surface exhibits worst catalytic activity. Thus, we can suggest that the higher methanol oxidation catalytic activity is originating from the increasing oxidation degree of surface Ru atoms in Pt/Ru bimetals. It is probable due to the content of Ru-OH increasing with the oxidation degree of surface Ru atoms, as Ru-OH is a critical component of the MOR of Pt-Ru catalyst which decided the electrocatalytic activity of Pt-Ru.25 Furthermore, the ratio of the forward anodic peak current density (If) to the reverse anodic peak current density (Ib) - If/Ib can be used as an important index to evaluate the catalyst tolerance to the CO accumulation.28-29 Our calculation indicates that Pt2Ru, PtRu and PtRu2 have almost the same If/Ib value, while the If/Ib value of PtRu-annealed is obviously larger. It may be attributed to the increasing alloying extent after annealing process, as it has been proved that the tolerance to the CO accumulation of Pt-Ru alloying catalyst will increase with the alloying degree.30 In a word, the best catalyst for oxidation of CO accumulation is not necessarily the best one for methanol oxidation.10 Moreover, chronoamperometry (CA) was also performed to investigate the long-term stability of those catalysts under the same conditions. Fig. 6b shows CA curves performed in 1.0 M KOH + 1.0 M CH3OH at -0.2 V (vs Ag/AgCl) for 2500 s. After a sharp drop in the initial period of around 300 seconds, the currents decay at a much slower speed and then approach a flat line. During the whole time, it was clear that current density produced on the Pt2Ru catalyst was higher than the current density

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

produced on the PtRu, PtRu2 and PtRu-annealed catalysts. These results are in agreement with those of the cyclic voltammetry measurements, indicating that Pt/Ru bimetals with higher Ru oxidation degree can pose better methanol oxidation catalytic activity. Conclusions

Bimetallic Pt-Ru nanoparticles with different Pt/Ru molar ratios were synthesized by a solvothermal method and characterized by various methods. Our observations revealed that these Pt-Ru nanoparticles have a Pt-rich core and a Ru-rich shell structure. After annealing at 500 ℃, the alloying extent of Pt/Ru nanoparticles increased, a portion of Pt atoms migrated to surface, and most of surficial oxidized Ru atoms were reduced and involved in alloying. The evaluations of methanol electro-oxidation activity elucidated that electrocatalytic performance improved with the increasing oxidation degree of superficial Ru atoms. This study provides useful information and deep insight for understanding the relationship of electrocatalytic performance of bimetallic nanoparticles with their structure, which may help us to further tune the bimetal’s structure, composition and catalytic activity for specific applications.

ACS Paragon Plus Environment

Page 14 of 27

Page 15 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Figure Captions

Fig. 1 XRD patterns of PtRu, PtRu-annealed, Pt2Ru and PtRu2.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 2 TEM images and histograms of particle-size distributions of (a) PtRu, (b) Pt2Ru, (c) PtRu2 and (d) PtRu after annealed treatment; (e) HAADF-STEM image and (f) the corresponding EDX elemental mapping image of PtRu.

ACS Paragon Plus Environment

Page 16 of 27

Page 17 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Fig. 3 XANES spectra at the (a) Pt L3-edge and (c) Ru K-edge for Pt foil, Ru foil, PtO2, RuO2 and all samples; (b) The comparison of the calculated Pt-L3 edge XANES spectra of pure Pt and Pt-Ru alloy with some Pt atoms substituted by Ru atoms in the first shell.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Fig. 4 XPS spectra of (a) Pt 4f and C 1s + Ru 3d for (b) PtRu, (c) PtRu-annealed, (d) Pt2Ru and (e) PtRu2. The entire Ru 3d + C 1s envelope was deconvolved for all spectra, but for clarity, only the fits for Ru 3d5/2 lines are shown. The envelopes are fitted with three Ru 3d5/2 peaks.

ACS Paragon Plus Environment

Page 18 of 27

Page 19 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Fig. 5 Fourier-transformed EXAFS spectra of (a) Pt L3-edge and (b) Ru K-edge for Pt foil, Ru foil, PtO2, RuO2 and all samples; (c) Schematic representation of the structure of the Pt-Ru nanoparticles with different molar ratio synthesized by EG reduction and after annealing.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 27

Fig. 6 (a) Cyclic voltammograms and (b) Chronoamperometric curves at -0.2 V for 2500 s towards methanol electro-oxidation of Pt-Ru nanoparticles. Electrolyte solution was 1.0 M KOH + 1.0M CH3OH (Scan rate: 50 mV/s).

Table 1. Alloying extent values of all samples SAMPLE

ΣNPt-M

ΣNRu-M

Pobserved

Robserved

JPt(%)

JRu(%)

PtRu

10.2

7.3

0.09

0.26

0.18

0.52

PtRu-annealed

10.1

6

0.19

0.53

0.38

1.06

PtRu2

10.8

7.5

0.1

0.2

0.15

0.61

Pt2Ru

10.1

7.5

0.07

0.12

0.21

0.18

ACS Paragon Plus Environment

Page 21 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Table 2. Binding energies of Ru species obtained from curve-fitted Ru 3d5/2 XPS spectra for PtRu catalysts. catalysts

Binding

assignment

energy/eV PtRu

PtRu-annealed

Pt2Ru

PtRu2

Relative concentration/%

280.0

Ru metal

58.25

280.9

RuO2

19.42

282.2

.

RuO2 xH2O

22.33

279.8

Ru metal

62.16

280.8

RuO2

21.62

282.2

.

RuO2 xH2O

16.22

280

Ru metal

45.46

280.9

RuO2

27.27

282.3

RuO2.xH2O

27.27

280

Ru metal

61.54

280.9

RuO2

19.23

282.2

.

19.23

RuO2 xH2O

Supporting Information EDX analyses of Pt2Ru, PtRu and PtRu2; Comparison of compositions determined from EDX and ICP; Comparison of k3-weighted EXAFS signals, experimental data and the fitting curves for Pt L3-edge and Ru K-edge; Cyclic voltammograms (CVs) of all samples in 1 M KOH; Best fit parameters of the Pt L3-edge and Ru K-edge EXAFS spectra. This material is available free of charge via the Internet at http://pubs.acs.org.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 27

AUTHOR INFORMATION Corresponding Author *(email: [email protected]; [email protected];)

Notes The authors declare no competing financial interest.

Acknowledgement. Financial supports come from 973 program (2014CB848900), NSF (U1232131, U1532112, 11375198, 11574280), the Postdoctoral Science Foundation of China (2015M581990), the Fundamental Research Funds for the Central Universities (WK2310000035) and User with Potential from CAS Hefei Science Center (CX2310000080). We also thank the SSRF (BL14W1), BSRF (1W1B),

MCD

and

Photoemission

Endstations

in

NSRL

for

helps

in

synchrotron-based measurements.

References

(1). Wang, D. Y.; Chou, H. L.; Lin, Y. C.; Lai, F. J.; Chen, C. H.; Lee, J. F.; Hwang, B. J.; Chen, C. C., Simple replacement reaction for the preparation of ternary Fe(1-x)PtRu(x) nanocrystals with superior catalytic activity in methanol oxidation reaction. J. Am. Chem. Soc., 2012, 134, 10011-10020. (2). Eid, K.; Wang, H.; He, P.; Wang, K.; Ahamad, T.; Alshehri, S. M.; Yamauchi, Y.; Wang, L., One-step synthesis of porous bimetallic PtCu nanocrystals with high electrocatalytic activity for methanol oxidation reaction. Nanoscale, 2015, 7, 16860-16866. (3). Zhang, H.; Jin, M.; Xia, Y., Enhancing the catalytic and electrocatalytic

ACS Paragon Plus Environment

Page 23 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

properties of Pt-based catalysts by forming bimetallic nanocrystals with Pd.

Chem. Soc. Rev., 2012, 41, 8035-8049. (4). Sau, T. K.; Lopez, M.; Goia, D. V., Method for preparing carbon supported Pt−Ru nanoparticles with controlled internal structure. Chem. Mater., 2009, 21, 3649-3654. (5). Bing, Y.; Liu, H.; Zhang, L.; Ghosh, D.; Zhang, J., Nanostructured Pt-alloy electrocatalysts for PEM fuel cell oxygen reduction reaction. Chem. Soc. Rev., 2010, 39, 2184-2202. (6). Figueiredo, M. C.; Sorsa, O.; Arán-Ais, R. M.; Doan, N.; Feliu, J. M.; Kallio, T., Trimetallic catalyst based on PtRu modified by irreversible adsorption of Sb for direct ethanol fuel cells. J. Catal., 2015, 329, 69-77. (7). Uribe-Godínez, J.; García-Montalvo, V.; Jiménez-Sandoval, O., A novel Rh–Ir electrocatalyst for the oxygen reduction reaction and the hydrogen and methanol oxidation reactions. Int. J. Hydrogen Energy, 2014, 39, 9121-9127. (8). Hassan, A.; Paganin, V. A.; Ticianelli, E. A., Effect of addition of Ru and/or Fe in the stability of PtMo/C electrocatalysts in proton exchange membrane fuel cells. Electrocatalysis, 2015, 6, 512-520. (9). Wiltshire, R. J.; King, C. R.; Rose, A.; Wells, P. P.; Davies, H.; Hogarth, M. P.; Thompsett, D.; Theobald, B.; Mosselmans, F. W.; Roberts, M. et al., Effects of composition on structure and activity of PtRu/C catalysts. Phys. Chem. Chem.

Phys., 2009, 11, 2305-2313. (10). Godoi, D. R. M.; Perez, J.; Villullas, H. M., Effects of alloyed and oxide

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

phases on methanol oxidation of Pt−Ru/C nanocatalysts of the same particle size. J. Phys. Chem. C, 2009, 113, 8518-8525. (11). Guo, J. W.; Zhao, T. S.; Prabhuram, J.; Chen, R.; Wong, C. W., Preparation and characterization of a PtRu/C nanocatalyst for direct methanol fuel cells.

Electrochim. Acta, 2005, 51, 754-763. (12). Sen, S.; Sen, F.; Gokagac, G., Preparation and characterization of nano-sized Pt-Ru/C catalysts and their superior catalytic activities for methanol and ethanol oxidation. Phys. Chem. Chem. Phys., 2011, 13, 6784-6792. (13). Iwasita, T.; Hoster, H.; John-Anacker, A.; Lin, W.; Vielstich, W., Methanol oxidation on PtRu electrodes. Influence of surface structure and Pt-Ru atom distribution. Langmuir, 2000, 16, 522-529. (14). Gasteiger, H. A.; Markovic, N.; Ross Jr, P. N.; Cairns, E. J., Methanol electrooxidation on well-characterized platinum-ruthenium bulk alloys. J. Phys.

Chem., 1993, 97, 12020-12029. (15). Huang, S. y.; Chang, C. m.; Wang, K. w.; Yeh, C. t., Promotion of platinum‐ ruthenium catalyst for electrooxidation of methanol by crystalline ruthenium dioxide. Chemphyschem, 2007, 8, 1774-1777. (16). Rolison, D. R.; Hagans, P. L.; Swider, K. E.; Long, J. W., Role of hydrous ruthenium oxide in Pt-Ru direct methanol fuel cell anode electrocatalysts: the importance of mixed electron/proton conductivity. Langmuir, 1999, 15, 774-779. (17). Ressler, T., WinXAS: a program for X-ray absorption spectroscopy data

ACS Paragon Plus Environment

Page 24 of 27

Page 25 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

analysis under MS-Windows. J. Synchrotron. Radiat., 1998, 5, 118-122. (18). Ankudinov,

A.;

Ravel,

B.;

Rehr,

J.;

Conradson,

S.,

Real-space

multiple-scattering calculation and interpretation of x-ray-absorption near-edge structure. Phys. Rev. B: Condens. Matter, 1998, 58, 7565. (19). Haines, J.; Leger, J.; Schulte, O.; Hull, S., Neutron diffraction study of the ambient-pressure, rutile-type and the high-pressure, CaCl2-type phases of ruthenium dioxide. Acta Crystallogr., Sect. B: Struct. Sci, 1997, 53, 880-884. (20). Häglund, J.; Guillermet, A. F.; Grimvall, G.; Körling, M., Theory of bonding in transition-metal carbides and nitrides. Phys. Rev. B: Condens. Matter, 1993,

48, 11685-11691. (21). Hoekstra, H. R.; Siegel, S.; Gallagher, F. X., Reaction of platinum dioxide with some metal oxides. Adv. Chem. Ser., 1971, 98, 39. (22). Chen, S.; Yang, Q.; Wang, H.; Zhang, S.; Li, J.; Wang, Y.; Chu, W.; Ye, Q.; Song,

L.,

Initial

reaction

mechanism

of

platinum

nanoparticle

in

methanol-water system and the anomalous catalytic effect of water. Nano Lett., 2015, 15, 5961-5968. (23). Bayindir, Z.; Duchesne, P.; Cook, S.; MacDonald, M.; Zhang, P., X-ray spectroscopy studies on the surface structural characteristics and electronic properties of platinum nanoparticles. J. Chem. Phys., 2009, 131, 244716. (24). Igarashi, H.; Fujino, T.; Zhu, Y.; Uchida, H.; Watanabe, M., CO tolerance of Pt alloy electrocatalysts for polymer electrolyte fuel cells and the detoxification mechanism. Phys. Chem. Chem. Phys., 2001, 3, 306-314.

ACS Paragon Plus Environment

The Journal of Physical Chemistry

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

(25). Rolison, D. R.; Hagans, P. L.; Swider, K. E.; Long, J. W., Role of hydrous ruthenium oxide in Pt-Ru direct methanol fuel cell anode electrocatalysts: the importance of mixed electron/proton conductivity. Langmuir, 1999, 15, 774-779. (26). Hwang, B.-J.; Sarma, L. S.; Chen, J.-M.; Chen, C.-H.; Shih, S.-C.; Wang, G.-R.; Liu, D.-G.; Lee, J.-F.; Tang, M.-T., Structural models and atomic distribution of bimetallic nanoparticles as investigated by X-ray absorption spectroscopy. J. Am. Chem. Soc., 2005, 127, 11140-11145. (27). Huang, Y.; Cai, J.; Guo, Y., Facile synthesis of a Bi-modified PtRu catalyst for methanol and ethanol electro-oxidation in alkaline medium. Int. J. Hydrogen

Energy, 2013, 38, 3250-3256. (28). Maiyalagan, T.; Dong, X.; Chen, P.; Wang, X., Electrodeposited Pt on three-dimensional interconnected graphene as a free-standing electrode for fuel cell application. J. Mater. Chem., 2012, 22, 5286. (29). Maiyalagan, T.; Alaje, T. O.; Scott, K., Highly stable Pt–Ru nanoparticles supported on three-dimensional cubic ordered mesoporous carbon (Pt– Ru/CMK-8) as promising electrocatalysts for methanol oxidation. J. Phys.

Chem. C, 2012, 116, 2630-2638. (30). Lee, K.-S.; Jeon, T.-Y.; Yoo, S. J.; Park, I.-S.; Cho, Y.-H.; Kang, S. H.; Choi, K. H.; Sung, Y.-E., Effect of PtRu alloying degree on electrocatalytic activities and stabilities. Appl. Catal. B, 2011, 102, 334-342.

ACS Paragon Plus Environment

Page 26 of 27

Page 27 of 27

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

TOC graphic

ACS Paragon Plus Environment