C: Physical Processes in Nanomaterials and Nanostructures

Aggregation/Self-Assembly-Induced Approach for Efficient AuAg Bimetallic Nanocluster-Based Photosensitizers Daiki Hikosou, Sastoshi Saita, Saori Miyata, Hirofumi Miyaji, Tetsuya Furuike, Hiroshi Tamura, and Hideya Kawasaki J. Phys. Chem. C, Just Accepted Manuscript • DOI: 10.1021/acs.jpcc.8b02373 • Publication Date (Web): 23 May 2018 Downloaded from http://pubs.acs.org on May 24, 2018

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Aggregation/Self-Assembly-Induced Approach for Efficient AuAg Bimetallic Nanocluster-Based Photosensitizers Daiki Hikosou,1) Sastoshi Saita,1) Saori Miyata,2) Hirofumi Miyaji,2) Tetsuya Furuike,1) Hiroshi Tamura,1) and Hideya Kawasaki1)* 1)

Department of Chemistry and Materials Engineering, Faculty of Chemistry, Materials and

Bioengineering, Kansai University, Suita-shi, Osaka 564-8680, Japan 2)

Department of Periodontology and Endodontology, Faculty of Dental Medicine, Hokkaido

University, Kita-ku, Sapporo 060-8586, Japan *Corresponding Author: Hideya Kawasaki E-mail: [email protected]

ABSTRACT: Great efforts have been devoted to the exploration of potential diagnostic and therapeutic applications of thiolate-protected gold nanoclusters (Au NCs). One of the therapeutic applications is the photosensitized generation of highly reactive singlet oxygen (1O2) using Au NCs for photodynamic therapy. However, there is scope for improving the 1O2-generation efficiency of Au NC photosensitizers. In this study, we exploit three strategies to improve the

ACS Paragon Plus Environment

1

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

1

Page 2 of 27

O2-generation efficiency of glutathione-protected Au NCs: (i) doping with silver (i.e., using

bimetallic AuAg NCs, (ii) achieving aggregation-induced emission (AIE) using a Au(I)–thiolate complex, and (iii) achieving self-assembly-induced emission (SAIE) using a polymer nanogel. The combination of these three effects dramatically increased the 1O2-generation efficiency and enhanced the luminescence of the glutathione-protected Au NCs, owing to the inhibition of the nonradiative decay pathways. Finally, the photosensitizers based on AuAg NC@nanogel composites were successfully used for antimicrobial photodynamic therapy (a-PDT) against oral bacteria. This study provides general insights on the molecular design of water-soluble Au NC photosensitizers for therapeutic applications.

INTRODUCTION Thiolate-protected gold nanoclusters (Au NCs) exhibit discrete energy levels owing to their ultra-small sizes (< 2 nm) and specific crystal structures, which result in their molecule-like properties such as a well-defined molecular structure, HOMO–LUMO transitions, chirality, photocatalytic properties, and strong luminescence. The ultra-small Au NCs have distinctly different physiochemical properties than their larger counterparts, plasmonic Au nanoparticles (> 3 nm), and their properties are governed by the number of Au atoms (i.e., size) and the molecular structure of the surface ligands.1–4 Therefore, various methods have been developed for fabricating atomically precise thiolate-protected Au NCs, and the well-defined structure of the thiolate-protected Au NCs with a staple motif oligomer of Au(I)–thiolate complexes has been determined by single-crystal X-ray crystallography.1–11

ACS Paragon Plus Environment

2

Page 3 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Recently, great efforts have been devoted to the exploration of potential diagnostic applications, such as biological analysis and biological imaging, and therapeutic applications of water-soluble Au NCs, because of their high stability, good targeting ability owing to specific surface ligands, and low toxicity.12–16 One of the therapeutic applications is the photosensitized generation of reactive oxygen species using Au NCs as a photosensitizer for photodynamic therapy (PDT).17–26 Previously, we have reported Au NC photosensitizers and the effects of their size and type of surface ligands on singlet oxygen (1O2) generation.27–30 The photo-excited Au NC undergoes intersystem crossing (ISC) from its lowest singlet excited state (S1) to the lowest triplet excited state (T1). Subsequently, the transfer of energy from the T1 state of the Au NC to the ground-state oxygen (3O2) generates 1O2, which causes oxidative damage of targets. Efficient 1

O2 generation by the Au NC photosensitizer is important in PDT. However, there is scope for

improving the 1O2-generation efficiency of Au NC photosensitizers. Extensive studies have been conducted on strategies to improve the 1O2-generation efficiency of organic photosensitizers.31,32 The incorporation of heavy atoms into molecular structures is one of the most widely used approaches for improving the 1O2-generation capability of organic photosensitizers.33 More recently, the exploitation of aggregation-induced emission (AIE) of organic photosensitizers has emerged as a novel strategy for enhanced fluorescence and efficient photosensitizing because of the inhibition of energy dissipation through nonradiative pathways,34–36 in contrast to the cases of aggregation-induced emission quenching and remarkable reduction in 1O2 generation. These strategies developed for organic photosensitizers motivated us to improve the 1O2-generation efficiency of Au NC photosensitizers by doping with another metal and exploiting AIE. Recently, extensive studies have been conducted on enhancing the luminescence of Au NCs by silver doping and AIE.37–41 Moreover, silver nanomaterials are

ACS Paragon Plus Environment

3

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 27

widely used as antimicrobial agents.42-45 However, to the best of our knowledge, there are no reports on the effects of silver doping and AIE on the 1O2-generation efficiency of Au NCs. Herein, we report the effects of silver doping and AIE on the 1O2-generation capability of glutathione-protected Au NCs (GS-Au NCs). We found that doping GS-Au NCs with silver (i.e., fabricating bimetallic AuAg NCs) and their aggregation to achieve AIE could enhance their luminescence as well as their 1O2-generation capability. Moreover, we propose a strategy to improve the 1O2-generation capability of AuAg NCs by incorporating them into a chitosan nanogel

(AuAg

NCs@nanogel)

via

self-assembly-induced

emission

(SAIE)

effects.

The difference between the two strategies, SAIE and AIE, is as follows: SAIE is due to the spontaneous and reversible organization of cationic polymer molecular units by anionic metal NCs into polymer nanogels via electrostatic interactions.

In contrast, AIE is due to the

aggregation of emissive thiolate-M(I) complexes on the surfaces of metal NC core, which show a higher photoluminescence efficiency. Finally, the photosensitizers based on the AuAg NCs@nanogel were successfully used for antimicrobial-PDT (a-PDT) against bacteria.

EXPERIMENTAL SECTION Materials.

All

Tetrachloroauric(III)

chemicals acid

were

used

(HAuCl4·3H2O,

as

received

99.99%),

without

further

Cu(NO3)·3H2O

purification.

(99.9%),

2,9,10-

anthracenediyl-bis(methylene)dimalonic acid (ABDA, >99%), glutathione (GSH, 98%), dimethylformamide (DMF, 99.5%), heavy water (D2O, 99.9%), acrylamide (99%), N,N’methylenebis-(acrylamide) (97.0%), glycerol (99.0%), N,N,N’,N’-tetramethyl-ethylenediamine (TEMED,99.0%), ammonium peroxodisulfate (APS, 99%), rhodamine B, 1 M tris-HCl (pH 8.8), 1 mol/L HCl, and 1 mol/L NaOH were purchased from Wako Pure Chemical Industries

ACS Paragon Plus Environment

4

Page 5 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Ltd., Japan. Sodium borohydride (NaBH4, 99.99%) and Pt(NH3)4Cl2 (98%) were purchased from Sigma-Aldrich, USA. Tris(hydroxymethyl)aminomethane (TRIS) was purchased from SERVA, Germany, and glycine was purchased from Peptide Institute, Japan. Nanopure water (resistivity 18.2 MΩ·cm) was obtained from a pure de-ionized (DI) water system (Barnstead NANO, Thermo Scientific, USA). Preparation of Au NCs and Bimetallic NCs. GS-Au NCs that show AIE were prepared according to a previously published procedure.37 Aqueous solutions of HAuCl4 (20 mM, 0.50 mL) and GSH (100 mM, 0.15 mL) were mixed with 4.35 mL of ultrapure water at 25 °C. The reaction mixture was heated to 70 °C under gentle stirring (500 rpm) for 24 h in air. The GS-Au NCs were separated by ultrafiltration using molecular weight cut-off membranes (MWCO: 3000 Da), and the separated product was diluted with pure water (or D2O). The final solution was stored in a refrigerator at 4 °C for further use. The bimetallic GS-AuAg NCs were synthesized under similar conditions, except a mixture of AgNO3: HAuCl4 (20 mM, 0.50 mL) and AgNO3 (20 mM, 0.50 mL) was used at an Ag:Au molar ratio of 0.2:1 for the synthesis. We also synthesized bimetallic GS-PtAu NCs at a Pt:Au molar ratio of 0.2:1 and GS-CuAu NCs at a Cu:Au molar ratio of 0.2:1 under similar conditions. Preparation of AuAg NCs@nanogel. The GS-AuAg NC-incorporated chitosan nanogel (AuAg NCs@nanogel) was prepared according to a previously published procedure.46 The aqueous suspension of the as-prepared GS-AuAg NCs (2.0 mL) was diluted with 2.0 mL of water (or D2O) under gentle stirring (500 rpm) at 25 °C. Then, 1 mL of a chitosan solution (5 mg/mL) was added to the GS-AuAg NC suspension under gentle stirring (500 rpm) at 25 °C. The pH of the resultant mixture was adjusted to 6.5 through dropwise addition of 1 M NaOH followed by gentle stirring (500 rpm) for 30 min at 25 °C.

ACS Paragon Plus Environment

5

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 27

Detection of 1O2 Generation. Singlet oxygen generation under the excitation of white lightemitting diode (LED) (SPF-D2, Shodensha, Japan) was monitored by the chemical oxidation of ABDA in an aqueous solution.47 ABDA can react irreversibly with 1O2, leading to a decrease in the ABDA absorption at 378 nm (Figure S1). Thus, 1.8 mL of a D2O suspension of the NCs (absorbance, 0.1 at 335 nm) was mixed with 0.2 mL of 0.5 mM ABDA in DMF and the mixture was irradiated with the LED light. The absorbance of the solution at 378 nm was monitored at 10 min intervals by recording their UV-vis spectra. Instrumentation and Characterization. Transmission electron microscopic (TEM) images of the nanoparticles were captured at 120 kV on a JEOL 1400 microscope. UV-Vis absorption spectroscopy and steady-state fluorescence spectroscopy were conducted using JASCO V-670 and FP-6300 spectrometers, respectively. All the measurements were performed at room temperature using 1-cm-path length cuvettes. Fluorescence lifetimes were determined by timecorrelated single photon counting using an LED at 340 nm with a Quantaurus-Tau fluorescence lifetime measurement system (C11367-03, Hamamatsu Photonics Co.). An inductively coupled plasma mass spectrometer (ICP-MS, Agilent Technologies, 7900) was used to determine the Ag and Au concentrations of the aqueous sample solution. X-ray photoelectron spectroscopy (XPS) was carried out on a VG ESCALAB 220i-XL spectrometer. Dynamic light scattering (DLS) was performed on a Malvern Zetasizer Nano ZS instrument equipped with a He-Ne laser operating at 632.8 nm and a scattering detector at 173°. Polyacrylamide gel electrophoresis (PAGE) was carried out on a five-lane electrophoresis system (Mini-Protean, BIO-RAD, USA). The contents of the acrylamide monomer and cross-linker in the resolving gels were 47 and 3 wt% [acrylamide/bis(acrylamide)], respectively. The eluting buffer contained 1.4 M Tris-HCl (pH ~

ACS Paragon Plus Environment

6

Page 7 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

8.4). The as-synthesized NCs were dissolved in 5% (v/v) water, after which 0.3 mL of the sample was loaded and eluted at 150 V for 3 h.

Antimicrobial Effects of AuAg NCs@nanogels under White LED Irradiation. AuAg NCs@nanogels were dispersed in a suspension of Streptococcus mutans (ATCC 35668) and dispensed into 48-well plates. Before incubation, the suspension was irradiated with white LED for 1 min. After incubation at 37 °C under anaerobic conditions for 24 h, the bacterial turbidity was determined using a turbidimeter (CO7500 Colourwave, Funakoshi Co., Ltd, Tokyo, Japan) at 590 nm. Statistical analysis was performed by Scheffe’s test, and ܲ values < 0.05 were considered statistically significant. All statistical analyses were performed using a software package (SPSS 11.0, IBM Corporation, Armonk, NY, USA). Samples of Streptococcus mutans were stained using the LIVE/DEAD® BacLight™ Bacterial Viability Kit (Thermo Fisher Scientific, Waltham, MA, USA) (henceforth referred to as the LIVE/DEAD kit), following the manufacturer’s instructions. Stained samples of Streptococcus mutans in the presence / absence of AuAg NCs@nanogels (the concentration of gold, 50 µg/mL) were examined after irradiation with a white LED for 1 min using confocal laser scanning microscopy (Biorevo BZ-9000, KeyenceCo., Osaka, Japan).

RESULTS AND DISCUSSION Effect of Metal Doping on Au NCs. The UV-vis spectrum of GS-Au NCs shows a continuous absorbance with no plasmonic absorbance (Figure 1a), and the emission spectrum shows a red fluorescence at 610 nm when excited at 335 nm (Figure 1b). These characteristics are consistent with those of luminescent Au(0)@Au(I)–thiolate NCs reported in literature.37 According to Xie’s

ACS Paragon Plus Environment

7

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 27

report, the fluorescence is attributed to AIE from the Au(I)–thiolate complexes condensed into a compact shell on the Au(0) core, resulting in phosphorescence via the metal-centered triplet states.37,38

Figure 1. (a) UV-vis spectra and (b) fluorescence spectra (λexcitation = 335 nm) of GS-Au NCs, AuAg NCs, AuCu NCs, and AuPt NCs.

Silver doping increases the fluorescence intensity of Au NCs.48–50 Guével et al. reported that a small amount of Ag doped into GS-Au NCs ([Ag]/[Au] ~0.02) is enough to achieve a strong emission, with ~ 5-fold enhancement of the emission intensity compared to that of GS-Au NCs.49 In this study, we prepared Ag-doped GS-Au NCs with a small [Ag]/[Au] ratio of 0.07, as determined by ICP-MS measurements. A high content of the Au(I)–thiolate complexes in the GS-AuAg NCs was confirmed by XPS. The Au 4f spectrum could be deconvoluted into Au(I) and Au(0) components with binding energies of 84.6 and 84.0 eV, respectively. The Au(I) content was estimated to be ~55% of the total Au content in the AuAg NCs (Figure S2). A new shoulder peak appeared at ~400 nm in the spectrum of GS-AuAg NCs (Figure 1a). From TEM

ACS Paragon Plus Environment

8

Page 9 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

image (Figure 2a) and DLS result (Figure 2b), the size of the GS-AuAg NCs was determined to be ~2 nm. Gel electrophoresis of the NCs with 5 bands showed no difference between the GSAuAg NCs and GS-Au NCs (Figure 2c). These results suggest a change in electronic state of the GS-Au NCs due to Ag doping with almost no change in the size of the GS-AuAg NCs.

Figure 2. (a) TEM image and (b) DLS size distribution profile of GS-AuAg NCs. (c) Gel electrophoresis of GS-Au NCs and GS-AuAg NCs. (d) DLS size distribution profile of AuAg NCs@nanogel.

The GS-AuAg NCs are more fluorescent than the GS-Au NCs (excitation at 335 nm and emission at 605 nm) (Figure 1b), and they exhibit a higher quantum yield than the GS-Au NCs

ACS Paragon Plus Environment

9

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 27

(7.2% for GS-AuAg and 1.2% for GS-Au NCs), as determined by employing rhodamine B as a reference. The stronger fluorescence of GS-AuAg NCs originates from the Au(I)/Ag(I)–thiolate motifs on the Au NC core, which could generate strong luminescence via AIE.50 Both GS-Au NCs and GS-AuAg NCs show biexponential decay of their luminescence, and their lifetimes are listed in Table 1. A short component, τ1 (0.25 µs), and a long component, τ2 (1.70 µs), are observed for the GS-Au NCs, whereas Ag doping of the Au NCs caused a notable increase in the fluorescence lifetime: τ1 = 0.41 µs and τ2 = 1.86 µs (Figure 3a). Based on the large Stokes shift (>200 nm) and the long-lifetime components in their excited-state decay, the luminescence is attributed to the phosphorescence resulting from the ligand-to-metal charge transfer (LMCT) or ligand-to-metal-metal charge transfer (LMMCT).37,38

Figure 3. (a) Fluorescence decay curves of Au NCs, AuAg NCs, and AuAg NCs@nanogel; the decay curves were obtained for the emission at 605 nm under the excitation wavelength of 335 nm. (b) Fluorescence spectra of Au NCs, AuAg NCs, and AuAg NCs@nanogel obtained with 335 nm excitation. Table 1. Parameters extracted from the fluorescence decay curves

ACS Paragon Plus Environment

10

Page 11 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Sample

λem /nm

*ττ / µs

τ1 / µs (**a1)

τ2 / µs (**a2)

Au NCs

610

1.33

0.25(0.70)

1.70(0.30)

AuAg NCs

610

1.51

0.41(0.59)

1.86(0.41)

AuCu NCs

610

0.61

0.12(0.84)

0.94(0.16)

AuPt NC

610

1.79

0.39(0.76)

2.49(0.24)

610

2.48

0.56(0.67)

3.18(0.33)

AuAg NC@nanogel

*τ = (τ12A1 + τ22A2) / (τ1A1 + τ2A2) (A: Amplitude) **a1 = A1/ (A1+A2), a2 = A2/ (A1+A2) Further, we examined the effects of doping other metals such as Cu and Pt into the Au NCs (GS-AuCu NCs and GS-AuPt NCs). The corresponding UV-vis spectra and fluorescence spectra are shown in Figure 1, together with those of GS-Au NCs. Enhanced luminescence could not be achieved for GS-AuCu and GS-AuPt NCs. Therefore, we focused our study on the GS-AuAg NCs and the effect of their incorporation into chitosan nanogels.

Effect of Incorporating GS-AuAg NC into a Chitosan Nanogel. Self-assembled chitosan nanogels can be applied in medical applications. Recently, Goswami et al. synthesized highly luminescent nanogels by the self-assembly of anionic GS-Au NCs and cationic chitosan through electrostatic interactions to obtain AIE-type luminescent GS-Au NCs in the nanogel.46 In the present study, we fabricated AIE-type luminescent GS-AuAg NCs in a chitosan nanogel (AuAg NCs@nanogel) in two steps. First, GS-AuAg NCs were prepared, and then, chitosan was introduced to induce the SAIE effect. The size of the AuAg NCs@nanogel was determined to be ~30 nm by DLS analysis (Figure 2d), while the size of the GS-AuAg NCs was ~2 nm. The UVvis spectrum of the AuAg NCs@nanogel is consistent with that of GS-AuAg NCs (Figure S3), which indicates that the GS-AuAg NCs did not degrade upon complexing with chitosan. The

ACS Paragon Plus Environment

11

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 12 of 27

AuAg NCs@nanogel exhibited a much stronger luminescence than that of the GS-AuAg NCs (Figure 4b), indicating the amplification of luminescence by the SAIE effect. In addition, the AuAg NCs@nanogel exhibited a higher quantum yield than that of the GS-AuAg NCs (quantum yield = 24% for nanogel-incorporated GS-AuAg NCs, 7.2% for GS-AuAg NCs, and 1.2% for GS-Au NCs) as determined using rhodamine B as the reference. Moreover, the AuAg NCs@nanogel showed a notable increase in the fluorescence lifetime (Figure 3): τ1 = 0.56 µs and τ2 = 3.18 µs (Table 1). The enhanced photoluminescence and the notable increase in the fluorescence lifetime of the nanogel can be explained by the inhibition of nonradiative decay pathways through spatial confinement in the nanogel-impregnated NCs.46

The strong

coordination between the positively charged amine groups of chitosan and the negatively charged carboxylic groups of GSH is formed within the confined space of the nanogel. 46 The strong coordinating bonds could restrict the relaxation channels of the excited M(0)@M(I)-SG NCs (M = Au or Ag) by locking the thiolate ligands in place, leading to fewer nonradiative decay pathways. The inhibition of nonradiative decay pathways in AuAg NCs@nanogel not only affords the high luminescence of the NCs, but also enables enhanced 1O2 generation.

Enhanced 1O2 generation of Au NCs by Ag doping. Efficient 1O2 generation is a prerequisite for photosensitizers used in PDT. The 1O2-generation efficiencies of GS-Au NCs, GS-AuAg NCs, GS-AuPt NCs, and GS-AuCu NCs under white LED irradiation were evaluated by a chemical method using ABDA. ABDA is selectively oxidized by 1O2 to the corresponding endoperoxide, leading to a decrease in the ABDA absorption. Figure 4a shows the decrease in the ABDA absorbance at 378 nm as a function of the irradiation time in the presence of GS-AuAg NCs under white-light irradiation, owing to the degradation of ABDA by the generated 1O2 in solution.

ACS Paragon Plus Environment

12

Page 13 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Under the same conditions, irradiation of ABDA alone as the control does not lead to an obvious change in its absorbance (Figure S4). The photo-oxidation rate of ABDA, i.e., the decrease in the ABDA absorbance under light irradiation (∆Abs), is larger for the GS-AuAg NCs than for the GS-Au NCs, as shown in Figure 4b. The photo-oxidation rate of ABDA in the presence of NCs is an indicator of the 1O2-generation capability of the NCs under light excitation. The observed result therefore indicates that the 1O2-generation capability of the GS-AuAg NCs is higher than that of the GS-Au NCs. Note that we did not observe any enhancement in the 1O2-generation capabilities of GS-AuPt NCs and GS-AuCu NCs as compared with that of GS-Au NCs (Figure S5).

Figure 4. (a) UV-vis spectra of ABDA in D2O and (b) ABDA absorbance at 378 nm (∆Abs) as a function of the irradiation time in the presence of AuAg NCs under white LED irradiation.

The important role of M(I)–thiolate ligand (SR) shell (M = Au or Ag) in luminescence enhancement has been well documented;37–41 however, its effect on 1O2 generation by NCs is

ACS Paragon Plus Environment

13

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 14 of 27

little known. To examine the role of the M(I)–SR ligand shell in 1O2 generation, we added a reducing agent, NaBH4, into the aqueous suspensions of GS-Au NC and GS-AuAg NC. After that, no luminescent reddish-brown dispersion of AuAg NC was obtained, as shown in Figures 5a–d. This is because, the strong reducing agent, NaBH4, decomposed the Au(I)–thiolate complexes into NCs.37 The 1O2-generation efficiencies of both the reduced GS-Au NCs and GSAuAg NCs dropped to ~10% as compared with those before the reduction (Figure 5e), because the content of the Au(I)–thiolate complexes in the resulting GS-AuAg NCs (or GS-Au NCs) became too low for 1O2 generation. This indicates that the M(I)–SR shell on the GS-AuAg NCs (or GS-Au NCs) plays an important role in 1O2 generation as well as luminescence enhancement, and the M(I)–SR shell of the NCs is responsible for the generation of the T1 state of the NCs which leads to 1O2 generation.

Figure 5. Digital photos of (a) AuAg NCs and (b) reduced AuAg NCs under ambient light. Digital photos of (c) AuAg NCs and (d) reduced AuAg NCs under UV light (365 nm). (e) 1O2generation efficiency (Ef) of the NCs normalized by the Ef of the Au NCs. The Ef value is estimated as, kobs/∆A400-800 nm, where kobs is the photo-oxidation rate constant of ABDA in the presence of NCs during light irradiation (i.e., the slope of the curve in Figure 4b) and ∆A400-800 nm

ACS Paragon Plus Environment

14

Page 15 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

is the total integrated absorbance between 400 and 800 nm in the UV-vis spectra of the Au NCs or AuAg NCs.

Enhanced 1O2 generation of AuAg NCs by the SAIE effect. The photo-oxidation rate of ABDA increased significantly when the AuAg NCs@nanogel was used as the photosensitizer under the same experimental conditions, because of the SAIE effect (Figure 4b). The estimated photo-oxidation rate constants (kobs) of ABDA during 30 min for GS-Au NCs, GS-AuAg NCs, and AuAg NCs@nanogel are 0.0034, 0.0046, and 0.0123 s-1, respectively. The photo-oxidation rate of ABDA in the presence of AuAg NCs@nanogel is higher than that in the presence of GSAuAg NCs. These results indicate that the 1O2-generation capability of AuAg NCs@nanogel is ~4.0 times higher than that of the GS-AuAg NCs. The overall trend is consistent with the increase in the average fluorescence lifetimes (1.3, 1.7, and 3.4 µs for GS-Au NCs, GS-AuAg NCs, and AuAg NCs@nanogel, respectively). These results further suggest that the increase in the 1O2-generation capability is primarily due to the inhibition of the nonradiative decay pathways, which also results in an increase in the luminescent quantum yield (1.2, 7.2, and 24% for GS-Au NCs, GS-AuAg NCs, and AuAg NCs@nanogel, respectively). In this study, we examined poly-dispersed AgAu nanoclusters, as shown in the gel electrophoresis results in Figure 2c. However, the 1O2-generation capability of AuAg NCs would depend on the size/composition of the AgAu NCs with atomic levels. In the future, the size/composition effect of the AgAu NCs on the 1O2-generation capability should be clarified using AgAu NCs with an atomically precise size and composition.

ACS Paragon Plus Environment

15

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 16 of 27

PDT using GS-AuAg NC-incorporated chitosan nanogels. The aforementioned results revealed that the AuAg NCs@nanogel has the highest 1O2-generation capability under white LED irradiation among the metal NCs examined here. Therefore, we applied the AuAg NCs@nanogel for a-PDT against oral bacterial cells in dental application. The a-PDT activity on Streptococcus mutans under white LED irradiation for a short period of 1 min after 24 h of incubation was evaluated by a turbidity assay method (Figure 6a). This method measures the turbidity directly associated with the growth over time of a bacterial population in the suspension. A low turbidity indicates a small amount of Streptococcus mutans in the suspension.29, 51

A suspension that was not irradiated with the LED was used as a control.

A small decrease in turbidity was observed after 24 h in the presence of the nanogel (the concentration of gold, 5 µg/mL) even without LED irradiation, indicating the antimicrobial effect of chitosan itself without the LED light. However, under white LED irradiation in the presence of the nanogel (the concentration of gold, 50 µg/mL), a dramatic decrease in the turbidity of the bacterial suspensions occurred, indicating the suppression of bacterial growth (i.e. antibacterial activity). It is likely that 1O2 generated by photoexcited AuAgNCs@nanogels suppressed S. mutans growth. Thus, this in turn indicates the a-PDT activity of the nanogel on Streptococcus mutans under white LED irradiation for only 1 min. The turbidity assay method is rapid, low cost, and nondestructive; however, it measures live as well as dead bacterial cell debris. To examine the fraction of dead bacterial cells, Streptococcus mutans (5.5×107 CFU/mL) was treated with the LIVE/DEAD kit dyes.29 The LIVE/DEAD kit is widely used for the enumeration of bacteria and provides an indication of the fraction of live or dead cells.29 In the absence of the AuAgNCs@nanogels (control), the LIVE/DEAD staining observations revealed that all samples after white LED irradiation

ACS Paragon Plus Environment

16

Page 17 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

consistently exhibited green fluorescence (live bacteria) (Figure 6b). In contrast, dead bacteria after white LED irradiation, as shown by the red fluorescence, are predominantly observed in the presence of the nanogel (Figure 6c). The LIVE/DEAD test thus supports the a-PDT activity of AuAgNCs@nanogels on Streptococcus mutans under white LED irradiation.

Figure 6. (a)Antimicrobial effects of AuAg NCs@nanogel at different Au concentrations on Streptococcus mutans (ATCC 35668) under white LED irradiation for 1 min after 24 h incubation (n = 5, mean ± standard deviation). *, P < 0.05 vs. other groups. Fluorescence

ACS Paragon Plus Environment

17

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 18 of 27

examination of the labeled Streptococcus mutans with the LIVE/DEAD kit after white LED irradiation for 1 min (b) in the absence of AuAg NCs@nanogel (control) and (c) in the presence of AuAg NCs@nanogel (the concentration of gold, 50 µg/mL).

CONCLUSION We proposed the exploitation of three efficient strategies to improve the 1O2-generation efficiency of GS-Au NCs: (i) Ag doping (i.e., formation of bimetallic AuAg NCs), (ii) AIE effect of the Au(I)–thiolate complex, and (iii) SAIE effect of the polymer nanogel. The increase in the 1

O2-generation efficiency of the NCs by these effects is accompanied by an increase in the

average fluorescence lifetime, indicating that the inhibition of nonradiative decay pathways enables the photo-excited NCs to undergo ISC from S1 to T1, and subsequently, the energy is transferred to 3O2 for 1O2 generation. Further, we examined the effects of doping different metal species such as Ag, Cu, and Pt into the Au NCs. Ag doping was found to be the most effective in improving the 1O2-generation capability of the GS-Au NCs. The AIE effect on the 1O2generation capability of the NCs was examined by the reductive decomposition of the Au(I)– thiolate complex into NCs. The chemical reduction of the Au(I)–thiolate complexes on the AuAg NCs (Au NCs) significantly decreased the 1O2-generation efficiency. The important role of the M(I)–SR ligand shell (M = Au or Ag) in 1O2 generation is suggested, since the M(I)–SR shell of the NCs is responsible for the generation of the T1 state of the NCs. Finally, the AuAg NCs@nanogel-based photosensitizers exhibited a significant a-PDT effect on Streptococcus mutans under white LED irradiation for only 1 min.

ACS Paragon Plus Environment

18

Page 19 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

The Supporting Information is available free of charge on the ACS Publications website at DOI:. Oxidation scheme of ABDA, XPS spectrum of AuAg NCs, and UV-vis spectra of AuAg NCs and AuAg NCs@nanogel, UV-vis spectra of ABDA under LED irradiation, ABDA absorbance change in the presence of Au NCs, AuAg NCs, AuCu NCs, and AuPt NCs under LED irradiation (PDF).

ACKNOWLEDGMENT This work was supported by the JSPS KAKENHI (Grant No. 15H03520, 15H03526, and 26107719) and the MEXT-Supported Program for the Strategic Research Foundation at Private Universities. This work was also financially supported in part by the Private University Research Branding Project: Matching Fund Subsidy from the Ministry of Education, Culture, Sports, Science and Technology (MEXT), Japan (2016–2020).

REFERENCES (1) Jin, R.; Zeng, C.; Zhou, M.; Chen, Y. Atomically Precise Colloidal Metal Nanoclusters and Nanoparticles: Fundamentals and Opportunities, Chem. Rev. 2016, 116, 10346–10413. (2) Goswami, N.; Yao, Q.; Chen, T.; Xie, J. Mechanistic Exploration and Controlled Synthesis of Precise Thiolate-gold Nanoclusters, Coordin. Chem. Rev. 2016, 329, 1-15. (3) Kurashige, W.; Niihori, Y.; Sharma, S.; Negishi, Y. Precise Synthesis, Functionalization and Application of Thiolate-protected Gold Clusters, Coordin. Chem. Rev. 2016, 320–321, 238250.

ACS Paragon Plus Environment

19

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 20 of 27

(4) Chakraborty, I.; Pradeep, T. Atomically Precise Clusters of Noble Metals: Emerging Link between Atoms and Nanoparticles, Chem. Rev. 2017, 117, 8208–8271. (5) Kawasaki, H.; Hamaguchi, K.; Osaka, I.; Arakawa, R. ph-Dependent Synthesis of PepsinMediated Gold Nanoclusters with Blue Green and Red Fluorescent Emission, Adv. Funct. Mater. 2011, 21, 3508–3515. (6) Yoshimoto, J.; Sangsuwan, A.; Osaka, I.; Yamashita, K.; Iwasaki, Y.; Inada, M.; Arakawa, R.; Kawasaki, H. Optical Properties of 2-Methacryloyloxyethyl Phosphorylcholine-Protected Au4 Nanoclusters and Their Fluorescence Sensing of C-Reactive Protein, J. Phys. Chem. C 2015, 119, 14319–14325. (7) Negishi, Y.; Nakazaki, T.; Malola, S.; Takano, S.; Niihori, Y.; Kurashige, W.; Yamazoe, S.; Tsukuda, T.; Häkkinen, H. A Critical Size for Emergence of Nonbulk Electronic and Geometric Structures in Dodecanethiolate-Protected Au Clusters, J. Am. Chem. Soc. 2015, 137, 1206–1212. (8) Zhou, M.; Zeng, C.; Chen, Y.; Zhao, S.; Sfeir, M. Y.; Zhu, M.; Jin, R. Evolution from the Plasmon to Exciton State in Ligand-protected Atomically Precise Gold Nanoparticles, Nat Commun. 2016, 7, 13240. (9) Yao, Q.; Feng, Y.; Fung, V.; Yu, Y.; Jiang, D.; Yang, J.; Xie, J. Precise Control of Alloying Sites of Bimetallic Nanoclusters via Surface Motif Exchange Reaction, Nat Commun. 2017, 8, 1555. (10)

Dimuthu K. L; Weerawardene, M.; Aikens, C. M. Origin of Photoluminescence of

Ag25(SR)18–Nanoparticles: Ligand and Doping Effect, J. Phys. Chem. C 2018, 122, 2440– 2447. (11)

Zhaoa, J.; Jin, R. Heterogeneous Catalysis by Gold and Gold-based Bimetal

ACS Paragon Plus Environment

20

Page 21 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

Nanoclusters, Nano Today, 2018, 18, 86-102. (12)

Song, X. R.; Goswami, N.; Yang, H. H.; Xie, J. Functionalization of Metal Nanoclusters for Biomedical Applications, Analyst 2016, 141, 3126-3140.

(13)

Zheng, Y.; Lai, L.; Liu, W.; Jiang, H.; Wan, X. Recent Advances in Biomedical

Applications of Fluorescent Gold Nanoclusters, Adv. Colloid Interface Sci. 2017, 242, 1-16. (14)

Shang, L.; Ulrich Nienhaus, G. Research Update: Interfacing Ultrasmall Metal

Nanoclusters with Biological Systems, APL Materials 2017, 5, 053101. (15) Zheng, K.; Setyawati, M. I.; Leong, D. T.; Xie, J. Antimicrobial Gold Nanoclusters, ACS Nano 2017, 11, 6904–6910. (16) Xie, Y.; Liu,Y.; Yang,Y.; Liu,Y.; Hu, F.; Zhu, K.; Jiang, X. Gold Nanoclusters for Targeting

MRSA

in

Vivo,

Angew.

Chem.

Int.

Ed.

Chemie.

2018,

DOI:

10.1002/anie.201712878. (17) Shibu, E. S.; Sugino, S.; Ono, K.; Saito, H.; Nishioka, A.; Yamamura, S.; Sawada, M.; Nosaka, Y.; Biju, V.

Singlet-oxygen Sensitizing Near-infrared-fluorescent Multimodal

Nanoparticles, Angew. Chem. Int. Ed. 2013, 52, 10559–10563. (18) Tao, Y.; Li, M.; Ren, J.; Qu, X. Metal Nanoclusters: Novel Probes for Diagnostic and Therapeutic Applications, Chem. Soc. Rev. 2015, 44, 8636-8663. (19) He, F.; Yang, G.; Yang, P.; Yu, Y.; Lv, R. ; Li, C. ; Dai, Y.; Gai, S.; Lin, J. A New Single 808 nm NIR Light-Induced Imaging-Guided Multifunctional Cancer Therapy Platform, Adv. Funct. Mater. 2015, 25, 3966–3976.

ACS Paragon Plus Environment

21

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 22 of 27

(20) Lv, R.; Yang, P.; He, F.; Gai, S. ; Yang, G. ; Dai, Y.; Hou, Z.; Lin, J. An Imaging-Guided Platform

for

Synergistic

Photodynamic/Photothermal/Chemo-therapy

with

pH/temperature-responsive Drug Release, Biomaterials 2015, 63, 115-127. (21) Yang, D.; Yang, G.; Gai, S.; He, F.; An, G.; Dai, Y.; Lva, R.; Yang, P. Au25 Cluster Functionalized

Metal–organic

Nanostructures

for

Magnetically

Targeted

Photodynamic/Photothermal Therapy Triggered by Single Wavelength 808 nm Nearinfrared Light, Nanoscale 2015, 7, 19568-19578. (22) Lei, Q.; Hu, J.-J.; Rong, L.; Cheng, H.; Sun, Y.-X.; Zhang, X.-Z. Gold Nanocluster Decorated Polypeptide/DNA Complexes for NIR Light and Redox Dual-Responsive Gene Transfection, Molecules 2016, 21, 1103. (23) Yang, D.; Gulzar, A.; Yang, G.; Gai, S.; He, F.; Dai, Y.; Zhong, C.; Yang, P. Au Nanoclusters Sensitized Black TiO2−x Nanotubes for Enhanced Photodynamic Therapy Driven by Near-Infrared Light, small 2017, 13, 1703007. (24) Ho-Wu, R.; Yau, S. H.; Goodson III, T. Efficient Singlet Oxygen Generation in Metal Nanoclusters for Two-Photon Photodynamic Therapy Applications, J. Phys. Chem. B, 2017, 121,10073–10080. (25) Cui, H.; Hu, D.; Zhang, J.; Gao, G.; Chen, Z.; Li, W.; Gong, P.; Sheng, Z.; Cai, L. Gold Nanoclusters–Indocyanine Green Nanoprobes for Synchronous Cancer Imaging, Treatment, and Real-Time Monitoring Based on Fluorescence Resonance Energy Transfer, ACS Appl. Mater. Interfaces 2017, 9, 25114–25127.

ACS Paragon Plus Environment

22

Page 23 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

(26) Yu, C.; Li, G.; Kumar, S.; Kawasaki, H.; Jin, R. Stable Au25 (SR)

18/TiO2

Composite

Nanostructure with Enhanced Visible Light Photocatalytic Activity, J. Phys. Chem. Lett. 2013, 4, 2847–2852. (27) Kawasaki, H.; Kumar, S.; Li, G.; Zeng, C.; Kauffman, D. R.; Yoshimoto, J.; Iwasaki, Y.; Jin, R. Generation of Singlet Oxygen by Photoexcited Au25 (SR)

18 clusters,

Chem. Mater.

2014, 26, 2777–2788. (28) Yamamoto, M.; Osaka, I.; Yamashita, K.; Hasegawa, H.; Arakawa, R.; Kawasaki, H. Effects of Ligand Species and Cluster Size of Biomolecule-protected Au Nanoclusters on Efficiency of Singlet-oxygen Generation, J. Lumin. 2016, 180, 315-320. (29) Miyata, S.; Miyaji, H.; Kawasaki, H.; Yamamoto, M.; Nishida, E.; Shitomi, K.; Tanaka, S.; Tanaka, H.; Iizuka, T. et al. Antimicrobial Photodynamic Activity and Cytocompatibility of Au25(Capt)18 Clusters Photoexcited by Blue LED Light irradiation, Int. J. Nanomed. 2017, 12, 2703-2716. (30) Yamamoto, M.; Shitomi, K.; Miyata, S.; Miyaji, H.; Aota, H.; Kawasaki, H. Bovine Serum Albumin-capped Gold Nanoclusters Conjugating with Methylene Blue for Efficient 1O2 Generation via Energy Transfer, J. Colloid Interface Sci. 2018, 510, 221-227. (31) Zhou, Z.; Song, J.; Nie, L.; Chen, X. Reactive Oxygen Species Generating Systems Meeting Challenges of Photodynamic Cancer Therapy. Chem. Soc. Rev. 2016, 45, 6597-6626. (32) Li, X.; Lee, S.; Yoon, J. Supramolecular Photosensitizers Rejuvenate Photodynamic Therapy, Chem. Soc. Rev. 2018, 47, 1174-1188.

ACS Paragon Plus Environment

23

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 24 of 27

(33) Zhao, J.; Wu, W.; Sun, J; Guo, S. Triplet Photosensitizers: from Molecular Design to Applications. Chem. Soc. Rev. 2013, 42, 5323–5351. (34) Hu,Q.; Gao, M.; Feng, G.; Hu,Q. Mitochondria-Targeted Cancer Therapy Using a Light-Up Probe with Aggregation-Induced-Emission Characteristic, Angew. Chem. Int. Ed. Chemie. 2014, 53, 14225–14229. (35) Xu, S.;Yuan, Y.; Cai, X.; Zhang, C. J.; Hu, F.; Liang, J.; Zhang, G.; Zhang, D.; Liu, B. Tuning the Singlet-triplet Energy Gap: a Unique Approach to Efficient Photosensitizers with Aggregation-Induced Emission (AIE) characteristics, Chem. Sci. 2015, 6, 5824-5830. (36) Liu, J.; Jin, C.; Yuan, B.; Liu, X.; Chen, Y.; Ji, L.; Chao, H. Selectively Lighting Up Twophoton Photodynamic Activity in Mitochondria with AIE-active Iridium(III) Complexes, Chem. Commun. 2017, 53, 2052-2055. (37) Luo, Z.; Yuan, X.; Yu, Y.; Zhang, Q.; Leong, D.T.; Lee, J. Y.; Xie, J.

From the

Aggregation-Induced Emission of Au (I)-Thiolate Complexes to Ultra-Bright Au (0)@ Au (I)-Thiolate Core-Shell Nanoclusters, J. Am. Chem. Soc. 2012, 134, 16662–16670. (38) Goswami, N.;Yao, Q.; Luo, Z.;Li, J.; Chen, T.; Xie, J. Luminescent Metal Nanoclusters with Aggregation-Induced Emission, J. Phys. Chem. Lett. 2016, 7, 962−975. (39) Liu, J.; Wu, Z.; Tian,Y.; Li,Y.; Ai,L.; Li,T.; Zou, H.; Liu, Y.; Zhang, X.; Zhang, H.; Yang, B. Engineering the Self-Assembly Induced Emission of Cu Nanoclusters by Au(I) Doping, ACS Appl. Mater. Interfaces 2017, 9, 24899–24907.

ACS Paragon Plus Environment

24

Page 25 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

(40) Jin, S.; Liu, W.; Hu, D.; Zou, X.; Kang, X.; Du, W.; Chen, S.; Wei, S.; Wang, S.; Zhu, M. Aggregation-Induced Emission (AIE) in Ag−Au Bimetallic Nanocluster, Chem. Eur. J. 2018, DOI: 10.1002/chem.201800189. (41) Wanga, J.; Goswami, N.; Shu, T.; Su, L.; Zhang, Z. pH-Responsive Aggregation-Induced Emission of Au Nanoclusters and Crystallization of the Au(I)–thiolate Shell, Mater. Chem. Front. 2018, DOI: 10.1039/C7QM00609H. (42) Xiu, Z.; Zhang, Q.; Puppal, H. L.; Colvin,V. L.; Alvarez, P. J. J. Negligible Particle-Specific Antibacterial Activity of Silver Nanoparticles, Nano Lett. 2012, 12, 4271–4275. (43) Zheng, K.; Setyawati, M. I.; Lim, T-P.; Leong, D. T.; Xie, J. Antimicrobial Cluster Bombs: Silver Nanoclusters Packed with Daptomycin, ACS Nano 2016, 10, 7934-7942. (44) Zheng, K.; Setyawati,M. I.; Leong, D. T.; Xie, J. Antimicrobial Silver Nanomaterials, Coordin. Chem. Rev. 2018, 357, 1-17. (45) Tominaga, C.; Hikosou, D.; Osaka, I.; Kawasaki, H. Ag7(MBISA)6 Nanoclusters Conjugated with Quinacrine for FRET Enhanced Photodynamic Activity under Visible Light Irradiation, Acta Phys.-Chim. Sin. 2018, 34, 805–811. (46) Goswami, N.; Lin, F.; Liu,Y.; Leong, D. T.; Xie, J. Highly Luminescent Thiolated Gold Nanoclusters Impregnated in Nanogel, Chem. Mater. 2016, 28, 4009−4016. (47) Idris, N. M.; Gnanasammandhan, M. K.; Zhang, J.; Ho, P. C.; Mahendran, R.; Zhang, Y. In Vivo Photodynamic Therapy Using Upconversion Nanoparticles as Remote-controlled Nanotransducers, Nature Medicine 2012, 18, 1580–1585. (48) Ganguly, M.; Jana, J.; Pal, A.; Pal, T. Synergism of Gold and Silver Invites Enhanced Fluorescence for Practical Applications, RSC Adv. 2016, 6, 17683–17703.

ACS Paragon Plus Environment

25

The Journal of Physical Chemistry 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 26 of 27

(49) Guével, X. L.; Trouillet, V.; Spies, C.; Li, J.; Laaksonen, T.; Auerbach, D.; Jung, G.; Schneider, M. High Photostability and Enhanced Fluorescence of Gold Nanoclusters by Silver Doping, Nanoscale 2012, 4, 7624-7631. (50) Dou, X.; Yuan, X.; Yu, Y.; Luo, Z.; Yao, Q.; Leong, D. T.; Xie, J. Lighting Up Thiolated Au@Ag Nanoclusters via Aggregation-Induced Emission, Nanoscale 2014, 6, 157–161. (51) Pan, H.; Zhang, Y.; He, G. X.; Katagori, N.; Chen, H. A Comparison of Conventional Methods for the Quantification of Bacterial Cells after Exposure to Metal Oxide Nanoparticles, BMC Microbiology 2014, 14, 222.

ACS Paragon Plus Environment

26

Page 27 of 27 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

The Journal of Physical Chemistry

TOC Graphic

ACS Paragon Plus Environment