Article

Sequential Process Combination of Photocatalytic Oxidation and Dark Reduction for the Removal of Organic Pollutants and Cr(VI) using Ag/TiO

2

Yeoseon Choi, Min Seok Koo, Alok D. Bokare, Dong-hyo Kim, Detlef W. Bahnemann, and Wonyong Choi Environ. Sci. Technol., Just Accepted Manuscript • DOI: 10.1021/acs.est.6b06303 • Publication Date (Web): 09 Mar 2017 Downloaded from http://pubs.acs.org on March 10, 2017

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

Environmental Science & Technology is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 33

Environmental Science & Technology

1

Sequential Process Combination of Photocatalytic Oxidation and

2

Dark Reduction for the Removal of Organic Pollutants and Cr(VI)

3

using Ag/TiO2

4

Yeoseon Choi,† Min Seok Koo,† Alok D. Bokare,† Dong-hyo Kim,† Detlef W. Bahnemann,‡

5

and Wonyong Choi*,†

6 7 8



9 10 11



Department of Chemical Engineering and Division of Environmental Science and Engineering, Pohang University of Science and Technology (POSTECH), Pohang, Korea 37673 Laboratory “Photoactive Nanocomposite Materials” Saint-Petersburg State University, SaintPetersburg, Russia and “Photocatalysis and Nanotechnology”, Institut fuer Technische Chemie, Gottfried Wilhelm Leibniz Universitaet Hannover, Hannover, Germany

12 13

Submitted to

14

Environmental Science & Technology

15

(Revised)

16

17

*Corresponding author.

Phone: +82-54-279-2283

E-mail: [email protected]

18

1

ACS Paragon Plus Environment

Environmental Science & Technology

19

ABSTRACT

20

We investigated a sequential photocatalysis-dark reaction, wherein organic pollutants were

21

degraded on Ag/TiO2 under UV irradiation and the dark reduction of hexavalent chromium

22

(Cr(VI)) was subsequently followed. The photocatalytic oxidation of 4-chlorophenol (4-CP),

23

a test organic substrate, induced the generation of degradation intermediates and the storage

24

of electrons in Ag/TiO2 which were then utilized for reducing Cr(VI) in the post-irradiation

25

period. The dark reduction efficiency of Cr(VI) was much higher with Ag/TiO2 (87%),

26

compared with bare TiO2 (27%) and Pt/TiO2 (22%). The Cr(VI) removal by Ag/TiO2 (87%)

27

was contributed by adsorption (31%), chemical reduction by intermediates of 4-CP

28

degradation (26%), and reduction by electrons stored in Ag (30%). When formic acid, humic

29

acid or ethanol was used as an alternative organic substrate, the electron storage effect was

30

also observed. The post-irradiation removal of Cr(VI) on Ag/TiO2 continued for hours, which

31

is consistent with the observation that a residual potential persisted on the Ag/TiO2 electrode

32

in the dark whereas little residual potential was observed on bare TiO2 and Pt/TiO2 electrodes.

33

The stored electrons in Ag/TiO2 and their transfer to Cr(VI) were also indicated by the UV-

34

visible absorption spectral change. Moreover, the electrons stored in the pre-irradiated

35

Ag/TiO2 reacted with O2 with showing a sign of low-level OH radical generation in the dark

36

period.

37 38 39 40 41

Keywords: post-irradiation effect, advanced oxidation processes, aquatic pollutant transformation, hexavalent chromium, electron storage in silver

42

2

ACS Paragon Plus Environment

Page 2 of 33

Page 3 of 33

Environmental Science & Technology

43

INTRODUCTION

44

The deposition of noble metals on semiconductor surface is an efficient way to enhance the

45

photocatalytic activity by creating a Schottky barrier at the semiconductor-metal interface,

46

which helps separating the photo-excited electrons in the conduction band (CB) of

47

semiconductor into the metal nanoparticles (NPs).1-3 Such separation of charge pairs through

48

the Schottky barrier facilitates the subsequent charge transfer at the semiconductor interface

49

with enhancing the overall photocatalysis and reactive oxygen species (ROS) generation.4-6

50

Various noble metals such as Pt, Au, and Ag have been frequently immobilized on TiO2 and

51

other semiconductors to increase the efficiency of photocatalytic oxidation (PCO) of organic

52

pollutants.5-8

53

The photocatalytic activities of these TiO2-metal composites show different behaviors

54

depending on the kind of the loaded metal. Although the electron transfer from the

55

semiconductor CB to noble metal NPs is very fast (~10 ps),5 the electron entrapment and

56

subsequent interfacial transfer to the aqueous electrolytes critically depends on the type of

57

noble metal. While the capacitive nature of Au and Ag impedes the charge transfer of

58

entrapped electrons out of the metal surface, the existence of an ohmic contact in the case of

59

Pt and Pd renders quick discharge of electrons at the solid/liquid interface.9-11 Wood et al.10

60

demonstrated that the electron transfer from photocatalyst (ZnO) to aqueous electrolytes was

61

delayed by the presence of Ag NPs, which serve as an electron storage that keeps electrons

62

for a longer time. The transfer rate of accumulated electrons was much slower for Ag/ZnO

63

than Au/ZnO, whereas Pt/ZnO did not exhibit any electron storage property at all. To

64

compare the electron storage properties depending on the kind of noble metals, Takai and

65

Kamat11 investigated the electron storage and discharge properties of M/TiO2 (M = Ag, Au

66

and Pt) colloid in deaerated ethanol under UV irradiation and concluded that the electron 3

ACS Paragon Plus Environment

Environmental Science & Technology

67

storage is most efficient in Ag/TiO2 compared to Au/TiO2 and Pt/TiO2. To be specific, they

68

estimated that Ag/TiO2 can store up to 51 electrons per an Ag atom under UV irradiation.

69

The electrons accumulated on Ag metal can be in equilibrium with TiO2 where the electrons

70

can be trapped as Ti(III) or in the conduction band with an elevated Fermi level, which may

71

explain how an Ag atom can hold such many electrons. Although the actual number of

72

electrons that can be stored in M/TiO2 should depend on many parameters such as the size of

73

metal particles, the light irradiation intensity, and the kind of electron donors and solvents,

74

the large electron storage capacity in Ag may enable its application for post-irradiation

75

reactions. On the other hand, Pt/TiO2 has an ohmic contact at the interface and the

76

photogenerated electrons on Pt/TiO2 are rapidly transferred to the aqueous electrolyte with

77

little chance of electron accumulation on Pt. The much smaller interfacial charge transfer

78

resistance of Pt/TiO2 than Ag/TiO2 was also confirmed in a recent study.12

79

Ag/TiO2 has been employed for the photocatalytic removal of water contaminants on

80

the basis of various properties which include bactericidal properties of silver species,13-15

81

electron accumulation in silver metal to improve the reactivity of the photo-generated holes16

82

and the plasmonic effect of silver nanoparticles to utilize the visible light spectrum.17, 18

83

Although the electron storage properties of Ag/TiO2 have also been the subject of many

84

fundamental investigations,10, 19, 20 the possible utilization of these stored electrons for the

85

transformation of water pollutants has been largely unexplored. Gunawan et al.21 used pre-

86

irradiated Ag/TiO2 as antimicrobial agent, but they focused on the effect of Ag+ dissolution

87

by pre-irradiation not on the stored electrons in Ag NPs. This study aims to utilize and

88

combine the characteristics of TiO2 photocatalyst and the silver NPs loaded on TiO2 for the

89

redox transformation of aquatic pollutants in a sequential light-dark process. Although the

90

photocatalytic activity of TiO2 and the electron storage capacity of Ag NPs are well known, 4

ACS Paragon Plus Environment

Page 4 of 33

Page 5 of 33

Environmental Science & Technology

91

the serial combination of those properties has not been proposed for the removal of water

92

contaminants. The electrons stored in Ag/TiO2 (capacitive charging) during UV illumination

93

might be utilized to activate redox conversions in the subsequent dark cycle (thermal

94

discharging). Considering great interests in making solar water treatment technologies more

95

viable, the idea of utilizing not only the irradiation period (daytime) but also the post-

96

irradiation period (night time) for remediation purpose can be a conceptually interesting

97

strategy.

98

Herein, we investigated a sequential treatment of oxidation (light) and reduction (dark)

99

using Ag/TiO2. For this purpose, 4-chlorophenol (4-CP) and Cr(VI) (hexavalent chromium)

100

were employed as model pollutants for PCO and dark thermal reduction, respectively. Since

101

both 4-CP and Cr(VI) are ubiquitous contaminants and have been extensively investigated for

102

their photocatalytic removal,22-28 they are good model substrates that can be employed for the

103

demonstration of this sequential process. During the UV-irradiation period, photo-generated

104

electrons are charged in Ag while 4-CP is degraded by hole-mediated oxidation with

105

generating intermediates. In the following dark period, the stored electrons in Ag and the

106

degradation intermediates are used to reduce Cr(VI). Sequential removal of 4-CP and Cr(VI)

107

was monitored and the dual activities of Ag/TiO2 were compared with those of bare TiO2 and

108

Pt/TiO2 to understand the mechanism of the sequential process.

109 110

EXPERIMENTAL SECTION

111

Materials. Chemicals and materials used in this work include: A commercial TiO2 (P25),

112

which is a mixture of anatase and rutile (8:2) with primary particle sizes of 20-30 nm was

113

used as the substrate TiO2 sample, Na2Cr2O7·2H2O (Cr(VI), Aldrich), 4-chlorophenol (4-CP,

114

Sigma), ethanol (EtOH, J. T. Baker), formic acid (Aldrich), hydroxyhydroquinone (HHQ, 5

ACS Paragon Plus Environment

Environmental Science & Technology

115

Aldrich), 4-chlorocatechol (4-CC, Kasei), 1,4-benzoquinone (BQ, Aldrich), perchloric acid

116

(HClO4, Sigma-Aldrich), acetone (Samchun), sulfuric acid (H2SO4, Sigma-Aldrich),

117

diphenyl-carbazide (DPC, Aldrich). Humic acid (HA) was purchased from the International

118

Humic Substances Society (http://www.ihss.gatech.edu). Deionized water (D. I. water) used

119

was ultrapure (18 MΩ-cm) and prepared by a Barnstead purification system.

120

Experimental procedure. Ag/TiO2 and Pt/TiO2 were prepared by using a typical photo-

121

deposition method.12 TiO2 was suspended in the aqueous solution containing methanol (4%,

122

v/v) and noble metal precursor (H2PtCl6 or AgNO3) and then stirred and sonicated for 30 min

123

before irradiation. After UV irradiation (200-W mercury lamp) for 30 min, the metal-loaded

124

TiO2 particles were filtered, sufficiently washed with D. I. water, and dried at 80 °C. The

125

prepared photocatalyst was suspended in an aqueous solution (0.5 g/L) containing target

126

organic species (300 µM) in a pyrex reactor. The suspension was dispersed well by ultra-

127

sonication and the pH was adjusted to 3.0 with 1 N HClO4. The suspension was stirred for 30

128

min in the dark to allow equilibrium adsorption of the model organic substrate. A 300-W Xe

129

arc lamp (Oriel) was used as a solar simulating light source. The incident light was filtered

130

through a 10-cm IR water filter and a UV cutoff filter (λ > 320 nm) that blocks the light of

131

wavelengths shorter than 320 nm to avoid the direct photolysis of organic substrates and the

132

incident light intensity was 1.7 W/cm2 (optical power meter, Newport 1918-R). After a

133

certain time of UV irradiation, the reactor was placed in the dark and then Cr(VI) was

134

subsequently spiked into the pre-irradiated suspension that was well stirred during the entire

135

dark reaction period. The sample aliquots were intermittently withdrawn and filtered through

136

a 0.45-µm PTFE filter (Millipore) for the analysis of Cr(VI). For experiments studying the

137

effect of oxidation intermediates, the photocatalyst was first filtered, and Cr(VI) was then

138

added in the filtrate solution. 6

ACS Paragon Plus Environment

Page 6 of 33

Page 7 of 33

Environmental Science & Technology

139

Analysis. The concentration of Cr(VI) was measured spectrophotometrically using the DPC

140

(diphenylcarbazide) method.27 An aliquot of 0.5 mL sample solution was added to a vial

141

containing 2.5 mL of prepared DPC reagent (100 mL of D.I. water and 4 mL of DPC reagent

142

that contains 5 mL of acetone, 50 µL of H2SO4, and 0.01 g of DPC). The vial was mixed

143

vigorously and kept standing for 30 min before the analysis. The absorbance measurements at

144

540 nm (ε = 6850 M-1cm-1) were done using a UV/visible spectrophotometer (Libra S22,

145

Biochrom). Quantitative analysis of organic substrates was done using a high performance

146

liquid chromatograph (HPLC Agilent 1100) equipped with a C-18 column (Nova-Pak C18)

147

and a photodiode-array detector (Waters 996). The eluent was composed of 0.1% phosphoric

148

acid aqueous solution and acetonitrile (75:25 v/v). The residual organic carbon content in the

149

irradiated organic substrate solution was monitored by a total organic carbon (TOC) analyzer

150

(TOC-VCSH, Shimadzu).

151

The generation of OH radicals in the irradiated or pre-irradiated suspension of bare TiO2,

152

Ag/TiO2, and Pt/TiO2 was indirectly monitored by the fluorescence emission of 7-

153

hydroxycoumarin (7-HC) that was produced from the reaction of OH radical and coumarin (a

154

probe reagent for OH radical).29 The fluorescence emission intensity of 7-HC was monitored

155

at 460 nm under the excitation at 332 nm using a spectrofluorometer (FluoroMax 4, HORIBA

156

Jobin Yvon Inc.) The appearance of Ag plasmon band with stored electrons was observed by

157

using a UV/visible spectrophotometer (Shimadzu UV-2401PC).

158

Characterization of photocatalysts. The BET surface area of photocatalyst samples was

159

measured by using nitrogen adsorption/desorption isotherms (Micromeritics Tristar 3000

160

analyzer at 77K). JEOL JEM-2200FS with image Cs-corrector (200 KeV, 0.1nm) was used

161

for scanning transmission electron microscopy (STEM) image of bright and dark field.

162

Crystalline phases were determined by X-ray-powder diffraction (XRD) using Cu-Kα 7

ACS Paragon Plus Environment

Environmental Science & Technology

163

radiation (Mac Science Co. M18XHF). The chromium species deposited on the photocatalyst

164

surface after reaction with Cr(VI) was analyzed by X-ray photoelectron spectroscopy (XPS)

165

(Theta probe AR-XPS, Thermo Fisher Scientific) using Al-Kα (1486.6 eV) as the X-ray

166

source.

167 168

RESULTS AND DISCUSSION

169

Three different catalysts (bare TiO2, Pt/TiO2 and Ag/TiO2) degraded 300 µM of 4-CP

170

within 60 min (Figure 1a), but the efficiency of 4-CP removal was retarded by the

171

coexistence of Cr(VI) (see Figure S1). A previous study also reported that the photocatalytic

172

degradation of organic pollutants can be hindered by the co-existence of Cr(VI).30 We carried

173

out a control experiment which employed bare TiO2 photocatalyst that was pre-adsorbed with

174

Cr(VI) and observed that its photocatalytic activity for 4-CP degradation was markedly

175

inhibited. This implies that the presence of Cr(VI) on the surface of TiO2 is an inhibitor of

176

PCO activity although Cr(VI) is a good electron acceptor which may facilitate the hole-

177

induced PCO. The most plausible explanation is that Cr(VI) serves as an external charge

178

recombination center where Cr(VI) reacts serially with electrons and holes to make null

179

photocatalytic cycles. Such role of Cr(VI) should block the pathways of ROS generation

180

(e.g., O2−, H2O2, •OH) with retarding the PCO process. To test the inhibitory role of Cr(VI),

181

the generation of OH radical was indirectly monitored by detecting 7-hydroxycoumarin (7-

182

HC) which is produced from the PCO reaction between OH radical and coumarin (coumarin

183

+ •OH → 7-HC). In the presence of Cr(VI), the generation of OH radical was indeed

184

retarded for all three photocatalysts (see Figure S2). Since Cr(VI) is an intrinsic inhibitor of

185

PCO, it is a better approach to remove 4-CP and Cr(VI) in a sequential process (as shown in

186

Figure 1a) than in one batch reactor. 8

ACS Paragon Plus Environment

Page 8 of 33

Page 9 of 33

Environmental Science & Technology

187

Among the photocatalysts, the PCO degradation efficiency was in the order of Pt/TiO2

188

> Ag/TiO2 > TiO2. Noble metal-loaded TiO2 was prepared by a typical photo-deposition

189

method, which did not change the BET surface area and the crystal structure of the substrate

190

TiO2 (P25) (see Figure S3). The average size of noble metal NPs of Pt/TiO2 and Ag/TiO2 was

191

1.5 nm and 4 nm, respectively (see Figure S4). The positive effects of noble metals deposited

192

on TiO2 on the PCO of organic compounds are well known and Pt is more efficient than Ag

193

in most reported cases.8, 31, 32 The role of Pt is markedly prominent in the photocatalytic

194

mineralization ability as shown in Fig. 1b. Ag/TiO2 was only slightly more efficient than bare

195

TiO2 for 4-CP removal and no better than bare TiO2 for the mineralization. When the parent

196

4-CP was completely removed (after 60 min of UV irradiation), the TOC removal was only

197

partial with bare TiO2 and Ag/TiO2 but was almost complete with Pt/TiO2.

198

On the other hand, the reactivity in the dark period that immediately followed the UV

199

PCO process was significantly different among the three photocatalysts. After 60 min of UV

200

irradiation (when all 4-CP was removed), the reduction of Cr(VI) under the dark condition

201

(right after UV light turn-off) was investigated by spiking 100 µM Cr(VI) into the pre-

202

irradiated catalyst suspension. The right panel of Figure 1a compares the time-dependent

203

profiles of [Cr(VI)] which exhibit two distinct regions. An initial immediate decrease in

204

[Cr(VI)] (regime I) was followed by a slow and gradual decrease (regime II). It is noted that

205

Ag/TiO2 shows an outstanding activity for Cr(VI) removal compared with bare TiO2 and

206

Pt/TiO2 systems. Although Pt/TiO2 was the most active for the PCO of 4-CP, it was the least

207

active for the following dark thermal reduction of Cr(VI). The followings can be proposed as

208

mechanisms that are responsible for the removal of Cr(VI) in the dark period: (1) adsorption

209

on the catalyst surface, (2) chemical reduction by remaining intermediates of 4-CP

210

degradation such as quinone derivatives,33-35 and (3) reduction by electrons in the noble metal 9

ACS Paragon Plus Environment

Environmental Science & Technology

Page 10 of 33

211

phase (Pt or Ag), which were stored during the pre-irradiation period. Control experiments

212

were carried out to estimate the contribution from each mechanism.

213

First, the removal of Cr(VI) by adsorption was estimated for bare TiO2, Ag/TiO2, and

214

Pt/TiO2 (see Figure 2a). In the case of bare TiO2 and Pt/TiO2, the total amount of Cr(VI)

215

removed by the adsorption is almost the same as observed in pre-irradiation-dark cycle

216

experiments (Figure 1a). Second, the chemical reduction by 4-CP oxidation intermediates

217

was negligible with bare TiO2 and Pt/TiO2 as shown in Figure 2b. This indicates the

218

adsorption mechanism is mainly responsible for Cr(VI) removal for both bare TiO2 and

219

Pt/TiO2 in the dark period. In contrast, both adsorption and chemical reduction mechanisms

220

contribute to initial rapid Cr(VI) removal in the case of Ag/TiO2. The photocatalytic

221

degradation of 4-CP is known to generate intermediates such as benzoquinone (BQ),

222

hydroquinone

223

hydroxybenzoquinone (HBQ), and other minor intermediates.36 We also confirmed the

224

generation of those intermediates during PCO of 4-CP in the presence of bare TiO2, Ag/TiO2

225

and Pt/TiO2 by HPLC analysis (Figure S5). To confirm that these intermediates of 4-CP

226

degradation reduce Cr(VI), four different quinone species were tested. As shown in Figure 3,

227

all 4 compounds (BQ, 4-CC, HQ and HHQ) exhibited Cr(VI) reduction capacity and HHQ

228

showed the highest activity. Since 4-CP was almost completely mineralized after 1 h PCO in

229

the case of Pt/TiO2, the Cr(VI) reduction by intermediates was negligible for Pt/TiO2 as

230

shown in Figure 2b. On the other hand, it is interesting to note that the reduction by

231

intermediates was significantly higher for Ag/TiO2 than bare TiO2 despite the fact that the

232

residual TOC values after 1 h PCO were similar for both Ag/TiO2 and bare TiO2 (see Figure

233

1b). This implies that intermediates generated from Ag/TiO2 PCO are more reactive towards

234

Cr(VI) than those from bare TiO2 PCO.

(HQ),

4-chlorocatechol

(4-CC),

hydroxyhydroquinone

10

ACS Paragon Plus Environment

(HHQ),

Page 11 of 33

Environmental Science & Technology

235

However, they cannot be responsible for the gradual decrease in [Cr(VI)] observed at a

236

longer time scale (Regime II in Figure 1a). These observations suggest that stored electrons

237

in the noble metal are mainly responsible for dark Cr(VI) removal (in regime II) in the

238

Ag/TiO2 system. It has been previously reported that the electrons trapped in bare TiO2 NPs

239

during UV irradiation can be used for reducing metal ions such as Cu(II),37 Ag(I),38 and

240

Cr(VI)39 immediately after turning off the light. However, the post-irradiation electron

241

transfer rate on bare TiO2 was fast enough to be completed in a sub-second time scale, which

242

could be monitored only by using the stopped flow technique. The presence of Ag NPs not

243

only increases the electron storage capacity significantly but also enables the slow release of

244

the stored electrons for a longer time. Based on the results of the aforementioned control

245

experiments, Figure 4a quantifies each contribution of the adsorption, the chemical reduction

246

by intermediates, and the reduction by stored electrons towards the total Cr(VI) removal. It

247

can be clearly seen that the contribution of the reduction by the stored electrons is

248

significantly higher in Ag/TiO2 (30%) compared to bare TiO2 (2.8%) and Pt/TiO2 (1.8%).

249

The pH dependence of the photocatalytic removal of 4-CP and the subsequent removal of

250

Cr(VI) in the post-irradiation (dark) period was compared (see Table S1). Although the PCO

251

activity was little influenced by the pH change (pH 3-10), the dark removal efficiency of

252

Cr(VI) was markedly influenced by pH, which dramatically decreased with increasing pH 3

253

to 10. Being an oxyanion, chromate should be electrostatically attracted to the positively

254

charged TiO2 surface (pHzpc ~ 6) at acidic condition and repelled from the negatively charged

255

TiO2 surface at alkaline condition. As a result, the reductive conversion of chromate anions

256

on Ag/TiO2 is favored at acidic condition and hindered at alkaline condition.

257

On the other hand, the post-irradiation (dark) reduction of Cr(VI) was also carried out

258

in the absence of dissolved O2 to investigate the effect of O2 on the Cr(VI) reduction 11

ACS Paragon Plus Environment

Environmental Science & Technology

259

pathways, which is shown in Figure 4b. The most outstanding feature of the anoxic system is

260

the increased contribution of the reduction by stored electrons for all catalysts. In particular,

261

the contribution of stored electrons was markedly enhanced for Pt/TiO2 from 2% (in the

262

presence of O2) to 55% (in the absence of O2). This indicates that the storage of electrons and

263

their subsequent transfer in the dark condition are enabled only in the absence of dissolved O2

264

for Pt/TiO2 since platinum is a good catalyst for O2 reduction.40 Therefore, electrons in the Pt

265

metal are immediately scavenged by dioxygen without leaving any electrons that would

266

discharge slowly in the following dark period.5, 7, 10 On the other hand, for Ag/TiO2, the

267

contribution by stored electrons was only moderately enhanced in the absence of O2 (Figure

268

4a vs 4b). This supports that the capacitive electron storage and discharge from Ag is little

269

affected by the presence of O2. That is, the storage of electrons in metals during the

270

irradiation period and the subsequent discharge of them in the following dark period are

271

enabled only with Ag/TiO2 regardless of the presence of O2.

272

As for the chemical reduction by intermediates in the anoxic condition, its contribution

273

was reduced with Ag/TiO2 but enhanced with Pt/TiO2 compared to that in the oxic condition.

274

This implies that the concentrations of 4-CP degradation intermediates in the anoxic

275

condition were reduced with Ag/TiO2 but enhanced with Pt/TiO2, compared with those in the

276

oxic condition. To investigate this effect, TOC measurements were compared between the

277

oxic and anoxic systems. After 1 h PCO of 4-CP, the residual TOC values were 36% and 0%

278

in the oxic condition and 95% and 88% in the anoxic condition for Ag/TiO2 and Pt/TiO2,

279

respectively. (see Figures 1b and S6) For Ag/TiO2, the PCO of 4-CP was significantly

280

retarded in the anoxic condition and hence lower concentration of intermediates should be

281

generated. As for Pt/TiO2, the PCO was also drastically retarded in the absence of O2, but

282

about 50% of 4-CP was removed after 1 h irradiation. Considering that the residual TOC was 12

ACS Paragon Plus Environment

Page 12 of 33

Page 13 of 33

Environmental Science & Technology

283

88% after 1 h PCO of Pt/TiO2, a significant fraction of removed 4-CP should be converted

284

into intermediates, which can reduce Cr(VI) in the dark phase (see Figure 4b). Since Pt/TiO2

285

can completely mineralize 4-CP after 1 h PCO in the presence of O2 with leaving little TOC,

286

the contribution of chemical reduction by intermediates was absent in the Pt/TiO2/oxic

287

system.

288

To further confirm the electron storage properties of Ag/TiO2, an additional control

289

experiment was carried out to exclude the competitive effect of the PCO intermediates. The

290

post-irradiation removal of Cr(VI) was carried out after 1 h UV irradiation of Ag/TiO2

291

suspension containing no organic pollutants (D.I. water only, aerated). Since the production

292

of organic intermediates should be absent in this case, the effect of stored electrons on Cr(VI)

293

reduction can be easily demonstrated as shown in Figure 4c. Even in the absence of organic

294

substrates, the intrinsic electron storage capacity of Ag/TiO2 is outstanding compared to

295

Pt/TiO2. The effects of other organic substrates on the post-irradiation removal of Cr(VI)

296

were also investigated with employing ethanol, formic acid, and humic acid. As seen in

297

Figure 5, intermediates generated during the PCO of these alternative substrates showed very

298

small or negligible Cr(VI) reduction capacity compared to the case of 4-CP. However, the

299

amount of Cr(VI) reduced by stored electrons remained almost the same (20-30 µM)

300

regardless of the kind of substrate organic compounds (even in their absence). The reduction

301

mechanism by stored electrons in Ag seems to operate by itself, not depending on the PCO of

302

organic substrates.

303

The observation that the removal of Cr(VI) on Ag/TiO2 continued even after hours in

304

the post-irradiation period implies that the stored electrons are very long-lived even in the

305

aerated solution. To monitor this slow discharge of electrons directly, the decay of the

306

photovoltage of the irradiated electrodes (bare TiO2, Pt/TiO2, and Ag/TiO2) upon turning off 13

ACS Paragon Plus Environment

Environmental Science & Technology

307

the light was recorded as a function of time as shown in Figure 6. The post-irradiation

308

potential decay on the Ag/TiO2 electrode is significantly retarded compared with bare TiO2

309

and Pt/TiO2 electrodes. Although the potential rapidly decayed within a minute, small

310

residual potential on Ag/TiO2 persisted for a much longer time (far beyond 30 minutes after

311

UV turn-off), which is consistent with the fact that the removal of Cr(VI) on Ag/TiO2

312

continued for hours in the post-irradiation period (see Figure 1a). Another evidence for the

313

stored electrons was obtained from UV/visible absorption spectra of Ag/TiO2 (see Figure 7).

314

Stored electrons in silver NPs induce the silver plasmon band.10, 11, 41 While Ag/TiO2 before

315

light irradiation exhibits no absorption peak in the range 300-900 nm, a peak at 450 nm was

316

observed only after UV illumination but not after visible light (λ > 420 nm) irradiation. Since

317

this peak cannot be ascribed to the plasmonic absorption peak of Ag NPs, it should be related

318

to the accumulation of electrons in the Ag metal (see Figure 7a). The UV-induced band at

319

450 nm did not change for 1 h even after the UV illumination was switched off, but decreased

320

in intensity upon spiking Cr(VI) (see Figure 7b). This confirms that the absorbance band at

321

450 nm is indicative of photo-induced electron accumulation, which disappears upon the

322

subsequent discharge on Ag/TiO2.

323

The post-irradiation catalytic effect of Ag/TiO2 might not be limited to Cr(VI)

324

reduction only. We tested several other chemical conversion reactions in the dark period

325

using the pre-irradiated Ag/TiO2. For example, the reductive conversion of nitrate (NO3-) by

326

electrons stored in Ag/TiO2 was negligible. The reductive discoloration of methylene blue in

327

the post-irradiation period, which had been demonstrated with the pre-irradiated Ag/TiO2 in

328

deaerated ethanol,11 was not observed in the present experimental condition (aerated aqueous

329

solution). However, we observed a sign of OH radical generation on Ag/TiO2 in the post-

330

irradiation period whereas bare TiO2 and Pt/TiO2 exhibited no such sign (see Figure 8). This 14

ACS Paragon Plus Environment

Page 14 of 33

Page 15 of 33

Environmental Science & Technology

331

implies that electrons stored in Ag/TiO2 reacted with dioxygen sequentially in the dark to

332

generate OH radicals (i.e., O2 → HO2• → H2O2 → •OH). This observation is consistent with a

333

previous report that PdO/TiON photocatalyst exhibited a bactericidal activity up to 8 hours in

334

the post-irradiation period.42 Small but persisting generation of OH radicals (or other ROS)

335

through the reaction of stored electrons should be responsible for the dark bactericidal

336

activity. Although the electrons stored in Ag/TiO2 are not energetic enough to be utilized for

337

a wide variety of contaminants removal, they have long-lasting reactive effects for selected

338

substrates.

339

Finally, the stability and reusability of catalysts need to be mentioned since this is of

340

high practical importance. The catalyst performance of bare TiO2, Pt/TiO2 and Ag/TiO2 was

341

tested through multiple cycles for PCO removal of 4-CP, PCO removal of 4-CP in the

342

presence of Cr(VI), and PCO removal of 4-CP followed by dark reaction of Cr(VI) (see

343

Figure S7). Regardless of whether Cr(VI) was co-present with 4-CP during the irradiation

344

period or added in the post-irradiation period, the PCO activity of the tested catalysts (bare

345

TiO2, Pt/TiO2, and Ag/TiO2) was irreversibly deactivated. The dark activity of Ag/TiO2 for

346

Cr(VI) removal in the post-irradiation period was also markedly reduced with repeating the

347

irradiation-dark cycles (see Figure S8). This implies that the catalyst surface was deactivated

348

by the reductive deposition of Cr(III) species. The XPS analysis of the catalyst surface after

349

the post-irradiation reaction with Cr(VI) clearly showed that the Cr(III) species is present on

350

Ag/TiO2, but not on bare TiO2 and Pt/TiO2. (see Figure S9).

351 352

ENVIRONMENTAL IMPLICATIONS

353

Most photocatalytic water treatment applications have been focused on pollutants removal

354

under continuous illumination (UV or visible light) conditions. Excess charges can be 15

ACS Paragon Plus Environment

Environmental Science & Technology

355

accumulated on the photocatalyst due to the difference between the interfacial charge transfer

356

rates of electron and hole to the aquatic redox species.43, 44 When electrons are accumulated

357

in the metal NPs during illumination, they can be subsequently discharged to suitable electron

358

acceptors in the absence of light. The utilization of such stored charges in the post-irradiation

359

process was applied to anticorrosion system.44 On the basis of this principle, this study

360

utilized the electron storage capacity of Ag NPs loaded on TiO2 surface to reduce Cr(VI) in

361

the following dark period. While the surface of Pt has ohmic contact for rapid discharge of

362

trapped electrons and exhibits a high electrochemical activity for O2 reduction,40 the

363

capacitive property of Ag and its lower catalytic activity for O2 reduction allows electron

364

accumulation and temporary storage even in the presence of dissolved O2. By coupling the

365

PCO of 4-CP with dark thermal reduction (Cr(VI)) reaction, the effect of metal loading on

366

TiO2 was examined in the presence of different organic substrates. The post-irradiation

367

removal of Cr(VI) was contributed by adsorption on catalyst, chemical reduction by organic

368

degradation intermediates, and reduction by electrons stored in noble metal NPs. In

369

particular, the reduction mechanism by stored electrons in Ag seems to operate for itself, not

370

depending on the PCO of organic substrates and the presence of dissolved O2.

371

The utilization of stored photo-electrons to initiate reductive conversions may

372

provide a useful concept to achieve continuous pollutant removal using both day

373

(illumination) and night (dark) cycles. This sequential combination of PCO and dark reaction

374

cycles can be employed in the design of photocatalytic water treatment reactors in which the

375

irradiated and non-irradiated parts can be integrated into a single treatment system. By

376

utilizing both UV PCO and dark reaction period, the overall process can be more energy

377

efficient for the removal of various pollutants. For example, the co-presence of 4-CP and

378

Cr(VI) in the photocatalyst suspension significantly retarded the PCO of 4-CP (see Figure S1) 16

ACS Paragon Plus Environment

Page 16 of 33

Page 17 of 33

Environmental Science & Technology

379

but this present sequential combination of PCO-dark reactions successfully removed both

380

pollutants with consuming the same amount of photon energy. However, it should be

381

mentioned that the present study is at a proof-of-concept stage and the real application might

382

be hindered by many practical problems such as low reactivity of stored electrons and

383

catalyst deactivation. The present system of photocatalytic removal of 4-CP combined with

384

the dark reaction of Cr(VI) may not be of great environmental significance but the proposed

385

concept can be ideally suitable for target applications where the long-lasting reactivity of

386

stored electrons in Ag/TiO2 can be utilized for the removal of low-level contaminants.

387

Further investigations of the proposed system may find more suitable applications.

388

17

ACS Paragon Plus Environment

Environmental Science & Technology

389

ASSOCIATED CONTENT

390

Supporting Information. PCO degradation of 4-CP with and without Cr(VI) (Figure S1);

391

Time profiles of 7-HC generation (Figure S2); XRD patterns and BET surface area (Figure

392

S3); STEM images (Figure S4); HPLC chromatograms of 4-CP degradation intermediates

393

(Figure S5); photocatalytic removal of 4-CP and TOC in the absence of O2 (Figure S6);

394

repetition tests of 4-CP degradation and Cr(VI) removal (Figure S7-S8); XPS analysis of

395

Cr(III) deposited on catalysts (Figure S9). This material is available free of charge via the

396

Internet at http://pubs.acs.org.

397

ACKNOWLEDGMENT

398

This work was supported by Global Research Laboratory (GRL) Program (NRF-

399

2014K1A1A2041044) and KCAP (Sogang Univ.) (2009-0093880), which were funded by the

400

Korea Government (MSIP) through the National Research Foundation (NRF).

18

ACS Paragon Plus Environment

Page 18 of 33

Page 19 of 33

401

Environmental Science & Technology

References

402

(1) Linsebigler, A. L.; Lu, G.; Yates, J. T. Photocatalysis on TiO2 surfaces: principles,

403

mechanisms, and selected results. Chem. Rev. 1995, 95 (3), 735-758.

404

(2) Khan, M. R.; Chuan, T. W.; Yousuf, A.; Chowdhury, M. N. K.; Cheng, C. K. Schottky

405

barrier and surface plasmonic resonance phenomena towards the photocatalytic reaction:

406

study of their mechanisms to enhance photocatalytic activity. Catal. Sci. Technol. 2015, 5 (5),

407

2522-2531.

408

(3) Chen, H.; Chen, S.; Quan, X.; Zhang, Y. Structuring a TiO2-based photonic crystal

409

photocatalyst with Schottky junction for efficient photocatalysis. Environ. Sci. Technol. 2010,

410

44 (1), 451-455.

411

(4) Park, H.; Kim, H.-i.; Moon, G.-h.; Choi, W. Photoinduced charge transfer processes in

412

solar photocatalysis based on modified TiO2. Energy Environ. Sci. 2016, 9 (2), 411-433.

413

(5) Schneider, J.; Matsuoka, M.; Takeuchi, M.; Zhang, J.; Horiuchi, Y.; Anpo, M.;

414

Bahnemann, D. W. Understanding TiO2 photocatalysis: Mechanisms and materials. Chem.

415

Rev. 2014, 114 (19), 9919-9986.

416

(6) Kim, J.; Lee, C. W.; Choi, W. Platinized WO3 as an environmental photocatalyst that

417

generates OH radicals under visible light. Environ. Sci. Technol. 2010, 44 (17), 6849-6854.

418

(7) Kim, J.; Lee, J.; Choi, W. Synergic effect of simultaneous fluorination and platinization of

419

TiO2 surface on anoxic photocatalytic degradation of organic compounds. Chem. Commun.

420

2008, (6), 756-758.

421

(8) Kim, J.; Monllor-Satoca, D.; Choi, W. Simultaneous production of hydrogen with the

422

degradation of organic pollutants using TiO2 photocatalyst modified with dual surface

423

components. Energy Environ. Sci. 2012, 5 (6), 7647-7656.

424

(9) Jakob, M.; Levanon, H.; Kamat, P. V. Charge distribution between UV-irradiated TiO2 19

ACS Paragon Plus Environment

Environmental Science & Technology

425

and gold nanoparticles: Determination of shift in the Fermi level. Nano Lett. 2003, 3 (3), 353-

426

358.

427

(10) Wood, A.; Giersig, M.; Mulvaney, P. Fermi level equilibration in quantum dot-metal

428

nanojunctions. J. Phys. Chem. B 2001, 105 (37), 8810-8815.

429

(11) Takai, A.; Kamat, P. V. Capture, store, and discharge. Shuttling photogenerated

430

electrons across TiO2-silver interface. ACS Nano 2011, 5 (9), 7369-7376.

431

(12) Choi, Y.; Kim, H. I.; Moon, G. H.; Jo, S.; Choi, W. Boosting up the low catalytic

432

activity of silver for H2 production on Ag/TiO2 photocatalyst: Thiocyanate as a selective

433

modifier. ACS Catal. 2016, 6 (2), 821-828.

434

(13) Li, M.; Noriega-Trevino, M. E.; Nino-Martinez, N.; Marambio-Jones, C.; Wang, J.;

435

Damoiseaux, R.; Ruiz, F.; Hoek, E. M. V. Synergistic bactericidal activity of Ag-TiO2

436

nanoparticles in both light and dark conditions. Environ. Sci. Technol. 2011, 45 (20), 8989-

437

8995.

438

(14) Reddy, M. P.; Venugopal, A.; Subrahmanyam, M. Hydroxyapatite-supported Ag-TiO2

439

as Escherichia coli disinfection photocatalyst. Water Res. 2007, 41 (2), 379-386.

440

(15) Jiang, Y.; Liu, D.; Cho, M.; Lee, S. S.; Zhang, F.; Biswas, P.; Fortner, J. D. In situ

441

photocatalytic synthesis of Ag nanoparticles (nAg) by crumpled graphene oxide composite

442

membranes for filtration and disinfection applications. Environ. Sci. Technol. 2016, 50 (5),

443

2514-2521.

444

(16) Xu, L. M.; Zhang, D. D.; Ming, L. F.; Jiao, Y. C.; Chen, F. Synergistic effect of

445

interfacial lattice Ag+ and Ag-0 clusters in enhancing the photocatalytic performance of TiO2.

446

Phys. Chem. Chem. Phys. 2014, 16 (36), 19358-19364.

447

(17) Yu, J.; Dai, G.; Huang, B. Fabrication and characterization of visible-light-driven

448

plasmonic photocatalyst Ag/AgCl/TiO2 nanotube arrays. J. Phys. Chem. C 2009, 113 (37), 20

ACS Paragon Plus Environment

Page 20 of 33

Page 21 of 33

Environmental Science & Technology

449

16394-16401.

450

(18) Zhang, H.; Wang, G.; Chen, D.; Lv, X.; Li, J. Tuning photoelectrochemical

451

performances of Ag-TiO2 nanocomposites via reduction/oxidation of Ag. Chem. Mater. 2008,

452

20 (20), 6543-6549.

453

(19) Mulvaney, P. Surface plasmon spectroscopy of nanosized metal particles. Langmuir

454

1996, 12 (3), 788-800.

455

(20) Henglein A. Reactions of organic free radicals at colloidal silver in aqueous solution.

456

Electron pool effect and water decomposition. J. Phy. Chem. 1979, 83 (17), 2209-2216.

457

(21) Gunawan, C.; Teoh, W. Y.; Marquis, C. P.; Lifia, J.; Amal, R. Reversible antimicrobial

458

photoswitching in nanosilver. Small 2009, 5 (3), 341-344.

459

(22) Yue, B.; Zhou, Y.; Xu, J.; Wu, Z.; Zhang, X.; Zou, Y.; Jin, S. Photocatalytic degradation

460

of aqueous 4-chlorophenol by silica-immobilized polyoxometalates. Environ. Sci. Techno.

461

2002, 36 (6), 1325-1329.

462

(23) Sun, B.; Reddy, E. P.; Smirniotis, P. G. Visible light Cr (VI) reduction and organic

463

chemical oxidation by TiO2 photocatalysis. Environ. Sci. Technol. 2005, 39 (16), 6251-6259.

464

(24) Kim, S.; Choi, W. Visible-light-induced photocatalytic degradation of 4-chlorophenol

465

and phenolic compounds in aqueous suspension of pure titania: demonstrating the existence

466

of a surface-complex-mediated path. J. Phys. Chem. B 2005, 109 (11), 5143-5149.

467

(25) Kim, G.; Lee, S. H.; Choi, W. Glucose-TiO2 charge transfer complex-mediated

468

photocatalysis under visible light. Appl. Catal. B-Envrion. 2015, 162, 463-469.

469

(26) Testa, J. J.; Grela, M. A.; Litter, M. I. Heterogeneous photocatalytic reduction of

470

chromium(VI) over TiO2 particles in the presence of oxalate: involvement of Cr(V)

471

species. Environ. Sci. Technol. 2004, 38 (5), 1589-1594.

472

(27) Kim, K.; Choi, W. Enhanced redox conversion of chromate and arsenite in ice. Environ. 21

ACS Paragon Plus Environment

Environmental Science & Technology

473

Sci. Technol. 2011, 45 (6), 2202-2208.

474

(28) Colon, G.; Hidalgo, M. C.; Navıo, J. A. Photocatalytic deactivation of commercial TiO2

475

samples during simultaneous photoreduction of Cr (VI) and photooxidation of salicylic

476

acid. J. Photoch. Photobio. A 2001, 138 (1), 79-85.

477

(29) Ishibashi, K. I.; Fujishima, A.; Watanabe, T.; Hashimoto, K. Detection of active

478

oxidative species in TiO2 photocatalysis using the fluorescence technique. Electrochem.

479

Commun. 2000, 2 (3), 207-210.

480

(30) Wang, L.; Wang, N.; Zhu, L.; Yu, H.; Tang, H. Photocatalytic reduction of Cr(VI) over

481

different TiO2 photocatalysts and the effects of dissolved organic species. J. Hazard. Mater.

482

2008, 152 (1), 93-99.

483

(31) Coleman, H. M.; Chiang, K.; Amal, R. Effects of Ag and Pt on photocatalytic

484

degradation of endocrine disrupting chemicals in water. Chem. Eng. J. 2005, 113 (1), 65-72.

485

(32) Li, C. H.; Hsieh, Y. H.; Chiu, W. T.; Liu, C. C.; Kao, C. L. Study on preparation and

486

photocatalytic performance of Ag/TiO2 and Pt/TiO2 photocatalysts. Separ. Purif. Technol.

487

2007, 58 (1), 148-151.

488

(33) Elovitz, M. S.; Fish, W. Redox interactions of Cr(VI) and substituted phenols: Products

489

and mechanism. Environ. Sci. Technol. 1995, 29 (8), 1933-1943.

490

(34) James, B. R. The challenge of remediating chromium-contaminated soil. Environ. Sci.

491

Technol. 1996, 30 (6), A248-A251.

492

(35) Zhang, H. K.; Lu, H.; Wang, J.; Zhou, J. T.; Sui, M., Cr(VI) reduction and Cr(III)

493

immobilization by acinetobacter sp HK-1 with the assistance of a novel quinone/graphene

494

oxide composite. Environ. Sci. Technol. 2014, 48 (21), 12876-12885.

495

(36) Theurich, J.; Lindner, M.; Bahnemann, D. W. Photocatalytic degradation of 4-

496

chlorophenol in aerated aqueous titanium dioxide suspensions: A kinetic and mechanistic 22

ACS Paragon Plus Environment

Page 22 of 33

Page 23 of 33

Environmental Science & Technology

497

study. Langmuir 1996, 12 (26), 6368-6376.

498

(37) Mohamed, H. H.; Mendive, C. B.; Dillert, R.; Bahnemann, D. W. Kinetic and

499

mechanistic investigations of multielectron transfer reactions induced by stored electrons in

500

TiO2 nanoparticles: a stopped flow study. J. Phys. Chem. A 2011, 115 (11), 2139-2147.

501

(38) Mohamed, H. H.; Dillert, R.; Bahnemann, D. W. Growth and reactivity of silver

502

nanoparticles on the surface of TiO2: a stopped flow study. J. Phys. Chem. A 2011, 115 (11),

503

12163-12172.

504

(39) Meichtry, J. M.; Dillert, R.; Bahnemann, D. W.; Litter, M. I. Application of the Stopped

505

Flow Technique to the TiO2-Heterogeneous Photocatalysis of Hexavalent Chromium in

506

Aqueous Suspensions: Comparison with O2 and H2O2 as Electron Acceptors. Langmuir

507

2015, 31 (22), 6229-6236.

508

(40) Yu, T. H.; Hofmann, T.; Sha, Y.; Merinov, B. V.; Myers, D. J.; Heske, C.; Goddard III,

509

W. A. Finding correlations of the oxygen reduction reaction activity of transition metal

510

catalysts with parameters obtained from quantum mechanics. J. Phys. Chem. C 2013, 117

511

(50), 26598-26607.

512

(41) Hirakawa, T.; Kamat, P. V. Charge separation and catalytic activity of Ag@TiO2 core-

513

shell composite clusters under UV-irradiation. J. Am. Chem. Soc. 2005, 127 (11), 3928-3934.

514

(42) Li, Q.; Li, Y. W.; Wu, P.; Xie, R.; Shang, J. K. Palladium oxide nanoparticles on

515

nitrogen-doped titanium oxide: Accelerated photocatalytic disinfection and post-illumination

516

catalytic “Memory”. Adv. Mater. 2008, 20 (19), 3717-3723.

517

(43) Kim, S.; Park, H. Sunlight-harnessing and storing heterojunction TiO2/Al2O3/WO3

518

electrodes for night-time applications. RSC Adv. 2013, 3 (38), 17551-17558.

519

(44) Tatsuma, T.; Saitoh, S.; Ohko, Y.; Fujishima, A. TiO2-WO3 photoelectrochemical

520

anticorrosion system with an energy storage ability. Chem. Mater. 2001, 13 (9), 2838-2842. 23

ACS Paragon Plus Environment

Environmental Science & Technology

521 522

Scheme 1. Conceptual illustration of photocatalytic degradation of 4-CP and the following

523

reductive removal of Cr(VI) in the dark. After the photocatalytic degradation reaction, the

524

reactor was placed in the dark and Cr(VI) was spiked. Cr(VI) can be removed by three

525

different mechanisms that include adsorption, reduction by 4-CP degradation intermediates,

526

and reduction by stored electrons.

527

24

ACS Paragon Plus Environment

Page 24 of 33

Page 25 of 33

Environmental Science & Technology

300

in the Dark

(a) UV irradiation

80

200 TiO2

150

Ag/TiO2

Pt/TiO2

regime I

TiO2

Pt/TiO2

100

Ag/TiO2

60 40 20

50 regime II

0 0

10

20

30

40

50

irradiation time (min)

0

60

120

[Cr(VI)] (µM)

[4-CP] (µM)

250

100

0 180

240

300

Dark reaction time (min)

100

[TOC]/[TOC0] x 100%

(b)

After 60 min UV irradiation

80 60 40 20 0

TiO2

Ag/TiO2

Pt/TiO2

528 529

Figure 1. (a) Time profiles of the photocatalytic degradation of 4-CP under UV irradiation

530

and the subsequent Cr(VI) removal in the dark (after turning off the light) and (b) the

531

resulting removal of total organic carbon (TOC) after 60 min UV irradiation. The

532

experimental conditions were [Cat] = 0.5 g/L, [noble metal (Pt or Ag) loading on TiO2] = 3.0

533

wt%, [4-CP]0 = 300 µM, [Cr(VI)]0 = 100 µM, pH0 = 3.0, air-equilibrated, and λ > 320 nm

534

irradiation.

535

25

ACS Paragon Plus Environment

Environmental Science & Technology

Page 26 of 33

100

[Cr(VI)] (µ M)

80 60 Pt/TiO2 TiO2

40

Ag/TiO2

(a) dark adsorption

20 0 0

30

60

90

120

150

180

time (min) 100

[Cr(VI)] (µM)

80 60

Pt/TiO2 TiO2

40

Ag/TiO2

(b) dark reduction by 4-CP oxidation intermediates

20 0 0

536

30

60

90

120

150

180

time (min)

537 538

Figure 2. Time profiles of Cr(VI) removal by (a) physical adsorption on catalyst in the dark,

539

and (b) dark thermal reduction induced by the remaining intermediates of 4-CP oxidation that

540

were generated in the pre-PCO period for 60 min. After the pre-PCO period, the catalyst was

541

filtered out and Cr(VI) was then added into the filtrate solution. The experimental conditions

542

were [Cat] = 0.5 g/L, [noble metal (Pt or Ag) loading on TiO2] = 3.0 wt%, [4-CP]0 = 300 µM,

543

[Cr(VI)]0 = 100 µM, pH0 = 3.0, air-equilibrated.

544

26

ACS Paragon Plus Environment

Page 27 of 33

Environmental Science & Technology

HHQ HQ 4CC BQ 4CP

Cr(VI) removal (%)

100 80 60 40 20 0 0

50

100

150

200

250

300

intermediates (µΜ) 545 546

Figure 3. Cr(VI) removal by various intermediates of 4-CP degradation in the dark.

547

Hydroxyhydroquinone

548

benzoquinone (BQ) were used as model intermediates. The Cr(VI) removal efficiency was

549

tested as a function of the intermediate concentration. The effect of 4-CP itself was also tested

550

as a control. The experimental conditions were [Cr(VI)]0 = 100 µM, pH0 = 3.0, air-

551

equilibrated. The reaction was finished within 10 min.

(HHQ),

hydroquinone

(HQ),

4-chlorocatechol

552

27

ACS Paragon Plus Environment

(4-CC),

and

Environmental Science & Technology

100

-

Cr(VI) removal (%)

(a) Oxic

stored e interm. adsorption

80 60 40 20 0

TiO2

Ag/TiO2

Pt/TiO2

Ag/TiO2

Pt/TiO2

100

(b) Anoxic Cr(VI) removal (%)

-

80

Stored e interm. adsorption

60 40 20 0

TiO2 100

-

Cr(VI) removal (% )

(c) DW

stored e adsorption

80 60 40 20 0

TiO2

Ag/TiO2

Pt/TiO2

553 554 555 556 557 558 559

Figure 4. Removal of Cr(VI) in pre-irradiated aqueous solution of bare TiO2, Ag/TiO2, and Pt/TiO2 (a) in air-equilibration and (b) in anoxic condition. (c) Removal of Cr(VI) in preirradiated deionized water suspension (without 4-CP, aerated) of bare TiO2, Ag/TiO2, and Pt/TiO2 (uncertainty of ±2%). The experimental conditions were [Cat] = 0.5 g/L, [4-CP]0 = 300 µM, [Cr(VI)]0 = 100 µM, pH0 = 3.0, air-equilibrated or Ar-saturated, and λ > 320 nm irradiation.

28

ACS Paragon Plus Environment

Page 28 of 33

Page 29 of 33

Environmental Science & Technology

Cr(VI) removal (%)

100

-

stored e interm. adsorption

80 60 40 20 0

4-CP 560

EtOH Formic acid

HA

DW

561

Figure 5. Removal of Cr(VI) in the pre-irradiated aqueous suspension of Ag/TiO2 which

562

contained various organic substrates (4-CP, EtOH, Formic acid, or HA) or deionized water

563

only (DW, as a control) (uncertainty of ± 2%). The experimental conditions were [Ag(3.0

564

wt%)/TiO2] = 0.5 g/L, [4-CP, EtOH, or formic acid]0 = 300 µM, [HA]0 = 1 ppm, [Cr(VI)]0 =

565

100 µM, pH0 = 3.0, air-equilibrated, and λ > 320 nm irradiation.

566

29

ACS Paragon Plus Environment

Environmental Science & Technology

1.4 Light OFF

Light ON

1.2

(E-E0)/(Eph-E0)

1.0 0.8 0.6

TiO2

0.4

Pt/TiO2 Ag/TiO2

0.2 0.0 0

10

20

30

40

50

60

70

time (min) 567 568

Figure 6. Time profiles of the normalized open circuit potential (OCP) of the bare TiO2,

569

Pt/TiO2, and Ag/TiO2 electrode before, during, and after UV irradiation. E0 is the OCP

570

stationary value in the dark, and Eph is the stationary potential under UV irradiation.

571

Experimental conditions were [4-CP]0 = 300 µM, [NaClO4]0 = 0.1 M, pH0 = 3.0, air

572

equilibrated, and λ > 320 nm irradiation.

573

30

ACS Paragon Plus Environment

Page 30 of 33

Page 31 of 33

Environmental Science & Technology

1.0

(a)

Absorbance

0.8

0.6 Ag/TiO2 0.4

0.2

VL (10 min) UV (1 min) UV (10 min) UV (60 min)

1.0

(b)

Absorbance

0.8

0.6

0.4

0.2 350

574

Ag/TiO2 UV (60 min) UV (60 min) + Cr(VI) spiking in the dark (10 min) 400

450

500

550

600

650

Wavelength (nm)

575

Figure 7. UV/visible absorption spectral changes of Ag/TiO2 under UV-irradiation. (a) a

576

broad band around 450 nm appeared under UV irradiation, but not under visible light. (b) The

577

UV-induced broad band disappeared after spiking Cr(VI) in the dark. Experimental

578

conditions were [Ag/TiO2] = 0.5 g/L (in D.I. water), pH0 = 3.0, [Cr(VI)]add = 100 µM, air-

579

equilibrated, and λ > 320 nm irradiation.

580

31

ACS Paragon Plus Environment

Environmental Science & Technology

Emission intensity (a.u.)

350 Ag/TiO2

300

TiO2 Pt/TiO2

250

Ag/TiO2 (Dark)

200 150 100 50 0

20

40

60

80

100

120

time (min)

581 582

Figure 8. Time profiles of 7-hydroxycoumarin (7-HC) production (monitored by its

583

fluorescence emission intensity) in the dark in the pre-irradiated suspensions of bare TiO2,

584

Pt/TiO2, and Ag/TiO2. Experimental conditions were [catalyst] = 0.5 g/L, [noble metal (Pt or

585

Ag) loading on TiO2] = 3.0 wt%, [coumarin]0 = 1 mM, pH0 =3.0, air-equilibrated, and pre-

586

irradiation (λ > 320 nm) for 1 hour.

587 588

32

ACS Paragon Plus Environment

Page 32 of 33

Page 33 of 33

589

Environmental Science & Technology

TOC graphic

590

33

ACS Paragon Plus Environment