Size-Dependent Activity Trends Combined with in Situ X-ray

May 27, 2016 - Bifunctional oxygen electrocatalysts play a vital role in important energy conversion and storage devices. Cost-effective, abundant, an...
1 downloads 10 Views 3MB Size
Research Article pubs.acs.org/acscatalysis

Size-Dependent Activity Trends Combined with in Situ X‑ray Absorption Spectroscopy Reveal Insights into Cobalt Oxide/Carbon Nanotube-Catalyzed Bifunctional Oxygen Electrocatalysis Bora Seo,†,∥ Young Jin Sa,†,∥ Jinwoo Woo,‡ Kyungjung Kwon,§ Jongnam Park,‡ Tae Joo Shin,⊥ Hu Young Jeong,*,⊥ and Sang Hoon Joo*,†,‡ †

Department of Chemistry and ‡School of Energy and Chemical Engineering, Ulsan National Institute of Science and Technology (UNIST), 50 UNIST-gil, Ulsan 44919, Republic of Korea § Department of Energy & Mineral Resources Engineering, Sejong University, 209 Neungdong-ro, Seoul 05006, Republic of Korea ⊥ UNIST Central Research Facilities (UCRF), Ulsan National Institute of Science and Technology (UNIST), 50 UNIST-gil, Ulsan 44919, Republic of Korea S Supporting Information *

ABSTRACT: Bifunctional oxygen electrocatalysts play a vital role in important energy conversion and storage devices. Costeffective, abundant, and active Co-based materials have emerged as promising bifunctional electrocatalysts for which identifying catalytically active structures under reaction conditions and unraveling the structure−activity relationships are of critical importance. Here, we report the size-dependent (3−10 nm) structure and catalytic activity of bifunctional cobalt oxide nanoparticle (CoOx NP) catalysts for the oxygen evolution reaction (OER) and the oxygen reduction reaction (ORR). In situ X-ray absorption spectroscopy (XAS) revealed that the majority of NPs during OER and ORR were composed of the Co3O4 and CoOOH phases regardless of their particle sizes. The OER activity increased with decreasing NP size, which correlated to the increased oxidation state and larger surface area in smaller NPs, whereas the ORR activity was nearly independent of NP size. These particle size-dependent catalytic activities in conjunction with the in situ XAS results can provide insights into the CoOx-catalyzed bifunctional oxygen electrode reactions. KEYWORDS: cobalt oxide, size effect, bifunctional catalysis, oxygen evolution reaction, oxygen reduction reaction

W

For the design of advanced cobalt oxide-based electrocatalysts, unraveling the nature of the active species and reaction mechanism is of critical importance, and understanding the nanoscale particle size effects can provide important clues. The particle size effects in cobalt (oxide)based catalysts have been established in a number of important reactions, including Fischer−Tropsch synthesis and CO2 hydrogenation.25,26 However, such insights have not yet been gained for bifunctional oxygen electrocatalysis; only a few sporadic works on the size dependency for respective OER or ORR have been reported.27,28 More importantly, an understanding of the size-dependent catalytic activity in symbiosis with in situ spectroscopic characterization can further provide more compelling evidence to establish the property relation-

ith increasing demand for clean energy technologies, renewable energy conversion and storage systems have generated tremendous interest.1,2 Bifunctional oxygen electrocatalysts that can catalyze both oxygen evolution reaction (OER) and oxygen reduction reaction (ORR) are ubiquitous and of pivotal importance in energy devices, such as unitized regenerative fuel cells and metal−air batteries.3−12 The viability of these energy devices is critically dependent on the catalytic performances of bifunctional oxygen electrocatalysts. Both OER and ORR involve the transfer of four electrons, rendering these reactions energetically demanding and sluggish. As such, noble metal-based materials like IrO2, RuO2, and Pt with fast reaction kinetics have been used prevalently as bifunctional oxygen electrocatalysts; however, they are costly and scarce.13,14 In this context, cost-effective and abundant transition metal oxides and hydroxides have emerged as a promising class of catalysts.15−24 Cobalt oxide-based bifunctional electrocatalysts have been of particular interest as economically viable and efficient bifunctional oxygen electrocatalysts.16−19,22−24 © XXXX American Chemical Society

Received: February 24, 2016 Revised: May 4, 2016

4347

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis

Figure 1. Characterizations of the CoOx/CNTs. (a−d) BF-TEM images of (a) CoOx(4.3)/CNTs, (b) CoOx(6.3)/CNTs, (c) CoOx(7.5)/CNTs, and (d) CoOx(9.5)/CNTs. (e−h) Corresponding AR-TEM images and FFT patterns (insets). (i) Histograms of the particle size distributions of the CoOx NPs.

temperature of precursor (Table S1 and Figure S1). Highresolution TEM (HR-TEM) images (Figure S1e−h) demonstrated that all of the NPs consisted of the crystalline CoO phase (cubic, a = 4.22 Å). CoOx NPs were then anchored onto the acid-treated CNTs with ultrasonication, followed by mild thermal annealing. We chose undoped CNTs rather than N-doped CNTs as the support material because the presence of both CoOx and nitrogen synergistically enhances catalytic activity via the formation of Co−N bonding, potentially hampering the extraction of catalytic activity exclusively from CoOx.16,30,31 The nominal content of Co in the CoOx/CNTs was around 12 wt %, as confirmed by inductively coupled plasma optical emission spectrometry (Table S1). Scanning electron microscopy (SEM) images (Figure S2) of the CoOx/CNTs revealed the preserved morphology after the loading of the CoOx NPs. TEM images of the CoOx/CNTs (Figure 1a−d) indicated that the CoOx NPs were successfully attached and uniformly distributed on the CNTs. The average particle sizes of the CoOx NPs in the four CoOx/CNTs were 4.3, 6.3, 7.5, and 9.5 nm (Figure 1i and Table S1). The size of the smallest CoOx NPs increased from that of the pristine NPs (3.0 nm) due to the phase transformation from metallic Co to Co3O4 during the annealing step and the smaller density of Co3O4 than that of metallic Co phase. Hereafter, these CoOx/CNTs are denoted as CoOx(4.3)/CNTs, CoOx(6.3)/CNTs, CoOx(7.5)/CNTs, and CoOx(9.5)/CNTs. The atomic-resolution TEM (ARTEM) images (Figure 1e−h and insets) showed that the smallest NPs had crystalline spinel structures of Co3O4, indicating the phase change from CoO to Co3O4 after loading onto the CNTs, whereas the other NPs remained in the same CoO phase, as evidenced by the AR-TEM images and the corresponding FFT patterns.

ships between structure (size, shape, and/or composition) and catalysis.29 Herein, we report the nanoscale size-dependent structure and catalytic activity of bifunctional electrocatalysts based on cobalt oxide nanoparticles (CoOx NPs) for both OER and ORR for the first time. CoOx NPs with four different particle sizes, tunable from 3 to 10 nm, were synthesized and deposited on acid-treated carbon nanotubes (CNTs), affording CoOx/ CNTs model catalysts to investigate bifunctional electrocatalysis in alkaline media. In situ X-ray absorption spectroscopy (XAS) analysis revealed that the composition of the sizecontrolled CoOx NPs was invariably Co3O4 and CoOOH with a small amount of Co(OH)2 under electrochemical OER and ORR conditions. This result suggests that Co(III) species are the key elements for OER, whereas they appear to be side products generated from the oxidation of Co(II) by a peroxide intermediate during ORR. The CoOx/CNT catalysts exhibited increasing OER activity with decreasing NP size, which could be correlated with abundant surface Co(III) species and the large surface area of small CoOx NPs. For ORR, no particle size dependence was found in the kinetic region; CoOx NPs mainly played an auxiliary role, promoting the reduction or disproportionation of peroxide generated from the two-electron transfer pathway of the ORR.



RESULTS AND DISCUSSION Preparation of the CoOx/CNTs model catalysts consisted of (i) the colloidal synthesis of CoOx NPs with different particle sizes,26 (ii) the attachment of prepared NPs to acid-treated CNTs, and (iii) mild annealing to remove residual organic surfactants around the CoOx NPs. Monodisperse, sizecontrolled CoOx NPs with average sizes of 3.0, 6.2, 7.4, and 9.1 nm were obtained by controlling thermal decomposition 4348

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis

Figure 2. (a) Wide-angle XRD patterns of the CoOx/CNTs with patterns for the CoOx standards displayed as vertical bars. The dashed gray line indicates the peak from the CNTs at 43°. (b) Enlarged XRD pattern in the 2θ range of 41−45°. (c) Radial distribution functions (RDFs) of the Co K-edge EXAFS spectra for the CoOx/CNTs and reference materials.

Figure 3. In situ electrochemical XAS analyses at OCV and 1.8 V (OER). (a) In situ XANES spectra of the CoOx/CNTs under OCV and an applied potential of 1.8 V (OER) compared with ex situ XANES spectra. (b) RDFs of the CoOx(4.3)/CNTs at OCV and 1.8 V (OER). Inset: enlarged RDFs for the first Co−O interatomic distance. (c) AR-TEM images and corresponding FFT patterns of the CoOx(9.5)/CNTs before and after the OER durability test, showing the transition of the phase from CoO to Co3O4.

Table 1. Phase Composition and Average Co Oxidation State of the CoOx NPs in the CoOx/CNTs As Determined by Linear Combination Fitting of the in Situ XANES at OCV, 1.8 V, and 0.6 V (vs RHE) sample

condition

Co3O4

CoOOH

CoO

Co(OH)2

average Co oxidation state

CoOx(4.3)/CNTs

OCV 1.8 V 0.6 V OCV 1.8 V 0.6 V OCV 1.8 V 0.6 V OCV 1.8 V 0.6 V

0.61 0.55 0.26 0.32 0.54 0.20 0.19 0.44 0.44 0.00 0.29 0.57

0.20 0.42 0.56 0.15 0.41 0.65 0.30 0.50 0.50 0.47 0.49 0.22

0.00 0.01 0.00 0.18 0.03 0.00 0.09 0.00 0.00 0.00 0.00 0.07

0.19 0.02 0.18 0.35 0.02 0.17 0.43 0.06 0.06 0.53 0.22 0.14

2.6 2.8 2.8 2.4 2.8 2.8 2.4 2.8 2.8 2.5 2.7 2.6

CoOx(6.3)/CNTs

CoOx(7.5)/CNTs

CoOx(9.5)/CNTs

diffraction peaks at 2θ = 36.5°, 42.8°, and 61.5° were commensurate with those of the CoO standard appeared in CoOx(6.3)/CNTs, CoOx(7.5)/CNTs, and CoOx(9.5)/CNTs.

X-ray diffraction (XRD) patterns (Figure 2a) of all the samples showed a common diffraction peak at 2θ = 25.7° coincident with those that appeared for the CNTs. The 4349

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis

Figure 4. In situ electrochemical XAS analyses at OCV and 0.6 V (ORR). (a) In situ XANES spectra of the CoOx/CNTs under OCV and an applied potential of 0.6 V (ORR) compared with ex situ XANES spectra. (b) RDFs of the CoOx/CNTs at 0.6 V.

CoOx/CNTs. The partial phase change from CoO to Co3O4 under OER conditions was further confirmed by an HR-TEM image of the CoOx(9.5)/CNTs after the OER (Figure 3c). The structural transformation was further observed by in situ EXAFS spectra of the CoOx(4.3)/CNTs (Figure 3b). The RDF curve under OER potential compared to that under OCV revealed three major changes. First, a slight shrinkage in Co−O bond length was observed under the OER potential for CoOx(4.3)/CNTs when compared to that under OCV (inset of Figure 3b). This is an indication of an increase in the oxidation state,32 possibly from Co3O4 to CoOOH. Second, the RDF peak intensities for Co−O and Co−Co increased, which correspond to the increase in the amount of adjacent di-μ-oxobridged CoO6 octahedra composing CoOOH33 that have been identified as an active phase for OER.34,35 Finally, under OER potential, the intensity of third major RDF peak intensity at 3.04 Å decreased, and the fourth major peak at 4.69 Å was negatively shifted, which indicated the diminishment of Co3O4 characteristic peaks as well as the evolution of CoOOH-like peaks. From these observations, we concluded that the surfaces of the CoOx NPs may be covered with a few layers of CoOOH because CoOOH is a thermodynamically stable phase under oxidizing potentials.36−38 We noted that the oxidation of the CoOx NPs occurred even at the OCV, as revealed by distinct changes between ex situ XANES spectra (solid curves in Figure 3a) and in situ XANES spectra at the OCV (long dashed curves in Figure 3a). We attributed it to the intermediate range of OCV (0.9−1.1 V vs RHE), which is between ORR and OER potentials. This phase transformation under nonelectrocatalytic conditions is beyond of the scope of this work and is subject to detailed investigation. When the XANES spectra were measured under the ORR potential (0.6 V vs. RHE), all of the CoOx/CNTs samples exhibited Co3O4/CoOOH-like XANES spectra, similar to the results of the XANES spectra taken under the OER potential, indicating the evolution of the Co(III) species during the ORR (Figure 4a). To access more detailed information, we scrutinized the XANES data with LCF analyses. The LCF analysis of in situ XANES at 0.6 V revealed that the CoOx NPs exist in Co3O4 and CoOOH phases with a small amount of

In the case of the CoOx(4.3)/CNTs, different diffraction peaks (2θ = 31.8°, 36.8°, 44.9°, 59.4°, and 65.2°) were observed and could match those of the Co3O4 standard. The radial distribution function (RDF) from Fourier transform of k3weighted extended X-ray absorption fine structure (EXAFS) spectrum (Figure 2b) of CoOx(4.3)/CNTs exhibited major peaks at 1.54, 2.48, and 3.06 Å corresponding to the Co−O, Cooct−Cooct, and Cotet−Cotet/Cotet−Cooct pairs of Co3O4, respectively.22 The other three samples showed peaks at 1.75 and 2.67 Å, which were similar to those of bulk CoO. As revealed by TEM, XRD, and EXAFS analyses, the CoOx NPs in the CoOx(4.3)/CNTs were mainly composed of the Co3O4 phase, whereas the CoOx NPs in the other three samples consisted of the CoO phase. The structural changes of the CoOx NPs under OER and ORR conditions were scrutinized using in situ electrochemical XAS with a homemade spectroelectrochemical cell. Figure 3a depicts in situ Co K-edge X-ray absorption near-edge spectroscopy (XANES) spectra of the CoOx/CNTs measured at open circuit potential (OCV) and OER potential (1.8 V vs reversible hydrogen electrode, RHE) in 0.1 M KOH electrolyte. Under the OER potential, all the samples exhibited similar XANES spectra resembling that of Co3O4 and CoOOH regardless of the CoOx NP size. We analyzed the in situ XANES spectra to understand the phases comprising the CoOx NPs under each potential with linear combination fitting (LCF) analyses (Figure S3). The resulting phase compositions and average Co oxidation states calculated by the relative amount of each phase are summarized in Table 1. We found that when the OER potential was applied, the average oxidation state of Co increased for all the samples accompanied by the increased amount of CoOOH phase, which is believed to be the active species for the OER. Under OER potential, the increment in the amount of Co3O4 in CoOx(6.3)/CNTs, CoOx(7.3)/CNTs, and CoOx(9.5)/CNTs was also observed. For the CoOx(4.3)/ CNTs, a large amount of Co3O4 was already present at OCV (61%), which was partially transformed to CoOOH, leading to the rise in the Co oxidation state. The analysis of the in situ XANES indicates that the phase transformation occurred from Co3O4 and/or CoO to Co3O4/CoOOH mixed phase in the 4350

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis Co(OH)2 in all samples (Table 1). The detailed numerical analysis revealed that with increased CoOx size the portion of Co3O4 increased whereas that of CoOOH decreased. The comparison of average oxidation state indicated a slightly lower oxidation state of the CoOx(9.5)/CNTs than that of the other CoOx/CNTs samples, perhaps because of a low surface fraction of the CoOx NPs that can participate in phase transformation (Table 1). The above XANES results under ORR potential could be further substantiated by in situ EXAFS results, which also identified Co3O4 and CoOOH phases as major species (Figure 4b). In the RDFs of the in situ EXAFS spectra at 0.6 V, the first two peaks, corresponding to Co−O and Co−Co interatomic distances appeared for all of the CoOx/CNTs. The other peaks at around 3.1 and 4.5 Å were also observed, which are known to originate from the Co3O4 and CoOOH phases (indicated by dashed lines in Figure 4b). The similar peak intensities between the samples except for the CoOx(9.5)/CNTs indicated that they had almost identical local structure. The different structural properties of the CoOx(9.5)/CNTs could be attributed to a lower portion of CoOOH and larger amount of Co3O4 comprising the CoOx(9.5)/CNTs than those of the other samples, as evidenced by LCF analysis (Table 1). When the applied potential was changed from OCV to ORR potential (0.6 V), the average oxidation state increased from ∼ +2.5 to ∼ +2.8, as revealed by the LCF analyses (Table 1 and Figure S3). The LCF analysis results indicated that Co(II) and Co(III) species were present in a ratio of around 1:1 at OCV, and Co(III) became the major species under the ORR potential. Some previous works consistently suggested that Co(II) on CoOx is relevant to catalytically active species for the ORR.39−41 In another early work, theoretical calculations suggested that the ORR on CoOOH is initiated over the Co(II) site followed by oxidation of the Co(II) to Co(III) species, which return to the Co(II) species for the next catalytic turnover.42 However, our in situ XAS result could not confirmatively conclude that the Co(III) species evolved at 0.6 V represents the catalytic intermediate in the ORR. As discussed in the electrochemical analysis below, in the CoOx/ CNTs, O 2 is initially reduced to peroxide catalyzed predominantly by the CNTs and subsequently the CoOx NPs disproportionate to the peroxide. The peroxide intermediate likely oxidizes the initial Co(II) species to Co(III) species concomitant to the peroxide disproportionation. Next, the redox behavior of the samples was assessed via cyclic voltammetry (CV) in N2-saturated 1 M KOH (Figure 5 and Figure S5). The CV results showed anodic peaks I, II, and III, which could be attributed to the oxidation of Co(II) to Co(III), the phase transition from Co3O4 to CoOOH, and the oxidation of Co(III) to Co(IV), respectively.41,43 The consecutive CV curves of the CoOx/CNTs, compiled from up to 5 sequential scans, revealed the gradual decrease of anodic peak II and nearly constant peak III, indicating an irreversible transition of surface Co3O4 to CoOOH and the reversible transition of Co(III) to Co(IV), respectively. Frei and co-workers reported that Co(III) species act as an initiator for the OER process.34 Stahl and co-workers suggested that the key process in the OER is related to the reversible interconversion between Co(III) and Co(IV).44 The reversible redox transition between Co(III) and Co(IV) in the CoOx/ CNTs-catalyzed OER was also observed by the presence of anodic peak III in consecutive CV scans (Figure S4), which is consistent with these previous works. Significantly, in the first

Figure 5. Redox properties of CoOx/CNTs. (a) First CV curves over a potential range of 0.05−1.5 V (vs RHE) at a scan rate of 20 mV s−1 in N2-saturated 1 M KOH. (b) An enlarged view around anodic peak II (indicated by the dotted box in a). (c) Potentials at the anodic peak II positions versus particle size.

CV curves, a negative shift of anodic peak II was observed with increasing CoOx NP size (Figure 5), which could be associated with the relatively lower oxidation state of larger CoOx NPs. The result indicates that CoOx NPs in CoOx(4.3)/CNTs are present in a more oxidized form than in the other three samples. They can serve more abundant Co(III) species, thereby facilitating the interconversion between Co(III) and Co(IV), which is considered as the active species in the OER. The CV results align well with the results from TEM, XRD, and EXAFS. However, the CV results are not well-correlated to the in situ XAS results because the in situ XAS spectra were taken after applying potential for 1 h, which can induce considerable phase transformation from Co3O4/CoO to CoOOH/Co3O4 in the CoOx NPs. This preconditioning could lead to the results that the CoOx NPs mainly consisted of Co3O4/CoOOH regardless of their particle sizes (Table 1 in the original manuscript). Hence, the experimental conditions for in situ 4351

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis

Figure 6. Electrochemical analyses of the CoOx/CNTs. (a) Polarization curves and (b) Tafel plots for the OER. (c) Polarization curves and (d) Tafel plots for the ORR.

CNTs almost overlapped (Figure 6d). This result suggested that the CoOx NPs did not improve the intrinsic ORR activity; rather, CoOx appeared to promote the reduction or disproportionation of peroxide species generated by the CNTs, as evidenced by the greater diffusion-limited currents of the CoOx/CNTs compared to those of the CNTs. In addition, the similar Tafel slopes might have indicated that the reaction rates of the CoOx/CNTs and CNTs were limited by the same step, which occurred on the CNTs. Therefore, we hypothesized that the ORR was initiated by the CNTs via the two-electron transfer pathway and that the CoOx NPs mainly played an auxiliary role, promoting the reduction or disproportionation of the generated peroxide. The fast and repetitive disproportionation of peroxide by CoOx led to the quasi-four-electron pathway for the ORR.28,47 We again confirmed the particle size independence of the ORR activity trend with CoOx/CNTs with a higher CoOx loading (Table S3 and Figure S5). The ORR activities of 32% CoOx(4.3)/CNTs, 35% CoOx(6.3)/CNTs, and 36% CoOx(9.5)/CNTs were almost the same regardless of their particle sizes, as evidenced by their overlapping LSV curves. It was also found that the high-loading 32% CoOx(4.3)/CNTs showed only marginal improvement of the ORR activity in the kinetic region (i.e., 0.7−0.85 V) compared with the low-loading 9.4% CoOx(4.3)/ CNTs. We found that the previously reported, high-performance CoOx/carbon hybrid catalysts usually contained nitrogen,16,23,30 potentially creating Co−N moieties, which are known to be highly active species for the ORR. The rather low ORR performances of our CoOx/CNTs are rationalized by the absence of nitrogen. We highlight the importance of preparing N-free metal oxides/carbon hybrid model catalysts to

XAS could not reflect the initial oxidation state of Co of fresh CoOx/CNTs. In contrast, under potentiodynamic conditions of the CV scans, the step-by-step transitions of oxidation states in CoOx NPs could be detected. Electrocatalytic OER and ORR activities were measured using the rotating disk electrode (RDE) in 0.1 M KOH (Figure 6 and Table S2). In the series of CoOx/CNTs, the OER activities increased with decreasing NP size; the potentials required to reach a current density of 10 mA cm−2 were 1.62, 1.64, 1.65, and 1.68 V for the CoOx(4.3)/CNTs, CoOx(6.3)/ CNTs, CoOx(7.5)/CNTs, and CoOx(9.5)/CNTs, respectively (Figure 6a). The greater OER activities in smaller CoOx NPs were likely attributed to the large active surface areas27 and the abundance of Co(III) that is the main source for the active Co(IV) species, initiating the OER as confirmed by the CV anodic peak (Figure 5).36,44 The Tafel slopes were 69, 69, 73, and 80 mV dec−1 for the CoOx(4.3)/CNTs, CoOx(6.3)/CNTs, CoOx(7.5)/CNTs, and CoOx(9.5)/CNTs, respectively (Figure 6b). A smaller Tafel slope was obtained for the smaller CoOx catalyst, indicating more favorable reaction kinetics. In CoOxbased OER catalysts, high oxidation state Co(IV) centers have been suggested to play an essential role in catalyzing the OER.36,37,45,46 Active Co(IV) species arise from the oxidation of Co(III) with oxidizing potential, as evidenced by the anodic peak III of the CVs (Figure S4). Unlike the case of the OER conditions, the CoOx/CNTs demonstrated nearly identical activities for the ORR independent of the CoOx NP size (Figure 6c). The onset potentials and diffusion-limited currents of the CoOx/CNTs were almost the same regardless of the NP sizes. Interestingly, the onset potential of the CoOx/CNTs was the same as those of the CNTs, and the Tafel plots of the CoOx/CNTs and 4352

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis

was heated to one of the desired temperatures (164, 168, 176, or 182 °C) at a heating rate of 5 °C min−1 under an Ar atmosphere. Once stabilized at the desired temperature, 1.5 mL of Co2(CO)8 (Sigma-Aldrich) in DCB (0.5 M) was quickly injected into the heated solution. The transparent, brownish solution immediately turned black, indicating the formation of colloidal nanoparticles. This colloidal suspension was aged for 20 min prior to stopping the heating and then cooled in a flow of air. For the cobalt nanoparticles to be separated, 5 mL of DCB and 25 mL of 2-propanol (99%, Sigma-Aldrich) were added to the suspension, followed by centrifugation at 8000 rpm for 15 min. After discarding the supernatant, precipitated nanoparticles were dispersed in chloroform (CHCl3, Samchun). Acid Treatment of the CNTs. First, 2.5 g of carbon nanotubes (CNTs, Carbon Nanomaterial Technology Company, MR 99) were mixed with 380 g of 6 M HCl (Samchun), and the mixture was stirred at 80 °C for 12 h. The suspension was filtered, washed with copious amounts of deionized (DI) water until the pH of the filtrate reached 7, and dried at 60 °C. The HCl-treated CNTs were subsequently washed with 390 g of 6 M HNO3 (Samchun). Synthesis of the CoOx/CNTs. The CoOx nanoparticles (NPs) loaded on the CNTs (CoOx/CNTs) were synthesized as follows. First, 350 mg of CNTs were dispersed in 50 mL of CHCl3 in a 100 mL Erlenmeyer flask. The flask was covered with Parafilm to avoid evaporation of the CHCl3. After stirring for 15 min, 38.9 mg of the as-prepared cobalt nanoparticles, dispersed in CHCl3, were added dropwise to the solution. Subsequent sonication in ice water for 3 h led to the homogeneous dispersion of CoOx nanoparticles on CNTs. The product was collected by centrifugation and dried at 60 °C. Finally, the surfactants surrounding the nanoparticles were removed following a previously reported method.48 The dried powder was annealed by raising the temperature from room temperature to 185 °C for 2 h and maintained at that temperature for 5 h under air. For comparative purposes, acidtreated CNTs without CoOx were also annealed at 185 °C for 5 h in the same manner as above. Synthesis of CoOOH. CoOOH was synthesized for use as a reference material for the X-ray absorption spectroscopy study, as previously reported.49 First, Co(OH)2 powder (Sigma-Aldrich) was dispersed in 40 mL of DI water. Next, 10 mL of 8 M NaOH was added dropwise, and 4 mL of H2O2 (30%, Sigma-Aldrich) was subsequently added with vigorous stirring. This reaction produces an explosive amount of O2 gas. The resulting dark-brown-colored suspension was stirred at 45 °C for 28 h. The product was filtered, washed with DI water several times, and dried overnight at 60 °C. The resulting CoOOH was found to be phase-pure with large crystallite size as revealed by XRD (Figure S9). Characterization Methods. Scanning electron microscopy (SEM) analysis was conducted on a Hitachi S-4800 scanning electron microscope operating at 10 kV. High-resolution transmission electron microscopy (HR-TEM) images were taken on a JEOL JEM-2100 electron microscope at an acceleration voltage of 200 kV. Atomic-resolution TEM (ARTEM) images were taken with a low-voltage spherical aberration-corrected TEM (FEI Titan3 G2 60−300 with an image Cs corrector) with an acceleration voltage of 80 kV. Xray powder diffraction (XRD) patterns were obtained with a high power X-ray diffractometer (Rigaku) equipped with Cu Kα radiation and operated at 40 kV and 200 mA. Wide-angle XRD patterns were measured in a 2θ range from 10° to 80° at a

investigate the particle size-dependent ORR activity originating from only metal oxides. Long-term stability is a critical factor for applying electrocatalysts in practical applications. Chronopotentiometry (CP) was conducted at a current density of 5 mA cm−2 (Figure S6). The CoOx/CNTs catalysts exhibited excellent durability with little decay in the OER activity and maintenance of their structures over 400 min of operation. TEM images after the CP measurements revealed that the phase of the CoOx NPs was maintained as Co3O4 with retained particle sizes for the CoOx(4.3)/CNTs (Figure S7b). However, a long-term test under an applied OER potential resulted in the structural change from CoO to Co3O4 for the largest CoOx NPs, as revealed by the FFT patterns in Figure S7d, which was consistent with the in situ XAS measurement results. In addition, we investigated the chemical states of Co before and after chronopotentiometry (CP) using X-ray photoelectron spectroscopy (XPS) (Figure S8). For the CoOx(4.3)/CNTs, the XPS spectra before and after the CP runs almost overlapped. For the CoOx(9.5)/CNTs, satellite peaks around 787 and 803 eV (indicated by dotted lines) disappear after OER, indicating a decrease in the number of surface Co(II) species via the oxidation of Co(II) species to Co(III). The results support well the conclusions drawn from the other characterizations, including TEM, XRD, XAS, and CV curves.



CONCLUSIONS In summary, we have investigated the size-dependent NP structures and catalytic activities of the CoOx/CNTs for bifunctional oxygen electrocatalysis. In situ electrochemical XAS measurements demonstrated that Co3O4 and CoOOH were the major species regardless of the CoOx particle size under both OER and ORR conditions. The OER activities of the CoOx/CNTs increased with decreasing particle size, which could be associated with the increased oxidation state and larger surface area of the smaller NPs. The ORR activity was independent of the CoOx NP size, revealing the auxiliary role of CoOx on the CoOx/CNTs for the reduction or disproportionation of peroxide rather than the reduction of oxygen. Combining in situ XAS with electrocatalytic activity trends, we suggested that the dominant Co(III) species are related to active intermediates for the OER, whereas they appear to be side products generated from the oxidation of Co(II) by a peroxide intermediate during the ORR. This work can offer a platform to explore the structural changes and reaction pathways of cobalt oxide for the rational design of advanced bifunctional oxygen electrocatalysts.



MATERIALS AND METHODS

Synthesis of Size-Controlled Cobalt Oxide Nanoparticles. Cobalt oxide nanoparticles were synthesized via a previously reported method26 with some modifications. For the synthesis, standard Schlenk techniques were used, and all manipulations with the cobalt carbonyl precursor were performed in a glovebox. First, 73 μL of oleic acid (99%, Sigma-Aldrich) in a 100 mL round-bottom flask were evacuated for 10 min and saturated with Ar. Subsequently, 7.5 mL of anhydrous o-dichlorobenzene (DCB, 99%, Sigma-Aldrich) were added. The flask was equipped with a long Liebig condenser, gas-volume spacer, and gas-release line to accommodate the large volume of CO, which was produced upon decomposition of the carbonyl precursor. With vigorous stirring, the mixture 4353

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis scan rate of 4° min−1. The Co-metal content of each sample was analyzed using an inductively coupled plasma optical emission spectrometry (ICP-OES) analyzer (Varian). The ICPOES analysis results are summarized in Table S1. X-ray Absorption Spectroscopy Experiments. X-ray absorption spectroscopy (XAS) experiments were conducted on the Beamlines 6D and 10C of the Pohang Accelerator Laboratory (PAL) in South Korea with a beam energy and current of 3 GeV and 300 mA, respectively. X-ray photon energy was monochromatized with a Si(111) double-crystal monochromator, which was detuned by around 15 and 30% at the 6D and 10C beamlines, respectively, to remove high-order harmonics. In situ XAS spectra were obtained by using a homemade spectroelectrochemical cell in fluorescence mode. Catalyst ink was dropped and dried on a piece of carbon fiber paper and contacted with the electrolyte (0.1 M KOH) in the cell. In situ XAS measurement at OCV was first conducted, and the subsequent XAS scan was then performed after applying ORR (0.6 V vs RHE, iR-corrected) or OER (1.8 V) potential for 1 h to give enough time for phase transformation. Background removal and normalization of the spectra were carried out by using IFEFFIT (Athena) software.50 Electrochemical Measurements. Electrochemical characterization of the catalysts was performed using an IviumStat electrochemical analyzer at room temperature (25 °C) and atmospheric pressure using a three-electrode system. A graphite counter electrode and a Hg/HgO reference electrode were used. All potentials in this report were converted to the reversible hydrogen electrode (RHE) scale. A rotating ring-disk electrode (RRDE) composed of a glassy carbon (GC) disk (4 mm in diameter) and a Pt ring was used as a working electrode. The RRDE was polished with a 1.0 μm alumina suspension and then with a 0.3 μm suspension to generate a mirror finish. The catalyst ink was prepared by mixing catalyst (7.5 mg), neutralized Nafion (0.2 mL), DI water (0.1 mL), and absolute ethanol (0.9 mL) with sonication for at least 1 h. Neutralized Nafion was prepared by mixing 0.1 M NaOH (99.99%, Sigma-Aldrich) and Nafion (5 wt %, SigmaAldrich) in a ratio of 1:2 (v:v), considering the proton concentration of Nafion (∼0.05 M), to minimize any transformation of the catalyst during the ink preparation.51 Next, 3 μL of the catalyst ink was pipetted with a microsyringe and deposited onto the GC electrode and dried at 70 °C for 2 min. The catalyst loading was 0.15 mg cm−2. For the redox properties of the samples to be investigated, cyclic voltammetry (CV) from 0.05 to 1.50 V (vs RHE) was conducted in N2-saturated 1 M KOH at a scan rate of 20 mV s−1 (Figure 5 and Figure S5). Before the activity measurements, electrochemical impedance spectroscopy (EIS) was conducted around an open circuit potential with a potential amplitude of 10 mV from 10000 to 1 Hz. Series resistance was determined at a high frequency intercept on the x axis (real part) of the EIS spectra, which was used to correct the iR-drop. The electrocatalytic activity toward the oxygen evolution reaction (OER) was obtained from 10 CV cycles in the range of 1.2 to 1.8 V (vs RHE) at a scan rate of 20 mV s−1 with an electrode rotating at 1600 rpm. The OER measurement was independently carried out three times, and the cathodic and anodic currents were averaged. The averaged and iRcompensated 10th CV scans are displayed in the report. Linear sweep voltammetry (LSV) polarization curves for the oxygen reduction reaction (ORR) were obtained by sweeping the potential from 1.1 to 0.2 V (vs RHE) at a scan rate of 5 mV s−1

in O2-saturated 0.1 M KOH with O2 bubbling at a rotating speed of 1600 rpm. The ORR measurements were independently repeated three times, and the averaged and iRcompensated data are presented. For the evaluation of the kinetics for the ORR, the kinetic current was extracted from the equation 1 1 1 = + I IK IL

where I, IK, and IL are the measured current, kinetic current, and diffusion-limited current, respectively. The logarithmic plot of the kinetic current density (just the current density in the case of the OER) versus the overpotential gives a linear Tafel plot η = −b log(JK ) + b log(J0 )

where η, b, JK, and J0 are the applied overpotential, Tafel slope, kinetic current density, and exchange current density, respectively.



ASSOCIATED CONTENT

S Supporting Information *

The Supporting Information is available free of charge on the ACS Publications website at DOI: 10.1021/acscatal.6b00553. Average particle sizes, OER and ORR activities, Co contents, TEM images and FFT patterns, SEM images, XANES and XPS spectra, CV and chronopotentiometry curves, and XRD patterns (PDF)



AUTHOR INFORMATION

Corresponding Authors

*E-mail: [email protected] (H.Y.J.). *E-mail: [email protected] (S.H.J.). Author Contributions ∥

B.S. and Y.J.S. contributed equally to this work.

Notes

The authors declare no competing financial interest.



ACKNOWLEDGMENTS This work was supported by the National Research Foundation (NRF) of Korea (2013R1A1A2012960, 2015M1A2A2056560), the KETEP funded by the Ministry of Trade, Industry, & Energy (MOTIE, 20133030011320), and the KEIT funded by the MOTIE (10050509). B.S. and Y.J.S. acknowledge the Global Ph.D. Fellowship (2013H1A2A1032647 to B.S. and 2013H1A2A1032644 to Y.J.S.). The EXAFS experiments performed at the Beamlines 6D and 10C of Pohang Accelerator Laboratory (PAL) were supported in part by the Ministry of Education and POSTECH.



REFERENCES

(1) Cook, T. R.; Dogutan, D. K.; Reece, S. Y.; Surendranath, Y.; Teets, T. S.; Nocera, D. G. Chem. Rev. 2010, 110, 6474−6502. (2) Chu, S.; Majumdar, A. Nature 2012, 488, 294−303. (3) Park, S.; Shao, Y.; Liu, J.; Wang, Y. Energy Environ. Sci. 2012, 5, 9331−9344. (4) Cao, R.; Lee, J.-S.; Liu, M.; Cho, J. Adv. Energy Mater. 2012, 2, 816−829. (5) Katsounaros, I.; Cherevko, S.; Zeradjanin, A. R.; Mayrhofer, K. J. J. Angew. Chem., Int. Ed. 2014, 53, 102−121. (6) Jiao, Y.; Zheng, Y.; Jaroniec, M.; Qiao, S. Z. Chem. Soc. Rev. 2015, 44, 2060−2086.

4354

DOI: 10.1021/acscatal.6b00553 ACS Catal. 2016, 6, 4347−4355

Research Article

ACS Catalysis (7) Zhang, J.; Zhao, Z.; Xia, Z.; Dai, L. Nat. Nanotechnol. 2015, 10, 444−452. (8) Duan, J.; Chen, S.; Jaroniec, M.; Qiao, S. Z. ACS Catal. 2015, 5, 5207−5234. (9) Mitlitsky, F.; Myers, B.; Weisberg, A. H. Energy Fuels 1998, 12, 56−71. (10) Ng, J. W. D.; Gorlin, Y.; Hatsukade, T.; Jaramillo, T. F. Adv. Energy Mater. 2013, 3, 1545−1550. (11) Bruce, P. G.; Freunberger, S. A.; Hardwick, L. J.; Tarascon, J.-M. Nat. Mater. 2012, 11, 19−29. (12) Cheng, F.; Chen, J. Chem. Soc. Rev. 2012, 41, 2172−2192. (13) Ioroi, T.; Kitazawa, N.; Yasuda, K.; Yamamoto, Y.; Takenaka, H. J. Electrochem. Soc. 2000, 147, 2018−2022. (14) Chen, G.; Bare, S. R.; Mallouk, T. E. J. Electrochem. Soc. 2002, 149, A1092−A1099. (15) Gorlin, Y.; Jaramillo, T. F. J. Am. Chem. Soc. 2010, 132, 13612− 13614. (16) Liang, Y.; Li, Y.; Wang, H.; Zhou, J.; Wang, J.; Regier, T.; Dai, H. Nat. Mater. 2011, 10, 780−786. (17) Cheng, F.; Shen, J.; Peng, B.; Pan, Y.; Tao, Z.; Chen, J. Nat. Chem. 2011, 3, 79−84. (18) Maiyalagan, T.; Jarvis, K. A.; Therese, S.; Ferreira, P. J.; Manthiram, A. Nat. Commun. 2014, 5, 3949. (19) Indra, A.; Menezes, P. W.; Sahraie, N. R.; Bergmann, A.; Das, C.; Tallarida, M.; Schmeiβer, D.; Strasser, P.; Driess, M. J. Am. Chem. Soc. 2014, 136, 17530−17536. (20) Jung, J.-I.; Jeong, H. Y.; Lee, J.-S.; Kim, M. G.; Cho, J. Angew. Chem., Int. Ed. 2014, 53, 4582−4586. (21) Chen, S.; Duan, J.; Bian, P.; Tang, Y.; Zheng, R.; Qiao, S.-Z. Adv. Energy Mater. 2015, 5, 1500936. (22) Sa, Y. J.; Kwon, K.; Cheon, J. Y.; Kleitz, F.; Joo, S. H. J. Mater. Chem. A 2013, 1, 9992−10001. (23) Masa, J.; Xia, W.; Sinev, I.; Zhao, A.; Sun, Z.; Grützke, S.; Weide, P.; Muhler, M.; Schuhmann, W. Angew. Chem., Int. Ed. 2014, 53, 8508−8512. (24) Ma, T. Y.; Dai, S.; Jaroniec, M.; Qiao, S. Z. J. Am. Chem. Soc. 2014, 136, 13925−13931. (25) den Breejen, J. P.; Radstake, P. B.; Bezemer, G. L.; Bitter, J. H.; Frøseth, V.; Holmen, A.; de Jong, K. P. J. Am. Chem. Soc. 2009, 131, 7197−7203. (26) Iablokov, V.; Beaumont, S. K.; Alayoglu, S.; Pushkarev, V. V.; Specht, C.; Gao, J.; Alivisatos, A. P.; Kruse, N.; Somorjai, G. A. Nano Lett. 2012, 12, 3091−3096. (27) Esswein, A. J.; McMurdo, M. J.; Ross, P. N.; Bell, A. T.; Tilley, T. D. J. Phys. Chem. C 2009, 113, 15068−15072. (28) Liu, J.; Jiang, L.; Zhang, B.; Jin, J.; Su, D. S.; Wang, S.; Sun, G. ACS Catal. 2014, 4, 2998−3001. (29) Rosen, J.; Hutchings, G. S.; Lu, Q.; Forest, R. V.; Moore, A.; Jiao, F. ACS Catal. 2015, 5, 4586−4591. (30) Olson, T. S.; Pylypenko, S.; Atanassov, P.; Asazawa, K.; Yamada, K.; Tanaka, H. J. Phys. Chem. C 2010, 114, 5049−5059. (31) Jin, H.; Wang, J.; Su, D.; Wei, Z.; Pang, Z.; Wang, Y. J. Am. Chem. Soc. 2015, 137, 2688−2694. (32) Friebel, D.; Louie, M. W.; Bajdich, M.; Sanwald, K. E.; Cai, Y.; Wise, A. M.; Cheng, M.-J.; Sokaras, D.; Weng, T.-C.; Alonso-Mori, R.; Davis, R. C.; Bargar, J. R.; Nørskov, J. K.; Nilsson, A.; Bell, A. T. J. Am. Chem. Soc. 2015, 137, 1305−1313. (33) Risch, M.; Zaharieva, K. I.; Gerencser, L.; Chernev, P.; Dau, H. J. Am. Chem. Soc. 2009, 131, 6936−6937. (34) Zhang, M.; de Respinis, M.; Frei, H. Nat. Chem. 2014, 6, 362− 367. (35) Plaisance, C. P.; van Santen, R. A. J. Am. Chem. Soc. 2015, 137, 14660−14672. (36) Liu, Y.-C.; Koza, J. A.; Switzer, J. A. Electrochim. Acta 2014, 140, 359−365. (37) Yeo, B. S.; Bell, A. T. J. Am. Chem. Soc. 2011, 133, 5587−5593. (38) Subbaraman, R.; Tripkovic, D.; Chang, K.-C.; Strmcnik, D.; Paulikas, A. P.; Hirunsit, P.; Chan, M.; Greeley, J.; Stamenkovic, V.; Markovic, N. M. Nat. Mater. 2012, 11, 550−557.

(39) Xiao, J.; Kuang, Q.; Yang, S.; Xiao, F.; Wang, S.; Guo, L. Sci. Rep. 2013, 3, 2300. (40) Menezes, P. W.; Indra, A.; González-Flores, D.; Sahraie, N. R.; Zaharieva, I.; Schwarze, M.; Strasser, P.; Dau, H.; Driess, M. ACS Catal. 2015, 5, 2017−2027. (41) Liang, Y.; Wang, H.; Diao, P.; Chang, W.; Hong, G.; Li, Y.; Gong, M.; Xie, L.; Zhou, J.; Wang, J.; Regier, T. Z.; Wei, F.; Dai, H. J. Am. Chem. Soc. 2012, 134, 15849−15857. (42) Johnson Wass, J. R. T.; Panas, I.; Á sbjörnsson, J.; Ahlberg, E. J. Electroanal. Chem. 2007, 599, 295−312. (43) Wu, L.; Li, Q.; Wu, C. H.; Zhu, H.; Mendoza-Garcia, A.; Shen, B.; Guo, J.; Sun, S. J. Am. Chem. Soc. 2015, 137, 7071−7074. (44) Gerken, J. B.; McAlpin, J. G.; Chen, J. Y. C.; Rigsby, M. L.; Casey, W. H.; Britt, R. D.; Stahl, S. S. J. Am. Chem. Soc. 2011, 133, 14431−14442. (45) McAlpin, J. G.; Surendranath, Y.; Dincă, M.; Stich, T. A.; Stoian, S. A.; Casey, W. H.; Nocera, D. G.; Britt, R. D. J. Am. Chem. Soc. 2010, 132, 6882−6883. (46) Song, F.; Hu, X. J. Am. Chem. Soc. 2014, 136, 16481−16484. (47) Liu, J.; Jiang, L.; Tang, Q.; Zhang, B.; Su, D. S.; Wang, S.; Sun, G. ChemSusChem 2012, 5, 2315−2318. (48) Li, D.; Wang, C.; Tripkovic, D.; Sun, S.; Markovic, N. M.; Stamenkovic, V. R. ACS Catal. 2012, 2, 1358−1362. (49) Yang, J.; Liu, H.; Martens, W. N.; Frost, R. L. J. Phys. Chem. C 2010, 114, 111−119. (50) Ravel, B.; Newville, M. J. Synchrotron Radiat. 2005, 12, 537− 541. (51) Suntivich, J.; Gasteiger, H. A.; Yabuuchi, N.; Shao-Horn, Y. J. Electrochem. Soc. 2010, 157, B1263−B1268.

4355