Structure and Luminescence of 2D Dilute Magnetic Semiconductors

The Cd1-xMnxSe·L0.5 species exhibit a strong Mn2+ luminescence (2.12 eV) at room temperature, which is driven by the 2D exciton ground-state transiti...
0 downloads 0 Views 202KB Size
1698

Chem. Mater. 2005, 17, 1698-1703

Structure and Luminescence of 2D Dilute Magnetic Semiconductors: Cd1-xMnxSe‚L0.5 (L ) Diamines) Jun Lu, Shuo Wei, Weichao Yu, Houbo Zhang, and Yitai Qian* Structure Research Laboratory and Department of Chemistry, UniVersity of Science and Technology of China, Hefei, Anhui, 230026, People’s Republic of China ReceiVed September 22, 2004. ReVised Manuscript ReceiVed January 22, 2005

The two-dimensional (2D) dilute magnetic semiconductors Cd1-xMnxSe‚L0.5 (L ) ethylenediamine, or en, and 1,6-hexanediamine, or hda, x ) 0-0.8) were synthesized in an autoclave at 120 °C. Ab initio structure solution from X-ray powder diffraction reveals the host compound CdSe‚hda0.5 (space group, Pbca, a ) 6.8852 Å, b ) 6.7894 Å, c ) 27.4113 Å) is structurally analogous to CdSe‚en0.5, except for a subtle difference in alignment of aliphatic diamine ligandssthe hda molecule deflects from the c axis and inclines toward the b axis. CdSe‚L0.5 shows well-defined UV absorption and emission peaks, which is attributed to a 2D exciton band edge transition due to size confinement effect in the c direction and the only photoemission level is the 2D exciton ground state with a long lifetime (7 µs) and intrinsic line width (177 meV) at room temperature. When Cd2+ is partly substituted by Mn2+, a strong Mn2+-related luminescence peak at 2.12 eV (584 nm) is obtained at room temperature, which can be assigned to Mn2+ internal transition (4T1 f 6A1); its excitation peak overlaps with the photoemission peak of the 2D exciton ground state which indicates that the Mn2+ emission is driven by the 2D exciton ground-state transition. For x ) 0.02, the photoluminescence intensity of Cd1-xMnxSe‚hda0.5 reaches maximum and enhances 28 times compared with that of Cd1-xMnxSe‚en. When x < 0.05, the Mn2+ luminescence is a characteristic single-exponential decay process with a well-defined constant lifetime of 375 µs. Electron spin resonance spectra show that Mn2+ substitutes Cd2+ ion and forms a [MnSe3N] coordination tetrahedron and that there are isolated Mn2+ luminescence centers in Cd1-xMnxSe‚hda0.5 (x < 0.05), which is the key factor for their stronger luminescence character compared to Cd1-xMnxSe‚en0.5.

1. Introduction Manganese-doped II-VI group compounds are typical diluted magnetic semiconductors (DMS), which have magnetic properties resulting from the paramagnetic Mn ion and the optical and electrical properties mostly derived from the host semiconductor lattice. Because of the s,p-d exchange interaction between band electron/hole and Mn2+ 3d5 electron,1-4 the DMS show outstanding magneto-optical properties such as giant Faraday rotation effect near the band edge, giant exciton Zeeman splitting, and a magnetic polaron state.5-7 These properties make it possible to fabricate high-performance microstructures of optoelectronic devices. Recently, there were considerable interests in the research on the nanostructures of DMS (quantum wells, quantum wires, and quantum dots), which were expected to show varieties of the optical phenomena due to the coexistence of quantum confinement effect and the exchange interaction.8 For instance, * To whom correspondence may be addressed. E-mail: [email protected].

(1) Bartholomew, D. U.; Furdyna, J. K.; Ramdas, A. K. Phys. ReV. B 1986, 34, 6943. (2) Oh, E.; Bartholomew, D. U.; Ramdas, A. K.; Furdyna, J. K.; Debska, U. Phys. ReV. B 1988, 38, 13183. (3) Dai, N.; Luo, H.; Zhang, F. C.; Samarth, N.; Dobrowolska, M.; Furdyna, J. K. Phys. ReV. Lett. 1994, 67, 3824. (4) Jonker, B. T.; Liu, X.; Chou, W. C.; Petrou, A.; Warnock, J.; Krebs, J. J.; Prinz, G. A. J. Appl. Phys. 1991, 69, 6098. (5) Furdyna, J. K. J. Appl. Phys. 1988, 64, R29. (6) Alonso, R. G.; Suh, E.-K.; Ramdas, A. K.; Samarth, N.; Luo, H.; Furdyna, J. K. Phys. ReV. B 1989, 40, 3720. (7) Goede, O.; Heimbrodt, W. Phys. Stat. Sol. 1988, 146, 11.

ZnS:Mn showed a Mn2+ internal transition (4T1 f 6A1) luminescence at 584 nm with a high quantum efficiency. It was found that the optical properties of Mn2+-doped CdSe nanocrystals are similar to those of undoped nanocrystals in an external magnetic field,9 and 2D Cd1-xMnxSe quantum wells exhibit giant magnetooptical effects and ultrafast exciton dynamics.10,11 The diamine-intercalated layered compounds, including ZnE‚L0.5, CdE‚L0.5, MnSe‚L0.5, and Zn1-xMnxSe‚L0.5 (E ) Se or Te and L ) aliphatic diamines), are a novel type of inorganic/organic (I/O) hybrid structures.12-16 It has been found that Zn1-xMnxSe‚L0.5 has a strong Mn2+-related luminescence and luminescent-enhancement effect for longer (8) Takahashi, N.; Takabayashi, K.; Shirado, E.; Souma, I.; Shen, J. X.; Oka, Y. J. Cryst. Growth 2000, 214/215, 183. (9) Mikulec, F. V.; Kuno, M.; Bennati, M.; Hall, D. A.; Griffin, R. G.; Bawendi, M. G. J. Am. Chem. Soc. 2000,122, 2532. (10) Oka, Y.; Yanata, K.; Okamoto, H.; Takahashi, M.; Shen, J. SolidState Electron. 1998, 42, 1267. (11) Oka, Y. Phys. Solid State 1998, 40, 778. (12) Huang, X.; Li, J. J. Am. Chem. Soc. 2000, 122, 8789. (13) Huang, X.; Li, J. Chem. Mater. 2001, 13, 3754. (14) Heuling, H. R., IV; Huang, X.; Li J.; Yeun, T.; Lin, C. L. Nano Lett. 2001, 1, 521. (15) Huang, X.; Li, J.; Zhang, Y.; Mascarenhas, A. J. Am. Chem. Soc. 2003, 125, 7049. Therein the reported lattice constants of powder CdSe‚en0.5 were a ) 7.0949, b ) 6.795, c ) 16.7212 Å, and V ) 806.17 Å3, and those of powder CdSe‚0.5pda were a ) 20.6660, b ) 6.8900, and c ) 6.7513 Å. (16) Deng, Z. X.; Li, L.; Li, Y. Inorg. Chem. 2003, 42, 2331. Therein, the reported lattice constants of single-crystal CdSe‚en0.5 were a ) 7.0848, b ) 6.7856, c ) 16.6940 Å, and V ) 802.56 Å3.

10.1021/cm048339y CCC: $30.25 © 2005 American Chemical Society Published on Web 03/11/2005

2D Dilute Magnetic Semiconductors

diamines molecules.17 Optical diffuse reflectance measurements indicated that CdSe‚en0.5 (en ) ethylenediamine) has a band gap of 3.41 eV (364 nm) with a large blue shift (∼1.67 eV) compared with that of bulk CdSe (1.74 eV), which can be attributed to the quantum confinement effect of the [CdSe] monolayers. This blushift makes the band gap value of CdSe‚en0.5 greater than the energy of Mn2+ internal transition (4T1 f 6A1, typical of 2.12 eV) and provides possibility for obtaining the Mn2+-related Stokes luminescence in Mn-doped CdSe‚L0.5. Except for the fact that the denity functional approximation (DFA) calculation reveals that the optical characters of these hybrid compounds are determined by the inorganic layer, so far, no other theoretical research has been reported on their band gap structure and optical properties. For MSe‚L0.5 (M ) Zn, Mn), crystallographic analysis revealed that these compounds consist of [MSe] 2D monolayer interconnected by diamine molecules.13 In the lattice of ZnSe‚en0.5, the [ZnSe] monolayer could be viewed as a 2D superlattice of x3a × c of the (110) plane of wurtzitetype ZnSe,17 and CdSe‚en0.5 is isostrucural with Zn and Mn counterparts.16 Although the strong quantum confinement effect was expected, no study has been reported on the exciton transition of [MSe] monolayer, Mn2+ emission, and luminescence decay in Cd1-xMnxSe‚L0.5. In this study, 2D DMS Cd1-xMnxSe‚L0.5 (L ) en and 1,6hexadiamine (hda), x ) 0-0.8) were synthesized in an autoclave at 120 °C. Ab initio structure solution from powder diffraction showed that the CdSe‚hda0.5 with a long c period (c ) 27.4 Å) is structurally analogous to CdSe‚en0.5 (c ) 16.7 Å) except that all hda ligands deflect from the c axis and incline to the b axis. UV absorption/emission features were observed at room temperature for CdSe‚hda0.5, which were assigned to the 2D exciton ground-state transition. Cd1-xMnxSe‚hda0.5 gave Mn2+ emission at 2.12 eV (584 nm) at room temperature, which was excited by the 2D exciton ground-state transition. Luminescence decay curves showed Mn2+ emission is a typical single-exponential decay process with a constant lifetime of 375 µs (x < 0.05). The Mn2+ luminescence intensity of Cd1-xMnxSe‚L0.5 (x ) 0.02) exhibited enhancement effect for L ) hda. The electron spin resonance spectra were employed to obtain an insight about the site symmetry of Mn2+ ions and the luminescenceenhancement effect. 2. Experimental Section 2.1. Synthesis. All chemicals are of analytical-grade purity, purchased from Shanghai Chemical Reagent Co., Ltd, and without further purification. CdSe‚L0.5 (L ) en and hda) were solvothermally synthesized as follows. Cd(CH3CO2)2‚2H2O (5 mmol) and 5 mmol of selenium powder were dissolved into 50 mL of solvent L. The mixture was sealed into 60 mL of Teflon-lined stainless steel autoclave and heated at 120 °C for 7 days, then cooled naturally. The products were washed with distilled water and absolute ethanol and then dried in a vacuum at 60 °C for 2 h. Mn(CH3CO2)2‚4H2O was used as the Mn-doping source, and Cd1-xMnxSe‚L0.5 (x ) 50 ppm -0.8) was prepared in a similar procedure with various molar ratio of Cd2+:Mn2+. (17) Lu, J.; Wei, S.; Peng, Y. Y.; Yu, W.; Qian, Y. T. J. Phys. Chem. B 2003, 107, 3027.

Chem. Mater., Vol. 17, No. 7, 2005 1699 2.2. Component Analysis. Elemental analysis of C, H, and N weight percentages of CdSe‚L0.5 (using a Perkin-Elmer 2400 elemental analyzer) were 5.688, 1.819, 6.223 (calcd. 5.429, 1.821, 6.326 wt %) for L ) en and 14.74, 3.233, 5.525 (calcd.14.443, 3.232, 5.614 wt %) for L ) hda. It can be seen that the obtained data of C, H, and N are consistent with the calculated values in the range of experimental error ((0.3%). Therefore, the chemical stoichiometry of CdSe‚L0.5 can be regarded as accurate. Inductively coupled plasma atomic emission spectra (ICP-AES, using an Atomscan Advantage Spectrometer, Therma Jarrell Ash Co.) were used to determine the Mn contents of Cd1-xMnxSe‚L0.5. For L ) hda, Cd2+:Mn2+ (molar ratio) ) 49/1, 19/1, 9/1, and 1/4, the determined Mn contents were x ) 0.0149 (49/1), 0.0488 (19/1), 0.0829 (9/1), and 0.791 (1/4), respectively. For L ) en, Cd2+:Mn2+ ) 19/1, the determined Mn content was x ) 0.045. Therefore, the Mn2+-doping solvothermal reactions for Cd1-xMnxSe‚L0.5 can be regarded as quantitative. 2.3. Structure Analysis. The powder X-ray diffraction (XRD) pattern of CdSe‚hda0.5 for ab initio structure solution was collected on a MXP 18 AHF X-ray diffractometer (MAC Science Co. Ltd., Japan) with a diffracted beam graphite monochromator and operating at 40 kV and 100 mA (Cu KR, λ ) 1.54184 Å). Data collection was carried out in a step-scan mode with a step-size of 0.02° in the angular range of 4.00-100.00°. The pattern was indexed by the TREOR18a method using program Fullprof18b to the orthorhombic system with unit cell dimensions of a ) 6.8852, b ) 6.7894, c ) 27.4113 Å, V ) 1281.379 Å3. The space group was assumed to be Pbca, and Z ) 8. The crystal structure was solved by direct methods with program EXPO.19 Refinement of the 4800 observations (666 reflections) of the pattern was carried out by the Rietveld method, based on a stoichiometry of CdSe‚hda0.5. The resulting unit cell parameters as well as the atomic parameters and space groups were input as initial values for Rietveld full-pattern refinement in program GSAS.20 After the initial refinement of the scale, background (function #2, Cosine Fourier series 8 terms), and unit cell parameters, profile function #2 was selected (pseudovoigt function with profile coefficients of 18 terms for Simpson’s rule integration21) and the profile parameters LX, LY, trns, asym, shft, GP, stec, ptec, sfec, were refined one by one. The preferred orientation corrections were made by applying spherical harmonics function, and atomic positions were refined finally. Hydrogen atoms and absorption effects were not included in the refinement. The details of the Rietveld refinement are described in Table 1. Nonhydrogen atomic positional parameters are given in Table 2. The reliability indices, a measure of how well the calculated pattern and structure agree with the observed data, are as follows: Rp ) 0.0675, Rwp ) 0.1567, and RF ) 0.1045.22 2.4. Optical Absorption and Photoluminescence (PL) Spectra. The optical absorption spectra of the CdSe‚L0.5 powders dispersed in ethanol were recorded on a Shimadzu 2401pc UV/vis spectrometer. The PL emission and excitation spectra of CdSe‚L0.5 and Cd1-xMnxSe‚L0.5 powders were obtained at room temperature using a Perkin-Elmer LS 55 luminescence spectrometer (Perkin-Elmer (18) (a) Werner, P. E.; Eriksson, L.; Westdahl, M. J. Appl. Crystallogr. 1985, 18, 367. (b) Roisnel, T.; Rodriguez-Carvajal, J. WinPLOTR; May, 2003. (19) Altomare, A.; Carrozzini, B.; Cascarano, G.; Giacovazzo, C.; Guagliardi, A.; Moliterini, A. G. G.; Rizzi, R.; Bura, M. C.; Polidore G.; Camalli, M. EXPO. A package for full-pattern decomposition and for solving crystal structure by direct methods. (20) VonDreele, R. B.; Larson, A. C. GSAS, General Structure Analysis System; Los Alamos National Laboratory: Los Alamos, NM, 2001. (21) (a) Howard, C. J. J. Appl. Crystallgr. 1982, 15, 615. (b) Thompson, P.; Cox, D. E.; Hastings, J. B. J. Appl. Crystallgr. 1987, 20, 79. (22) Details of powder pattern indexing result and Rietveld refinement plot see Supporting Information.

1700 Chem. Mater., Vol. 17, No. 7, 2005

Lu et al.

Table 1. Crystallographic Data for CdSe‚hda0.5 empirical formula Fw space group a, b, c (Å) V (Å3) Z T (K) λ (Å) Fcalc(g cm-3) pattern range (2θ deg) step size (2θ deg) step scan time (s) no. contributing reflns (KR1 + KR2) no. refinement parameters Rwp Rp R(F2)

C3H8NCdSe 1995.79 Pbca (No. 61) 6.8852, 6.7894, 27.4113 1281.379 8 293(2) 1.54056, 1.54439 2.586 4-100 0.02 2 666 66 0.1567 0.0675 0.1045

Table 2. Atomic Coordinates for CdSe‚hda0.5 atom

x

y

z

Cd Se N C(1) C(2) C(3)

0.1000(1) -0.0473(6) -0.0650(2) 0.0369(6) 0.5359(5) -0.0021(4)

0.1925(6) 0.3154(1) 0.3613(1) 0.5265(6) 0.4240(3) 0.6939(9)

0.7178(5) 0.7994(9) 0.6552(2) 0.4308(4) 0.9817(8) 0.3949(2)

Instruments Co., Ltd., USA) with Rhodamine 101 as the interior standard for luminescence intensity, and measurement conditions were identical in all cases; therefore relative intensities can be compared. Luminescence decay curves were obtained by a delay method using a Jobin Yvon Fluorolog 3-TAU luminescence spectrometer (Jobin Yvon Instruments Co., Ltd., France) at room temperature and excitation pulse was produced from a 450-W Xe flash lamp. 2.5. Electron Spin Resonance (ESR) Spectra of Cd1-xMnxSe‚L0.5. Room-temperature ESR spectra of Cd1-xMnxSe‚L0.5 powder were obtained using a JEOL JES-FA200 ESR spectrometer (300 K, 9.063 GHz, X-band). Microwave power employed was 5 mW; sweep width ranged from 2000 to 4000 G. Modulation frequency and modulation amplitude were 100 kHz and 3.5 G, respectively.

3. Results and Discussion 3.1. Structure Description. Figure 1 illustrates a structure view of CdSe‚hda0.5 along the a axis, which is a 3D network with [CdSe] monolayer interconnected by bridging hda molecules with all-trans configuration. The [CdSe] monolayer with a thickness of 0.27 nm and the [CdSe3N] coordination tetrahedra are structurally analogous to CdSe‚ en0.5.16 And the [CdSe] monolayer can also be regarded as a shrunken 2D superlattice (x3a × c) of the (110) plane of wurtzite-type CdSe.17,22 On the other hand, besides the increase of interlayer distance between the [CdSe] monolayer as expected, a subtle structural difference is that all the hda molecules align with deflection from the c axis and inclination toward the b axis, while the en molecules are parallel with the c axis and align vertically to bridge Cd atoms in CdSe‚en0.5. The [CdSe] monolayers supply a 2D system of valence band electrons/holes, which will result in strong quantum-confined effect and exciton transition as described below. 3.2. Absorption and Luminescence Spectroscopy of Undoped CdSe‚hda0.5. Figure 2a shows the room-temperature absorption (1) and emission (2) spectra of the undoped

Figure 1. Structure view of CdSe‚hda0.5 shown along the a axis with the unit cell outlined. The large cyan and red spheres are Cd and Se atoms; small black and blue spheres are C and N atoms, respectively.

CdSe‚hda0.5 which has a well-defined absorption peak at 354 nm (3.50 eV) and a sharp emission peak at 362 nm (3.43 eV) with a Stokes shift of 70 meV and a full width at halfmaximum of 177 meV. Higher energy absorption features can also be resolved at 313 nm (3.96 eV) and 342 nm (3.62 eV) in the absorption spectrum. CdSe‚en0.5 shows similar absorption/emission spectra,22 which indicate that the UV absorption/emission originate from the valence electron transition process in the [CdSe] monolayer, while independent of the length of diamine molecules. The [CdSe] monolayer, separated by aliphatic diamine molecules, has a dimension of 0.27 nm in the c direction, far less than the exciton Bohr radius of CdSe (5.6 nm), which results in the confinement of electron/hole motion in the c direction and the formation of 2D exciton analogous to semiconductor superlattice.23 It is known that, due to 3D quantum confinement, high-quality CdSe colloidal nanocrystals exhibit bandedge exciton absorption/emission with several tens of millielectonvolts of Stokes shift, which is also similar to the current result. Therefore, the UV absorption/emission peaks can be assigned to a c-confined 2D exciton transition of the [CdSe] monolayer, and its transition energy of 2D exciton is greater than that of the smallest CdSe colloidal nanocrystals available (2.6 nm, 2.5 eV9) due to the strong size confinement (0.27 vs 5.6 nm). Compared with the diffuse reflectance spectra of CdSe‚en0.5,15 the absorption spectrum 1 shows the same peak at ∼3.4-3.5 eV but a very long tail (23) Yoffe, A. D. AdV. Phys. 1993, 42, 173.

2D Dilute Magnetic Semiconductors

Chem. Mater., Vol. 17, No. 7, 2005 1701

Figure 2. (a) c-Confined 2D exciton absorption (1) and emission (2) spectra of CdSe‚hda0.5 (excitation wavelength 313 nm). For comparison, the excitation spectrum (3) of Mn2+ emission (584 nm) in Cd0.98Mn0.02Se‚hda0.5 is also shown. (b) Decay curve of 2D exciton luminescence; the inset in (b) is the ln I-t plot to obtain the luminescence lifetime.

to the red, which does not occur in the former. An unavoidable cause for this difference is the specimen measurement state (polycrystalline powder is used in diffuse reflectance experiments, here is the microcrystals suspension). Therefore, it can be expected that the long red tail is related to the interaction between the lamellar polycrystalline particles and dispersive solvent (ethanol), in which the affection of surface states and defects cannot be absolutely excluded for they have been theoretically predicted in ZnTe‚ en0.5 by density functional theory within local density approximation.12 On the other hand, the 3.43-eV (362-nm) emission peak excited by the 3.96-eV (313-nm) photons can also be stimulated by any photons with energy higher than 3.43 eV. This implies that a 2D exciton ground state is the only photoemission exciton energy level in the UV spectral regime. Furthermore, the c dimension of [CdSe] monolayer is identified in the whole lattice and a size-selective treatment is not needed, which is indispensable for colloidal nanocrystals to minimize inhomogeneous spectral broadening and obtain well-defined exciton absorption/emission peaks. Therefore, the peak width of 177 meV for 3.43 eV of emission totally originates from intrinsic homogeneous broadening and implies a narrow 2D exciton ground state in the band gap. The photoemission process of 2D exciton ground state was probed by luminescence decay dynamics, and the decay curve is shown in Figure 2b, which can be fitted into a singleexponential decay with a lifetime of 7 µs (inset)22 within the detectable decay time scale (>1 µs). This is comparable with the band-edge dark exciton lifetime (∼1 µs at 10 K) of wurtzite CdSe nanocrystals and far exceeds that of their bulk counterpart (∼1 ns at 4 K).24 In CdSe nanocrystals, it has been established that the long radiative lifetime of bandedge dark exciton states (dipole forbidden excitons with total angular momentum projection Fm ) (2) results from the intrinsic crystal/shape anisotropy (nonspherical morphology and wurtzite structure lift the degeneracy of band edge excitons) and confinement-enhanced electron-hole exchange (24) (a) Crooker, S. A.; Barrick, T.; Hollingsworth, J. A.; Klimov, V. I. Appl. Phys. Lett. 2003, 82, 2793. (b) Takabayashi, K.; Takahashi, N.; Yagi, I.; Souma, I.; Shen, J. X.; Oka, Y. J. Lumin. 2000, 87-89, 347.

interaction.25 The enhanced exchange effect due to carrier confinement was also confirmed in GaAs/GaAlAs quantum wells,26 and exchange interaction splits the localized exciton in porous silicon, which results in slow radiative states at lower energy.27 The [CdSe] monolayer in CdSe‚L0.5 has strong quantum confinement in the c direction and is structurally derived from wurtzite CdSe (a ≈ x3aW, b ≈ cW, aW, and cW are lattice parameters of wurtzite CdSe). Furthermore, the 2D excition ground state has a comparable radiative lifetime with 3D-confined CdSe QDs; therefore, it is possible that the 2D exciton states were modified by similar factors. Of course, it is absolutely necessary that an in-depth study on the 2D exciton PL at low temperature, and/or in magnetic field, and luminescence dynamics on a sub-microsecond scale be performed, which would be favorable to elucidate the origin of the unique long lifetime 2D excition. On the other hand, for these undoped compounds, no intrinsic luminescence peak at 584 nm was found with excitation at 362 nm. 3.3. Mn2+ Luminescence Spectroscopy of Cd1-xMnxSe‚hda0.5. Figure 3 shows the PL excitation (left) and emission (right) spectra of the isomorphous Cd1-xMnxSe‚L0.5 (x ) 0.02), where the spectra for L ) en was magnified by 5 times for comparison. Both of them show emission peaks at 2.12 eV (584 nm) with a half width of 200 meV, which can be assigned to the typical Mn2+ internal transition (4T1 f 6A1).28,29 The half widths of the emission peaks (200 meV) indicate that the inhomogeneous broadening is unobvious, that is, Mn2+ ions have homogeneous coordination environments. In the excitation spectrum (Figure 2a, curve (25) (a) Nirmal, M.; Norris, D. J.; Kuno, M.; Bawendi, M. G.; Efros, Al. L.; Rosen, M. Phys. ReV. Lett. 1995, 75, 3728. (b) Efros, Al. L.; Rosen, M.; Kuno, M.; Nirmal, M.; Norris, D. J.; Bawendi, M. G. Phys. ReV. B 1996, 54, 4843. (c) Norris, D. J.; Efros, Al. L.; Rosen, M.; Bawendi, M. G. Phys. ReV. B 1996, 53, 16347. (26) (a) Stark, J. B.; Knox, W. H.; Chemla, D. S. Phys. ReV. B 1992, 46, 7919. (b) Potemski, M.; Maan, J. C.; Fasolino, A.; Ploog, K.; Weimann, G. Surf. Sci. 1990, 229, 151. (27) Calcott, P. D. J.; Nash, K. J.; Canham, L. T.; Kane, M. J.; Brumhead, D. J. Lumin. 1993, 57, 257. (28) Norris, D. J.; Yao, Nan; Charnock, F. T.; Kennedy, T. A. Nano Lett. 2001, 1, 3. (29) Norman, T. J.; Magana, D., Jr.; Wilson, T.; Burns, C.; Zhang, J. Z.; Cao, D.; Bridges, F. J. Phys. Chem. B 2003, 107, 6309.

1702 Chem. Mater., Vol. 17, No. 7, 2005

Lu et al.

Figure 5. Mn2+ luminescence lifetime vs Mn contents (x) dependence of Cd1-xMnxSe‚hda0.5.

Figure 3. The PL excitation and emission spectra of Cd1-xMnxSe‚L0.5 (x ) 0.02): (a) L ) hda and (b) L ) en, where the spectra have been magnified by 5 times.

Figure 4. Mn2+ luminescence decay curve of Cd0.98Mn0.02Se‚hda0.5. The inset is the lnI-t plot. The solid circle and line are the experimental and fitted curves, respectively.

3), the narrow excitation peak at 3.41 eV (364 nm) is consistent with the 2D exciton emission peak in CdSe‚hda0.5 (curve 2), indicating that the Mn2+ emission is driven by the 2D exciton ground-state transition of [CdSe] monolayer. The Mn2+ emission intensity is 2 orders of magnitude greater than that of 2D exciton at 362 nm, which shows that Mn2+ is a high-effective acceptor for 2D exciton ground-state transition energy.30 Compared with that of L ) en (7.2), the emission intensity increases 28 times for L ) hda (201), which shows the luminescence-enhancement effect and implies that the long period in c direction is more favor for the enhancement of Mn2+-related emission, which was previously found in Zn1-xMnxSe‚L0.5.17 The Mn2+ luminescence decay curve of Cd0.98Mn0.02Se‚ hda0.5 is shown in Figure 4; the plot of ln I vs decay time (t) could be well-fit into a typical single-exponential decay process with a lifetime of 366 µs (Figure 4, inset). This value (30) Rigby, N. E.; Allen, W. E. J. Lumin. 1988, 42, 143.

is comparable with those of ZnSe:Mn, which are not well established and varied between 30 and 800 µs.31 And the well-defined lifetimes show thermal quenching has no effect on the luminescence at room temperature. The Mn2+ contents dependence of lifetime (Figure 5) reveals, for x ranging from 0.001 to 0.05, the lifetime almost remains constant at 375 µs. Then it decreases slowly in the regime of 0.05-0.01 and drops to 300 µs at x ) 0.1. for x > 0.1; the luminescence intensity decreases obviously, and the decay curve could not be fit into a single-exponential decay process within the time scale of 2 ms; the lifetime could only be estimated from the curve section less than 1 ms and reduces rapidly with the increasing Mn2+ contents and falls to 180 µs at x ) 0.6, which indicates that concentration quench dominates luminescence and results in a complex decay process. It could be expected that the formation of exchange-coupled Mn2+ pairs for higher Mn2+ concentrations (>0.05 in the current study), and due to exchange interaction, the spin selection rule is partially lifted and the lifetime of the Mn2+ emission is reduced. This could explain the Mn2+ luminescence lifetimes of Cd1-xMnxSe‚hda0.5. But no redshift of Mn2+ emission is observed with increasing Mn2+ concentrations, which is an evidence for Mn2+ pair formation in CdSe:Mn. Therefore, it can be concluded that, when x < 0.05, the Mn2+ internal transition (4T1 f 6A1) emission is a typical isolated ion transition process without obvious exchange interaction. 3.4. ESR Spectroscopy of Cd1-xMnxSe‚hda0.5. It is known that the total electron spin of Mn2+ (S ) 5/2) is sensitive to changes of its coordination environment and modifies the crystal field via its spin Hamiltonian parameters; therefore the Mn2+ ESR spectra was used as a probe to study the Mn2+ coordination state and Mn2+-Mn2+ interaction in Cd1-xMnxSe‚L0.5. In parts a and b of Figure 6, only a kind of signal, six well-resolved hyperfine lines, could be observed, which are from the 55Mn nucleus (I ) 5/2) and correspond to the allowed transition (∆mS ) (1, ∆mI ) 0) where mS and mI are electron spin and nuclear spin quantum numbers, respectively. The hyperfine constant A ) 64.5 × 10-4 cm-1 and (31) Suyver, J. F.; Wuister, S. F.; Kelly, J. J.; Meijerink, A. Phys. Chem. Chem. Phys. 2000, 2, 5445.

2D Dilute Magnetic Semiconductors

Chem. Mater., Vol. 17, No. 7, 2005 1703

effect. It seems that the intralayer Mn2+-Mn2+ interaction is also absent in Cd1-xMnxSe‚hda0.5 (x < 0.02) lattice, the reason to which is not very clear and need to study further. 4. Conclusion

Figure 6. Room-temperature Mn2+ ESR spectra of Cd1-xMnxSe‚L0.5 powder specimens: (a) x ) 0.01, L ) hda; (b) x ) 0.02, L ) hda; (c) x ) 0.05, L ) hda; (d) x ) 0.02, L ) en.

line widths of 8 G are consistent with that of tetrahedral coordination Mn2+ in CdSe:Mn crystals,32 which indicates that the doping Mn2+ ions substitute in a Cd2+ site, form [MnSe3N] coordination tetrahedra, and all the Mn2+ ions have a homogeneous coordination environment without Mn2+Mn2+ interaction. Between the six intense lines, several weak lines (seven in Figure 6a) are observed which could be assigned to double spin transition (∆mS ) (1, ∆mI ) (1) where both ms and mI change simultaneously.32 For higher Mn concentration (x ) 0.05, Figure 6c), the second type signal, a broad mainly symmetrical line (line width of 270 G), appears and originates from the electron spin-spin (ms ) 1/2 f ms ) -1/2) interactions, which indicates that Mn2+-Mn2+ interaction has been present,33 and six weak hyperfine lines superimpose the broad main line, which implies that some isolated Mn2+ still exist in the monolayer. This is different from that in Figure 6d (L ) en, for x ) 0.02) where the six hyperfine lines completely disappear and a complex broad line (line width of 440 G) indicating that Mn2+-Mn2+ interaction dominates in Cd0.98Mn0.02Se‚en0.5. An isolate Mn2+ is a strong luminescence center, and the enhancement of Mn2+-Mn2+ interaction due to their close proximity is responsible for the Mn2+ luminescence quench.33 Acording to the ESR spectra, the luminescent-enhancement effect could be explained as isolated Mn2+ can more readily exist in Cd1-xMnxSe‚L0.5 lattice with a long c period (L ) hda), that is, when the diamine molecules became longer, the interlayer distances of [Cd1-xMnxSe] layers increase and the interlayer Mn2+-Mn2+ interaction weakens, and the 2Dconfined character of PL process become more prominent, which undoubtedly contribute to luminescent-enhancement (32) Gonzalez Beermann, P. A.; McGarvey, B. R.; Muralidharan, S.; Sung, R. C. W. Chem. Mater. 2004, 16, 915. (33) Borse, P. H.; Srinivas, D.; Shinde, R. F.; Date, S. K.; Vogel, W.; Kulkarni, S. K. Phys. ReV. B 1999, 60, 8659.

In summary, 2D DMS Cd1-xMnxSe‚L0.5 (L ) en and hda, x ) 0-0.8) have been synthesized in an autoclave at 120 °C. According to the ab initio structure solution from powder XRD pattern, the host compound CdSe‚hda0.5 (Pbca, a ) 6.8852, b ) 6.7894, c ) 27.4113 Å) is structurally analogous to CdSe‚en0.5 except that hda molecules deflect from the c axis and incline to the b axis to bridge two Cd atoms in the adjacent inorganic layer. The strong size confinement effect in the c-direction results in the formation of 2D exciton in CdSe‚L0.5, which is responsible for the UV absorption/ emission features at room temperature. The 2D exciton ground state is the only photoemission exciton energy level available, and its longer lifetime (7 µs) is expected to be related to confinement-enhanced electron-hole exchange interaction in the c direction and the structural anisotropy of [CdSe] monolayer. When Cd2+ is partly substituted by Mn2+, a strong Mn2+ internal transition (4T1 f 6A1) luminescence located at 2.12 eV (584 nm) is obtained at room temperature; its sharp excitation peak overlaps with the 2D exciton emission peak, which indicates that the Mn2+ emission is driven by the 2D exciton ground-state transition. For x ) 0.02, the luminescence intensity of Cd1-xMnxSe‚hda0.5 reaches maximum and enhances 28 times compared with that of L ) en. When x < 0.05, the Mn2+ luminescence is a characteristic singleexponential decay process with a well-defined constant lifetime of 375 µs. ESR spectra show that Mn2+ substitutes the Cd2+ ion in the inorganic monolayer and that isolated Mn2+ luminescence center located in a tetragonal site in Cd1-xMnxSe‚hda0.5 is a key factor for their strong luminescence character (enhancement effect) compared to Cd1-xMnxSe‚en0.5. Our results indicate that Cd1-xMnxSe‚hda0.5 is a typical 2D DMS; it has a strong Mn2+ luminescence due to the highefficiency energy transfer from 2D exciton ground state which forms via strong size confinement effect in the c direction. Their optical properties including the UV absorption and emission, longer lifetime 2D exciton ground state, and Mn2+ luminescence are different from those of CdSe: Mn nanocrystals or quantum wells. And it can be speculated that the other important properties, magneto-optical effect, for example, is also unique and worth further investigation. Acknowledgment. This work was supported by the National Natural Science Foundation of China, and the National Key Fundamental Research and Development Program of China (973 Program). Supporting Information Available: Reitveld refinement of the structure of CdSe‚hda0.5, structure relationship of CdSe‚L0.5 and hexagonal CdSe, and absorption/emission spectra of CdSe‚en0.5 (PDF). This material is available free of charge via the Internet at http://pubs.acs.org. CM048339Y