Superhydrophobic and Slippery Lubricant-Infused ... - ACS Publications

Subscriber access provided by University of Otago Library

Article

Superhydrophobic and Slippery Lubricant-Infused Flexible Transparent Nanocellulose Films by Photo-Induced Thiol-Ene Functionalization Jiaqi Guo, Wenwen Fang, Alexander Welle, Wenqian Feng, Ilari Filpponen, Orlando J. Rojas, and Pavel A. Levkin ACS Appl. Mater. Interfaces, Just Accepted Manuscript • DOI: 10.1021/acsami.6b11741 • Publication Date (Web): 16 Nov 2016 Downloaded from http://pubs.acs.org on November 17, 2016

Just Accepted “Just Accepted” manuscripts have been peer-reviewed and accepted for publication. They are posted online prior to technical editing, formatting for publication and author proofing. The American Chemical Society provides “Just Accepted” as a free service to the research community to expedite the dissemination of scientific material as soon as possible after acceptance. “Just Accepted” manuscripts appear in full in PDF format accompanied by an HTML abstract. “Just Accepted” manuscripts have been fully peer reviewed, but should not be considered the official version of record. They are accessible to all readers and citable by the Digital Object Identifier (DOI®). “Just Accepted” is an optional service offered to authors. Therefore, the “Just Accepted” Web site may not include all articles that will be published in the journal. After a manuscript is technically edited and formatted, it will be removed from the “Just Accepted” Web site and published as an ASAP article. Note that technical editing may introduce minor changes to the manuscript text and/or graphics which could affect content, and all legal disclaimers and ethical guidelines that apply to the journal pertain. ACS cannot be held responsible for errors or consequences arising from the use of information contained in these “Just Accepted” manuscripts.

ACS Applied Materials & Interfaces is published by the American Chemical Society. 1155 Sixteenth Street N.W., Washington, DC 20036 Published by American Chemical Society. Copyright © American Chemical Society. However, no copyright claim is made to original U.S. Government works, or works produced by employees of any Commonwealth realm Crown government in the course of their duties.

Page 1 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

ACS Applied Materials & Interfaces

1

Superhydrophobic and Slippery Lubricant-

2

Infused Flexible Transparent Nanocellulose

3

Films by Photo-Induced Thiol-Ene

4

Functionalization

5

Jiaqi Guo 1, Wenwen Fang 2, Alexander Welle 3, Wenqian Feng 4, Ilari Filpponen 1, Orlando J.

6

Rojas 1,5, Pavel Levkin 4,6*

7

1

8

University, FI-00076, Espoo, Finland

9

2

Department of Materials Science and Engineering, Aalto University, FI-00076, Espoo, Finland

10

3

Institute of Functional Interfaces, Karlsruhe Institute of Technology and Karlsruhe Nano Micro

11

Facility, Karlsruhe Institute of Technology, 76021 Karlsruhe, Germany

12

4

13

Eggenstein-Leopoldshafen, Germany

14

5

Department of Applied Physics, Aalto University, FI-00076, Espoo, Finland

15

6

Institute of Organic Chemistry, Karlsruhe Institute of Technology (KIT), Karlsruhe, Germany

Bio-based Colloids and Materials (BiCMat), Department of Bioproducts and Biosystems, Aalto

Institute of Toxicology and Genetics, Karlsruhe Institute of Technology (KIT), 76344

16 17 18

1 ACS Paragon Plus Environment


1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

19

Page 2 of 23

ABSTRACT

20

Films comprising nanofibrillated cellulose (NFC) are suitable substrates for flexible devices

21

in analytical, sensor, diagnostic and display technologies. However, some major challenges in such

22

developments include the high moisture sensitivity of NFC and the complexity of current methods

23

available for functionalization and patterning. In this work, we present a facile process for tailoring

24

the surface wettability and functionality of NFC films by a fast and versatile approach. Firstly, the

25

NFC films were coated with a layer of reactive nanoporous silicone nanofilament by

26

polycondensation of trichlorovinylsilane (TCVS). The TCVS afforded reactive vinyl groups,

27

thereby enabling simple UV-induced functionalization of NFC films with various thiol-containing

28

molecules via the photo “click” thiol-ene reaction. Modification with perfluoroalkyl thiols resulted

29

in robust superhydrophobic surfaces, which could then be further transformed into transparent

30

slippery lubricant-infused NFC films that displayed repellency against both aqueous and organic

31

liquids with surface tensions as low as 18 mN·m-1. Finally, transparent and flexible NFC films

32

incorporated hydrophilic micropatterns by modification with OH, NH2 or COOH surface groups,

33

enabling space-resolved superhydrophobic-hydrophilic domains. Flexibility, transparency,

34

patternability and perfect superhydrophobicity of the produced nanocellulose substrates warrants

35

their application in biosensing, display protection, biomedical and diagnostics devices.

36 37

KEYWORDS: photochemistry; thiol-ene reaction; nanocellulose; superhydrophobicity; slippery

38

lubricant-infused porous surface; SLIPS; superhydrophobicity; surface patterning.

39 40 41


Page 3 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

42


INTRODUCTION

43

Numerous efforts have been devoted to replace glass and plastic films with sustainable

44

materials with competitive strength, coefficient of thermal expansion and heat-resistance.1-3 Films

45

and nanopapers prepared from nanofibrillated cellulose (NFC, also named as CNF) are ideal

46

alternatives owing to the fact that they are mechanically strong (up to 350 MPa strength to rupture),

47

light-weighted (density of ~1.6 kg·m-3) and transparent (above 90% optical transmission); also,

48

they exhibit a low coefficient of thermal expansion (CTE < 8.5 ppm·K-1), are non-toxic and

49

biocompatible.4-8 Taken the above advantages into account, NFC films have been considered in

50

recent years for utilization in electronic devices including displays, transistors, organic light-

51

emitting diodes (OLEDs), touchscreens, lithium ion batteries, solar cells, transparent conductive

52

electrodes and antennas.9-14 More practical applications have taken advantage of the inherent

53

properties of NFC, which can be developed upon modification for uses as gas barriers, fire

54

retardant, shape-memory materials, optical systems, oil/water stabilizers, sensors, etc.15-20

55

However, owing to the high density of hydroxyl and oxygen-containing groups, NFC are highly

56

sensitive to moisture.21 To a large extent, this inherent characteristic related to water sorption

57

affects the properties of NFC-based materials (e.g. mechanical and barrier properties)22,23 and

58

further limits their applications.24,25 Thus, there is a strong need of methods for tailoring chemical

59

properties and enabling patterning of NFC films to generate additional functionality and improve

60

their applicability.

61

Introducing hydrophobic moieties to tailor cellulose wettability has been reported in the

62

literature via non-covalent adsorption through physical/chemical processing or covalent

63

attachment of hydrophobic moieties.26,27 Coating with cationic surfactants, mixing with lignin and

64

other procedures have been attempted.28,29 Chemical modification by esterification, amidation and



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 4 of 23

65

polymer grafting have been proposed.30-33 Sehaqui et al. reported on the grafting of alkyl chains

66

on NFC film. 30 Shimizu et al. published a procedure to attach quaternary alkylammoniums (QAs)

67

that resulted in the nanocellulose with hydrophobic properties.28 Given their rather smooth surface,

68

the maximum water contact angle (WCA) of NFC films has been limited to 130° while displaying

69

water droplet adhesion and high WCA hysteresis.28,30 Moreover, to the best of our knowledge,

70

there are no simple methods available for the fabrication of functional (hydrophobic-hydrophilic)

71

patterns on nanocellulose films.

72

Superhydrophobic surfaces (WCA > 150° and WCA hysteresis < 10°) possess extreme water

73

repellency, self-cleaning and various other unique properties that are useful in many applications.34

74

Numerous techniques have been reported to create superhydrophobic surfaces.35 Among them, a

75

promising route is the growth of polydimethylsiloxane nanofilaments, as was first reported in 2004

76

by Jung et al.36 and Zimmermann et al.,37,38 the nature of which was later described in detail by

77

Korhonen, Ras and coworkers.39 This simple approach has shown excellent superoleophobic

78

properties as well as resilience toward chemical and mechanical abrasion.40 More recently, we

79

expanded this approach by developing UV-reactive silicone nanofilaments on glass substrate,

80

thereby enabling formation of functional superhydrophobic patterns.41

81

Here we report a novel and facile process to functionalize, pattern and tailor the wetting

82

properties of NFC films. First, transparent and reactive porous TCVS silicone nanofilaments

83

(TCVS-SNFs) were installed onto the surface of the NFC films by in-situ polycondensation of

84

trichlorovinylsilane, which introduced both nanoscale roughness and reactive vinyl groups that

85

can be functionalized via photo-click thiol-ene reaction.42,43 Thereafter, superhydrophobicity was

86

developed by further modifying the NFC film with either alkyl or perfluoroalkyl thiols. In addition,


Page 5 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


87

slippery lubricant-infused NFC films (termed here as SLI-NFC), displaying perfect repellency

88

against both aqueous and organic liquids with low surface tension, was demonstrated (Figure 1).

89 90 91

Figure 1. Schematic illustration of the functionalization of films of nanofibrillated cellulose (NFC). The

92

NFC film surface is used as a substrate for growing silicone nanofilaments (SNFs) carrying reactive vinyl

93

groups (TCVS-SNFs) (i). The vinyl groups can be reacted with thiolated compounds via photo-induced

94

thiol-ene click reaction (ii and iii). For instance, they can carry hydrophilic or hydrophobic groups to endow

95

superhydrophobicity (ii) or superhydrophilicity (iii), respectively. The fabrication of a slippery, liquid-

96

infused porous NFC film surfaces (SLI-NFC) can be achieved by impregnation of porous NFC films that

97

have been fluorinated by the thiol-ene click reaction with a low-surface-energy, chemically inert lubricant

98

(iv).

99

EXPERIMENTAL SECTION

100

Materials. NFC films (A4 size) were provided by VTT Technical Research Center of

101

Finland.

102

hydrochloride and 1H, 1H, 2H, 2H-perfluorodecanethiol were purchased from Sigma-Aldrich,

Trichlorovinylsilane

(TCVS),

1-butanthiol,

2-mercaptoethanol,

cysteamine



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 6 of 23

103

Germany. Dichloromethane, n-hexane (HEX), ethyl acetate, dimethyl sulfoxide (DMSO), and

104

glycerol (GLY) were obtained from Merck, Germany. 4 Å molecular sieves and tetrahydrofuran

105

were purchased from Alfa Aesar, Germany. Toluene (99.5%, extra dry over 4 Å molecular sieves)

106

and dimethylformamide (DMF) were provided by VWR, Germany. Krytox 103 was purchased

107

from DuPond, Germany. Anhydrous ethanol and methylene blue hydrate were purchased from

108

Fluka, Germany. Food dye was obtained from August Teomasen Corp. (USA).

109

Growth of functional TCVS silicone nanofilaments (TCVS-SNFs) on NFC film. The

110

presence of traces of water in toluene was found critical for the success of the reaction. In order to

111

study the effect of water concentration, TCVS content and reaction time, certain volume (3.6 µL,

112

5.0 µL, 7.2 µL) of Millipore water (18.2 MΩ·cm) was added to 40 mL of dry toluene in a Falcon

113

tube. In order to fully disperse water in toluene, the mixture was sonicated at 50 °C for 40 min.

114

One piece of dried NFC film (1.5*1.5 cm) was immediately immersed into the toluene-water

115

mixture. Certain volume of TCVS (25 µL, 50 µL) was then added. After certain reaction time (6

116

or 24 h), the NFC film was washed thoroughly with ethanol and then dried under nitrogen flow.

117

Prior to immersion into toluene-water solution, the NFC film was dried under vacuum for 2 h. The

118

NFC film was placed horizontally in the Falcon tube.

119

Thiol-ene modification of NFC surface. The silane-modified NFC film was positioned on

120

a glass slide and then wetted with ca. 100 μL of hydrophobic thiol compounds: 20% (v/v) 1H, 1H,

121

2H, 2H-perfluorodecanethiol solution in ethyl acetate or 20% (v/v) 1-butanthiol in ethanol. In order

122

to improve the reaction efficiency, the sample was covered with a quartz slide (Science Services

123

GmbH, München, Germany). The covered NFC film was immediately irradiated with UV light

124

(OAI model 30 deep-UV collimated light source, San Jose, CA, USA) equipped with a 500 W

125

HgXe lamp (260 nm, ~9 mW·cm-2) (Ushio GmbH, Steinhöring, Germany) for 5 min. After


Page 7 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


126

irradiation, the NFC film was thoroughly washed with acetone or ethanol, depending on the thiol

127

compound used. Superhydrophilic NFC films were achieved by photo-induced thiol-ene reaction

128

with cysteamine or 2-mercaptoethanol.

129

Preparation of slippery, lubricant-infused NFC film (SLI-NFC). NFC films carrying

130

TCVS-SNFs were reacted with 1H, 1H, 2H, 2H-perfluorodecanethiol solution (20% (v/v) 1H, 1H,

131

2H, 2H-perfluorodecanethiol solution in ethyl acetate) under UV light (260 nm, ~9 mW·cm-2) for

132

5 min. After washing with acetone and drying under nitrogen flow, the superhydrophobized NFC

133

film was impregnated by spreading 20 L·cm-2 lubricant fluid (Krytox 103) with a pipette and

134

kept for 2 h to ensure spontaneous, complete wicking throughout the capillary structure of the

135

films. Afterwards, the NFC film was positioned vertically overnight to remove by gravity any

136

excess of lubricant.

137

Preparation of superhydrophobic-superhydrophilic patterns via thiol-ene reaction.

138

NFC films modified with the TCVS-SNFs were positioned on a glass slide that was wetted with

139

20 % of 1H, 1H, 2H, 2H-perfluorodecanethiol (in ethyl acetate) and covered with a photomask.

140

After exposure for 1 minute under UV light (260 nm, ~9 mW·cm-2), the NFC film was rinsed

141

immediately with acetone in a dark room and dried under nitrogen flow. In order to prepare

142

superhydrophilic areas, the NFC film was re-positioned on the glass slide and covered with a quartz

143

slide after addition of 100 µL of cysteamine hydrochloride or 2-mercaptoethanol solution (20% in

144

ethanol). After 1 min exposure to UV light, the NFC film was completely rinsed with ethanol and

145

dried with a nitrogen flow. The prepared NFC film carrying the hydrophobic-hydrophilic patterns

146

was stored until further use.

147

Characterization. Surface morphology of TCVS-SNFs grown on the NFC films was

148

assessed by using Scanning Electron Microscopy (SEM) (Zeiss Sigma VP). Prior to imaging, the



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 8 of 23

149

samples were sputtered with a ca. 7 nm Au/Pt layer (Emitech K100X). Transmittance of the

150

samples in 300~1000 nm was recorded by using a UV-Vis spectrophotometer (Biotek Epoch 2,

151

Germany). The static and dynamic water contact angles (advancing and receding water contact

152

angles) were measured with a custom-built contact angle system equipped with a UK 1115 digital

153

camera. The data were analyzed with Image J software. The static contact angle value and standard

154

deviations were obtained from the average of at least three measurements for each sample. Bending

155

and abrasion tests under load were carried out in order to investigate the mechanical robustness of

156

the NFC films carrying the TCVS-SNFs. Bending was performed for 100 cycles at a bending angle

157

of 45° while abrasion tests were conducted by cyclic displacement of 10 g or 100 g loads on the

158

surface. The water contact angles were measured before and after the experiments. ToF-SIMS

159

measurements were performed with a ToF.SIMS5 instrument (ION-TOF GmbH, Münster,

160

Germany) equipped with a Bi cluster primary ion source and a reflectron type analyzer. All the

161

ToF-SIMS spectra were normalized by total counts.

162

RESULTS AND DISCUSSION

163

Reactive NFC films. The NFC films used in this study were prepared in a pilot modular unit

164

that uses NFC hydrogels and the solvent casting technique. The NFC films had a thickness of ca.

165

20 μm and were flexible, translucent, strong and easy-to-handle (Figure 2a). SEM images in Figure

166

2b indicate a smooth NFC film surface that comprised cellulose nanofibers with a width of 5 - 20

167

nm and only nanometer scaled roughness (ca. 100 nm).44 Compared with traditional paper, the

168

transparency of the NFC films is very high (Figure 3c), with over 60% light transmittance at

169

wavelengths above 500 nm. Given that the both surface morphology (micro/nano structure) and

170

chemical composition (surface energy) play key roles in controlling surface wettability, we


Page 9 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


171

modified both characteristics of the NFC films.45 In NFC films, with their characteristic smooth

172

surfaces, the development of hydrophobicity is limited to water contact angles (WCA) of < 120°.

173

Hence, here we took advantage of the growth of reactive silicone nanofilaments, as reported by Li

174

et al.41 The active TCVS-SNFs micro/nanostructures were grown on the surface of the NFC films

175

(1.5 cm * 1.5 cm) by simple immersion in the TCVS solution (containing toluene and water) of a

176

given composition. TCVS condensing with water undergoes hydrolysis and polycondensation to

177

form a cross-linked porous polymeric silicone nanofilament layer on the NFC film (vertical

178

polymerization) (Figure S1). For instance, SEM images of the NFC films reveal full coverage with

179

TCVS-silicone nanofilaments (TCVS-SNFs) after immersion in 40 mL toluene containing 625

180

ppm TCVS and 125 ppm water (Figure 2c). As a result of the polycondensation process, TCVS

181

formed a porous TCVS-SNFs bearing photo-reactive vinyl groups. The full coverage and the

182

introduction of vinyl functional groups were further confirmed by time-of-flight secondary ion

183

mass spectroscopy (ToF-SIMs) (Figure 2d and Figure S2). The structure and properties of the

184

TCVS-SNFs coating layer is affected by several parameters, for instance reaction time and the

185

composition of the precursor TCVS solution (TCVS, solvent and water).

186



1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60

Page 10 of 23

187 188

Figure 2. (a) Photographs of a printed A4 paper sheet covered with a NFC film to illustrate its transparency

189

and flexibility (inset). The scale bar corresponds to 20 mm, (b) SEM image of the surface of a NFC film to

190

reveal the surface topography. Scale bars correspond to 2 µm and 200 nm, respectively (inset). (c) SEM

191

image revealing the surface topography of a NFC film after growing TCVS-SNFs on the NFC surface, such

192

as that shown in (b). Scale bars correspond to 2 µm and 200 nm (inset). (d) ToF-SIMS of chemical 2D

193

scans of the functionalized NFC film in (c) showing the distribution of C2H3+ fragments.

194

Superhydrophobic/hydrophilic NFC films via thiol-ene click reaction. Figure 3a includes

195

the values of the water contact angle (WCA) of NFC films after modification. The initial static

196

WCA (θst) of NFC film was 33° owing to the hydrophilic characteristics of cellulose which

197

comprises hydroxyl and oxygen-containing groups. TCVS-SNFs grown on the surface of the NFC

198

films produced a micro/nanostructured layer that resulted in an increased θst of 123° (Table S1).

199

In order to further investigate the possibility for the NFC films coated with TCVS-SNFs to

200

develop superhydrophobicity or superhydrophilicity, the prepared hydrophobic and reactive NFC 10 ACS Paragon Plus Environment

Page 11 of 23

1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 17 18 19 20 21 22 23 24 25 26 27 28 29 30 31 32 33 34 35 36 37 38 39 40 41 42 43 44 45 46 47 48 49 50 51 52 53 54 55 56 57 58 59 60


201

surface was modified with various alkylthiols via the photo-induced thiol-ene reaction.

202

Functionalization of the reactive TCVS-NFC film with hydrophobic 1-butanthiol (named therein

203

“alkylated NFC” surface) or with 1H,1H,2H,2H-perfluorodecanethiol (named thereafter as

204

“fluorinated NFC” surface) endowed the surface with superhydrophobicity (see supporting video

205

V1). The θst for the alkylated and the fluorinated NFC were 166° and 167°, respectively. The WCA

206

hysteresis for both surfaces were < 3°. We note that after installation of the fluorinated compound,

207

the θst of both sides of the NFC film was > 155° (and WCA hysteresis < 3°). The “fluorinated NFC”

208

surface showed pinning of droplets of solvents, including glycerol ( = 64.0 mN·m-1) or n-hexane

209

( = 18.4 mN·m-1) even at 90o (Figure 4 a). Functionalization of the reactive TCVS-NFC film with

210

hydrophilic cysteamine or 2-mercaptoethanol resulted in a decrease of θst from 123° to ca. 8° in

211

both cases (Figure 3a).

212

In order to verify the superhydrophobic character of the fluorinated NFC films, a water

213

droplet was deposited on films that were positioned horizontally. As the film was moved in one

214

direction at a constant velocity (0.4 cm·s-1), it was observed that the water droplet did not adhere

215

on the surface, confirming a very low WCA hysteresis (Figure 3b and supporting video V2). It is

216

well known that a hierarchical micro/nano scale roughness is required for producing

217

superhydrophobic surfaces; however, this can cause a reduction in transparency due to increased

218

scattering of light. Thus, it is difficult to create superhydrophobic surfaces that at the same time

219

are transparent.41 Remarkably, functionalization of the NFC films with TCVS-SNFs did not

220

significantly affect their transparency (Figure 3a and Figure S3). From the UV-Vis data, we found

221

a reduction by only 130° (Figure S4).

243

Omniphobic and slippery lubricant-infused hydrophobic NFC films (SLI-NFC). Liquid

244

infused porous polymer surfaces (SLIPS) introduced by Aizenberg et al. have attracted attention

245

in the scientific community due to their simple fabrication, highly repellent properties towards

246

various liquids,46-48 as well as antiicing,49 antibiofouling,50-53 excellent eukaryotic cell54 and blood

247

repellency.55 Omniphobic slippery membranes and films possessing the above mentioned

248

properties could find numerous applications in biomedical, biotechnological and other industries.56

249

Hydrophobic NFC films are uniquely suited for this application due to the transparency, good

250

mechanical properties, availability and low costs of cellulose. To create a slippery lubricant-

251

infused NFC membrane (SLI-NFC), we impregnated a fluorinated NFC membrane with

252

perfluoropolypropylene oxide lubricant (Krytox 103). The Krytox 103 was infiltrated into the

253

roughened nanostructure formed by TCVS-SNFs on the NFC film surface. Thus, we created

254

surfaces with high roughness (TCVS-SNFs growth) and matched the surface chemistry

255

(fluorination) to facilitate the spontaneous spreading of Krytox 103 in the porous NFC film. The

256

produced SLI-NFC film showed excellent omniphobic liquid repellent properties (Figure 4 a) and

257

enhanced optical transparency (Figure 3 c). Thus, the SLI-NFC films possessed high contact angles

258

with very low contact angle hysteresis (α